, Volume 29, Issue 24, pp 6413–6419 | Cite as

Size effects due to Cosserat elasticity and surface damage in closed-cell polymethacrylimide foam

  • W. B. Anderson
  • R. S. Lakes
Papers

Abstract

This article describes the experimental investigation of Cosserat (or micropolar) elasticity and surface damage effects in closed-cell polymethacrylimide foams of different densities. The method of size effects was used to find the degree of Cosserat behaviour for both cylindrical and square cross-section specimens in bending and torsion. The foams were found to behave as Cosserat materials in which slender specimens appear less stiff than thick ones, provided sufficient care is taken when machining the specimens. Surface damage caused by the machining process may cause the apparent stiffness to decrease with decreasing specimen size, giving an opposite softening size effect.

Keywords

Polymer Foam Experimental Investigation Material Processing Machine Process 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    J. Awerbuch and S. Madhukar, J. Reinf. Plast. Compos. 4 (1985) 3.Google Scholar
  2. 2.
    E. Cosserat and F. Cosserat, “Theorie des corps deformables” (Hermann et Fils, Paris, 1909).Google Scholar
  3. 3.
    R. D. Mindlin, Int. J. Solids Struct. 1 (1965) 265.Google Scholar
  4. 4.
    A. C. Eringen, in “Fracture” Vol. 1, edited by H. Liebowitz (Academic, New York, 1968) p. 621.Google Scholar
  5. 5.
    R. D. Gauthier and W. E. Jahsman, J. Appl. Mech. 42 (1975) 369.Google Scholar
  6. 6.
    P. N. Kaloni and T. Ariman, J. Appl. Math., Phys. (ZAMP) 18 (1967) 136.Google Scholar
  7. 7.
    R. S. Lakes, Int. J. Solids Struct. 22 (1986) 55.Google Scholar
  8. 8.
    Idem R. S. Lakes, J. Mater. Sci. 18 (1983) 2572.Google Scholar
  9. 9.
    Idem R. S. Lakes, J. Eng. Mater. Tech. 113 (1991) 148.Google Scholar
  10. 10.
    E. Kröner, Int. J. Solids Struct. 3 (1967) 731.Google Scholar
  11. 11.
    A. C. Eringen, Int. J. Engng Sci. 10 (1972) 425.Google Scholar
  12. 12.
    R. S. Lakes, Boeing Technical Report (Boeing Commercial Airplanes, Seattle, WA, 1993).Google Scholar
  13. 13.
    M. Hlavacek, Int. J. Solids Struct. 112 (1975) 199.Google Scholar
  14. 14.
    G. Adomeit, in Proceedings of IUTAM Symposium on Mechanics of Generalized Continua, Freudenstadt, Stuttgart, edited by E. Kroner (Springer, Berlin, 1967).Google Scholar
  15. 15.
    R. Brezny and D. J. Green, J. Mater. Sci. 25 (1990) 4571.Google Scholar
  16. 16.
    W. B. Anderson, C. P. Chen and R. S. Lakes, Cellular Polym. 13 (1994) 1.Google Scholar
  17. 17.
    G. V. Krishna-Reddy and N. K. Venkatasub-Ramanian, J. Appl. Mech. 45 (1978) 429.Google Scholar
  18. 18.
    H. C. Park and R. S. Lakes, Int. J. Solids. Struct. 23 (1987) 485.Google Scholar
  19. 19.
    R. F. Karlak, in Proceedings of Conference on Failure Modes in Composites, IV (Metallurgical Society of AIME, Chicago, 1977) p. 106.Google Scholar
  20. 20.
    J. M. Whitney and R. J. Nuismer, J. Compos. Mater. 8 (1974) 253.Google Scholar
  21. 21.
    I. M. Daniel, Exper. Mech. 18 (1978) 246.Google Scholar
  22. 22.
    R. E. Rowlands, I. M. Daniel and J. B. Whiteside, ibid. 13 (1973) 31.Google Scholar
  23. 23.
    H. C. Park and R. S. Lakes, J. Biomechan. 19 (1986) 385.Google Scholar
  24. 24.
    S. K. Maiti, M. F. Ashby and L. J. Gibson, Scripta Metall. 18 (1984) 213.Google Scholar
  25. 25.
    L. J. Gibson and M. F. Ashby, “Cellular Solids” (Pergamon, Oxford, UK, 1987) p. 157.Google Scholar
  26. 26.
    R. S. Lakes, Cellular Polym. 12 (1993) 17.Google Scholar

Copyright information

© Chapman & Hall 1994

Authors and Affiliations

  • W. B. Anderson
    • 1
  • R. S. Lakes
    • 1
    • 2
  1. 1.Department of Biomedical EngineeringThe University of IowaIowa CityUSA
  2. 2.Department of Mechanical Engineering and Center for Laser Science and EngineeringThe University of IowaIowa CityUSA

Personalised recommendations