Abstract
Ferroelectric Hf x Zr1-x O2 thin films are considered promising candidates for future lead-free CMOS-compatible ferroelectric memory application. The inductive crystallization behaviors and the ferroelectric performance of Hf0.5Zr0.5O2 thin films prepared by atomic layer deposition were investigated. Inductive crystallization can be induced by the film growth condition and appropriate top electrode selection. In this work, a Ni/Hf0.5Zr0.5O2/Ru/Si stack annealed at 550°C for 30 s in N2 ambient after the Ni top electrode has been deposited was manufactured, and it shows the best ferroelectric hysteresis loop in the dielectric thickness of 25 nm, with a remanent polarization value of 6 μC/cm2 and a coercive field strength of 2.4 MV/cm measured at 10 kHz. Endurance, retention, and domain switching current characteristics were evaluated well for potential application in the field of ferroelectric field effect transistor (FeFET) and nonvolatile ferroelectric memories (FeRAM).
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Background
The well-known perovskite-based ferroelectric materials, such as lead zirconate titanate (PZT) and strontium bismuth tantalate (SBT), have been widely applied to solid-state devices. As a promising candidate for lower power, higher density nonvolatile memories, severe challenges should be solved before integrating such ferroelectric materials into conventional CMOS technology [1,2].
Currently, high-k materials, such as HfO2, ZrO2, Al2O3, Ta2O5, and ZnO, have received much interest as dielectrics in MOSFET structures, flash memory, RF, mixed signal ICs, and so on. Among the oxides mentioned, HfO2 and ZrO2 have been profoundly studied and have great potential to be put into applications [3]. Ferroelectric performance in SiO2-doped HfO2 with a remanent polarization (P r) above 10 μC/cm2 and a coercive field strength (E c) of 1 MV/cm was reported [1]. Ferroelectric Hf0.5Zr0.5O2 thin films for nonvolatile memory applications were recommended [4], which showed a P r value of 16 μC/cm2 and E c of 1 MV/cm. In addition, polarization measurements on Al:HfO2 based metal-insulator-metal capacitors also showed an antiferroelectric-to-ferroelectric transition depending on annealing conditions and aluminum content [5]. From the point of crystallography, previous experimental phenomena resulted from the special phase transformation that happened in the crystal structure of the annealed thin film, which caused a rare orthorhombic phase with the non-centrosymmetric space group Pbc21.
In this work, a ferroelectric metal-insulator-metal (MIM) capacitor utilizing the Hf0.5Zr0.5O2 layer was investigated. Ru was defined as the bottom electrode and the source of external stress to induce crystallization with the assistant effect of the Ni top electrode. In consideration of the precisely controlled factors of high-quality nanolaminate films, including inter-facial roughness, inter-diffusion between layers, layer-to-layer consistency, and conformality, the Hf0.5Zr0.5O2 layer was prepared by atomic layer deposition (ALD) because it is more powerful in preparing such multilayers than other techniques, which keeps the precursors separated during the reaction [6,7]. Physical and electrical characterization of the device performance was carried out including the analysis of crystallinity, polarization-voltage (P-V) hysteresis loops, endurance, retention, and domain switching current. Several material aspects of Hf0.5Zr0.5O2 thin films were discussed in order to give better insight into their ferroelectric properties and guidelines for transistor fabrication.
Methods
Planar MIM capacitors were manufactured on Si substrates. The bottom electrode structure consisted of a 300-nm-thick SiO2 layer, 20-nm TiN, and 100-nm Ru at least for the purpose of induced crystallization. Hf0.5Zr0.5O2 thin films (10 to 25 nm) were grown in a single-wafer ALD reactor using tetrakis-(dimethylamino)-zirconium (TDMA-Zr) and tetrakis-(ethylmethylamino)-hafnium (TEMA-Hf) as precursors at 200°C. H2O was used as oxidant and nitrogen (N2) as purge and carrier gas. The 50-nm-thick Ni top electrode was deposited by sputtering technology under a power of 50 W in the cluster system. A subsequent rapid thermal processing (RTP) step was set at 823 K for 30 s in N2 ambient, resulting in crystallization.
Dielectric layer thickness was controlled accurately by adjusting the total cycle number and evaluated by spectroscopic ellipsometry. The stoichiometry was defined by varying the Zr/Hf + Zr ratio of the precursors and monitored by X-ray photoelectron spectroscopy (XPS) on samples without thermal treatment. Accordingly, X-ray diffraction (XRD) and transmission electron microscopy (TEM) were utilized to confirm the crystallinity of thin films. On the part of electrical characteristics, P-V measurements were performed to present MIM capacitors exhibiting ferroelectric polarization hysteresis at different test signals with the additional tests of endurance, retention, and domain switching current.
Results and discussion
There are three kinds of crystallization phases of pure HfO2 under atmospheric pressure. Monoclinic phase (m-phase), which is stable at ordinary temperature, will turn to tetragonal phase (t-phase) at 2,000 K approximately, and cubic (c-phase) at 2,900 K. Besides, the orthorhombic phase (o-phase) may exist under high pressure. Ferroelectricity could not be found in HfO2-based materials prepared with normal methods, usually aimed at late-model high-k dielectric in research and application. So the experiment phenomena suggested that the t-phase possibly appears in high temperature and leads to a special transformation to the needed o-phase under stress during cooling in the HfO2-based thin film, leading to ferroelectricity.
There are two potential reasons for ferroelectric performance appearing in the thin film. One is doping in HfO2 thin films, which stabilizes the t-phase possibly during annealing and enhances the objective transformation during cooling. The other is external stress from electrodes, inhibiting the transformation from the t-phase to m-phase and resulting in a shearless transformation into the o-phase instead. In this work, Zr was chosen as the doping material and Ru and Ni as the bottom and top electrodes, respectively.
A TEM cross section of the MIM capacitor with a 25-nm-thick Hf0.5Zr0.5O2 thin film is shown in Figure 1. The Ni top electrode is formed at room temperature, followed by RTP at 823 K for 30 s in N2 ambient to crystallize the as-deposited amorphous Hf0.5Zr0.5O2 thin films, which enables CMOS-compatible device processing and also offers BEOL compatibility, compared with high heat budget of the SiO2-doped HfO2 system [1].
Evidence for the ferroelectric performance of the Ru/Hf0.5Zr0.5O2/Ni MIM capacitor is given by the P-V hysteresis measurement shown in Figure 2. In order to investigate the influence of mechanical encapsulation on HfZrO thin films, two samples were prepared with the only difference in the sequence of the deposition of the top electrode and the annealing of the thin film. If RTP is carried out before the deposition of the top electrode, the structure is known as uncapped (Figure 2a) and the opposite as capped (Figure 2b). Besides, from the results of our research, it is obvious that with the increase of thin film thickness, P r raises while E c is reduced. This is because of the larger quantity of domains [8]. So, 25 nm has been chosen as the thickness of the sample thin film.
It can be observed that the capped structure with a P r value of about 6 μC/cm2 and E c of 2.4 MV/cm at the peak voltage of 14 V expresses more stable and typical loops at variational frequencies compared with uncapping, especially in the range of high frequency, which means less leakage during the test of electrical characteristics and better ferroelectricity. Meanwhile, these loops are not closed because of the defects existing in the thin films, which makes enrichment of charges due to the positive electric field and forms the pinning effect decreasing the quantity of reversible domain when the extra electric field reverses.
The choice of bottom electrode can affect the structure of the deposited ferroelectric thin film and its performance [9]. Figure 3 shows the contribution of the inductive crystallization effect of the Si/SiO2/TiN/Ru bottom electrode by XRD spectra, compared with a sample on Si-sub. Both of them have a capped structure. The reference powder pattern of the Hf x Zr1-x O2 system for the orthorhombic phase with space group Pbc21 [1,10] is calculated from the literature, whose estimated lattice parameters are 5.26 Å (a), 5.07 Å (b), and 5.08 Å (c).
In consideration of the effects of thermal stress and inevitable mechanical error during measurement, in spite of the typical phase mixture, the XRD results of the two samples has shown a diffraction pattern indicating a significant fraction of o-phase HfO2 which is similar for a rare orthorhombic phase with space group Pbc21, not centrosymmetric and therefore does not exclude ferroelectricity. It is obvious that the sample with the Ru bottom electrode shows more and stronger intensity of the o-phase peaks, which could be concluded that the grain size gets larger and the crystalline quality is improved, resulting in the increase of P r.
For practical application in the field of ferroelectric field effect transistor (FeFET) or nonvolatile ferroelectric memories (FeRAM), HfO2-based ferroelectric thin films should achieve superior performance on endurance cycling and data retention. Figure 4 shows the change of P r of the MIM capacitor with a 25-nm-thick thin film and Ni top electrode in capped crystallization as a function of the number of work cycles and retention time, respectively.
There is an evident effect of ferroelectric polarization fatigue during the endurance cycling test when P r has reduced to about 5 μC/cm2 after 106 work cycles, being inferior to traditional ferroelectric materials such as SBT, which will not give a clear indication of fatigue after 109 times of switching. The phenomenon of fatigue in ferroelectric materials is caused by the pinning effect in the electric domain structure when the charged defects or oxygen vacancies are removed under the drive of external electric field and arrive at the surface of electrodes finally, which is called interface scenario admittedly [11].
On the other hand, the test performance of retention time is better. Because of a high Schottky barrier formed in the contact between the HfO2-based thin film and the Ni electrode, lesser intrinsic leakage current has been secured and enforced the optimization of retention of the MIM capacitor. In addition to the contact characteristic, appropriate bias voltage and residual injected interface charge can also improve the data retention significantly [12].
With the influence of external electric field, spontaneous polarization will alter its orientation, inducing the domain switching current (Figure 5). The peaks of current slightly increase, and the values of time to reach the peak gradually decrease with the increasing of electric field strength during the test, suggesting the higher speed of domain wall inversion. Combining with Figure 5b, it is clear that a high P r gives rise to a high polarization reversal current. Through the test results, although the one structure presents the best ferroelectric hysteresis loop, its switching current has risen up to about 80 mA in the 12-V test voltage. Considering the electrode area of only 1.1 × 10−3 cm2, the severe phenomenon of leakage is clear, which needs improvements.
Conclusions
Ferroelectric cells with the Ru bottom electrode and the o-phase 25-nm-thick Hf0.5Zr0.5O2 thin film provided the inductive crystallization of Hf0.5Zr0.5O2 conventional ferroelectric performance. Such devices yielded a P r value of 6 μC/cm2 and E c strength of 2.4 MV/cm measured at 10 kHz. Accordingly, electrical tests were utilized to obtain the characteristic features, such as low retention loss expected for FeFET and FeRAM. Further systematic research is necessary for promoting ferroelectric Hf x Zr1-x O2 as promising materials for lead-free FeFET memory technologies.
References
Boscke TS, Muller J, Brauhaus D, Schroder U, Bottger U. Ferroelectricity in hafnium oxide: CMOS compatible ferroelectric field effect transistors. Appl Phys Lett. 2011;99:102903.
Muller J, Schroder U, Boscke TS, Muller I, Bottger U, Wilde L, et al. Ferroelectricity in yttrium-doped hafnium oxide. J Appl Phys. 2011;110:114113.
Fang RC, Sun QQ, Zhou P, Yang W, Wang PF, Zhang DW. High-performance bilayer flexible resistive random access memory based on low-temperature thermal atomic layer deposition. Nanoscale Res Lett. 2013;8:92.
Muller J, Boscke TS, Brauhaus D, Schroder U, Bottger U, Sundqvist J, et al. Ferroelectric Zr0.5Hf0.5O2 thin films for non-volatile memory applications. Appl Phys Lett. 2011;99:112901.
Mueller S, Mueller J, Singh A, Riedel S, Sundqvist J, Schroeder U, et al. Incipient ferroelectricity in Al-doped HfO2 thin films. Adv Funct Mater. 2012;22:2412–7.
Yu-Zhu G, Hong-Liang L, Geng Y, Ye Z-Y, Zhang Y, Sun Q-Q, et al. Optical and microstructural properties of ZnO/TiO2 nanolaminates prepared by atomic layer deposition. Nanoscale Research Letters. 2013;8:107.
Ding S-J, Chen H-B, Cui X-M, Chen S, Sun Q-Q, Zhou P, et al. Atomic layer deposition of high-density Pt nanodots on Al2O3 film using (MeCp)Pt(Me)3 and O2 precursors for nonvolatile memory applications. Nan Res Lett. 2013;8:80.
Wang J, Zhang TY. Size effects in epitaxial ferroelectric islands and thin films. Phys Rev B. 2006;73:144107.
Kim KT, Kim CI, Kim JG. Effect of LaNiO3 electrode on microstructural and ferroelectric properties of Bi3.25Eu0.75Ti3O12 thin films. Thin Solid Films. 2007;515:8082–6.
Seokhwan B, Seungjun L, Sunyeol J, Semyung K, Wooho J, Seokhoon K, et al. Physical and electrical properties of hafnium-zirconium-oxide films grown by atomic layer deposition. J Electrochem Soc. 2008;155(9):H633–7.
Tagantsev AK, Stolichnov I, Colla EL. Polarization fatigue in ferroelectric films: basic experimental findings, phenomenological scenarios, and microscopic features. J Appl Phys. 2001;90(3):1387–402.
Muller J, Boscke TS, Schroder U, Mikolajick T, Frey L. Nanosecond polarization switching and long retention in a novel MFIS-FET based on ferroelectric HfO2. IEEE Electron Device Lett. 2012;33(2):185–7.
Acknowledgements
This work was supported by the NSFC (61376092, 61376093, 51172046), Shanghai Rising-Star Program (14QA1400200), Program of Shanghai Subject Chief Scientist (14XD1400900), and the S&T Committee of Shanghai (14521103001).
Author information
Authors and Affiliations
Corresponding authors
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
XZ carried out the manufacturing of samples and physical tests, and drafted the manuscript. LC and QS conceived the study and participated in its design and coordination. LW made the electrical tests. PZ, HL, PW, SD, and WZ participated in the design of the study and helped to draft the manuscript. All authors read and approved the final manuscript.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhang, X., Chen, L., Sun, QQ. et al. Inductive crystallization effect of atomic-layer-deposited Hf0.5Zr0.5O2 films for ferroelectric application. Nanoscale Res Lett 10, 25 (2015). https://doi.org/10.1186/s11671-014-0711-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-014-0711-4