Abstract
Background
Superhydrophobic substrate modifications are an effective way to improve SERS sensitivity by concentrating analyte molecules into a small surface area. However, it is difficult to manipulate low-volume liquid droplets on superhydrophobic substrates.
Results
To overcome this limitation, we deposited a hydrophilic Ti3C2Tx film on a superhydrophobic ZnO nanorod array to create a SERS substrate with improved analyte affinity. Combined with its interfacial charge transfer properties, this enabled a rhodamine 6G detection limit of 10−11 M to be achieved. In addition, the new SERS substrate showed potential for detection of biological macromolecules, such as microRNA.
Conclusion
Combined with its facile preparation, the SERS activity of ZnO/Ti3C2Tx suggests it may provide an ultrasensitive environmental pollutant-monitoring and effective substrate for biological analyte detection.
Graphical Abstract
Similar content being viewed by others
Introduction
Surface-enhanced Raman scattering (SERS) is a widely used and powerful tool for analyzing molecules and biomarkers [1], in vivo imaging [2], and environmental pollutants [3,4,5,6]. Recent development of new surface-enhancing materials and methods has markedly improved SERS detection limits [7,8,9]. Notably, the combination of nanostructured plasmics and Raman spectroscopy has enabled single molecule detection [10,11,12]. However, the surface enhancement is restricted to “hot spots” with an area of a few nm2 [13,14,15,16]. The detection or identification of low-concentration analytes remains challenging because random diffusion of molecules on the hydrophilic substrate results in poor spatial localization [17]. This random diffusion makes it time-consuming to search for molecules of interest within the enhanced area [18, 19].
Various strategies have been used to overcome the above problems [20,21,22], such as the use of superhydrophobic substrates to markedly enhance SERS intensity [17, 23,24,25,26]. Such substrates overcome the diffusion limit by concentrating molecules into a small area, resulting in a threefold increase in Raman intensity compared with ordinary hydrophilic substrates [23]. Superhydrophobic substrates can be fabricated using photolithography and those noble metal nanoparticle decorated SERS platform can achieve a detection limit of 10−18 M using rhodamine 6G (R6G) as a SERS probe [17]. However, the fabrication processes are sophisticated and the required equipment is expensive. Thus, more facile methods are required to prepare SERS substrates that confine the analyte molecule. Manipulating the morphology of inorganic nanoarrays may lead to new superhydrophobic substrates [27]. Among these inorganic materials, ZnO is an ideal candidate because it enables the facile synthesis and regulation of nanostructures [28]. Moreover, it can be easily decorated on the surface of different substrates, such as glass slides [29] and polydimethylsiloxane [30]. Although superhydrophobic SERS substrates can increase the Raman intensity remarkably, their poor affinity for aqueous analytes makes these molecules difficult to attach, which reduces the efficiency of the detection process.
Herein, we report a facile method to fabricate a SERS substrate comprising a two-dimensional (2D) Ti3C2Tx monolayer on a supporting superhydrophobic ZnO nanorod array (Fig. 1). The hydrophilicity of the Ti3C2Tx surface increases the affinity of aqueous analytes and its intrinsic metallic conductivity and plasmon resonance enhance Raman scattering intensity [31,32,33]. We prepared a small-area Ti3C2Tx spot on a superhydrophobic ZnO nanorod array and demonstrated that the hydrophobic substrate concentrates the analyte within the enhancement area and thus greatly improves the Raman scattering intensity. Density functional theory (DFT) calculations further showed that the interfacial charge transfer also contributes to the intensity enhancement. The ZnO/Ti3C2Tx substrate provides a cost-effective SERS platform for ultrasensitive analyte detection and identification.
Material and methods
Material
LiF was purchased from Aladdin Reagents (Shanghai), 200 mesh MAX Ti3AlC2 was purchased from 11 technology co.,LTD, hydrochloric acid (HCl), Zinc nitrate hexahydrate (Zn(NO3)2), Hexamethylenetetramine (HMTA), potassium permanganate were purchased from Sinopharm Chemical Reagent Co. Ltd. (China), Rhodamine 6G (R6G), methylene blue (MB), acid blue (AB), crystal violet (CV) were purchased from MACKLIN. All chemicals were used as received without further purification. miRNA with sequence of UUUGUACUACACAAAAGUACUG (sense(5'-3')) was purchased from RIBOBIO co.,LTD.
Fabrication of monolayer Ti3C2Tx
Monolayer Ti3C2Tx was obtained as previously described [34, 35]. Typically, 1.6 g LiF was added in 20 mL 9 M HCl in 5 min and magnetic stirred for another 5 min. Then, 1 g Ti3AlC2 was added over the course of 5 min in case of overheat. Etching was performed at room temperature for 24 h. The acidic mixture was centrifugated at 3500 rpm until pH ≥ 5 (each cycle for 5 min). Sediment was re-dispersed by hand-shaking every time. The Ti3C2Tx colloid was collected when the supernatant turned stable dark-green. After that, monolayer Ti3C2Tx was collected after centrifugation at 3500 rpm for 1 h by collecting the supernatant.
Preparation of ZnO/Ti3C2Tx SERS substrate and enhancement performance
Glass slides were pretreated using potassium permanganate and n-butanol as described previously [36]. To successfully construct ZnO nanorods on the glass slide surface, the pretreated glasses were firstly encapsulated by PDMS to form a 75 mm × 4 mm × 1 mm microchannel. Then, reaction solutions of 0.05 M Zn(NO3)2 and 0.05 M HMTA were injected by pump in two Teflon tubes at 50 µL/min for 2 h at 90 ℃ [37, 38]. After that, PDMS was removed and the obtained ZnO decorated glass slide was thoroughly washed by distilled water. The ZnO decorated glass slide was then dried in oven at 90 ℃ for further use. ZnO film was prepaered as previously described[39].
To fabricate ZnO/Ti3C2Tx SERS substrate, 4 µL 1–2 mg/mL monolayer Ti3C2Tx aqueous solution was dropped onto ZnO decorated glass slide and dried at room temperature for further use. Before test, 4 µL 10–6 to 10–10 M R6G was dropped on the ZnO/Ti3C2Tx SERS substrate and dried at room temperature. Laser of 532 nm was used in the experiments at power of 5 mW with a static mode and 20 s exposure time to reduce background noise. As for Raman mapping, step of 1 µm and 2 s exposure time at 532 nm were adopted.
DFT simulations and calculations
First-principles calculations of the enhancing mechanism in our systems used the DFT-based projector augmented-wave method implemented in the Materials Studio software [40]. The exchange–correlation energy was treated using the generalized gradient approximation of Perdew, Burke, and Ernzerhof [41, 42]. The energy cutoff for the plane wave basis expansion was set to 400 eV during the geometry relaxation. The 3 × 3 × 1 Monkhorst–Pack k-point sampling grid was used to calculate the surface structures. The self-consistent calculations used an energy convergence threshold of 10−5 eV. The equilibrium lattice constants were optimized using a maximum stress constraint of 0.03 eV/Å on each atom. Spin polarization was allowed in all calculations. The Ti3C2 (001) and ZnO (101) surfaces were obtained from their corresponding bulk supercell structures. To describe the charge transfer at the interface of these structures, lattice parameters of a = 12.384727 and b = 19.073 were established. Finally, the molecular adsorption energy (Eb) was calculated using the expression [43] Eb = Etotal − E1 − E2, where E1, E2, and Etotal are the respective energies of the interface, molecule, and interface with molecules adsorbed.
Results and discussion
Characterization of Ti3C2Tx nanosheets
Two-dimensional Ti3C2Tx nanosheets were prepared by selectively etching the Al layer from Ti3AlC2. As shown by the X-ray powder diffraction (XRD) patterns (Fig. 2A), the main peaks corresponding to MAX-phase Ti3AlC2 disappeared after etching, and the (002) diffraction angle decreased from 9.5° to 7.5°. Large Ti3C2Tx nanosheets were obtained using an in situ HCl/LiF etching method (Fig. 2B). High-resolution transmission electron microscopy and selected area electron diffraction showed that monolayered Ti3C2Tx sheets were successfully derived from MAX-phase Ti3AlC2 (Fig. 2C). Elemental composition maps obtained using X-ray energy-dispersive spectroscopy further proved that the Al layer was completely removed from the Ti3C2Tx surface (Fig. 2D, Additional file 1: Figure S1). These results demonstrate the successful etching of the atomic Al layer in Ti3AlC2.
Characterization of the ZnO/Ti3C2Tx SERS substrate
The ZnO nanorod arrays were prepared using a microfluidic chemical reaction. As shown in Fig. 2E, the XRD spectrum of the prepared ZnO was the same as that of ZnO with hexagonal wurtzite structure. Field emission SEM showed that the inclined ZnO nanorods with a length of ≈2.5 µm and a uniform hexagonal structure were successfully decorated on the glass substrate (Fig. 2F).
Small-area ZnO/Ti3C2Tx spots were prepared by depositing Ti3C2Tx solutions on a ZnO nanorod-modified glass substrate. To prevent oxidation of the Ti3C2Tx, the spots were dried at room temperature. As shown in Fig. 2G–I, the coverage area of the 2D Ti3C2Tx nanosheets was improved by increasing the concentration of the Ti3C2Tx solution. Furthermore, Fig. 2H shows that the Ti3C2Tx nanosheets were supported by the tips of ZnO nanorods and closely attached to the inclined nanorods. With the increasing concentration of Ti3C2Tx, a thin film gradually formed on the ZnO nanorod array (inset of Fig. 2I). Therefore, ZnO/Ti3C2Tx was fabricated by concentrating Ti3C2Tx nanosheets on ZnO nanorod arrays surface (Fig. 2J).
Hydrophilicity of prepared substrates
The hydrophilicities of the Ti3C2Tx film, ZnO nanorod array, and ZnO/Ti3C2Tx were assessed by measuring the surface contact angles of water droplets. The Ti3C2Tx film was hydrophilic, having contact angles of 77.6 ± 2° and 72.5 ± 3° for droplet volumes of 1 and 4 μL, respectively (Fig. 3A). The ZnO nanorod array surface was superhydrophobic (Fig. 3B), having a low affinity for droplet volumes less than 4 µL. Even 4 μL droplets maintained a contact angle of 150.2 ± 2° and a relatively spherical shape. Under gravity, droplet volumes of 6 and 8 µL made greater contact with the substrate surface and had an ellipsoidal shape. These results proved that the superhydrophobic substrate was successfully fabricated by decorating the glass slide with the ZnO nanorod array. Coating the ZnO with Ti3C2Tx resulted in a contact angle of 130.7 ± 4° for 4 µL droplets (Fig. 3C). Smaller contact angles were observed for droplet sizes less than 4 µL, which may be explained by the micro/nanostructure of ZnO/Ti3C2Tx. For example, if the droplet is larger than the hydrophilic modification area, the edge of ZnO/Ti3C2Tx substrate can still be superhydrophobic. Importantly, ZnO/Ti3C2Tx showed a higher hydrophilicity than the ZnO nanorod array, as evidenced by the smaller contact angles and easier droplet attachment. These results demonstrate that the ZnO/Ti3C2Tx substrate greatly improved the water droplet attachment and maintained high contact angles after Ti3C2Tx modification.
SERS performance of the ZnO/Ti3C2Tx substrate
Amorphous ZnO nanocages have remarkable SERS activity [44]. Here, crystalline ZnO also showed SERS activity, with a hexagonal wurtzite ZnO nanorod array yielding an R6G detection limit of 10−6 M. As indicated in Fig. 4A, characteristic peaks of R6G can be clearly identified. However, the characteristic Raman scattering peaks at 614, 773, 1360, 1500, 1573, and 1650 cm−1 were almost undetectable at an R6G concentration of 10−7 M.
An R6G detection limit of 10−7 M was achieved using Ti3C2Tx film (Fig. 4B), which is consistent with a previously reported value [32]. Different Ti3C2Tx films were prepared by filtering Ti3C2Tx nanosheets (0.5–2.0 mg in 30 mL water) on a polytetrafluoroethylene membrane (50 mm of diameter). At an R6G concentration of 10−6 M, all films had slight difference of SERS activity (Additional file 1: Figure S2). However, reducing the R6G concentration from 10−6 to 10−7 M resulted in markedly lower intensities of the Raman peaks at 773 and 1500 cm−1 and rendered the characteristic peaks at 614, 1360, 1573, and 1650 cm−1 undetectable. The SERS activity of the ZnO/Ti3C2Tx substrate was much higher than that of pristine ZnO and Ti3C2Tx, resulting in an R6G detection limit of 10−11 M (Fig. 4C) with enhancement factors (EFs) of 1.49 × 107 and 7.88 × 106 at peaks of 614 and 1360 cm−1, respectively (Additional file 1: Table S1, calculation details were presented in supporting information). The EF of ZnO/Ti3C2Tx is 2.10fold of Ti3C2Tx and 2.73fold of ZnO at peak of 614 cm−1. At 1360 cm−1, the EF of ZnO/Ti3C2Tx is 1.65fold and 2.64fold of Ti3C2Tx and ZnO, respectively. As can be seen in Additional file 1: Figure S6, with the decrease of analyte concentration, the distribution of Raman signal becomes uneven. This indicates that the distribution of molecules on the substrate is not uniform with decreasing concentration. According to the Raman mapping, 10–11 M R6G could be detected by mapping method. Thus, the combination of ZnO and Ti3C2Tx enhanced the R6G detection sensitivity by five orders of magnitude compared with that of pristine ZnO and four orders of magnitude compared with that of pristine Ti3C2Tx. The ZnO/Ti3C2Tx substrate was also highly sensitive to methylene blue (MB), yielding a detection limit of 10−10 M (Additional file 1: Figure S7a).
The SERS performance of the ZnO substrate may be influenced by the ZnO/Ti3C2Tx interfacial properties. A ZnO film and a ZnO(film)/Ti3C2Tx substrate were fabricated to assess the contribution of hydrophobic micro/nanostructure to the SERS activity (Additional file 1: Figure S3a and b). The ZnO film substrate had a higher SERS sensitivity compared with that of pristine ZnO, enabling detection of 10−6 M R6G (Fig. 4D). The ZnO(film)/Ti3C2Tx substrate had an even higher SERS sensitivity, achieving an R6G detection limit of 10−8 M (Fig. 4E). Contact angle measurements indicated both ZnO film and ZnO(film)/Ti3C2Tx were hydrophilic, displaying 4 µL droplet contact angles of 37.1 ± 1.2° and 77.5 ± 1°, respectively (Additional file 1: Figure S4a and b). The above results demonstrate that the hydrophobic micro/nanostructure of ZnO/Ti3C2Tx may contribute more to the Raman scattering intensity than the hydrophilic micro/nanostructure of ZnO (film)/Ti3C2Tx.
DFT calculation of charge transfer properties
To further explore the enhancement mechanism, first-principles DFT calculations were employed. Using the optimized ZnO/Ti3C2Tx (Fig. 5A) and ZnO/Ti3C2Tx-R6G (Additional file 1: Figure S5a) interface structures, the charge density difference was calculated. The results clearly identified a charge transfer mechanism at the interface, enabling electron transfer from the ZnO nanorod surface to Ti3C2Tx nanosheet (Fig. 5B). The work of adhesion (Wad) describes the relationship between the interface distance and system energy in the interface. The DFT calculations showed that Wad is lowest at an interface distance of ≈2.0 Å (Fig. 5C). This suggests that the distance between ZnO and Ti3C2Tx surfaces is ≈2.0 Å, which results in their chemisorption. The calculated energy of R6G absorption on the ZnO/Ti3C2Tx interface is −2.36 eV, indicating that the interface has a large adsorption capacity for R6G molecules.
DFT simulations were also carried out to investigate charge transfer phenomena at the interface between Ti3C2Tx and R6G and found that charge can be further transferred from Ti3C2Tx to R6G molecules (Fig. 5D, top view Additional file 1: Figure S5b). These results are consistent with UV–vis spectra of Ti3C2Tx-R6G (Fig. 5E), which show difference in the peak position between 500 and 550 nm that could be explained by the chemisorption of Ti3C2Tx and R6G. Moreover, the calculated density of states of ZnO/Ti3C2Tx-R6G increased toward the Femi level after adsorption of R6G (Fig. 5F), which again indicates there is interfacial charge transfer between the substrate and R6G. Chemisorption was likewise observed between Ti3C2Tx with MB, together with an obvious absorption peak shift (Fig. 5g), suggesting charge transfer also occurs between Ti3C2Tx and MB and leads to high SERS activity (detection limit of 10−10 M). However, because of the physisorption of the AB and CV molecules with the Ti3C2Tx surface, no obvious absorption peak shift was observed (Fig. 5H, I), which could explain why the SERS enhancement of AB and CV is limited (Additional file 1: Figure S7b, c). Considering that the group of ZnO(film)/Ti3C2Tx with a larger contact area between Ti3C2Tx and ZnO film did not show more significant enhancement performance, this suggests that the hydrophobic structure plays a more important role in Raman enhancement. These results suggest that the observed SERS performance of the ZnO/Ti3C2Tx substrate may result from a synergy between its analyte-concentrating ability and interfacial charge transfer properties.
To evaluate the spatial distribution of the SERS intensity, the Raman intensity from 10−6 M R6G drop-cast on the ZnO/Ti3C2Tx substrate was mapped at 1360 cm−1. The signal distribution on the substrate did not exhibit a coffee ring effect, and its signal was slightly stronger in the depressions than in the protrusions (Fig. 6A and B). To investigate the reason for this phenomenon, we took SEM images of the distribution of gold nanoparticles on the substrate to simulate the distribution of R6G (Fig. 6C). According to the image, gold nanoparticles tend to aggregate more in the depression than elsewhere, so the intensity of the Raman signal in the depression is also slightly stronger than elsewhere. Despite the slightly different molecular distributions, the overall signal intensity remained relatively uniform. Statistical analysis of 1360 cm−1 peak intensity in Fig. 6D yielded a relative standard deviation of only 6.23%, which indicates the platform is highly homogeneous and thus capable of providing reproducible signals. Area mapping of 10–6 M to 10–11 M was performed as can be seen in Additional file 1: Figure S6, with the decrease of analyte concentration, the distribution of Raman signal becomes uneven. This indicates that the distribution of molecules on the substrate is not that uniform with decreasing concentration, which result in the signal variation. A more reasonable sampling method is to first find the location of the analyte by point measurement, and then do the area mapping based on this, then analyze the area where the signal is more concentrated.
Finally, the ability of the ZnO/Ti3C2Tx substrate to detect biological macromolecules was assessed. Using microRNA as an analyte (Fig. 6e), a detection limit of 10−6 M was obtained and characteristic peaks at 925 cm−1 and 1040 cm−1 [45] were clearly observed at microRNA concentrations from 10−4 to 10−6 M. The measured Raman intensities show a certain linear relationship at the two characteristic peaks of 925 cm−1 and 1040 cm−1(R2925 cm−1 = 0.9858, R21040 cm−1 = 0.9865) with a detection limit of 10–6 M. We speculate that there are two possible causes of this phenomenon. As can be seen in Additional file 1: Figure S7, the distribution of analytes was uneven at low concentration, which result in the uneven distribution of Raman signal. Another possibility is that different nucleobase pairs (U and A) adsorb differently to the substrate [46,47,48], resulting in different signal intensities that enhanced by ZnO/Ti3C2Tx substrate. Besides, the ZnO/Ti3C2Tx substrate yielded a much lower Raman intensity than that obtained using a SERS substrate composed of Au nanoparticles (Additional file 1: Figure S8a and b). However, the signal stability of the SERS performance of ZnO/Ti3C2Tx was higher, especially at the peaks of 925 cm−1 and 1040 cm−1, characteristic peaks can be clearly identified even at 10–6 M, which may result from its greater analyte-concentrating ability compared with that of the hydrophilic Au nanoparticles. The stable SERS performance of ZnO/Ti3C2Tx suggests it may provide a new substrate for biological analyte detection.
Conclusion
In summary, a hydrophobic micro/nanostructured ZnO/Ti3C2Tx SERS substrate was developed and yielded a detection limit of 10−11 M using R6G as target analytes. DFT calculations were used to study the mechanism underlying the SERS activity. Synergy between the hydrophobic nanostructure and ZnO/Ti3C2Tx interfacial charge transfer were found to enhance the SERS activity. Moreover, the platform shows potential for miRNA detection. This work provides a new strategy of combining a semiconductor nanoarray with 2D Ti3C2Tx for designing and fabricating high-performance SERS platforms.
Availability of data and materials
Data availability—the data generated during the current study are available within the article. Supplementary material related to this article can be found in the online version.
References
Liang J, Teng P, Xiao W, He G, Song Q, Zhang Y, et al. Application of the amplification-free SERS-based CRISPR/Cas12a platform in the identification of SARS-CoV-2 from clinical samples. J Nanobiotechnol. 2021;19:273.
Bock S, Choi YS, Kim M, Yun Y, Pham XH, Kim J, et al. Highly sensitive near-infrared SERS nanoprobes for in vivo imaging using gold-assembled silica nanoparticles with controllable nanogaps. J Nanobiotechnol. 2022;20:130.
Cardinal MF, Vander Ende E, Hackler RA, McAnally MO, Stair PC, Schatz GC, et al. Expanding applications of SERS through versatile nanomaterials engineering. Chem Soc Rev. 2017;46:3886–903.
Ding S-Y, You E-M, Tian Z-Q, Moskovits M. Electromagnetic theories of surface-enhanced Raman spectroscopy. Chem Soc Rev. 2017;46:4042–76.
Zong C, Xu M, Xu L-J, Wei T, Ma X, Zheng X-S, et al. Surface-enhanced Raman spectroscopy for bioanalysis: reliability and challenges. Chem Rev. 2018;118:4946–80.
Langer J, Jimenez de Aberasturi D, Aizpurua J, Alvarez-Puebla RA, Auguié B, Baumberg JJ, et al. Present and future of surface-enhanced Raman scattering. ACS Nano. 2020;14:28–117.
Haldavnekar R, Venkatakrishnan K, Tan B. Next generation SERS- atomic scale platform for molecular level detection. Appl Mater Today. 2020;18:100529.
Ran P, Jiang L, Li X, Li B, Zuo P, Lu Y. Femtosecond photon-mediated plasma enhances photosynthesis of plasmonic nanostructures and their SERS applications. Small. 2019;15:1804899.
Chen R, Du X, Cui Y, Zhang X, Ge Q, Dong J, et al. Vertical flow assay for inflammatory biomarkers based on nanofluidic channel array and SERS nanotags. Small. 2020;16:2002801.
Huang JA, Mousavi MZ, Zhao Y, Hubarevich A, Omeis F, Giovannini G, et al. SERS discrimination of single DNA bases in single oligonucleotides by electro-plasmonic trapping. Nat Commun. 2019;10:5321.
Lee J, Crampton KT, Tallarida N, Apkarian VA. Visualizing vibrational normal modes of a single molecule with atomically confined light. Nature. 2019;568:78–82.
Le Ru EC, Etchegoin PG. Single-molecule surface-enhanced Raman spectroscopy. Annu Rev Phys Chem. 2012;63:65–87.
Michaels AM, Nirmal M, Brus LE. Surface enhanced Raman spectroscopy of individual rhodamine 6G molecules on large Ag nanocrystals. J Am Chem Soc. 1999;121:9932–9.
Stöckle RM, Suh YD, Deckert V, Zenobi R. Nanoscale chemical analysis by tip-enhanced Raman spectroscopy. Chem Phys Lett. 2000;318:131–6.
De Angelis F, Patrini M, Das G, Maksymov I, Galli M, Businaro L, et al. A hybrid plasmonic-photonic nanodevice for label-free detection of a few molecules. Nano Lett. 2008;8:2321–7.
Schuller JA, Barnard ES, Cai W, Jun YC, White JS, Brongersma ML. Plasmonics for extreme light concentration and manipulation. Nat Mater. 2010;9:193–204.
De Angelis F, Gentile F, Mecarini F, Das G, Moretti M, Candeloro P, et al. Breaking the diffusion limit with super-hydrophobic delivery of molecules to plasmonic nanofocusing SERS structures. Nat Photonics. 2011;5:682–7.
Nair PR, Alam MA. Performance limits of nanobiosensors. Appl Phys Lett. 2006;88:233120.
Sheehan PE, Whitman LJ. Detection limits for nanoscale biosensors. Nano Lett. 2005;5:803–7.
Eftekhari F, Escobedo C, Ferreira J, Duan X, Girotto EM, Brolo AG, et al. Nanoholes as nanochannels: Flow-through plasmonic sensing. Anal Chem. 2009;81:4308–11.
Lassiter JB, Aizpurua J, Hernandez LI, Brandl DW, Romero I, Lal S, et al. Close encounters between two nanoshells. Nano Lett. 2008;8:1212–8.
Xiao L, Wang C, Dai C, Littlepage LE, Li J, Schultz ZD. Untargeted tumor metabolomics with liquid chromatography–surface-enhanced Raman spectroscopy. Angew Chemie Int Ed. 2020;59:3439–43.
Xu F, Zhang Y, Sun Y, Shi Y, Wen Z, Li Z. Silver nanoparticles coated zinc oxide nanorods array as superhydrophobic substrate for the amplified SERS effect. J Phys Chem C. 2011;115:9977–83.
Lee HK, Lee YH, Zhang Q, Phang IY, Tan JMR, Cui Y, et al. Superhydrophobic surface-enhanced Raman scattering platform fabricated by assembly of Ag nanocubes for trace molecular sensing. ACS Appl Mater Interfaces. 2013;5:11409–18.
Kao Y-C, Han X, Lee YH, Lee HK, Phan-Quang GC, Lay CL, et al. Multiplex surface-enhanced Raman scattering identification and quantification of urine metabolites in patient samples within 30 min. ACS Nano. 2020;14:2542–52.
Li X, Lee HK, Phang IY, Lee CK, Ling XY. Superhydrophobic-oleophobic Ag nanowire platform: an analyte-concentrating and quantitative aqueous and organic toxin surface-enhanced Raman scattering sensor. Anal Chem. 2014;86:10437–44.
Du X, Liu D, An K, Jiang S, Wei Z, Wang S, et al. Advances in oxide semiconductors for surface enhanced Raman scattering. Appl Mater Today. 2022;29:101563.
Wang ZL. Nanostructures of zinc oxide. Mater Today. 2004;7:26–33.
Hu W, Liu Y, Chen T, Liu Y, Li CM. Hybrid ZnO nanorod-polymer brush hierarchically nanostructured substrate for sensitive antibody microarrays. Adv Mater. 2015;27:181–5.
Cui H, Liu Q, Li R, Wei X, Sun Y, Wang Z, et al. ZnO nanowire-integrated bio-microchips for specific capture and non-destructive release of circulating tumor cells. Nanoscale. 2020;12:1455–63.
Ye Y, Yi W, Liu W, Zhou Y, Bai H, Li J, et al. Remarkable surface-enhanced Raman scattering of highly crystalline monolayer Ti3C2 nanosheets. Sci China Mater. 2020;63:794–805.
Sarycheva A, Makaryan T, Maleski K, Satheeshkumar E, Melikyan A, Minassian H, et al. Two-dimensional titanium carbide (MXene) as surface-enhanced Raman scattering substrate. J Phys Chem C. 2017;121:19983–8.
Li G, Bin GW, Qiu T, Cong S, Zhao Z, Ma R, et al. Surface-modified two-dimensional titanium carbide sheets for intrinsic vibrational signal-retained surface-enhanced Raman scattering with ultrahigh uniformity. ACS Appl Mater Interfaces. 2020;12:23523–31.
Li J, Kurra N, Seredych M, Meng X, Wang H, Gogotsi Y. Bipolar carbide-carbon high voltage aqueous lithium-ion capacitors. Nano Energy. 2019;56:151–9.
Alhabeb M, Maleski K, Anasori B, Lelyukh P, Clark L, Sin S, et al. Guidelines for synthesis and processing of two-dimensional titanium carbide (Ti3C2Tx MXene). Chem Mater. 2017;29:7633–44.
Wu Z, Zhao D, Hou C, Liu L, Chen J, Huang H, et al. Enhanced immunofluorescence detection of a protein marker using a PAA modified ZnO nanorod array-based microfluidic device. Nanoscale. 2018;10:17663–70.
Zhao D, Wu Z, Zhang W, Yu J, Li H, Di W, et al. Substrate-induced growth of micro/nanostructured Zn(OH)F arrays for highly sensitive microfluidic fluorescence assays. ACS Appl Mater Interfaces. 2021;13:28462–71.
Zhao D, Wu Z, Yu J, Wang H, Li Y, Duan Y. Highly sensitive microfluidic detection of carcinoembryonic antigen via a synergetic fluorescence enhancement strategy based on the micro/nanostructure optimization of ZnO nanorod arrays and in situ ZIF-8 coating. Chem Eng J. 2020;383:123230.
Li H, Wang J, Liu H, Zhang H, Li X. Zinc oxide films prepared by sol–gel method. J Cryst Growth. 2005;275:e943–6.
Blöchl PE. Projector augmented-wave method. Phys Rev B. 1994;50:17953–79.
Joubert D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys Rev B Condens Matter Mater Phys. 1999;59:1758–75.
Perdew JP, Burke K, Ernzerhof M. Generalized gradient approximation made simple. Phys Rev Lett. 1996;77:3865–8.
Yang Z, Liu G. First-principles study on the influence of compressive deformation on the oxygen adsorption energy and electrical properties of phosphorene. Phys B Condens Matter. 2019;563:72–8.
Wang X, Shi W, Jin Z, Huang W, Lin J, Ma G, et al. Remarkable SERS activity observed from amorphous ZnO nanocages. Angew Chemie Int Ed. 2017;56:9851–5.
Bell SEJ, Sirimuthu NMS. Surface-enhanced Raman spectroscopy (SERS) for sub-micromolar detection of DNA/RNA mononucleotides. J Am Chem Soc. 2006;128:15580–1.
El Amri C, Marie-Helene B, Marie-Christine M. Adenine and RNA in mineral samples. Surface-enhanced Raman spectroscopy (SERS) for picomole detections. Spectrochim Acta A Mol Biomol Spectrosc. 2003;59:2645–54.
Driskell JD, Primera-pedrozo OM, Dluhy RA, Zhao Y, Tripp RA. Quantitative surface-enhanced Raman spectroscopy based analysis of MicroRNA mixtures. Appl Spectrosc. 2009;63:1107–14.
Driskell JD, Seto AG, Jones LP, Jokela S, Dluhy RA, Zhao Y, et al. Rapid microRNA (miRNA) detection and classification via surface-enhanced Raman spectroscopy (SERS). Biosens Bioelectron. 2008;24:917–22.
Acknowledgements
We gratefully acknowledge the financial support by the National Natural Science Foundation of China (No. 82172736), Special project for Clinical Research in Health Industry of Shanghai Municipal Health Commission (20214Y0102), the State Key Laboratory of Oncogenes and Related Genes (No. SB21-09). The authors would like to thank the shiyanjia lab (www. shiyanjia.com) for the Raman mapping test.
Author information
Authors and Affiliations
Contributions
YS, YL and YD worked together in designing the conceptualization of this project. YD participated in the guidance of the work throughout the whole process. ZW performed the experiments, drew schematics and wrote the manuscript. DZ assisted in evaluating the results, discussion and editing the manuscript. XH and JL provided the software and calculation. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Additional file 1.
Supplementary Material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.
About this article
Cite this article
Wu, Z., Zhao, D., Han, X. et al. Deposition of hydrophilic Ti3C2Tx on a superhydrophobic ZnO nanorod array for improved surface-enhanced raman scattering performance. J Nanobiotechnol 21, 17 (2023). https://doi.org/10.1186/s12951-022-01756-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s12951-022-01756-4