Crack propagation in linear viscoelastic solids: some new results

  • L. N. McCartney
Article

Abstract

An extension of a theory of linear viscoelastic fracture is derived which removes a former restriction that Poisson's ratio is a constant. The new formulation thus includes both material property characteristics, i.e. the bulk (dilatation) and shear (distortion) linear viscoelastic compliances. Characteristic crack growth laws, assuming a Dugdale region ahead of the crack, are developed for creep laws which depend linearly upon time but are thought to be representative of more general materials. Examples include a single crack, a linear array of cracks, and a specialized cyclic load application.

Keywords

Material Property Civil Engineer Load Application Cyclic Load Property Characteristic 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Résumé

Une extension de la théorie de la rupture viscoélastique est déduite; cette extension se dégage de la restriction antérieure suivant laquelle le rapport de Poisson est une constante. La nouvelle formulation comporte donc deux caractéristiques des propriétés des matériaux, à savoir les compliances viscoélastiques linéaires d'ensemble (dilatation) et de cisaillement (distorsion). Les lois de croissance caractéristiques de la fissure supposant une région de Dugdale en amont de celle-ci sont développées pour des lois de fluage dépendant linéairement du temps; on pense cependant qu'elles sont représentatives de matériaux plus généraux. Des exemples comportant une fissure simple, une série simple de fissures alignées et une application spécifique de sollicitations cycliques sont fournies.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    L.N. McCartney, International Journal of Fracture, 13 (1977) 641.Google Scholar
  2. [2]
    D.S. Dugdale, Journal of Mechanics and Physics of Solids, 8 (1960) 100.Google Scholar
  3. [3]
    B.A. Bilby, A.H. Cottrell, E. Smith and K.H. Swinden, Proceedings of the Royal Society, London A279 (1964) 1.Google Scholar
  4. [4]
    L.N. McCartney, International Journal of Fracture, 12 (1976) 273.Google Scholar

Copyright information

© Sijthoff & Noordhoff International Publishers 1978

Authors and Affiliations

  • L. N. McCartney
    • 1
  1. 1.Division of Materials ApplicationsNational Physical LaboratoryTeddingtonU.K.

Personalised recommendations