Abstract
Synthesis of low cost, durable and efficient electrocatalysts that support oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) are the bottlenecks in water electrolysis. Here we propose a strategy for the development of controllably alloyed, porous, and low density nickel (Ni) and cobalt (Co) based alloys - whose electrocatalytic properties can be tuned to make them multifunctional. Ni and Co based alloy with the chemical structure of Ni1Co2 is identified as an efficient OER catalyst among other stoichiometric structures in terms of over potential @ 10 mAcm−2 (1.629 V), stability, low tafel slope (87.3 mV/dec), and high Faradaic efficiency (92%), and its OER performance is also found to be on par with the benchmarked IrO2. Tunability in the porous metal synthesis strategy allowed the incorporation of graphene during the Ni sponge formation, and the Ni- incorporated nitrogen doped graphene sponge (Ni-NG) is found to have very high HER activity. A water electrolysis cell fabricated and demonstrated with these freestanding electrodes is found to have high stability (>10 hours) and large current density (10 mAcm−2 @ 1.6 V), opening new avenues in the design and development of cost effective and light weight energy devices.
Similar content being viewed by others
Introduction
Rational organization and design of bulk porous multi-metallic architectures are highly demanding and receiving tremendous attention from the scientific community due to their immense applications in energetics1. On the other hand, advancement in atomically thin layered materials (2D materials), witnessed during the last decade, has initiated everlasting attempts towards the development of composites of metals/metal oxides and 2D materials based electrocatalysts2,3,4,5,6. Despite the development of numerous metal free 2D materials based catalysts, benchmarked conventional metals in energy technologies are still remain as unbeatable in terms of over potential and long-standing performance7,8,9. Nevertheless the expensive and scarce metals in conventional energetics need to be replaced/ reduced for viable futuristic energy technologies.
One of the ways for the efficient reduction of metal usage (‘metal management’) is the creation of porous metallic structures such as sponges or foams (with their 75–95% of the volume consists of void spaces) which will eventually help to decrease the weight of the device. Further, low density porous materials provide enhanced surface area than their bulk high density counter parts that can lead to large electrode-electrolyte contact areas and high specific and mass activities10,11,12. Various approaches were reported for the development of metallic foams (foams are hard and rigid, unlike sponges), where de-alloying, combustion synthesis, liquid polyol reduction method, decomposition of metal complexes etc. are to name a few13,14,15,16,17,18,19. All the above mentioned techniques rely on laborious multistep processes including casting in inert atmospheres. Here we propose a single step alloying process for the development of multi-metallic sponges using a template free bulk synthesis method, and demonstrated the performance of these sponges in water electrolysis.
Splitting of water into oxygen and hydrogen is identified as one of the promising alternatives to address the energy crisis via the production of electric energy and hydrogen fuel19,20,21. Efficient oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) are the two key components in water splitting technology. OER and HER reaction kinetics are inherently sluggish and impose large over potentials. This results in to large losses in the overall efficiency of the respective devices, and hence catalysts need to be supplemented to improve the reaction kinetics. Though enormous efforts have been devoted to find effective catalysts, precious metals based catalysts such as RuO2 and IrO2 are still remain as unbeatable for OER23,24,25. However, these precious metal oxides are not suitable for large-scale applications and sustainable energy technologies. Development of active (low over potential), durable (stability in the performance), and inexpensive catalysts is therefore of high topical concern.
Among various abundant transition metals, Ni is probably the most studied catalytic material in its various forms26,27,28. Ni is a good electrode material in alkaline medium for OER due to its relatively low over potential, low cost and high corrosion resistance29,30,31. Further, spinel oxides of Co are also identified as good catalysts for OER32,33,34,35. Co (metallic and its other forms such as oxides or hydroxides) or Fe is often used as an additive to improve the reversibility, electrocatalytic activity and stability of pure Ni36,37,38,39,40,41. In the case of HER, the most successful catalysts identified to the date are mainly based on platinum based materials. Recently, the concept of engineering the same material by doping/alloying to make them enabled for bi- or tri- functional catalysis is gaining interest. For example, a recent report cite the possibility of metal/metal oxide/doped graphene composites for multifunctional catalysis - oxygen reduction, oxygen evolution and hydrogen evolution reactions, whose properties can be on par with commercial noble metal based catalysts42. Hence incorporation of porous graphene in to metallic sponges, if possible, can bring multiple functionalities in to graphene.
Herein, we report a one pot, economically feasible, and scalable synthesis method to produce Ni/Co based catalysts for various energy technologies including water splitting with ‘enhanced activity and appealing stability’ using readily available nickel and cobalt salts (a schematic of the concept is portrayed in Fig. 1). Different weight ratios of nickel nitrate hexahydrate [Ni (NO3)2.6H2O] and cobalt nitrate hexahydrate [Co (NO3)2.6H2O], are used as Ni and Co sources respectively, and ethylene glycol (EG) is used as both solvent and reducing agent. In a simple procedure, a sudden introduction of reactant solution [EG+ Ni (NO3)2+ Co (NO3)2)] in to a hot glass dish (maintained at a temperature of 300 °C) leads to the evolution of NO2 from the metal precursors and subsequent production of fluffy sponges. The HER catalyst is also developed using the same procedure with the introduction of nitrogen incorporated graphene (NG)during the reaction and it leads to the formation of highly stable nitrogen doped graphene wrapped nickel sponges (Ni-NG). Finally, a water electrolysis cell is demonstrated by using Ni-Co alloy as anode and Ni-NG as cathode.
Results and Discussions
Material synthesis and characterization
In the optimized synthesis procedure for Ni sponges, 36 g of Ni (NO3)2.6H2O (Sigma-Aldrich) and 18 mL of EG (C2H6O2) (Sigma-Aldrich) were taken in a 100 mL beaker and ultra-sonicated for 1 hour. The resultant mixture was poured into a cylindrical crystalline glass dish, which was pre-heated to a temperature of 300 °C using a hot plate in the ambient atmosphere. A sudden introduction of reactants in to the hot glass dish leads to the evolution of NO2 gas and subsequent production of fluffy Ni sponge. Here EG is found to be acting as reducing agent for the reduction of nickel (II) ion to metallic nickel43. The same synthesis route was followed for the preparation of Ni-Co alloy sponges. Here Ni (NO3)2.6H2O and Co(NO3)2.6H2O, were mixed together taking a total amount of 36 g in the weight ratio of 1:1, 1:2 and 2:1 respectively and the resulting sponges were named as Ni1Co1, Ni1Co2 and Ni2Co1(deduced from the crystal structure studied later using XRD, X-ray fluorescence (XRF), X-ray photoelectron spectroscopy (XPS), and energy dispersive X-ray spectroscopy (EDS)) respectively. Cobalt oxide (Co3O4) sponge was resulted from the reaction of Co(NO3)2.6H2O and EG in the absence of Ni salt, since the energy needed for the reduction of Co (II) to Co (0) is higher than that of Ni (II) to Ni (0)44.
Powder X-ray diffraction (Bruker XRD, CuKα radiation, λ= 1.5418 Å) experiments were performed on sponges before and after the electrochemical experiments as shown in Fig. 2A,B. The XRD pattern of the Ni sponge revealed that the peaks at 2θ values 44.8, 52.2 and 76.6 belong to (111), (200) and (220) planes respectively (JCPDS no: 870712) indicating the formation of face centered cubic (fcc) Ni. Ni sponge XRD shows the absence of oxide peaks in it (either nil or less than 2% of the detectable level of XRD). The XRD pattern of the Co3O4 sponge shows peaks at 19.09, 31.34, 36.89, 38.67, 44.2, 59.4, 65.37, 73.5 and 77.5 correspond to (111), (220), (222), (311), (400), (511), (440), (620) and (533) planes of Co3O4 (JCPDS card no. 42–1467). The XRD pattern of the all samples of Ni-Co sponges are showing peaks at angles 2θ = 44.48, 51.92 and 76.35 belong to planes (111), (200) and (220) respectively, which correspond to that of Ni-Co alloys45.
(A,B) XRD patterns of different types of Ni and Co sponges before and after OER experiments. (C–E) FESEM images of Ni, Co3O4 and Ni1Co2 sponges respectively. (F) HRTEM image of Ni1Co2 (arrows represent the pores in the sponge), (G,H) are the STEM-EDS elemental mapping for Ni and Co in the corresponding TEM image shown in the inset of (F) respectively.
To find out the elemental composition of different Ni-Co alloys, XRF studies are conducted on sponges (Figure S1). The elemental composition (Ni:Co) in Ni1Co1, Ni2Co1 and Ni1Co2 are found to be 49.30:50.70, 66.36:33.64 and 32.99:67.01 respectively. To confirm further the observed elemental composition, EDS analysis is conducted on various sponges (Figure S2). The elemental compositions calculated from EDS are found to be in close agreement with the XRF values (49.50:50.50, 66.89:33.11 and 33.72:66.80 for Ni1Co1, Ni2Co1 and Ni1Co2 respectively).
The morphology of the as prepared binary Ni-Co alloy structures are examined via field emission scanning electron microscope (FESEM). Figure 2C–E shows the FESEM images of various sponges. It is clear from the figures that all the images exhibit the characteristics of interconnected porous network structure with a wide range of pore sizes (micro to mesoscopic pores). BET (supporting information, Figure S3A) surface area of the Ni1Co2 is calculated as ~10 m2/g which is much higher than that of commercial Ni sponge (0.01–0.1 m2/g). The isotherm shows a type-II adsorption isotherm (negligible concave section) - which is attributed to the microporous volume uptake while rapid rise in total volume near P/Po = 1 corresponds to a microporous material (which further confirmed from Hg intrusion porosimetry, supporting information Figure S3B). The Hg porosimetry results show that the pore diameter varies from ~4 μm to 262 μm. FESEM images at different magnifications are shown in supporting information (Figure S4).
Though the morphologies of different sponges are same, there is a large variation in their calculated bulk densities (tapped density). Ni sponge is having lowest density and with the increase in Co to Ni ratio, the densities of the sponges are found to be increased. The densities of the sponges are found to be 45 mg/cc, 60 mg/cc, 72 mg/cc, 100 mg/cc and 122 mg/cc for Ni, Ni2Co1, Ni1Co1, Ni1Co2 and Co3O4 respectively. High resolution transmission electron microscope (HRTEM) image of Ni1Co2 sponge (which in the later section is discussed as the best material among the other sponges towards OER) is carried out and is shown in Fig. 2F. The HRTEM image has been taken after dispersing the sponge in acetone and drop casting it on a copper grid. The image shows that the sponge still keeps the structural integrity and porous nature. The elemental mapping performed using this Scanning TEM (STEM) - EDS is shown in Fig. 2G,H. Uniform distribution of Ni and Co throughout the sponge is evident from the mapping. It indicates the uniform alloying of the formed Ni1Co2 sponge.
In order to have a better insight about the chemical states of the sponges at the surface, XPS studies were conducted on as prepared Ni1Co2 sample without ion etching. The characteristic peaks of Ni, Co and O are observable in the survey spectrum. The XPS spectra of Co2p and Ni2p are shown in the Fig. 3. The broad Ni2p3/2 shows the presence of metallic Ni (~852.6 eV) and NiO (~853.7 eV). The multiple-split peaks in between 870–885 eV also indicate the presence of oxides (NiO) in the sample. The presence of multiple oxidation states is evident in the case of Co2p spectrum too (Fig. 3B). This indicates that a small percentage of surface oxidation has occurred during the sponge formation, though the amount is negligibly small to detect using wide angle XRD. The plasma treated surface etching followed by EDS studies conducted on Ni1Co2 sponges indicate that the presence of oxygen is limited to the surface of the sponge (~50 nm from the surface, supporting information S5). Further to evaluate the exact thickness of the oxide layer formed on the surface Rutherford back scattering (RBS) experiment is performed on the Ni1Co2. Figure 3C,D shows the RBS data taken at some of the energies. The oxygen peak starts appearing at 3.036 MeV and disappears after 3.078 MeV. All the spectra are simulated with three layered structure using SIMNRA software. From the RBS data we found out that the oxygen is only up to a depth of nearly ~44 nm, correlating with EDS studies.
Electrochemical OER Studies
Linear sweep voltammograms (LSVs) for oxygen evolution reaction on various Ni and Co based samples are performed and the results are shown in Fig. 4A. The Ni1Co2 has shown highest activity (low onset potential and high current density) towards OER. The Electrocatalytic activity of Ni1Co2 before and after pre- oxidation is shown in Figure S6. After the pre-oxidation, OER activity of all the sponges increased drastically due to the formation of elecrtocatalytically active oxide rich surface, where the oxide layer will enhance the adsorption kinetics while inner metallic core will contribute to the conductivity of carriers. The Tafel slopes of different samples after pre-oxidation are given in Fig. 4C. Tafel slopes are calculated as 96.4 mV/dec, 94.8 mV/dec, 94.3 mV/dec, 92.8 mV/dec and 87.3 mV/dec for Ni, Co3O4, Ni2Co1, Ni1Co1 and Ni1Co2 respectively. The lower Tafel slope value of Ni1Co2 suggests its higher OER activity. During the OER measurements, Ni1Co2 shows a significantly low over potential (1.629 V) to reach a current density of 10 mAcm−2 in comparison to that of Ni1Co1 (1.654 V), Co3O4 (1.674 V), Ni2Co1 (1.686 V) and Ni (1.744 V) as shown in Fig. 4D. The stable Ni-Co-oxide/Ni-Co alloy hetero structure is responsible for the augmented electrocatalytic properties of Ni1Co2. Figure 4B shows the LSVs for the effect of scan rate on peak current for the Ni1Co2 sample. Inset of the Fig. 4B shows the plot of peak current vs scan rate. Thin layer diffusion occurring at the electrodes is proved by scan rate dependent peak current measurements (supporting information Figure S7). The slope of the log (peak current) vs log (scan rate) is found to be ~0.98, indicating the thin layer diffusion as reported in the literature46.
(A) LSVs for the comparison of oxygen evolution activities of different catalysts in 0.1 M KOH, scan rate 10 mV/s (inset magnifies the area marked by dotted circle). (B) LSVs of Ni1Co2 at various scan rate ranging from 10 mv/s to 50 mV/s, inset shows the plot of peak current vs scan rate showing the linearity. (C) Tafel plot derived from (A) for various catalysts, and (D) potential needed to achieve the current density 10 mAcm−2 (over potentials of various electrodes).
To calculate the charge transfer resistance during OER measurements electrochemical impedance spectroscopy (EIS) is conducted on various samples using a three electrode system by applying a potential of 1.594 V in 0.1 M KOH. The frequency of the ac voltage was swept in the range of 100 KHz to 1 Hz, and the impedance data were fitted to the semicircle for calculating the Rct values. The Rct values for different sponges are found to be 710 Ω, 514 Ω, 407 Ω, 287 Ω and 23 Ω for Ni, Co3O4, Ni2Co1, Ni1Co1 and Ni1Co2 respectively (Supporting information, Figure S8). The less charge transfer resistance of Ni1Co2 is in concordance with the enhancement in its OER performance. The OER performance of Ni1Co2 is compared with that of the benchmarked catalyst IrO2 and is shown in supporting information Figure S9. The higher activity of Ni1Co2 towards OER is evident from this graph. Further, the Faradaic efficiency of the Ni1Co2 electrode is calculated as 92% using Rotating Ring Disc Electrode (RRDE) voltammetry (the details are given in supporting information, Figure S10). The RRDE experiment confirms the formation of O2 at the anode, whilst to further confirm the formation of O2, a ‘blue bottle’ experiment is conducted where the oxidation of leuco- methylene blue to methylene blue is shown as a confirmatory test for the formation of O2 at the anode (please see the details in supporting information Figure S11 and Video S1).
Electrochemical HER studies
The above discussed Ni1Co2 based sponge is studied for it’s HER catalytic performance in alkaline media. The alkaline HER catalytic activities of various sponges namely, Ni, nitrogen doped graphene powder (NG), Ni1Co2, and Ni-NG, are compared and it is shown in supporting information, Figure S12. It is observed that the HER catalytic activity of Ni sponge is improved with the incorporation of NG (a recent study indicates that nitrogen doping can introduce more HER active sites in graphene resulting in to a higher HER efficiency with higher amount of nitrogen. Hence NG can bring HER activity in Ni sponge and this is in tune with the report of Fei et al.47. Hence a water electrolysis full cell can be developed without the aid of benchmarked precious metal/metal oxide catalysts. The porous morphology of Ni-NG is shown in supporting information Figure S13. The XPS survey spectrum is shown in the supporting information indicating the presence of Ni, carbon (C), nitrogen (N) and oxygen. The presence of oxygen and multiple oxidation states of Ni in Ni2p spectrum indicate the traces of NiO in the Ni-NG sponge (supporting information Figure S14).
HER polarization plots measured in 0.1 M KOH with Ni-NG and benchmarked Pt/C are shown in Fig. 5A. The over potentials measured at 10 mAcm−2 for Ni-NG and Pt/C are found to be −0.246 V and −0.126 V respectively. This value obtained for Ni-NG is found to be far better in terms of stability and over potential than that of the previously reported Ni based catalysts, and comparable with that of the recently reported other HER catalysts48,49. The Tafel slopes calculated for Ni-NG and Pt/C are 44 mV/dec and 36 mV/dec, respectively. The lower Tafel value of Ni-NG suggests the favorable HER occurring at Ni- NG.
Hydrogen evolution activity Ni-NG catalyst in comparison with Pt/C, (B) Image shows the production of O2 and H2 at an operating potential of 1.59 V using the freestanding spongy catalysts electrodes developed and inserted in to a commercial Ni sponge using hydraulic pressurizer, (C) Chronopotetentiometric response at 10 mAcm−2 showing the stability in performance, and (D) Chronoamperometric analysis at different operating voltages.
Water electrolysis cell setup using Ni1Co2 and Ni-NG
Recently Dai et al. reported a water electrolysis cell (1.5 V) operated with their catalyst as cathode and Ni- Fe layered double hydroxide as anode50. Here, we demonstrate the water electrolysis cell with our own catalysts working at similar potentials. A two electrode cell is developed as shown in Fig. 5B by incorporating the anode material (Ni1Co2 sponge) and cathode material (Ni-NG sponge) on a commercial Ni sponge (loading of 10 mgcm−2) by applying a pressure of 1 MPa using a hydraulic pressurizer (schematic of the same is shown in Fig. 1). The photographic image of the sponge and the electrode morphology are shown in supporting information Figure S15. The advantage of such a fluffy and spongy catalyst is the possibility of its direct incorporation into other electrodes without the aid of any external binder (use of binder will increase the resistance). The electrolysis cell shows a very high stability >10 hr at a current density of 10 mA cm−2 as shown in Fig. 5C. In order to check the current density at different potentials chronoamperometric measurements are performed and are shown in Fig. 5D. The stability of the electrodes in different working potentials is evident from these studies which ensure the commercial feasibility of this water electrolysis set up.
Conclusions
A bulk method for the development of free standing metallic sponges with the possibility of one step controllable alloying is discussed. Out of various stoichiometric combinations of Ni-Co based sponges tested, Ni1Co2 sponge showed enhanced OER activity (low over potential 1.629 V at 10 mAcm−2), long stability, low tafel slope (87.3 mV/dec), and high Faradaic efficiency, and its OER performance is comparable to precious metal oxide based benchmarked catalyst. It is further proven that Ni1Co2/oxide heterostructure is playing the key role in augmented OER process. The synthesis strategy is extended to develop graphene based HER catalyst, where the developed Ni-NG sponge’s HER performance is comparable to that of Pt/C- a well-known commercially available HER catalyst. A complete water electrolysis cell is designed with the developed catalysts and its performance is studied. The enormous stability (>10 hours) and performance (10 mAcm−2 at 1.59 V) of the developed full cell indicates the feasibility of these freestanding electrodes based cells for commercial energy production applications.
Methods
Synthesis of Different Types of Sponges
36 g of Ni(NO3)2.6H2O (Sigma-Aldrich) was added to 18 mL of EG (C2H6O2) (Sigma-Aldrich) and ultra-sonicated for 1 hour. After that the resultant mixture was poured into a cylindrical crystalline glass dish, which was pre-heated to a temperature of 300 °C for 30 minutes by using a hot plate in the ambient atmosphere. A sudden introduction of reactants in to the hot glass dish leads to the evolution of NO2 gas bubbles and subsequent production of fluffy Ni sponge. Cobalt oxide (Co3O4) sponge was prepared by the reaction of Co(NO3)2.6H2O (36 g) and EG (18 mL) by using the same procedure mentioned above for Ni sponge. The same synthesis route is followed for the preparation of Ni-Co alloy sponges. Here reactants Ni(NO3)2.6H2O and Co(NO3)2.6H2O (sigma-Aldrich), were mixed together taking a total amount of 36 g in the weight ratio of 1:1, 1:2 and 2:1 and the resulting sponges named as Ni1Co1, Ni1Co2 and Ni2Co1. For the synthesis of Ni-NG, 36 g of Ni(NO3)2.6H2O (Sigma-Aldrich) and 100 mg of NG(prepared by heating GO with melamine (1:5 ratio) for 3 hrs at 800 °C)51 were added to 18 mL of EG (C2H6O2) (Sigma-Aldrich) and ultra-sonicated for 1 hour. The resultant mixture was poured in to a cylindrical dish preheated for 1 hour leads to the formation of Ni-NG sponges.
Material Characterization
XRD of the powder samples were taken using Bruker X-ray powder diffractometer with Cu-Kα radiation. XPS analysis was done by using PHI 5000 Versa Probe ULVAC instrument and CARLZEIXX- SUPRA 55 VP was used for FESEM analysis. HRTEM images and selected area diffraction patterns (SAED) were performed using JEM 2100 field emission gun transmission electron microscope with an accelerating voltage of 200 kV. Rutherford backscattering spectra are taken by using MeV Helium ions from 1.7 MV tandetron accelerator at IGCAR, Kalpakkam, India.
Electrochemical Experiments
All the electrochemical experiments were conducted in 0.1 M KOH with a glassy carbon electrode as the working electrode, platinum auxiliary electrode, and Ag/AgCl as reference electrode in a conventional three- electrode cell. The measured potentials vs Ag/AgCl were converted to the reversible hydrogen electrode (RHE) scale according to the Nernst equation,
![](http://media.springernature.com/lw329/springer-static/image/art%3A10.1038%2Fsrep31202/MediaObjects/41598_2016_Article_BFsrep31202_Equ1_HTML.gif)
where, ERHE is the converted potential vs. RHE, EoAg/AgCl = 0.197 at 25 °C, and EAg/AgCl is the experimentally measured potential against Ag/AgCl reference.
Catalyst inks were prepared by sonication of a mixture of 4 mg catalyst powder (sponge), 50 μL nafion (5 wt% dispersion in lower aliphatic alcohol and water) and 1 mL isopropanol/water mixture. The ink was drop casted onto the readily polished glassy carbon (GC) electrode to obtain a loading of 0.28 mg cm−2. Prior to the test, all Ni-containing catalysts (sponges) were electrochemically activated (chrono-amperometry for 2 hours at 1.564 V) to enhance the electrocatalytic activity of sponges. The pre-treatment of the electrodes will help to form a stable oxide layer which in turn results in to a saturated OER current.
Additional Information
How to cite this article: Vineesh, T. V. et al. Controllably Alloyed, Low Density, Free-standing Ni-Co and Ni-Graphene Sponges for Electrocatalytic Water Splitting. Sci. Rep. 6, 31202; doi: 10.1038/srep31202 (2016).
References
Zhu, C., Du, D., Eychmuller, A. & Lin, Y. Engineering Ordered and Nonordered Porous Noble Metal Nanostructures: Synthesis, Assembly, and Their Applications in Electrochemistry. Chem. Rev. 115, 8896–8943 (2015).
Chen, S., Duan, J., Ran, J., Jaroniec, M. & Qiao, S. Z. N-doped Graphene Film-Confined Nickel Nanoparticles as a Highly Efficient Three- Dimensional Oxygen Evolution Electrocatalyst. Energy Environ. Sci. 6, 3693–3699 (2013).
Hou, Y. et al. Strongly Coupled 3D Hybrids of N-doped Porous Carbon Nanosheet/CoNi Alloy-Encapsulated Carbon Nanotubes for Enhanced Electrocatalysis. Small 11, 5940–5948 (2015).
Liu, X. et al. Adv. Funct. Mater. 25, 57999 (2015).
Bikkarolla, S. K. & Papakonstantinou, P. CuCo2O4 Nanoparticles on Nitrogenated Graphene as Highly Efficient Oxygen Evolution Catalyst. J. Power Sources 281, 243–251 (2015).
Zhao, A. et al. Spinel Mn-Co oxide in N-doped Carbon Nanotubes as a Bifunctional Electrocatalyst Synthesized by Oxidative Cutting. J. Am. Chem. Soc. 136, 7551–7554 (2014).
Arán-Ais, R. M. et al. Elemental Anisotropic Growth and Atomic-Scale Structure of Shape-Controlled Octahedral Pt–Ni–Co Alloy Nanocatalysts. Nano Lett. 15, 7473–7480 (2015).
Reier, T., Oezaslan, M. & Strasser, P. Electrocatalytic Oxygen Evolution Reaction (OER) on Ru, Ir, and Pt Catalysts: A Comparative Study of Nanoparticles and Bulk Materials. ACS Catal. 2, 1765 (2012).
Nakagawa, T., Beasley, C. A. & Murray, R. W. Efficient Electro-Oxidation of Water Near Its Reversible Potential by a Mesoporous Nanoparticle film. J. Phys. Chem. C. 113, 12958–12961 (2009).
Ding, Y., Chen, M. & Erlebacher, J. Mettallic Mesoporous Nanocomposites for Electrocatalysis. J. Am. Chem. Soc 124, 6876–6877 (2004).
Marozzi, C. A. & Chialvo. Development of Electrode Morphologies of interest in Electrocatalysis: Part 2: Hydrogen Evolution Reaction OnMacroporous Nickel Electrodes. Electrochimica Acta 45, 2111 (2000).
Chen, S. & Qiao, S. Z. Hierarchially Porous Nitrogen- Doped Graphene –NiCo2O4 Hybrid Paper as an Advanced Electrocatalytic water splitting Material. ACS Nano 7, 10190–10196 (2013).
Chang, J. K., Hsu, S. H., Sun, I. W. & Tsai, W. T. Formation of Nanoporous Nickel by Selective Anodic Etching of the Nobler Copper Component from Electrodeposited Nickel- Copper Alloys. J. Phy. Chem. C. 112, 1371–1376 (2008).
Tappan, B. C. et al. Ultralow-Density Nanostructured Metal Foams: Combustion Synthesis, Morphology and Composition. J. Am. Chem. Soc. 128, 6589–6594 (2006).
Viau, G., Ravel, F., Acher, O., Vincent, F. F. & Fievent, F. Preparation and Microwave Characterization of spherical and monodisperse Co20Ni80 particles. J. Appl. Phys 176, 6570–6572 (1994).
Zakaria, M. B. et al. Controlled Synthesis of NanoporousNickel Oxide with Two Dimenssional Shapes Through Thermal Decomposition of Metal- Cyanide Hybrid Coordination Polymers. Chem. Eur. J. 21, 3605–3612 (2015).
Sun, L., Chein, C. L. & Searson, P. C. Fabrication of Nanoporous Nickel by Electrochemical Dealloying. Chem. Mater. 16, 3125–3129 (2004).
Yang, Y., Fei, H., Ruan, G., Xiang, C. & Tour, J. M. Efficient Electrocatalytic Oxygen Evolution on Amorphous Nickel Cobalt Binary Oxide Nanoporous Layers. ACS Nano. 8, 9518–9523 (2014).
Yang, Y., Fei, H., Ruan, G. & Tour, J. M. Porous Cobalt-Based Thin Film as a Bifunctional Catalyst for Hydrogen Generation and Oxygen Generation Adv. Mater. 27, 3175–3180 (2015).
Xie, G. et al. Graphene- Based Materials for Hydrogen Generation from Light –Driven Water Splitting. Adv. Mater. 25, 3820–3839 (2013).
Kudo, A. & Miseki, Y. Heterogeneous Photocatalyst Materials for Water Splitting. Chem. Soc. Rev 38, 253–278 (2009).
Yin, Z. et al. Full Solution-Processed Synthesis of All Metal Oxide- Based Tree-like Heterostructures on Fluorine- Doped Tin Oxide for Water Splitting. Adv. Mater. 24, 5374–5378 (2012).
Fabbri, E., Habereder, A., Walter, K., Kotz, R. & Schimidt, T. J. Developments and perpectives of oxide-based catalysts for the Oxygen Evolution Reaction. Catal. Sci. Technol. 4, 3800–3821 (2014).
McCrory, C. C. L., Jung, S., Peters, J. C. & Jaramillo, T. F. Benchmarking Heterogeneous Electrocatalysts for the Oxygen Evolution Reaction. J. Am. Chem. Soc. 135, 16977–16987 (2013).
Trotochaud, L., Ranney, J. K., Williams, K. N. & Boettcher, S. W. Solution Cast Metal Oxide Thin Film Electrocatalysts fir Oxygen Evolution. J. Am. Chem. Soc. 134, 17253–17261 (2012).
Ren, J., Antonietti, M. & Fellinger, T. Water Splitting Using a Simple Ni/N/C Paper Electrocatalyst. Adv. Energy Mater. 5, 1401660–1401667 (2015).
Fominykh, K. et al. Ultrasmall Dispersible Crystalline Nickel Oxide Nanoparticles as High-Performance Catalysts for Elctrochemical Water splitting. Adv. Funct. Mater. 24, 3123–3129 (2014).
Popczun, E. J. et al. Nanostructured Nickel Phosphide as an Electrocatalyst for the Hydrogen Evolution Reaction. J. Am. Chem. Soc. 135, 9267–9270 (2013).
Huanga, Y. S., Zeng, X. T., Hub, X. F. & Liu, F. M. Corrosion Resistance Properties of Nickel Composite Coatings. Electrochimica. Acta 49, 4313–4319 (2004).
Fan, C., Piron, D. L., Sleb, A. & Paradis, P. Study of Electrodeposited Nickel- Molybdenum, Nickel-Tungsten, Cobalt-Molybdenum, and Cobalt- Tungsten as Hydrogen Electrode on Alkaline Water Electrolysis. J. ELectrochem. Soc. 141, 382–387 (1994).
Lian, K., Thorpe, S. J. & Kirk, D. W. The Electrocatalytic Activity of Amorphous and Crystalline Ni-Co alloys on the oxygen evolution reaction. Electrochimica Acta. 37, 169–175 (1992).
Wang, Y. et al. Reduced Mesoporous Co3O4 Nanowires as Efficient Water Oxidation Electrocatalyst and Supercpacitor electrodes. Adv. Energy Mater. 4, 1400696–1400702 (2014).
Yan, X., Tian, L., He, M. & Chen, X. Three- Dimensional Crystalline/Amorphous Co/Co3O4 Core/ShellNanosheets as Efficient Electrocatalysts for the Hydrogen Evolution Reaction. Nano Lett. 15, 6015–6021 (2015).
Zhou, X. et al. Hollow Fluffy Co3O4 Cages as Efficient Electroactive Materials for Supercapacitor and Oxygen Evolution Reaction. ACS Appl. Mater. Interfaces 7, 20322–20331 (2015).
Hamdani, M., Singh, R. N. & Chartier, P. Co3O4 and Co-Based Spinel Oxides Bifunctional Electrodes. Int. J. Electrochem. Sci. 5, 556–577 (2010).
Peng, Z., Jia, D., Enizi, A. M. A., Elzatahry, A. A. & Zheng, G. From Water Oxidation to Reduction: Homologous Ni-Co Based Nanowires as Complementpry Water Splitting Electrocatalysts. Adv. Energy Mater. 5, 1402031–1402038 (2015).
Liu, X. et al. Integrating NiCo Alloy with Their Oxides as Efficient Bi- functional Catalyst for Rechargeable Zinc-Air Batteries. Angew. Chem. Int. Ed. 54, 9654–9658 (2015).
Chen, S., Duan, J., Jaroniec, M. & Qiao, S. Z. Three- Dimenssional N-Doped Graphene Hydrogel/NiCo Double Hydroxide Electrocatalysts for Highly Efficient Oxygen Evolution. Angew. Chem. Int. Ed. 52, 13567–13570 (2013).
Bao, J. et al. Ultrathin Spinel-Structured Nanosheets Rich in Oxygen Deficiencies for Enhanced Electrocatalytic Water Oxidation. Angew. Chemie - Int. Ed. 54, 7399–7404 (2015).
Fan, J., Chen, Z., Shi, H. & Zhao, G. In-situ Grown, Self-Supported Iron-Cobalt-Nickel Alloy Amorphous Oxide Nanosheets with Low Overpotential toward Water Oxidation. Chem. Commun. 52, 4290–4293 (2016).
Shi, H. & Zhao, G. Water Oxidation on Spinel NiCo2O4 Nanoneedles Anode: Microstructures, Specific Surface Character, and the Enhanced Electrocatalytic Performance. J. Phys. Chem. C 118, 25939–25946 (2014).
Liu, X. et al. Metal (Ni,Co)- Metal Oxids/ Graphene nanocomposites as Multifunctional Electrocatalysts. Adv. Funct. Mater. 25, 5799–5808 (2015).
Philip, M. R., Narayanan, T. N., Praveen Kumar, M., Arya, S. B. & Pattanayak, D. K. Self-Protected Nickel-Graphene Hybrid Low Density 3D scaffolds. J. Mater. Chem. A. 2, 19488–19494 (2014).
Li, Y. D., Li, L. Q., Liao, H. W. & Wang, H. R. Preparation of Pure Nickel, Cobalt, Nickel-Cobalt and Nickel- Copper Alloys by Hydrothermal Reduction. J. Mater. Chem 9, 2675–2677 (1999).
Wei, X. W., Zhou, X. M., Wu, K. L. & Chen, Y. 3-D flower-like NiCo alloy nano/microstructures grown by a surfactant-assisted solvothermal process. Cryst. Eng. Com. 13, 1328–1332 (2011).
Sims, M. J., Rees, N. V., Dickinson, E. J. F. & Compton, R. G. Effect of Thin Layer Diffusion in the Electrochemical Detection of Nicotine on Basal Plane Pyrolytic Graphite (BPPG) electrodes modified with layers of Multi-Walled Carbon nanotubes (MWCNT-BPPG). Sensors and Actuators B. 44, 153–158 (2010).
Fei, H. et al. Atomic Cobalt on Nitrogen- Doped Graphene for Hydrogen Generation. Nat. Commun. 6, 8668–8674 (2016).
McKone, J. R., Sadtler, B. F., Werlang, C. A., Lewis, N. S. & Gray, H. B. Ni-Mo Nanopowders for Efficient Electrochemical Hydrogen Evolution. ACS Catal. 3, 166–169 (2013).
Xing, Z., Lia, Q., Wanga, D., Yanga, X. & Sun, X. Self-supported nickel nitride as an efficient high-performance three-dimensional cathode for the alkaline hydrogen evolution reaction. Electrochimica Acta 191, 841–845 (2016).
Gong, M. et al. Nanoscale Nickel Oxide/Nickel Heterostructures for Active Hydrogen Evolution Electrocatalysis. Nat. Commun. 5, 54695–54699 (2014).
Sheng, Z. et al. Catalyst Free Synthesis of Nitrogen-Doped Graphene via Thermal Annealing Graphite Oxide with Melamine and Its Excellent Electrocatalysis. ACS Nano 5, 4350–4358 (2011).
Acknowledgements
TNN and TVV acknowledge Tata Institute of Fundamental Research-Centre for Interdisciplinary Sciences (TCIS), Hyderabad for the financial support. SA acknowledges financial support through the institute start up fund (OLP 0088). Authors thank Prof. Vijayamohanan K. Pillai, Director, CSIR- CECRI for his valuable suggestions and support during the research. TVV thanks UGC for SRF. Authors thank Dr. Sundaravel and Dr. Amarendra, IGCAR, Kalpakkam, India for permitting to conduct RBS experiments in their facility.
Author information
Authors and Affiliations
Contributions
T.V.V. and T.N.N. conceived, planned and designed the work. T.N.N., T.V.V. and S.A. discussed the work. T.V.V. conducted most of the experiments. S.M. helped for the sponge synthesis and characterization. M.G.H. conducted the TEM imaging experiments. V.P. conducted the SEM and EDS studies. All the authors discussed the data and S.A., T.V.V. and T.N.N. co-wrote the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Vineesh, T., Mubarak, S., Hahm, M. et al. Controllably Alloyed, Low Density, Free-standing Ni-Co and Ni-Graphene Sponges for Electrocatalytic Water Splitting. Sci Rep 6, 31202 (2016). https://doi.org/10.1038/srep31202
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep31202
- Springer Nature Limited
This article is cited by
-
Advances in green synthesis and applications of graphene
Nano Research (2021)
-
Sulfur-doped graphene aerogels reinforced with carbon fibers as electrode materials
Journal of Materials Science (2020)
-
Transition metal ions regulated oxygen evolution reaction performance of Ni-based hydroxides hierarchical nanoarrays
Scientific Reports (2017)