Abstract
An experimental determination of the mean vortex velocity in superconductors mostly relies on the measurement of flux-flow resistance with magnetic field, temperature, or driving current. In the present work we introduce a method combining conventional transport measurements and a frequency-tuned flashing pinning potential to obtain reliable estimates of the vortex velocity. The proposed device is characterized using the time-dependent Ginzburg-Landau formalism, where the velocimetry method exploits the resonances in mean vortex dissipation when temporal commensuration occurs between the vortex crossings and the flashing potential. We discuss the sensitivity of the proposed technique on applied current, temperature and heat diffusion, as well as the vortex core deformations during fast motion.
Similar content being viewed by others
Introduction
The resistive state of superconducting thin films in an external magnetic field and applied transport current is a consequence of the dissipative motion of vortices1,2. While the slowly moving Abrikosov vortices retain their cylindrical core, it has been theoretically shown that vortices traveling at high velocities exhibit core deformation and tailgating of quasiparticles (for recent studies of the behavior of vortex core quasiparticles under applied current see Ref. 3,4), due to which moving vortices tend to align and connect to the wake of the preceding vortex5. Such elongated vortices are often referred to as Abrikosov-Josephson, resembling the ones found at step-edges and grain boundaries6,7,8,9,10. Their further acceleration in increasing current leads to the formation of a phase-slip11, a line of suppressed superconductivity across which the phase of the superconducting order parameter changes by 2π, and along which phase singularities move with high velocity. Those coreless yet moving singularities are often referred to as Josephson vortices (in analogy to those in S-N-S junctions12,13,14,15).
Real-time observations of the vortex motion are notoriously difficult to achieve, because vortex velocity in the condensate largely exceeds the sweeping rate in most of the scanning probe techniques and the time between two consecutive frames in snapshot techniques16,17. Estimates of the average vortex velocity reported in literature have been mainly obtained from transport measurements18,19,20. Relative vortex velocity, and vortex-vortex interaction within the dynamic regime have also been studied in the past, using the Corbino setup21. Even the dispersion of the vortex velocities has been measured22. All of the obtained results concurred that the speed of the Abrikosov vortices can be as high as several km/s, while the velocity of Josephson vortices can rise to 100 km/s23.
The investigation of magnetic flux dynamics in superconductors by means of (passive) stroboscopic effects has been of experimental interest since the late 1970’s24. More recently, theoretical investigations of motion of the flux patterns under periodic light illumination predicted (active) stroboscopic resonances in resistance and voltage when the excitation frequency matches the frequency of the characteristic vortex dynamics25. Following the same prescription, in this paper we devise a concept for vortex velocity measurement stemming from the stroboscopic states in a superconductor with a dynamic pinning landscape. We show that this approach, in which we take into account spatial and temporal heat dissipation, is able to precisely capture vortex velocities, even very high ones, and thereby discern different vortex phases at the crossover from Abrikosov to Josephson ones, each of which are tunable either by external modulation, or by temperature, current, or magnetic field.
Results
We consider a thin superconducting film (of size L × W, with thickness d ≪ λ, ξ, where λ and ξ are the field penetration depth and superconducting coherence length, respectively), exposed to an external magnetic field H, and dc transport current density J, which exhibits recurring stroboscopic resonances when exposed to external potential that periodically suppresses and recovers superconductivity in the channel (of width Wch) across the specimen, as depicted in Fig. 1. Such time-periodic potential can be achieved in several ways. For example, mode-locked solid-state lasers can emit pulse repetition rates between 50 MHz and a few gigahertz26 (in extreme cases above 100 GHz), and can modulate the superconducting condensate by localized heating. Note that in order to confine light to few tens of nm (corresponding to the size of the channel in our work), one can envisage to use nanoscale metallic waveguides which transform the long wavelength incoming light into surface plasmon polaritons able to be focused down to the required scales27. Recently demonstrated nano-heating source28, using a single Ag nanowire as resistive nano-heater and where possible bandwidth can be tuned by the pulsed current, could possibly be used to locally deplete the superconducting condensate periodically. Alternatively, one can envisage the use of low-temperature scanning electron microscopy29, operating down to 4 K, where electron beam sizes of few tens of nm are equipped with fast electrostatic beam blankers with rising time of sub-ns and repetition rate of 300 MHz.
As a representative example we use parameters for NbN thin films30 [ξ(0) = 4.2 nm being the coherence length at 0 K, the critical temperature Tc = 12.7 K, and the normal state conductivity σn = 4241 S/cm] and the sample size of L × W × d = 400 × 100 × 6 nm3. Bath temperature is set to T0 = 0.9Tc, to respect the validity domain of the employed time-dependent Ginzburg-Landau (TDGL) theory2, and applied field is H = 90 mT. Using the TDGL simulations2,31 (see Methods) we reveal the dynamic response of the sample to the applied current in the presence of an external magnetic field and a periodic confining potential across the sample, by calculating the temporal evolution of the spatial profile of the superconducting order parameter Ψ(r, t), the Cooper-pair density |Ψ(r, t)|2 and the electrostatic potential φ. For the pulsating potential we use the temporal oscillation of local temperature, hence we also take into account the diffusion of heat in the system. For the latter, the equation of thermal balance32 is employed to monitor the spatial and temporal evolution of the temperature T(r, t):
where parameters C, K, and h are the dimensionless heat capacity, heat conductivity and heat-transfer coefficients, respectively (see Methods for details). (∇φ)2 represents the Joule losses generated by the normal component of the current density, and VT is the excess heat generated by the external source, modelled by inside the channel of width Wch = 5ξ(0), and 0 outside ( is the amplitude of the potential, and τ is the period of the oscillations).
The calculated time-averaged voltage as a function of the channel flashing period [V(τ)] is shown in Fig. 2 for five values of applied current density J. As the channel transits between hot (ON) and cold (OFF), and vice versa, the superconducting order parameter in the channel is being suppressed and recovered, respectively, creating a favorable path for vortices to travel across the sample. The order parameter Ψ(r, t) relaxes over a finite time, of the order of the Ginzburg-Landau time τGL(0)/(1 − T/Tc) (see Methods), and is also influenced by the pinning potential period, τ, which in our simulations is at least one order of magnitude larger than τGL(0). Because of these competing time-scales, it is obvious that thermal variations will not cause instantaneous changes in Ψ(r, t). In fact, the response of the condensate in the channel depends on the thermal diffusion of the heat supplied by the time-dependent pinning potential. The time over which the thermal diffusion becomes relevant is proportional to the ratio C/K in Eq. (1). In principle, the parameters used to calculate heat diffusion (thermal capacity, conductivity and heat transfer coefficient) are temperature dependent33 and also depend on the substrate properties (e.g. thickness of the substrate ds, heat capacity cs, and heat conductivity ks of the substrate). For example, in the refs 32,34 effective heat capacity cf + ds cs/d and effective heat conductivity kf + ds ks/d are used (cf and kf are the real-unit heat capacity and heat conductivity of the film, respectively), with heat transfer coefficient ks/ds which depends entirely on the thermal properties of the substrate. However, it is the respective ratio’s of C, K, and h that determine the equilibration of temperature in the system. Since the temperature dependence of individual parameters is not generic (or known) for all materials, we restrict our analysis to few characteristic parametric choices, known in literature and covering the regimes of both slow and fast heat diffusion in the system. Mainly for the computational convenience, we use C = 0.03 (which corrensponds to the real-unit heat capacity of the film cf = 0.15 mJ/cm3K, see Methods), K = 0.06 (with corresponding heat conductivity of the film in real units kf = 1.33 mW/cmK, see Methods), and h = 2 × 10−4 (the real-unit heat transfer coefficient of the film hf = 16.94 W/cm2K, see Methods)34,35,36,37. We note, however, that if only temperature-independent thermal parameters of the superconducting film close to Tc are taken into account, one can use Wiedemann-Franz law to estimate the dimensionless heat capacity C = 0.65 (cf = 3.25 mJ/cm3K) and heat conductivity K = 0.06 (kf = 1.33 mW/cmK) independently of the considered material. In reality the substrate influence can hardly be neglected, and for example, in NbN films considered in ref. 38 the effective heat capacity was dscs/d + cf = 2.4 mJ/cm3K, total heat conductivity dsks/d + kf = 1.1 mW/cmK, and hf = 56.5 W/cm2K. Thus, for either set of parameters the thermalization time τth defined by the ratio C/K does not exceed 100τGL(0), which is considerably shorter than the period τ of the thermal potential VT used in this work. A case of C and K leading to a thermalization time τth exceeding the period of the pinning potential τ would lead to heat accumulation in the channel due to the ineffective heat removal via diffusion, causing full depletion of superconductivity (i.e. forming a permanent Josephson junction, and completely suppressing stroboscopic effects, which is not of interest in the present analysis). Additionally, we estimate the time needed for a vortex to cross the considered sample, τcross, to be of the order of 1000τGL(0). When τ is in the range (τth, τcross) effective heat removal is established, causing the distinct ON and OFF states in the channel, but there exists no synchronised vortex motion in the sample, and thus no characteristic dynamics is found. Only when vortex motion in the channel will be completely governed by switching between ON and OFF states, causing the particular stroboscopic behavior of the condensate.
Stroboscopic resonances and the link to vortex velocity
Here we point out general features of the stroboscopic regime governed by the switching between hot and cold states, in the presented setup. In the regime τ > τcross a synchronization between the vortex motion and the flashing channel will arise whenever the flashing period is long enough for an integer number of vortices to cross the sample along the depletion region, i.e. τ = nτcross. During the synchronization, stroboscopic effect appears and manifests as recurring voltage drops in the V(τ). Quasi-periodic behavior of the V(τ) characteristics shown in Fig. 2 corroborates that, where in each consecutive stroboscopic state an additional vortex participates in the dynamics, relating the order of the resonance n exactly to the number of crossing vortices while the channel is open. In other words, the shift in the period τ between the subsequent resonances exactly corresponds to the average crossing time of one vortex, τcross. This enables one to extract the average vortex velocity from the (experimentally accessible) voltage characteristics shown in Fig. 2 (as W/τcross). During each resonance, the average voltage of the system follows a 1/τ functional dependence (specifically Vn = 2πn/τ), which is indicated by dotted lines in Fig. 2. To emphasize again, the drops in V(τ) exhibit periodicity which is exactly equal to the τcross. Note that if the Eq. (1) is not taken into account (instantaneous heat diffusion and perfect heat removal in the system, as discussed in ref. 25 voltage resonances given in Fig. 2 are more narrow, with significantly shorter periodicity (~0.6τ cross). Fractional resonances observed in Fig. 2 (e.g. around τ = 600τGL(0) and 1600τGL(0), for J = 4.9 × 10−3j0, where j0(0) is current density unit, see Methods) originate from odd number of vortices traversing the channel over the pulse duration of 2τ. With prolonged flashing the occurrence of fractional resonances diminishes. By taking the above mentioned parameters of NbN, one can estimate the frequency (1/τ) presented in Fig. 2 to be in the range 4 GHz (shown stroboscopic resonances are expected to persist at lower frequencies as well) to 120 GHz26, which is still below the gap frequency of NbN (νgap ≈ 1 THz). The same values yield τcross ≈ 40 ps, vortex velocity km/s, and observed voltage drops during the resonances ≈0.5 mV. The required pinning frequency to properly observe the resonances must be higher than 1/τcross (≈25 GHz). It is possible to lower 1/τcross by selecting a material with larger τGL(0) or longer inelastic scattering time25. Alternatively, one can force vortices to travel longer distances by making the samples wider, thereby proportionally increasing τcross. Additionally, we note here that all superconducting and vortex-related time-scales become longer if the temperature is lowered, without any qualitative changes to the reported stroboscopic behavior of the superconducting condensate, which is seemingly more convenient for practical realization of our predictions. However, since the specific heat, the thermal conductivity, and the heat transfer coefficient decrease with decreasing temperature, the heating becomes more localized - which may lead to heat accumulation so that periodic oscillations of the order parameter may no longer be achieved39. Note that this problem of local periodic heating and continuous cooling has been addressed in ref. 40 in the context of current driven phase slips in superconducting nanowires.
Characteristic dynamics of the condensate
Figure 3(a,b) present the real-time voltage V(t) for one value of the current density (J = 5.2 × 10−3j0), during the first [τ = 1100τGL(0)] and the second [τ = 2260τGL(0)] resonance, respectively (see Fig. 2). Instances (1)-(6) point out characteristic features of the superconducting dynamics through Cooper-pair density snapshots. The temporal dependence of the voltage in Fig. 3(a) (overlapped with the pinning intensity profile - dotted red line) correlates the vortex entry with a voltage peak at instance (1), just as the channel switches ON, pushing away the pre-existing vortex towards the sample edge. The subsequent exit of the pre-existing vortex produces a small peak in the voltage at instance (2). As the channel cools down one vortex remains in the sample, minimizes the voltage (3), and the cycle ends. One should easily notice that effectively, one vortex has crossed the sample during the flash of the potential, for an oscillation period corresponding to the first resonance. Dynamics during the second resonance in Fig. 3(b) shows a more complex voltage profile. Starting from channel ON, point (4) denotes time frame during which entrance of two new vortices in the sample occurs, as well as the exit of the pre-existing vortex [see snapshots (4.1), (4.2) and (4.3)]. At instance (5) the first of the two vortices that entered the sample leaves, with accompanying peak in the voltage. Finally, as the channel turns OFF, one remaining vortex is trapped, and the cycle ends. To facilitate the visualization and comparison of the first four resonances between the vortex dynamics and the pinning potential, we provide the animated data (entitled Supplementary-Animation1.gif) in the Supplementary Material.
Vortex velocimetry
Typically in experiments the vortex velocity can only be reliably estimated at high magnetic fields, since vortex-vortex interaction dominates over vortex-pinning and therefore the velocity distribution function is very narrow41. As discussed above, stroboscopic resonances occur with periodicity that matches the crossing time of one additional vortex (τcross) from which one can determine the average vortex velocity during the resonance. To verify this, in our numerical simulations we directly tracked the velocities of individual vortices as they pass along the channel, by developing a software capable of mapping the vortex trajectory in real time (shown in Fig. 4, for one value of applied current). The obtained velocity profiles resemble the velocity profiles measured in ref. 24. From this distribution of instantaneous vortex velocities we can compute the average vortex velocity (red line) which indeed matches the ratio of the channel length W and the corresponding V(τ) resonance period, τcross (green line), as predicted in the above analysis. Furthermore, by substituting the characteristic values of ξ(0) and Tc for different materials one can easily compare the vortex velocities to be expected. Using the parameters of Al (ξ(0) = 90 nm, τGL(0) = 0.38 ps, Tc = 1.37 K42) and Pb (ξ(0) = 33 nm, τGL(0) = 72 fs, Tc = 7.2 K43), one obtains the velocity multiplier ratios: and , estimating expected velocity for Abrikosov vortices to be significantly larger than in NbN.
Discussion
In what follows, we discuss the thermal effects related to the resonances and the vortex behavior through V(τ) characteristics shown in Fig. 5 for the same current used in Fig. 4, in the case when: (a) bath temperature is varied and (b) maximal temperature in the channel is varied. From Fig. 5(a) one can conclude that the resonant states are well preserved at low bath temperatures (), and that their behavior follows the trend exhibited in Fig. 2, where all vortices traverse the sample in a single line along the channel [snapshot (1) in Fig. 5(a)]. Especially for the lowest considered bath temperature T0 = 0.86Tc, stroboscopic states appear at integer resonances, without exhibiting fractional resonances. Clear stroboscopic states persist up to a bath temperature exceeding 0.9Tc, after which four additional crossing channels appear next to the pinning channel, along which vortices traverse with mismatched velocities. This excess vortex motion outside the pinning channel causes a jump to the higher dissipative state [snapshot (2) in Fig. 5(a), corresponding to T0 = 0.92Tc]. In principle, stroboscopic resonances in the V(τ) characteristic still exist in the higher dissipative state, but are concealed and heavily smeared by the voltage harmonics produced from freely moving vortices out of the depletion region.
As a consequence of an external potential modulation, heat released in the channel varies, which affects the vortex motion in the channel. In Fig. 5(b) we show how the V(τ) characteristics change with increase of the thermal potential amplitude, . For a weak amplitude [] non-invasive regime is instated, where the vortex motion is barely affected, due to which the resonances are accompanied by very weak voltage oscillations. These oscillations become more visible as the amplitude is increased [], and we have resonant states comparable to results in Fig. 2. For further increased amplitude, more and more vortices pass through the channel during the resonance, so the V(τ) shifts to the left. For the selected value of the flashing period τ = 1000τGL, we show that by simple tuning of in the range [0.6h(Tc − T0)/Tc, h(Tc − T0)/Tc] one can switch between different resonant states and thereby manipulate the vortex velocity in the channel, thus entering the invasive mode. Moreover, the obtained results show that by varying the heat released in the channel, one can even controllably switch between different vortex phases and study them in more detail. Snapshots of the Cooper-pair density in Fig. 5(b) indicate that the vortex core deforms progressively with increasing heating, so that the found vortex phase at the same resonance for sequentially increasing can change from the Abrikosov vortex (1), to Abrikosov-Josephson transition (2), and then Josephson vortex (3)6,15,44,45,46 [we provide animated data for different vortex phases in the Supplementary Material (entitled Supplementary-Animation2.gif)]. The accompanying change in τcross indicates that vortex velocity multiply increases during the transition between these vortex phases. Finally we emphasize that for any given applied magnetic field (of magnitude lower than Hc2), one can tune either the current or the local temperature in order to switch between different resonances and study different types of vortices with core deformation.
To summarise, in this manuscript we presented the unique properties of the resistive state in a type II superconductor with a thermally induced flashing channel of depleted superconductivity. Stroboscopic synchronization between the vortex dynamics and the thermal oscillations in the channel is found and we directly link the shift between the subsequent resonances in the measured voltage versus the flashing period to the time needed for one additional vortex to traverse the channel. As a consequence, the voltage characteristics versus the period of the pinning potential provides a direct and reliable measure of the vortex velocity, unattainable otherwise, and that in a broad range of velocities, from slow Abrikosov vortices, to tenfold faster Josephson ones. Our velocimetry method therefore enables experimental confirmation of the limits of vortex velocity and the realistic characterization of the speed of the emerging vortex-based devices and technology47,48,49,50.
Methods
In this work, the generalized time-dependent Ginzburg-Landau (TDGL)2,31 equation is used to describe the behavior of the superconducting condensate (with order parameter Ψ(r, t)) in the presence of applied magnetic field (H) (with vector potential (A)) and transport current density J, when time-dependent thermal pinning potential is present in the specimen:
where u = 5.79 is the ratio of the relaxation times for amplitude and phase of the order parameter2,31,51, and the parameter Γ = 2τinΔ(0)/ħ = 10 (τin is the inelastic phonon-electron scattering time) effectively characterizes the viscosity of the superconducting condensate to the vortex motion. This equation is coupled with the thermal balance equation [Eq. (1)] and with the equation for the electrostatic potential φ:
The generalized time-dependent Ginzburg-Landau theory used in this work was derived for the gapless superconductors containing high concentration of paramagnetic impurities. In the gapless case, the mechanism for pair-breaking is the strong inelastic electron-phonon scattering, and all the relevant quantities, such as Ψ and A, must relax on the time-scale longer than the inelastic phonon-electron scattering time (τGL(0)/(1 − T/Tc) ≫ τin). Characteristic length over which these relaxation processes occur is (where vF is the Fermi velocity, and l is the mean free path). This length is the distance over which an electric field can penetrate into the superconductor, and in the case of gapless superconductors it must be below the coherence length . For majority of the materials, the previous conditions for slow temporal and spatial variation are satisfied at temperatures close to Tc.
In our formalism, all distances are expressed in units of ξ(0), time in units of τGL(0) = πħ/8kBTcu, and temperature in units of Tc. Ψ is in units of Δ(0) = 4kBTcu1/2/π, φ in units of φ0(0) = ħ/e*τGL(0), vector potential A is scaled to As(0) = Hc2(0)ξ(0) [Hc2(0) = Φ0/2πξ2(0)], and current density to j0 = σnφ0(0)/ξ(0), where σn is normal state conductivity. In Eq. (1) dimensionless heat capacity is obtained as , dimensionless heat conductivity as , while the dimensionless heat transfer coefficient is defined as .
At the superconductor-vacuum (SV) boundary, the current density component perpendicular to the interface vanishes [nSV(∇ − iA)Ψ = 0 and nSV∇φ = 0, where the nSV is the unit vector perpendicular to the surface of the SV boundary], and all heat is assumed to be transferred to the substrate (nSV∇T = 0). We consider metallic current leads (SN contacts), where the applied current transforms completely into normal current (−nSN∇φ = J and Ψ = 0, nSN being the unit vector perpendicular to the surface of the SN boundary). There, the temperature is set to the critical temperature (TSN = Tc).
In all simulations, adaptive simulation time is taken, with an initial value of 5 × 104τGL(0), sufficiently long for a system to reach the dynamic equilibrium, and then extended by thirty temporal periods of the pinning potential (tsim = 5 × 104τGL(0) + 30τ) for averaging of the outputs. The above equations are solved self-consistently in an iterative procedure, where the generalized time-dependent Ginzburg-Landau equation [Eq. (2)] is solved using a combination of Euler and Gauss-Seidel method52. We used the spectral Fourier method to solve the equation for the electrostatic potential, while the solver for the equation of thermal balance [Eq. (1)] was based the Crank-Nicolson scheme and Alternating Direction Implicit method.
Additional Information
How to cite this article: Jelić, Ž.L. et al. Velocimetry of superconducting vortices based on stroboscopic resonances. Sci. Rep. 6, 35687; doi: 10.1038/srep35687 (2016).
References
Ivlev, B. I., Kopnin, N. B. & Maslova, L. A. Dynamics of the resistive state of a superconductor. Zh. Eksp. Teor. Fiz. 78, 1963–1978 (1980).
Ivlev, B. I. & Kopnin, N. B. Electric currents and resistive states in thin superconductors. Adv. in Phys. 33, 47–114 (1984).
Maldonado, A., Vieira, S. & Suderow, H. Supercurrent on a vortex core in 2H-NbSe2: Current-driven scanning tunneling spectroscopy measurements. Phys. Rev. B 88, 064518 (2013).
Berthod C. Quasiparticle spectra of Abrikosov vortices in a uniform supercurrent flow. Phys. Rev. B 88, 134515 (2013).
Vodolazov, D. Y. & Peeters, F. M. Rearrangement of the vortex lattice due to instabilities of vortex flow. Phys. Rev. B 76, 014521 (2007).
Gurevich, A. Nonlocal Josephson electrodynamics and pinning in superconductors. Phys. Rev. B 46, 3187(R) (1992).
Roditchev, D. et al. Direct observation of Josephson vortex cores. Nat. Phys. 11, 332–337 (2015).
Brun, C. et al. Remarkable effects of disorder on superconductivity of single atomic layers of lead on silicon. Nat. Phys. 10, 444–450 (2014).
Yoshizawa, S. et al. Imaging Josephson vortices on the surface superconductor Si(111)-( )-In using a scanning tunnelling microscope. Phys. Rev. Lett. 113, 247004 (2014).
Andronov, A., Gordion, I., Kurin, V., Nefedov, I. & Shereshevsky, I. Kinematic vortices and phase slip lines in the dynamics of the resistive state of narrow superconductive thin film channels. Physica. C 213, 193–199 (1993).
Sivakov, A. G., Glukhov, A. M. & Omelyanchouk, A. N. Josephson behavior of phase-slip lines in wide superconducting strips. Phys. Rev. Lett. 91, 267001 (2003).
Skocpol, W. J., Beasley, M. R. & Tinkham, M. Phase-slip centers and nonequilibrium processes in superconducting tin microbridges. J. Low Temp. Phys 16, 145 (1974).
Kuznetsov, V. I. & Tulin, V. A. Synchronization of high-frequency vibrations of slipping phase centers in a tin whisker under microwave radiation. Sov. Phys. JETP 86, 1364 (1998).
Wallraff, A. et al. Quantum dynamics of a single vortex. Nature 425, 6954 (2003).
Berdiyorov, G. R. Milošević, M. V. & Peeters, F. M. Kinematic vortex-antivortex lines in strongly driven superconducting stripes. Phys. Rev. B 79, 184506 (2009).
Wertheimer, M. R. & Gilchrist, J. G. Flux jumps in type II superconductors. J. Phys. Chem. Solids 28, 2509 (1967).
Bolz, U., Biehler, B., Schmidt, D., Runge, B. U. & Leiderer, P. Dynamics of the dendritic flux instability in Yba2Cu3O7−δ films. Europhys. Lett. 64, 517 (2003).
Grimaldi, G. et al. Speed limit to the Abrikosov lattice in mesoscopic superconductors. Phys. Rev. B 92, 024513 (2015).
Wördenweber, R. Mechanism of vortex motion in high-temperature superconductors. Rep. Prog. Phys. 62, 187–236 (1999).
Wördenweber, R., Hollmann, E., Schubert, J., Kutzner, R. & Panaitov, G. Regimes of flux transport at microwave frequencies in nanostructured high-Tc films. Phys. Rev. B 85, 064503 (2012).
López, D. et al. Spatially resolved dynamic correlation in the vortex state of high temperature superconductors. Phys. Rev. Lett. 82, 1277 (1999).
Forgan, E. M. et al. Measurement of vortex motion in a type-II superconductor: A novel use of the neutron spin-echo technique. Phys. Rev. Lett. 85, 3488 (2000).
Lee, J. U., Nordman, J. E. & Hohenwarter, G. Josephson vortex flow in superconducting single crystal Bi2Sr2CaCu2Ox . Appl. Phys. Lett. 67, 1471 (1995).
Chimenti, D. E. & Huebner, R. P. Stroboscopic study of flux dynamics in superconductors during current-induced breakdown. Solid State Commun. 21, 467–470 (1977).
Jelić, Ž. L., Milošević, M. V., Van de Vondel, J. & Silhanek, A. V. Stroboscopic phenomena in superconductors with dynamic pinning landscape. Sci. Rep. 5, 14604 (2015).
Mangold, M. et al. Pulse repetition rate scaling from 5 to 100 GHz with a high-power semiconductor disk laser. Opt. Express 22, 6099 (2014).
Schuller, J. A. et al. Plasmonics for extreme light concentration and manipulation. Nat. Mat. 9, 193–204 (2010).
Yeo, J. et al. Single Nanowire Resistive Nano-heater for Highly Localized Thermo-Chemical Reactions: Localized Hierarchical Heterojunction Nanowire Growth. Small 10, 5014 (2014).
Gross, R. & Koelle, D. et al. Low-temperature scanning electron microscopy of superconducting thin films and Josephson junctions. Rep. Prog. Phys. 57, 651 (1994).
Bartolf, H. et al. Current-assisted thermally activated flux liberation in ultrathin nanopatterned NbN superconducting meander structures. Phys. Rev. B 81, 024502 (2010).
Kramer, L. & Watts-Tobin, R. J. Theory of dissipative current-carrying states in superconducting filaments. Phys. Rev. Lett. 40, 1041 (1978).
Gurevich, A. V. & Mints, R. J. Self-heating in normal metals and superconductors. Rev. Mod. Phys. 59, 941 (1987).
Suderow, H., Brison, J. P., Marcenat, C. & Salce, B. Thermal diffusivity and conductivity measurements for Si:P near the metal-insulator transition. J. Phys.: Conden. Matter 8, 999–1009 (1996).
Vodolazov, D. Y., Peeters, F. M., Morelle, M. & Moshchalkov, V. V. Masking effect of heat dissipation on the current-voltage characteristics of a mesoscopic superconducting sample with leads. Phys. Rev. B 71, 184502 (2005).
Berdiyorov, G. R. et al. Large magnetoresistance oscillations in mesoscopic superconductors due to current-excited moving vortices. Phys. Rev. Lett. 109, 057004 (2012).
Berdiyorov, G. R., Milošević, M. V. & Peeters, F. M. Spatially dependent sensitivity of superconducting meanders as single-photon detectors. Appl. Phys. Lett. 100, 262603 (2012).
Vodolazov, D. Y., Elmuradov, A. & Peeters, F. M. Critical currents of the phase slip process in the presence of electromagnetic radiation: Rectification for time asymmetric ac signal. Phys. Rev. B 72, 134509 (2005).
Zotova, A. N. & Vodolazov, D. Y. Photon detection by current-carrying superconducting film: A time-dependent Ginzburg-Landau approach. Phys. Rev. B 85, 024509 (2012).
Sahu, M. et al. Individual topological tunnelling events of a quantum field probed through their macroscopic consequences. Nat. Phys. 5, 503–508 (2009).
Pekker, D., Shah, N., Sahu, M., Bezryadin, A. & Goldbart, P. M. Stochastic dynamics of phase-slip trains and superconductive-resistive switching in current-biased nanowires. Phys. Rev. B 80, 214525 (2009).
Silhanek, A. V. et al. Influence of artificial pinning on vortex lattice instability in superconducting films. New J. of Phys. 14, 053006 (2012).
Adami, O.-A. et al. Onset, evolution, and magnetic braking of vortex lattice instabilities in nanostructured superconducting films. Phys. Rev. B 92, 134506 (2015).
Silhanek, A. V. et al. Formation of stripelike flux patterns obtained by freezing kinematic vortices in a superconducting Pb film. Phys. Rev. Lett. 104, 017001 (2010).
Silin, V. P. Pinning of Abrikosov-Josephson vortices. Zh. Eksp. Teor. Fiz. 110, 741–755 (1996).
Gurevich, A. et al. Flux flow of Abrikosov-Josephson vortices along grain boundaries in high-temperature superconductors. Phys. Rev. Lett. 88, 097001 (2002).
Silin, V. P. Travelling small-scale Josephson vortices. Zh. Eksp. Teor. Fiz. 60, 442–445 (1994).
Milošević, M. V., Kanda, A., Hatsumi, S., Peeters, F. M. & Ootuka, Y. Local current injection into mesoscopic superconductors for the manipulation of quantum states. Phys. Rev. Lett. 103, 217003 (2009).
Milošević, M. V. & Peeters, F. M. Vortex manipulation in a superconducting matrix with view on applications. App. Phys. Lett. 96, 192501 (2010).
Milošević, M. V., Berdiyorov, G. R. & Peeters, F. M. Fluxonic cellular automata. App. Phys. Lett. 91, 212501 (2007).
Golod, T., Iovan, A. & Krasnov, V. M. Single Abrikosov vortices as quantized information bits. Nat. Comm. 6, 8626 (2015).
Baranov, V. V., Balanov, A. G. & Kabanov, V. V. Current-voltage characteristic of narrow superconducting wires: Bifurcation phenomena. Phys. Rev. B 84, 094527 (2011).
Milošević, M. V. & Geurts, R. The Ginzburg-Landau theory in application. Physica C 470, 791–795 (2010).
Acknowledgements
This work was supported by the Research Foundation-Flanders (FWO) and EU COST action MP1201. The work of Ž.L.J. and A.V.S. was partially supported by “Mandat d’Impulsion Scientifique” MIS F.4527.13 of the F.R.S.-FNRS.
Author information
Authors and Affiliations
Contributions
All authors participated in obtaining the results and contributed to the final scientific statement of the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Jelić, Ž., Milošević, M. & Silhanek, A. Velocimetry of superconducting vortices based on stroboscopic resonances. Sci Rep 6, 35687 (2016). https://doi.org/10.1038/srep35687
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep35687
- Springer Nature Limited