Abstract
As a new eco-friendly thermoelectric material, copper tin sulfide (Cu2SnS3) ceramics were experimentally studied by Zn-doping. Excellent electrical transport properties were obtained by virtue of 3-dimensionally conductive network for holes, which are less affected by the coexistence of cubic and tetragonal phases that formed upon Zn subsitition for Sn; a highest power factors ~0.84 mW m−1 K−2 at 723 K was achieved in the 20% doped sample. Moreover, an ultralow lattice thermal conductivity close to theoretical minimum was observed in these samples, which could be related to the disordering of atoms in the coexisting cubic and tetragonal phases and the interfaces. Thanks to the phonon-glass-electron-crystal features, a maximum ZT ~ 0.58 was obtained at 723 K, which stands among the tops for sulfide thermoelectrics at the same temperature.
Similar content being viewed by others
Introduction
Eco-friendly sulfides have attracted special interests beyond telluride and selenides in various fields including thermoelectrics (TEs) for which a high ZT value termed as thermoelectric dimensionless figure of merit is desired for practical applications of power generation and steady-state cooling (ZT = S2σT/κ, where S is Seebeck coefficient, σ is electrical conductivity, T is absolute temperature, and κ is thermal conductivity comprising of electronic component κe and phonon component κlat)1. Especially encouraging are the recent findings in binary copper sulfide of Cu1.8S2 with ZT ~ 0.5 at 673 K and superionic α-Cu1.97S with phonon-liquid-electron-crystal (PLEC) behavior3 and a strikingly high ZT ~ 1.7 at 1000 K. Nevertheless, the liquid-like electromigration of Cu and the phase transitions would be detrimental for its long-term TE performance4. Alternatively, researches on multinary sulfides have demonstrated a much higher structural and electrical stability due to the pinning effect of atoms other than Cu, indicating their promising prospect as TEs5.
Focused in the present study is a ternary compound of copper tin sulfide, Cu2SnS3 (hereafter CTS), which has a melting point of 1129 K6 and a direct band gap of 0.9–1.3 eV7,8. CTS has been reported to adapt three different structures as shown in Fig. 1, including monoclinic (ICSD-91762), cubic (ICSD-43532) and tetragonal (ICSD-50965) symmetries that can be viewed as superstructure derivatives from sphalerite type structure. These CTS structures are all based on corner-sharing tetrahedra with Cu and Sn9,10 positioned at the tetrahedral site coordinated with 4 S atoms at the corners and thus are recognized as diamond-like ternary compounds, but the arrangement of metal atoms inside the S sublattice is different from each other. In the monoclinic structure of CTS, Cu and Sn atoms fully occupy the separated 2a tetrahedral sites orderly. While in the tetragonal structure, there are three different occupations for the tetrahedral sites, i.e. the 2a tetrahedral sites (accounting for 1/4 of total) are occupied by Cu atoms only, and the 4d and 2b sites (1/2 and 1/4 of total for each) are occupied by the composite atoms M1 [43.6(2) at% Sn + 56.4(2) at% Cu] and M2 [46.3(3) at% Sn + 53.7(3) at% Cu], respectively, which means a high-degree disordering of Cu and Sn atoms at these sites. For the cubic structure, however, the tetrahedral sites become equivalent and are fully occupied by composite atoms M3 (66.7% Cu + 33.3% Sn), corresponding to a complete disordering of metal atoms in this structure. Besides, the MS4 tetrahedra are symmetric only in the cubic structure, while distorted in the monoclinic and tetragonal ones with different M-S distances and M-S-M bond angles. The structural anharmonicity features of atoms disordering and structural distortion would favor in disrupting the phonon transport to suppress the lattice thermal conductivity10,11,12, let alone the effect of interface and boundary in case of multiphase coexistence, which is commonly observed in similar ternary sulfide systems. Moreover, they all possess excellent electrical transport properties due to its 3-dimentional conductive network of hybridized 3d(Cu)-3p(S) orbitals and S-S 3p orbitals at the upper valence band, which is in favor of p-type TE performance due to its large density-of-states (DOS)13. As a result, the CTS materials can be a potential material of phonon-glass-electron-crystal which is an important characteristic of good TEs. By now, however, little has been reported in particular on CTS as a TE candidate.
Here, we investigated the pristine and hole-doped CTS in form of bulk ceramics with respect to crystal structure and TE properties, for which Zn was selected as the acceptor dopant for substituting Sn in view of its similar radius (60 pm, C.N. = 4) to that of Sn4+ (55 pm, C.N. = 4) and Cu+ (60 pm, C.N. = 4)14. Results revealed a monoclinic-tetragonal and/or cubic crystal structure evolution upon Zn-doping, and a low thermal conductivity was obtained in the heavily doped samples, for which the cation disordering in the derived cubic and tetragonal phases should have played a primary role. Moreover, the method of Zn-doping led to a significant improvement of electrical transport properties, with a maximum power factor of ~0.8 mW m−1 K−2 at 723 K. And as a result, a highest ZT of ~0.58 at 723 K was achieved, which stands among the tops of sulfide TEs, suggesting CTS as a promising eco-friendly TE material.
Results and Discussion
For the sample pellets sintered by spark plasma sintering (SPS) from synthesized powders, the phase composition and crystal structure were analyzed first by powder X-ray diffraction (XRD). Results shown in Fig. 2 revealed an interesting structural evolution in Cu2Sn1−xZnxS3 with x from 0 to 0.20. As one can see for the pristine (x = 0) sample, the diffraction patterns are indexed well to the monoclinic structure (PDF#27-0198) in agreement with the prediction by Onoda et al.10, while different from the report by Chen et al.11, presumably due to the different synthetic parameters. Upon Zn-doping with x = 0.05, Cu2Sn1−xZnxS3 turned to adopt a cubic structure (PDF#89-2877), which is not the case for the model employed in a previous simulation work13 by Zhang et al., where a monoclinic symmetry was presumed to be preserved. With x further increasing to 0.20, the XRD patterns of Cu2Sn1−xZnxS3 were found to be similar to that of cubic one, except for some tiny diffraction peaks due to the tetragonal structure (PDF#89-4714), e.g. the (101) peak at 18.31° which was absent in the cubic phases (marked with ♦ in the inset of Fig. 2), suggesting that in these samples the tetragonal phase may coexist as a secondary phase. Besides, a continuous shift of the (111) and (112) peaks respectively for cubic and tetragonal structures at around 28.3° was observed toward the higher 2θ side with x increasing from 0.05 to 0.20 as shown in the inset, which indicated a lattice contraction instead of expansion of a for the two structures, which should be caused by the further ionization of Cu+ into smaller-sized Cu2+ as discussed later.
In order to confirm the crystal structure evolution corresponding to Zn doping, the Cu2Sn1−xZnxS3 ceramic samples with x = 0 and 0.05 were selected for transmission electron microscopy (TEM) observation. Figure 3a shows a typical selected-area electron diffraction (SAED) pattern of the pristine sample. It can only be indexed as the [100] zone axis with monoclinic symmetry. By tilting the sample about 28.5°, another SAED pattern was obtained, as shown in Fig. 3b, which was indexed as the monoclinic [110] zone axis. The SAED pattern obtained from the 5% Zn-doped sample (Fig. 3c) exhibits typical diffraction patterns of the cubic [110] direction. When tilted about 35.3° to the [111] zone axis, observed is the pattern as shown in Fig. 3d. These careful SAED analyses unambiguously confirmed that the pristine sample took the monoclinic structure whereas the 5% Zn-doped sample took the cubic structure, consistent with the previous XRD analyses. Figures 3e–h are the corresponding high resolution TEM (HRTEM) images of Fig. 3a–d, respectively. The lattice fringes of the monoclinic (020) and (00-1) planes are clearly seen in Fig. 3e, and so are those of the cubic (1–11) and (002) planes in Fig. 3g, demonstrating good crystallinity and high quality of the samples. Considering the possible coexistence of multiphase in Cu2Sn1−xZnxS3 samples with x = 0.10 ~ 0.20, the XRD patterns were analyzed with Rietveld refinement method using program RIETAN-VENUS to deduce the quantitative mass ratio of monoclinic (space group: Cc), orthorhombic (space group: I-42 m) and cubic (space group: F-43 m) phases. The derived index of Rwp was low, suggesting good fitting between the experimental and calculated intensities, as shown in Fig. 4. Refinement results (Table 1) show that, with the increase of x, the mole fraction of cubic phase decreased from 54.8% (x = 0.10) to about 34% (x = 0.15, 0.20), with an increasing content of tetragonal phase from 24.1% to 60.6% correspondingly, while that of monoclinic phase was lowered from 21.1% to ~5%. Although the microstructure features (e.g. lattice defects and strains) of the grain boundaries and interfaces are still unknown, the coexistence of these phases should serve to additionally intensify phonon scattering, beside the effect owing to disordered arrangement of metal atoms, to reach a low lattice thermal conductivity. Nevertheless, due to the similarity of 3-dimensionally interconnected conductive network of Cu-S and S-S, the coexistence mainly of cubic and tetragonal structures would not affect the electrical transport properties severely for the doped samples, as discussed in the following contexts.
As to the electrical transport properties, electrical conductivity (σ) and Seebeck coefficients (S) for all samples are shown in Fig. 5. The pristine CTS exhibits a very low σ, indicative of a non-degenerate state with a low carrier concentration. The σ value increases gradually with increasing temperature from 323 K to 573 K, following strictly a small polaron hopping model15, which reflects the localized states of Cu-3d and S-3p orbitals when the sample is undoped and thus essentially non-degenerate. The increase of σ at temperatures above 573 K should be resulted by the intrinsic thermal bipolaron excitation. By contrast, the σ values for the doped compounds decrease with increasing temperature, showing a degenerate semiconductor behavior; Moreover, they increase almost linearly with the amount of Zn. These results can be explained by that the substitution of Zn ([Ar]3d104s2) for Sn ([Kr]4d105s25p2) would have introduced acceptor levels within the band gap that trapped the electrons excited from the valence band maximum of the hybridized d-p orbitals, forming Cu2+ essentially and leaving behind the increased concentration of holes and the metallic electrical properties consequently.
TE properties of the Cu2Sn1−xZnxS3 samples: (a) electrical conductivity, (b) hole mobility, (c) Seebeck coefficient, (d) power factor. The inset in (a) shows the electrical conductivity as a function of reciprocal temperature for pristine CTS and the inset in (b) shows the carrier concentration. The dash line in (b) represents the μ ∝ T−1 relationship.
To gain more insight into the transport properties in these CTS compounds, Hall Effect measurement was performed to determine the carrier concentration n and its mobility μ. As shown in Fig. 5b, n of all samples (see the inset) remain essentially constant across the whole temperature range of interest, and they increase with the Zn content, x, reaching a high level of 1021 cm−3. The Hall mobility μ decreases proportionally to T−1 as temperature increases above 448 K, which is characteristic of the predominant acoustic phonon scattering16,17. The departure below 448 K reveals that impurity scattering from ionized defects becomes important near the room temperature. More importantly, the μ values are very close in the doped cubic and cubic-tetragonal mixed phases of CTS, which is caused by that the pathways for holes in these structures are similar, being along Cu-S-Cu channels 3-dimensionally extending throughout the crystal lattices despite the slight difference regarding the coordination of metal atoms in the different phases, and are less affected by the impact of dopant atoms.
Shown in Fig. 5c are the p-type Seebeck coefficients (S) for Cu2Sn1−xZnxS3 (x = 0–0.20) samples. For the pristine CTS, S climbs as temperature rises up to 573 K, the decrease thereafter (see the inset of Fig. 5a) is probably due to the intrinsic thermal excitation of electrons from valence to conduction bands, which is in accordance with the rapid increase of σ from 573 K. For all the Zn-doped samples, the S values for Cu2Sn1−xZnxS3 decrease with increasing x due to the enhanced n, e.g. from 410.0 μV K−1 (x = 0) to 117.3 μV K−1 (x = 0.20) at 723 K. The S increases almost linearly with increasing temperature due to the continuous increase of chemical potential, while without a perceivable abrupt change which has occurred in Cu1.8S2, reflecting the preservation of initial crystal structure in the studied temperature range. This phenomenon is considered beneficial to improving the structural durability of TE devices against temperature fluctuation during the long-term operation. The S values decrease regularly with increasing σ, which seems to suggest that the aforementioned phase change has little influence on S in agreement with the deduction that the valence band is almost unaffected by the dopant atoms as discussed above. The S data are basically comparable with other representative tetrahedron-based sulfides (Cu1.8S2, Cu2ZnSnS418) but are a little smaller than that of the state-of-the-art selenides and telluride TEs with a similar σ, e.g., Pb1−xNaxSe (~160 μV K−1)19,20, and Bi0.5Sb1.5Te3 (~240 μV K−1)21. However, thanks to the significantly enhanced σ after doping, the power factor (PF) of the Cu2Sn1−xZnxS3 (x = 0–0.20) samples increase largely with increasing x. The highest PF of ~0.84 mW m−1 K−2 at 723 K is achieved in the x = 0.20 sample, which is almost 20 times larger than that of the pristine CTS (0.047 mW m−1 K−2), and is comparable to that of Cu2−xS.
For further information about the effect of crystal structure on electrical transport properties, density-of-states (DOS) effective mass of carriers (m*) were calculated using the equation based on simple parabolic approximation22: , where h, kB, ne, Fn and ζ are the Plank constant, Boltzmann constant, carrier concentration, Fermi integral, and chemical potential, respectively (see Supplementary Table S1). The obtained high m* values (2.4–3.0) m0 with a high hole concentration level of 1021 cm−3 for samples with x = (0.10–0.20) are satisfactorily close, suggesting the minor influence of the two different crystal symmetries (cubic and tetragonal) on electronic structures. They are similar to the simulated single parabolic band model results of (2.5–4.2) m0 which correspond to carrier concentrations at 1020 cm−3 level13. The m* value increases with x, from 1.45 m0 at 300 K for the x = 0.05 compound to 2.45 m0 for the x = 0.20 sample, close to the reported results in Zn-doped Cu2SnSe323, and this behavior is qualitatively in accordance with the predicted higher m* at elevated carrier concentrations for Cu2SnX3 (X = S, Se)13.
To clarify the physical mechanism for the increase of m* with x in these samples, first principles calculations were performed and the DOS effective mass is calculated by fitting the calculated total DOS using parabolic bands. Results (see Supplementary Figure S1) indicate that the valance electronic structures after heavy Zn-doping are not changed substantially except for a shift of Fermi energy into deeper levels with larger x, which reflects the minor influence of acceptor dopant on the band structure of CTS. (Therefore in the following calculations, the DOS of non-doped Cu2SnS3 unit cell were used to calculate the m* with the Fermi energy determined according to the measured carrier concentration.) As can be seen clearly in Table 2, the calculated m* values increase gradually with the increase of n and are well in accordance with the results derived from measured Seebeck coefficients. Thus, it confirms that the increase of m* drives from the Fermi energy shifting into deeper inside the valance band where the multiple hole pockets along the high-symmetry line A-M13 can also be incorporated, while without much effect due to the crystal structure evolution. This would be beneficial for attaining high power factor even at heavy Zn-doping levels.
Thermal conductivities (κ) at 323–723 K for all samples are plotted in Fig. 6a. Generally, the κ values decrease largely from (2.1 ± 0.5) W m−1 K−1 at 323 K to a low level of (0.9 ± 0.4) W m−1 K−1 at 723 K, basically falling in a range for chalcogenide materials reported previously21,24,25,26,27. For a detailed inspection into the heat transport behavior, the electronic thermal conductivity was evaluated following the Wiedemann-Franz relation28 (κe = LσT, where the calculated Lorenz number, L, are given in Supplementary Figure S2), and the lattice component κlat was obtained by subtraction of the total κ with κe. As shown in Fig. 6b, all the κlat values as a whole are relatively low (within 1.45–2.38 W m−1 K−1 at 323 K), as a primary result of the soft and inhomogeneous interatomic (Cu-S and Sn-S) bonding with different electronic and mass polarity. Approximately, they decrease proportionally to T−1 with temperature, implying the phonon-phonon Umklapp process dominating in the phonon transport.
TE properties of the Cu2Sn1−xZnxS3 samples: (a) thermal conductivity, (b) lattice thermal conductivity, (c) variation of lattice thermal conductivity with x at 323 K (black diamonds) and 723 K (red circles), respectively, with a schematic crystal structure evolution from monoclinic, cubic to coexistent phases, which are exactly composed of cubic (major) and tetragonal (minor) for Cu2Sn1−xZnxS3. Dotted lines are imaginary tendency of κlat as a function of doping content, and (d) ZT. The theoretical minimum thermal conductivity of CTS at high temperatures (cited from ref. 13) is also plotted in (b) for comparison.
More importantly, it shows obviously a large decrease in the κlat for the doped samples from that of pristine CTS in the whole temperature range, even approaching the theoretical minimum (0.3 W m−1 K−1) for Cu-Sn-S systems at high temperatures13. Meanwhile, for the doped samples, the κlat values are almost constant despite of their different doping levels, as shown in Fig. 6c. It has been known that with the structural change from pristine monoclinic into the cubic and tetragonal structures of doped samples, the local symmetry of [MS4] are improved while the metal atoms are rearranged from an ordered state in the monoclinic structure into a completely disordered state (at the 4a sites) in cubic structure and partially disordered state (at the 2b and 4d sites) in tetragonal structure according to the reported crystallographic database. Thus it concludes, the random (either completely or partially) distribution of Cu, Zn and Sn and vacancies, rather than the local distortion of [MS4] tetrahedra, may have played an important role in suppressing the lattice thermal conduction possibly by thoroughly disrupting the normal phonon transport5. In addition, the coexistence of cubic and tetragonal and even monoclinic phases should be taken into account of phonon scattering at the interfaces and grain boundaries.
The calculated dimensionless figure of merit (ZT) of Cu2Sn1−xZnxS3 is shown in Fig. 6d. The ZTs increase with temperature in all samples. Though the largest PF = 0.84 mW m−1 K−2 is obtained for the x = 0.20 sample, its ZT suffers from the rise of κ by the large electronic contribution. Instead, the highest ZT ~ 0.58 is achieved in the x = 0.10 sample, which stands the highest among Pb-free sulfide TE materials except the PLEC Cu2S3 till now, and even surpasses many selenides and tellurides (e.g., Cu1.8S2 and CuGaTe229) at the same temperature (see Supplementary Table S2).
Conclusion
Cu2SnS3 (CTS) compounds can be viewed as a good thermoelectric material with structural and electrical features of phonon-glass-electron-structure, and can be tuned into excellent p–type TE materials through Zn-doping. First of all, CTS is favored by the disordered arrangement of metal atoms in the cubic and tetragonal phases and the interfaces and grain boundaries in the multiphase samples which significantly enhance the phonon scattering, leading to an ultralow lattice thermal conductivity. Second, CTS is benefited from its special electronic nature that is mainly determined by the Cu-3d and S-3p orbitals which is less affected by the coexistence of cubic and tetragonal phases, and allows relatively independent manipulation of carrier concentration through doping without affecting the valence band, and meanwhile, the DOS m* that increases with carrier concentration ensures high power factor achievable by heavy doping. These findings are expected to be helpful for further investigation into the CTS-like compounds as environment-friendly TE materials. Based on the result that the lattice thermal conductivity is readily low at high temperatures, further efforts should be directed to the enhancement of PF, e.g. by way of band engineering or carrier energy filtering.
Methods
Pristine and heavily hole-doped (by Sn-site-Zn-doping) CTS ingots with nominal compositions of Cu2Sn1−xZnxS3 (x = 0, 0.05, 0.10, 0.15, 0.20) were first synthesized by direct reaction of high purity element powders with a molar ratio of Cu:Sn:Zn:S = 2:1−x:x:3 in a sealed silica tube at high temperatures. Powder obtained through grinding the corresponding ingot was then consolidated into pellets by spark plasma sintering under 50 MPa at 773 K for 5 min. Relative density of the as-produced pellets was determined by the Archimedes method to be ~94% of the theoretical value for all samples.
Phase composition and crystal structure were checked by X-ray diffraction (XRD) analysis with an ARL X’TRA diffractometer (SmartLab3, RIGAKU, Japan) using Cu Kα radiation. TEM specimens were prepared by a standard procedure which includes mechanical grinding, polishing, precision dimpling, and ion milling. SAED analyses and HRTEM observations were performed on an electron microscope operated at 200 kV (JEM-2100, JEOL, Japan). Seebeck coefficient and electrical conductivity were measured in the radial direction of a bar-shaped sample with dimensions of 10 mm × 3 mm × 3 mm by a conventional steady state method and a four-probe method, respectively, in a He atmosphere at 323–723 K with a commercial system (LSR-3). Hall effect measurement for carrier concentration and mobility was conducted with a van der Pauw configuration under vacuum using the ResiTest8300 system (Toyo Tech. Co.) Thermal diffusivity (D) was measured in the axial direction of a disk-shaped sample of Φ 10 mm × 1 mm using a Netzsch laser flash diffusivity instrument (LFA457, Netzsch, Germany). Thermal conductivity (κ) was calculated by κ = DdCp, where Cp is the specific heat capacity measured by differential scanning calorimetry (DSC: 2910, TA instruments), and d is the mass density measured using the Archimedes method.
The first principles calculations were performed using the Quantum-ESPRESSO package30, and the Garrity-Bennett-Rabe-Vanderbilt (GBRV) high-throughput pseudo-potential library31. Local density approximation (LDA) was used along with ultrasoft pseudopotentials for all the atoms. A plane wave basis with kinetic energy cutoff of 600 eV was used to ensure the convergence in all the calculations. A k-point sampling of 3 × 5 × 7 was used for Cu2SnS3 unit cell, and for larger cells the k-mesh are reduced accordingly. The atomic positions are relaxed until all the force components on each atom are less than 10−3 atomic unit. For density of states calculations, a denser k-point sampling of 5 × 7 × 11 was used for Cu2SnS3 unit cell.
Additional Information
How to cite this article: Shen, Y. et al. Eco-friendly p-type Cu2SnS3 thermoelectric material: crystal structure and transport properties. Sci. Rep. 6, 32501; doi: 10.1038/srep32501 (2016).
References
Qurashi, A. Introduction: An Overview of Metal Chalcogenide Nanostructures for Renewable Energy Applications. (John Wiley & Sons, Inc., 2014).
Ge, Z. H. et al. Synthesis and transport property of Cu1.8S as a promising thermoelectric compound. Chem. Commun. 47, 12697–12699 (2011).
He, Y. et al. High thermoelectric performance in non-toxic earth-abundant copper sulfide. Adv. Mater. 26, 3974–3978 (2014).
Dennler, G. et al. Are Binary Copper Sulfides/Selenides Really New and Promising Thermoelectric Materials? Adv. Energy Mater. 4, 201301581 (2014).
Qiu, P., Zhang, T., Qiu, Y., Shi, X. & Chen, L. Sulfide bornite thermoelectric material: a natural mineral with ultralow thermal conductivity. Energy Environ. Sci. 7, 4000–4006 (2014).
Fiechter, S., Martinez, M., Schmidt, G., Henrion, W. & Tomm, Y. Phase relations and optical properties of semiconducting ternary sulfides in the system Cu–Sn–S. J. Phys. Chem. Solids 64, 1859–1862 (2003).
Fernandes, P. A., Salomé, P. M. P. & Cunha, A. F. d. A study of ternary Cu2SnS3 and Cu3SnS4 thin films prepared by sulfurizing stacked metal precursors. J. Phys. D: Appl. Phys. 43, 215403 (2010).
Zhai, Y.-T. et al. Structural diversity and electronic properties of Cu2SnX3 (X = S, Se): A first-principles investigation. Phys. Rev. B 84, 075213 (2011).
Su, Z. et al. Fabrication of ternary Cu–Sn–S sulfides by a modified successive ionic layer adsorption and reaction (SILAR) method. J. Mater. Chem. 22, 16346 (2012).
Onoda, M., Chen, X. A., Sato, A. & Wada, H. Crystal structure and twinning of monoclinic Cu2SnS3 . Mater. Res. Bull. 35, 1563–1570 (2000).
Chen, X. A., Wada, H., Sato, A. & Mieno, M. Synthesis, electrical conductivity, and crystal structure of Cu4Sn7S16 and structure refinement of Cu2SnS3 . J. Solid State Chem. 139, 144–151 (1998).
Su, Z. et al. Fabrication of ternary Cu–Sn–S sulfides by a modified successive ionic layer adsorption and reaction (SILAR) method. J. Mater. Chem. 22, 16346 (2012).
Xi, L. et al. Chemical bonding, conductive network, and thermoelectric performance of the ternary semiconductors Cu2SnX3 (X = Se, S) from first principles. Phys. Rev. B 86, 155201 (2012).
Shannon, R. D. Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Crystallographica 32, 751–767 (1976).
Ahmad, M., Rafiq, M. A., Rasool, K., Imran, Z. & Hasan, M. M. Dielectric and transport properties of bismuth sulfide prepared by solid state reaction method. J. Appl. Phys. 113, 043704 (2013).
Zeier, W. G., Zevalkink, A., Schechtel, E., Tremel, W. & Snyder, G. J. Thermoelectric properties of Zn-doped Ca3AlSb3 . J. Mater. Chem. 22, 9826 (2012).
Rowe, D. M. Thermoelectrics Handbook. Crc Press (2005).
Liu, M.-L., Huang, F.-Q., Chen, L.-D. & Chen, I. W. A wide-band-gap p-type thermoelectric material based on quaternary chalcogenides of Cu2ZnSnQ4 (Q = S,Se). Appl. Phys. Lett. 94, 202103 (2009).
Chasapis, T. C. et al. Understanding the role and interplay of heavy-hole and light-hole valence bands in the thermoelectric properties of PbSe. Phys. Rev. B 91, 085207 (2015).
Liu, W. et al. Convergence of Conduction Bands as a Means of Enhancing Thermoelectric Performance of n-Type Mg2Si1−x Sn x Solid Solutions. Phys. Rev. Lett. 108, 166601 (2012).
Kim, S. I. et al. Dense dislocation arrays embedded in grain boundaries for high-performance bulk thermoelectrics. Science 348, 109–114 (2015).
Vining, C. B. A model for the high-temperature transport properties of heavily doped n-type silicon-germanium alloys. J. Appl. Phys. 69, 331–341 (1991).
Raju, C. et al. Thermoelectric properties of Zn doped Cu2SnSe3 . Mater. Chem. Phys. 147, 1022–1028 (2014).
Liu, M.-L., Chen, I. W., Huang, F.-Q. & Chen, L.-D. Improved Thermoelectric Properties of Cu-Doped Quaternary Chalcogenides of Cu2CdSnSe4 . Adv. Mater. 21, 3808–3812 (2009).
Shi, X., Xi, L., Fan, J., Zhang, W. & Chen, L. Cu−Se Bond Network and Thermoelectric Compounds with Complex Diamond like Structure. Chem. Mater. 22, 6029–6031 (2010).
Zeier, W. G. et al. Phonon scattering through a local anisotropic structural disorder in the thermoelectric solid solution Cu2Zn1−x Fe x GeSe4 . J. Am. Chem. Soc. 135, 726 (2013).
Ge, Z. H. et al. Low-cost, abundant binary sulfides as promising thermoelectric materials. Mater. Today (2015).
Fan, J. et al. Structural evolvement and thermoelectric properties of Cu3−x Sn x Se3 compounds with diamond-like crystal structures. Dalton T. 43, 16788–16794 (2014).
Plirdpring, T. et al. Chalcopyrite CuGaTe2: A High-Efficiency Bulk Thermoelectric Material. Adv. Mater. 24, 3622–3626 (2012).
Giannozzi, P. et al. QUANTUM ESPRESSO: a modular and open-source software project for quantum simulations of materials. J. Phys.: Condens. Matter 21, 395502 (2009).
Garrity, K. F., Bennett, J. W., Rabe, K. M. & Vanderbilt, D. Pseudopotentials for high-throughput DFT calculations. Comp. Mater. Sci. 81, 446–452 (2014).
Acknowledgements
This research was supported by the Natural Science Foundation of China under Grant No. 51272103 and the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD). The authors thank Prof. Yanfeng Gao, Prof. Jun Luo and their research team at Shanghai University for their kind assistance on thermal diffusivity and specific heat capacity measurements.
Author information
Authors and Affiliations
Contributions
Y.S., Y.Y. and Y.W. designed the experiments. Y.S. carried out the experiments under supervision of Y.W. and wrote the main manuscript text. C.L. and R.H. performed the TEM, SAED and HRTEM experiments and analyzed the results. R.T. and K.K. performed the Hall effect measurement. R.Z. performed the calculations and data analysis. L.P., C.W., K.K. and Y.W. commented on the manuscript and made suggestions for revision. All authors took part in the discussion of the results.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Shen, Y., Li, C., Huang, R. et al. Eco-friendly p-type Cu2SnS3 thermoelectric material: crystal structure and transport properties. Sci Rep 6, 32501 (2016). https://doi.org/10.1038/srep32501
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep32501
- Springer Nature Limited
This article is cited by
-
Effects of the growth process on surface morphology of Cu2(Sn1−xGex)S3 thin films
Journal of Materials Science: Materials in Electronics (2024)
-
Tuning Thermoelectric Properties of Spin-Coated Cu2SnS3 Thin Films by Annealing
Journal of Electronic Materials (2023)
-
Phase evolution and thermoelectric performance of Cu2SnS3
Journal of Materials Science: Materials in Electronics (2023)
-
Effect of the stacking order, annealing temperature and atmosphere on crystal phase and optical properties of Cu2SnS3
Scientific Reports (2022)
-
Synergistic effect of In doping on electrical and thermal properties of Cu2SnSe3 thermoelectric system
Journal of Materials Science: Materials in Electronics (2021)