Monatshefte für Chemie / Chemical Monthly

, Volume 108, Issue 3, pp 567–575 | Cite as

Dehydratisierung von Butanolen an Hartstoffcarbiden

Katalytische Eigenschaften von Hartstoffen, 1. Mitt.
  • Rudolf Bürkl
  • Heinrich Noller
Anorganische, Struktur- und Physikalische Chemie
Received:

Dehydration of butanols on refractory carbides

Abstract

The dehydration of 1-butanol and 2-butanol was studied in a microcatalytic reactor over refractory carbides (except Hf and Cr) in a temperature range between 40 and 500°C. The activity was comparable with that of oxides and salts. Varying the pulse size, the surface coverage — and the amount of reaction products—was found to be in good correlation with aLangmuir adsorption isotherm. Heats of adsorption and activation energies were calculated from experiments at different temperatures, the activation energies, using two different methods with good agreement. The activity of the refractory carbides increased in the periodic table of the elements from the left to the right and from bottom to top, as observed with salt-catalysts.

This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Literatur

  1. 1.
    D. Baresel, W. Gellert, W. Sarholz undG. Schulz-Ekloff, Chemie-Ing.-Techn.46, 573 (1974).Google Scholar
  2. 2.
    H. Binder, A. Köhling, W. Kuhn, W. Lindner undG. Sandstede, Nature224, 1299 (1969).Google Scholar
  3. 3.
    H. Böhm, Nature227, 483 (1970).Google Scholar
  4. 4.
    G. Vértes, G. Horányi undS. Szakács, J. Chem. Soc. Perkin Trans. II1973, 1400.Google Scholar
  5. 5.
    H. Buchner, M.-A. Gutjahr, K. Gross undK.-D. Beccu, Mh. Chem.104, 160 (1973).Google Scholar
  6. 6.
    R. B. Levy undM. Boudart, Science181, 547 (1973).Google Scholar
  7. 7.
    L. H. Bennett, J. R. Cuthill, A. J. McAlister, N. E. Erickson undR. E. Watson, Science187, 858 (1975).Google Scholar
  8. 8.
    H. Noller undK. Ostermeier, Ber. Bunsenges. physik. Chem.63, 191 (1959).Google Scholar
  9. 9.
    L. K. Doraiswamy undD. G. Tajbl, Cat. Rev.-Sci. Eng.10, 177 (1974).Google Scholar
  10. 10.
    S. F. Exell, R. Roggen, J. Gillot undB. Lux, Paper No. 258, Electrochemical Soc., Boston, October 7–11, 1973.Google Scholar
  11. 11.
    K. Thomke, Dissertation, Techn. Hochsch. Wien, 1972.Google Scholar
  12. 12.
    P. Andreu, M. Rosa-Brusin, C. Sanchez undH. Noller, Z. Naturforsch.22 b, 809 (1967).Google Scholar
  13. 13.
    W. Kladnig, Dissertation, Techn. Hochsch. Wien, 1972.Google Scholar
  14. 14.
    H. Zoidl, Diplomarbeit, Techn. Hochsch. Wien, 1972.Google Scholar
  15. 15.
    V. Gutmann, Coord. Chem. Rev.15, 207 (1975).Google Scholar
  16. 16.
    H. Noller, P. Andreu undM. Hunger, Angew. Chem.83, 185 (1971).Google Scholar
  17. 17.
    H. Noller undW. Kladnig, Cat. Rev.-Sci. Eng.13, 149 (1976).Google Scholar
  18. 18.
    R. Bürkl, Dissertation, Techn. Univ. Wien, 1976.Google Scholar
  19. 19.
    K. Schwarz, persönliche Mitteilung.Google Scholar

Copyright information

© Springer-Verlag 1977

Authors and Affiliations

  • Rudolf Bürkl
    • 1
  • Heinrich Noller
    • 1
  1. 1.Institut für Physikalische ChemieTechnische Universität WienWienÖsterreich

Personalised recommendations