Abstract
The synthesis of diamond was performed at a pressure of 8 GPa and a temperature of 1700°C in the Mg–Zn–C system and, after the product was chemically purified, the resulting diamond powder was classified by grain sizes. The effect produced by the ratio between coarse and fine diamond powder fractions and the sintering parameters on the structure and physicomechanical properties of sintered diamond polycrystals was studied. The wear resistance of synthesized samples was investigated when turning a cylindrical X drillability granite core sample from the Korostyshiv deposit. The high-pressure sintering of a mixture of synthesized coarsely and finely dispersed diamond powders was shown to provide a 2.46-fold decrease in the residual porosity as compared to sintering under the same pressure for the diamond powders synthesized in the systems based on iron group metals. Among the resulting polycrystalline samples, the highest hardness determined at a Knoop indenter load of 9.8 N was 66 GPa to attain 87% from the hardness of natural type Ia diamond single crystal (face (100)). Polycrystalline diamond elements sintered in a Toroid 30 high-pressure autoclave at a pressure of 8 GPa and a temperature of 1780°C from the purified product of synthesis in the Mg–Zn–C system with a diameter of 15 mm and a height of 3 mm demonstrated the highest wear resistance, which was 5.6–10.9 times higher than for the reference specimen sintered from the powder synthesized in the Ni–Mn–C system.
REFERENCES
Kocherzhinskii, Yu.A., Shul’zhenko, A.A., Shishkin, V.A. Belyankina, A.V., and Tovstogan, V.M., Substructure and properties of polycrystalline diamonds depending on the thermodynamic parameters of sintering, in Vliyanie vysokogo davleniya na strukturu i svoistva materialov (Effect of High Pressure on the Structure and Properties of Materials), Kyiv: Inst. Sverkhtverd. Mater. Akad. Nauk USSR, 1983, pp. 34–40.
Shul’zhenko, A.A. and Gargin, V.G., Properties and structure of diamond polycrystals obtained at different sintering temperatures, Sverkhtverd. Mater., 1984, no. 2, pp. 26–30.
Fedoseev, D.V., Sokolina, G.A., and Yakovlev, E.N., Plastic deformation of diamond powders at high pressure, Dokl. Akad. Nauk SSSR, 1985, vol. 282, no. 3, pp. 601–604.
Britun, V.F., Oleynik, G.S., and Semenenko, N.P., Deformation process during high-pressure sintering of the diamond powders produced by catalyc synthesis, J. Mater. Sci., 1992, vol. 27, no. 16, pp. 4472–4476.
Mackenzie, J.K. and Shuttleworth, R., A phenomenological theory of sintering, Proc. Phys. Soc. B, 1949, vol. 62, no. 12, pp. 833–852.
Bochechka, A.A., Formation of polycrystals from diamond micropowders under high pressure and temperature conditions, Sverkhtverd. Mater., 1999, no. 6, pp. 18–25.
Gargin, V.G., Effect of heating conditions on the strength of synthetic diamonds, Sverkhtverd. Mater., 1981, no. 4, pp. 9–11.
Sverkhtverdye materialy. Poluchenie i primenenie (Superhard Materials: Synthesis and Use), 6 vols, vol. 1: Sintez almaza i podobnykh materialov (Synthesis of Diamond and Similar Materials), Shul’zhenko, A.A., Ed., Kyiv: Inst. Sverkhtverd. Mater. im. V.N. Bakulya, 2003.
Bakul’, V.N., Shul’zhenko, A.A., and Get’man, A.F., UK Patent 1377104, 1975.
Chernienko, A.I. and Bochechka, A.A., Thermal stability and level of residual stresses in diamond grains synthesized in the Mg–Zn–B–C system, Tez. 3-i mezhdunar. Samsonovskoi konf. “Materialovedenie tugoplavkikh soedinenii” (Proceedings of 3rd International Samsonov Conference “Materials Science of Refractory Compounds”), Kyiv, 2012, p. 99.
Novikov, N.V., Fedoseev, D.V., Shul’zhenko, A.A., and Bogatyreva, G.P., Sintez almazov (Synthesis of Diamonds), Kyiv: Naukova Dumka, 1987.
Kruk, V.B., Vazhnev, V.P., and Lepikhova, T.G., Purification of synthetic diamonds from impurities, Sint. Almazy, 1974, vol. 2, pp. 11–13.
Nikitin, Yu.I., Tekhnologiya izgotovleniya i kontrol’ kachestva almaznykh poroshkov (Production Technology and Quality Control of Diamond Powders), Kyiv: Naukova Dumka, 1984.
Petasyuk, G.A., System-criterion method of quantitative assessment of the homogeneity of superhard dispersed materials, Fiz.-Khim. Mekh. Mater., 2003, no. 5, pp. 101–105.
Petasyuk, G.A., Extrapolation geometric method for measuring the external specific surface area of powders of superhard materials, Izmer. Tekh., 2008, no. 1, pp. 59–64.
Safonova, M.N., Petasyuk, G.A., and Syromyatnikova, A.S., Komp’yuterno-analiticheskie metody diagnostiki ekspluatatsionnykh kharakteristik almaznykh poroshkov i kompozitsionnykh materialov na ikh osnove (Computer-Analytical Methods for Diagnosing the Performance Characteristics of Diamond Powders and Composite Materials Based on Them), Novosibirsk: Sib. Ord. Ross. Akad. Nauk, 2013.
Shul’zhenko, A.A., Gargin, V.G., Shishkin, V.A., and Bochechka, A.A., Polikristallicheskie materialy na osnove almaza (Diamond-Based Polycrystalline Materials), Novikov, N.V., Ed., Kyiv: Naukova Dumka, 1989.
Kivilis, S.S., Plotnomery (Density Meters), Moscow: Energiya, 1980.
Bochechka, O.O., Isonkin, O.M., Chernienko, O.I., Kushch, O.V., and Sokolyuk, D.V., Wear resistance of polycrystals and “diamond–tungsten carbide” composite, sintered from diamond powders synthesized in the Mg–Zn–C system, during granite core turning, Instrum. Materialozn., 2021, no. 24, pp. 265–270.
Cherniyenko, O.I., Bochechka, O.O., Tkach, V.M., Bilyavina, N.M., Petasyuk, G.A., Romanko, L.O., Gavrilova, V.S., and Filatov, Yu.D., Special features of the diamond crystallization in the Mg–Zn–B–C system, J. Superhard Mater., 2015, vol. 37, no. 6, рр. 18–33. https://doi.org/10.3103/S1063457615060027
Ignat’eva, I.Yu., Barabash, O.M., and Legkaya, T.N., Study of the evolution of the phase diagram of the Mg–C system depending on pressure based on thermodynamic calculations, Sverkhtverd. Mater., 1990, no. 5, pp. 3–7.
Bochechka, O.O., Petasyuk, G.A., Chernienko, O.I., Kushch, O.V., Gavrilova, V.S., Gnatenko, I.O., and Garashchenko, V.V., The influence of the composition and properties of diamond powders synthesized in the Mg–Zn–C system on the formation of polycrystals from them during high-pressure sintering, Instrum. Materialozn., 2021, no. 24, pp. 237–249.
Bochechka, A.A., The analysis of the motive forces of sintering micro- and nanosized diamond powders at high pressure, J. Superhard Mater., 2009, vol. 31, no. 5, pp. 292–299.
Geguzin, Ya.E., Fizika spekaniya (Physics of Sintering), Moscow: Nauka, 1984, 2nd ed.
Bochechka, A.A. and Gargin, V.G., Estimation of changes in pressure during sintering of diamond-carbide plates in a high-pressure apparatus of the “toroid” type, Sverkhtverd. Mater., 1998, no. 3, pp. 31–39.
Bochechka, O.O., Fiziko-khimichni osnovi spikannya almaznikh poroshkiv pid dieyu visokogo tisku ta visokoi temperature (Physico-Chemical Basis of Sintering of Diamond Powders under the Action of High Pressure and High Temperature), Kyiv: Naukova Dumka, 2019.
Bochechka, A.A., Romanko, L.A., Gavrilova, V.S., Konoval, S.M., and Nazarchuk, S.N., Special features of sintering diamond powders of various dispersions at high pressures, J. Superhard Mater., 2007, vol. 29, no. 1, pp. 17–23.
Bochechka, O.O., Isonkin, O.M., Osipov, O.S., Chernienko, O.I., Gavrilova, V.S., Gnatenko, I.O., Mel’iichuk, Yu.O., and Kushch, O.V., Wear resistance of diamond polycrystalline elements sintered at a pressure of 8 GPa from diamond powder synthesized in the Mg–Zn–C system, in Instrumental’ne materialoznavstvo (Instrumental Materials Science), Kyiv: Inst. Sverkhtverd. Mater. im. V.N. Bakulya Nats. Akad. Nauk Ukr., 2022, vol. 25, pp. 232–238.
ACKNOWLEDGMENTS
The authors are sincerely grateful to Yu.A. Melniychuk, PhD in Engineering, for the mechanical treatment of diamond polycrystalline elements.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
The authors declare that they have no conflicts of interest.
Additional information
Translated by E. Glushachenkova
About this article
Cite this article
Bochechka, O.O., Kushch, O.V., Isonkin, O.M. et al. Effect of the Granular Composition of Diamond Powder Synthesized in the Mg–Zn–C System on the Structure, Physicomechanical Properties, and Performance Characteristics of Crystals Sintered from It under High Pressure. J. Superhard Mater. 45, 336–347 (2023). https://doi.org/10.3103/S1063457623050027
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.3103/S1063457623050027