Abstract
The BiFeO3/BaTiO3 (BFO/BTO) multilayers were deposited on Pt/Ti/SiO2/Si substrates using sol-gel spin coating technique. The electric and magnetic studies on BFO/BTO multilayer structures were carried out for different number of layers. Enhancement in multiferroic properties were seen for all the prepared multilayers as compared to individual BTO and BFO thin films. Maximum value of ferroelectric polarization 71.18 µC/cm2 and saturation magnetization 69.85 emu/cm3 was obtained for multilayer structure having five layers. The observed enhancement in the multiferroic properties of the multilayer system is due to the increased interfacial stress and multiferroic coupling between the alternating layers.
Similar content being viewed by others
References
J. Wang, T. J. Zhang, J. H. Xiang and B. S. Zhang, Mater. Chem Phys 108, 445–8 (2008).
D. L. Polla, L. F. Francis, Annu Rev Mater Sci 28, 563–97 (1998).
J. Wang, J. B. Neaton, H. Zheng, V. Nagarajan, S. B. Ogale, B. Liu, D. Viehland, V. Vaithyanathan, D. G. Scholm, M. Wuttig and R. Ramesh, Science 299, 1719 (2003).
W. Cai, S. Zhong, C. Fu, G. Chen and X. Deng, Mater Res Bull 50, 259–267 (2014).
X. Ren, Nature Mater 3, 91–94 (2004).
G. H. Haertling, J Amer Ceram Society 82, 797–818 (1999).
S. Gupta, M. Tomar and V. Gupta, J. Exp. Nanosci. 8(3), 261 (2013).
N. Zhao, L. Wan, L. Cao, D. Yu, S. Yu, R. Sun, Mater Lett 65, (2011) 3574–3576.
N. Ortega, A. Kumar, R.S. Katiyar, C. Rinaldi, J. Mater. Sci. 44 5127 (2009).
J.P. Zhou, H. He, Z. Shi, C.W. Nan, Appl. Phys. Lett. 88 013111 (2006).
N. Ortega, P. Bhattacharya, R.S. Katiyar, P. Dutta, A. Manivannan, M.S. Seehra, I.Takeuchi, S.B. Majumder, J. Appl. Phys. 100 126105 (2006).
P. Murugavel, M.P. Singh, W. Prellier, B. Mercey, Ch. Simon and B. Raveau, J. Appl. Phys. 97 103914 (2005).
H. Zheng, J. Wang, S.E. Lofland, Z. Ma, L. Mohaddes-Ardabili, T. Zhao, L. Salamanca-Riba, S.R. Shinde, S.B. Ogale, F. Bai, D. Viehland, Y. Jia, D.G. Schlom, M. Wuttig, A. Roytburd and R. Ramesh, Science 303 661 (2004).
H. Toupet, V.V. Shvartsman, F. Le Marrec, P. Borisov,W. Kleemann and M. Karkut, Integr. Ferroelectr. 100 165 (2008).
M.S. Ivanov, N.E. Sherstyuk, E.D. Mishina, A.S. Sigov, V.M. Mukhortov and V.T. Moshnyaga, Ferroelectrics 433 158 (2012).
A. Chen, H. Zhou, Z. Bi, Y. Zhu, Z. Luo, A. Bayraktaroglu, J. Phillips, E.-M. Choi, J.L. MacManus-Driscoll, S.J. Pennycook, J. Narayan, Q. Jia, X. Zhang, H. Wang, Adv. Mater. 25 1028 (2013).
S. Sharma, M. Tomar, A. Kumar, N. K. Puri and V. Gupta, Physica B 448, (2014) 125–127.
S. Sharma, M. Tomar, A. Kumar, N. K. Puri and V. Gupta, Adv Sci Lett 20, 1316–1320, 2014.
M. Kumar, A. Srinivas, and S. V. Suryanarayana, J. Appl. Phys. 87(2), 855–862 (2000).
T. Chen, J. Wang, X. Zhong, F. Wang, B. Li and Y. Zhou, Ceramics International (2013).
C.W. Nam, Appl. Phys. Lett. 81 954 (2007).
J. Ryu, A.V. Carazo, K. Uchino and H.E. Kim, Jpn. J. Appl. Phys. 40 4948 (2001).
P. Yang, K. M. Kim, J. Y. Lee, J. Zhu, and H. Y. Lee, Integ Ferro 113, 26–30 (2009).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Sharma, S., Tomar, M., Kumar, A. et al. Multiferroic BiFeO3/BaTiO3 thin films fabricated by chemical solution deposition technique. MRS Online Proceedings Library 1805, 222 (2015). https://doi.org/10.1557/opl.2015.622
Published:
DOI: https://doi.org/10.1557/opl.2015.622