Study of Steel Corrosion Cracking Mechanisms for VVER RPV Internals Based on Simulation Tests

  • RADIATION MATERIALS SCIENCE
  • Published:
Inorganic Materials: Applied Research Aims and scope

Abstract

Different hypotheses of irradiation assisted stress corrosion cracking for materials of internals in the light water reactor environment were analyzed. Irradiation-induced grain boundary chromium depletion, localized deformation, and material hardening were considered. Heat treatment and cold working of 18Cr–10Ni–Ti steel were made to simulate the influence of neutron irradiation. Autoclave tests in the light water reactor environment at a temperature 290°C and at a strain rate of 3 × 10–7 s–1 were carried out. 18Cr–10Ni–Ti steel specimens in the initial state, after heat treatment, and after heat treatment followed by cold working were used. Fracture surfaces and lateral surfaces of specimens were examined by scanning electron microscopy. The microstructure of the material was also examined using transmission electron microscopy. It was shown that the grain boundary chromium depletion and the material hardening are not the main causes of corrosion cracking of 18Cr–10Ni–Ti steel in the primary coolant deoxygenated environment. The localization of deformation has a profound effect on corrosion cracking in the absence of the grain boundary sliding. The conditions determining the crack propagation by the corrosion cracking mechanism are defined.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1.
Fig. 2.
Fig. 3.
Fig. 4.
Fig. 5.
Fig. 6.
Fig. 7.
Fig. 8.
Fig. 9.
Fig. 10.
Fig. 11.
Fig. 12.
Fig. 13.

Similar content being viewed by others

REFERENCES

  1. Margolin, B.Z., Varovin, A.Ya., Minkin, A.I., Sorokin, A.A., Piminov, V.A., Evdokimenko, V.V., Fedosovskii, M.E., Sherstobitov, A.E., Ovchinnikov, A.G., Erak, D.Yu., Bobkov, A.V., Timofeev, A.M., Timokhin, V.I., Yakushev, S.V., and Vasil’ev, V.G., Change of geometry of WWER-1000 core baffle: calculations and measurements, Vopr. Materialoved., 2015, no. 3 (83), pp. 182–196.

  2. Karzov, G.P. and Margolin, B.Z., Radiation damage of WWER PVI materials and possible service life prolongation, 10-ya Mezhdunarodnaya nauchno-tekhnicheskaya konferentsiya “Bezopasnost’, effektivnost’ i ekonomika atomnoi energetiki” (The Tenth Int. Sci.-Tech. Conf. “Safety, Efficiency, and Economics of Nuclear Energy Industry”), Moscow: Rosenergoatom, 2016, no. 2, pp. 8–15.

  3. Pogodin, V.P., Bogoyavlenskii, V.L., and Sentyurev, V.P., Mezhkristallitnaya korroziya i korrozionnoe rastreskivanie nerzhaveyushchikh stalei v vodnykh sredakh (Intergranular Corrosion and Corrosion Cracking of Stainless Steel in Aquatic Environment), Moscow: Atomizdat, 1970.

    Google Scholar 

  4. Namburi, H.K., Hojna, A., and Zdenek, F., Effect of tensile strain on microstructure of irradiated core internal material, Proc. 24th Int. Conf. Nuclear Energy for New Europe, Portoroz, 2015.

  5. Ernestova, M., Influence of the neutron spectrum on the sensitivity to IASCC and microstructure of CW 316 material, Proc. Fontevraud 8th Int. Symp. “Contribution of Materials Investigations and Operating Experience to LWRs Safety, Performance and Reliability,” Avignon, France, September15–18, 2014, Paris: Soc. Fr. Energ. Nucl., 2014.

  6. Pokor, C., Toivonen, A., Wintergerst, M., et al., Determination of the time to failure curve as a function of stress for a highly irradiated AISI 304 stainless steel after constant load tests in simulated PWR water environment, Proc. Fontevraud 7th Int. Symp. “Contribution of Materials Investigations to Improve the Safety and Performance of LWRs,” Avignon, France, September 26–30, 2010, Paris: Soc. Fr. Energ. Nucl., 2010, no. O3-A008-T2.

  7. Bruemmer, S.M., Simonen, E.P., Scott, P.M., et al., Radiation-induced material changes and susceptibility to intergranular failure of light-water-reactor core internals, J. Nucl. Mater., 1999, vol. 274, pp. 299–314.

    Article  CAS  Google Scholar 

  8. Arioka, K., Yamada, T., Terachi, T., et al., Influence of carbide precipitation and rolling direction on intergranular stress corrosion cracking of austenitic stainless steels in hydrogenated high-temperature water, Corrosion, 2006, vol. 62, pp. 568–572.

    Article  CAS  Google Scholar 

  9. Lozano-Perez, S., Yamada, T., Terachi, T., et al., Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content, Acta Mater., 2009, vol. 57, no. 18, pp. 5361–5381.

    Article  CAS  Google Scholar 

  10. Fukuya, K., Current understanding of radiation-induced degradation in light water reactor structural materials, J. Nucl. Sci. Technol., 2013, vol. 50, no. 3, pp. 213–254.

    Article  CAS  Google Scholar 

  11. Jacobs, A.J., Wozadlo, J.P., Nakata, K., et al., Radiation effects on the stress corrosion and other selected properties of type 304 and type 316 stainless steel, Proc. Third Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems–Water Reactors, Warrendale, Pa: Metall. Soc., 1987, pp. 673–680.

  12. Scott, P., A review of irradiation assisted stress corrosion cracking, J. Nucl. Mater., 1994, vol. 211, pp. 101–122.

    Article  CAS  Google Scholar 

  13. Bruemmer, S.M., Charlot, L.A., and Atterige, D.G., Sensitization development in austenitic stainless steels-measurement and prediction of thermomechanical history effects, Corrosion, 1987, vol. 44, p. 427.

    Article  Google Scholar 

  14. Jacobs, A.J., Wozadlo, J.P., Nakata, K., et al., Grain boundary composition and irradiation-assisted stress corrosion cracking resistance in type 348 stainless steel, Corrosion, 1994, vol. 50, pp. 731–740.

    Article  CAS  Google Scholar 

  15. Fujii, T., Tohgo, K., Kenmochi, A., et al., Experimental and numerical investigation of stress corrosion cracking of sensitized type 304 stainless steel under high-temperature and high-purity water, Corros. Sci., 2015, vol. 97, pp. 139–149.

    Article  CAS  Google Scholar 

  16. Logan von, H.L., The Stress Corrosion of Metals, New York: Wiley, 1966.

  17. Busby, J.T., Was, G.S., and Kenik, E.A., Isolating the effect of radiation-induced segregation in irradiation-assisted stress corrosion cracking of austenitic stainless steels, J. Nucl. Mater., 2002, vol. 302, pp. 20–40.

    Article  CAS  Google Scholar 

  18. Chung, H.M., Ruther, W.E., Sanecki, J.E., et al., Irradiation-assisted stress corrosion cracking of austenitic stainless steels: recent progress and new approaches, J. Nucl. Mater., 1996, vol. 239, pp. 61–79.

    Article  CAS  Google Scholar 

  19. Fukuya, K., Nishioka, H., Fujii, K., et al., Characterization of surface oxides formed on irradiated stainless steels in simulated PWR primary water, Proc. Fontevraud 8th Int. Symp. “Contribution of Materials Investigations and Operating Experience to LWRs Safety, Performance and Reliability,” Avignon, France, September 15–18, 2014, Paris: Soc. Fr. Energ. Nucl., 2014.

  20. Zuek, V.A., Rud’, R.A., Petel’guzov, I.A., et al., Analysis of corrosion films on stainless steels, Vopr. At. Nauki Tekh., 2010, no. 1 (95), pp. 141–149.

  21. Hanninen, H., Aho-Mantila, I., and Torronen, K., Environment sensitive cracking in pressure boundary materials of light water reactors, Int. J. Pressure Vessels Piping, 1987, vol. 30, pp. 253–291.

    Article  Google Scholar 

  22. Scott, P.M., Environment-assisted cracking in austenitic components, Int. J. Pressure Vessels Piping, 1996, vol. 65, pp. 255–264.

    Article  Google Scholar 

  23. Margolin, B.Z., Fedorova, V.A., and Filatov, V.M., Durability evaluation method for vessel internals of VVER by criterion of initialization of intergranular stress corrosion cracking of irradiated austenitic steels, Inorg. Mater.: Appl. Res., 2011, vol. 2, no. 6, pp. 624–632.

    Article  Google Scholar 

  24. Jiao, Z., Busby, J.T., and Was, G.S., Deformation microstructure of proton-irradiated stainless steels, J. Nucl. Mater., 2007, vol. 361, pp. 218–227.

    Article  CAS  Google Scholar 

  25. Was, G.S., Farkas, D., and Robertson, I.M., Micromechanics of dislocation channeling in intergranular stress corrosion crack nucleation, Curr. Opin. Solid State Mater. Sci., 2012, vol. 16, pp. 134–142.

    Article  CAS  Google Scholar 

  26. Karlsen, W., Diego, G., and Devrient, B., Localized deformation as a key precursor to initiation of intergranular stress corrosion cracking of austenitic stainless steels employed in nuclear power plants, J. Nucl. Mater., 2010, vol. 406, pp. 138–151.

    Article  CAS  Google Scholar 

  27. Margolin, B.Z., Gulenko, A.G., Buchatskii, A.A., Nesterova E.V., and Kashtanov, A.D., Study of the effect of thermal aging on durability and plasticity of Kh18N9 steel, Inorg. Mater.: Appl. Res., 2011, vol. 2, no. 6, pp. 633–639.

    Article  Google Scholar 

  28. Jiao, Z. and Was, G.S., Localized deformation and IASCC initiation in austenitic stainless steels, J. Nucl. Mater., 2008, vol. 382, pp. 203–209.

    Article  CAS  Google Scholar 

  29. Little, E.A., Fracture mechanics evaluations of neutron irradiated type 321 austenitic steel, J. Nucl. Mater., 1986, vol. 139, pp. 261–276.

    Article  CAS  Google Scholar 

  30. Li, X. and Almazouzi, A., Deformation and microstructure of neutron irradiated stainless steels with different stacking fault energy, J. Nucl. Mater., 2009, vol. 385, pp. 329–333.

    Article  CAS  Google Scholar 

  31. Hirth, J.P. and Lothe, J., Theory of Dislocations, New York: McGraw-Hill, 1968.

    Google Scholar 

  32. Chen, Y., Rao, A.S., Alexandreanu, B., et al., Slow strain rate tensile tests on irradiated austenitic stainless steels in simulated light water reactor environments, Nucl. Eng. Des., 2014, vol. 269, pp. 38–44.

    Article  CAS  Google Scholar 

  33. Hänninen, H., Aho-Mantila, I., and Torronen, K., Environment sensitive cracking in pressure boundary materials of light water reactors, Int. J. Pressure Vessels Piping, 1987, vol. 30, pp. 253–291.

    Article  Google Scholar 

  34. Bali, S.C., Kain, V., and Raja, V.S., Effect of low-temperature sensitization on intergranular stress corrosion cracking behavior of austenitic stainless steels in simulated boiling water reactor environment, Corrosion, 2009, vol. 65, no. 11, pp. 726–740.

    Article  CAS  Google Scholar 

  35. Hide, K., Onchi, T., Mayuzumi, M., et al., Intergranular cracking of irradiated thermally sensitized type 304 stainless steel in high-temperature water and inert gas, Corrosion, 1995, vol. 51, no. 10, pp. 757–766.

    Article  CAS  Google Scholar 

  36. Sorokin, A.A., Margolin, B.Z., Kursevich, I.P., Minkin, A.I., Neustroev, V.S., and Beloserov, S.V., Effect of neutron irradiation on tensile properties of materials for pressure vessel internals of WWER type reactors, Vopr. Materialoved., 2011, no. 2 (66), pp. 131–152.

  37. Kursevich, I.P., Margolin, B.Z., Prokoshev, O.Yu., and Kohonov, V.I., Mechanical properties of austenitic steels on neutron irradiation: the effect of various factors, Vopr. Materialoved., 2006, no. 4 (48), pp. 55–68.

  38. Massoud, T., Maurice, V., Klein, L., et al., Nanostructure and local properties of oxide layers grown on stainless steel in simulated pressurized water reactor environment, Corros. Sci., 2014, vol. 84, pp. 198–203.

    Article  CAS  Google Scholar 

  39. Scully, J.C., The Fundamentals of Corrosion, Oxford: Pergamon, 1966.

    Google Scholar 

  40. Jiao, Z., Was, G., and Miura, T., Aspects of ion irradiations to study localized deformation in austenitic stainless steels, J. Nucl. Mater., 2014, vol. 452, pp. 328–334.

    Article  CAS  Google Scholar 

  41. Margolin, B.Z., Gulenko, A.G., Buchatskii, A.A., and Balakin, S.M., Forecasting of crack growth rate in conditions of creep and neutron irradiation, Vopr. Materialoved., 2005, no. 4 (44), pp. 59–68.

  42. Alexandreanu, B., Capell, B., and Was, G.S., Combined effect of special grain boundaries and grain boundary carbides on IGSCC of Ni–16Cr–9Fe–xC alloys, Mater. Sci. Eng., A, 2001, vol. 300, pp. 94–104.

    Article  Google Scholar 

  43. Ulmer, D.G. and Altstetter, C.J., Hydrogen-induced strain localization and failure of austenitic stainless steels at high hydrogen concentrations, Acta Metall. Mater., 1991, vol. 39, no. 6, pp. 1237–1248.

    Article  CAS  Google Scholar 

Download references

ACKNOWLEDGMENTS

Experimental studies were performed on the equipment of the Test and Technological Complex of Irradiated and Radionuclide Materials and Center for Collective Use Composition, Structure, and Properties of Structural and Functional Materials of the National Research Center Kurchatov Institute—CRISM Prometey with financial support of the Ministry of Education and Science of the Russian Federation within the framework of the agreement 14.595.21.0004.

Author information

Authors and Affiliations

  1. National Research Center Kurchatov Institute—CRISM Prometey, 191015, St. Petersburg, Russia

    B. Z. Margolin, N. E. Pirogova, V. A. Potapova, A. A. Sorokin, N. V. Bardashova, S. N. Petrov & M. S. Mikhailov

Authors
  1. B. Z. Margolin
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. N. E. Pirogova
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. V. A. Potapova
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. A. A. Sorokin
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. N. V. Bardashova
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. S. N. Petrov
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. M. S. Mikhailov
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to B. Z. Margolin.

Additional information

The article was translated by the authors.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Margolin, B.Z., Pirogova, N.E., Potapova, V.A. et al. Study of Steel Corrosion Cracking Mechanisms for VVER RPV Internals Based on Simulation Tests. Inorg. Mater. Appl. Res. 9, 1221–1236 (2018). https://doi.org/10.1134/S2075113318060187

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1134/S2075113318060187

Keywords:

Search

Navigation