Abstract
We present a study of the interaction mechanisms in magnetic trilayer structures with an MgO barrier grown by molecular beam epitaxy. The interlayer exchange coupling, Aex, is determined using SQUID magnetometry and ferromagnetic resonance (FMR), displaying an unexpected oscillatory behaviour as the thickness, tMgO, is increased from 1 to 4 nm. Transmission electron microscopy confirms the continuity and quality of the tunnelling barrier, eliminating the prospect of exchange arising from direct contact between the two ferromagnetic layers. The Gilbert damping is found to be almost independent of the MgO thickness, suggesting the suppression of spin pumping. The element-specific technique of x-ray detected FMR reveals a small dynamic exchange interaction, acting in concert with the static interaction to induce coupled precession across the multilayer stack. These results highlight the potential of spin pumping and spin transfer torque for device applications in magnetic tunnel junctions relying on commonly used MgO barriers.
Similar content being viewed by others
Introduction
Much attention is currently devoted to the study of spin-transfer torque (STT)1,2,3,4, through which it is possible to realize spontaneous magnetization precession and switching. Spin pumping from a ferromagnet (FM) into a non-magnetic (NM) material is one of the most promising candidates for these applications5. Spin pumping has been under intense scrutiny since it was first proposed in 20026, studying the generation of pure spin currents by ferromagnetic resonance (FMR). Of particular importance is the transmission of spins across NM barriers, such as the conductors Ag (ref. 7), Au (ref. 8), and Cu (ref. 9), or insulators like MgO (ref. 10) and SrTiO3 (ref. 11). The efficacy of spin pumping is governed by the spin diffusion length of the NM layer, and the spin mixing conductance of the FM/NM interface12. Spin pumping is heavily suppressed in insulators, leading to very short spin-coherence lengths, often under a nm11. However, coupling of the spin and charge degrees of freedom, and associated charge pumping in tunnelling heterostructures with an insulating barrier, can complicate interpretation of the results5,13,14. It is useful to investigate spin pumping through insulating layers using probes that are insensitive to charge-based effects.
Here, we present a study of spin pumping and static exchange coupling in MgO-based magnetic heterostructures grown by molecular-beam epitaxy (MBE). These magnetic tunnel junctions (MTJs) are well-established high tunnelling magnetoresistance ratio elements15,16. The strength and character of the interactions is determined in Co50Fe50 /MgO/Ni magnetic heterostructures using superconducting quantum interference device (SQUID) magnetometry and vector network analyser (VNA) FMR. The structures are of high crystalline quality, as demonstrated by transmission electron microscopy (TEM). Static interlayer exchange is observed through shifts in the resonant field. X-ray detected FMR (XFMR) measurements confirm the presence of static exchange coupling, but demonstrate that for the thinnest MgO barrier there is also a component of spin pumping. These results show the importance of spin transfer in technologically-relevant MTJs, demonstrating that torques can be achieved for suitably thin barriers.
Ferromagnetic Resonance
In the classical limit the spin dynamics of a ferromagnet are governed by the damped Landau-Lifshitz-Gilbert (LLG) equation of motion, describing the precession of the magnetisation about an effective field arising from internal and external fields:
with γ the gyromagnetic ratio, m is the unit magnetisation vector of the material, α the dimensionless Gilbert damping parameter, and Heff the effective magnetic field. Through Heff the various energy terms, such as the exchange energy, the demagnetisation energy, the in-plane cubic and uniaxial anisotropies, the static exchange, and the Zeeman energy enter the equation.
The static interlayer exchange coupling is a general term for any interaction that acts to (anti-)align the magnetisations of the two layers in a magnetic trilayer structure such as a spin valve or an MTJ. Examples of such interactions include Ruderman-Kittel-Kasuya-Yosida (RKKY), superexchange, Néel or orange peel coupling, and direct exchange through a discontinuous spacer layer. The presence of a static interaction modifies the LLG equation with an additional term17:
where β is the interlayer exchange, and i, j index magnetic layers. The interlayer exchange is defined as18,19:
with Aex the interlayer exchange constant, t the thickness of the magnetic layer, ϕM the equilibrium orientation of the magnetization, and i, j indices label the magnetic layers. The sign of Aex indicates whether the interaction favours parallel (positive) or antiparallel (negative) alignment.
In FMR experiments, additional interaction mechanisms must be considered. As the magnetisation of a ferromagnetic layer precesses on resonance it acts as a spin battery, generating a pure spin current transverse to the axis about which it precesses. When the FM layer is thicker than the ferromagnetic coherence length, a pure spin current can be driven into an adjacent NM layer. A spin current can persist across the spacer layer, and in a trilayer structure either return to the first FM/NM interface, or else flow through to a second NM/FM interface. If it is not reflected here, it crosses the interface and is absorbed by the FM, inducing precession through the STT4.
The increased flow of spin momentum out of the FM layer acts as an additional channel for energy loss, leading to an increase in damping. This damping is linear with resonant frequency, and can thus be described in the same terms as Gilbert damping. The absorbed spin current leads to a comparable anti-damping term in the off-resonance layer.
With the addition of these two coupling mechanisms, the LLG for a trilayer system becomes:
where superscripts denote magnetic layers, and is the effective field acting on layer i. The intrinsic Gilbert damping is , while are spin source (m = n) and spin sink (m ≠ n) terms. The XFMR results can be modelled using this a linearised solution of this equation.
The presence of these coupling mechanisms alters the magnetodynamics of the on- and off-resonance layer. The static coupling shifts the resonant field of both layers, as it functions as an additional field term in the Kittel equation. Spin pumping, on the other hand, broadens the resonances by providing an additional energy loss mechanism. However, the most important change is the precession induced in the off-resonance layer, wherein the exchange interactions transfer energy between the two layers. This leads to changes in both the phase and amplitude of precession, with the phase being the more sensitive probe.
Results
Structural properties of the magnetic trilayer structures
The structural properties of the grown magnetic heterostructures were studied using transmission electron microscopy (TEM). Figure 1b–d shows cross-sectional TEM images of the magnetic heterostructures. These images demonstrate epitaxial growth of the films, and confirm that the MgO barrier is continuous (down to the thinnest barrier thickness of 1 nm, see Supplementary Fig. S1 for details).
Figure 2 shows hysteresis loops measured by SQUID-VSM for all four magnetic heterostructures, displaying a reduction in static interlayer coupling as a function of increasing tMgO. For the thinnest MgO barrier (tMgO = 1 nm, Fig. 2a) the two layers are strongly bound, and there is a single switching step, with a coercive field of 2 mT. As the thickness of the barrier increases, the layers decouple and behave independently. For tMgO = 2 and 3 nm (Fig. 2bc), the coupling between the two layers appears to cause winding, leading to a smeared out transition as opposed to sharp steps. Nevertheless, two distinct steps in the hysteresis loop can be identified.
As the TEM measurements show that the MgO barrier appears to be continuous, the observed coupling cannot be due to direct, large-area contact between the two ferromagnetic layers, but it is more likely to be resulting from tunnelling across the barrier. However, there is some evidence of surface roughness of the MgO, which could lead to a Néel orange-peel coupling.
Lab-based FMR measurements
VNA-FMR measurements were performed to determine values for the interlayer exchange coupling and magnetocrystalline anisotropy parameters for all samples. Figure 1a shows a representative field-frequency map for the sample with tMgO = 1 nm. Fits to resonance fields were performed as a function of RF frequency and magnetization alignment using the Kittel equation20, including the interlayer exchange field17,18, using Eq. (3).
The extracted interlayer coupling is shown in Fig. 3b, while values for all the fitting parameters are given in Table 1. The complete suppression of the interaction at tMgO = 2 nm is surprising, as it suggests an oscillatory coupling strength, a phenomenon more often associated with coupling across NM conductive layers (see, e.g., ref. 21). This finding is in contrast to previous work on MgO, e.g., ref. 18. Note that in spin-dependent tunnelling such an oscillatory thickness-dependence has been observed for MgO barriers in Fe/MgO/Fe tunnelling structures22.
The total Gilbert damping was extracted from the frequency dependence of the linewidth, ΔH, using23
with ΔH0 the extrinsic broadening. Results for both FM layers are plotted as a function of MgO barrier thickness in Fig. 3c. Within the error bars, there is no change in the Gilbert damping of the Ni layer, which supports the assertion that an insulating layer such as MgO does not permit a spin current to flow. The data for the CoFe layer is more complicated, showing at first a slight increase, then a drop in damping. Microscopy and magnetic characterization gave no evidence of a change in the structural or magnetic properties of the CoFe layer to account for this finding.
While a drop in damping with increasing interlayer thickness is usually indicative of spin pumping, the trend here does not match the exponential decay observed in previous studies7,11,24. Measurements on comparable bare CoFe layers yielded a Gilbert damping of ~3 × 10−3. This suggests that at least some of the spins pumped by the precessing magnetization of the CoFe are absorbed. The lower damping in the case of the thinnest MgO layer could be in part due to the strong static exchange coupling observed.
Synchrotron-based FMR measurements
XFMR measurements were performed to study off-resonance precession induced by static exchange coupling and the STT exerted by pumped spins. Figure 4 shows the amplitude and phase of precession at 4 GHz for each layer in the sample with tMgO = 1 nm, with the magnetic field applied along the easy axis of the CoFe. The resonance in the Ni layer is easily identified, with a peak in amplitude at 28 mT. Off-resonance precession is induced in the CoFe layer; the resulting dynamic XMCD signal is approximately ten times smaller than that of the Ni. There is also a small phase feature in the Co, which is predominantly unipolar in character. Taken together with the bipolar shape of the Co amplitude variation, this indicates that the static interaction is primarily responsible for induced precession in the CoFe.
Solid lines in Fig. 4 are fits to the data using a macrospin solution of the coupled LLG equation, as outlined in, e.g., refs 9 and 24. The values of static exchange coupling and magnetocrystalline anisotropy determined in Table 1 were used to calculate the amplitude and phase of precession for each layer. In order to reproduce the slightly distorted features in the Co, a dynamic interaction had to be introduced, accounting for 50% of the total Gilbert damping in the Ni layer, and assuming perfect transmission of spins. This modifies the shape of the Co features, mixing the characteristics of the two interactions. With this included the model reproduces the experimental data, although it underestimates the linewidth of the Ni mode due to the presence of inhomogeneous broadening arising from non-Gilbert damping in the samples. The measurement of a component of dynamic interaction shows that a suitably thin MgO barrier will permit a spin current to flow, while for thicker barriers the pumped spin current is entirely scattered within the MgO.
Discussion
We have presented a study of the coupled magnetodynamics of magnetic heterostructures, demonstrating that both static and dynamic coupling can exist across a suitably thin MgO barrier. SQUID-VSM and VNA-FMR showed the presence of a static interaction acting to align the two layers, with an apparent oscillatory coupling strength — a surprising result that will stimulate further investigation of such structures. Moreover, it was observed that the pure spin current generated by ferromagnetic resonance is absorbed by the MgO, increasing Gilbert damping in the ferromagnetic layers. Layer-resolved XFMR measurements showed that the resulting dynamic interaction can persist across a 1-nm-thick barrier and induce off-resonance precession through spin transfer torque. These results demonstrate how the coupling between magnetic layers can be manipulated through the choice of barrier material and thickness, and illustrate the differing regimes of static and dynamic coupling that can be thus attained. The two interactions can cooperatively transfer energy between layers during ferromagnetic resonance. The pure spin current can persist for a short distance across an insulating barrier, and exert a spin-transfer torque on a neighbouring layer, an important finding for the diverse and active field of STT-MRAM.
Methods
Thin film growth
The magnetic multilayer samples were prepared by MBE on epi-ready MgO(001) substrates. Reflection high-energy electron diffraction (RHEED) measurements were performed throughout the growth to monitor crystal quality (cf. Fig. 1a). The full structure is MgO/Co50Fe50 (15)/MgO(tMgO)/Ni(8)/Ag(4) (nominal thicknesses in nm), with tMgO = 1, 2, 3, and 4 nm (equivalent to ~4.7, 9.5, 14.2, and 19.0 monolayers). The substrates were annealed at 700 °C to improve surface quality, then cooled to 500 °C for the deposition of stoichiometric Co50Fe50. The samples were further cooled to room temperature for deposition of MgO onto the epitaxial Co50Fe50 (hereafter referred to as CoFe, for brevity). The MgO barriers were annealed at 300 °C for 20 minutes leading to a sharpening of the RHEED streaks, as shown in Fig. 1a, indicative of good crystalline quality, before being again cooled to room temperature for the deposition of Ni and finally the Ag capping layer.
Electron microscopy
Structural properties of the grown magnetic heterostructures were studied using a JEOL 2200FS double aberration-corrected (scanning) transmission electron microscope (S)TEM. Cross-sectional TEM specimen were prepared using conventional methods that include mechanical thinning and polishing followed by Ar ion milling in order to achieve electron transparency25.
Magnetometry
Magnetometry was carried out using a SQUID vibrating sample magnetometer (VSM). FMR measurements were performed using a VNA and octupole electromagnet. Real and imaginary components of the microwave transmission parameter, S12, were measured as a function of magnetic field (strength and angle), and RF frequency. Plotting the resonant field as a function of frequency and bias field angle yields anisotropy and exchange coupling parameters using the Kittel equation20 including static exchange coupling17,24. See the Supplementary Information for a discussion of the Kittel equation.
X-ray detected Ferromagnetic resonance
Indirect measurements of spin transfer using VNA-FMR are unable to provide a conclusive determination of the presence of spin pumping within the heterostructures. XFMR measurements address this limitation, studying the coupled magnetodynamics with a layer-resolved probe, which reveals more information about the nature of the coupling mechanisms. Further, XFMR can determine whether a pumped pure spin current is absorbed by the MgO barrier, or whether some component crosses it, to be absorbed by the spin sink layer. The XFMR measurements were performed on beamline I10 at the Diamond Light Source (UK) and beamline 4.0.2 at the Advanced Light Source (USA). The magnetic samples are excited by microwave radiation, phase-locked to the synchrotron master oscillator, resulting in a steady precession about the effective field close to the FMR condition. The oscillating magnetization component along the incident x-ray beam direction is probed using x-ray magnetic circular dichroism (XMCD). Element, and consequently layer specificity, is obtained by tuning the x-ray energy to the Ni and Co L3 edges. For full details of the XFMR methodology, we refer to ref. 26.
Additional Information
How to cite this article: Baker, A. A. et al. Spin pumping in magnetic trilayer structures with an MgO barrier. Sci. Rep. 6, 35582; doi: 10.1038/srep35582 (2016).
References
Sankey, J. C., Cui, Y.-T., Sun, J. Z., Slonczewski, J. C., Buhrman, R. A. & Ralph, D. C. Measurement of the spin-transfer-torque vector in magnetic tunnel junctions. Nat. Phys. 4, 67 (2008).
Diao, Z., Li, Z., Wang, S., Ding, Y., Panchula, A., Chen, E., Wang, L.-C. & Huai, Y. Spin-transfer torque switching in magnetic tunnel junctions and spin-transfer torque random access memory. J. Phys.: Condens. Matter 19, 165209 (2007).
Katine, J. A. & Fullerton, E. E. Device implications of spin-transfer torques. J. Magn. Magn. Mater. 320, 1217 (2008).
Stiles, M. D. & Zangwill, A. Anatomy of spin-transfer torque. Phys. Rev. B 66, 014407 (2002).
Moriyama, T., Cao, R., Fan, X., Xuan, G., Nikolić, B. K., Tserkovnyak, Y., Kolodzey, J. & Xiao, J. Q. Tunnel barrier enhanced voltage signal generated by magnetization precession of a single ferromagnetic layer. Phys. Rev. Lett. 100, 067602 (2008).
Brataas, A., Tserkovnyak, Y., Bauer, G. E. W. & Halperin, B. I. Spin battery operated by ferromagnetic resonance. Phys. Rev. B 66, 060404 (2002).
Kardasz, B. & Heinrich, B. Ferromagnetic resonance studies of accumulation and diffusion of spin momentum density in Fe/Ag/Fe/GaAs (001) and Ag/Fe/GaAs (001) structures. Phys. Rev. B 81, 094409 (2010).
Heinrich, B., Tserkovnyak, Y., Woltersdorf, G., Brataas, A., Urban, R. & Bauer, G. E. W. Dynamic exchange coupling in magnetic bilayers. Phys. Rev. Lett. 90, 187601 (2003).
Marcham, M. K., Shelford, L. R., Cavill, S. A., Keatley, P. S., Yu, W., Shafer, P., Neudert, A., Childress, J. R., Katine, J. A., Arenholz, E., Telling, N. D., van der Laan, G. & Hicken, R. J. Phase-resolved x-ray ferromagnetic resonance measurements of spin pumping in spin valve structures. Phys. Rev. B 87, 180403 (2013).
Mosendz, O., Pearson, J. E., Fradin, F. Y., Bader, S. D. & Hoffmann, A. Suppression of spin-pumping by a MgO tunnel-barrier. Appl. Phys. Lett. 96, 022502 (2010).
Du, C. H., Wang, H. L., Pu, Y., Meyer, T. L., Woodward, P. M., Yang, F. Y. & Hammel, P. C. Probing the spin pumping mechanism: Exchange coupling with exponential decay in Y3Fe5O12/barrier/Pt heterostructures. Phys. Rev. Lett. 111, 247202 (2013).
Tserkovnyak, Y., Brataas, A., Bauer, G. E. W. & Halperin, B. I. Nonlocal magnetization dynamics in ferromagnetic heterostructures. Rev. Mod. Phys. 77, 1375 (2005).
Tserkovnyak, Y., Moriyama, T. & Xiao, J. Q. Tunnel-barrier-enhanced dc voltage signals induced by magnetization dynamics in magnetic tunnel junctions. Phys. Rev. B 78, 020401 (2008).
Xiao, J., Bauer, G. E. W. & Brataas, A. Charge pumping in magnetic tunnel junctions: Scattering theory. Phys. Rev. B 77, 180407 (2008).
Yuasa, S., Nagahama, T., Fukushima, A., Suzuki, Y. & Ando, K. Giant room-temperature magnetoresistance in single-crystal Fe/MgO/Fe magnetic tunnel junctions Nat. Mater. 3, 868 (2004).
Parkin, S. S., Kaiser, C., Panchula, A., Rice, P. M., Hughes, B., Samant, M. & Yang, S. H. Giant tunnelling magnetoresistance at room temperature with MgO(100) tunnel barriers. Nature Mater. 3, 862 (2004).
Arena, D. A., Vescovo, E., Kao, C.-C., Guan, Y. & Bailey, W. E. Weakly coupled motion of individual layers in ferromagnetic resonance. Phys. Rev. B 74, 064409 (2006).
Caprile, A., Manzin, A., Coisson, M., Pasquale, M., Schumacher, H. W., Liebing, N., Sievers, S., Ferreira, R., Serrano-Guisan, S. & Paz, E. Static and dynamic analysis of magnetic tunnel junctions with wedged MgO barrier. IEEE Trans. Magn. 51, 1 (2015).
Stenning, G. B. G., Shelford, L. R., Cavill, S. A., Hoffmann, F., Haertinger, M., Hesjedal, T., Woltersdorf, G., Bowden, G. J., Gregory, S. A., Back, C. H., de Groot, P. A. J. & van der Laan, G. Magnetization dynamics in an exchange-coupled NiFe/CoFe bilayer studied by x-ray detected ferromagnetic resonance. New J. Phys. 17, 013019 (2015).
Kittel, C. On the theory of ferromagnetic resonance absorption. Phys. Rev. 73, 155 (1948).
Azevedo, A., Chesman, C., Rezende, S. M., de Aguiar, F. M., Bian, X. & Parkin, S. S. P. Biquadratic exchange coupling in sputtered (100) Fe/Cr/Fe. Phys. Rev. Lett. 76, 4837 (1996).
Butler, W. H., Zhang, X. G., Schulthess, T. C. & MacLaren, J. M. Spin-dependent tunneling conductance of Fe|MgO|Fe sandwiches. Phys. Rev. B 63, 054416 (2001).
Kalarickal, S. S., Krivosik, P., Wu, M., Patton, C. E., Schneider, M. L., Kabos, P., Silva, T. J. & Nibarger, J. P. Ferromagnetic resonance linewidth in metallic thin films: Comparison of measurement methods. J. Appl. Phys. 99, 093909 (2006).
Baker, A. A., Figueroa, A. I., Love, C. J., Cavill, S. A., Hesjedal, T. & van der Laan, G. Anisotropic absorption of pure spin currents. Phys. Rev. Lett. 116, 047201 (2016).
Lari, L., Lea, S., Feeser, C., Wessels, B. W. & Lazarov, V. K. Ferromagnetic InMnSb multi-phase films study by aberration-corrected (scanning) transmission electron microscopy. J. Appl. Phys. 111, 07C311 (2012).
Figueroa, A. I., Baker, A. A., Collins-McIntyre, L. J., Hesjedal, T. & van der Laan, G. Spin pumping through a topological insulator probed by x-ray detected ferromagnetic resonance. J. Magn. Magn. Mater. 400, 178 (2016).
Acknowledgements
Beamtime awarded on I10 at the Diamond Light Source (DLS) under proposal SI-11501 and on 4.0.2 at the Advanced Light Source are acknowledged. A.A.B. was supported by DLS and EPSRC through a Doctoral Training Award. V.K.L. was supported by EPSRC grant EP/K03278X/1.
Author information
Authors and Affiliations
Contributions
A.A.B., G.v.d.L. and T.H. conceived the idea and A.A.B. and T.H. grew the device structures. A.A.B., A.I.F., G.v.d.L. and T.H. carried out the XFMR experiments and D.P. and V.K.L. the electron microscopy. A.A.B. and T.H. wrote the paper with comments and input from all authors. All authors contributed to the discussions.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Baker, A., Figueroa, A., Pingstone, D. et al. Spin pumping in magnetic trilayer structures with an MgO barrier. Sci Rep 6, 35582 (2016). https://doi.org/10.1038/srep35582
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep35582
- Springer Nature Limited
This article is cited by
-
Ultrafast optical observation of spin-pumping induced dynamic exchange coupling in ferromagnetic semiconductor/metal bilayer
Scientific Reports (2022)
-
Eigen damping constant of spin waves in ferromagnetic nanostructure
Scientific Reports (2019)