Journal of Materials Science

, Volume 27, Issue 9, pp 2353–2362 | Cite as

Influence of thermal quench on fracture strength, elastic modulus and internal friction of glass plates

  • Chin-Chen Chiu
  • E. D. Case
Papers
Received:
Accepted:

Abstract

The fracture strength and residual stress in glass microscope slides for water, oil and air thermal quenching are compared with the authors' prior theoretical analysis. In addition, elastic modulus and internal friction measurements are used to evaluate the effects of the thermal quenching.

Keywords

Polymer Residual Stress Elastic Modulus Theoretical Analysis Internal Friction 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    C. C. Chiu andE. D. Case,J. Mater. Sci. 26 (1991) 000.Google Scholar
  2. 2.
    D. P. H. Hasselman, R. Badaliance, K. R. McKinney andE. P. Chen,ibid. 11 (1976) 458.Google Scholar
  3. 3.
    M. Ashizuka, T. E. Easler andR. C. Bradt,J. Amer. Ceram. Soc. 66 (1983) 542.Google Scholar
  4. 4.
    H. Kamizono andK. Niwa,J. Mater. Sci. Lett. 3 (1984) 588.Google Scholar
  5. 5.
    F. V. Tooley, “Handbook of Glass Manufacture”, Vol. 1 (Ogden, New York, 1961) p. 391.Google Scholar
  6. 6.
    E. D. Case,J. Mater. Sci. 19 (1984) 3702.Google Scholar
  7. 7.
    K. Matsushita, S. Kuratani, T. Okamoto andM. Shimada,J. Mater. Sci. Lett. 3 (1984) 345.Google Scholar
  8. 8.
    F. P. Mallinder andB. A. Proctor,Phys. Chem. Glasses 5 (4) (1964) 91.Google Scholar
  9. 9.
    J. D. L. Vega andD. C. Bogue,Chem. Eng. Commun. 53 (1987) 23.Google Scholar
  10. 10.
    N. M. Pavlushkin, S. I. Silvestrovich, V. M. Firsov andV. D. Kazakov,J. Mater. Sci. 4 (1969) 479.Google Scholar
  11. 11.
    J. V. Fitzgerald,J. Amer. Ceram. Soc. 34 (1951) 388.Google Scholar
  12. 12.
    D. E. Day andG. E. Rindone,ibid. 44 (1961) 161.Google Scholar
  13. 13.
    E. Schreiber, O. L. Anderson andN. Soga, “Elastic Constants and Their Measurements (McGraw-Hill, New York, 1974) p. 82.Google Scholar
  14. 14.
    J. B. Wachtman,Rev. Sci. Instrum. 29 (1958) 517.Google Scholar
  15. 15.
    H. M. Chou andE. D. Case,Mater. Sci. Engng 100 (1988) 7.Google Scholar
  16. 16.
    B. R. Lawn andD. B. Marshall,Phys. Chem. Glasses 18 (1) (1977) 7.Google Scholar
  17. 17.
    D. B. Marshall andB. R. Lawn,J. Amer. Ceram. Soc. 60 (1977) 86.Google Scholar
  18. 18.
    Idem, ibid. 61 (1978) 21.Google Scholar
  19. 19.
    G. R. Anstis, P. Chantikul, B. R. Lawn andD. B. Marshall,ibid. 64 (1981) 533.Google Scholar
  20. 20.
    R. C. Buchanan, “Ceramic Materials for Electronics” (Dekker, New York, 1986) p. 10.Google Scholar
  21. 21.
    R. E. Reed-Hill, “Physical Metallurgy Principles”, 2nd Edn (Van Nostrand-Reinhold, New York, 1973) p. 704.Google Scholar
  22. 22.
    H. S. Carslaw andJ. C. Jaeger, “Conduction of Heat in Solids” (Clarendon, Oxford, 1959) p. 24.Google Scholar
  23. 23.
    W. D. Kingery, H. K. Bowen andD. R. Uhlmann, “Introduction to Ceramics” (Wiley, New York, 1976) p. 822.Google Scholar
  24. 24.
    A. Paul, “Chemistry of Glasses” (Chapman and Hall, New York, 1982) p. 76.Google Scholar
  25. 25.
    O. S. Narayanaswamy,J. Amer. Ceram. Soc. 61 (1978) 146.Google Scholar
  26. 26.
    E. Volterra andE. C. Zachmanoglou, “Dynamics of Vibrations” (Merrill Books, Columbus, Ohio, 1965) p. 321.Google Scholar
  27. 27.
    C. C. Chiu andE. D. Case,Mater. Sci. Engng,A132 (1991) 39.Google Scholar
  28. 28.
    I. H. Shames andC. L. Dym, “Energy and Finite Element Methods in Structural Mechanics” (Hemisphere, New York, 1985) p. 334.Google Scholar
  29. 29.
    G. A. Gogotsi, Y. L. Groushevsky andK. K. Strelov,Ceram. Internat. 4 (1978) 113.Google Scholar
  30. 30.
    M. V. Swain,J. Amer. Ceram. Soc. 73 (1990) 621.Google Scholar
  31. 31.
    C. W. Smith, Exper. Mech.20 (1980) 390.Google Scholar
  32. 32.
    A. Shukla andJ. W. Dally,Ibid.,21 (1981) 63.Google Scholar

Copyright information

© Chapman & Hall 1992

Authors and Affiliations

  • Chin-Chen Chiu
    • 1
  • E. D. Case
    • 1
  1. 1.Department of Metallurgy, Mechanics and Materials ScienceMichigan State UniversityEast LansingUSA

Personalised recommendations