Influence of the chemical composition of kenaf bast and core on the alkaline pulping response

  • Yoshito OhtaniEmail author
  • Bibhuti Bushan Mazumder
  • Kazuhiko Sameshima
Original Paper

Abstract

The bast and core of kenaf,Hibiscus cannabinus L., have markedly different chemical components and alkaline cooking responses. The bast had about double the hot-water extractives content and only about half the lignin content of the core. The core contained a large amount of hemicellulose, mostly composed of xylan. The lignin structures of bast and core were also quite different: The former had a significant abundance of syringyl structures. Evidence showed that the bast was much more easily delignified than the core. When the bast and core were cooked together in alkaline condition, the pulp yields at the same kappa number were higher than those of the individual pulpings of bast and core. The bast-core pulping gave a positive effect on the yield of bast pulp in the sodaanthraquinone and kraft pulpings. On the other hand, kenaf was abundant in the hot water extractives. These extractives consumed alkali during cooking to a relatively large extent but acted as a protector of hemicellulose and slightly increased the pulp yields.

Key words

Kenaf Bast and core Alkaline pulping Lignin Hot-water extractives 

References

  1. 1.
    Morimoto M (1999) Recent topics on the utilization of non-wood plant fibers — from FAO yearbook forest products 1997-. Jpn J Paper Technol 42(9):1–5Google Scholar
  2. 2.
    Morimoto M (1998) Nonwood plant fiber pulp — the status quo and future. Jpn TAPPI 52:1205–1211CrossRefGoogle Scholar
  3. 3.
    Kaldor AF (1992) Kenaf, an alternate fiber for the pulp and paper industries in developing and developed countries. TAPPI J 75(10):141–145Google Scholar
  4. 4.
    Neto CP, Seca A, Fradinho D, Coimbra MA, Domingues F, Evtuguin D, Silvestre A, Cavaleiro JAS (1996) Chemical composition and structural features of the macromolecular components of Hibiscus cannabinus grown in Portugal. Ind Crop Prod 5:189–196CrossRefGoogle Scholar
  5. 5.
    Seca AML, Cavaleiro JAS, Domingues FMJ, Silvestre AJD, Evtuguin D, Neto CP (1997) Structural characteristics of the bark and core kenaf lignin (variety Salvador). In: Proceedings 9th International Symposium on Wood and Pulping Chemistry, June 9–12, Montreal, (132) 1–4Google Scholar
  6. 6.
    Seca AML, Cavaleiro JAS, Domingues FMJ, Silvestre AJD, Evtuguin D, Neto CP (1998) Structural characterization of the bark and core lignins from kenaf (Hibiscus cannabinus). J Agric Food Chem 46:3100–3108CrossRefGoogle Scholar
  7. 7.
    Pande H, Roy DN (1996) Delignification kinetics of soda pulping of kenaf. J Wood Chem Technol 16:311–325CrossRefGoogle Scholar
  8. 8.
    TAPPI test methods, T222 om-88. TAPPI Press, Atlanta, GAGoogle Scholar
  9. 9.
    TAPPI useful method 250. TAPPI Press, Atlanta, GAGoogle Scholar
  10. 10.
    Usuda M, Mizumachi H, Iiyama K. Morohoshi N. Yamaguchi A (eds) (1985) Mokuzai Kagaku Jikkensho II Kagaku-hen, Chugai-Sangyo,p 155Google Scholar
  11. 11.
    TAPPI Test Methods, T203 om-93. TAPPI Press, Atlanta, GAGoogle Scholar
  12. 12.
    Usuda M, Mizumachi H, Iiyama K, Morohoshi N, Yamaguchi A (eds) (1985) Mokuzai Kagaku Jikkensho II Kagaku-hen, Chugai-Sangyo, pp 187–190Google Scholar
  13. 13.
    Chen CL (1992) Nitrobenzene and cupric oxide oxidations. In: Lin SY, Dence CW (eds) Methods in lignin chemistry. Springer, Berlin, pp 301–321CrossRefGoogle Scholar
  14. 14.
    Usuda M, Mizumachi H, Iiyama K, Morohoshi N, Yamaguchi A (eds) (1985) Mokuzai Kagaku Jikkensho II Kagaku-hen, Chugai-Sangyo, pp 160–161Google Scholar
  15. 15.
    Ohtani Y, Noguchi T, Sameshima K (1996) Influence of anthraquinone addition method on alkaline pulping of kenaf bast. Sen'i Gakkaishi 52:175–179CrossRefGoogle Scholar
  16. 16.
    TAPPI Test Methods, T236 cm-85. TAPPI Press, Atlanta, GAGoogle Scholar
  17. 17.
    Aorigele, Konno H, Sano Y, Uraki Y, Sasaya N, Sameshima K (1993) Separation and utilization of kenaf components obtained by continuous acetic acid pulping under normal pressure (in Japanese). In: Proceedings of the Hokkaido Branch, Japan Wood Research Society, vol 25, pp 57–61Google Scholar
  18. 18.
    Abbott TP, Bagby MO, James C, Peterson RE (1986) A14C balance on nitrobenzene oxidized kenaf lignin. J Wood Chem Technol 6:487–494CrossRefGoogle Scholar
  19. 19.
    Ralph J (1996) An unusual lignin from kenaf. J Natural Prod 59:341–342CrossRefGoogle Scholar
  20. 20.
    Abbott TP, Tjarks LW, Bagby MO (1987) Kenaf lignin structure by correlation of CMR, FTIR and chemical analysis. In: Proceedings of the Pulping Conference, pp 177–183Google Scholar
  21. 21.
    Abbott TP, Palmer DM, Gordon SH, Bagby MO (1988) Solid state analysis of plant polymers by FTIR. J Wood Chem Technol 8:1–28CrossRefGoogle Scholar
  22. 22.
    Kuroda K, Mazumder BB, Ohtani Y, Sameshima K (1999) Characterization of kenaf (Hibiscus cannabinus L.) lignin by analytical pyrolysis. In: Proceedings of the 2nd annual meeting of the American Kenaf Society, March, San Antonio, TX, pp 125–137Google Scholar
  23. 23.
    Wilder HD, Daleski EJ (1965) Delignification rate studies. Part II of a series on kraft pulping kinetics. TAPPI 48:293–297Google Scholar
  24. 24.
    Wilson G, Proctor AR (1970) Reactions of wood components with hydrogen sulphide. Part V. The kinetics of kraft and soda delignification of western hemlock. Pulp Paper Mag Can 71:T483-T487Google Scholar
  25. 25.
    Nakauchi A, Sameshima I, Ohtani Y, Sameshima K, Kumai S, Fukumi R (1998) Development of industrial plant resources in the Japanese mountainous villages. II. Analyses of kenaf chemical components as the plant resources for agroforestry. Bull Kochi Univ For 25:219–226Google Scholar

Copyright information

© The Japan Wood Research Society 2001

Authors and Affiliations

  • Yoshito Ohtani
    • 1
    Email author
  • Bibhuti Bushan Mazumder
    • 1
  • Kazuhiko Sameshima
    • 1
  1. 1.Department of Forest Science, Faculty of AgricultureKochi UniversityKochiJapan

Personalised recommendations