Mechanical and corrosion properties of low antimony lead alloys

  • T. Rogatchev
  • St. Ruevski
  • D. Pavlov
Article

Abstract

The mechanical properties (tensile strength, hardness, and relative elongation) of lead alloys containing 2–3% Sb, 0.1–0.5% Sn, and 0.1–0.5% As in the as-cast state and after annealing and quenching were determined. It is established that quenching significantly improves the mechanical properties of the alloys. By variation of the tin content and the thermal treatment conditions it is possible to obtain within certain limits the desired mechanical properties. The anodic dissolution c.d. of lead, and lead alloys containing 2.2% Sb, 0.11% As and 0.25% Sn was determined as a function of the potential. It is found that this alloy has a higher rate of anodic dissolution and lower oxygen overvoltage than those of pure lead.

Keywords

Oxygen Physical Chemistry Mechanical Property Tensile Strength Treatment Condition 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    J. Burbank, U.S. Naval Res. Lab. Report, 6078 (1964).Google Scholar
  2. [2]
    J. L. Dawson, M. L. Gillibrand and J. Wilkinson, ‘Power sources’ vol. 3, p. 1, Editor D. H. Collins, Oriel Press, Newcastle-upon-Tyne (England), 1971.Google Scholar
  3. [3]
    E. Pelzel,Z. Metallkde 49 (1958) 102.Google Scholar
  4. [4]
    H. Horchers and M. Kainz,Metallwissenschaft und Technik 25 (1965) 103.Google Scholar
  5. [5]
    H. Horchers and K. Bunnenberg,Metall 15 (1961) 765.Google Scholar
  6. [6]
    H. Borchers., S. C. Nijhawan and W. Sharfenberger,Metallwissenschaft und Technik. 28 (1974) 863.Google Scholar
  7. [7]
    G. Gordiakova, M. Dasojan, N. Bolotovsky, V. Bolotovsky, G. Krivchenko,Sb. rabot Chim. Ist. toka 9 (1974) 11 L. Energia 1974.Google Scholar
  8. [8]
    D. Pavlov, M. Boton, M. Stoijanova,Isv, Inst, Fisikochimia Bulg. Acad. Nauk 5 (1965) 55; D. Pavlov and T. Rogatchev,Werkstoffe und korrosion 19 (1968) 671.Google Scholar

Copyright information

© Chapman and Hall Ltd 1976

Authors and Affiliations

  • T. Rogatchev
    • 1
  • St. Ruevski
    • 1
  • D. Pavlov
    • 1
  1. 1.Central Laboratory of Electrochemical Power SourcesBulgarian Academy of SciencesSofiaBulgaria

Personalised recommendations