Transformation-induced plasticity in two-phase (α+γ) Fe-Cr-Ni alloys

  • K. Wakasa
  • T. Nakamura
Papers
Received:
Accepted:

Abstract

The relationship between the fracture elongation and the value of α′ martensite per unit tensile strain has been studied for the two-phase (α + γ) Fe-Cr-Ni alloys containing 10%, 35% and 52% 7. The elongation has a peak in the elongation-test temperature curve. The peak elongation is dependent upon both the delay of necking and a suitable value of α′ martensite per unit tensile strain.

Keywords

Polymer Martensite Tensile Strain Temperature Curve Fracture Elongation 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    K. Mathieu, Arch. Eisenhüttenw. 6 (1942) 215.Google Scholar
  2. 2.
    V. F. Zackay, E. R. Parker, D. Fahr and R. Busch, Trans. ASM. 60 (1967) 252.Google Scholar
  3. 3.
    J. P. Bressanelli and A. Moskowitz, ibid 59 (1966) 223.Google Scholar
  4. 4.
    I. Tamura, T., Maki and H. Hato, J. Japan Inst. Met. 33 (1969) 1376.Google Scholar
  5. 5.
    G. R. Chanani, V. F. Zackay and E. R. Parker, Met. Trans. 2 (1971) 133.Google Scholar
  6. 6.
    A. Rosen, R. Jago and T. Kjer, J. Mater. Sci. 7 (1972) 870.Google Scholar
  7. 7.
    P. C. Maxwell, A. Goldberg and J. C. Shyne, Met Trans. 5 (1974) 1319.Google Scholar
  8. 8.
    T. Maki, H. Onodera, and I. Tamura, Preprint Jap. Inst. Met. Symp. (1974) p. 121.Google Scholar
  9. 9.
    T. Nakamura and K. Wakasa, Scripta Met. 9 (1975) 959.Google Scholar
  10. 10.
    Y. Tomoda and I. Tamura, Preprint Jap. Inst. Met. Symp. (1973) p. 159.Google Scholar
  11. 11.
    J. E. Dorn and S. Rajnak, Trans. Met. Soc. AIME 230 (1964) 1052.Google Scholar
  12. 12.
    H. M. Otte, Acta Met. 5 (1957) 614.Google Scholar
  13. 13.
    B. Cina, ibid 6 (1958) 748.Google Scholar
  14. 14.
    J. Dash and H. M. Otte, ibid 11 (1963) 1169.Google Scholar
  15. 15.
    R. P. Reed, ibid 10 (1962) 865.Google Scholar
  16. 16.
    R. Lagneborg, ibid 12 (1964) 823.Google Scholar
  17. 17.
    J. M. Marder and A. R. Marder, Trans. ASM. 62 (1969) 1.Google Scholar
  18. 18.
    J. M. Chilton, C. J. Barton and G. R. Speich, JISI 209 (1970) 184.Google Scholar
  19. 19.
    C. A. Apple, R. N. Caron and G. Krauss, Met. Trans. 5 (1974) 593.Google Scholar
  20. 20.
    K. Wakasa and T. Nakamura, Scripta Met. 10 (1976) 129.Google Scholar

Copyright information

© Chapman and Hall Ltd. 1977

Authors and Affiliations

  • K. Wakasa
    • 1
  • T. Nakamura
    • 1
  1. 1.Department of Metallurgical EngineeringTokyo Institute of TechnologyTokyoJapan

Personalised recommendations