Mechanical properties of a zircon matrix composite reinforced with silicon carbide whiskers and filaments

  • R. N. Singh
Papers

Abstract

The influence of a silicon carbide whisker reinforcement on room temperature mechanical properties of a monolithic zircon ceramic and zircon composites uniaxially reinforced with silicon carbide monofilaments was studied in a flexure mode. The strength of a monolithic zircon was increased by the addition of whisker reinforcement, but the composite failure was still brittle in nature. In contrast, zircon composites reinforced with SiC whiskers and filaments showed toughened composite-like behaviour and produced higher first matrix cracking strength and toughness than the composites reinforced with only SiC filaments. In addition, the whisker reinforcement had insignificant influence on the ultimate strength of filament-reinforced composites. These results were related to changes in measured fibre-matrix interfacial properties, which indicated that composites with high first matrix cracking strength and toughness can be designed and fabricated via independently tailoring the matrix and the fibre-matrix interfacial properties.

Keywords

Polymer Mechanical Property Zircon Carbide Brittle 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    R. N. Singh and A. R. Gaddipati, J. Mater. Sci. in press.Google Scholar
  2. 2.
    R. N. Singh, ibid. in press.Google Scholar
  3. 3.
    Idem., J. Amer. Ceram. Soc. 73 (1990) 2399.Google Scholar
  4. 4.
    U.S. Patent No. 4 340 636 (1982).Google Scholar
  5. 5.
    M. Sutcu, J. Mater. Sci. 23 (1988) 928.Google Scholar
  6. 6.
    B. Budianski, J. W. Hutchinson and A. G. Evans, J. Mech. Phys. Solids 34 (1986) 167.Google Scholar
  7. 7.
    R. N. Singh, Mater. Res. Soc. Symp. Proc. 120 (1988) 259.Google Scholar
  8. 8.
    M. K. Brun and R. N. Singh, Adv. Ceram. Mater. 3 (1988) 506.Google Scholar
  9. 9.
    Idem., J. Amer. Ceram. Soc. 73 (1990) 2930.Google Scholar
  10. 10.
    C. E. Curtis and H. G. Sowman, ibid. 36 (1953) 190.Google Scholar
  11. 11.
    M. Sutcu, Acta Metall. 37 (1989) 65.Google Scholar
  12. 12.
    R. N. Singh, “Influence of Thermophysical Properties on Fibre-Matrix Interfacial Shear Stress in Zircon-Silicon Carbide Composites”, in preparation.Google Scholar
  13. 13.
    Idem., J. Amer. Ceram. Soc. 72 (1989) 1764.Google Scholar
  14. 14.
    J. Aveston, G. A. Cooper and A. Kelly, in “Properties of Fibre Composites”, Conference Proceedings of the National Physical Laboratory (IPC Science and Technology Press Ltd, Surrey, UK, 1971) pp. 15–26.Google Scholar
  15. 15.
    R. N. Singh and M. Sutcu, J. Mater. Sci. in press.Google Scholar

Copyright information

© Chapman and Hall Ltd 1991

Authors and Affiliations

  • R. N. Singh
    • 1
  1. 1.GE Corporate Research and DevelopmentSchenectadyUSA

Personalised recommendations