Abstract
The linear poly(L-lactide) and poly(D-lactide) (PLLA, PDLA) with relative lower molecular weights were synthesized, and PLLA/PDLA blends at various content of PDLA were prepared by solution casting. The morphology and growth of poly(lactide) stereocomplex (PLA SC) were investigated by polarized optical microscope. Results revealed that the morphology of SC in the blends strongly depended on the content of PDLA and the annealing temperature. Dendritic and irregular SC with looser structure developed in the specimens with lower content of PDLA, and regular SC spherulites with birefringent and compact structure produced in the specimens with higher content of PDLA. The growth rate (G) of SC increased gradually as the content of PDLA enhanced in the blends. As the annealing temperature enhanced, the SC with brighter and more compact structure appeared. The G value increased at first before declining as the annealing temperature elevated from the 130 to 190°C. And the nonlinear behavior of the growth of SC in the dissimilar specimens was analyzed.
Similar content being viewed by others
References
X. Pang, X. L. Zhuang, Z. H. Tang, and X. S. Chen, Biotechnol. J. 5, 1125 (2010).
R. E. Drumright, P. R. Gruber, and D. E. Henton, Adv. Mater. 12, 1841 (2000).
J. Pinto, E. Solorzano, M. A. Rodriguez-Perez, B. Notario, J. Escudero, M. D. Leon, and D. Velasco, Diffus. Solids Liq. IX 353, 131 (2014).
M. Hutchinson, J. Dorgan, D. Knauss, and S. Hait, J. Polym. Environ. 14, 119 (2006).
N. Delpouve, G. Stoclet, A. Saiter, E. Dargent, and S. Marais, J. Phys. Chem. B 116, 4615 (2012).
A. J. Svagan, A. Åkesson, M. Cárdenas, S. Bulut, J. C. Knudsen, J. Risbo, and D. Plackett, Biomacromolecules 13, 397 (2012).
J. Shao, Y. L. Liu, S. Xiang, X. C. Bian, J. R. Sun, G. Li, X. S. Chen, and H. Q. Hou, Chin. J. Polym. Sci. 33, 1713 (2015).
H. Tsuji and Y. Ikada, Macromolecules 25, 5719 (1992).
W. Hoogsteen, A. R. Postema, A. J. Pennings, G. Ten Brinke, and P. Zugenmaier, Macromolecules 23, 634 (1990).
D. Sawai, K. Takahashi, T. Imamura, K. Nakamura, T. Kanamoto, and S. H. Hyon, J. Polym. Sci., Part B: Polym. Phys. 40, 95 (2002).
L. Cartier, T. Okihara, Y. Ikada, H. Tsuji, J. Puiggali, and B. Lotz, Polymer 41, 8909 (2000).
J. M. Zhang, Y. X. Duan, H. Sato, H. Tsuji, I. Noda, S. Yan, and Y. Ozaki, Macromolecules 38, 8012 (2005).
J. Shao, J. Sun, X. Bian, Y. Zhou, G. Li, and X. Chen, CrystEngComm 15, 6469 (2013).
J. Shao, J. Sun, X. Bian, Y. Cui, Y. Zhou, G. Li, and X. Chen, Macromolecules 46, 6963 (2013).
Y. Ikada, K. Jamshidi, H. Tsuji, and S. H. Hyon, Macromolecules 20, 904 (1987).
L. Chang and E. M. Woo, Macromol. Chem. Phys. 212, 125 (2011).
T. Okihara, M. Tsuji, A. Kawaguchi, K. I. Katayama, H. Tsuji, S. H. Hyon, and Y. Ikada, J. Macromol. Sci., Part B: Phys. 30, 119 (1991).
H. Tsuji and Y. Ikada, Polymer 40, 6699 (1999).
M. Kakuta, M. Hirata, and Y. Kimura, Polym. Rev. 49, 107 (2009).
M. Hirata and Y. Kimura, Polymer 49, 2656 (2008).
D. Karst and Y. Yang, Macromol. Chem. Phys. 209, 168 (2008).
H. Tsuji, S. H. Hyon, and Y. Ikada, Macromolecules 24, 5651 (1991).
J. Shao, J. Sun, X. Bian, Y. Cui, G. Li, and X. Chen, J. Phys. Chem. B 116, 9983 (2012).
J. Shao, S. Xiang, X. Bian, J. Sun, G. Li, and X. Chen, Ind. Eng. Chem. Res. 54, 2246 (2015).
H. Tsuji and Y. Ikada, Macromolecules 26, 6918 (1993).
J. Zhang, Y. Duan, A. J. Domb, and Y. Ozaki, Macromolecules 43, 4240 (2010).
J. Shao, Y. Guo, S. Xiang, D. Zhou, X. Bian, J. Sun, G. Li, and H. Hou, CrystEngComm 18, 274 (2016).
H. Tsuji and Y. Tezuka, Biomacromolecules 5, 1181 (2004).
P. Pan, L. Han, J. Bao, Q. Xie, G. Shan, and Y. Bao, J. Phys. Chem. B 119, 6462 (2015).
S. Nouri, C. Dubois, and P. G. Lafleur, Polymer 67, 227 (2015).
S. Brochu, R. E. Prud’homme, I. Barakat, and R. Jerome, Macromolecules 28, 5230 (1995).
S. Saeidlou, M. A. Huneault, H. Li, P. Sammut, and C. B. Park, Polymer 53, 5816 (2012).
S. H. Li and E. M. Woo, Polym. Int. 57, 1242 (2008).
R. Lv, R. Tian, B. Na, P. Zhang, and Q. Liu, J. Phys. Chem. B 119, 15530 (2015).
J. Bai, J. Wang, W. Wang, H. Fang, Z. Xu, X. Chen, and Z. Wang, ACS Sustainable Chem. Eng. 4, 273 (2016).
M. Brzezinski and T. Biela, Macromolecules 48, 2994 (2015).
B. Na, J. Zhu, R. Lv, Y. Ju, R. Tian, and B. Chen, Macromolecules 47, 347 (2014).
D. Maillard and R.E. Prud’homme, Macromolecules 43, 4006 (2010).
H. Xu, D. Wu, X. Yang, L. Xie, and M. Hakkarainen, Macromolecules 48, 2127 (2015).
X. Wang and R.E. Prud’homme, Macromolecules 47, 668 (2014).
L. Chang and E. M. Woo, Polymer 52, 68 (2011).
Author information
Authors and Affiliations
Corresponding author
Additional information
The article is published in the original.
Rights and permissions
About this article
Cite this article
Shao, J., Guo, Y., Ye, S. et al. The morphology and growth of PLA stereocomplex in PLLA/PDLA blends with low molecular weights. Polym. Sci. Ser. A 59, 116–123 (2017). https://doi.org/10.1134/S0965545X1701014X
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0965545X1701014X