Abstract
Low-cost TiB whiskers reinforced titanium matrix composite (TMCs) was fabricated with enhanced mechanical performances using in situ technologies and hot working. Morphologies observation indicates that needle-like TiB whiskers with a hexagonal transverse section grow along the [010] direction due to B27 crystal structure and its growth mechanism. Mechanical properties tests show that the mechanical behavior of the TiB whiskers reinforced TMCs is dependent on the deformation amplitudes applied in hot-working. The improvement in yield strength by hot-working is attributed to the TiB whiskers realignment and the refinement of microstructure. Models are constructed to evaluate the realignment of TiB whisker during deformation and the increase in yield strength of the composite at elevated temperatures. These models clarify the alignment effect of TiB whiskers under various deformation amplitudes applied in hot-workings and reveals the yield strength dependence on TiB whiskers orientation.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Titanium matrix composites (TMCs) present high strength at room and moderately elevated temperature. Ceramic reinforcements in TMCs can improve the modulus, strength and creep resistance of the matrix significantly1,2,3. Many reinforcements have been used in TMCs, such as TiB, TiC, SiC, Al2O3 and TiB2. TiB ceramic is regarded as a powerful reinforcement because it presents excellent chemical stability and thermal stability in the Ti matrix4,5,6,7,8. Among the various designs of TMCs, the in situ synthesis techniques, in which reinforcements are formed in situ in matrix through reactions between reactants with matrix, have been paid great attention due to the low interface contamination and incompatibility between the matrix and the reinforcements9,10,11,12,13,14,15.
The in situ processing techniques have evolved over last decades for the preparation of ceramic phase reinforced composites, including self-propagating high-temperature synthesis, mechanical alloying, reactive squeeze casting, exothermic dispersion technology, reactive hot pressing process, reactive spontaneous infiltration, direct reaction synthesis, combustion assisted cast and directed melt oxidation process16,17,18,19,20,21,22,23,24,25,26. But cost of most preparation methods of TMCs is high. On the other hand, mechanical properties of the TMCs are not improved significantly by the just addition of reinforcement simply. The facile processing is under challenge for the TMCs fabrication with high mechanical properties.
The mechanical behavior of TMCs is different from those of matrix alloy, but it depends on the matrix, the reinforcement, reinforcement/matrix interfaces and processing technology. In recent years, numerous studies have been performed on hot-working to process TMCs based on the traditional hot-working technology of Ti alloys, such as rolling, extrusion and forging. These studies indicate that mechanical properties of the composite are great dependent on the microstructure of matrix, inclusions and second phases, and these factors can be controlled by hot-working27,28,29,30,31,32. Furthermore, Gorsse et al.33 found that the composite with aligned TiB whiskers along tensile direction presented higher strengths compared to that in which the orientation of TiB whiskers is random. Guo34 studied the evolution of TiB whiskers orientation in the composite during rolling suggesting a model to predict the orientation of TiB whiskers with deformation amplitude. However, the effect of TiB orientation on the mechanical behavior of TMCs is not clear enough, and the model between them has not been set up by present studies. And these studies may be very useful in the optimizing mechanical behavior of such composites.
The aim of this work is to study the effect of deformation amplitude applied in hot-working on TiB whiskers orientation and the mechanical behavior dependent on the TiB whisker realignment. In this work, mechanical behaviors of the TMC with various deformation amplitudes applied in hot-working is characterized and analyzed. It was clarified that the improvement in yield strength by hot-working results from the TiB whiskers realignment and the refinement of microstructure. And a model is constructed to evaluate the yield strength of TMCs reinforced with whiskers based on the dependence of the inclinations of whiskers and grain size of matrix.
Results and Discussion
TiB whisker morphology and formation mechanism
Figure 1(a) shows the TiB distribution in the cast composite and morphologies of TiB deep etched. The size of TiB needles diameter in this work are about 1 μm to 3 μm with an aspect ratio about 12.2 ± 4.3. Surface of TiB needles is clean and flat. TEM bright field image of TiB and corresponding selected area diffraction patterns are presented in Fig. 1(b), which indicates that needle-like TiB whisker is B27 orthorhombic structure and lattice parameters a = 0.612 nm, b = 0.306 nm and c = 0.456 nm. And the whisker axis of TiB is parallel to the [010] crystal orientation of the B27 cell. TiB grow faster along the [010] direction leading to a rod-like morphology that was reported by several research groups. Li et al.35 found that TiB prepared using the reactive hot pressing was elongated needles with hexagonal cross-sections. The size of TiB whiskers in cross-section is about 1~2 μm with an aspect ratio about 20. Rod-like TiB with a size 2~6 μm in cross-section and an aspect ratio 10~15 was prepared in combustion assisted cast processed Ti matrix composite by Ranganath et al.36. Similarly, rod-like TiB with a length about 4 μm and aspect ratios 5~10 was also prepared in reactive squeeze casting processed TMCs37,38,39,40. Diameter and aspect ratio of TiB whiskers may be different through various synthetic methods. The diameter of TiB in this work is similar to that of TiB by reactive hot pressing, but its aspect ratio is similar to that using CAC method.
The formation of needle TiB morphology can be explained from its crystal structure. Lundstrom41 suggested the crystal structures of many borides are all constructed by the same crystal cell: a trigonal prism with a boron atom lying at the center and six Ti atoms lying at six vertexes. In the B27 crystal structure, such trigonal prisms are assembled along their edges. Along the [010] direction of B27 structure, boron atoms form zigzagging chains and boron-free ‘pipes’ with a trapezoidal cross-section are formed by Ti atoms, as presented in Fig. 1(c). According to the ‘Periodic Bond Chain’ theory, TiB would grow faster along the [010] direction of B27 than along the [10], [101] and [100] directions. And TiB would grow into needle or whisker morphology with the axis parallel to the [010] crystal direction of B27 structure. Because growth of crystals is usually restricted by the slowest-growing crystal planes, (10), (101 and (100) planes form the surfaces of TiB whiskers, as presented in Fig. 1(b,c).
Modeling of the realignment of TiB whiskers by hot-working
It is well understood that TiB whiskers in the composite realign along the flow direction during composite deformation. Guo21 studied the realignment effect of TiB by rolling suggesting a model to evaluate the variation of TiB whiskers orientation with deformation amplitude. In this model, the orientation of TiB whiskers is defined as the orientation angle that is the angle of length directions of TiB with respect to the rolling direction, and the variation of orientation angle of TiB whiskers with deformation amplitude is described by a probability density function. In Eq. (1), P(α) is the initial probability density function, but P(θ) is the probability density function after the hot-working, as presented in Fig. 2(a), then the following equation can be obtained:
If the thickness of the composite becomes 1/n of the initial one after the hot-working, the of TiB whisker orientation (orientation angle θ after deformation) can be calculated with the initial orientation angle α and the deformation amplitude (n), as presented in Fig. 2(a). The orientation angle θ after deformation can be calculated with Eq. (2):
In Eq. 1–3 α is the initial orientation angle of TiB whisker (the angle of the length of TiB whisker direction respect to horizontal direction) and θ is the orientation angle of the TiB whisker after deformation.
Derivation of Eq. (3) to α:
Substituting tan α = n2tan θ, which is based on the Eq. (2), into Eq. (4):
Substituting Eq. (5) into Eq. (1):
Due to the initial orientation angles of TiB whiskers distributing uniformly from 0 to in the cast composite, the probability density of TiB orientation angles is a constant. Because the integral value of the probability density from 0 to is 1, then
Thus,
Substituting this value into Eq. (6):
According to Eq. (9), the probability density function of TiB whiskers P(θ) is a function of the deformation amount. Figure 2(b) shows the effect of the deformation amplitude applied in this work on the probability density function P(θ). As presented in Fig. 2(b), the increase of deformation amplitude applied in hot-working decreases the orientation angle of TiB whiskers significantly, which should affect the mechanical behavior of the composite.
Modeling of strengthening effect of TiB whisker
A shear-lag model42 was used to evaluate the strengthening effect of TiB whiskers in composites with the length direction of whiskers parallel to the tensile direction.
where σym is the yield strength of the matrix. l/d and V are the aspect ratio and the volume fraction of the whiskers, respectively. In Eq. (10), the length direction of the whiskers must be parallel to the loading direction during the tensile tests of the composite. However, the orientation of TiB whiskers in this composite does not meet this requirement. The orientation of the TiB whisker in the composite on its strengthening effect should be taken into account.
For such composites in which orientation of TiB whiskers is disorder in the matrix, Fukuda et al.43 suggested a probability theory to evaluate orientation and length of whiskers on its strengthening effect in composites reinforced by whiskers. In this model, the yield strength increase of the composite by TiB (ΔσTiB) was modified by adding an strengthening factor C0 ranging from 0 to 1 in Eq. (10), and C0 is dependent on the orientation and length of TiB whiskers in the composite. The strengthening effect of TiB can be predicted by Eq. (11), and C0 is given by Eq. (12):
where θ is the orientation angle of TiB, i.e. the angle of the length direction of whiskers with respect to tensile direction; θ0 is the critical angle that determines whether a whisker is a “bridging fiber”or not; p(θ) is the TiB orientation angle probability density function; h(l) is the TiB whiskers length probability density function; β is a constant ranging from 0 to 1 determining whether a whisker is a “bridging fiber” or not44; l, lc and , are the maximum length, critical length and average length of the TiB whiskers, respectively. The value of average aspect ratio was calculated to be 12.2 ± 4.3, but that of the critical aspect ratio of TiB whiskers is about 2.07 45. Due to the significantly higher value of average aspect ratio compared with that of the critical aspect ratio, all TiB whiskers in the present composite are regarded as the bridging whiskers in order to simplify the model. Then β is equal to 0 and θ0 is equal to . Under above assumption, based on Eq. (12) C0 can be simplified to be:
Based on Eq. (13), it is necessary to evaluate the probability density function of TiB whiskers (p()) firstly in order to calculate its strengthening factor C0.
It is well understood that TiB whiskers formed randomly in the preparation process of the composite. Then, TiB whiskers orientation angles in the cast composite distribute uniformly from 0 to , and the TiB whisker orientation angles probability density is a constant. Because the integral of this probability density from 0 to is 1.
Substituting Eq. (9) into Eq. (13), TiB whisker strengthening factor variation with deformation amplitude applied in hot-working on can be calculated by Eq. (16):
Effect of TiB whiskers realignment on mechanical behavior of TMC
Mechanical properties of the composite with various deformation amplitudes by tensile tests are presented in Fig. 3(a), in which the tensile direction is parallel to the longitudinal direction of the composite rods. Figure 3(a) shows that hot working increases yield strength of the composite significantly. The increase of the yield strength by hot-working may result from two factors: (a) TiB whisker realignment by deformation of the composite. (b) Grain/microstructure refinement because of dynamic recrystallization during the hot-working. Figure 3(b) shows the effect of TiB whisker realignment and grain/microstructure refinement of the composite by the hot working with various deformation amplitudes.
The increase of yield strength of the composite by grain/microstructure refinement can be calculated by Hall–Petch equation46. The strengthening effect by grain/microstructure refinement is not ignorable when the volume fraction of reinforcement in composite is low47. The strengthening effect by the grain/microstructure refinement can be calculated by:
where σym and σ0 are the yield strength and strength constant of the matrix, respectively. K and Gd are the strengthening coefficient and the grain diameter, respectively48. As Eq. (11) described, yield strength of the composite can be modeled as following including the TiB whiskers strengthening effect:
In above equation, σyc represents the composite yield strength. Taking account into the strengthening effect by grain/microstructure refinement, substitute Eq. (17) into Eq. (18):
Figure 3(c) presents the modeled yield strengths with Eq. 19 and the measured values of the composite by tensile tests. As presented in Fig. 3(c), the modeled and measured results are in good agreement with each other and show that this model is effective. But for the composite with large amplitude deformation, all yield strengths modeled by this model are larger slightly than measure values. The overestimation in yield strength for the composite with large amplitude deformation may result from the break of some TiB whiskers during hot-working, which is a common observation in the composite with large amplitude deformation. The break of TiB whisker decreases its strengthening effect due to the decrease in its aspect ratio, but this effect has not been included in this modeling.
Based on above results and discussion, it can be seen that the mechanical behavior of the TMCs is dependent on orientation of TiB whiskers. The improvement in yield strength by hot-working can be attributed to the TiB whiskers realignment and the refinement of grain/microstructure. A suggested model can be used to evaluate the yield strength of TMCs including the realignment of TiB whisker with various deformation amplitudes applied in hot-working.
Methods
Preparation of the in situ composite
Composite used in this work was TiB ceramic reinforced Ti-1100 matrix. The composite preparation flow chart is presented in Fig. 4. In the preparation of this composite, the raw materials are sponge titanium (grade I), boron powder (99.95%, particle size 4~8 μm), aluminum thread (98%), silicon powder (99.95%, particle size 6~12 μm), sponge zirconium (99.5%), and Ti–Sn, Al–Mo master alloys. The composition of Ti-1100 was prepared with Ti–6Al–2.75Sn–4Zr–0.4Mo–0.45Si in weight percent. Sponge titanium, boron powder and other raw materials were prepared with 4 v. % TiB/Ti-1100 component, and volume fraction of the TiB was added with formula (20).
In above formula, iV, iM, ρR and ρM is TiB volume fraction, TiB weight fraction, density of TiB and density of Ti-1100 alloy, respectively.
Proportional sponge titanium, boron powder and other raw materials were mechanically mixed firstly. Then, the mixed raw materials were pressed into preformed bars in a mold with a press machine. The preformed bars were welded into big ones as the electrode used in the subsequent melting processing. The electrode bars was melted in a vacuum arc furnace. During the melting process, through the reaction between titanium with boron TiB was prepared (Ti + B → TiB). In order to improve the composite chemical homogeneity, the composite was melted three times. Homogenization of the composite was carried out at 1423 K for 1.5 h then was cooled by air. After homogenization, the composite was treated by a hot working on a pressure machine. Before the hot-working, molds used in the hot working were heated to 1123 K, the composite was heated to 1273 K. The composite temperature measured by infrared device was ensured above 1123 K during the hot-working treatment. After hot-working, samples were cooled to ambient temperature by water. The deformation amplitude applied in the hot-working was calculated with the reduction ratio in thickness, where , H0 is the thickness of the sample before hot-working, and Hi is the thickness of the sample after hot-working. In particular, it should be pointed out that the composite preparation method used in this work was same to the preparation method that usually used to produce Ti alloys, as presented in Fig. 4.
Characterization
Morphology observation samples of the composite were cut from ingot then ground and mechanical polished. Samples for scan electron microscopy (SEM) observation were etched by Kroll’s reagent (2~6 mL HF, 4~12 mL HNO3, 100 mL water). Samples for transmission electron microscopy (TEM) observation were prepared with a twin-jet device operated at 293~303 K and 30~50 V with an electrolyte 10% HClO4 and 90% CH3COOH. TEM samples were observed on a JEM-2010 electron microscope operated at 200 kV.
Plate samples for tensile tests were machined from the composite with 3.0 mm in thickness, 12 mm in width and 50.0 mm in gauge length. Tensile tests were carried out on a Zwick/Roell 100 kN tensile testing machine. Before tests, the tensile samples were heated to test temperatures in a furnace equipped on the tensile machine and held for 5 min. The tensile tests started with 5.0 × 10−3 s−1 strain rate. Tensile tests were carried out three times for each sample, and the presented result of the sample was the average of the three times.
Additional Information
How to cite this article: Ma, F. et al. The mechanical behavior dependence on the TiB whisker realignment during hot-working in titanium matrix composites. Sci. Rep. 6, 36126; doi: 10.1038/srep36126 (2016).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Ibrahim, I. A., Mohamed, F. A. & Lavernia, E. J. Particulate reinforced metal matrix composites-a review. J. Mater. Sci. 26, 1137–1156 (1991).
Kagawa, Y., Fujita, T. & Okura, A. Temperature dependence of tensile mechanical properties in SiC fiber-reinforced Ti matrix composite. Acta Metall. Mater. 42, 3019–3026 (1994).
Jansson, S., Dal Bello, D. J. & Leckie, F. A. Transverse and cyclic thermal loading of the fiber reinforced metal-matrix composite SCS6/Ti-15-3. Acta Metall. Mater. 42, 4015–4024 (1994).
Tjong, S. C. & Ma, Z. Y. Microstructural and mechanical characteristics of in-situ metal matrix composites. Mater. Sci. Eng. R. 29, 49–113 (2000).
Lu, W. J., Zhang, D., Wu, R. J. & Mori, H. Preparing TiC titanium-matrix composites using in situ technology. Metall. Trans. A 33, 3055–3059 (2002).
Nardone, V. C. & Prewo, K. M. On the strength of discontinuous silicon carbide reinforced aluminum composites. Scripta Metal 20, 43–48 (1986).
Ma, Z. Y., Tjong, S. C. & Gen, L. In-situ Ti-TiB metal-matrix composite prepared by a reactive pressing process. Scripta Mater. 42, 367–373 (2000).
Ma, F. C., Wang, T. R., Liu, P., Li, W., Liu, X. K., Chen, X. H., Pan, D. & Lu, W. J. Mechanical properties and strengthening effects of in situ (TiB+TiC)/Ti-1100 composite at elevated temperatures. Mater. Sci. Eng. A 654, 352–358 (2016).
Lu, W. J., Zhang, D., Wu, R. J., Sakata, T. & Mori, H. Creep rupture life of in situ synthesized (TiB+TiC)/Ti matrix composites. Scripta Materialia 44, 2449–2455 (2001).
Liu, Z. D., Zhang, X. C., Xuan, F. Z., Wang, Z. D. & Tu, S. T. In situ synthesis of TiN/Ti3Al intermetallic matrix composite coatings on Ti6Al4V alloy. Mater. Design 37, 268–273 (2012).
Fan, Z., Miodownik, A. P., Chandrasekaran, L. & Ward-Close, M. Young’s moduli of in situ Ti/TiB composites obtained by rapid solidification processing. J. Mater. Sci. 29, 1127–1134 (1994).
Huang, L. J., Geng, L., Xu, H. Y. & Peng, H. X. In situ TiC particles reinforced Ti6Al4V matrix composite with a network reinforcement architecture. Mater. Sci. Eng. A 528, 2859–2862 (2011).
Huang, L. J., Geng, L. & Peng, H. X. Microstructurally inhomogeneous composites: Is a homogeneous reinforcement distribution optimal? Progress in Mater. Sci. 71, 93–168 (2015).
Rastegari, H. & Abbasi, S. M. Producing Ti-6Al-4V/TiC composite with superior properties by adding boron and thermo-mechanical processing. Mater. Sci. Eng. A 564, 473–477 (2013).
Jia, L., Li, S. F., Imai, H., Chen, B. & Kondoh, K. Size effect of B4C powders on metallurgical reaction and resulting tensile properties of Ti matrix composites by in-situ reaction from Ti-B4C system under a relatively low temperature. Mater. Sci. Eng. A 614, 129–135 (2014).
Choi, Y., Mullins, M. E., Wijayatilleke, K. & Lee, J. K. Fabrication of metal matrix composites of TiC-Al through self-propagating synthesis reaction. Metall. Trans. 23A, 2387–2392 (1992).
Zhang, L. C., Xu, J. & Eckert, J. Thermal stability and crystallization kinetics of mechanically alloyed TiC∕Ti-based metallic glass matrix composite. J. Appl. Phys. 100, 033514 (2006).
Satyaprasad, K., Mahajan, Y. R. & Bhanuprasad, V. V. Strengthening of Al/20 v/o TiC composites by isothermal heat treatment. Scripta Metall. Mater. 26, 711–716 (1992).
Mitra, R., Chiou, W. A., Weertman, J. R. & Fine, M. E. Interfaces in as-extruded XD Al/TiC and Al/TiB2 metal matrix composites. J. Mater. Res. 8, 2380–2392 (1993).
Soboyejo, W. O., Lederich, R. J. & Sastry, S. M. L. Mechanical behavior of damage tolerant TiB whisker-reinforced in situ titanium matrix composites Acta Metall. Mater. 42, 2579–2591 (1994).
Ranganath, S. & Mishra, R. S. Steady state creep behaviour of particulate- reinforced titanium matrix composites. Acta Mater. 44, 927–935 (1996).
Nagorka, M. S., Lucas, G. E. & Levi, C. G. Novel oxide-dispersion-strengthened copper alloys from rapidly solidified precursors: part 2. Creep behavior. Metall. Mater. Trans. 26A, 873–881 (1995).
Zhang, L. C. & Attar, H. Selective Laser Melting of Titanium Alloys and Titanium Matrix Composites for Biomedical Applications: A Review. Adv. Eng. Mater. 18, 463–475 (2016).
Gao, Y. P., Shi, R. P., Nie, J. F., Dregia, S. A. & Wang, Y. Z. Group theory description of transformation pathway degeneracy in structural phase transformations. Acta Mater. 109, 353–363 (2016).
Tjong, S. C., Wu, S. Q. & Zhu, H. G. Wear behavior of in situ TiB2-Al2O3/Al and TiB2-Al2O3/Al-Cu composites. Composites Sci. Technol. 59, 1341–1347 (1999).
Attar, H., Bönisch, M., Calin, M., Zhang, L. C., Scudino, S. & Eckert, J. Selective laser melting of in situ titanium–titanium boride composites: Processing, microstructure and mechanical properties. Acta Mater. 76, 13–22 (2014).
Park, J. M., Lim, K. R., Park, E. S., Hong, S., Park, K. H., Eckert, J. & Kim, D. H. Internal structural evolution and enhanced tensile plasticity of Ti-based bulk metallic glass and composite via cold rolling. J. Alloys Compounds 615, S113–S117 (2014).
Basiri Tochaee, E., Madaah Hosseini, H. R. & Seyed Reihani, S. M. On the fracture toughness behavior of in-situ Al-Ti composites produced via mechanical alloying and hot extrusion. J. Alloys Compounds 681, 12–21 (2016).
Gao, Y., Zhou, N., Yang, F., Cui, Y., Kovarik, L., Hatcher, N., Noebe, R., Mills, M. J. & Wang, Y. P-phase precipitation and its effect on martensitic transformation in (Ni,Pt)Ti shape memory alloys. Acta Mater. 60, 1514–1527 (2012).
Benghalem, A. & Morris, D. G. Microstructure and strength of wire-drawn Cu-Ag filamentary composites. Acta Mater. 45, 397–406 (1997).
Gao, Y., Zhou, N., Wang, D. & Wang, Y. Pattern formation during cubic to orthorhombic martensitic transformations in shape memory alloys. Acta Mater. 68, 93–105 (2014).
Morris, D. G. & Munoz-Morris, M. A. High creep strength, dispersion- strengthened iron aluminide prepared by multidirectional high-strain forging. Acta Mater. 58, 6080–6089 (2010).
Gorsse, S. & Miracle, D. B. Mechanical properties of Ti6Al-4V/TiB composites with randomly oriented and aligned TiB reinforcements. Acta Mater. 51, 2427–2442 (2003).
Guo, X. L., Wang, L. Q., Wang, M. M., Qin, J. N., Zhang, D. & Lu, W. J. Effects of degree of deformation on the microstructure, mechanical properties and texture of hybrid-reinforced titanium matrix composites. Acta Mater. 60, 2656–2667 (2012).
Li, D. X., Ping, D. H., Lu, Y. X. & Ye, H. Q. Characterization of the microstructure in TiB-whisker reinforced Ti alloy matrix composite. Mater. Lett. 16, 322–326 (1993).
Lu, W. J., Zhang, D., Zhang, X. N., Wu, R. J., Sakata, T. & Mori, H. Microstructure and tensile properties of in situ (TiB+TiC)/Ti6264 (TiB:TiC = 1:1) composites prepared by common casting technique. Mater. Sci. Eng. A 311, 142–150 (2001).
Soboyejo, W. O., Lederich, R. J. & Sastry, S. M. L. Mechanical behavior of damage tolerant TiB whisker-reinforced in situ titanium matrix composites. Acta Metall. Mater. 42, 2579–2591 (1994).
Ragarajan, S., Aswath, P. B. & Soboyejo, W. O. Microstructure development and fracture of in-situ reinforced Ti-8.5Al-1B-1Si. Scripta Mater. 35, 239–245 (1996).
Dubey, S., Soboyejo, W. O. & Srivatsan, T. S. Deformation and fracture properties of damage tolerant in-situ titanium matrix composites. Appl. Compos. Mater. 4, 361–374 (1997).
Tong, X. C., Shen, N. F. & Liu, B. C. Structure of a rapidly solidified Al-Fe-Ti-C alloy. J. Mater. Sci. 30, 3680–3689 (1995).
Lundstrom, T. In ‘Boron and refractory borides’, (edited by Matkovich, V. I. ) pp. 351–376 (Springer-Verlag, Berlin, 1977).
Cox, H. The elasticity and strength of paper and other fibrous materials. J Appl Phys 3, 72–79 (1952).
Fukuda, H. & Chou, T. W. Probabilistic theory of the strength of short-fibre composites with variable fibre length and orientation. J. Mater. Sci. 17, 1003–1007 (1982).
Bader, M. G., Chou, T. W. & Quigley, J. J. Proceedings of the symposiums on new developments and applications in composites. TMS-AIME, St. Louis (1978).
Xiao, L., Lu, W. J., Qin, J. N., Chen, Y. F., Zhang, D. & Wang M. M. Steady state creep of in situ TiB plus La2O3 reinforced high temperature titanium matrix composite. Mater. Sci. Eng. A 499, 500–504 (2009).
Hall, E. O. The deformation and aging of mild steel. Proc. Phys. Soc. London B 64, 747–752 (1951).
Se, I., Tamirisakandala, S., Miracle, D. B. & Ramamurty, U. Microstructural effects on the mechanical behavior of a modified Ti-6Al-4V alloys. Acta Mater. 55, 4983–4993 (2007).
Sauer, C. & Lutjering, G. Influence of α layers at βgrain boundaries on mechanical properties of Ti-alloys. Mater. Sci. Eng. A 319–321, 393–397 (2001).
Acknowledgements
Financial supports from the Shanghai Research Council (project IDs: 09ZR1422100, 11441900500, 11441900501) and Hyper Tech Research Council of Shanghai (project IDs: 10YZ94) are gratefully acknowledged. F.C.M. acknowledges the experimental support from the Key Laboratory of Advanced Metal-based Electrical Power Materials.
Author information
Authors and Affiliations
Contributions
F.C.M. designed the study with advice from P.L. and W.J.L. The composite was prepared by F.C.M. and W.J.L. The hot forging of the composite was performed by F.C.M., W.L. and X.H.C. Microstructural observation and electron diffraction patterns were obtained by F.C.M., W.L. and K.Z. Mechanical properties of the composite was measured by X.K.L. and F.C.M. Mechanical model mathematical model used in this work were suggested and discussed by F.C.M. and D.P. All authors discussed the results; F.C.M. wrote the manuscript, with discussions mainly with P.L. and D.P.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Ma, F., Liu, P., Li, W. et al. The mechanical behavior dependence on the TiB whisker realignment during hot-working in titanium matrix composites. Sci Rep 6, 36126 (2016). https://doi.org/10.1038/srep36126
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep36126
- Springer Nature Limited
This article is cited by
-
Dry-Sliding Wear Mechanisms of Shot-Peened Additive Manufactured Alpha Titanium Featuring TiB Particles
Tribology Letters (2021)
-
Effects of Substrate Composition and Treatment Times on the Erosive Wear of Titanium Aluminide Coating: Prepared By Pack Cementation
Journal of Bio- and Tribo-Corrosion (2021)
-
Effect of Forging on Microstructure, Mechanical Properties and Acoustic Emission Characteristics of Al Alloy (2014): 10 wt.% SiCp Composite
Journal of Materials Engineering and Performance (2019)
-
Oxygen-Induced Mechanical Property Variations of Rapidly Solidified Ti-Based Bulk Metallic Composites
Journal of Materials Engineering and Performance (2019)
-
Microstructures and mechanical properties of in situ TiC–β–Ti–Nb composites with ultrafine grains fabricated by high-pressure sintering
Scientific Reports (2018)