Abstract
Background
Large bone defects have always been a great challenge for orthopedic surgeons. The use of a good bone substitute obtained by bone tissue engineering (BTE) may be an effective treatment method. Artificial hydroxyapatite, a commonly used bone defect filler, is the main inorganic component of bones. Because of its high brittleness, fragility, and lack of osteogenic active elements, its application is limited. Therefore, its fragility should be reduced, its osteogenic activity should be improved, and a more suitable scaffold should be constructed.
Methods
In this study, a microhydroxyapatite whisker (mHAw) was developed, which was doped with the essential trace active elements Mg2+ and Sr2+ through a low-temperature sintering technique. After being formulated into a slurry, a bionic porous scaffold was manufactured by extrusion molding and freeze drying, and then SiO2 was used to improve the mechanical properties of the scaffold. The hydrophilicity, pore size, surface morphology, surface roughness, mechanical properties, and release rate of the osteogenic elements of the prepared scaffold were detected and analyzed. In in vitro experiments, Sprague–Dawley (SD) rat bone marrow mesenchymal stem cells (rBMSCs) were cultured on the scaffold to evaluate cytotoxicity, cell proliferation, spreading, and osteogenic differentiation.
Results
Four types of scaffolds were obtained: mHAw-SiO2 (SHA), Mg-doped mHAw-SiO2 (SMHA), Sr-doped mHAw-SiO2 (SSHA), and Mg-Sr codoped mHAw-SiO2 (SMSHA). SHA was the most hydrophilic (WCA 5°), while SMHA was the least (WCA 8°); SMHA had the smallest pore size (247.40 ± 23.66 μm), while SSHA had the largest (286.20 ± 19.04 μm); SHA had the smallest Young's modulus (122.43 ± 28.79 MPa), while SSHA had the largest (188.44 ± 47.89 MPa); and SHA had the smallest compressive strength (1.72 ± 0.29 MPa), while SMHA had the largest (2.47 ± 0.25 MPa). The osteogenic active elements Si, Mg, and Sr were evenly distributed and could be sustainably released from the scaffolds. None of the scaffolds had cytotoxicity. SMSHA had the highest supporting cell proliferation and spreading rate, and its ability to promote osteogenic differentiation of rBMSCs was also the strongest.
Conclusions
These composite porous scaffolds not only have acceptable physical and chemical properties suitable for BTE but also have higher osteogenic bioactivity and can possibly serve as potential bone repair materials.
Similar content being viewed by others
Background
Bones are the main supports and structures for movement in the human body and can provide protective spaces for the brain, heart, lungs, liver, and other organs. Bones also possess a robust regenerative capacity and can regenerate completely under the appropriate conditions after they are broken or slightly injured. Bone healing consists of three continuous and partially overlapping processes [1]. In the first stage, immunoregulation, stem cell recruitment, and chondrogenesis occur. In the second stage, cartilage is absorbed, and new bone is formed under the combined action of osteoclasts and osteoblasts. In the third stage, the newly formed remodeled bone returns to normal, and the repair is complete. However, when a bone defect is too large to heal itself, it is called a large-size or critical-size bone defect, and the repair process cannot be spontaneously completed.
Large bone defects are always caused by severe trauma, tumor removal, infection, or congenital malformation, and reconstruction of these defect sites is a major challenge for orthopedic surgeons and patients [2, 3]. Currently, the main treatment measures for these large bone defects include autogenous bone grafts, allografts, and artificial bone substitutes [3,4,5]. However, the above treatment methods have specific deficiencies during the treatment process. Autografts, as the gold standard, have complications, including an increased surgical site, limited bone mass, bleeding, and additional pain. Allografts frequently pose risks, including immunological rejection and pathophoresis from the donor. Hopefully, bone tissue engineering (BTE) can provide more choices for patients with bone defects, although there is still much to be done to approach or achieve the therapeutic effects of autologous bone. Notably, the application of single materials will always present problems, such as poor mechanical properties, poor osteogenic properties, tumorigenicity, and mismatch between the degradation rate and the rate of new bone formation [5, 6].
Over the past few years, BTE has been used to promote bone regeneration, as substantial efforts and confidence have been placed in scientific research. With the development of new technologies, different types of scaffolds have been established and applied in bone repair, but only a few scaffolds have shown satisfactory results [5, 7, 8]. Long bones are mostly composed of an outer layer of cortical bone and an inner layer of cancellous bone, and the proportion and distribution of cancellous or cortical bone of irregular bones, such as vertebrae and skull, vary according to their functions. The major organic component of natural bone is type I collagen (COL1), and the major inorganic component is hydroxyapatite (HA: Ca10(PO4)6(OH)2) [9], which also contains necessary elements, such as Mg2+, Si4+, and Sr2+, and other metal ions [5, 10,11,12,13].
As the main inorganic component of natural bone, HA has excellent biocompatibility, good cell adhesion, and good osteoconductivity [9, 14,15,16] and can be divided into macroscopic, micron, and nanoscale sizes. Research in recent years has confirmed that, compared with scaffolds based on HA particles, scaffolds based on micron-sized HA during bone repair have better hierarchical porous structures and enhanced mechanical properties as well as improved biological activity and biological responses [18,19,20]. The trace elements Mg2+, Si4+, and Sr2+ in bone also have important osteogenic and vascular functions. Mg has good osteoconductivity and osteoinductivity, promotes vasodilation, sprawling, and new blood vessel formation, increases blood perfusion, and has good tissue affinity. It participates in early osteogenic differentiation, midterm new bone formation, and late bone remodeling [17,18,19]. Mg and Sr also have good biological safety in tissues and the blood and certain antibacterial properties (including resistance to methicillin-resistant Staphylococcus aureus) [20,21,22]. However, its rapid degradation rate limits its applications in orthopedics [23]. Si is nontoxic or has only very low toxicity and shows good biocompatibility, degradability, and biological excretion [24]. Si4+ can recruit bone marrow mesenchymal stem cells (BMSCs) and promote their osteogenic differentiation in the early stage, improve the adhesion and proliferation of osteoblasts, and promote the formation and structural stabilization of COL1. Si4+ can also promote the precipitation and mineralization of the bone matrix in the midterm phase of bone repair. Moreover, angiopoietin-2 is upregulated through the cell signaling pathway to regulate blood vessel formation [5, 25,26,27]. Sr has outstanding antiosteoporosis performance through the inhibition of the differentiation and activity of osteoclasts and has certain osteogenic and strong angiogenic functions, as well as antibacterial properties [28,29,30,31,32,33]. In addition, when multiple ions work together, their bone repair and antibacterial effects are better [9, 12, 31, 34, 35]. An ideal bone repair material should be biocompatible, biodegradable, and nontoxic, has suitable physical properties, and shows good osteogenic and angiogenic abilities [4, 9, 34].
Inspired by the composition and porous structure of natural bone and the osteogenic function of mHAws, including magnesium, strontium, and silica mentioned above, this study aimed to develop a biomimetic porous scaffold as a bone filling material with acceptable mechanical strength, a structure similar to natural bone, and good osteogenesis-promoting effects. Its mechanical strength was closer to that of natural bone enough to support local soft tissues. It had a rough surface microenvironment suitable for cell growth, similar to the porous structure of cancellous bone, and achieved the local sustained release of the osteogenic active elements silicon, magnesium, and strontium. In vitro experiments were performed to verify its cell proliferation and osteogenic differentiation ability.
Results
Fabrication and characterization of the scaffolds
Pure mHAw-, Mg-doped mHAw-, Sr-doped mHAw-, and Mg-Sr codoped mHAw were successfully synthesized. Scanning electron microscopy (SEM) observations and analysis showed that the lengths of the prefabricated mHAws ranged from a few microns to tens of microns, while the mHAws were several microns in diameter (Fig. 1a). The SHA, SMHA, SSHA, and SMSHA scaffolds were prepared according to the mentioned method, as shown in Fig. 9. Briefly, through low-temperature sintering, the doped mHAws were extruded into porous ceramics, complexed with silica to enhance their mechanical strength, and cut to the required size.
Morphologies of the microhydroxyapatite whiskers observed by SEM (a). Hydrophilic images of SHA, SMHA, SSHA, and SMSHA (b–e), respectively. Water contact angles of SHA, SMHA, SSHA, and SMSHA (f). Pore sizes of the four scaffolds (g). Young’s moduli of the four scaffolds (h). The compressive strengths of four scaffolds (i). (n = 5, * P < 0.05, # P > 0.05 compared with SHA)
Hydrophilicity properties
As shown in Fig. 1b–f, the WCAs of the SHA, SMHA, SSHA, and SMSHA scaffolds were 5°, 8°, 6°, and 6° after measurement, respectively. The smaller the WCA, the better the hydrophilicity. The WCAs of the four scaffolds all reflected good hydrophilicity. SHA had the smallest WCA, SMHA had the largest WCA, and SSHA and SMSHA had the same WCA, indicating that the hydrophilicity of the scaffolds will be affected after doping with different ions. These biomaterials had good hydrophilicity, which is conducive to the attachment and growth of cells [36, 37]. As SMHA had the largest WCA, SHA had the smallest WCA, and SSHA and SMSHA (both doped with Sr) had smaller WCAs than SMHA, these results indicate that Sr is more hydrophilic than Mg.
Pore sizes of the scaffold
Since a significant feature of natural bone is its porous structure, the design of the porous structure in ceramic bone scaffolds can provide favorable conditions for bone regeneration. The average pore sizes of SHA, SMHA, SSHA, and SMSHA were 267.20 ± 10.66 μm, 247.40 ± 23.66 μm, 286.20 ± 19.04 μm, and 269.40 ± 33.00 μm, respectively (Fig. 1g). Thus, the pore sizes of the four scaffolds were similar.
Mechanical properties
Compared with natural bone, most of the scaffolds that are developed for bone regeneration have insufficient mechanical properties. Therefore, it is necessary to develop a preparation process to improve the mechanical properties of scaffolds, and material methods and structural improvements have been used to achieve this goal. To reduce the risks of the high brittleness and fragility associated with hydroxyapatite, the prepared pure mHAw, Mg-doped mHAw, Sr-doped mHAw, and Mg-Sr codoped mHAw scaffolds were immersed in silica gel, and the mechanical properties of the scaffolds were found to be enhanced by SiO2 complexation. The Young’s moduli of SHA, SMHA, SSHA, and SMSHA were 122.43 ± 28.79 MPa, 164.56 ± 32.99 MPa, 188.44 ± 47.89 MPa, and 163.28 ± 50.55 MPa, respectively, as shown in Fig. 1h.
When developing a new bone tissue engineering material, in addition to other performance requirements for specific applications, the goal should be to prepare strong and stiff materials. HA is a weak bioceramic, so it cannot be used alone as the main load-bearing bone substitute in the human body. A high compressive strength can effectively support the surrounding tissues to prevent collapse [38], and the appropriate compressive strength can be adapted to the strength of natural bone. The compressive strengths of SHA, SMHA, SSHA, and SMSHA were 1.72 ± 0.29 MPa, 2.47 ± 0.25 MPa, 1.87 ± 0.52 MPa, and 2.04 ± 0.35 MPa, respectively (Fig. 1i), and both SMHA and SMSHA were in the range of cancellous bone [39].
SEM observations and surface roughness measurement
Promising scaffolds should have a suitable microscopic morphology to allow sufficient cell contact for the stimulation of cell responses. SEM confirmed that the four scaffolds (SHA, SMHA, SSHA, and SMSHA) had rough surface morphologies, meeting the microscopic morphology required for osteogenic differentiation and the growth of BMSCs. The surface of the scaffold with macropores is defined as the macroporous surface of the scaffold (Fig. 2a1–a2, b1–b2, c1–c2, and d1–d2), and the surface without macropores is defined as the microporous surface of the scaffold (Fig. 2a3–a4, b3–b4, c3–c4, and d3–d4). A macroporous surface has lotus root-like pores, which facilitate blood penetration, blood vessel formation, and the other functions mentioned above. More importantly, it also provides a bionic microenvironment for the stimulation of BMSC bioactivity.
Moreover, both the macroporous surface and the microporous surface are rough, which is conducive to the attachment of cells. The optical profiler analysis results showed that the surface roughness levels of the scaffolds were different. In terms of the surface roughness of the macroporous surface, SHA was the highest, followed by SMSHA. In terms of the microporous surface, the roughness levels of the four scaffolds were similar, as shown in Fig. 3.
Optical profiler images of surface roughness. The surface roughness levels of the macroporous surfaces of SHA (a), SMHA (b), SSHA (c) and SMSHA (d); the surface roughness levels of the microporous surfaces of SHA (e), SMHA (f), SSHA (g) and SMSHA (h). Macroporous surface roughness parameters (i), microporous surface roughness parameters (j), Ra average roughness, Rq root mean square roughness, (n = 3, * P < 0.05, # P > 0.05)
Element distribution and content of the scaffolds
Except for silicon and oxygen, EDS element mapping showed that the distribution density of each element on the macroporous surface and the microporous surface was similar for each scaffold. Analysis showed that the main elements of SHA (Ca, P, O, and Si) (Additional file 1: Figure S1), SMHA (Ca, P, O, Si, and Mg) (Additional file 1: Figure S2), SSHA (Ca, P, O, Si, and Sr) (Additional file 1: Figure S3), and SMSHA (Ca, P, O, Si, Mg and Sr) (macroporous surface shown in Fig. 4b1–h1, microporous surface shown in Fig. 4b2–h2) were uniformly distributed on the corresponding scaffold. These results indicated that this doping method is effective and feasible.
Elemental content analysis showed that four main peaks of Ca, P, O, and Si could be detected for the four types of scaffolds on both macroporous surfaces (Fig. 5a1–d1) and microporous surfaces (Fig. 5a2–d2). Of the four scaffolds, Mg and Sr had different elements, SMHA had Mg peaks, SSHA had Sr peaks, and SMSHA had both Mg peaks and Sr peaks compared with SHA (Fig. 5a1–a2). However, the elemental contents of the macroporous surfaces and the microporous surfaces were slightly different, and the SMHA scaffold doped with Mg showed a lower content of Mg than the Sr content of the SSHA-doped Sr scaffold, which is related to the difficulty in replacing Ca2+ in mHAws with Mg2+ during the sintering process.
Release of osteogenic active elements
After the test, it was noted that each scaffold had its own unique ion release kinetics. The release rates of the four scaffolds' osteogenic active elements in PBS solution and the changes in the concentrations of Si, Mg, and Sr in PBS for different immersion times are shown in Fig. 6. Among them, the release of Si4+ was relatively stable, the release of Mg2+ showed a downward trend, and the release of Sr2+ was relatively stable.
In vitro cell studies
Cell viability and proliferation
Cell live/dead staining confirmed that these scaffolds are beneficial to cell viability and growth. Living cells were stained green by calcein AM, and dead cells were stained red by EthD-1, as observed by upright fluorescence microscopy. Most of the cells on the scaffolds were green living cells, and the red-stained dead cells were almost invisible (Fig. 7a–d). The CCK-8 assay is a typical way to test the proliferation of cells. CCK-8 solution reacts with dehydrogenase in the mitochondria of living cells to produce yellow formazan, and the amount of formazan produced is proportional to the number of living cells. A microplate reader was used to measure the optical density (OD) values to evaluate the number of living cells, which indirectly reflects the cytotoxicity of the scaffolds. The rBMSCs cultured on the four scaffolds had good viability, as shown in the experimental results in Fig. 7e. The results of the live/dead staining and CCK-8 assays confirmed both that these four scaffolds had good biocompatibility and that their biosafety was favorable for the proliferation and spread of rBMSCs.
Live/dead staining to assess the viability of rBMSCs cultured on the SHA, SMHA, SSHA, and SMSHA scaffolds (a–d), respectively. The CCK-8 assay assessed the proliferation of rBMSCs (e) (n = 5, * P < 0.05, # P > 0.05 compared with SHA). The surface area (f) and typical cell morphology (g–j) of rBMSCs cocultured with SHA, SMHA, SSHA, and SMSHA for 3 days, respectively (n = 5, * P < 0.05, # P > 0.05 compared with SHA)
Surface area and morphological shape of rBMSCs
After culturing for 3 and 7 days, observation of the morphological shape of the rBMSCs with an upright fluorescence microscope verified that imaging cells cocultured with the scaffolds may be a simple way to assess the area of cell spreading organization and the cytoskeletal structure [40,41,42]. The shapes of the rBMSCs cocultured with the four types of scaffolds all showed different spreading organization areas (Fig. 7f–j). The analysis showed that SMHA and SMSHA were more conducive to an increase in cell spreading organization, which may be related to doping with Mg.
Bone regeneration in the defect site requires the proliferation and differentiation of the surrounding BMSCs to spread and cross, and cell spreading is driven by filopodia, pseudopods, and the cytoskeleton in a suitable physical and chemical environment. Morphological shapes, filopodia, and pseudopods were observed on rBMSCs cocultured with the four scaffolds and the rBMSCs cultivated with SMHA or SMSHA had a polygonal osteoblast-like shape and the largest numbers of filopodia and pseudopods (Fig. 8a1–d2).
Scaffolds induce the expression of genes related to bone formation in rBMSCs
Next, the osteogenic abilities of these scaffolds were further verified. After 7 and 14 days of culture on the scaffolds, the expression levels of rBMSC bone-specific genes, including COL1 (the main organic component of bone extracellular matrix), BMP2 (a factor that strongly promotes bone regeneration), Runx2 (an osteoblastic transcript factor that guides BMSCs to differentiate into osteoblasts), and ALP (a biochemical marker of early osteogenesis), were determined along with the angiogenic gene VEGF (a growth factor to enhance vascularization for tissue repair) and the housekeeping gene GAPDH (a constantly expressed gene) and were evaluated by RT–qPCR (the primer sequences are shown in Table 1). Compared with the SHA scaffold, the rBMSCs cultured on the SMHA, SSHA, and SMSHA scaffolds showed higher expression levels of COL1, BMP2, Runx2, ALP, and VEGF on the 7th and 14th days, and the SMSHA scaffold displayed the highest expression levels (Fig. 8e–i). The gene expression profiles of COL1, ALP, Runx2, and VEGF indicated good osteoblast proliferation and maturation.
Morphology of the rBMSCs cocultured with the four scaffolds and fold changes in osteogenic-related gene expression in rBMSCs cultured on the four scaffolds. Morphologies of the rBMSCs cocultured with SHA, SMHA, SSHA, and SMSHA for 3 days (a1–d1) and 7 days (a2–d2) (10 ×), respectively; arrows indicate the filopodia. The changes in expression of COL1, BMP2, Runx2, ALP, and VEGF in rBMSCs cultured on the four scaffolds (e–i) compared with GAPDH (j) (n = 3, * P < 0.05, # P > 0.05 compared with SHA or 14 d compared with 7 d of each scaffold)
Discussion
The design of new bone filling materials for BTE needs to consider hydrophilicity, cytotoxicity, morphology, mechanical properties, osteogenic activity, and related factors. Composite bone repair materials based on hydroxyapatite have been a mainstream research topic in recent years, but their applications have been limited due to the inherent defects of hydroxyapatite. Based on the needs of bone tissue engineering and the goal of improving HA performance, active osteogenic elements are incorporated to improve the bone repair ability of the material. Micron hydroxyapatite whiskers have been researched and synthesized, and a porous scaffold has been successfully fabricated. Micron-sized HA may have better biological activity, and it can be increased to produce a biological scaffold with a porous structure [9]. These scaffolds have excellent hydrophilicity, and studies have revealed that the hydrophilic surface of biological materials can regulate the adsorption of fibronectin and fibrinogen and that these materials have a greater potential to promote the differentiation of macrophages into the anti-inflammatory phenotype [43, 44]. Notably, the doped Mg2+ and the hydrophilic surface of a material have some of the same cell signaling pathways (PI3K and NF-κB) in terms of exerting anti-inflammatory effects and assisting in osteogenesis [44,45,46].
Dense cortical bone has very few pores, spongy cancellous bone has many pores, and natural bone structure bionic materials have better application advantages in BTE [47]. These characteristics are closely related to the morphology and surface roughness of the scaffold. The pore sizes and surface roughness of the scaffold must match the requirements of bone regeneration to facilitate the attachment, migration, proliferation, and osteogenic differentiation of BMSCs and provide space for the deposition of calcium and phosphorus while promoting the formation and growth of blood vessels to provide nutrients and for the transportation of metabolic waste [4, 48,49,50]. The ideal pore size range for new bone regeneration is 150–350 μm [4]. mHAw-based scaffolds show roughness and have micropores, and the porous scaffold extruded by this die has more abundant pores with a suitable pore diameter, which is beneficial to the additive manufacturing of BTE. The effect of surface roughness, which results in a larger surface area for cell attachment, is an easy-to-customize and cost-effective factor that can affect cell behavior. The surface roughness of each scaffold is in the range of Ra ~ 0.7–3.1 μm, which facilitates the osteogenic differentiation of MSCs [51]. Therefore, the pore diameters and rough surface morphology of mHAw-based scaffolds may meet the needs of BTE.
The excellent mechanical properties of porous scaffolds can provide sufficient physical support and biochemical stimulation to facilitate bone formation [52]. The elastic modulus is an important index to measure the stiffness of a material, and Young’s modulus is the most important and characteristic mechanical property of elastic materials. The compressive strength levels of natural bone are 2–12 MPa for cancellous bone and 100–230 MPa for cortical bone [39]. The modulus of elasticity of cortical bone is 5–27 GPa and that of cancellous bone is 0.76–20 GPa [53]. In this study, silica was complexed with the scaffolds to enhance their mechanical properties, avoid the low strength of HA, and make the elastic moduli of the four scaffolds more similar to that of cancellous bone to support local soft tissues and demonstrated the good processing performance of mHAw. In addition, silicon has good osteogenic activity, which can provide a large amount of Si4+ during the degradation process of these scaffolds in bone defect sites. All scaffolds realized the sustained and stable release of Si4+, and the Si4+ release kinetics of the four scaffolds are similar.
HA chemically modified by ionic substitution has been demonstrated to be more advantageous than HA alone in accelerating bone regeneration and promoting the reabsorption of cell-mediated ceramic scaffolds [12, 54, 55]. Although SMHA and SMSHA scaffolds had difficulty doping Mg2+ and had less magnesium content, the release rates of Mg2+ were higher, and their abilities to induce the proliferation and osteogenic differentiation of BMSCs were also stronger. The live/dead, CCK-8, rBMSC area, and morphology results confirmed that SMSHA facilitated rBMSC attachment, proliferation, and spreading to a greater extent than the SHA, SMHA, and SSHA scaffolds, suggesting that SMSHA can release Si4+, Mg2+, and Sr2+, three active elements, to synergistically exert biological activity [56]. The larger the surface area of the BMSCs is, the greater the possibility of osteogenesis. Additionally, the smaller the area of cell spreading organization is, the greater the tendency of BMSCs to undergo apoptosis [41]. High-efficiency Mg2+ release has a significant role in promoting the osteogenic activity of rBMSCs [42]. Although the strontium contents in SSHA and SMSHA were high, its release rates were low. The release kinetics of Mg2+ and Sr2+ are variable, so there are differences in in vitro biological osteogenesis. Therefore, the cell proliferation and osteogenic activity of SSHA were lower those that of SMHA and SMSHA, which may be related to the ion release rate.
Bone-related genes are important factors that regulate bone regeneration. Compared with SHA, the expression levels of COL1, BMP2, ALP, VEGF, and Runx2 increased to varying degrees in rBMSCs cultured on the SMHA, SSHA, and SMSHA scaffolds, while GAPDH was constantly expressed, indicating that Mg2+ and Sr2+ can promote the expression of these factors and rBMSC osteogenic differentiation. These gene expression profiles may be stimulated by Mg2+, Sr2+, or the combination of Mg2+ and Sr2+ [8, 12, 57] on the basis of mHAws and silica. In the early stage of new bone formation, COL1 participates in bone mineralization to form osteoids, and in the later stage, COL1 aligns with HA crystals to form mature bone [8, 57]. Both Mg2+ and upregulated BMP2 can promote the osteogenic differentiation of BMSCs [8, 58]. VEGF plays an important stimulatory role in all stages of bone development and repair, including endochondral ossification and intramembranous ossification, and in bone, it is mainly derived from osteoblasts [59,60,61]. Runx2 can guide BMSCs to differentiate into osteoblasts and upregulate osteocalcin and osteopontin [62]. mHAws, silica, magnesium, and strontium have broad application prospects in bone regeneration. The use of Mg-Sr codoped mHAw scaffolds for bone repair may be a promising method to avoid the limitations of individual applications and can synergistically promote bone formation.
Conclusions
Based on the strategy of low-temperature sintering and extrusion molding, four scaffolds were synthesized: SHA, SMHA, SSHA, and SMSHA, which were mainly composed of microhydroxyapatite whiskers doped with magnesium and strontium and complexed with silica to enhance the mechanical properties. Each scaffold had a high specific porous surface area, porosity, rough surface morphology, and sustained release of osteogenic active factors, promoting the adhesion and proliferation of SD rBMSCs. Compared with SHA, the SMHA, SSHA, and SMSHA scaffolds more effectively stimulated the osteogenic and angiogenic differentiation of rBMSCs in vitro. Therefore, the prepared scaffolds have strong potential application value in the field of biomedical bone tissue engineering. In further research, these four scaffolds will be transplanted into animals to verify their capacity to promote bone regeneration and new blood vessel formation in vivo.
Materials and methods
Scaffold fabrication and bone repair mechanism
The raw materials and their roles were calcium nitrate to provide calcium ions, diammonium hydrogen phosphate to provide phosphate, urea as a nitrogen source to form an alkaline environment, sorbitol as a template agent to guide whisker growth, and nitric acid as a catalyst. These raw materials were sequentially added to ultrapure water, and after being fully dissolved, they were made into a reaction solution, and configured with a ratios of Ca (or Ca + Mg, Ca + Sr, or Ca + Mg/Sr)/P of 1.67. The pH of each solution was adjusted to 2 ~ 3. The prepared solutions were heated in a water bath to 94 °C for 20 h to obtain the mHAws. The obtained mHAws were washed with distilled water 6 ~ 7 times, filtered with suction, and dried at 60 °C. Konjac glucomannan was then added to the hydroxyapatite whiskers at a ratio of 10%, an appropriate amount of ultrapure water was added and the solution was mixed well. (Konjac glucomannan was obtained by separated and removed starch, pigments, alkaloids, and sulfur dioxide from refined konjac powder. It plays the role of binder and thickener in the process of preparing whiskers, and could be completely removed in the sintering process.)
The mixed slurry was extruded through a die to form a porous ceramic scaffold, which was freeze dried at minus 10 °C to remove the excess water from the scaffold. The dried scaffold was cut to the required size and placed in a muffle furnace for firing at 450 °C (sintering rate was 5 °C/min). The fired scaffold was immersed in liquid silica gel, removed after two hours, and dried, and the dried scaffold was placed in a muffle furnace again at 400 °C, and fired for an additional four hours to prepare a porous ceramic scaffold containing SiO2. In this way, the silica-complexed mHAw scaffold (SHA), silica-complexed Mg-doped mHAw scaffold (SMHA), silica-complexed Sr-doped mHAw scaffold (SSHA), and silica-complexed Mg-Sr codoped mHAw scaffold (SMSHA) were prepared, and the fabrication process is shown in Fig. 9. The mechanism by which SMSHA induces bone repair in bone defects is shown in Fig. 9e–f.
Fabrication of a porous hierarchical scaffold with Mg-Sr codoped SiO2-complexed microhydroxyapatite whiskers (mHAws). SEM micrograph of Mg-Sr codoped mHAws (a). Element mapping of Mg-Sr codoped mHAws (b). Prepared SMSHA scaffold (size 0.8 × 0.8 × 0.8 cm): the macroporous surface (c) and the microporous surface (d). Schematic diagram of scaffold filling bone defect (e) for BMSC osteogenic differentiation and bone regeneration (f)
Hydrophilicity tests
Orthopedic grafts need to have a certain degree of hydrophilicity. Testing the hydrophilicity is an indirect method to detect the potential biological application value of these materials. The hydrophilicity of each of the scaffolds was confirmed by measuring the water contact angle (WCA) of the scaffold surface using a water contact angle measurement instrument (CA100A, Shanghai, China). Briefly, 5 μl of ultrapure water was dropped onto the surface of the holder under ambient conditions, and then the contact angle was measured. All measurements were repeated 3 times on different parts of each scaffold.
Pore size tests
A main characteristic of porous ceramic scaffolds for bone regeneration is their pores, which can perform specific functions. Five samples of each scaffold were randomly selected, and the pore size from the cross-sectional surface of each sample was randomly measured by scanning electron microscopy (SEM; TESCAN VEGA3, Czech Republic, Europe). Then, the average pore size in each of the corresponding scaffolds was calculated.
Mechanical properties
The SHA, SMHA, SSHA, and SMSHA scaffolds were cut into 8 × 8 × 8 mm3 cubes, and then the mechanical properties of each scaffold were measured using a static and dynamic material testing machine (HY-0230, Shanghai, China) with a load of 240 N. Five samples in each group were tested at a speed of 1 mm/min, and load–displacement curves were obtained. According to ISO 844:2004, the load–displacement curves can be used to calculate the Young’s moduli and compressive strengths of the scaffolds.
Morphology and structural characterization analysis
It is very important that the surface roughness and morphology of mHAw scaffolds mimic the porous structure of natural bone, and a rough surface morphology is conducive to the attachment, sprawling, proliferation, and osteogenic differentiation of BMSCs [50]. The mHAw scaffold surface morphology was verified by SEM, an optical profiler (Bruker Counter GT K 3D) was used to analyze the surface roughness parameters of the scaffolds, and the Ra (average roughness) and Rq (root mean square roughness) of all the scaffolds were calculated.
Inductively coupled plasma optical emission spectrometry (ICP-OES) and energy dispersive spectroscopy (EDS) measurements
Scaffold cut into cubes (8 × 8 × 8 mm3) was placed in a glass container. According to the standards of GB/T 16,886.13–2001 and GB/T 16,886.12–2001, the mass volume ratio of scaffold and phosphate buffered saline (PBS, pH = 7.4) was 1 g:15 ml. After constant temperature (37 °C) and speed (70 rpm) shaking for 1, 3, 7, and 14 days, 5 ml of degradation solution was collected at each time point, and an equal volume of fresh PBS was added at the same time. ICP-OES (PE Avio 200) was used to determine the release rate of the osteogenic active element Si4+ in the four scaffolds, and inductively coupled plasma mass spectrometry (ICP-MS, iCAP Qc) was used to measure the ion release rates of Mg and Sr. A 10 kV FESEM (S-4800, HITACHI, Tokyo, Japan) equipped with energy dispersive spectroscopy (EDS) capabilities was used to scan the chemical morphology map and various elemental contents of the cross sections of each scaffold.
In vitro cell experiments
Cell culture
Sprague–Dawley (SD) rats (120 g, 5–6 weeks old, purchased from the Department of Veterinary Medicine, Kunming Medical University) were euthanized and disinfected. Their femurs and tibias were removed from both sides, the epiphyses were cut at both ends, and the bone marrow cavities were flushed repeatedly with Dulbecco’s modified Eagle’s medium (DMEM; Gibco, USA). After centrifugation at 1000 rpm for 5 min, the cells were resuspended in DMEM supplemented with 1% penicillin/streptomycin and 10% fetal bovine serum (FBS; Gibco, USA) for cell culture. The cells were cultured in an incubator containing 5% carbon dioxide at 37 °C. Rat bone marrow-derived mesenchymal stem cells (rBMSCs) were obtained after 7 days of culture (the nonadherent cells were removed during the culture, and the cells were passaged when the fusion exceeded 80%), and passages 3 to 5 were used for cell experiments.
Cell viability and proliferation
After the rBMSCs (1 × 105) were incubated on each scaffold (8 mm × 2 mm) for 3 days, the survival of the rBMSCs was determined by fluorescent staining; that is, rBMSCs were treated with a staining kit (Solarbio, China) containing calcein AM and EthD-1 for the live/dead staining assay. In this assay, dead cells were stained red, and living cells were stained green. To further evaluate the proliferation of rBMSCs cultured for 1 day, 3 days, and 7 days according to the aforementioned method, a sample of complete DMEM was removed at each time point, and 550 μl of DMEM containing 10% Cell Counting Kit-8 (CCK-8, Dojindo, Japan) solution was added to each microplate well. After incubation for 1–4 h under cell culture conditions, 5 replicate wells were set in a 96-well plate, and 100 μl of incubation solution was added to each well. The absorbance of each solution was measured with a microplate reader (Bio–Rad 680, USA) at a wavelength of 450 nm to evaluate the viability and proliferation ability of the rBMSCs on each scaffold.
Cell morphology and surface area
To analyze the effects of various scaffolds on cell morphology and surface area, rBMSCs cocultured with the four scaffolds were washed twice with PBS after coculture for 3 days. The cytoplasm of the rBMSCs was stained with calcein AM obtained from the live/dead viability kit and was then used to stain live cells. Fluorescence images were obtained with an upright fluorescence microscope (OLYMPUS, BX53F, Tokyo, Japan), the morphological shapes of the rBMSCs were observed, and then the typical cell surface areas were calculated using cellSens Standard software (OLYMPUS, Tokyo, Japan).
Osteogenic gene expression analysis
The effects of the scaffolds on the expression levels of rBMSC osteogenic genes were studied by real-time quantitative polymerase chain reaction (RT–qPCR). rBMSCs were seeded on each scaffold in duplicate at a density of 2 × 105 cells per scaffold. After 7 or 14 days of culture, the cells on the scaffold were lysed with 1 ml of TRIzol (Invitrogen, USA) to isolate and obtain total RNA. Complementary DNA (cDNA) was synthesized using the PrimeScript First Strand cDNA Synthesis kit (Thermo Scientific, Lithuania) according to the manufacturer’s instructions. A real-time PCR kit (FastStart Universal SYBR@ Green Master, Roche, Germany) was used on a thermal cycler (Applied Biosystems, Australia) to analyze type I collagen (COL1), bone morphogenetic protein 2 (BMP2), Runt-related transcription Factor 2 (Runx2), alkaline phosphatase (ALP), and vascular endothelial growth factor (VEGF) cDNA. The housekeeping gene glyceraldehyde 3-phosphate dehydrogenase (GAPDH) was used to analyze the changes in the expression levels of the above genes.
Statistical analysis
To determine the differences between each scaffold at each time point, one-way analysis of variance (ANOVA) and Student–Newman–Keuls post hoc tests were used for statistical analysis. Quantitative data are expressed as the mean ± standard deviation. A value of P < 0.05 was considered statistically significant. GraphPad Prism 7 software was used for all statistical analyses.
Availability of data and materials
The datasets used and/or analyzed during the current study are available from the corresponding author on reasonable request.
Abbreviations
- BTE:
-
Bone tissue engineering
- mHAws:
-
Micron-sized HA whiskers
- SHA:
-
Silica-complexed mHAw scaffold
- SMHA:
-
Silica-complexed Mg-doped mHAw scaffold
- SSHA:
-
Silica-complexed Sr-doped mHAw scaffold
- SMSHA:
-
Silica-complexed Mg-Sr codoped mHAw scaffold
- WCA:
-
Water contact angle
- SEM:
-
Scanning electron microscopy
- EDS:
-
Energy dispersive spectroscopy
- DMEM:
-
Dulbecco’s modified Eagle’s medium
- FBS:
-
Fetal bovine serum
- rBMSCs:
-
Rat bone marrow-derived mesenchymal stem cells
- BMSCs:
-
Bone marrow mesenchymal stem cells
- CCK-8:
-
Cell counting Kit-8
- RT-qPCR:
-
Real-time quantitative polymerase chain reaction
- COL1:
-
Type I collagen
- BMP2:
-
Bone morphogenetic protein 2
- Runx2:
-
Runt-related transcription factor 2
- ALP:
-
Alkaline phosphatase
- VEGF:
-
Vascular endothelial growth factor
- GAPDH:
-
Glyceraldehyde 3-phosphate dehydrogenase
References
Einhorn TA, Gerstenfeld LC. Fracture healing: mechanisms and interventions. Nat Rev Rheumatol. 2014;11(1):45–54.
Shen X, Zhang Y, Gu Y, Xu Y, Liu Y, Li B, Chen L. Sequential and sustained release of SDF-1 and BMP-2 from silk fibroin-nanohydroxyapatite scaffold for the enhancement of bone regeneration. Biomaterials. 2016;106:205–16.
Tarchala M, Harvey EJ, Barralet J. Biomaterial-stabilized soft tissue healing for healing of critical-sized bone defects: the Masquelet technique. Adv Healthc Mater. 2016;5(6):630–40.
Liu WC, Chen S, Zheng L, Qin L. Angiogenesis assays for the evaluation of angiogenic properties of orthopaedic biomaterials—a general review. Adv Healthc Mater. 2017;6(5):1600434.
Wang SJ, Jiang D, Zhang ZZ, Chen YR, Yang ZD, Zhang JY, Shi J, Wang X, Yu JK. Biomimetic nanosilica-collagen scaffolds for in situ bone regeneration: toward a cell-free, one-step surgery. Adv Mater. 2019;31(49):e1904341.
Koons GL, Diba M, Mikos AG. Materials design for bone-tissue engineering. Nat Rev Mater. 2020;5(8):584–603.
Liu H, Xu GW, Wang YF, Zhao HS, Xiong S, Wu Y, Heng BC, An CR, Zhu GH, Xie DH. Composite scaffolds of nano-hydroxyapatite and silk fibroin enhance mesenchymal stem cell-based bone regeneration via the interleukin 1 alpha autocrine/paracrine signaling loop. Biomaterials. 2015;49:103–12.
Lai Y, Li Y, Cao H, Long J, Wang X, Li L, Li C, Jia Q, Teng B, Tang T, et al. Osteogenic magnesium incorporated into PLGA/TCP porous scaffold by 3D printing for repairing challenging bone defect. Biomaterials. 2019;197:207–19.
Sun TW, Yu WL, Zhu YJ, Yang RL, Shen YQ, Chen DY, He YH, Chen F. Hydroxyapatite nanowire@magnesium silicate core-shell hierarchical nanocomposite: synthesis and application in bone regeneration. ACS Appl Mater Interfaces. 2017;9(19):16435–47.
Nabiyouni M, Brückner T, Zhou H, Gbureck U, Bhaduri SB. Magnesium-based bioceramics in orthopedic applications. Acta Biomater. 2018;66:23–43.
Shuai C, Li S, Peng S, Feng P, Lai Y, Gao C. Biodegradable metallic bone implants. Mater Chem Front. 2019;3(4):544–62.
Wu C, Chen Z, Yi D, Chang J, Xiao Y. Multidirectional effects of Sr-, Mg-, and Si-containing bioceramic coatings with high bonding strength on inflammation, osteoclastogenesis, and osteogenesis. ACS Appl Mater Interfaces. 2014;6(6):4264–76.
Moghanian A, Firoozi S, Tahriri M, Sedghi A. A comparative study on the in vitro formation of hydroxyapatite, cytotoxicity and antibacterial activity of 58S bioactive glass substituted by Li and Sr. Mater Sci Eng C Mater Biol Appl. 2018;91:349–60.
Cox SC, Thornby JA, Gibbons GJ, Williams MA, Mallick KK. 3D printing of porous hydroxyapatite scaffolds intended for use in bone tissue engineering applications. Mater Sci Eng C Mater Biol Appl. 2015;47:237–47.
Li X, Ma B, Li J, Shang L, Liu H, Ge S. A method to visually observe the degradation-diffusion-reconstruction behavior of hydroxyapatite in the bone repair process. Acta Biomater. 2020;101:554–64.
Saleem M, Rasheed S, Yougen C. Silk fibroin/hydroxyapatite scaffold: a highly compatible material for bone regeneration. Sci Technol Adv Mater. 2020;21(1):242–66.
Xie L, Yu H, Yang W, Zhu Z, Yue L. Preparation, in vitro degradability, cytotoxicity, and in vivo biocompatibility of porous hydroxyapatite whisker-reinforced poly(L-lactide) biocomposite scaffolds. J Biomater Sci Polym Ed. 2016;27(6):505–28.
Shuai C, Cao Y, Gao C, Feng P, Xiao T, Peng S. Hydroxyapatite whisker reinforced 63s glass scaffolds for bone tissue engineering. Biomed Res Int. 2015;2015:1–8.
Kane RJ, Weiss-Bilka HE, Meagher MJ, Liu Y, Gargac JA, Niebur GL, Wagner DR, Roeder RK. Hydroxyapatite reinforced collagen scaffolds with improved architecture and mechanical properties. Acta Biomater. 2015;17:16–25.
Li Y, Liu G, Zhai Z, Liu L, Li H, Yang K, Tan L, Wan P, Liu X, Ouyang Z, et al. Antibacterial properties of magnesiumin vitroand in anin vivomodel of implant-associated methicillin-resistant staphylococcus aureus infection. Antimicrob Agents Chemother. 2014;58(12):7586–91.
Feyerabend F, Wendel HP, Mihailova B, Heidrich S, Agha NA, Bismayer U, Willumeit-Romer R. Blood compatibility of magnesium and its alloys. Acta Biomater. 2015;25:384–94.
Moghanian A, Ghorbanoghli A, Kazem-Rostami M, Pazhouheshgar A, Salari E, Saghafi Yazdi M, Alimardani T, Jahani H, Sharifian Jazi F, Tahriri M. Novel antibacterial Cu/Mg-substituted 58S-bioglass: synthesis, characterization and investigation of in vitro bioactivity. Int J Appl Glas Sci. 2019;11(4):685–98.
Yan T, Tan L, Zhang B, Yang K. Fluoride conversion coating on biodegradable AZ31B magnesium alloy. J Mater Sci Technol. 2014;30(7):666–74.
Shadjou N, Hasanzadeh M. Bone tissue engineering using silica-based mesoporous nanobiomaterials: recent progress. Mater Sci Eng C Mater Biol Appl. 2015;55:401–9.
Gotz W, Tobiasch E, Witzleben S, Schulze M. Effects of silicon compounds on biomineralization, osteogenesis, and hard tissue formation. Pharmaceutics. 2019;11(3):117.
Honda M, Kikushima K, Kawanobe Y, Konishi T, Mizumoto M, Aizawa M. Enhanced early osteogenic differentiation by silicon-substituted hydroxyapatite ceramics fabricated via ultrasonic spray pyrolysis route. J Mater Sci Mater Med. 2012;23(12):2923–32.
Niu LN, Jiao K, Qi YP, Nikonov S, Yiu CK, Arola DD, Gong SQ, El-Marakby A, Carrilho MR, Hamrick MW, et al. Intrafibrillar silicification of collagen scaffolds for sustained release of stem cell homing chemokine in hard tissue regeneration. FASEB J. 2012;26(11):4517–29.
Liu J, Rawlinson SC, Hill RG, Fortune F. Strontium-substituted bioactive glasses in vitro osteogenic and antibacterial effects. Dent Mater. 2016;32(3):412–22.
Brauer DS, Karpukhina N, Kedia G, Bhat A, Law RV, Radecka I, Hill RG. Bactericidal strontium-releasing injectable bone cements based on bioactive glasses. J R Soc Interface. 2013;10(78):20120647.
Chen Y, Zheng Z, Zhou R, Zhang H, Chen C, Xiong Z, Liu K, Wang X. Developing a strontium-releasing graphene oxide-/collagen-based organic-inorganic nanobiocomposite for large bone defect regeneration via MAPK signaling pathway. ACS Appl Mater Interfaces. 2019;11(17):15986–97.
Xing M, Wang X, Wang E, Gao L, Chang J. Bone tissue engineering strategy based on the synergistic effects of silicon and strontium ions. Acta Biomater. 2018;72:381–95.
Alkhraisat MH, Rueda C, Cabrejos-Azama J, Lucas-Aparicio J, Marino FT, Torres Garcia-Denche J, Jerez LB, Gbureck U, Cabarcos EL. Loading and release of doxycycline hyclate from strontium-substituted calcium phosphate cement. Acta Biomater. 2010;6(4):1522–8.
Moghanian A, Firoozi S, Tahriri M. Characterization, in vitro bioactivity and biological studies of sol-gel synthesized SrO substituted 58S bioactive glass. Ceram Int. 2017;43(17):14880–90.
Mao L, Xia L, Chang J, Liu J, Jiang L, Wu C, Fang B. The synergistic effects of Sr and Si bioactive ions on osteogenesis, osteoclastogenesis and angiogenesis for osteoporotic bone regeneration. Acta Biomater. 2017;61:217–32.
Moghanian A, Nasiripour S, Miri Z, Hajifathali Z, Hosseini SH, Sajjadnejad M, Aghabarari R, Nankali N, Miri AK, Tahriri M. Structural and in vitro biological evaluation of sol-gel derived multifunctional Ti+4/Sr+2 co-doped bioactive glass with enhanced properties for bone healing. Ceram Int. 2021;47(20):29451–62.
Zhu Q, Li X, Fan Z, Xu Y, Niu H, Li C, Dang Y, Huang Z, Wang Y, Guan J. Biomimetic polyurethane/TiO2 nanocomposite scaffolds capable of promoting biomineralization and mesenchymal stem cell proliferation. Mater Sci Eng C Mater Biol Appl. 2018;85:79–87.
Sharifi F, Atyabi SM, Norouzian D, Zandi M, Irani S, Bakhshi H. Polycaprolactone/carboxymethyl chitosan nanofibrous scaffolds for bone tissue engineering application. Int J Biol Macromol. 2018;115:243–8.
Wang Q, Feng Y, He M, Zhao W, Qiu L, Zhao C. A hierarchical janus nanofibrous membrane combining direct osteogenesis and osteoimmunomodulatory functions for advanced bone regeneration. Adv Func Mater. 2020;31(8):2008906.
Henkel J, Woodruff MA, Epari DR, Steck R, Glatt V, Dickinson IC, Choong PF, Schuetz MA, Hutmacher DW. Bone regeneration based on tissue engineering conceptions—a 21st century perspective. Bone Res. 2013;1(3):216–48.
Zhang C, Wang W, Hao X, Peng Y, Zheng Y, Liu J, Kang Y, Zhao F, Luo Z, Guo J, et al. A novel approach to enhance bone regeneration by controlling the polarity of GaN/AlGaN heterostructures. Adv Func Mater. 2020;31(5):2007487.
Jiao F, Zhao Y, Sun Q, Huo B. Spreading area and shape regulate the apoptosis and osteogenesis of mesenchymal stem cells on circular and branched micropatterned islands. J Biomed Mater Res A. 2020;108(10):2080–9.
Xiang H, Yang Q, Gao Y, Zhu D, Pan S, Xu T, Chen Y. Cocrystal strategy toward multifunctional 3D-printing scaffolds enables NIR-activated photonic osteosarcoma hyperthermia and enhanced bone defect regeneration. Adv Func Mater. 2020;30(25):1909938.
Schoenenberger AD, Tempfer H, Lehner C, Egloff J, Mauracher M, Bird A, Widmer J, Maniura-Weber K, Fucentese SF, Traweger A, et al. Macromechanics and polycaprolactone fiber organization drive macrophage polarization and regulate inflammatory activation of tendon in vitro and in vivo. Biomaterials. 2020;249:120034.
Lv L, Xie Y, Li K, Hu T, Lu X, Cao Y, Zheng X. Unveiling the mechanism of surface hydrophilicity-modulated macrophage polarization. Adv Healthcare Mater. 2018;7(19):1800675.
Zhang X, Zu H, Zhao D, Yang K, Tian S, Yu X, Lu F, Liu B, Yu X, Wang B, et al. Ion channel functional protein kinase TRPM7 regulates Mg ions to promote the osteoinduction of human osteoblast via PI3K pathway: in vitro simulation of the bone-repairing effect of Mg-based alloy implant. Acta Biomater. 2017;63:369–82.
Su NY, Peng TC, Tsai PS, Huang CJ. Phosphoinositide 3-kinase/Akt pathway is involved in mediating the anti-inflammation effects of magnesium sulfate. J Surg Res. 2013;185(2):726–32.
Liu Y, Luo D, Wang T. Hierarchical structures of bone and bioinspired bone tissue engineering. Small. 2016;12(34):4611–32.
Kim HD, Amirthalingam S, Kim SL, Lee SS, Rangasamy J, Hwang NS. Biomimetic materials and fabrication approaches for bone tissue engineering. Adv Healthcare Mater. 2017;6(23):1700612.
Zhang X, Zeng D, Li N, Wen J, Jiang X, Liu C, Li Y. Functionalized mesoporous bioactive glass scaffolds for enhanced bone tissue regeneration. Sci Rep. 2016;6(1):1–12.
Du Y, Guo JL, Wang J, Mikos AG, Zhang S. Hierarchically designed bone scaffolds: from internal cues to external stimuli. Biomaterials. 2019;218:119334.
Li M, Fu X, Gao H, Ji Y, Li J, Wang Y. Regulation of an osteon-like concentric microgrooved surface on osteogenesis and osteoclastogenesis. Biomaterials. 2019;216:119269.
Peng Z, Zhao T, Zhou Y, Li S, Li J, Leblanc RM. Bone tissue engineering via carbon-based nanomaterials. Adv Healthc Mater. 2020;9(5):e1901495.
Hengsberger S, Kulik A, Zysset P. A Combined atomic force microscopy and nanoindentation technique to investigate the elastic properties of bone structural units. Eur Cell Mater. 2001;1:12–7.
Baba Ismail YM, Wimpenny I, Bretcanu O, Dalgarno K, El Haj AJ. Development of multisubstituted hydroxyapatite nanopowders as biomedical materials for bone tissue engineering applications. J Biomed Mater Res A. 2017;105(6):1775–85.
Landi E, Uggeri J, Sprio S, Tampieri A, Guizzardi S. Human osteoblast behavior on as-synthesized SiO(4) and B-CO(3) co-substituted apatite. J Biomed Mater Res A. 2010;94(1):59–70.
Wang S, Liu L, Zhou X, Yang D, Shi Z, Hao Y. Effect of strontium-containing on the properties of Mg-doped wollastonite bioceramic scaffolds. Biomed Eng Online. 2019;18(1):119.
Yoshizawa S, Brown A, Barchowsky A, Sfeir C. Magnesium ion stimulation of bone marrow stromal cells enhances osteogenic activity, simulating the effect of magnesium alloy degradation. Acta Biomater. 2014;10(6):2834–42.
Díaz-Tocados JM, Herencia C, Martínez-Moreno JM, Montes de Oca A, Rodríguez-Ortiz ME, Vergara N, Blanco A, Steppan S, Almadén Y, Rodríguez M, Muñoz-Castañeda JR. Magnesium chloride promotes osteogenesis through notch signaling activation and expansion of mesenchymal stem cells. Sci Rep. 2017;7(1):1–12.
Street J, Bao M, deGuzman L, Bunting S, Peale FV Jr, Ferrara N, Steinmetz H, Hoeffel J, Cleland JL, Daugherty A, et al. Vascular endothelial growth factor stimulates bone repair by promoting angiogenesis and bone turnover. Proc Natl Acad Sci U S A. 2002;99(15):9656–61.
Keramaris NC, Calori GM, Nikolaou VS, Schemitsch EH, Giannoudis PV. Fracture vascularity and bone healing: a systematic review of the role of VEGF. Injury. 2008;39:S45–57.
Deckers MM, Karperien M, vander Bent C, Yamashita T, Papapoulos SE, Löwik CW. Expression of vascular endothelial growth factors and their receptors during osteoblast differentiation. Endocrinology 2000; 141:1667–1674.
García JR, García AJ. Biomaterial-mediated strategies targeting vascularization for bone repair. Drug Deliv Transl Res. 2015;6(2):77–95.
Acknowledgements
Not applicable
Funding
The present study was funded by the National Natural Science Foundation of China (grant No.82060416,81760029), the Health Science and Technology Project of Yunnan province (grant No.2017NS022), Special program for Applied basic research of Yunnan Science and Technology Agency- Kunming Medical University (grant No.2018FE001- 146, 2018FE001-213, 2019FE001-240, 2019FE001- 079), Yunnan Province Clinical Center for Bone and joint Diseases (ZX2019-03–04), Scientific and technological innovation team for spine degenerative disease research of Kunming Medical University (grant No. CXTD201805), and Yunnan health training project of high level talents.
Author information
Authors and Affiliations
Contributions
CL and BW conceived the idea; CL, TY, and ZL designed the experiment; CL, ZJ, and ZS carried out the experiments; CL, TY, ZL, and BW analyzed the data and wrote the manuscript; QC and ZG assisted with the experiments; BW, QC, and ZG contributed to scientific discussion of the paper. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Ethics approval and consent to participate
The experimental protocol was approved by the Animal Experiment Ethics Committee of Kunming Medical University (kmmu2021268).
Consent for publication
Not applicable.
Competing interests
The authors declare that they have no competing interests.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Additional file 1: Figure S1
. Elemental mapping images of SHA. SEM images (a1, a2). All elemental distribution images (b1, b2). Ca, P, O, Si distribution images (c1-f1, c2-f2), respectively. Macroporous surfaces (a1-f1) and microporous surfaces (a2-f2), respectively. Figure S2. Elemental mapping images of SMHA. SEM images (a1, a2). All elemental distribution images (b1, b2). Ca, P, O, Si, Mg distribution images (c1-g1, c2-g2), respectively. Macroporous surfaces (a1-g1) and microporous surfaces (a2-g2), respectively. Figure S3. Elemental mapping images of SSHA. SEM images (a1, a2). All elemental distribution images (b1, b2). Ca, P, O, Si, Sr distribution images (c1-g1, c2-g2), respectively. Macroporous surfaces (a1-g1) and microporous surfaces (a2-g2), respectively.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.
About this article
Cite this article
Li, C., Yan, T., Lou, Z. et al. Characterization and in vitro assessment of three-dimensional extrusion Mg-Sr codoped SiO2-complexed porous microhydroxyapatite whisker scaffolds for biomedical engineering. BioMed Eng OnLine 20, 116 (2021). https://doi.org/10.1186/s12938-021-00953-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s12938-021-00953-w