Abstract
The new generation of ternary Pb(In1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 ferroelectric single crystals have potential applications in high power devices due to their surperior operational stability relative to the binary system. In this work, a reversible, large electric field induced strain of over 0.9% at room temperature, and in particular over 0.6% above 380 K was obtained. The polarization rotation path and the phase transition sequence of different compositions in these ternary systems have been determined with increasing electric field applied along [001] direction based on x-ray diffraction data. Thereafter, composition dependence of field-temperature phase diagrams were constructed, which provide compositional and thermal prospectus for the electromechanical properties. It was found the structural origin of the large stain, especially at higher temperature is the lattice parameters modulated by dual independent variables in composition of these ternary solid solution crystals.
Similar content being viewed by others
Introduction
Over the past century, material scientists have made great efforts to seek and create new materials with significant mechanical response functionalities for applications in sensing and actuation, ranging from inorganic to organic1, metal to nonmetal2, and bulk to nano materials3,4. Of the many types of actuator materials (including magnetostrictive2,5, photostrictive6,7, and shape memory alloys2,4), piezoelectric materials3,8,9,10,11,12,13,14 are widely used due to their superior high force generation, high frequency capabilities, displacement accuracy, and/or device miniaturization8. In particular, relaxor ferroelectric binary single crystals, regarded as generation I15,16,17, i.e., (1 − x)Pb(Mg1/3Nb2/3)O3-xPbTiO3 (PMN-PT) and (1 − x)Pb(Zn1/3Nb2/3)O3-xPbTiO3] (PZN-PT), with compositions near the morphotropic phase boundary (MPB), exhibit ultrahigh electromechanical coefficients that are up to an order of magnitude larger than that of conventional Pb(ZrxTi1−x)O3 (PZT) ceramics8,18,19. This important breakthrough20 triggered a race for theoretical understanding of the origin of such high responses in perovskite oxides21,22,23,24,25, and for the experimental identification of the MPB that is a nearly vertical boundary between rhombohedral (R) and tetragonal (T) phases26,27,28.
In spite of the ultrahigh electromechanical properties of these bianary crystals, several obstacles have restricted them from practical applications15,16. These includes (i) deterioration in performance with increasing temperature, which limits their operational temperature ranges; and (ii) the coercive field is on the order of 2 kV/cm, which restricts their usage to low power applications. In order to circumvent these difficulties, numerous investigations have been performed, including doping (Mn) binary crystals, crystallization or texture orientation instead of conventional PZT ceramics, and adding solid solution components to achieve ternary systems15,16.
The challenges associated with property superiority, operational stability, cost and crystal size, have been addressed, in particular after the development of ternary Pb(In1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 (PIN-PMN-PT) single crystals15,16,29,30. This generation II system combines the advantages of two respective MPBs, determined by the two individual binary PMN-PT and PIN-PT solid solutions (see Fig. 1(b)). In turn, the MPB zone, rather than a line in the binary systems, offers a higher degree of structural instability and thus provides the possibility to enhance the electromechanical properties16. Furthermore, due to complexity in its compositional components, the electromechanical property and Curie temperature (TC) can be simultaneously optimized and enhanced by varying the concentration of the components near the MPB region, rather than by property tradeoffs as in a binary system (i.e., increase of TC at cost of decrease in piezoelectric properties).
Comparison of piezoelectric and dielectric properties of ternary PIN-PMN-PT and binary PMN-PT systems.
(a) Photograph for an as-grown large-size PIN-PMN-PT ternary crystal (larger and clearer ones are presented in Fig. S1). (b) Phase diagram for these generation II crystals, where the rhombohedral and tetragonal phases are separated by a MPB zone. (c) Temperature dependent dielectric constant at 1 kHz in the zero-field-heating condition and unipolar E-induced strains for crystals (d) A, (e) B, (f) C and (g) PMN-30PT. (h) Temperature dependence of the maximum unipolar strains under E = 50 kV/cm for the crystals A, B, C, and PMN-30PT. (h) Piezoelectric coefficient d33 of various piezoelectric material systems, including the binary crystal PMN-PT, new generation (A-, B- and C-) ternary crystals, and conventional PZT ceramics (refs 40,41) as a function of Tc. For the PMN-PT system, the d33 of PMN-30PT was measured in this work, whereas that for other compositions was cited from refs 29,45.
However, to date, due to the multiplicity of induced phase transitions with E and temperature31, the sequence of temperature dependent field-induced strains is not clear for ternary PIN-PMN-PT crystals. This presents a significant challenge to end-users on how to select crystals with different compositions for specific application conditions, especially with regards to operational temperature ranges. In this paper, the electromechanical and piezoelectric properties of PIN-PMN-PT with compositions near the MPB have been systematically characterizated. Large field-induced strains >0.6% in the high temperature range from 360 K to 380 K have been obtained. Furthermore, the field-temperature phase diagrams were established by a comprehensive x-ray diffraction study. The results provide a compositional and thermal prospectus for the electromechanical properties, which can assist end-users to choose compositions for actuation applications at various operational temperature ranges.
Results and Discussion
Dielectric and piezoelectric properties
Three typical regions of the as-grown crystal with a nominal composition of 33PIN-35PMN-32PT were selected for investigation (designated as A, B and C), as shown in Fig 1(a). The compositions of the A-, B- and C-crystal were determined to be 31PIN-37.2PMN-31.8PT, 25.4PIN-41.2PMN-33.4PT and 28.8PIN-33.3PMN-37.9PT by quantitative X-ray fluorescence analysis (PHILIPS PW2404 X-ray fluorescence spectrometer) based the standard of In2O3, MgO and TiO232,33. All the three crystals are located near MPB, but A- and B- crystals in the rhombohedral region, while C-crystal in the MPB, close to tetragonal region, as schematically illustrated in Fig. 1(b). The ground state of the crystals will be discussed based on the diffraction data. Figure 1(c) shows the dielectric constant (εr) as a function of temperature for [001] oriented crystals. The results demonstrate that the binary PMN-30PT has a TC near 413 K; whereas the ternary A-, B- and C-crystals have higher TC values of 445, 452 and 475 K, respectively. The improvement of the Curie temperature provides potential superiority of ternary crystals to be operated in a wider temperature range. Except for the ferroelectric-paraelectric phase transition peaks, no other additional peaks were apparent for either PMN-30PT or the ternary A-crystal; however, additional peaks were distinguishable at lower temperatures for the ternary B- and C-crystals near 367 and 315 K, respectively. These additional phase transitions will be discussed in more detail below.
The E-induced strain (S) for (001) oriented crystals is shown in Fig. 1(d–g). These data were taken at various temperatures under a maximum ac electric field (Em) of 50 kV/cm. For the ternary A-crystal, it can be seen that the S-E curve is nearly linear and anhysteretic at 300 K. On heating to 420 K, the value of Sm under Em = 50 kV/cm increased, reaching a maximum value and then subsequently decreasing. Interestingly, the degree of hysteresis also increased and subsequently decreased. For the ternary B-, C- and binary PMN-30PT crystals, the S-E curves approach a saturation near Em = 50 kV/cm at all the temperatures studied. It is worth noting that similar results in the ternary ferroelectric crystals with compositions near the MPB were also observed by Zhang et al.34. Interestingly, diffuse inflections, rather than discontinuous jumps (i.e., first-order-like characteristic35) in S were found for all the ternary crystals studied, especially at room temperature, which is in contrast to the [001]-oriented binary PMN-30PT crystal that has two abrupt jumps due to the previously reported phase transformational sequence of MA → MC → T26,36,37,38. The atypical S-E curves for ternary systems might be due to a bifurcated polarization rotation path or diffuse phase transitions with increasing E39.
The temperature dependence of Sm at Em = 50 kV/cm is summarized in Fig. 1(h). Among the ternary and binary crystals studied, the B-crystal was found to exhibit the highest value of Sm over the temperature range from 300 to 420 K amongst the ternary and binary crystals studied. The value of Sm for the B-crystal near linearly decreased with increasing temperature. Strains as high as Sm = 0.9% were obtained under Em = 50 kV/cm at room temperature for the B-crystal, which was 1.5× higher than that of PMN-30PT. Note that the enhancement was even larger for the B-crystal if higher fields were applied, as its S-E curve did not completely saturate (see Fig. 1e). In contrast, the other crystals exhibited discontinuous decreases in Sm with increasing temperature: A-crystal near 315 and 385 K, C-crystal near 320 and 350 K, and the binary PMN-30PT near 320 and 340 K (see Fig. 1h). These abrupt changes are indicative of phase transformations, as will be discussed based on x-ray diffraction below.
Comparing the results in Fig. 1(h), it was found the significance was not only the enhancement of Sm in the ternary crystals at room temperature, but also the large value of Sm can be achieved at high temperature range, especially for B-crystal, relative to the binary PMN-30PT ones. Obviously, all the ternary crystals exhibit a large value of Sm > 0.5% over the moderate high temperature range, while PMN-30PT have a much lower value <0.3% above 365 K. In particular, the value of Sm of B-crystal is ×2.8 larger than that of PMN-30PT around 365 K, and ×1.8 larger at 420 K. These results reveal that the new generation ternary crystals, especially the B-crystal, have ambiguous preponderance in actuator applications over high temperature range.
With regards to practical applications, the piezoelectric coefficient d33 and the value of TC are two key figures of merit, which significantly depend on crystal composition. Figure 1(i) shows the values of d33 for various piezoelectric material systems as a function of their TC. It can be seen that the value of d33 for PMN-PT crystals with a composition near MPB can reach above 2000 pC/N, while their value of TC is near 410 K. Development of higher TC values for binary crystals (i.e, doping Mn), unfortunately, cause a significant decrease in the piezoelectric constant, which is another technical obstacle for their practical applications in high-power actuators. The TC of conventional piezoceramics, such as PZT, is much higher than that of the binary crystals, but unfortunately, the piezoelectric constant was found to be on the order of 200–700 pC/N40,41. However, for the generation II ternary crystals, the d33 value is comparable to (and even higher than) that of the binary crystals, but their TC values are several tens degree higher than that for the binary crystals. For the A- and B-crystal, the value of d33 was greater than 2000 pC/N, and their TC was between 450 and 455 K. The C-crystal has a significantly higher TC of about 480 K, with a d33 value of about 1500 pC/N. These results demonstrate the superior characteristics of new generation II crystals in high-temperature range applications.
Electric field-temperature phase diagram
In order to better understand the structural origin of the temperature dependence of Sm, x-ray diffraction was performed on A-, B- and C-crystals for various thermal and electrical histories. Based on these diffraction data, electric field-temperature diagrams for the ternary crystals, together with that of the binary PMN-30PT one, have been established, as shown in Fig. 2. This summary is presented first for the convenience of the readers: the raw data, including line and reciprocal-space mesh scans (RMS) will be given below and in the supplementary document. Circles designate the phase transformational temperatures and fields, obtained by increasing field beginning from the annealed state at each typical temperature.
Electric field-temperature phase diagram for the ternary A-, B- and C-crystals, and the binary PMN-30PT crystal.
The data of the binary PMN-30PT crystal was adapted from ref. 38. The open circles represent the phase transformational temperatures and fields that were determined from high-resolution x-ray diffraction measurements. These data points were obtained on in situ increasing electric-fields and temperatures. Both the solid and dash lines are to guide the eyes. The regions in different colors indicate the different phase fields, and regions of phase coexistence are designated by color mixture.
X-ray diffraction data and phase transition sequence
Figure 3 shows the evolution of line scans around the (002)C zone of ternary A-, B-, and C-crystals with temperature on zero-field-heating condition. Scans were obtained at 20 K intervals beginning from the annealed state. Only a single diffraction peak was observed for the A-crystal over the entire measurement temperature range (Fig. 3a). The exception was the presence of weak humps on the low 2θ side at temperatures 420 and 440 K, indicating a weak tetragonal (002)T phase may coexist with the R and C phases, analogous to that previously reported in binary crystals at low PT contents27. For the B-crystal, a broad single peak was found below 360 K; but on heating to 380 K, an additional peak appeared on the high 2θ side. On further heating above 400 K, the initial broad peak gradually vanished and a doublet peak became evident. This line profile evolution reveals a R → T transition near 380 K, which agrees well with the discontinuity observed in the εr-temperature curve (see Fig. 1c). Note that the initial broad peak is asymmetric, where a weak tail existed at the lower 2θ side. This peak tail may be due to phase coexistence, as the B-crystal was quite close to the MPB. After heating to 460 K, a subsequent T → C transition was found. This is evidenced by the appearance of a single cubic (002) peak, and the simultaneous disappearance of the tetragonal (200)-(002) doublet splitting. For the C-crystal, a tetragonal (200)T peak of significant intensity was observed below 480 K, and a T → C phase transition was evidenced at 500 K as the tetragonal (200)-(002) doublet merged into a sharp cubic (002)C singlet. At temperatures below 340 K, in addition to the tetragonal (200)T peak, a broad tail that extended to lower values of 2θ was found. This is consistent with its composition being near to the MPB region but on the tetragonal phase. Phase coexistence near and below 340 K is a probable explanation for these line profile charactertics below 360 K, and to its εr-temperature curve (see Fig. 1c), which is similar to that previously reported for PMN-34PT crystals42.
In order to provide a link between the macroscopic strain characteristic and the evolution of the structure, comprehensive x-ray diffraction experiments were performed on the ternary crystals with E applied in situ along the [001] direction. Figure 4 shows the evolution of the diffraction peaks around (002)C zone with increasing and decreasing E using field step of 2 kV/cm (typical results shown here). These data were taken at a temperature of 330 K. Additional results at other temperatures are given in Figs S2–4. It is obvious that the peaks shift towards lower values of 2θ with increasing E (top panel), while shifting back towards higher value of 2θ with decreasing E (bottom panel).
For the A-crystal, a singlet diffraction peak was found that gradually moved with increasing E up to 20 kV/cm, which thereafter split into three peaks at E = 28 kV/cm. Analogous to prior reports of binary crystals under E//[001]36,37,38,43, it can be conjectured that MA, MC and T phases coexist; correspondingly, these three peaks can be indexed as (002)T, (002)MC and (002)MA from low to high 2θ. A singlet remained and gradually shifted to lower 2θ values with increasing field between 0 ≤ E ≤ 12 kV/cm for the B-crystal. For E = 12 kV/cm the singlet was splitted into two peaks of comparable intensities, indicating a region of two-phase coexistence. With further increase of E, a single sharp peak became apparent, which was nearly insensitive to further increase of E (see Fig. 4b). These features unambiguously show that a T phase appears.
The annealed C-crystal had a complex diffraction profile whose diffraction peaks were difficult to resolve. This may be due to being near the MPB region but on the T phase. Upon application of E//[001], the diffraction peaks became considerably more distingushable, as can be seen in Fig. 4(c). In this case, a strong asymmetrical peak was found that had a tail at lower 2θ values under E = 2 kV/cm. These results demonstrate that the c-axis of the monoclinic phase is rotated and fixed along the E field direction, and that a low volume fraction of tetragonal c-domain may coexist with it that are also aligned parallel to E. With further increasing E, the monoclinic phase gradually transformed into the T one, as manifested by the relative intensity of doublet (i.e., (002)T-(002)M) under E = 4 and 6 kV/cm. For E > 8 kV/cm, a single c-domain T phase was obtained. It is interesting to note that this tetragonal single c-domain state was metastable after removal of E, as no diffraction intensity corresponding to the monoclinic phase was apparent near 44.7°, in contrast to that observed at 300 K (see Fig. S4a). At higher temperatures (i.e., 360 K), the metastable single c-domain state was partially restored to a multi-domain state upon removal of E, at least a small fraction of a-domains was found near 44.9° due to depoling (see Fig. S4b). This diffraction feature reveals a structural origin for the noticable decrease in Sm near 320 K (Fig. 1g), and a slight increase with increasing E thereafter. Changes in Sm with temperature above 350 K was also observed, which can be explained by a tradeoff between depoling effects and a temperature dependent c/a ratio (see Fig. 3c): i.e., with increasing temperature, the fraction of a-domains increased, but the strain contribution from the unequal crystallographic axis switching decreased.
To clarify and determine the phase transformation sequence in Fig. 2, reciprocal-space mesh scans were performed about the (200)C and (220)C zones at various temperatures with E//[001]C for A-, B- and C-crystals, as shown in Fig. 5 and S5–S9. For the A-crystal, the R phase was evidenced by a broad peak around the (002)C (see Fig. S5a), and a doublet about (220)C (see Fig. S6a) under small E. Above 4 kV/cm, the pseudocubic (220) reflection exhibited the characteristic triple splitting of the MA phase, which consists of a (040)MA b-domain and two twined a-domains. The (200)C zone exhibited the signature doublet splitting consisting of two twined
domains. At 330 K, a similar domain configuration evolution and phase transformational sequence was obtained, but the R → MA transition occurred at a lower field of E = 3 kV/cm, as shown in Fig. 5b. Note that at E = 2 kV/cm, only a broad single peak with a small splitting along the transverse direction was found around (200)C, while a weak triplet was observed around (220)C. With increasing field to E = 10 kV/cm, a complex domain configuration was found: which consisted of a strong peak around (220)C accompanied by weak diffraction tails (see Fig. 5c). Moreover, line scans around (002)C revealed a single peak with a weak tail on the low 2θ side. These abnormal domain configurations can be attributed to coexistence of MA and MC phases by referring to the polarization rotation pathways for binary crystals26,37,38. Complex domain configurations were also observed under a moderate field of E = 2 kV/cm at 390 K. These results indicate the coexistence of MA and MC phases, in particular in consideration of the observation of a doublet in the (002)C line scans. At 420 K, a single domain configuration along both (200)C and (220)C became sharp under E > 0.5 kV/cm, and the lattice parameters extracted from line scans revealed that the structure is tetragonal.
For the B-crystal, the R phase was stable under moderate field level, as evidenced by a broad diffraction peak around (002)C and a doublet-like feature about (220)C (see Fig. 5d, S7a and S8a). On application of higher E, the (200)C diffraction split into two peaks (i.e., E = 4 kV/cm at 300 and 330 K, and E = 2 kV/cm at 360 K, as shown in Fig. 5d, S7a,b). These domain configurations reveal a R → MA transition with increasing E. It is important to note that atypical domain configurations around (220)C were found in the MA phase (see Fig. 5e): a b-domain and only a single a-domain was observed, rather than a b-domain containing two a-domains as in previous studies26,37,38. Absence of diffraction peaks can be common in ferroelectric crystals due to defects, or internal stress, in the crystals that break domain equivalency10. With increasing E to 10 kV/cm, a phase transition of MA → T was found near 360 K, which was manifested as a sharp single domain with a slight tail around (220)C (see Fig. S7b), where the twined doublet was merged into a sharp single (200)T that had undistinguishable tails. At 390 K, the reciprocal-space mesh scans provide conclusive evidence of the coexistence of R and T phases at E = 0 kV/cm: strong (200)T and (002)R can be seen in Fig. S7c. Upon application of E > 2 kV/cm, the two phase coexistence disappeared, and the system transformed into a single domain as evidenced by singlets about both (200)C and (220)C.
For the C-crystal, the evolution of the line scans and phase transition sequence with increasing E were easier to distinguish relative to the A-and B- crystals (see Fig. 4c). Therefore, the reciprocal-space mesh scans were performed under E = 4 kV/cm at various temperatures, as shown in Fig. 5(g–h) and S9. At 300 K, the (200)C and (220)C Bragg peaks split along the longitudinal direction, demonstrating a coexistence of monoclinic and tetragonal phases (see Fig. 4c). As can be seen in Fig. 5(g) and S9(a), a single strong peak coexisted with a weak triplet, i.e., (200)T, (020)MC b-domain and two twined a-domains. This reveals a predominant tetragonal phase with a small fraction of the MC phase. The domain configuration along (220)C was more complex, however, a single strong peak was obvious, corresponding to the (220)T domain, where the lattice parameter is consistent with that for (200)T. At higher temperatures (i.e., 330 and 360 K), a pure T phase field was obtained on application of E = 4 kV/cm.
Finally, the structural origin of large strain for ternary crystals at high temperature range can be understood by the electric field-induced phase transitions (see Fig. 2). Based on the symmetry-allowed polarization rotation theory, a final state of single tetragonal c-domain can be approached under application of large E-filed parallel to the polar vector of tetragonal phase21. For crystals with compositions near the MPB, the electric field induced strain was mainly attribtued to lattice change due to the phase transition from MA → MC and MC → T26,31,36,44. As discussed in Fig. 1h, the value of Sm for PMN-30PT crystals obviously decreased at 330 and 365 K, and was ~0.3% over the temperature above 365 K. Based on the phase diagram, it can be conjectured that the first dropping of Sm at 330 K was resulted from the temperature induced phase transition of MA → MC, resulting in the vanishing of strain contribution via E-filed induced unit cell distortion of MA to MC, while the second one at 365 K was due to the temperature induced phase transition of MC → T, leading to the disappearance of strain contribution from the polarization rotation from monoclinic plane to [001]. In turn, the strain of PMN-30PT crystals at high temperature range (i.e., above 365 K) was mainly from the polarization extension of tetragonal c-domain. Nevertheless, the B-crystal was still in the R-phase field at temperature around 365 K, indicating the main strain contribution is polarization rotation, i.e, MA → T phase transition. At temperature above 390 K, even thought the B-crystal in T-phase field, the diffraction data shows that it was in multi-domain state, rather than a single tetragonal c-domain in PMN-30PT38: a sharp tetragonal c domain was remained, which was coexisted with a weak tetragonal a domain at 390 K (see Fig. S3c). These multi-domain states are the structural origin of B-crystal exhibiting a much larger strain than PMN-30PT at higher temperature region. In other words, again, under E//[001], the strain in B-crystal was contributed from the polarization rotation and domain switching, rather than a polarization extension in PMN-30PT at this high temperature region.
Conclusions
In conclusion, a reversible, large E-field induced strain of over 0.9% at room temperature, and in particular over 0.6% above 380 K, was observed in a new generation of ternary piezoelectric single crystals. The polarization rotation path and the phase transition sequence of different compositions in these ternary systems have been determined with increasing E applied along [001] direction based on x-ray diffraction data. Electric field-temperature phase diagrams were then constructed. For crystals in the R phase field, a composition-induced bifurcation of the polarization rotation path was observed, and in particular, in contrast to binary PMN-30PT, no MC phase (or at least no single phase) was found during the E-field induced phase transition sequence. The large strain in ternary crystals, especially at higher temperature, is attributed to the lattice parameters modulated by dual independent variables in composition of these ternary solid solution crystals.
Methods
Specimen preparation
High-quality and large size ternary crystals with nominal composition of 33PIN-35PMN-32PT were grown by a modified Bridgman method29 using high purity (better than 99.99%) PbO, In2O3, MgO, Nb2O5 and TiO2 as starting materials. Due to composition segregation, the real composition of the crystals was varied from those correspond to tetragonal, MPB and rhombohedral regions32. Three typical compositions from the corresponding regions with dimensions of 4 × 3 × 3 mm3 were selected for investigations. The compositions were determined to be 31PIN-37.2PMN-31.8PT, 25.4PIN-41.2PMN-33.4PT and 28.8PIN-33.3PMN-37.9PT by Energy Dispersive X-ray Spectroscopy. These crystals were designated as A, B and C, respectively. To compare the properties and structures of this new generation of crystals with previsouly reported binary system, a binary PMN-30PT crystal was also prepared into dimensions of 3 × 3 × 0.5 mm3, which was oriented along the [001] direction in its thickness. It is well-known to exhibit the highest piezoelectric and electromechanical properties for the binary systems15. All the ternary crystals were oriented along pseudocubic (100)/(010)/(001) planes, diced into rectangular parallelepipeds with dimensions of 4 × 3 × 3 mm3, and all the faces were polished to 0.25 μm. In case of dielectric breakdown under application of high E, the corresponding rectangular parallelepipeds were then cut into several pieces along the longitudinal direction with thicknesses ranging from 0.5 to 1.5 mm. Note that these pieces had the same composition as the initial rectangular parallelepipeds due to a negligible composition gradient within such small crystals. The cut faces were successively re-polished perpendicular to the [001] direction to a roughness of 0.25 μm using a polishing grinder. Prior to the property and structure measurements, all crystals were annealed at 800 K in air for 1 hour to release any pre-stress induced during the crystal growth and polishing.
Dielectric and piezoelectric property measurements
Gold electrodes were deposited on the top and bottom surfaces by sputtering, then the macro-properties were measured along the thickness direction of the specimens. The temperature-dependent dielectric constant of crystals A, B and C, together with PMN-30PT, were characterized using a LCR meter (HP 4284A) in the zero-field-cooling condition. Unipolar strain vs E curves were measured in the temperature range of 300 to 420 K at 5 K temperature steps at a frequency of 1 Hz using a modified Sawyer-Tower circuit and linear variable differential transducer (LVDT) driven by a lock-in amplifier (Stanford Research SR850). The data was recorded under E = 50 kV cm−1 after at least two runs, thus the unipolar strain curves in Fig. 1(c–f) were recoverable (i.e., not a one-time effect from poling), and consistent with the way actuators are used. The specimens were poled under E = 10 kV/cm at 400 K for 15 mins, then cooled to 300 K. The piezoelectric coefficient d33 for various crystals were measured using a quasi-static Berlincourt d33 meter.
X-ray diffraction
X-ray diffraction studies were performed using a Philips MPD high-resolution system. Facility details can be found in a previous publication31. Diffraction measurements for the ternary crystals were performed along pseudocubic (002) and (220) zones in the zero-field-heating condition from the annealed states. Line scans were performed over the corresponding angular regions with a 2θ step interval of 0.002°, whereas reciprocal-space mesh scans were taken with a 2θ interval of 0.005°. Studies were performed under electric field by coating gold electrodes on the appropriate faces, and attaching thin wires on the electroded sides using a small drop of conducting epoxy. Silicon grease with a high dielectric breakdown strength was used to prevent arcing. We designated the electroded faces as (001). First, to determine the phase transition under E, comprehensive line scans along the (00L) direction (i.e., electrodes was on top and bottom faces) were performed on the A-, B- and C-crystals at various temperatures by first increasing and subsquently decreasing E. The E was increased until arching or even dielectric breakdown occurred, or until a sharp single peak was observed that was insensitive to further increase in E (i.e., saturation state). At each temperature, measurements were began from the annealed condition. Upon finishing the measurements along (001), the electrodes were removed using a polishing blanket with 0.25 μm aluminum powder. Then, the specimen was re-electroded on one pair of side faces perpendicular to the original (001) by sputtering. Thereafter, diffraction measurements were carried out along the (H00) and (HH0) zones. Next, to determine the domain configuration and stable phases, reciprocal-space mesh scans were obtained around the (200) Bragg peaks in the (H, 0, L) zone; and around (220) in the (H, H, L) zone. The mesh scans were recorded by a sequence of 2θ-ω scans at different ω offsets, and were shown in plots of intensity as a function of reciprocal lattice units (rlu). In this study, we fixed the value of rlu at a* = 2π/a = 1.550 Å−1, and all reciprocal-space mesh scans of PIN-PMN-PT were plotted in reference to this reciprocal unit.
Additional Information
How to cite this article: Wang, Y. et al. Large field-induced-strain at high temperature in ternary ferroelectric crystals. Sci. Rep. 6, 35120; doi: 10.1038/srep35120 (2016).
References
Zhang, Q. M. et al. An all-organic composite actuator material with a high dielectric constant. Nature 419, 284–287 (2002).
Ren, X. B. & Otsuka, K. Origin of rubber-like behaviour in metal alloys. Nature 389, 579–582 (1997).
Zhang, J. X. et al. Large field-induced strains in a lead-free piezoelectric material. Nature Nanotechnology 6, 97–101 (2011).
Chluba, C. et al. Ultralow-fatigue shape memory alloy films. Science 348, 1004–1007 (2015).
Cao, H. et al. Role of Nanoscale Precipitates on the Enhanced Magnetostriction of Heat-Treated Galfenol (Fe1 − xGax) Alloys. Physical Review Letters 102, 127201 (2009).
Finkelmann, H., Nishikawa, E., Pereira, G. G. & Warner, M. A new opto-mechanical effect in solids. Physical Review Letters 87, 015501 (2001).
Kundys, B., Viret, M., Colson, D. & Kundys, D. O. Light- induced size changes in BiFeO3 crystals. Nature Materials 9, 803–805 (2010).
Park, S. E. & Shrout, T. R. Ultrahigh strain and piezoelectric behavior in relaxor based ferroelectric single crystals. Journal of Applied Physics 82, 1804–1811 (1997).
Zhang, S. T. et al. High-Strain Lead-free Antiferroelectric Electrostrictors. Advanced materials 21, 4716–4720 (2009).
Ren, X. B. Large electric-field-induced strain in ferroelectric crystals by point-defect-mediated reversible domain switching. Nature Materials 3, 91–94 (2004).
Liu, X. & Tan, X. Giant Strains in Non-Textured (Bi Na)TiO -Based Lead-Free Ceramics. Advanced materials 28, 574–578 (2016).
Pramanick, A. et al. Strain incompatibility and residual strains in ferroelectric single crystals. Scientific Reports 2, 00929 (2012).
Maurya, D. et al. Giant strain with ultra-low hysteresis and high temperature stability in grain oriented lead-free K0.5Bi0.5TiO3-BaTiO3-Na0.5Bi0.5TiO3 piezoelectric materials. Scientific Reports 5, 08595 (2015).
Walker, J. et al. Dual strain mechanisms in a lead-free morphotropic phase boundary ferroelectric. Scientific Reports 6, 19630 (2016).
Zhang, S. J. & Li, F. High performance ferroelectric relaxor-PbTiO3 single crystals: Status and perspective. Journal of Applied Physics 111, 031301 (2012).
Ye, Z. G. High-Performance Piezoelectric Single Crystals of Complex Perovskite Solid Solutions. Mrs Bulletin 34, 277–283 (2009).
Webber, K. G., Zuo, R. & Lynch, C. S. Ceramic and single-crystal (1 − x)PMN-xPT constitutive behavior under combined stress and electric field loading. Acta Materialia 56, 1219–1227 (2008).
Paik, D. S., Park, S. E., Wada, S., Liu, S. F. & Shrout, T. R. E-field induced phase transition in <001>-oriented rhombohedral 0.92Pb(Zn1/3Nb2/3)O3-0.08PbTiO3 crystals. Journal of Applied Physics 85, 1080–1083 (1999).
Wu, F., Cai, W., Yeh, Y. W., Xu, S. & Yao, N. Energy scavenging based on a single-crystal PMN-PT nanobelt. Scientific Reports 6, 22513 (2016).
Service, R. F. Materials science - Shape-changing crystals get shiftier. Science 275, 1878–1878 (1997).
Fu, H. X. & Cohen, R. E. Polarization rotation mechanism for ultrahigh electromechanical response in single-crystal piezoelectrics. Nature 403, 281–283 (2000).
Ahart, M. et al. Origin of morphotropic phase boundaries in ferroelectrics. Nature 451, 545–548 (2008).
Jin, Y. M., Wang, Y., Khachaturyan, A. G., Li, J. F. & Viehland, D. Conformal miniaturization of domains with low domain-wall energy: Monoclinic ferroelectric states near the morphotropic phase boundaries. Physical Review Letters 91, 197601 (2003).
Xu, G., Wen, J. S., Stock, C. & Gehring, P. M. Phase instability induced by polar nanoregions in a relaxor ferroelectric system. Nature Materials 7, 562–566 (2008).
Kutnjak, Z., Petzelt, J. & Blinc, R. The giant electromechanical response in ferroelectric relaxors as a critical phenomenon. Nature 441, 956–959 (2006).
Noheda, B. et al. Polarization rotation via a monoclinic phase in the piezoelectric 92% PbZn1/3Nb2/3O3-8% PbTiO3. Physical Review Letters 86, 3891–3894 (2001).
Noheda, B., Cox, D. E., Shirane, G., Gao, J. & Ye, Z. G. Phase diagram of the ferroelectric relaxor (1 − x)PbMg1/3Nb2/3O3-xPbTiO3 . Physical Review B 66, 054104 (2002).
La-Orauttapong, D. et al. Phase diagram of the relaxor ferroelectric (1 − x)Pb(Zn1/3Nb2/3)O3-xPbTiO3 . Physical Review B 65, 144101 (2002).
Li, X. B. & Luo, H. S. The Growth and Properties of Relaxor-Based Ferroelectric Single Crystals. Journal of the American Ceramic Society 93, 2915–2928 (2010).
Zhang, S. J. et al. Polarization fatigue in Pb(In0.5Nb0.5)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 single crystals. Acta Materialia 58, 3773–3780 (2010).
Wang, Y. J. et al. Temperature-induced and electric-field-induced phase transitions in rhombohedral Pb(In1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 ternary single crystals. Physical Review B 90, 134104 (2014).
Zhang, Y. Y. et al. The compositional segregation, phase structure and properties of Pb(In1/2Nb1/2)O-3-Pb(Mg1/3Nb2/3)O-3-PbTiO3 single crystal. Journal of Crystal Growth 318, 890–894 (2011).
Chen, J. W. et al. Compositional segregation, structural transformation and property-temperature relationship of high-Curie temperature Pb(In1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 single crystals. Journal of Materials Science-Materials in Electronics 26, 9316–9328 (2015).
Zhang, S. J., Luo, J., Hackenberger, W. & Shrout, T. R. Characterization of Pb(In1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 ferroelectric crystal with enhanced phase transition temperatures. Journal of Applied Physics 104, 064106 (2008).
Davis, M., Damjanovic, D. & Setter, N. Electric-field-, temperature-, and stress-induced phase transitions in relaxor ferroelectric single crystals. Physical Review B 73, 014115 (2006).
Ohwada, K. et al. Neutron diffraction study of the irreversible R-MA-MC phase transition in single crystal Pb(Zn1/3Nb2/3)(1−x)TixO3 . Journal of the Physical Society of Japan 70, 2778–2783 (2001).
Ohwada, K., Hirota, K., Rehrig, P. W., Fujii, Y. & Shirane, G. Neutron diffraction study of field-cooling effects on the relaxor ferroelectric Pb[(Zn1/3Nb2/3)0.92Ti0.08]O3 . Physical Review B 67, 094111 (2003).
Bai, F. M. et al. X-ray and neutron diffraction investigations of the structural phase transformation sequence under electric field in 0.7Pb(Mg1/3Nb2/3)-0.3PbTiO3 crystal. Journal of Applied Physics 96, 1620–1627 (2004).
Noheda, B. et al. Electric-field-induced phase transitions in rhombohedral Pb(Zn1/3Nb2/3)(1−x)TixO3 . Physical Review B 65, 224101 (2002).
Saito, Y. et al. Lead-free piezoceramics. Nature 432, 84–87 (2004).
Jaffe, B., Cook, W. & Jaffe, H. Piezoelectric Ceramics. Academic Press Limited (1971).
Wang, R. et al. Phase coexistence and domain configuration in Pb(Mg1/3Nb2/3)O3-0.34PbTiO3 single crystal revealed by synchrotron-based X-ray diffractive three-dimensional reciprocal space mapping and piezoresponse force microscopy. Applied Physics Letters 108, 152905 (2016).
Noheda, B. et al. Electric-field-induced phase transitions in rhombohedral Pb(Zn1/3Nb2/3)(1 − x)TixO3 . Physical Review B 65, 224101 (2002).
Ohwada, K., Hirota, K., Rehrig, P. W., Fujii, Y. & Shirane, G. Neutron diffraction study of field-cooling effects on the relaxor ferroelectric Pb(Zn1/3Nb2/3)(0.92)Ti0.08O3 . Physical Review B 67, 094111 (2003).
Guo, Y. P. et al. The phase transition sequence and the location of the morphotropic phase boundary region in (1−x)Pb(Mg1/3Nb2/3)O3–xPbTiO3 crystal. Journal of Physics-Condensed Matter 15, L77–L82 (2003).
Acknowledgements
The Chinese part of this collaborative work was supported by the National Science Foundation of China (51602156 and 11134004), Natural Science Foundation of Jiangsu Province, China (BK20160824), the Fundamental Research Funds for the Central Universities (30916011208), the Opening Project of Key Laboratory of Inorganic function material and device, and Chinese Academy of Sciences (KLIFMD-2015-01). The US part of this collaborative work was sponsored by the Office of Naval Research (N00014-13-1-0049).
Author information
Authors and Affiliations
Contributions
Y.W. conceived this work and designed the experiments. Y.W. and J.L. performed the experiments. Y.W. and H.L. prepared the single crystals. The data analysis was performed by Y.W., L.C., G.Y. H.L. D.V. and Y.W. wrote the manuscript with D.V. assistance. All authors reviewed and commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Wang, Y., Chen, L., Yuan, G. et al. Large field-induced-strain at high temperature in ternary ferroelectric crystals. Sci Rep 6, 35120 (2016). https://doi.org/10.1038/srep35120
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep35120
- Springer Nature Limited
This article is cited by
-
Improved pyroelectric properties and domain structures via poling and depoling effects in Mn-doped PIN–PMN–PT single crystals