Abstract
It is known for Fe–Al–Ta alloys, that a homogeneous distribution of strengthening Laves phase precipitates in the matrix and aligned at the grain boundaries can be obtained when the formation of the stable Laves phase is preceded by the formation of the metastable Heusler phase. Several Fe–Al–Nb alloys with different Al and Nb contents and with or without boron doping are studied to elucidate whether comparable microstructures can be obtained in this system. It was found that the Heusler phase only occurs within a limited composition range. The time-dependent evolution of the microstructure shows that the transformation proceeds faster in Fe–Al–Nb alloys. Microhardness was measured in dependence on the microstructural evolution with increasing annealing time, and compressive yield stress was determined for alloys annealed 700 °C/1000 h to evaluate the influence of microstructure and composition.
Graphic Abstract
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Due to their outstanding wear and corrosion resistance, iron aluminides are considered for structural applications at high temperatures [1]. Because of their low density and good mechanical properties at moderate temperatures, they are particularly interesting for energy-saving components, specifically for moving parts such as turbine blades. However, high temperature mechanical properties, such as yield stress and creep resistance are still not sufficient for wider industrial application. Through different alloying concepts, e.g. strengthening coherent or incoherent second phases such as borides or Laves phase precipitates, the mechanical properties of iron aluminides can be further enhanced at higher temperatures [2, 3]. In many Fe–Al–X systems the Laves phase forms directly from the melt and solidifies as coarse dendrites [4, 5]. In this case, the distribution of the Laves phase cannot be controlled, and rather brittle alloys are obtained [5]. It has been shown recently, that a controlled homogeneous distribution of Laves phase can be achieved in Fe–Al–Ta alloys, where the formation of the stable hexagonal C14 Laves phase is kinetically retarded. Instead of the Laves phase, coherent precipitates of metastable L21 Heusler phase form when the Fe–Al matrix becomes supersaturated with Ta on cooling. The transformation from the metastable Heusler phase to the stable Laves phase can be controlled through the choice of heat treatment, thermomechanical processing or doping the alloy with boron. Thereby different microstructures with fine-scaled and homogeneously distributed Laves phase precipitates inside the Fe–Al matrix or at grain boundaries can be obtained [3]. Previous research shows that the Fe–Al–Nb system is the only other system, where the formation of the stable Laves phase is preceded by the formation of the metastable Heusler phase [6, 7]. The present research continues the work on the influence of boron on the microstructure and the mechanical properties in Fe–Al–Nb alloys [8]. It is part of a larger project, which aims at clarifying whether mechanisms, which enable a microstructural design—and thereby tailoring of mechanical properties—in Fe–Al–Ta alloys, can also be realized in case of Fe–Al–Nb. As the properties of the Fe–Al–Ta alloys are considered as attractive by industries, Fe–Al–Nb alloys with comparable properties would be a slightly more light-weight, but specifically more economically efficient, alternative.
Therefore, the composition range where the Heusler phase may form and the transformation kinetics from metastable Heusler phase to stable Laves phase are studied. Microstructures are characterized by metallography, crystallographic structures and compositions of the stable phases were determined. A preliminary evaluation of the resulting mechanical properties has been performed by microhardness and compression tests.
Experimental
Alloys of five different compositions, with Al contents between 25 and 34 at.% and 2–3 at.% Nb, partially doped with boron (< 100 ppm), were produced by vacuum induction melting from Fe (99.9 wt.%), Al (99.9 wt.%), Nb (99.9 wt.%) and B (99.4 wt.%) under argon and cast into copper molds of 20 mm diameter. Compositions were selected on the basis of the existing phase diagrams [9, 10] in a way that a sufficient supersaturation of the Fe–Al matrix is attained on cooling and that the alloys contain at least 5 vol.% of precipitates at 700 °C, which is a possible application temperature. Because boron doping facilitated the transformation from Heusler to Laves phase in Fe–Al–Ta alloys, three alloys were doped with boron. The actual alloy compositions were determined by wet chemical analysis. Heat treatments were performed at 700 °C for 1 h, 10 h, 100 h and 1000 h in order to evaluate the microstructural evolution and kinetics of the transformation from metastable L21 Heusler phase to the stable C14 Laves phase. Metallographic sections were prepared by grinding and polishing the alloys, the last step being polishing with a 0.5 µm-particles diamond suspension. Additional preparation with an oxide polishing suspension (OPS) for a few seconds was only used in some cases.
The microstructure of the alloys in the as-cast condition and after heat treatment was inspected by light optical and scanning electron microscopy (SEM: LEO 1550 VP, Zeiss). Phases were characterized by X-ray diffraction (XRD: Bruker D8 Advance A25) on metallographic sections by scanning the 2θ range from 20° to 125° using Co-Ka-radiation (λ = 0.1709 nm). The chemical compositions of the phases were established by wavelength-dispersive electron probe microanalysis (EPMA: Jeol JXA-8100).
For mechanical testing at higher temperatures cuboidal shaped samples with dimensions 10 × 5 × 5 mm3 were cut by electrical discharge machining (EDM), while for tests at room temperature and at 200 °C cylindrical samples of 10 mm height and 5 mm diameter were employed, which, in contrast to the rectangular samples, showed no shearing at these low temperatures. Compression tests were performed at a deformation rate of 10–4 s−1 between room temperature and 800 °C (ZwickRoell Z100). The microhardness was established by Vickers indents with 0.0098 N.
Results and discussion
Microstructural observations
Nominal and actual compositions of the alloys are shown in Table 1. Systematically lower amounts of Al and slightly higher amounts of B are observed. The lower amounts of Al may be explained by preferential evaporation of Al during the induction melting. The increased B contents reflect the difficulty of precisely adjusting such low alloying contents, though the actual deviation should not exceed the effect of doping the alloys. Compositions of phases as determined by EPMA after heat treatment of the alloys at 700 °C for 1000 h are also shown in Table 1. The crystallographic structures of the phases for all alloys after 700 °C/1000 h, as determined via XRD, are D03 for the Fe3Al matrix and C14 for the Laves phase. Though, at 700 °C the Fe–Al matrix is actually B2-ordered for all compositions, but it transforms to D03 during cooling to room temperature [6]. As an example the diffractogram of alloy Fe-24.4Al-2Nb-0.03B annealed 700 °C/1000 h is shown in Fig. 1. In the boron-doped alloys, no boride precipitates were observed by XRD, SEM or EMPA.
The microstructures of all alloys in the as-cast condition and after annealing for various times at 700 °C are shown in Figs. 2, 3, 4. The grains are globular with a grain size > 50 μm in the middle of the alloys, while at the edges elongated grains of about 150 µm length are observed. The latter started solidifying at the cold crucible wall. No larger pores were observed in any of the investigated alloys. For the alloys with about 32 and 34 at.% Al, the grain boundaries are almost completely covered by a second phase already in the as-cast condition (Fig. 2).
These particles have an elongated, needle- or plate-like shape and are about 3 μm long (see Fig. 4d). According to their composition determined by EPMA, these particles are the Laves phase. The Laves phase apparently solidified during cooling as Fe–Al + Laves phase eutectic, which is clearly discernible at higher magnification at triple points of the grain boundaries (Fig. 2a). In contrast to the more Al-rich alloys, Fe-24.4Al-2Nb-0.03B shows only very few precipitates at the grain boundaries (Fig. 2d).
Figure 3 shows the microstructures after heat treatment at 700 °C/1000 h. From previous investigations, it can be assumed that after this time the alloys are in equilibrium at 700 °C [9]. Compared to the as-cast state, there is little change in the microstructures of the alloys with about 32 and 34 at.% after this heat treatment. The Laves phase has coarsened at the grain boundaries and few new Laves phase precipitates have formed within the Fe–Al grains. In contrast, Fe–24.4Al–2Nb–0.03B shows a remarkable microstructural development. After 700 °C/1000 h it shows a microstructure with an evenly distribution of Laves phase particles in the matrix and at grain boundaries (Fig. 3c). In order to understand the differences in the microstructures after 700 °C/1000 h, the observations of the microstructural development with increasing annealing time is very helpful (Fig. 4). In the as-cast condition there are few Laves phase precipitates at the grain boundaries (Fig. 4a) and an indication of some kind of “structuring” is visible in the Fe–Al matrix. Already after 1 h annealing at 700 °C (Fig. 4b), the amount of Laves phase at the grain boundaries has markedly increased and the “structuring” in the Fe–Al matrix now has the typical appearance, known for the coherent precipitation of fine Heusler phase particles [3]. Moreover, there is a zone along the grain boundaries, where the Laves phase precipitates grew, without any Heusler phase precipitates. Such a precipitation free zone (PFZ) is typical for the formation of the stable Laves phase at the grain boundaries by dissolution of the neighboring metastable Heusler phase [3]. After 10 h no Heusler phase can be observed any longer in the micrographs (Fig. 4c). Instead, some small Laves phase precipitates are found within the Fe–Al grains. With prolonged annealing time (Fig. 4d, e), the amount of these small precipitates in the Fe–Al grains increases and the Laves phase precipitates at the grain boundaries grow together and form a continuous layer (Fig. 4e).
The microstructural evolution in Fe–24.4Al–2Nb–0.03B with increasing annealing time is paralleled by the change in the Nb content in the Fe–Al matrix (Fig. 5), as determined by EPMA. Because the Heusler phase precipitates shown in Fig. 4b are too fine-scaled to be resolved by EPMA, measurements of the Fe–Al matrix after 1 h annealing are actually for Fe–Al + Heusler phase. The data in Fig. 5 show a significant decrease of the Nb content after 100 h at 700 °C. This should indicate that after 10 h there is still a marked amount of Heusler phase present in the matrix, though it is not any longer visible in the micrograph (Fig. 4c). However, as the Heusler phase is so fine-scaled, only ongoing transmission electron microscopy (TEM) will be able to clarify this. Actually, the presence of coherent Heusler phase precipitates in Fe–25Al–2Nb after annealing for 8–10 h at 700 °C has been revealed by TEM before [6, 7]. After 1000 h the Nb content in the Fe–Al matrix has decreased to 0.4 at.% (Table 1), which is about the value that has been previously reported for the solubility in Fe-25Al [7] and which is expected in equilibrium [9]. Measurement of the composition of the Fe–Al matrix in the alloys with about 32 and 34 at.% Al shows that the Nb content does not decrease with prolonged annealing, revealing that in these alloys the Fe–Al matrix was not supersaturated with Nb at 700 °C. As supersaturation is a prerequisite for the formation of metastable Heusler phase [3, 6, 7] and thereby for the formation of evenly distributed fine-scaled Laves phase precipitates, it becomes clear why such a microstructure is only obtained in the case of Fe–24.4Al–2Nb–0.03B, but not for the alloys with higher Al contents.
The present results also give an indication up to which Al content the metastable Heusler phase may occur in Fe–Al alloys. Only at 24.4 at.% Al, the Heusler phase is observed while at 31 at.% Al and at higher Al contents it is not observed any longer. Previous studies demonstrated the occurrence of metastable Heusler phase in alloys in the range of 15–30 at.% Al [11], which is in line with the present results. At least for the alloys with about 32 and 34 at.% Al, doping with boron has no significant effect on the microstructure (Fig. 3. The current research continues the work on boron-doped Fe–Al–Nb alloys by Azmi et at.[8]. In that work, a microstructure with evenly distributed Laves phase within the matrix and at the grain boundaries was obtained in an alloy with 25.9 at.% Al, 2.5 at.% Nb and 0.07 at.% B after annealing at 700 °C for1000 h. The alloy has also been investigated in the as-cast condition and after 100 h annealing at 700 °C, but no evidence of the Heusler phase was found.
Figure 6 shows the time–temperature-transformation (TTT) diagram for the transformation of the metastable Heusler phase to the stable Laves phase [6, 7]. Additional data for Fe–24.4Al–2Nb–0.03B indicate that the transformation in the B-doped alloy proceeds faster at 700 °C than in the ternary alloys. However, as no data for ternary alloys with annealing times longer than 10 h exist, this point has to be clarified. Compared to Fe–Al–Ta alloys [3], the transformation (indicated by a dashed line in Fig. 6) occurs earlier at a given temperature for Fe–Al–Nb(–B) alloys.
Mechanical properties
Figure 7 shows the compressive yield stress σ0.2 for the Fe–Al–Nb(–B) alloys heat-treated 700 °C/1000 h in comparison with the boron-doped alloys from [8], a hot-rolled and “as-cast” alloy, both additionally annealed 1000 °C/50 h, with a similar composition [12], and an Fe–25Al–2Ta alloy [13]. For the Fe–Al–Nb(–B) alloys, no marked difference between individual alloys is noticed, showing that the B-doping has no effect on the yield strength. However, Fe–24.4Al–2Nb–0.03B seems to have the lowest strength at high temperatures. This indicates that the obtained microstructure is still not efficient for strengthening, possibly because the Laves phase precipitates are already too coarse (2.5 µm feret diameter) and distances between the particles are too large (about 6 µm) to act as barriers for dislocation motion. The observation that the alloys with higher Al contents are somewhat stronger at high temperatures, though their Laves phase precipitates are even coarser, may be attributed to the considerably higher Nb content in the Fe–Al matrix (Table 1), resulting in higher solid solution hardening. The yield stress at high temperatures of the boron-doped alloys with 1.5 at.% Nb (from [8]) with homogeneously distributed Laves phase precipitates in the matrix and at grain boundaries is similar to that of the present alloys. The as-cast alloy has a slightly higher yield stress, probably because of the higher amount of Nb in the matrix and, therefore a stronger solid solution hardening effect [8]. The rolled alloy with 25.8 at.% Al and 2.7 at.% Nb shows the highest yield stress at high temperatures due to homogeneously distributed Laves phase precipitates in addition to the higher Nb solubility in the matrix and therefore an increased solid solution hardening effect [12]. The Fe–25Al–2Ta alloy, shown for comparison, has been heat treated 1000 °C/200 h, resulting in a microstructure with Laves phase precipitates (2.4 µm diameter and 30 µm inter-particle spacing) inside the Fe–Al matrix and at the grain boundaries, which is comparable to the present ones [12]. The compressive yield stress is about the same as for the present alloys, though possibly a little bit higher at 800 °C.
The microhardness of the Fe–Al matrix in dependence on the aging time at 700 °C is shown in Fig. 8. For the alloy Fe–24.4Al–2Nb–0.03B, the microhardness is measured in the matrix containing Heusler phase precipitates after 1 h heat treatment and increasing fraction of Laves phase precipitates after 10 h heat treatment. In view of the large scatter of the data any detailed analysis seems speculative. Again, no significant influence of B on the microhardness was noted.
Conclusions
Microstructure analysis and phase characterization via EPMA and XRD indicate that in Fe–Al–Nb–B alloys the formation of fine-scaled, homogeneously distributed Laves phase is preceded by the formation of the metastable Heusler phase. The Heusler phase forms in the alloy with about 24 at.% Al and 2 at.% Nb and doped with boron after 1 h of heat treatment and transforms into the stable Laves phase upon longer annealing. The Heusler-to-Laves phase transformation occurs faster than in the Fe–Al–Ta system. No significant influence of boron on the microstructure and the mechanical properties could be observed. The yield stress of Fe–Al–Nb alloys is in the same order of magnitude as for an Fe–Al–Ta alloy of comparable composition and microstructure.
Data availability
The datasets generated during and/or analyzed during the current study are available from the corresponding author on reasonable request.
References
C.G. McKamey, Iron aluminides, in Physical Metallurgy and Processing of Intermetallic Compounds. ed. by N.S. Stoloff, V.K. Sikka (Chapman Hall, New York, 1996), pp. 351–391
M. Palm, F. Stein, G. Dehm, Iron aluminides. Annu. Rev. Mater. Res. 49, 297–326 (2019)
P. Prokopčáková, M. Švec, M. Palm, Microstructural evolution and creep of Fe-Al alloys. Int. J. Mater. Res. 107, 396–405 (2016)
R. Krein, M. Palm, The influence of Cr and B additions on the mechanical properties and oxidation behaviour of L21-ordered Fe–Al–Ti-based alloys at high temperatures. Acta Mater. 56, 2400–2405 (2008)
M. Palm, Fe-Al materials for structural applications at high temperatures: current research at MPIE. Int. J. Mater. Res. 100, 277–287 (2009)
D.G. Morris, M.A. Muñoz-Morris, The stress anomaly in FeAl–Fe3Al alloys. Intermetallics 13, 1269–1274 (2005)
D.M. Dimiduk et al., A structural study of ordered pre. Acta Metall. 36, 2947–2958 (1988)
S.A. Azmi et al., Microstructure and mechanical properties of Fe–Al–Nb–B alloys. MRS Adv. 2, 1353–1359 (2017)
M. Palm, Phase equilibria in the Fe corner of the Fe–Al–Nb system between 800 and 1150°C. J. Alloys Compd. 475, 173–177 (2009)
O. Prymak, F. Stein, Solidification and high-temperature phase equilibria in the Fe–Al-rich part of the Fe–Al–Nb system. Intermetallics 18, 1322–1326 (2010)
D.G. Morris et al., Strengthening at high temperatures by precipitates in Fe–Al–Nb alloys. Intermetallics 14, 1204–1207 (2006)
P. Kratochvíl et al., The effect of Nb addition on the microstructure and the high-temperature strength of Fe3Al aluminide. Metall. Mater. Trans. A. 49, 1598–1603 (2018)
D.D. Risanti, G. Sauthoff, Strengthening of iron aluminide alloys by atomic ordering and Laves phase precipitation for high-temperature applications. Intermetallics 13, 1313–1321 (2005)
Acknowledgments
The authors would like to thank Michael Kulse and Dennis Klapproth for alloy processing, Jürgen Wichert for heat treatments and Irina Wossack for EPMA measurements. Partial financial support by the Federal Ministry for Economic Affairs and Energy through grant 0324317C is gratefully acknowledged.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
On behalf of all authors, the corresponding author states that there is no conflict of interest.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Gedsun, A., Stein, F. & Palm, M. Development of new Fe–Al–Nb(–B) alloys for structural applications at high temperatures. MRS Advances 6, 176–182 (2021). https://doi.org/10.1557/s43580-021-00045-w
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/s43580-021-00045-w