A theory of crack nucleation in high strain fatigue

  • C. Laird
  • A. R. Krause
Article

Abstract

From previous observations of the surfaces of metals cycled in high strain fatigue, the mechanism of crack nucleation is considered a plastic instability phenomenon. A model for crack nucleation based on this conclusion is now developed quantitatively and a simple relationship between the number of cycles to nucleate a crack and the applied, plastic, strain range thus predicted. Since the model is valid for any material capable of plastic deformation, plasticine has been cycled in reversed bending to test its prediction. Cracks were observed to form in the plasticine by puckering of the surface at stress concentrations, in direct confirmation of the model. Moreover, the crack nucleation measurements on the plasticine and data on metals, taken from the literature, are considered to be in reasonable agreement with the prediction of the model.

Keywords

Fatigue Reasonable Agreement Strain Range Simple Relationship Crack Nucleation 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Résumé

A partir d'observations précédentes faites sur la surface des métaux soumis à la fatigue oligocyclique, on a déduit que le mécanisme de formation de la fissure relevait d'un phénomène d'instabilité plastique.

Sur la base de cette conclusion, on développe à présent quantitativement un modèle de formation de la fissure, ce qui permet de prédire use relation simple entte le sombre de cycles nécessaires pour amorcer une fissure et l'écart de déformation plastique appliquée par cycle.

Le modèle étant appliquable à tout materiau susceptible de déformation plastiques, on a soumis à flexion alternée de la plasticise afin d'en vérifier les prédictions.

On a observé que, pour ce matériau, les fissures prenaient naissance par un processus de plissement de la surface aux endroits de concentration de tension, ce qui confirme directement le modèle proposé. En outre, les mesures de formation des fissures dans la plasticise ont été comparées aux données existantes dans la littérature, et qui se refèrent aux métaux.

Cette comparaison prêche en faveur d'une concommitence raisonnable des observations expérimentales et des prédictions du modèle.

Zusammenfassung

Ausgelrend von früheren Experimenten an Metalloberflächen, die starken Ermüdungs-verformungen unterworfen wurden, wird die Art der Rissentstehung als ein plastisches Instabilitätsphänomen betrachtet. Ein darauf aufbauendes Modell für die Rissentstehung wird quantitativ entwickelt and eine einfache Beziehung zwischen der Anzahl der zur Rissentstehung führenden Ermüdungsvorgänge and dem angewandten Verformungsbereich angegeben. Da das Modell auf jedes plastisch verformbare Material anwendbar ist, wurde seine Gültigkeit an Plastilin getestet, das periodischen Biegungen unterworfen wurde. Es wurden Risse im Plastilin beobachtet, die sich, entsprechend dem Modell, durch Faltenbildung der Oberfläche bei Stellen erhöhter Spannung ausbildeten. Ausserdern lässt sich feststellen, dass sowohl die Messergebnisse über Rissentstehung an Plastilin als auch die, der Literatur entnommenen, Messergebnisse an Metallen in brauchbarer Übereinstimmung mit den Aussagen des Modells stehen.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    N. Thompson and N.J. Wadsworth, Advances in Physics, 1958, 7, pp. 72–169.Google Scholar
  2. 2.
    D.H. Avery and W.A. Bockofen, Fracture of Solids, Edited by D.C. Drucker and J J. Gilman, J. Wiley and Sons, New York 1963, pp. 339–382.Google Scholar
  3. 3.
    C. Laird, “Influence of Metallurgical Structure on the Mechanism of Fatigue Crack Propagation’, A.S.T.M. 69th Annual Meeting, Atlantic City 1966. To be published in A.S.T.M. S.T.P. 415, 1967.Google Scholar
  4. 4.
    PJ.E. Forsyth, ‘A Two Stage Process of Fatigue Crack Growth’, Proc. of the Crack Propagation Symposium, Cranfield, 1961.Google Scholar
  5. 5.
    C. Laird and G.C. Smith, Phil. Mag., 1963, 8, pp. 1945–1963.Google Scholar
  6. 6.
    C. Laird and G.C. Smith, Phil. Mag., 1962, 7, pp. 847–857.Google Scholar
  7. 7.
    D.S. Kemsley, J. Inst. Metals, 1956, 85, pp. 420–422.Google Scholar
  8. 8.
    J. Porter and J.C. Levy, J. Inst. Metals, 1960, 89, pp. 86–89.Google Scholar
  9. 9.
    C. Laird, Ph. D. Thesis, Cambridge University, 1962.Google Scholar
  10. 10.
    R.C. Boettner, C. Laird and A.J. McEvily, Jr., Trans. A.I.M.E., 1963, 233, pp. 379–387.Google Scholar
  11. 11.
    C. Laird and C.E. Feltner, Trans. A.I.M.E., In press.Google Scholar
  12. 12.
    L.F. Coffin, Trans. A.I.M.E., 1960, 82D, pp. 671–682.Google Scholar
  13. 13.
    F.A. McClintock, Fracture of Solids, Edited by D.C. Drucker and J.J. Gilman, J. Wiley and Sons, New York 1963, pp. 65–102.Google Scholar
  14. 14.
    A.J. McEvily, Ford Motor Co., private communication.Google Scholar
  15. 15.
    H.W. Liu,Am. Soc. Mech. Engr., 1962, Paper No. 62-2.Google Scholar
  16. 16.
    J. Holden, Acta Met., 1963, 11, pp. 691–701.Google Scholar
  17. 17.
    J.E. Pratt, Acta Met., 1967, 15, pp. 319–327.Google Scholar
  18. 18.
    C.E. Feltner and C. Laird, Acta Met., In Press.Google Scholar
  19. 19.
    L.F. Coffin and J. Tavernelli, Gen. Elec. Research Lab., 1958, Report No. 58-RL-2100.Google Scholar
  20. 20.
    S.S. Manson, N.A.C.A., Tech. Note, 1953, T.N. 2933.Google Scholar
  21. 21.
    L. Northcott and H.G. Baron, J. Iron and Steel Inst., 1956, 184, pp. 385–408.Google Scholar
  22. 22.
    L.U. de Sitter, Structural Geology, McGraw-Hill Book Co., New York, 1956.Google Scholar
  23. 23.
    PJ.E. Forsyth and D.A. Ryder, Metallurgia, 1961, 63, pp. 117–124.Google Scholar
  24. 24.
    J. Weertman, Proc. of Intl. Conf. on Fracture, Sendai, Sept. 1965.Google Scholar

Copyright information

© Wolters-Noordhoff Publishing 1968

Authors and Affiliations

  • C. Laird
    • 1
  • A. R. Krause
    • 1
  1. 1.Scientific LaboratoryFord Motor CompanyDearborn

Personalised recommendations