Tribological behavior of a steel transformation induced by plasticity (TRIP) subjected to adhesive wear

  • Original Paper
  • Published:
MRS Advances Aims and scope Submit manuscript

Abstract

The experimental study of the resistance to adhesive wear of low-alloy steel through friction tests is presented. The steel was manufactured in an induction furnace from AISI-1018 steel with additions of FeMn and FeSi. Subsequently, it was hot rolled and heat treated to obtain the microstructure of a Transformation-induced Plasticity (TRIP) steel with σu = 890 MPa, S = 30.75%, and hardness of 22 HRC. Friction tests were carried out according to the ASTM G-77 standard with three different loads (52.6, 103.5, and 154.4 N), and the friction coefficients and wear mechanisms were determined. The results show that, by increasing the load, the coefficient of friction decreases by 47%, this reduction could be associated with a martensitic transformation induced by plasticity on the surface. The wear mechanisms observed for the three loads were adhesion with accumulated and oxidative material flow and the fatigue mechanism only occurred for the 154-N load.

Graphical abstract

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3

Similar content being viewed by others

Data availability

The data that support the findings of this study are available from the corresponding author upon request. In addition, some data are provided as supplementary material.

References

  1. R. Rana, S.B. Singh, Automotive steels: design, metallurgy, processing and applications (Woodhead Publishing, Sawston, 2016)

    Google Scholar 

  2. Worldautosteel.org (2016) Advanced high-strength steels application guidelines, http://www.worldautosteel.org/download_files/AHSS%20Guidelines%20V6/00_AHSSGuidelines_V6_20170430.pdf. Accessed 17 Jul 2023

  3. V.F. Zackay, E.R. Parker, D. Fahr, R. Busch, ASM Trans Quart 60, 2 (1967)

    Google Scholar 

  4. N. Fonstein, Advanced high strength sheet steels, 1st edn. (Springer International Publishing, New York, NY, USA, 2015), pp.191–200

    Book  Google Scholar 

  5. M. Sabzi, M. Farzam, Mater. Res. Express (2019). https://doi.org/10.1088/2053-1591/ab3ee3

    Article  Google Scholar 

  6. S. Bhattacharyya, Wear (1966). https://doi.org/10.1016/0043-1648(66)90136-0

    Article  Google Scholar 

  7. Z. Tourki, H. Bargui, H. Sidhom, J. Mater. Process. Technol. (2005). https://doi.org/10.1016/j.jmatprotec.2003.08.010

    Article  Google Scholar 

  8. E. Van der Heide, D.J. Schipper, Wear (2003). https://doi.org/10.1016/S0043-1648(03)00324-7

    Article  Google Scholar 

  9. J.Y. Choi, W. Jin, Scr. Mater. (1997). https://doi.org/10.1016/S1359-6462(96)00338-7

    Article  Google Scholar 

  10. J.P. Riviere, C. Brin, J.P. Villain, Appl. Phys. A: Mater. Sci. Process. (2003). https://doi.org/10.1007/s00339-002-1481-x

    Article  Google Scholar 

  11. W. Hübner, Tribol. Int. (2001). https://doi.org/10.1016/S0301-679X(01)00006-8

    Article  Google Scholar 

  12. W. Hübner, A. Pyzalla, K. Aßmus, E. Wild, T. Wroblewski, Wear (2003). https://doi.org/10.1016/S0043-1648(03)00164-9

    Article  Google Scholar 

  13. A. Soulami, K.S. Choi, Y.F. Shen, W. Liu, X. Sun, M.A. Khaleel, Mater Sci Eng A (2011). https://doi.org/10.1016/j.msea.2010.10.031

    Article  Google Scholar 

  14. O. Acselrad, A. Ribeiro de Souza, I.S. Kalashnikov, S.S. Camargo Jr., Wear (2004). https://doi.org/10.1016/j.wear.2004.07.004

    Article  Google Scholar 

  15. D. Bu, H. Peng, Y. Wen, N. Li, Mater. Des. (2011). https://doi.org/10.1016/j.matdes.2011.01.032

    Article  Google Scholar 

  16. Standard ASTM E18-15, Standard test methods for rockwell hardness of metallic materials (2015). https://www.astm.org/e0018-15.html. Accessed 9 Jan 2023

  17. Standard ASTM E975-13, Standard practice for X-ray determination of retained austenite in steel with near random crystallographic orientation (2013). https://www.astm.org/e0975-13.html. Accessed 9 Jan 2023

  18. Standard ASTM G-77, Standard test method for ranking resistance of materials to sliding wear using block-on-ring wear test (2017). https://www.astm.org/g0077-17.html. Accessed 9 Jan 2023

  19. P. Jacques, Phase transformations in transformation induced plasticity (TRIP)-assisted multiphase steels, in Phase Transformations in Steels. ed. by E. Pereloma, D. Edmonds (Woodhead Publishing, Portsmouth, 2012), p.680

    Google Scholar 

  20. D. Dowson, History of tribology (Professional Engineering Publ, London, 1998)

    Google Scholar 

  21. L. Ceschini, C. Martini, A. Morri, Tribol. Int. (2015). https://doi.org/10.1016/j.triboint.2015.07.032

    Article  Google Scholar 

  22. I. Mejía, A. Bedolla-Jacuinde, J.R. Pablo, Wear (2013). https://doi.org/10.1016/j.wear.2013.01.054

    Article  Google Scholar 

  23. S. Katoch, R. Sehgal, V. Singh, Tribol. Mater. Surf. Interfaces (2016). https://doi.org/10.1080/17515831.2016.1263030

    Article  Google Scholar 

  24. Z.Y. Yang, M.G.S. Naylor, D.A. Rigney, Wear (1985). https://doi.org/10.1016/0043-1648(85)90007-9

    Article  Google Scholar 

  25. I.A. Inman, P.K. Datta, H.L. Du, J.S. Burnell-Gray, S. Pierzgalski, Tribol. Int. (2005). https://doi.org/10.1016/j.triboint.2005.02.007

    Article  Google Scholar 

  26. I.I. Garbar, Tribol. Int. (2002). https://doi.org/10.1016/S0301-679X(02)00032-4

    Article  Google Scholar 

  27. M. Wang, C. Zhang, D. Sun, Z. Yang, F. Zhang, Mater. Sci. Technol. (2019). https://doi.org/10.1080/02670836.2019.1613043

    Article  Google Scholar 

  28. Y.S. Lee, K. Ishikawa, M. Okayasu, Metals Mater. Int. (2019). https://doi.org/10.1007/s12540-018-00229-4

    Article  Google Scholar 

Download references

Acknowledgments

The authors thank the IIMM-UMSNH, TecNM-ITM, and the UASLP Institute of Metallurgy for the facilities granted to carry out this work, a special recognition to Eng. Jaime López Soria from TecNM-ITM for his support in the merger of the steel, as well as the M.C. Claudia Guadalupe Elías Alfaro from the Institute of Metallurgy of the UASLP for her support in the characterization of samples.

Funding

This research received no specific grant from any funding agency in the public, commercial, or not-for-profit sectors.

Author information

Authors and Affiliations

  1. Universidad Autónoma del Estado de Hidalgo, Escuela de Ingeniería Mecánica, Ciudad Sahagún, Hidalgo, México

    José-Sergio Pacheco-Cedeño

  2. División de Estudios de Posgrado e Investigación, TecNM, Instituto Tecnológico de Morelia, Morelia, Michoacán, México

    Pedro Garnica-González

  3. Instituto de Investigaciones Metalúrgicas y Materiales, Universidad Michoacana de San Nicolás Hidalgo, Morelia, Michoacán, México

    Francisco Vapeani Guerra-López

  4. Facultad de Ingeniería-Instituto de Metalurgia UASLP, Sierra Leona #550 Col. Lomas 2a Sección, San Luis Potosí, San Luis Potosí, México

    José de Jesús Cruz-Rivera

Authors
  1. José-Sergio Pacheco-Cedeño
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Pedro Garnica-González
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Francisco Vapeani Guerra-López
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. José de Jesús Cruz-Rivera
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

JSP-C conceived the experiments and wrote the article. PG-G performed the experiments. FVG-L contributed to the casting processes and analyzed the experimental results. JJC-R analyzed the data and performed microstructural characterization.

Corresponding author

Correspondence to José-Sergio Pacheco-Cedeño.

Ethics declarations

Conflict of interest

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

Ethical approval

Not applicable.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary Information

Below is the link to the electronic supplementary material.

Supplementary file1 (DOCX 858 KB)

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Pacheco-Cedeño, JS., Garnica-González, P., Guerra-López, F.V. et al. Tribological behavior of a steel transformation induced by plasticity (TRIP) subjected to adhesive wear. MRS Advances 8, 1161–1166 (2023). https://doi.org/10.1557/s43580-023-00690-3

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1557/s43580-023-00690-3

Search

Navigation