Effect of water and ice on strength and fracture toughness of intermittently bonded boron-epoxy composites

  • A. G. Atkins
  • Y. W. Mai
Papers
Received:
Accepted:

Abstract

The effects of water and ice on the strength and fracture toughness of boron-epoxy composites with polyurethane intermittent bonding have been investigated. Neither simple soaking in water nor soaking followed by freezing and thawing have marked effects on the strength of the fully-coated composites, but they have disastrous effects on the uncoated composites. Toughness is affected only marginally, with some small reductions in the fully-coated samples, and with essentially no effect on the uncoated composites. An analysis is presented which explains adequately the experimental strength and toughness results obtained, and which is based on an argument that water absorption reduces the interfacial shear strength only of the uncoated areas and not those regions coated by the polyurethane varnish. The results indicate that the advantages of appropriate intermittent bonding (i.e. high strength combined with high toughness) are retained in wet conditions so that such composites may be favourably used in such adverse environmental conditions.

Keywords

Polymer Fracture Toughness Shear Strength Polyurethane Water Absorption 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    T. U. Marston, A. G. Atkins andD. K. Felbeck,J. Mater. Sci. 9 (1974) 447.Google Scholar
  2. 2.
    A. G. Atkins,Nature, Letters 252 (1974) 116.Google Scholar
  3. 3.
    Idem, J. Mater. Sci. 10 (1975) 819.Google Scholar
  4. 4.
    J. Cook andJ. E. Gordon,Proc. Roy. Soc. (London) A282 (1964) 508.Google Scholar
  5. 5.
    P. W. R. Beaumont andB. Harris,J. Mater. Sci. 7 (1972) 1265.Google Scholar
  6. 6.
    B. Harris, P. W. R. Beaumont andE. M. de Ferran,ibid 6 (1971) 238.Google Scholar
  7. 7.
    H. T. Sumsion andD. P. Williams, in “Fatigue of Composite Materials”, ASTM STP 569 (1975) pp. 226–247.Google Scholar
  8. 8.
    B. Gershon andG. Marom,J. Mater. Sci. 10 (1975) 1549.Google Scholar
  9. 9.
    C. Gurney andJ. Hunt,Proc. Roy. Soc. (London) A299 (1967) 508.Google Scholar
  10. 10.
    C. Gurney andY. W. Mai,Eng. Fract. Mech. 4 (1972) 853.Google Scholar
  11. 11.
    C. Gurney andK. M. Ngan,Proc. Roy. Soc. (London) A325 (1971) 207.Google Scholar
  12. 12.
    C. Gurney, Y. W. Mai andR. C. Owen,ibid A340 (1975) 213.Google Scholar
  13. 13.
    Y. W. Mai,J. Adhesion 7 (1975) 141.Google Scholar
  14. 14.
    Y. W. Mai, A. G. Atkins andR. M. Caddell,Int. J. Fracture 9 (1975) 939.Google Scholar
  15. 15.
    A. G. Atkins, paper presented at AIAA/ASME/-SAE 16th Structures, Structural Dynamics, and Materials Conference, Denver, Colorado, 27–29 May, 1975. See alsoTrans. AIAA (Journal of Aircraft),12 (1976) 850.Google Scholar
  16. 16.
    M. R. Piggott,J. Mater. Sci. 5 (1970) 669.Google Scholar
  17. 17.
    P. W. R. Beaumont, J. Fitzrandolph, D. C. Philips andA. S. Tetelman,J. Com. Mater. 5 (1971) 542. See alsoP. W. R. Beaumont, J. Fitzrandolph, D. C. Philips andA. S. Tetelman J. Mater. Sci. 7 (1972) 289.Google Scholar
  18. 18.
    A. Kelly, in “Strong Solids” (Oxford University Press, 1966).Google Scholar

Copyright information

© Chapman and Hall Ltd. 1976

Authors and Affiliations

  • A. G. Atkins
    • 1
  • Y. W. Mai
    • 2
  1. 1.Delta Materials Research LimitedIpswichUK
  2. 2.Department of Mechanical EngineeringImperial College of Science and TechnologyLondonUK

Personalised recommendations