Abstract
In this study, microstructures and properties of the Mg-Al alloy with strontium addition are studied. After the addition of strontium structure analysis was performed to investigate phase evaluation. The potentiostatic measurements were also carried out in 3.5% NaCl solution with the results showing that the effect of adding strontium element to magnesium- aluminum alloys on corrosion behavior of this metal was strongly dependent on microstructure of the final alloy (e.g. grain size, type, intermetallic compounds, etc.). The major second phase included Al4Sr and Al2Sr, but the amount and morphology of these compounds was different in the alloys. The results indicated a reduction in the amount of Mg17 Al12 phase and corrosion rate as well as a rise in the resistance to cavitations.
Similar content being viewed by others
References
Novak, M., Vojtech, D., Novak, P., and Vitu, T., Appl. Surf. Sci., 2011, vol. 257, p. 9982.
Sadreddini, S., Salehi, Z., and Rassaie, H., Appl. Surf. Sci., 2015, vol. 324, p. 393.
Campo, M., Carboneras, M., Lopez, M.D., et al., Surf. Coat. Technol., 2008, vol. 230, p. 3224.
Yu, S.R., Liu, Y., Li, W., et al., Compos., Part B, 2011, vol. 43, p. 1070.
Friedrich, H. and Schumann, S., J. Mater. Process. Technol., 2001, vol. 117, p. 276.
Janz, A., Grobner, J., Mirkovic, D., et al., Intermetallics, 2007, vol. 15, p. 506.
Gao, X., Zhu, S.M., Muddle, B.C., and Nie, J.F., Scr. Mater., 2005, vol. 53, p. 1321.
Wu, L., Pan, F.-S., Yang, M.-B., et al., Trans. Nonferrous Met. Soc. China, 2011, vol. 21, p. 784.
Witte, F., Hort, N., Vogt, C., et al., Curr. Opin. Solid State Mater. Sci., 2008, vol. 12, p. 63.
Kim, B.H., Kyung, C.P., Yong, H.P., and Ik, M.P., J. Mater. Sci. Eng. A, 2011, vol. 528, p. 808.
L'Espérance, G., Plamondon, P., and Kunst, M., Intermetallics, 2010, vol. 18, p. 1.
Manson, J.D., Typical Micro Structure of Cast Metals, London: Inst. Br. Found. Men, 1981, p. 32.
Nayeb-Hashemi, A.A. and Clark, J.B., Phase Diagrams of Binary Magnesium Alloys, Materials Park, OH: ASM Int., 1998, p. 376.
Zhang, Z., Coutune, A., and Luo, A., Scr. Mater., 1998, vol. 39, p. 45.
Gruzleski, J.E. and Aliraveci, C.A., US Patent 5143564, 1992.
Zhou, J.X. and Wang, J., Metall. Mater. Trans. A, 2006, vol. 37, p. 1333.
Suzuki, A., Saddock, N.D., Lara-Curzio, E., et al., Metall. Mater. Trans. A, 2007, vol. 38, no. 2, p. 420.
Fan, J., Xu, B., Wang, S., et al., Rare Metal Mater. Eng., 2012, vol. 41.
Nam, N.D., Kim, W.C., Kim, J.G., et al., J. Alloys Compd., 2011, vol. 509, p. 4839.
Byeong, H.K., Kyung, C.P., Yong, H.P., and Ik, M.P., J. Mater. Sci. Eng. A, 2011, vol. 528, p. 808.
Zhou, W., Corros. Sci., 2010, vol. 52, p. 1035.
Liu, C., Xin, Y., Tang, G., and Chu, P.K., Mater. Sci. Eng. A, 2007, vol. 456, p. 350.
Ghayad, I.M., Girgis, N.N., and Abdul-Azim, A.N., J. Metall. Mater. Sci. Eng., 2013, vol. 3, p. 21.
Wu, T., Peng, X.D., Wang, D.Y., and Xie, W.D., Mater. Sci. Forum, 2009, vols. 610–613, p. 964.
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
Rights and permissions
About this article
Cite this article
Nayeri, T., Yari, M. & Sadreddini, S. Effect of Sr on the Microstructure and Properties of Mg-6Al Alloy. Prot Met Phys Chem Surf 52, 273–278 (2016). https://doi.org/10.1134/S2070205116020209
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S2070205116020209