Abstract
The influence of treating the melts by electromagnetic acoustic fields on the structure and properties of Al–12% Si and Al–20% Si binary alloys is investigated. In the course of experiments, the frequency of the electromagnetic field induced in the loop antenna varies as 500, 1000, and 2000 kHz. The melts are treated after their degassing and refining. It is established that this treatment method of the melts leads to a reduction of the total preparation time of alloy by 12% on average. The short-term treatment of the melts by electromagnetic acoustic fields promotes the refinement of the main phase components of alloys and an increase in their mechanical properties. When treating the Al–12% Si eutectic alloy with a frequency of 500 kHz, α-Al dendrites are refined from 30 to 22 μm and eutectic Si crystals are refined from 13 to 10 μm. When treating the Al–20%Si eutectic alloy with a frequency of 1000 kHz, eutectic Si crystals diminished from 8 to 5 μm and these of primary Si diminished from 90 to 62 μm. The ultimate tensile strength of the Al–12%Si eutectic alloy increases 13% under the mentioned treatment modes, while the relative elongation increases 17%; as for the Al–20% Si eutectic alloy, the same characteristics increases 9 and 65%, respectively. Based on these investigations, it is concluded that the selection of the treatment parameters of the melts of the Al–Si system by electromagnetic acoustic fields should be determined by the silicon content in the alloy. It is necessary to treat the melt by waves with a higher oscillation frequency with an increase in the silicon concentration. This treatment method makes it possible to form the modified fine-crystalline structure of alloy and, consequently, improves their mechanical properties. It can be successfully used when fabricating fine-crystalline foundry alloys and in the production of alloys of the Al–Si system. To determine the optimal treatment parameters depending on the structure of the initial charge and alloy nature, additional investigations are required.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Nappi, C., The Global Aluminium Industry 40 Years from 1972, World Aluminium, 2013, pp. 1–27.
Brodova, I.G., Popel, P.S., and Eskin, G.I., Liquid Metal Processing: Application to Aluminium Alloy Production, New York–London: Gordon&Breach, 2004.
Deev, V.B., Poluchenie germetichnikh alyminievikh splavov iz vtorichnykh materialov (Fabrication of Sealed Aluminum Alloys from Recycled Materials), Moscow: Flinta–Nayka, 2006.
Wang, J., He, S., Sun, B., Zhou, Y., Guo, Q., and Nishio, M., A356 alloy refined by melt thermal treatment, Int. J. Cast Met. Res., 2001, no. 14, pp. 165–168.
Gu, Z.H., Wang, H.Y., Zheng, N., Zha, M., Jiang, L.L., Wang, W., and Jiang, Q.C., Effect of melt superheating treatment on the cast microstructure of Mg-1.5Si-1Zn alloy, J. Mater. Sci., 2008, vol. 43, no. 3, pp. 980–984.
Liu, Z., Liu, X.M., and Xie, M., Microstructure and properties of in situ Al–Si–Mg2Si composite prepared by melt superheating, Appl. Mech. Mater., 2011, vols. 52–54, pp. 750–754.
Li, Q.L., Xia, T.D., Lan, Y.F., and Li, P.F., Effects of melt superheat treatment on microstructure and wear behaviours of hypereutectic Al-20Si alloy, Mater. Sci. Technol., 2014, vol. 30, no. 7, pp. 835–841.
Eskin, G.I., The influence of cavitation treatment of the melt on the structure and properties of cast and deformed light alloys, Vestn. Ross. Akad. Estestv. Nauk, 2010, no. 3, pp. 82–89.
Han, Y., Li, K., Wang, J., and Sun, B., Influence of high-intensity ultrasound on grain refining performance of Al–5Ti–1B master alloy on aluminium, Mater. Sci. Eng. A, 2005, vol. 405, pp. 306–312.
Jian, X., Xu, H., Meek, T.T., and Han, Q., Effect of power ultrasound on solidification of aluminium A356 alloy, Mater. Lett., 2005, no. 59, pp. 190–193.
Bhojak, K., Mavani, A., and Bhatt, N., Ultrasonic treatment to molten FEM©TM aluminum alloy and effects of ultrasound treatment melt temperature on hardness, Int. J. Res. Adv. Eng., 2013, vol. 1, no. 3, pp. 1–12.
Glushchenkov, V.A., Chernikov, D.G., Nikitin, V.I., and Nikitin, K.V., The effects of pulsed magnetic fields on the melt, Metall. Mashinostr., 2012, no. 4, pp. 47–50.
Belkin, V.S., Bukharin, V.A., and Dubrovin, V.K., Nanosekundnye elektromagnitnye impul’sy i ikh primenenie (Nanosecond Electromagnetic Pulses and Their Application), Chelyabinsk: Tatiana Lurie, 2001.
Ri, E.Kh., Ri, Hosen., Dorofeev, S.V., and Yakimov, V.I., Vliyanie oblucheniya zhidkoi fazy nanosekundnymi elektromagnitnymi impul’sami na ee stroenie, protsessy kristallizatsii, strukturoobrazovaniya i svoistva liteinykh splavov (Effect of the Irradiation of the Liquid Phase by Nanosecond Electromagnetic Pulses on Its Structure, Crystallization, Structure and Properties of Casting Alloys), Vladivostok: Dal’nauka, 2008.
Zarembo, V.I. and Kolesnikov, A.A., Background resonant acoustic control of heterophase processes, Theor. Found. Chem. Technol., 2006, vol. 49, no. 5, pp. 483–495.
Nikitin, V.I., Nikitin, K.V., and Timoshkin, I.Yu., RF Patent 2448180, 2011.
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © I.Yu. Timoshkin, K.V. Nikitin, V.I. Nikitin, V.B. Deev, 2016, published in Izvestiya Vysshikh Uchebnykh Zavedenii, Tsvetnaya Metallurgiya, 2016, No. 3, pp. 28–33.
About this article
Cite this article
Timoshkin, I.Y., Nikitin, K.V., Nikitin, V.I. et al. Influence of treatment of melts by electromagnetic acoustic fields on the structure and properties of alloys of the Al–Si system. Russ. J. Non-ferrous Metals 57, 419–423 (2016). https://doi.org/10.3103/S1067821216050163
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.3103/S1067821216050163