Plasma spraying of composite coatings is developed and investigated. Three-dimensional capillary porous titanium (3DCP Ti) coatings with a thickness of 1 mm are sprayed using a wire. Hydroxyapatite (HA) coatings with a thickness of 0.08–0.35 mm are sprayed on 3DCP Ti coatings at a temperature of 300–550°C. The joint between the coating and plastic is analyzed at shear. The plastic simulates bone tissue that grows into the coating surface. The heating of the 3DCP Ti coating to 550°С when the HA coating is being sprayed increases the shear strength of the coating with respect to the plastic to 9.8 MPa. Modeling approximations are proposed for the shear of the joint between the coating and the plastic.
Similar content being viewed by others
References
Berndt, C.C., et al., A review of hydroxyapatite coatings manufactured by thermal spray, in Advances in Calcium Phosphate Biomaterials, Berlin: Springer-Verlag, 2014, pp. 267–329.
Dorozhkin, S.V., Review calcium orthophosphate deposits: Preparation, properties and biomedical applications, Mater. Sci. Eng., C, 2015, vol. 55, pp. 272–326.
Sahay, V., Lare, P.J., and Hahn, H., Physical and mechanical characterization of porous coatings for medical and dental devices, Proc. Third National Thermal Spray Conf. “Thermal Spray, Research, and Application, Long Beach, CA, May 20–25, 1990”, Metals Park, 1990, pp. 425–430.
Harris, D.H., Bioinert CP–Ti and Ti–6Al–4V Coatings by the Arc-Plasma Spray Process, Dayton, OH: Titan. Dev. Assoc., 1990, pp. 636–645.
Borsari, V., Giavaresi, G., Fini, M., Torricelli, P., Salito, A., Chiesa, R., and Giardino, R., Physical characterization of different-roughness titanium surfaces, with and without hydroxyapatite coating, and their effect on human osteoblast-like cells, J. Biomed. Mater. Res., Part B, 2005, vol. 75, no. 2, pp. 359–368.
Borsari, V., Fini, M., Giavaresi, G., Tschon, M., Chiesa, R., Chiusoli, L., and Giardino, R., Comparative in vivo evaluation of porous and dense duplex titanium and hydroxyapatite coating with high roughnesses in different implantation environments, J. Biomed. Mater. Res., 2009, vol. 89, no. 2, pp. 550–560.
Kalita, V.I., Gnedovets, A.G., Mamaev, A.I., Mamaeva, V.A., Malanin, D.A., and Pisarev, V.B., Plasma deposited bioactive porous coatings for intrabone implants, Proc. 17th Int. Symp. on Plasma Chemistry (ISPC–17), Toronto, August 7–12, 2005, Toronto: Univ. of Toronto Press, 2005,pp. 1105–1106.
Gnedovets, A.G., Kalita, V.I., Komlev, D.I., Yerokhin, A.L., and Matthews, A., Plasma spraying of capillary- porous coatings: experiments, modeling and applications, Int. Vacuum Congr. IVC-16/ICSS-12/NANO-8, Venice, Trento: Italian Vac. Soc., 2004, pp. 398–399.
Kalita, V.I., Bocharova, M.A., Gnedovets, A.G., Trushnicova, A.S., Yerokhin, A.L., Matthews, A., and Shaternicov, B.N., Structure and mechanical properties of novel plasma sprayed titanic capillary-porous for intrabone implants, Int. Vacuum Congr. IVC-16/ICSS-12/NANO-8, Venice, Trento: Italian Vac. Soc., 2004, pp. 58–59.
Kalita, V.I., Bocharova, M.A., Trushnikova, A.S., and Shaternikov, B.N., Surface structure of titanium materials intended for intraosseous implants, Russ. Metall. (Engl. Transl.), 2005, no. 3, pp. 282–288.
Kalita, V.I. and Gnedovets, A.G., Plasma spraying of capillary porous coating: Experiments, modeling, and biomedical applications, Plasma Process. Polym., 2005, no. 2, pp. 485–492.
Van Oirschot B.A., Eman R.M., Habibovic P., Leeuwenburgh S.C., Weinans H., Alblas J., de Boer J. Comparing the osteophilicity of bone implant surface modifications in a cassette model on the decorticated goat spinal transverse process. Surface Modifications for Endosseous Implant Materials, 2015, pp. 21–43.
Kalita, V.I., Komlev, D.I., Komlev, V.S., and Radyuk, A.A., The shear strength of three-dimensional capillaryporous titanium coatings for intraosseous implants, Mater. Sci. Eng., C, 2016, vol. 60, pp. 255–259.
Xien, Y.T., Zhengn, X.B., Huang, L.P., and Ding, C.X., Key,short communication. In vitro cytocompatibility of plasma-sprayed dicalciumsilicate/zirconia composite coatings, Ceram. Int., 2013, vol. 39, pp. 4707–4711.
Rakngarm Nimkerdphol, A., Otsuka, Y., and Mutoh, Y., Effect of dissolution/precipitation on the residual stress redistribution of plasma-sprayed hydroxyapatite coating on titanium substrate in simulated body fluid (SBF), J. Mech. Behav. Biomed. Mater., 2014, vol. 36, pp. 98–108.
Khalid M., Mujahid M., Khan A. Nusair, and Rawat R.S., Dip-coating of nanohydroxyapatite on titanium alloy with plasma assisted ?-alumina buffer layer: A novel coating approach, J. Mater. Sci. Technol., 2013, vol. 29, no. 6, pp. 557–564.
Demnati, I., Grossin, D., Combes, C., and Rey, C., Plasma-sprayed apatite coatings: Review of physical–chemical characteristics and their biological consequences, J. Med. Biol. Eng., 2014, vol. 34, no. 1, pp. 1–7.
Mohseni, E., Zalnezhad, E., and Bushroa, A.R., Comparative investigation on the adhesion of hydroxyapatite coating on Ti–6Al–4V implant: A review paper, Int. J. Adhes. Adhes., 2014, vol. 48, pp. 238–257.
Clemens, J.A.M., Klein, C.P.A.T., Vriesde, R.C., Rozing, P.M., and de Groot, K., Healing of large (2 mm) gaps around calcium phosphate-coated bone implants: a study in goats with a follow-up of 6 months, J. Biomed. Mater. Res., 1998, vol. 40, pp. 341–349.
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © V.I. Kalita, D.I. Komlev, A.Yu. Ivannikov, A.A. Radyuk, V.S. Komlev, V.I. Mamonov, M.A. Sevast’ianov, A.S. Baikin, 2016, published in Perspektivnye Materialy, 2016, No. 10, pp. 37–47.
Rights and permissions
About this article
Cite this article
Kalita, V.I., Komlev, D.I., Ivannikov, A.Y. et al. The shear strength of Ti–HA composite coatings for intraosseous implants. Inorg. Mater. Appl. Res. 8, 296–304 (2017). https://doi.org/10.1134/S2075113317020083
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S2075113317020083