Melt elongation and structure of linear polyethylene (HDPE)
- 155 Downloads
Different linear polyethylenes (HDPE) were elongated in the molten state at constant strain rates up to very large total strains (maximum stretch ratio λ=270). The structure of these polyethylenes was investigated by GPC, C-13-NMR, and IR. From the structural parameters it follows that the strain hardening of the HDPE melts investigated here is not due to the short chain branches of the mainly linear molecules but influenced by a small amount of very long molecules of the molecular weight distribution. For the influence of the temperature on the strain hardening phenomenon an unexpected result was found additionally.
KeywordsPolymer Molecular Weight Polyethylene Strain Hardening Weight Distribution
Unable to display preview. Download preview PDF.
- Meissner, J., Rheol. Acta10 (1971), 230Google Scholar
- Macosko, C.W., Lorntson, J.M., SPE Techn. Papers19 (1973), 461Google Scholar
- Tsang, W.K.W., Dealy J.M., J. Non-Newt. Fluid Mech.9 (1981), 203Google Scholar
- Münstedt, H., Laun, H.M., Rheol. Acta20 (1981), 211Google Scholar
- Axelson, D.E., Levy, G.C., Mandelkern, L., Macromolecules12 (1979), 41Google Scholar
- Meissner, J., Raible, T., Stephenson, S.E., J. Rheol.25 (1981), 1Google Scholar
- Linster, J.J., Ph.D. dissertation No. 7692, ETH Zürich (1984)Google Scholar
- Münstedt, H., J. Rheol.24 (1980), 847Google Scholar
- Franck, A., Meissner, J., Rheol. Acta23, (1984), 117Google Scholar
- Raible, T., Meissner, J. in G. ASTARITA, G. MARRUCCI, and L. NICOLAIS (editors):Rheology, Vol. 2 (1980), 425, Plenum Corp. New YorkGoogle Scholar