Evaluation ofKIc of brittle solids by the indentation method with low crack-to-indent ratios

  • K. Niihara
  • R. Morena
  • D. P. H. Hasselman
Article

Keywords

Polymer Brittle Indentation Method Brittle Solid 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    A. G. EVANS and E. A. CHARLES,J. Amer. Ceram. Soc. 59 (1976) 371.Google Scholar
  2. 2.
    B. R. LAWN and E. R. FULLER,J. Mater. Sci. 10 (1975) 2016.Google Scholar
  3. 3.
    A. G. EVANS, “Fracture Mechanics of Ceramics”, Vol. 1, edited by R. C. Bradt, D. P. H. Hasselman and F. F. Lange (Plenum Press, New York, 1974) p. 17.Google Scholar
  4. 4.
    J. J. PETROVIC, L. A. JACOBSON, P. K. TALTY and A. K. VASUDEVAN,J. Amer. Ceram. Soc. 58 (1975) 113.Google Scholar
  5. 5.
    S. PALMQVIST,Jernkontorets Ann. 141 (1957) 300.Google Scholar
  6. 6.
    Idem,,Arch. Eisenhuettenwes 33 (1962) 629.Google Scholar
  7. 7.
    V. W. DAWIHL and G. ALTMEYER,Z. Metallik 55 (1964) 231.Google Scholar
  8. 8.
    B. R. LAWN and M. V. SWAIN,J. Mater. Sci. 10 (1975) 113.Google Scholar
  9. 9.
    B. R. LAWN and T. R. WILSHAW, ibid.10 (1975) 1049.Google Scholar
  10. 10.
    A. G. EVANS and T. R. WILSHAW,Acta Metall. 24 (1976) 939.Google Scholar
  11. 11.
    B. C. EDWARDS and P. J. PHILLIPS,J. Mater. Sci. 10 (1975) 1236.Google Scholar
  12. 12.
    B. R. LAWN, T. JENSEN and A. ARORA, ibid.11 (1976) 573.Google Scholar
  13. 13.
    M. G. MENDIRATTA and J. J. PETROVIC, ibid.11 (1976) 973.Google Scholar
  14. 14.
    B. R. LAWN and A. G. EVANS, ibid.12 (1977) 2195.Google Scholar
  15. 15.
    I. M. OGILVY, C. M. PERROT and J. M. SUITER,Wear 43 (1977) 239.Google Scholar
  16. 16.
    J. T. HAGAN,J. Mater. Sci. 14 (1979) 462.Google Scholar
  17. 17.
    J. T. HAGAN and M. V. SWAIN,J. Phys. D. Appl. Phys. 11 (1978) 2091.Google Scholar
  18. 18.
    J. LANKFORD and D. L. DAVIDSON,J. Mater. Sci. 14 (1979) 1662.Google Scholar
  19. 19.
    Idem,, ibid.14 (1979) 1669.Google Scholar
  20. 20.
    J. T. HAGAN, ibid.14 (1979) 2975.Google Scholar
  21. 21.
    B. R. LAWN and D. B. MARSHALL,J. Amer. Ceram. Soc. 62 (1979) 347.Google Scholar
  22. 22.
    J. T. HAGAN,J. Mater. Sci. 15 (1980). 1417.Google Scholar
  23. 23.
    J. T. HAGAN, M. V. SWAIN and J. E. FIELD, “The Science of Ceramic Machining and Surface Finishing II” edited by B. J. Hockey and R. W. Rice (NBS Special Publication, U.S. Government Printing Office, Washington DC, 1979) p. 15.Google Scholar
  24. 24.
    J. E. BLENDELL, PhD Thesis, MIT, 1979.Google Scholar
  25. 25.
    G. C. SIH, “Handbook of Stress Intensity Factors”, (Lehigh University Press, Bethlehem, PA., 1973).Google Scholar
  26. 26.
    K. NIIHARA,Yogyo-kyokai-Shi, unpublished work.Google Scholar

Copyright information

© Chapman and Hall Ltd 1982

Authors and Affiliations

  • K. Niihara
    • 1
  • R. Morena
    • 1
  • D. P. H. Hasselman
    • 1
  1. 1.Department of Materials EngineeringVirginia Polytechnic Institute and State UniversityBlacksburgUSA

Personalised recommendations