Phase equilibria in the system CaO-ZnO-B2O3 at 850°C

  • 64 Accesses

Abstract

Phase equilibria in the system CaO-ZnO-B2O3 were investigated at 850°C using X-ray powder diffraction techniques. The binary phases reported previously were confirmed, but no ternary phases were found. Solid solution effects were investigated for the binary phases by comparison of the patterns, whereas for calcium oxide and zinc oxide, accurate lattice parameters were compared. No solid solutions were detected.

This is a preview of subscription content, log in to check access.

References

  1. 1.

    E. T. Carlson,J. Res. Nat. Bur. Stand. 9 (1932) 825.

  2. 2.

    B. L. Fletcher, J. R. Stevenson, andA. Whitaker,J. Amer. Ceram. Soc. 53 (1970) 95.

  3. 3.

    P. B. Hart andC. S. Brown,J. Inorg. Nuclear Chem. 24 (1962) 1057.

  4. 4.

    A. Whitaker,J. Mater. Sci. 7 (1972) 189.

  5. 5.

    E. R. Segnit,J. Amer. Ceram. Soc. 37 (1954) 274.

  6. 6.

    ASTM X-ray Powder Diffraction Data File, Card No. 4-0777. American Society for Testing and Materials, Philadelphia, Pennsylvania.

  7. 7.

    ASTM X-ray Powder Diffraction Data File, Card No. 5-0664. American Society for Testing and Materials, Philadelphia, Pennsylvania.

  8. 8.

    S. V. Berger,Acta Chem. 7 (1953) 611.

  9. 9.

    F. C. Kracek, G. W. Morey, andH. E. Merwin,Amer. J. Sci. 35A (1938) 143.

  10. 10.

    D. E. Harrison andF. A. Hummel,J. Electrochem Soc. 103 (1956) 491.

  11. 11.

    H. Bauer,Z. anorg. Chem. 320 (1963) 306.

  12. 12.

    J. Fayos, S. García-Blanco, andL. Rivoir,Anales Real Soc. Españ. Fís. Quím. 62A (1966) 297.

  13. 13.

    H. E. Swanson andE. Tatge J. Res. Nat. Bur. Stand. 46 (1951) 318.

  14. 14.

    Yu. s. Leonov,Doklady Akad. Nauk. S.S.S.R. 114 (1957) 976. See alsoSoviet Physiks “Doklady” 2 (1957) 261.

  15. 15.

    Idem, Zhur. neorg. Khim. 3 (1958) 1245.

  16. 16.

    J. B. Nelson andD. P. Riley,Proc. Phys. Soc. Lond. 57 (1945) 160.

  17. 17.

    E. Wait,Technol. Report AERE-R3598 (1961).

  18. 18.

    L. H. Van Vlack, “physical Ceramics for Engineers” (Addison-Wesley Publishing Co. Inc., Reading, Massachusetts, 1964) 52.

  19. 19.

    Idem, ibid, 302.

Download references

Author information

Rights and permissions

Reprints and Permissions

About this article

Cite this article

Whitaker, A., Borton, D.F. Phase equilibria in the system CaO-ZnO-B2O3 at 850°C. J Mater Sci 7, 194–197 (1972). https://doi.org/10.1007/BF00554181

Download citation

Keywords

  • Oxide
  • Polymer
  • Calcium
  • Zinc
  • Solid Solution