Abstract
Developing highly efficient pharmaceuticals to eradicate pathogens and facilitate wound healing is of great concern. Despite some cationic carbon dots (CDs) have been used for sterilization, hardly any anionic CDs with antimicrobial activity have appeared. In the present work, we engineered a string of anionic CDs (especially CD31) as valid broad-spectrum bactericides to kill bacteria. Furthermore, CD31 conjugated with ɛ-polylysine (Plys) to construct injectable, and self-healing hydrogel (CD-Plys) that possess the advantages of remarkable broad spectrum antibacterial activity, excellent wound healing ability and satisfied biocompatibility. CD-Plys could dramatically accelerate wound healing with epithelization and enhanced angiogenesis. Taken together, this work provides a two-pronged strategy to explore CDs-based antimicrobial agents for disease therapy and tissue engineering.
Similar content being viewed by others
Introduction
Bacterial infection is a major risk to worldwide people’s lives, therefore, exploiting innovative strategies to combat microorganisms is highly needed. Although some antibiotics have successfully inhibited bacterial diseases, their abuse aggravates antibiotic resistance of microbes [1,2,3]. The emergence of nanotechnology provides an alternative strategy to design non-antibiotic bactericides. Multitudinous nanoscale germicides, such as noble metal (eg. Au, Ag, Pd, Ru, Pt) [4,5,6,7,8,9,10,11,12] nanoparticles (NPs), metallic oxide [13,14,15,16,17] (eg. ZnO, TiO2 and CuO) NPs, and carbonaceous nanomaterials [18,19,20] have been exploited as antimicrobial alternatives, which exhibit high potency with broad spectrum antibacterial activity. However, the clinical applications of these nanofungicides may be hindered due to their inherent cytotoxicity, high cost or long-term retention. Therefore, it is crucial to develop nontoxic and environmentally benign antimicrobial agents for effectively killing bacteria, either from the academic research or clinic therapy point of view.
Carbon dots (CDs) have wide applications in bioimaging [21,22,23,24,25,26,27,28,29,30,31], sensing [32,33,34,35,36,37], drug/dye/protein delivery [38,39,40,41] and cancer therapy [42,43,44,45,46,47,48,49,50], owning to their excellent characteristics including small size, easy surface functionalization, high stability, strong hydrophilicity, good biocompatibility and low toxicity. By contrast, the potential antibacterial capacity of CDs has been less explored [51,52,53], although CDs possess the advantages of durable and environmentally friendly than metal-containing nanofungicides and traditional antibiotics. Furthermore, most of CDs have to utilize external reagents or equipment to achieve bacteriostasis. For instance, Sun et al. has reported CDs can effectively kill bacteria under the exposure to visible light [54]. Huang et al. prepared halogen/nitrogen-doped CDs to kill bacteria by producing reactive oxygen species upon LED irradiation [55]. Zhang et al. prepared cerium-doped CDs for wound healing under UV excitation [56]. Qu et al. enhanced the antibacterial performance of CDs at the aid of H2O2 [57]. However, adding agents or light illumination is relatively sophisticated and might bring about accidental injury to certain tissues. Therefore, exploiting CDs-based nanofungicides to kill bacteria and heal wound infections with no external activation is becoming the focus of concern. It is generally believed that highly positively charged CDs can easily interact with negatively charged bacteria and directly disrupt the bacterial cell membranes via electrostatic interaction [58]. For example, quaternized CDs constructed by Wu’s group inactivated Gram-positive bacteria [51, 59]. Quaternized CDs fabricated by Zhao et. al could kill both Gram-positive and Gram-negative bacteria [60]. Supercationic CDs synthesized by Jian et al. could effectively eliminate non-multidrug-resistant and multidrug-resistant bacteria, and methicillin-resistant S. aureus [61]. Nevertheless, as far as we know, rare negatively charged CDs with remarkable antibacterial activity have been reported.
Hydrogels are three-dimensional soft materials with porous structures, excellent water absorption ability, and good biocompatibility. The practical applications of traditional hydrogels are usually impeded by the weaknesses of poor mechanical properties and limited functions. Lately, nanohydrogels those are constructed from nanomaterials including metal-containing NPs [62,63,64,65,66,67], metal-free NPs [68, 69] and metal organic frameworks [70, 71], integrate the functions of nanoagents and macromolecules, significantly enrich the potential applications of hydrogels. What’s more, CDs-based nanohydrogels integrate the characteristics inherited from CDs and polymers, have shown wide applications in sensing [72,73,74], environmental pollutants removal [75], microbial elimination [76], cartilage regeneration [77], and supercapacitors [78] to name just a few. Unfortunately, few reports on CDs antibacterial hydrogels were mentioned so far. Therefore, there is an urgent need to develop a facile mode to construct antibacterial CDs-based hydrogel for killing bacteria and healing tissue infections effectively.
Herein, Glutaraldehyde (GA), a widely used cross-linking agent and disinfectant, acted as a precursor to react with PEG200 at the volume ratio of 100:1, 10:1, 3:1, 1:1, 1:3, 1:10, 1:100, and obtained a series of negatively charged CDs denoted as CD1001, CD101, CD31, CD11, CD13, CD110 and CD1100 (Scheme 1a). The zeta potential of CD1001, CD101, CD31, CD11, CD13, CD110 and CD1100 was -13.2, -9.8, -9.0, -11.1, -14.9, -20.4 and -20.4 mV, respectively (Additional file 1: Fig. S1). Among the CDs, CD31 exhibited the most significant inhibitory effect on E. coli and S. aureus, with the minimum inhibitory concentration (MIC) of 64 and 32 μg/mL, respectively. The aldehyde groups on the surface of CDs could destroy the bacterial membrane and efficaciously eradicate pathogens [79, 80]. Meanwhile, the other fungicide, ɛ-Polylysine (Plys) also could eliminate E. coli and S. aureus with MIC of 128 µg/mL. The win–win co-operation of these two germicides was achieved by the conjugation of CD31 with Plys to form stable, injectable, self-healing and antibacterial CD-Plys hydrogel (Scheme 1b). CD-Plys exhibited enhanced broad-spectrum antimicrobial efficacy (Scheme 1b–c) and can automatically adapt to different conditions of wounds to promote wound closure, avoid infection and contaminating, supply wound healing with three-dimensional physiological environment and facilitate wound healing (Scheme 1c). The hemolysis and cytotoxicity assays verified that CD-Plys has good biocompatibility. Moreover, in vivo wound healing experiments demonstrated that CD-Plys could completely cover the whole wounds and promote full-thickness skin wound healing. Therefore, CD-Plys has great potential for application in bacteria-induced wound infection and tissue reconstruction.
Schematic illustration for (a) The preparation of CDs and their antimicrobial ctivity against Gram-negative and Gram-positive bacteria. b Synthesis of CD-Plys hydrogel and its inhibitory effect on E. coli and S. aureus. c CD-Plys hydrogel acts as a wound dressing to prevent bacterial infection and promote wound healing on mouse models
Materials and methods
Synthesis of CDs
Taking CD31 as an example, GA (300 µL) and PEG200 (100 µL) were dissolved in 5 mL of ethanol. The solution was transferred to a Teflon-lined autoclave and heated for 140 min at 150 °C. After cooled to room temperature, the resultant brown solid was dispersed in deionized water and centrifuged at 10,000 rpm for 20 min to remove carbon aggregates The crude product was dialyzed against water by a dialysis bag (cutoff Mn: 3.5 kDa) for 24 h, and the brown CDs were obtained by freeze-drying.
The preparation and purification process of CD1001, CD101, CD11, CD13, CD110 and CD1100 was similar with that of CD31, except the volume ratio of GA and PEG200 was 100:1 (1000 µL:10 µL), 10:1 (100 µL:10 µL), 3:1 (300 µL:100 µL), 1:1 (100 µL:100 µL), 1:3 (100 µL:300 µL), 1:10 (10 µL:100 µL), 1:100 (10 µL:1000 µL), respectively.
Synthesis of CD-Plys hydrogel.
The aqueous solution of Plys (400 mg/mL, 1 mL) and CDs (200 mg/mL, 1 mL) was added to a vial and the mixture was kept at room temperature for 40 min for gelation, and the gel viscosity was verified by the method from “stable to inversion”.
Materials
ε-Polylysine (Plys) was purchased from Meilun Biotechnology Co., Ltd. Agar, peptone, and yeast powder were purchased from CSI Biochemical Technology Co., Ltd. Sodium chloride, sodium hydroxide, glutaraldehyde, absolute ethanol, and polyethylene glycol (PEG200) were purchased from Sinopharm Chemical Reagent Co., Ltd. The live/dead cell double staining kit was purchased from Jiangsu KGI Biotechnology Co., Ltd. The MTT Cell Proliferation and Cytotoxicity Assay Kit was purchased from Shanghai Yuanye Biological Technology Co., Ltd. The cell culture medium (DMEM) was purchased from Gibco. SYTO 9/PI kit was purchased from Jiangsu KeyGEN Biotechnology Co., Ltd. LB liquid medium (peptone 1%, yeast powder 0.5%, sodium chloride 1%). LB solid medium (peptone 1%, yeast powder 0.5%, sodium chloride 1%, agar powder 1.5%).
Characterization
Fourier transform infrared (FTIR) spectroscopy was obtained by a Bruker Vertex 70 IR spectrophotometer. UV–Vis absorption spectra were performed on a UV-2450PC spectrophotometer (Shimadzu, Japan). The fluorescence spectra were measured by LS-55 fluorescence spectrometer (Perkin-Elmer, USA). Transmission electron microscopy (TEM) images were acquired by JEM-1011 electron microscope (JEOL Co., Japan). Morphology characterization of CD-Plys was performed on scanning electron microscopy (SEM, Micromeritics FEI PHILIPS) with an accelerating voltage of 10 kV. Samples were mounted onto the specimen stubs by means of a conductive double-sided adhesive tape and sputtered with gold for 40 s. X-ray diffraction (XRD) patterns of CD31, Plys and CD-Plys were performed on Bruker D8 diffractometer. The zeta potentials of CD31, Plys and CD-Plys were measured by Zeta-sizer Nano ZS (Malvern Instruments Ltd., UK). The rheometer (Anton Paar, Physical MCR 302) was carried out to evaluate dynamic rheology behavior of CD-Plys. The bacterial confocal images of CD31, Plys and CD-Plys were obtained using Zeiss confocal laser microscope (ZEISS LSM 700).
In vitro antibacterial activities of CDs and Plys
The suspended E. coli and S. aureus cells post-treatment with various concentration of the CDs or Plys were incubated at 37 °C for 30 min, respectively. The 200 µL solution of samples co-incubated with bacteria were surface-plated on Luria–Bertani agar plates, and the plates were incubated at 37 °C for 24 h. The number of colonies was counted, and the viable cell numbers of the treated samples and the controls were calculated in CFU/mL.
Rheological properties of CD-Plys hydrogel
We measured the storage modulus (G') and loss modulus (G'') of CD-Plys hydrogel by a rheometer. The hydrogel sample was placed in the center of a 25 mm cone, the upper plate was placed at 0.5 mm, and the temperature was set at 37 ℃. First, the angular frequency was fixed, and the G' of the sample within the range of the shear stress of 0.01 ~ 100% was measured. We took the shear stress as the abscissa and G' as the ordinate to determine the linear viscoelasticity. Then we selected the angular frequency from 0.1 to 100 rad/s, measured the G’ and G” of the sample, and used the angular frequency as the abscissa and G’ and G” as the ordinate to plot the rheology curve.
Hemolysis assay
Blood was incubated with CD-Plys hydrogel, PBS and Triton X-100 at 37 °C for 60 min, respectively. After centrifugation, the absorbance of the supernatant in each group at 540 nm was determined.
The hemolysis (%) was calculated by the following equation:
where ODx, ODo and ODy are the absorbance values of the hydrogel, diluted blood in PBS and diluted blood in Triton X-100, respectively.
MTT assay
The cytotoxicities of CDs and Plys were evaluated toward L929 fibroblast cell lines by MTT assay. Firstly, 1.0 × 104 cells were seeded into a 96 well plate in DMEM and in a humidified 5% CO2 incubator at 37 °C. Afterwards L929 fibroblast cells were treated for 24 h with different concentrations of CD31 or Plys DMEM solution. Next, 10 μL of MTT solution was added to each well and incubated for 4 h in the dark. Dimethyl sulfoxide was added to dissolve the MTT formazan crystals. Finally, the absorbance was measured at 490 nm using a microplate reader (Bio TeKtronixELX808TM USA). All the assays were conducted in four parallel groups.
The cytotoxicity of CD-Plys was evaluated by direct contact with L929 cells. 100 µL of CD-Plys solution was introduced to each well of 96-well cell culture plates. After 60 min, CD-Plys hydrogel formed and washed with sterile PBS solution. Thereafter, L929 cells were seeded on CD-Plys at a density of 1.0 × 104 cells per well. The cells were incubated for 12, 24 and 48 h in a humidified 5% CO2 incubator at 37 °C, and the cell viability was determined by MTT assay. OD values at 490 nm were measured by a microplate reader. All the experiments were performed in four parallel groups.
In vitro antibacterial assays
The antibacterial activity of CD-Plys hydrogel was evaluated using an inhibition zone assay against E. coli and S. aureus. First, the density of E. coli or S. aureus was adjusted to 105 CFU/mL and then the bacteria were spread on the agar surface, respectively. Afterward, the hydrogel were placed on the center of agar plates, and co-cultured with E. coli or S. aureus for 24 h at 37 °C. The antibacterial effect was compared by the diameter of the inhibition zone.
Bacteria live/dead staining assay
The bacteria and CD-Plys were cocultured for 4 h, and stained with SYTO 9 (green fluorescence) and PI (red fluorescence) for 30 min in the dark. Then the mixture was observed by CarlZeiss LSM 710 confocal laser scanning microscope (Zurich, Switzerland).
In vivo infected wound healing
All animal procedures were conducted under the guidelines approved by the Animal Ethics Committee of Changchun Institute of Applied Chemistry, Chinese Academy of Sciences (No. 2021–0004). The infected wound on the skin of the mice were created to evaluate the in vivo antibacterial and healing abilities of CDs, Plys, CD-Plys. In total, the 24 female mice were randomly divided into eight groups. After the fur of the dorsal skin in all mice was shaved, full-thickness skin excisional round wounds (8 mm in diameter) were created on the dorsal of mice. The wound was infected with E. coli (1 × 105 CFU in 20 L PBS) or S. aureus (1 × 105 CFU in 20 L PBS), then treated with PBS (control group), CDs, Plys and CD-Plys, respectively. The wound was covered with sterile gauze, and all the above operations were performed under pentobarbital anesthesia. In addition, the camera was used to record the pictures of wound, and the data were analyzed with image J software at 0, 3, 5, and 7 days after treatment. The closure rate of wound in the four groups at each time point was calculated by the formula:
A0 represents the initial wound area and At represents the residual wound area at each time point.
Skin colony counting method
One days after treatment, the wound tissues were harvested and soaked in sterile saline (1 mL) to obtain the bacteria containing solutions. Aliquots of diluted samples were placed on agar for the growth of bacteria and the colonies were counted for analysis after the solutions were cultured at 37 °C.
Histological analysis
After 7 days of treatment, all the mice were sacrificed, and the tissues of the wound skins were harvested. The photographs of hematoxylin and eosin (H&E) stained sections were taken by using an optical microscope (Nikon, Japan).
Results and discussion
Synthesis and in vitro antibacterial activities of CDs
CDs were synthesized from various volume ratio of GA and PEG200 via solvothermal method at 150 °C for 140 min (see supporting information). As a proof of concept, we selected E. coli and S. aureus as models for Gram-negative and Gram-positive bacteria to estimate the antibacterial activities of CDs via bacterial growth inhibition assays. As shown in Fig. 1a, b, the growth of E. coli and S. aureus was determined by the dose of CDs, the bacterial viability gradually decreased with concentrations increasing from 8 to 16, 32, 64, 128, and 256 μg/mL. CD110 could partly inhibit the proliferation of E. coli and and S. aureus until the concentration was up to 256 and 64 μg/mL, respectively. By contrast, CD1100 exhibited no bacteriostatic effect within the experimental concentration range (Additional file 1: Fig. S2 and S3). Among the CDs, CD31 exhibited the strongest bactericidal activity and its antibacterial activity was further estimated by colony-forming unit (CFU) counting assay. As depicted in Fig. 1c, the number of colonies of the two strains apparently decreased with the concentrations of CD31 rising from 8 to 256 μg/mL. The minimum inhibitory concentration (MIC) of CD31 against E. coli and S. aureus was 64 and 32 μg/mL, respectively, demonsreating CD31 is a broad-spectrum and efficient sterilant. The antibacterial efficacy of Plys was assessed in a similar way, the survival rate of E. coli and S. aureus lowered with increasing the dose of Plys (Additional file 1: Fig. S4), and the MIC of Plys toward the two bacterial strains was 128 µg/mL (Additional file 1: Fig. S5). The cytocompatibility of CD31 (Additional file 1: Fig. S6) and Plys (Additional file 1: Fig. S7) was evaluated toward L929 cells by MTT assay. All of the cell viabilities were over 89%, even the concentration was as high as 400 µg/mL, verifying both CD31 and Plys have favorable biocompatibility. Robust bactericidal activities as well as excellent biocompatibility make CD31 and Plys great candidates for antibacteria.
In vitro antibacterial assay of CDs. Antimicrobial assay of CDs against a E. coli and b S. aureus. Data expressed as mean ± SD (n = 3), *P < 0.05; **P < 0.01; ***P < 0.001. P values represent the outcome of Multiple Comparisons in Analysis of Variance (ANOVA). c LB agar plates of E. coli or S. aureus inoculated with CD31 for 2 h
Characterization of CD31
Transmission electron microscopy (TEM) image (Fig. 2a) displays that CD31 is spherical with the average diameter of 6.96 ± 0.3 nm. CD31 has broad absorption in the UV–vis region with two typical absorption band at 233 nm and 292 nm (Additional file 1: Additional file 1: Fig. S8), the former is ascribed to π-π* transition (C = C) and the latter corresponds to n-π* transition (C = O). The emission spectra of CD31 (Additional file 1: Fig. S9a) indicate that CD31 has the maximum emission at 483 nm under the optimal excitation of 400 nm. Fourier transform infrared (FT-IR) spectrum (Additional file 1: Fig. S10) of CD31 exhibit peaks at 3000–2800 cm−1 (–OH and –CH2), ~ 1700 cm−1 (–CHO) and ~ 1100 cm−1 (–C–O). The X-ray diffraction pattern (XRD) of CD31 is depicted in Additional file 1: Fig. S11, and the peak centered at 24.2° confirms the crystalline feature of CD31.
a TEM analysis of CD31. The insert is the size distribution of CD31. b SEM image of CD-Plys hydrogel. Scale bar: 200 nm. c Photographs of the Plys solution (400 mg/mL), the CD31 solution (200 mg/mL), and CD-Plys hydrogel (Plys = 400 mg/mL, CD31 = 200 mg/mL) at room temperature. d The injectability of CD-Plys hydrogel under d natural light and e UV (365 nm) light. f Self-healing performance of CD-Plys hydrogel. g Frequency sweep measurement for CD-Plys hydrogel. h Strain sweep measurement for CD-Plys hydrogel at fixed angular frequency of 1 Hz. i Hemolytic activity of CD-Plys hydrogel
Synthesis and characterization of CD-Plys hydrogel
The gelation process of CD-Plys was shown in Fig. 1c, the aqueous solution of Plys (400 mg/mL) was mixed with CD31 aqueous solution at a mass ratio of 2:1. The mixture of Plys and CD31 stood at room temperature for 40 min. In the process, the aldehyde groups on CD31 covalently linked the amino groups of Plys via Schiff-base reaction to form CD-Plys hydrogel, and the hydrogel viscosity was verified by the method from “stable to inversion” (Fig. 2c). The emission spectra of CD-Plys hydrogel are shown in Additional file 1: Fig. S9b, the maximum emission of CD-Plys is observed at 530 nm, which is red-shifted by 45 nm with respect to that of CDs. FT-IR spectra were conducted to elucidate the formation of CD-Plys hydrogel (Additional file 1: Fig. S10). The FT-IR spectrum of CD-Plys hydrogel has the characteristic vibration of imine bonds (1658 cm−1), along with the weakening of characteristic peak (1700 cm−1) of aldehyde groups, indicating the successful conjugation of the aldehyde groups in CD31 with the amino groups in Plys. The XRD spectrum of Plys presents a strong spike at 27.4° and a broad band at 40.3°, while CD-Plys has two broad characteristic peaks at 25.8° and 39.5° (Additional file 1: Fig. S11), verifying that CD-Plys was resoundingly synthesized from CD31 and Plys. The zeta potential of CD31, Plys and CD-Plys is -9.0, 9.29 and 9.18 mV, respectively, further proving the successful preparation of CD-Plys hydrogel (Additional file 1: Fig. S12).
The scanning electron microscopy (SEM) analysis reveals that CD-Plys hydrogel possesses porous structure, which can be attributed to the interwoven network between CD31 and Plys (Fig. 2b). The inherent porous structure of CD-Plys hydrogel can significantly enhance the area of contact with wound, and quickly absorb blood and tissue exudates. In addition, extrusion experiment was carried out to assess the injectability of CD-Plys gel. As shown in Fig. 2d and1e, CD-Plys hydrogel could be continuously injected on the glass slide through the syringe needle, wrote the letter “CCUT” (referring to Changchun University of Technology) and “CIAC” (referring to Changchun Institute of Applied Chemistry). The photographs in Fig. 2f demonstrate the self-repairing properties of CD-Plys hydrogel. The cutted two pieces could fuse together within 30 min after they touched with each other. Since imine bonds in the network are reversible, CD-Plys could be cut in half readily. Once these two fragments are in contact with each other, the amino groups on the fracture surface will react quickly with the contacted aldehyde groups and regenerate imine bonds, to reconfigure the hydrogel matrix for self-repairing, thereby inducing the robust self-healing capability of CD-Plys. Rheological analysis under different frequencies and strains was carried out in order to verify the mechanical property of CD-Plys. As depicted in Fig. 2g, the storage modulus (G') values are much higher than the loss modulus (G'') in the the whole frequency sweep range, confirming that CD-Plys does possess a well-developed 3D network. As the frequency increases, the maximum G' value reaches 3.3 kpa, indicating that CD-Plys has relatively high mechanical strength. Furthermore, we investigated the thixotropic behavior of CD-Plys by a dynamic rheometer. Figure 2h shows that the hydrogel structure of CD-Plys is not broken until the strain exceeds 400%. The hemolytic toxicity of CD-Plys was evaluated toward red blood cells (RBCs) and shown in Fig. 2i and Additional file 1: Fig. S13. Only 1.4% of RBCs lysed in CD-Plys hydrogel group, indicating that CD-Plys has good hemocompatibility. The cytocompatibility of CD-Plys toward L929 cells was assessed by MTT assay (Additional file 1: Fig. S14). The cell viability was over 95% even after direct contact with CD-Plys for 48 h. The excellent biological safety endows CD-Plys hydrogel with great potential in biomedical applications.
In vitro antibacterial of CD-Plys hydrogel
The antibacterial activity of CD-Plys hydrogel against E. coli and S. aureus was assessed by the standard agar disc diffusion assay. When E. coli or S. aureus was treated with CD-Plys hydrogel that prepared from various concentrations (50 or 200 mg/mL) of CDs and Plys (200 mg/mL) at 37 °C for 24 h, distinct inhibition zones were formed (Fig. 3a). For 200 mg/mL of CDs, the zone diameter in E. coli and S. aureus group is about 2.0 ± 0.05 cm and 3.0 ± 0.06 cm, respectively. For 50 mg/mL of CDs, the zone diameter in E. coli group and S. aureus group is about 1.0 ± 0.02 cm and 1.7 ± 0.02 cm, respectively. The results demonstrated CD-Plys had an excellent broad-spectrum antibacterial efficacy against both E. coli and S. aureus and its antibacterial activity was proportional to the concent of CDs. Moreover, CD-Plys exhibits higher antibacterial activity on S. aureus than E. coli. Then the contacting-antibacterial ability of CD-Plys was assessed against E. coli and S. aureus, by coating CD-Plys on the surface of agar plates. The bacteria cultivation without CD-Plys was set as the control. As depicted in Fig. 3b, almost no E. coli or S. aureus colonies were proliferated for the bacterial suspension collected from the substrate coated with CD-Plys, while bacteria colonies were observed obviously for the control group. These results confirm that CD-Plys can be used as a local antibacterial coating with antibacterial effect. In order to further assess the antibacterial activity of CD-Plys, we performed live/dead staining assays by using SYTO 9 green dye and propidium iodide (PI) red dye to stain live and dead bacteria, respectively. E. coli and S. aureus were incubated with CD-Plys for 12 h, and then costained by SYTO 9 and PI. As depicted in Fig. 3c, d, the bacteria in the control groups emitted intense green fluorescence, indicating that they were alive. By contrast, the bacteria in the CD-Plys groups displayed strong red signals, implying that all of them were eradicated by CD-Plys.
In vitro antibacterial assay of CD-Plys hydrogel. a Antibacterial sensitivity of CD-Plys hydrogel against E. coli and S. aureus with agar diffusion tests at 24 h. b LB agar inoculated with uncoated or CD-Plys hydrogel coated substrates. The white dots are colonies of live bacteria in the plates. SYTO 9/PI staining images of E. coli c and S. aureus d treated without/with CD-Plys hydrogel. Scale bar, 20 µm
Antibacterial mechanism of CD31 and CD-Plys
SEM was utilized to study the bacteria’s morphological changes after treatment with CD31 and CD-Plys (Fig. 4). Without treatment, the bacteria had regular shapes with intact membrane and clear edges. After incubation with CD31, the membranes of E. coli shrank and cracked, while S. aureus were disrupted and the cytoplasm outflowed. As we all know, the surface properties of nanoantibiotics directly affect their interaction with bacteria. Although the zeta potential of CD31 was negative, the aldehyde groups could irreversibly destroy the bacterial cell wall and the cytoplasmic membrane, eventually leading to the bacterial death. As for the bacteria treated with CD-Plys, more serious phenomena of shrinkage, collapse, cracking, fusing together and leakage of intracellular components were observed, verifying that CD-Plys could seriously damaged the bacterial cells.
SEM images of E. coli and S. aureus treated with CD31 and CD-Plys. Bacteria without treatment were set as controls
In vivo antibacterial and skin wound healing of CD-Plys hydrogel
The favorable antibacterial capacity and good cytocompatibility of CD-Plys encouraged us to evaluate the bacteria inhibition and wound healing efficiency of CD-Plys in vivo. Full-thickness wound defect models with round skin injuries (8 mm in diameter) were created on the back of mice. Afterward, 48 mice were randomly divided into 8 groups. Mice in the four groups were infected by E. coli, while the others were infected by S. aureus. The wound healing processes under different conditions were monitored (Fig. 5a, b), and traces of wound closure were drawn during 7 days of treatment (Fig. 5c). The wound healing rates at 3, 5, and 7 days were evaluated and depicted in Fig. 5d, e. For all of these mice, the wound size decreased gradually with time. On the third day, the epidermis of infected wounds in the two CD-Plys groups began to regenerate. On the seventh day, the two groups mice treated with CD-Plys exhibited the best wound healing, the wound were nearly closed with the healing rate of 90% (E. coli) and 92% (S. aureus), respectively, moreover, a lot of hair grew out. The results confirmed that the enhanced antibacterial activity of CD-Plys was the synergistic effect of CD31 and Plys, which could significantly accelerate skin wound closure and tissue regeneration.
In vivo infected wound healing evaluation. a Time-dependent images of E. coli infected wounds. b Time-dependent images of S. aureus infected wounds. c Traces of wound area during 7 days of treatments (0 days: red pattern; 3 days: blue pattern; 5 days: yellow pattern; 7 days: green pattern). Wound healing rate of d E. coli or e S. aureus infected wound at different time points, data are presented as mean with standard deviation as error bars (n = 6)
After 24 h of treatment, the residual bacteria were extracted from the wound tissue, incubated with LB medium for 24 h, and then measured by standard plate counting methods (Fig. 6a). There were nearly no bacterial colonies in the wound tissues those were treated with CDs, Plys or CD-Plys hydrogel. The statistical analysis of Fig. 6a was shown in Fig. 6b (E. coli) and Fig. 6c (S. aureus), respectively. The results suggest that CD-Plys hydrogel exhibits the strongest antibacterial capability.
In vivo assessment of CD-Plys hydrogel with antibacterial effects on infected wounds and skin wound healing capability. a The E. coli and S. aureus bacteria were obtained from wound tissues and incubated on LB agar plates. The percentage of b E. coli and c S. aureus colonies appeared on the LB agar plate to the control groups (n = 6)
Histological analysis was used to evaluate the quality of regenerated wound tissue. After 7 days of treatment, the tissues were dissected and stained with hematoxylin and eosin (H&E) (Fig. 7). E. coli and S. aureus infected tissues in the control groups showed severe inflammatory cell infiltration. For CD31 and Plys groups, a few new blood vessels and hair follicles were observed. The CD-Plys groups exhibit the well-organized lamellar epithelium and orderly granulation tissue, with a large number of new blood vessels and hair follicles. The results of tissue sections indicated that CD-Plys could be used as an effective wound dressing material for treatment of bacterial infections and facilitating skin wound healing process.
H&E stained images of skin tissues treated with PBS, CD31, Plys and CD-Plys, respectively. (blood vessels: yellow arrows; hair follicles: blue arrows). Scale bar: 200 µm
Conclusions
All in all, negatively charged CD31 with potent antimicrobial activity was synthesized from GA and PEG200, which could effectively destroy E. coli and S. aureus with MIC of 64 and 32 μg/mL, respectively. Then CD31 reacted with Plys to fabricate CD-Plys hydrogel. CD-Plys could integrate the favorable attributes from CD31 and Plys, and achieve synergy antibacterial effect of “one plus one greater than two”. Combined with the fascinating features of favorable injectability, eximious self-healing, excellent biocompatibility and exceptional broad-spectrum antimicrobial activity, CD-Plys could significantly promote full-thickness cutaneous wound healing with accelerated wound closure and improved skin regeneration. Overall, this study provides a new strategy for fabricating outstanding antibacterial wound dressing to efficiently promote the healing of microbial infection wounds.
Availability of data and materials
Availability of data and materials is available from the journal or from the author.
References
Millan RCMAS. The evolution of antibiotic resistance. Science. 2019;365(6458):1082–3.
Chatterjee A, Modarai M, Naylor NR, Boyd SE, Atun R, Barlow J, Holmes AH, Johnson A, Robotham JV. Quantifying drivers of antibiotic resistance in humans: a systematic review. The Lancet. 2018;18(12):368–78.
Chellat MF, Raguz L, Riedl R. Targeting antibiotic resistance. Angew Chem Int Ed. 2016;55(23):6600–26.
Cao C, Ge W, Yin J, Yang D, Wang W, Song X, Hu Y, Yin J, Dong X. Mesoporous silica supported silver-bismuth nanoparticles as photothermal agents for skin infection synergistic antibacterial therapy. Small. 2020;16(24):2000436.
Wu M, Ma B, Pan T, Chen S, Sun J. Silver-nanoparticle-colored cotton fabrics with tunable colors and durable antibacterial and self-healing superhydrophobic properties. Adv Funct Mater. 2016;26(4):569–76.
Cai T, Fang G, Tian X, Yin JJ, Chen C, Ge C. Optimization of antibacterial efficacy of noble-metal-based core-shell nanostructures and effect of natural organic matter. ACS Nano. 2019;13(11):12694–702.
Xie Y, Yang J, Zhang J, Zheng W, Jiang X. Activating antibacterial effect of 4,6-diamino-2-pyrimidinethiol-modified gold nanoparticles by reducing their sizes. Angew Chem Int Ed. 2020;59(52):23471–5.
Weng C, Shen L, Ang WH. Harnessing endogenous formate for antibacterial prodrug activation by in cellulo ruthenium-mediated transfer hydrogenation reaction. Angew Chem Int Ed. 2020;59(24):9314–8.
Deng T, Zhao H, Shi M, Qiu Y, Jiang S, Yang X, Zhao Y, Zhang Y. Photoactivated trifunctional platinum nanobiotics for precise synergism of multiple antibacterial modes. Small. 2019;15(46):1902647.
Linklater DP, Baulin VA, Le Guevel X, Fleury JB, Hanssen E, Nguyen THP, Juodkazis S, Bryant G, Crawford RJ, Stoodley P, Ivanova EP. Antibacterial action of nanoparticles by lethal stretching of bacterial cell membranes. Adv Mater. 2020;32(52):2005679.
Xie X, Sun T, Xue J, Miao Z, Yan X, Fang W, Li Q, Tang R, Lu Y, Tang L, Zha Z, He T. Ag nanoparticles cluster with pH-triggered reassembly in targeting antimicrobial applications. Adv Funct Mater. 2020;30(17):2000511.
Ivanova A, Ivanova K, Tied A, Heinze T, Tzanov T. Layer-by-layer coating of aminocellulose and quorum quenching acylase on silver nanoparticles synergistically eradicate bacteria and their biofilms. Adv Funct Mater. 2020;30(24):2001284.
Zhou Y, Guo Y, Li J, Wei W, Li D, Luo L, Xu X, Zhou Z. Excellent antibacterial activities in the dark of ZnO nanoflakes with oxygen vacancies on exposed facets. J Mater Chem A. 2020;8(23):11511–4.
Wang R, Shi M, Xu F, Qiu Y, Zhang P, Shen K, Zhao Q, Yu J, Zhang Y. Graphdiyne-modified TiO2 nanofibers with osteoinductive and enhanced photocatalytic antibacterial activities to prevent implant infection. Nat Commun. 2020;11(1):4465.
Xu J, Zhou X, Gao Z, Song YY, Schmuki P. Visible-light-triggered drug release from TiO2 nanotube arrays: a controllable antibacterial platform. Angew Chem Int Ed. 2016;55(2):593–7.
Li X, Liang M, Jiang S, Cao S, Li S, Gao Y, Liu J, Bai Q, Sui N, Zhu Z. Pomegranate-like CuO2@SiO2 nanospheres as H2O2 Self-supplying and robust oxygen generators for enhanced antibacterial activity. ACS Appl Mater Interfaces. 2021;13(19):22169–81.
Xi J, Wei G, An L, Xu Z, Xu Z, Fan L, Gao L. Copper/Carbon hybrid nanozyme: tuning catalytic activity by the copper state for antibacterial therapy. Nano Lett. 2019;19(11):7645–54.
Zheng K, Li K, Chang TH, Xie J, Chen PY. Synergistic antimicrobial capability of magnetically oriented graphene oxide conjugated with gold nanoclusters. Adv Funct Mater. 2019;29(46):1904603.
Kong X, Liu X, Zheng Y, Chu PK, Zhang Y, Wu S. Graphitic graphitic carbon nitride-based materials for photocatalytic antibacterial application. Mat Sci Eng R. 2021;145:100610.
Xin Q, Shah H, Nawaz A, Xie W, Akram MZ, Batool A, Tian L, Jan SU, Boddula R, Guo B, Liu Q, Gong JR. Antibacterial carbon-based nanomaterials. Adv Mater. 2019;31(45):1804838.
Su Y, Liu S, Guan Y, Xie Z, Zheng M, Jing X. Renal clearable hafnium-doped carbon dots for CT/Fluorescence imaging of orthotopic liver cancer. Biomaterials. 2020;255:120110.
Zheng M, Li Y, Liu S, Wang W, Xie Z, Jing X. One-pot to synthesize multifunctional carbon dots for near infrared fluorescence imaging and photothermal cancer therapy. ACS Appl Mater Interfaces. 2016;8(36):23533–41.
Zheng M, Ruan S, Liu S, Sun T, Qu D, Zhao H, Xie Z, Gao H, Jing X, Sun Z. Self-targeting fluorescent carbon dots for diagnosis of brain cancer cells. ACS Nano. 2015;9(11):11455–61.
Zhang J, Zheng M, Zhang F, Xu B, Tian W, Xie Z. Supramolecular hybrids of AIEgen with carbon dots for noninvasive long-term bioimaging. Chem Mater. 2016;28(23):8825–33.
Hua XW, Bao YW, Zeng J, Wu FG. Nucleolus-targeted red emissive carbon dots with polarity-sensitive and excitation-independent fluorescence emission: high-resolution cell imaging and in vivo tracking. ACS Appl Mater Interfaces. 2019;11(36):32647–58.
Liu J, Li D, Zhang K, Yang M, Sun H, Yang B. One-step hydrothermal synthesis of nitrogen-doped conjugated carbonized polymer dots with 31% efficient red emission for in vivo imaging. Small. 2018;14(15):1703919.
Feng Q, Zheng M, Xie Z. Room temperature phosphorescent carbon dots for latent fingerprints detection and in vivo phosphorescence bioimaging. Sensor Actuat B-Chem. 2021;35: 130976.
Wang B, Lu S. The light of carbon dots: from mechanism to applications. Matter. 2021;5(1):110–49.
Ai L, Yang Y, Wang B, Chang J, Tang Z, Yang B, Lu S. Insights into photoluminescence mechanisms of carbon dots: advances and perspectives. Sci Bull. 2021;66(8):839–56.
Yang X, Sui L, Wang B, Zhang Y, Tang Z, Yang B, Lu S. Red-emitting, self-oxidizing carbon dots for the preparation of white LEDs with super-high color rendering index. Sci China Chem. 2021;64(9):1547–53.
Wang B, Cai H, Waterhouse GI, Qu X, Yang B, Lu S. Carbon dots in bioimaging biosensing and therapeutics: a comprehensive review. Small Sci. 2022;2(6):2200012. https://doi.org/10.1002/smsc.202200012.
Gao P, Wang J, Zheng M, Xie Z. Lysosome targeting carbon dots-based fluorescent probe for monitoring pH changes in vitro and in vivo. Chem Eng J. 2020;381:122665.
Gao P, Xie Z, Zheng M. Chiral carbon dots-based nanosensors for Sn(II) detection and lysine enantiomers recognition. Sen Actuat. 2020;319:128265.
Zheng M, Xie Z, Qu D, Li D, Du P, Jing X, Sun Z. On-off-on fluorescent carbon dot nanosensor for recognition of chromium(VI) and ascorbic acid based on the inner filter effect. ACS Appl Mater Interfaces. 2013;5(24):13242–7.
Gao P, Liu S, Su Y, Zheng M, Xie Z. Fluorine-doped carbon dots with intrinsic nucleus-targeting ability for drug and dye delivery. Bioconjug Chem. 2020;31(3):646–55.
Pan L, Sun S, Zhang A, Jiang K, Zhang L, Dong C, Huang Q, Wu A, Lin H. Truly fluorescent excitation-dependent carbon dots and their applications in multicolor cellular imaging and multidimensional sensing. Adv Mater. 2015;27(47):7782–7.
Gao P, Xie Z, Zheng M. Small nanoparticles bring big prospect: the synthesis, modification, photoluminescence and sensing applications of carbon dots. Chin Chem Lett. 2022;33:1659–72.
Lu S, Li Z, Fu X, Xie Z, Zheng M. Carbon dots-based fluorescence and UV–vis absorption dual-modal sensors for Ag+ and l-cysteine detection. Dyes Pigm. 2021;187: 109126.
Liu J, Li R, Yang B. Carbon dots: a new type of carbon-based nanomaterial with wide applications. ACS Cent Sci. 2020;6(12):2179–95.
Hou L, Chen D, Wang R, Wang R, Zhang H, Zhang Z, Nie Z, Lu S. Transformable honeycomb-like nanoassemblies of carbon dots for regulated multisite delivery and enhanced antitumor chemoimmunotherapy. Angew Chem Int Ed. 2021;60(12):6581–92.
Wang B, Song H, Qu X, Chang J, Yang B, Lu S. Carbon dots as a new class of nanomedicines: opportunities and challenges. Coord Chem Rev. 2021;442:214010.
Chen S, Sun T, Zheng M, Xie Z. Carbon dots based nanoscale covalent organic frameworks for photodynamic therapy. Adv Funct Mater. 2020;30(43):2004680.
Su Y, Lu S, Gao P, Zheng M, Xie Z. BODIPY@carbon dot nanocomposites for enhanced photodynamic activity. Mater Mater Chem Front. 2019;3(9):1747–53.
Zheng M, Liu S, Li J, Qu D, Zhao H, Guan X, Hu X, Xie Z, Jing X, Sun Z. Integrating oxaliplatin with highly luminescent carbon dots: an unprecedented theranostic agent for personalized medicine. Adv Mater. 2014;26(21):3554–60.
Jia Q, Ge J, Liu W, Zheng X, Chen S, Wen Y, Zhang H, Wang P. A magnetofluorescent carbon dot assembly as an acidic H2O2 -driven oxygenerator to regulate tumor hypoxia for simultaneous bimodal imaging and enhanced photodynamic therapy. Adv Mater. 2018;30(13):1706090.
Li J, Yang S, Deng Y, Chai P, Yang Y, He X, Xie X, Kang Z, Ding G, Zhou H, Fan X. Emancipating target-functionalized carbon dots from autophagy vesicles for a novel visualized tumor therapy. Adv Funct Mater. 2018;28(30):1800881.
Yu Y, Song M, Chen C, Du Y, Li C, Han Y, Yan F, Shi Z, Feng S. Bortezomib-encapsulated CuS/Carbon dot nanocomposites for enhanced photothermal therapy via stabilization of polyubiquitinated substrates in the proteasomal degradation pathway. ACS Nano. 2020;14(8):10688–703.
Sun S, Chen Q, Tang Z, Liu C, Li Z, Wu A, Lin H. Tumor microenvironment stimuli-responsive fluorescence imaging and synergistic cancer therapy by carbon-dot-Cu(2+) nanoassemblies. Angew Chem Int Ed. 2020;59(47):21041–8.
Zhang X, Chen X, Guo Y, Gao G, Wang D, Wu Y, Liu J, Liang G, Zhao Y, Wu FG. Dual gate-controlled therapeutics for overcoming bacterium-induced drug resistance and potentiating cancer immunotherapy. Angew Chem Int Ed. 2021;60(25):14013–21.
Gao P, Chen S, Liu S, Liu H, Xie Z, Zheng M. Chiral carbon dots-enzyme nanoreactors with enhanced catalytic activity for cancer therapy. ACS Appl Mater Interfaces. 2021;13(47):56456–64.
Yang J, Gao G, Zhang X, Ma Y-H, Chen X, Wu F-G. One-step synthesis of carbon dots with bacterial contact-enhanced fluorescence emission: fast gram-type identification and selective gram-positive bacterial inactivation. Carbon. 2019;146:827–39.
Ye Z, Li G, Lei J, Liu M, Jin Y, Li B. One-step and one-precursor hydrothermal synthesis of carbon dots with superior antibacterial activity. ACS Appl Bio Mater. 2020;3(10):7095–102.
Dong X, Ge L, Abu Rabe DI, Mohammed OO, Wang P, Tang Y, Kathariou S, Yang L, Sun Y-P. Photoexcited state properties and antibacterial activities of carbon dots relevant to mechanistic features and implications. Carbon. 2020;170:137–45.
Meziani MJ, Dong X, Zhu L, Jones LP, LeCroy GE, Yang F, Wang S, Wang P, Zhao Y, Yang L, Tripp RA, Sun YP. Visible-light-activated bactericidal functions of carbon “Quantum” dots. ACS Appl Mater Interfaces. 2016;8(17):10761–6.
Huang H, Anand A, Lin C, Lin H, Lin Y, Harroun S, Huang C. LED irradiation of halogen/nitrogen-doped polymeric graphene quantum dots triggers the photodynamic inactivation of bacteria in infected wounds. Carbon. 2021;174:710–22.
Zhang M, Zhai X, Ma T, Huang Y, Yan C, Du Y. Multifunctional cerium doped carbon dots nanoplatform and its applications for wound healing. Chem Eng J. 2021;423(1):130301.
Sun H, Gao N, Dong K, Ren J, Qu X. Graphene quantum dots-band-aids used for wound disinfection. ACS Nano. 2014;8(6):6202–10.
Sun B, Wu F, Zhang Q, Chu X, Wang Z, Huang X, Li J, Yao C, Zhou N, Shen J. Insight into the effect of particle size distribution differences on the antibacterial activity of carbon dots. J Colloid Interf Sci. 2020;584:505–19.
Yang J, Zhang X, Ma YH, Gao G, Chen X, Jia HR, Li YH, Chen Z, Wu FG. Carbon dot-based platform for simultaneous bacterial distinguishment and antibacterial applications. ACS Appl Mater Interfaces. 2016;8(47):32170–81.
Zhao C, Wang X, Yu L, Wu L, Hao X, Liu Q, Lin L, Huang Z, Ruan Z, Weng S, Liu A, Lin X. Quaternized carbon quantum dots with broad-spectrum antibacterial activity for the treatment of wounds infected with mixed bacteria. Acta Biomater. 2022;138:528–44.
Jian HJ, Wu RS, Lin TY, Li YJ, Lin HJ, Harroun SG, Lai JY, Huang CC. Super-cationic carbon quantum dots synthesized from spermidine as an eye drop formulation for topical treatment of bacterial keratitis. ACS Nano. 2017;11(7):6703–16.
Zhang H, Sun X, Wang J, Zhang Y, Dong M, Bu T, Li L, Liu Y, Wang L. Multifunctional injectable hydrogel dressings for effectively accelerating wound healing: enhancing biomineralization strategy. Adv Funct Mater. 2021;31(23):2100093.
Fan L, Duan M, Xie Z, Pan K, Wang X, Sun X, Wang Q, Rao W, Liu J. Injectable and radiopaque liquid metal/calcium alginate hydrogels for endovascular embolization and tumor embolotherapy. Small. 2020;16(2):1903421.
Shi L, Wang F, Zhu W, Xu Z, Fuchs S, Hilborn J, Zhu L, Ma Q, Wang Y, Weng X, Ossipov DA. Self-healing silk fibroin-based hydrogel for bone regeneration: dynamic metal-ligand self-assembly approach. Adv Funct Mater. 2017;27(37):1700591.
Wang F, Feng CL. Metal-ion-mediated supramolecular chirality of l-phenylalanine based hydrogels. Angew Chem Int Ed. 2018;57(20):5655–9.
Xu X, Jerca FA, Jerca VV, Hoogenboom R. Covalent poly(2-isopropenyl-2-oxazoline) hydrogels with ultrahigh mechanical strength and toughness through secondary terpyridine metal-coordination crosslinks. Adv Funct Mater. 2019;29(48):1904886.
Zang X, Hohman JN, Yao K, Ci P, Yan A, Wei M, Hayasaka T, Zettl A, Schuck PJ, Wu J, Lin L. Metallo-hydrogel-assisted synthesis and direct writing of transition metal dichalcogenides. Adv Funct Mater. 2019;29(27):1807612.
Hu Q, Li G, Liu X, Zhu B, Chai X, Zhang Q, Liu J, He C. Superhydrophilic phytic-acid-doped conductive hydrogels as metal-free and binder-free electrocatalysts for efficient water oxidation. Angew Chem Int Ed. 2019;58(13):4318–22.
Li M, Liang Y, He J, Zhang H, Guo B. Two-pronged strategy of biomechanically active and biochemically multifunctional hydrogel wound dressing to accelerate wound closure and wound healing. Chem Mater. 2020;32(23):9937–53.
Kim B, Na J, Lim H, Kim Y, Kim J, Kim E. Robust high thermoelectric harvesting under a self-humidifying bilayer of metal organic framework and hydrogel layer. Adv Funct Mater. 2019;29(7):1807549.
Wang L, Xu H, Gao J, Yao J, Zhang Q. Recent progress in metal-organic frameworks-based hydrogels and aerogels and their applications. Coordin Chem Rev. 2019;398:213016.
Guo X, Xu D, Yuan H, Luo Q, Tang S, Liu L, Wu Y. A novel fluorescent nanocellulosic hydrogel based on carbon dots for efficient adsorption and sensitive sensing in heavy metals. J Mater Chem A. 2019;7(47):27081–8.
Pandey PK, Preeti RK, Prasad T, Bohidar HB. Multifunctional, fluorescent DNA-derived carbon dots for biomedical applications: bioimaging, luminescent DNA hydrogels, and dopamine detection. J Mater Chem. 2020;8(6):1277–89.
Won HJ, Ryplida B, Kim SG, Lee G, Ryu JH, Park SY. Diselenide-bridged carbon-dot-mediated self-healing, conductive, and adhesive wireless hydrogel sensors for label-free breast cancer detection. ACS Nano. 2020;14(7):8409–20.
Singh S, Jelinek R. Sunlight-activated phase transformation in carbon dothydrogel facilitates water purification and optical switching. ACS Appl Polym Mater. 2020;2:2810–8.
Nayak S, Prasad SR, Mandal D, Das P. Carbon dot cross-linked polyvinylpyrrolidone hybrid hydrogel for simultaneous dye adsorption, photodegradation and bacterial elimination from waste water. J Hazard Mater. 2020;392: 122287.
Lu Z, Liu S, Le Y, Qin Z, He M, Xu F, Zhu Y, Zhao J, Mao C, Zheng L. An injectable collagen-genipin-carbon dot hydrogel combined with photodynamic therapy to enhance chondrogenesis. Biomaterials. 2019;218:119190.
Wei JS, Ding C, Zhang P, Ding H, Niu XQ, Ma YY, Li C, Wang YG, Xiong HM. Robust negative electrode materials derived from carbon dots and porous hydrogels for high-performance hybrid supercapacitors. Adv Mater. 2019;31(5):1806197.
Zi Y, Zhu M, Li X, Xu Y, Wei H, Li D, Mu C. Effects of carboxyl and aldehyde groups on the antibacterial activity of oxidized amylose. Carbohydr Polym. 2018;192:118–25.
Luo H, Lan H, Cha R, Yu X, Gao P, Zhang P, Zhang C, Han L, Jiang X. Dialdehyde nanocrystalline cellulose as antibiotic substitutes against multidrug-resistant bacteria. ACS Appl Mater Interfaces. 2021;13:33802–11.
Acknowledgements
Not applicable.
Funding
The financial support from the National Natural Science Foundation of China (No. 51873023), the Science and Technology Development Plan of Changchun City (No. 21ZY38).
Author information
Authors and Affiliations
Contributions
CM: Methodology, investigation, software, writing-original draft. XW: Methodology, investigation. JT: Investigation. ZX: Conceptualization, resources, supervision, writing—review & editing. MZ: Conceptualization, resources, supervision, writing—review & editing, data curation. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Ethics approval and consent to participate
This work has received approval for research ethics from Changchun Institute of Applied Chemistry Chinese Academy of Sciences and a proof of approval (No. 2022–0006) is available upon request.
Consent for publication
Not applicable.
Competing interests
The authors declare no conflicts of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Additional file 1: Figure S1.
Zeta potential of CDs. Figure S2. Antimicrobial assay of CD110 and CD1100 against E. coli. Figure S3. Antimicrobial assay of CD110 and CD1100 against S. aureus. Figure S4. Antimicrobial assay of Plys toward E. coli and S. aureus. Figure S5. Antimicrobial assay of Plys toward S. aureus with LB agar. Figure S6. MTT assay of CD31 toward L929 cells. Figure S7. MTT assay of Plys toward L929 cells. Figure S8. UV-vis spectrum of CD31 in deionized water. Figure S9. Photoluminescent spetra of (a) CD31 aqueous solution and (b) CD-Plys under the excitation of different wavelengths. Figure S10. FT-IR spectra of CD31 (black solid line), Plys (red solid line) and CD-Plys (blue solid line). Figure S11. The X-ray diffraction pattern of CD31 (black), Plys (red) and CD-Plys hydrogel (blue). Figure S12. Zeta potentials of CD31, Plys and CD-Plys hydrogel. Figure S13. The hemolysis assay of PBS, CD-Plys and Triton X-100. Figure S14. MTT assay of CD-Plys with direct contact with L929 cells for 12, 24 and 48 h.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.
About this article
Cite this article
Mou, C., Wang, X., Teng, J. et al. Injectable self-healing hydrogel fabricated from antibacterial carbon dots and ɛ-polylysine for promoting bacteria-infected wound healing. J Nanobiotechnol 20, 368 (2022). https://doi.org/10.1186/s12951-022-01572-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s12951-022-01572-w