Abstract
Mixed-valence manganese oxides present striking properties like the colossal magnetoresistance, metal-insulator transition (MIT) that may result from coexistence of ferromagnetic, metallic and insulating phases. Percolation of such phase coexistence in the vicinity of MIT leads to first-order transition in these manganites. However the length scales over which the electronic and magnetic phases are separated across MIT which appears compelling for bulk systems has been elusive in (La1−yPry)1−xCaxMnO3 films. Here we show the in-plane length scale over which charge and magnetism are correlated in (La0.4Pr0.6)1−xCaxMnO3 films with x = 0.33 and 0.375, across the MIT temperature. We combine electrical transport (resistance) measurements, x-ray absorption spectroscopy (XAS), x-ray magnetic circular dichroism (XMCD), and specular/off-specular x-ray resonant magnetic scattering (XRMS) measurements as a function of temperature to elucidate relationships between electronic, magnetic and morphological structure of the thin films. Using off-specular XRMS we obtained the charge-charge and charge-magnetic correlation length of these LPCMO films across the MIT. We observed different charge-magnetic correlation length for two films which increases below the MIT. The different correlation length shown by two films may be responsible for different macroscopic (transport and magnetic) properties.
Similar content being viewed by others
Introduction
Colossal magnetoresistance (CMR)1 perovskite manganites exhibit numerous phase transitions2,3,4,5,6,7,8,9, like metal–insulator transition (MIT), ferromagnetic–paramagnetic (FM–PM) and structural phase transitions. A rich variety of electronic and magnetic phases often coexist and compete with one another1,2,3,4,5,6,7,8,9 in mixed phase manganites that can be used to achieve interesting functionalities. It is well recognized that many mixed-valence manganites phase separate between the FM metallic phase and the charge-ordered (CO) insulating phases. When driven by disorder near first-order transitions, the length scale of phase-separated domains can be much less than a micron2,9,10,11,12.
Bulk (La1−yPry)1−xCaxMnO3, is a system6,11,12,13,14 exhibiting phase separation in the range of nanometers to microns for x = 0.339 and 0.37511. Recently Moshnyaga et al.15 predicted that electronic phase separation (EPS) in thin films of a (La1−yPry)1−xCaxMnO3 with x = 0.33 and y = 0.40, develops at the nanometer scale, in which adjacent FM nanodomains are antiferromagnetic (AFM) coupled. The EPS at nanometer length scale at the surface of (La0.4Pr0.6)1−xCaxMnO3, (LPCMO) film with x = 0.33 was observed using conductive atomic force microscope (cAFM)16. Further a combination of cAFM16 and transport measurements as a function of applied stress17 on LPCMO film with x = 0.33 also suggested that the growth of anisotropic electronic (metallic) domain resulting into anisotropic response of the MIT and resistance of the sample.
Recently using polarized neutron reflectivity we observed that magnetic ordering in LPCMO film with x = 0.33 was not caused by the metal-insulator transition; rather magnetic ordering first occurs at higher temperatures18. In addition the results also indicated a magnetic percolation threshold of 0.6 (assuming metallic and ferromagnetic phases are from same parts of the LPCMO film), which is consistent with two-dimensional spin lattices. However, direct evidence for coexistence of magnetic and nonmagnetic regions and their length scales has been elusive in LPCMO films.
Here we show that the in-plane length scales over which charge and magnetism are correlated in (La0.4Pr0.6)1−xCaxMnO3 films with x = 0.33 and 0.375 are different. Two single crystal (La0.4Pr0.6)1−xCaxMnO3 (LPCMO) films with x = 0.33 and 0.375, hence forth known as samples S1 and S2, respectively, were epitaxially grown on (110) NdGaO3 (NGO) substrates19,20,21. Using x-ray absorption spectroscopy (XAS), x-ray magnetic circular dichroism (XMCD), and specular/off-specular x-ray resonant magnetic scattering (XRMS)22,23,24 we quantitatively estimated charge-charge and charge-magnetic correlation length of the samples across MIT. We observed smaller in-plane charge correlation length for LPCMO film with x = 0.33 than that of film with x = 0.375, which is consistent with the length scale associated with conductivity map of the films. We also observed different charge-magnetic correlation length for two films which increases below the MIT. However both chemical and magnetic surfaces show similar fractal dimension of ~2.7 with similar atomic scale roughness ~4 Å.
Results
Transport and conductivity measurements
The electrical transport (resistance) measurements were taken using the two-probe method25 in a closed cycle helium cryostat. The temperature was varied between room temperature to 20 K with an accuracy of better than 0.1 K. Figure 1 shows resistance normalized to the 300 K resistance [R(T)/R(300 K)] from S1 and S2. We cooled and warmed our samples at a rate of 0.4 K/min. We obtained an insulator to metal (while cooling) (TIM) and metal to insulator (while warming) (TMI) transition temperatures (location of the peaks of dR/dT) of 50.7 K and 68.7 K, respectively—a difference of ΔT ~18 K for S1. Locations of TIM and TMI are shown as dashed lines in Fig. 1. However, the MIT for S2 occurred at higher temperatures (TIM = 105.6 K and TMI = 109.0 K) with a smaller thermal hysteresis ~4 K. We have grown number of samples S1 and S2 and observed similar variation of R(T) [See Supplementary Fig. S1] as shown in Fig. 1. For similar thickness of samples S1 and S2, we observed that sample S2 shows MIT at higher temperature, which is ~40 K more than that of sample S1, suggesting a composition dependent variation of macroscopic properties (resistance) with respect to temperature. Earlier macroscopic magnetization measurements on similarly grown sample S1 have suggested a Curie temperature of ~130 K19,20,21. The Curie temperature for similarly grown S2 is ~150 K [See Supplementary Fig. S2].
Temperature dependent morphology and conductance measurements on the surface of similarly grown LPCMO film with x = 0.33 (S1) were reported elsewhere16. For cAFM measurements both the samples were cooled to lowest temperature of ~45 K and then measurements were taken during the cooling and warming cycle at different temperatures. The R(T) measurements for the samples on which cAFM measurements were made are different [See Supplementary Fig. S3]. Figure 2(a,b) depict the topography with a scan area of 2 μm × 2 μm of identically grown samples S1 and S2, showing distinct morphologies of the two samples. However the atomic scale morphological parameters, roughness and roughness exponent, for two films as obtained from off-specular x-ray reflectivity (XRR), discussed latter, are similar. To compare the conductivity map we have measured the cAFM images of the surfaces of identically grown samples S1 and S2 at a temperature below the TMI, while warming the samples. Figure 2(c,d) show the cAFM images at 50 K and 85 K with scan areas of 0.4 μm × 0.4 μm and 2.8 μm × 2.8 μm of the surface of identically grown samples S1 and S2, respectively. The cAFM images show the existence of metallic and insulating phases. The maximum size of metallic domains [Fig. 2(c)] at 50 K for S1 was ~1700 Å, whereas for S2 it was ~9000 Å at 85 K [Fig. 2(d)]. We observed even larger metallic domains (~12000 Å) for S2 at 50 K (not shown here).
Hard (non-resonant) X-ray reflectivity
XRR involves measurement of the x-ray radiation reflected from a sample as a function of wave vector transfer Q (i.e., the difference between the outgoing and incoming wave vectors) [inset (i) of Fig. 3]. In case of specular reflectivity (angle of incidence, θi = angle of reflection, θf), , where λ is the x-ray wavelength] and , thus we obtain the depth dependent chemical profile of the sample26. Whereas in the case of off-specular reflectivity (θi ≠ θf), the reflectivity (as a function of Qx at fixed Qz) provides information about the correlation of structure across the sample plane26,27,28,29,30, e.g. roughness. The x-ray specular reflectivity is qualitatively related to the Fourier transform of the electron scattering length density (ESLD) depth profileρ(z) averaged over the whole sample area26,27.
The specular reflectivities were calculated using the dynamical formalism of Parratt31, and parameters of the model were adjusted to minimize the value of reduced χ2 –a weighted measure of goodness of fit32. The specular XRR data, normalized to the asymptotic value of the Fresnel reflectivity26 , from S1 (closed triangle) and S2 (closed square) are shown in Fig. 3(a) along with the best fit (solid lines). Inset (ii) represents the ESLD depth profile of these samples which best fitted the specular XRR. We obtained a thickness of 200 ± 10 and 180 ± 10 Å for LPCMO layer in S1 and S2, respectively, from specular XRR33. Different ESLD model with different χ2 for fitting specular XRR data is reported in ref. 33. We obtained chemical non uniformity at both the interfaces (air-film and film-substrate) resulting to different ESLD profiles at interfaces for both films20,21,33.
Investigation of interface morphology of thin film, using the distorted-wave Born approximation (DWBA) formalism, was developed by Sinha et al.29 which has been subsequently extended to multilayer hetrostructures34,35,36,37. We collected off-specular (diffuse) reflectivity at different angles of incidence in the scattering plane termed as detector scan35. Figure 3(b,c) show the off-specular XRR data as a function of Qx at two values of Qz, (= 0.17 Å−1 and 0.23 Å−1) from S1 and S2, respectively. We analyzed the off-specular XRR measurements from the samples under the approximation of self-affine fractal surface, where in-plane height-height correlation function C(x, y) is usually assumed29,34,35,36,37: ; where σ is the rms value of the surface roughness (correlated roughness), h is the roughness exponent, known as Hurst parameter and ξ is the in-plane correlation length of the roughness. The exponent 0 < h < 1 determines the fractal dimension (D = 3–h) of the interface (i.e., how jagged the interface is; smoother interfaces have larger values of h)29. The off-specular XRR were simulated using the formalism developed by Holý et al.34 to obtain the incoherent diffuse scattering cross-section (see Eq. (16) in ref. 34). The σ, h and ξ for each interface are the parameters of the fit to off-specular XRR data while other parameters obtained from the specular XRR (i.e. thickness and electron density) were kept fixed. We fitted off-specular reflectivity as a function of Qx at two values of Qz, with the same set of parameters (Table 1). Fits to the off-specular XRR are shown as solid line in Fig. 3(b,c). Errors reported for parameters obtained from both hard and soft (discussed later) x-ray scattering measurements represent the perturbation of a parameter that increased χ2 corresponds to a 2σ error (95% confidence)32. It is evident from the analysis of off-specular hard XRR (Table 1) that samples show drastically different charge-charge (height-height) correlation length even though they show similar atomic scale roughness (σ) and roughness exponent (h), this may be due to different composition (doping) of the films. However the contribution of height-height distribution (surface morphology) from two films which are drastically different (AFM images) can lead to different correlation length.
X-ray absorption spectroscopy and X-ray resonant scattering
The XAS and XMCD were calculated by averaging and taking the difference of the photocurrent signals from each polarization (right (I+) and left (I−) circularly polarized), (I+ + I−)/2 and (I+ − I−), respectively. The XMCD is proportional to an average near-surface magnetic moment of a few nanometers23,24. Since XRMS relies on measuring the reflected x-ray beam, it is sensitive to the magnetization depth profile of a few tens of nanometers23,24.
XAS and XMCD measurements of the Mn L edge in an applied magnetic field of 700 Oe were taken at an angle of incidence of 10° from the plane of the film’s surface. Figure 4(a,b) show the Mn L3 and L2 edge total electron yield (TEY) average absorption (I+ + I−) spectra from S1 and S2, respectively, at 150 K (dash lines) and 20 K (solid lines). Similar profiles of XAS spectra have been observed at the intermediate temperature of measurements while warming and cooling the samples. Identical shapes of XAS spectra as a function of temperature suggest that the charge state and local electronic environment of Mn atoms at the surface of both the samples remains unchanged with temperature. However small change in XAS spectra near Mn L3 edge may be resulted from additional modification in surface electronic properties as suggested by off-specular XRR measurements. Figure 4(c,d) show the XMCD spectra from S1 and S2, respectively, at 150 K (dash lines) and 20 K (solid lines). The maximum of the (negative) XMCD signal at the Mn L3 edge can be seen at ~640.5 eV, which was the energy used for the off-specular XRMS experiments discussed later. Comparing XMCD data at lowest temperature measured (20 K), in the metallic region (Fig. 1) for both the samples, we observed the magnitude of the near-surface magnetization for the S1 is nearly 5% larger than that of the S2. Figure 4(e,f) show the XRMS spectra from S1 and S2, respectively, at 150 K (dash lines) and 20 K (solid lines). XRMS spectra from two samples at low temperature are quite different suggesting different magnetization depth profiles for the samples.
The total average magnetization in the surface region is proportional to the area bounded by the XMCD spectra23,24. We estimated the temperature dependent magnetization of the samples using XMCD and XRMS spectra. Figure 4(g,h) show the variation of normalized magnetization from XMCD and XRMS spectra from S1 and S2, respectively, while field cooling. The XMCD signal from S1 decreases faster than the XRMS signal from the same sample, with decreasing temperature. Whereas the opposite behavior was observed for S2. Thus the variations of near-surface magnetism of Mn with temperature depend on the chemical compositions and on the correlations of the phases of the surfaces.
By measuring the specular reflectivity at maximum XMCD (E = 640.5 eV), hysteresis loops for the Mn moment can be obtained. Figure 5(a,b) depict the normalized element selective hysteresis loops measured at the L3 edge of Mn (maximum XMCD, 640.5 eV) from S1 and S2, respectively, at different temperatures while cooling the samples. We also measured these hysteresis curves while warming the samples. The temperature dependence of the coercive field (Hc) of S1 and S2 are shown in the Fig. 5(c,d), respectively. We found thermal hysteresis of Hc about 11 K and ~0 K for S1 and S2, respectively, which is consistent with the thermal hysteresis of resistance (~18 K and 4 K) for S1 and S2.
XRMS modeling and Off-specular X-ray resonant magnetic reflectivity
The XRMS, (I+ − I−), is the charge-magnetic interference term in the scattering amplitude and provides an alternative method for measuring the magnetic dichroism from the subsurface (within few ten of nm depth) region. In the soft x-ray regime, the longer wavelengths require calculation of the specular intensities using the magneto-optic boundary matrix formalism38,39. The charge-magnetic term in the scattering amplitude can be interpreted as interference between specularly reflected x rays from the chemical and magnetic structures.
Magnetization depth profiles were obtained from the energy-dependent XRMS using a magneto-optical matrix formalism developed by Zak et al.38 using the classical dielectric tensor. The formalism requires knowledge of the energy dependence of the refractive index, n± = 1 − (δn ± δm) + i(βn ± βm) of the charge contributions, δn and βn, and the magnetic contributions, δm and βm. The optical (δn, βn) and magneto-optic (δm, βm) constants were obtained from XAS and XMCD measurement using the Kramers-Kronig transform39,40. Figure 6(a,b) show the optical constants (δn, βn) as a function of energy obtained from XAS spectra of S1 and S2, respectively at 20 K. Similarly Fig. 6(c,d) show the magneto-optic constants (δm, βm) as a function of energy as obtained from XAS spectra of S1 and S2, respectively at 20 K. We estimated optic constants and magneto-optic constants for S1 and S2 at different temperatures. Furthermore, we used the chemical structure, i.e. the thickness and roughness parameters, obtained from the non resonant XRR measurements, to analyze the XRMS data at different temperatures. Figure 6(e,f) show the XRMS data (closed circles) at 20 K and corresponding fit (solid line) from S1 and S2, respectively. The magnetization profile near the surface (few tens of nm) which best fit the XRMS data at 20 K for S1 and S2 are shown in Fig. 6(g,h), respectively. We obtained reduced magnetizations at the surfaces of both films—a result consistent with earlier PNR measurements on similar samples20,21. The reduced magnetization at the surface was attributed to presence of chemical non uniformity in this region20,21. For a comparison we have also fitted XRMS data (dash-dot blue lines in Fig. 6(e,f)) assuming uniform magnetization profile (dash-dot blue lines in Fig. 6(g,h)), which resulted in poor fit over whole energy range. Inset of Fig. 6(e) depicts the magnified version of Fig. 6(e), illustrating the difference between fittings of XRMS data at 20 K, assuming uniform and non uniform magnetization depth profile near surface.
Diffuse magnetic scattering can arise from both the fluctuation of the magnetic domains41 and spin42, which will manifest as magnetic roughness. Since the XRMS measurements were carried out at sufficiently high magnetic fields close to saturation the fluctuation of domain can be neglected and thus off-specular XRMS data can be treated within the same DWBA framework as for the laboratory based x-ray diffuse scattering measurements43,44. The mathematical descriptions of off-specular (diffuse) XRMS, specifically in reflectivity geometry have been discussed in detail elsewhere45,46,47,48,49. It has been demonstrated theoretically and experimentally that the diffuse difference (I+ − I−) intensity (charge-magnetic scattering) results predominantly from charge-magnetic cross-correlations while the diffuse sum (I+ + I−) intensity (charge scattering) results predominantly from charge-charge correlations46,47. The experimentally measured diffuse charge scattering data as a function of Qx, at fixed Qz = 0.113 Å−1, at an energy of 640.7 eV, from S1 and S2, at different temperatures while warming is shown in the insets (i) and (ii) of Fig. 7, respectively. The diffuse charge scattering data at different temperatures remain similar suggesting that the charge-charge correlation length does not vary with temperature.
Using optic and magneto-optic constants at 640.7 eV estimated from the specular XRMS energy dependent data and other parameters (thickness, number density etc.) obtained from the hard XRR measurements, we fitted the diffuse (both charge and charge-magnetic) XRMS data at different temperatures with different morphological parameters (σ, h and ξ)43,44. The form of the correlation function for both the charge-charge and charge-magnetic fits is that for a self-affine fractal surface with a cutoff length46, i.e., and ; where ξcc and ξcm are charge-charge and charge-magnetic correlation lengths and hcc and hcm are the corresponding Hurst parameters defining the texture of chemical and magnetic roughness46. Figure 7 shows the diffuse charge scattering data from S1 (open circles) and S2 (open triangle). The corresponding solid lines in Fig. 7 were fit to diffuse charge scattering data assuming similar morphological parameters (Table 1) as obtained from the non-resonant off-specular XRR data analysis (Fig. 3).
Figure 8 shows the diffuse charge-magnetic scattering data as a function of Qx, at fixed Qz = 0.113 Å−1, at a few temperatures while warming the samples S1 (left panel) and S2 (right panel) in a field of ~700 Oe. Solid lines in Fig. 8 are fits to the diffuse scattering data at different temperatures. We obtained smaller correlated root mean square roughness ~1.5 ± 0.6 Å as compared to σc, for charge-magnetic correlated surface which did not vary with temperature. Lower panels of Fig. 8 show a comparison of diffuse charge-magnetic scattering data (symbol) and corresponding fit (solid lines) at 70 K and 50 K, with in a smaller Qx range near specular ridge, illustrating significant difference. The other morphological parameters (hcm and ξcm) obtained from these measurements are plotted as a function of temperature in Fig. 9(a,b) for S1 and S2, respectively. It is also evident from the Fig. 9 that the Hurst parameters obtained from diffuse charge-magnetic XRMS data remains invariant with temperature with average values of hcm ≈ 0.25 ± 0.05 and 0.28 ± 0.05 for S1 [Fig. 9(a)] and S2 [Fig. 9(b)], respectively, - a result again similar to that obtained from charge scattering data for S1 (hcc = 0.25 ± 0.03) and S2 (hcc = 0.20 ± 0.03). The morphological parameters at few temperatures obtained from these measurements are shown in Table 2.
Discussion
The morphological parameters (in-plane correlation length and roughness exponent) obtained from non resonant Cu Kα off-specular XRR (Fig. 3) are purely due to charge scattering with negligible magnetic contribution. We obtained similar morphological parameters from non resonant Cu Kα off-specular XRR and soft x-ray diffuse sum (I+ + I−) intensity (charge scattering) measurements (Fig. 7). We obtained an in-plane charge-charge correlation length () of ~3200 ± 400 Å and 9000 ± 800 Å for the LPCMO surface of S1 and S2, respectively, which is much larger as compared to that of the buried substrate-film interface (~500 ± 100 Å). A comparison of non resonant Cu Kα off-specular XRR data and corresponding fits assuming different for S1 and S2 are depicted in Fig. 10(a,b), respectively, suggest different values of for the two samples. In addition both LPCMO surfaces showed a fractal surface with a Hurst parameter (roughness exponent) of ~0.22 (fractal dimension D ~2.7) for charge scattering data. Thus both S1 and S2 show similar roughness as well as a fractal surface (Table 1) but the charge-charge correlation length is drastically different, suggesting the slight composition change for LPCMO may lead to different long-range strain interactions and hence the correlations.
It is evident from Fig. 9 that the in-plane length scale, over which charge and magnetism are correlated, for S1 around 100 K–120 K (above MIT), is the same as the in-plane charge-charge correlation (~3200 ± 400 Å) length scale in the insulating phase. A rapid increase of the in-plane charge-magnetic correlation length can be observed at temperature below 70 K (near TMI). We obtained higher (~3–4 times of ) for S1 at temperatures below 70 K. Larger charge-magnetic correlation length as compared to charge-charge correlation length for a Fe/Gd multilayer using diffuse XRMS data was also observed earlier46. In contrast, we obtained smaller values of (~2000–7500 Å) than the (~9000 ± 800 Å) for S2. However () increases with decreasing temperature for both the samples. In addition similar Hurst parameters obtained for S1 and S2 from the diffuse charge-magnetic scattering data (Table 2), which are similar to the Hurst parameters obtained from charge-charge scattering data. Thus, the distribution of magnetic moments possesses the same fractal dimension (D ~2.7) characteristic of the underlying chemical structure.
Further, to know the correlation of magnetic domain length scales and the length scale over which chemical and magnetic roughness are correlated, we compared the results from cAFM measurements at 50 K and diffuse XRMS data at low temperatures (~50 K and 20 K) from S1 and S2. cAFM measurements at 50 K indicate different length scales for the two samples. S1 has smaller ferromagnetic (assuming the metallic phase is ferromagnetic) domains (~1700 Å) as compared to that of S2 (~12000 Å) at 50 K. of S1 (~3200 Å) and S2 (~9000 Å) shows a similar trend and suggest that the surface roughness (or charge) are correlated to similar length scales. However, the at 50 K for S2 (~6000 Å) is smaller than that of S1 (~8000 Å). The results suggest that charge and magnetic roughness are correlated to much higher (lower) length scale in S1 (S2) as compared to the metallic domain area observed by cAFM. Similar trends were observed when we compared the metallic phase obtained from cAFM and from diffuse XRMS at temperatures lower but near to TMI for S1 (~50 K) and S2 (~85 K).
A typical metallic insulator phase map at low temperature as suggested by cAFM can be depicted in Fig. 10(c) for S1 and S2. Just below the MIT, the metallic phases in S1 are separated by smaller insulator regions as compared to S2, where we have larger metallic phase separated by large insulator regions. The different values of for S1 and S2, even though both the film showing similar σcc and hcc, may be due to doping, x, (different internal stress associated with doping) and different defects (stripes) etc., for different films. As temperature decreases below the MIT, the ferromagnetic (metallic) phases of S1 and S2 grow differently. In the case of S1, we have smaller ferromagnetic domains separated by smaller size non magnetic (insulator) phase (Fig. 10(c)) and hence the ferromagnetic domains may be correlated to larger length scale. Additionally the stripe domain in S1 may also enhance ferromagnetic correlation. Therefore the higher magnetic correlation length for S1 may also reflect in higher values of as compared to. Whereas in the case of S2, the length scales of both metallic (ferromagnetic) and insulating phases are larger (Fig. 10(c)) as compared to that of S1 and hence show < .
It is noted that the composition variation for sample S1 and S2 is very small. However the internal stress associated with this small doping may influence the large long-range strain interactions in the films and hence resulting to different morphology and correlation length, since a strain dependent morphology for interfaces is well known in thin film. We observed different length scale over which charge and magnetism are correlated across MIT of S1 and S2. Different temperature dependent charge-magnetic correlation and related length scales shown by two samples may also influence the percolation of different phases across the MIT’s of these systems. Different percolation of conducting phase while heating and cooling cycle across MIT for LPCMO film grown identically as S1 was also observed earlier by cAFM16. Therefore different charge-magnetic correlation across MIT for these systems may be one reason for observing different thermal hysteresis behavior of macroscopic (transport, magnetism) properties.
Conclusion
We measured the depth dependence of the chemical and magnetic structures as well as the in-plane charge-magnetic correlation length of the (La0.4Pr0.6)1−xCaxMnO3 (LPCMO) films of similar thickness ~20 nm, with x = 0.33 (S1) and 0.375 (S2) across the MIT. We observed higher MIT for S2, which is ~40 K higher than that of S1. The large difference in MIT for S1 and S2 with similar thickness may be arising due to change in chemical pressure11 as a result of different compositions for two samples. We observed reduced surface magnetization for both the LPCMO films compared to the film bulk. The thermal hysteresis in resistance measurements (macroscopic) of the films is correlated with the thermal hysteresis of the coercivity as measured by specular XRMS from these manganite films. Using non-resonant (Cu Kα) XRR data, we obtained in-plane charge –charge correlation length of 3200 Å and 9000 Å for S1 and S2, respectively, which were further confirmed by charge diffuse XRMS data. The temperature dependent charge diffuse XRMS data also confirmed that the in-plane charge-charge correlation lengths are independent of temperature. Using magnetic diffuse XRMS data we obtained an increase in the in-plane charge-magnetic correlation length (≥5000 Å) below the MIT’s for both samples S1 and S2. However, the charge-magnetic correlation length and charge-charge correlation length above the metal to insulator transition were the same for S1. In addition the in-plane charge-magnetic correlation length of S2 is always smaller than its in-plane charge-charge correlation length at all temperatures. Such a different correlation lengths for two films, which show similar roughness and roughness exponent, might have resulted due to different chemical pressure in the films for different doping. The variation of length scale over which the charge and magnetic phases are correlated may influence the percolation of different metallic/magnetic phases across metal insulator transitions of these systems and hence produce different thermal hysteresis of the transport and magnetic properties.
Methods
Sample Growth and characterization
Two single crystal (La0.4Pr0.6)1−xCaxMnO3 (LPCMO) films with x = 0.33 and 0.375, hence forth known as samples S1 and S2, respectively, were epitaxially grown on (110) NdGaO3 (NGO) substrates in the step-flow-growth-mode using pulsed KrF laser (248 nm) deposition (PLD). During growth, the substrate temperature was 780 °C, O2 partial pressure was 130 mTorr, laser fluence was 0.5 J/cm2, and the repetition rate of the pulsed laser was 5 Hz19. Previously, scanning transmission electron energy-loss spectroscopy (EELS) microscopy20,21 found the composition of an identically prepared film (S1) to be (La1−yPry)1−xCaxMnO3(y ~ 0.57, x ~ 0.27) averaged over the entire thickness of the sample. cAFM measurements were carried out on samples which were identically prepared as S1 and S2 and details of measurements are reported elsewhere16. The depth dependent structure and in-plane morphological parameters of the deposited films were obtained using non resonant (Cu Kα radiation, wavelength = 1.54 Å) specular and off-specular X-ray reflectometry, respectively.
Resonant X-ray scattering
To study the electronic and magnetic properties of the LPCMO samples, two complementary soft x-ray techniques were used at beamline 4-ID-C of the Advanced Photon Source (APS): XMCD and XRMS22,23,24. The XMCD technique, measured through total electron yield (TEY), probes spin-dependent absorption. The photocurrents (scattering intensity) in XMCD (XRMS) measurements for right (RCP, I+) and left (LCP, I−) circular polarizations of the incident beam were measured independently. Both measurements were taken simultaneously by switching the polarization between LCP and RCP, across the Mn L2,3 edges at a fixed incident angle of 10°. Measurements were taken over a temperature range of 20–150 K, using in-plane fields of 700 Oe to saturate the magnetic moment of the sample. The sum (I+ + I−) (x-ray absorption spectroscopy, XAS) provides information on the electronic environment of the Mn 3d electrons. While magnetic information is contained in the difference (I+ − I−) signal, which in absorption and scattering are referred to as the XMCD and the XRMS, respectively23,24. We also measured the Off-specular (diffuse) XRMS from the samples at the Mn resonant energy of 640.5 eV.
Additional Information
How to cite this article: Singh, S. et al. Composition dependence of charge and magnetic length scales in mixed valence manganite thin films. Sci. Rep. 6, 29632; doi: 10.1038/srep29632 (2016).
References
Helmolt, R., von, Wecker, J., Holzapfel, B., Schultz, L. & Samwer, K. Giant negative magnetoresistance in perovskite like La2/3Ba1/3MnOx ferromagnetic films. Phys. Rev. Lett. 71, 2331 (1993).
Dagotto, E. Nanoscale Phase Separation in Manganites (Springer-Verlag, Heidelberg, 2002).
Millis, A. J. Lattice effects in magnetoresistive manganese perovskites. Nature 392, 147 (1998).
Tokura, Y. & Nagaosa, N. Orbital physics in transition-metal oxides. Science 288, 462 (2000).
Mathur, N. D. & Littlewood, P. B. Mesoscopic texture in manganites. Physics Today 56, 25 (2003).
Ahn, K. H., Lookman, T. & Bishop, A. R. Strain-induced metal–insulator phase coexistence in perovskite manganites. Nature 428, 401 (2004).
Salamon, M. B. & Jaime, M. The physics of manganites: Structure and transport. Rev. Mod. Phys. 73, 583 (2001).
Jin, S., Tiefel, T. H., McCormack, M., Fastnacht, R. A. Ramesh, R. & Chen, L. H. Thousandfold Change in Resistivity in Magnetoresistive La-Ca-Mn-O Films. Science 264, 413 (1994).
Fath, M. et al. Spatially Inhomogeneous Metal-Insulator Transition in Doped Manganites. Science 285, 1540 (1999).
Becker, T. et al. Intrinsic Inhomogeneities in Manganite Thin Films Investigated with Scanning Tunneling Spectroscopy. Phys. Rev. Lett. 89, 237203 (2002).
Uehara, M., Mori, S., Chen, C. H. & Cheong, S.-W. Percolative phase separation underlies colossal magnetoresistance in mixed-valent manganites. Nature 399, 560 (1999).
Zhang, L., Israel, C., Biswas, A., Greene, R. L. & Lozanne, A. Direct Observation of Percolation in a Manganite Thin Film. Science 298, 805 (2002).
Ghivelder, L. & Parisi, F. Dynamic phase separation in La5∕8−yPryCa3∕8MnO3 . Phys. Rev. B 71, 184425 (2005).
Sarma, D. D. et al. Direct Observation of Large Electronic Domains with Memory Effect in Doped Manganites. Phys. Rev. Lett. 93, 097202 (2004).
Moshnyaga, V. et al. Intrinsic antiferromagnetic coupling underlies colossal magnetoresistance effect: Role of correlated polarons. Phys. Rev. B 89, 024420 (2014).
Singh, S., Fitzsimmons, M. R., Jeen, H., Biswas, A. & Hawley, M. E. Temperature dependence of nanometer-size metallic phase texture and its correlation with bulk magnetic and transport properties and defects of a (La0.4Pr0.6)0.67Ca0.33MnO3 film. Appl. Phys. Lett. 101, 022404 (2012).
Singh, S., Fitzsimmons, M. R., Jeen, H. & Biswas, A. Influence of the magnitude and direction of applied elastic stress on the transport properties of (La0.4Pr0.6)0.67Ca0.33MnO3 thin films. Appl. Phys. Lett. 104, 201602 (2014).
Singh, S., Fitzsimmons, M. R., Lookman, T., Jeen, H. & Biswas, A. Elastically controlled manipulation of the magnetic order parameter and the metal-insulator transition in a manganite thin film. Phys. Rev. B 90, 060407(R) (2014).
Jeen, H. & Biswas, A. Single domain to multidomain transition due to in-plane magnetic anisotropy in phase-separated (La0.4Pr0.6)0.67Ca0.33MnO3 thin films. Phys. Rev. B 83, 064408 (2011).
Singh, S. et al. Magnetic Nonuniformity and Thermal Hysteresis of Magnetism in a Manganite Thin Film. Phys. Rev. Lett. 108, 077207 (2012).
Singh, S. et al. Role of elastic bending stress on magnetism of a manganite thin film studied by polarized neutron Reflectometry. Phys. Rev. B 85, 214440 (2012).
C. T. Chen et al. Experimental Confirmation of the X-Ray Magnetic Circular Dichroism Sum Rules for Iron and Cobalt. Phys. Rev. Lett. 75, 152 (1995).
J. W. Freeland et al. Suppressed magnetization at the surfaces and interfaces of ferromagnetic metallic manganites. J. Phys.: Condens. Matter 19, 315210 (2007).
J. Chakhalian et al. Magnetism at the interface between ferromagnetic and superconducting oxides. Nature Phys. 2, 244 (2006).
Dhakal, T., Tosado, J. & Biswas, A. Effect of strain and electric field on the electronic soft matter in manganite thin films. Phys. Rev. B. 75, 092404 (2007).
M. R. Fitzsimmons & C. Majkrzak Modern Techniques for Characterizing Magnetic Materials (Springer, New York, Chap. 3, pp. 107–155 2005).
R. M. Richardson et al. Study of Off-Specular Neutron Reflectivity Using a Model System. J. Appl. Crystallogr. 30, 943 (1997).
Singh, S. et al. Structural and Magnetic Depth Profiling and Their Correlation in Self-Assembled Co and Fe Based Phthalocyanine Thin Films. J. Phys. Chem. C 118, 4072 (2014).
Sinha, S. K. Sirota, E. B. Garoff, S. & Stanley, H. B. X-ray and neutron scattering from rough surfaces. Phys. Rev. B 38, 2297 (1988).
Basu, J. K. & Sanyal, M. K. Ordering and growth of Langmuir–Blodgett films: X-ray scattering studies. Phys. Rep. 363, 1–84 (2002).
Parratt, L. G. Surface Studies of Solids by Total Reflection of X-Rays. Phys. Rev. 95, 359 (1954).
Press, W. H., Flannery, B. P., Teukolsky, S. A. & Vetterling, W. T. Numerical Recipes in Fortran: The Art of Scientific Computation 2nd ed. (Cambridge University Press, Cambridge, 1992).
Singh, S., Freeland, J. W., Fitzsimmons, M. R., Jeen, H. & Biswas, A. Electronic and magnetic properties of manganite thin films with different compositions and its correlation with transport properties: An X-ray resonant magnetic scattering study. J. Appl. Phys. 116, 222205 (2014).
Holý, V., Kuběna, J., Ohlídal, I., Lischka, K. & Plotz, W. X-ray reflection from rough layered systems. Phys. Rev. B 47, 15896 (1993).
Schlomka, J.-P., Tolan, M., Schwalowsky, L., Seeck, O. H., Stettner, J. & Press, W. X-ray diffraction from Si/Ge layers: Diffuse scattering in the region of total external reflection. Phys. Rev. B 51, 2311 (1995).
Pape, I., Hase, T., Tanner, B. & Wormington, M. Analysis of grazing incidence X-ray diffuse scatter from Co–Cu multilayers. Physica B 253, 278 (1998).
Pynn, R. Neutron scattering by rough surfaces at grazing incidence. Phys. Rev. B 45, 602 (1992).
Zak, J., Moog, E. R., Liu, C. & Bader, S. D. Universal approach to magneto-optics. J. Magn. Magn. Mater. 89, 107 (1990).
Kavich, J. J. et al. Nanoscale suppression of magnetization at atomically assembled manganite interfaces: XMCD and XRMS measurements. Phys. Rev. B 76, 014410 (2007).
Brück, S., Macke, S., Goering, E., Ji, X., Zhan, Q. & Krishnan, K. M. Coupling of Fe and uncompensated Mn moments in exchange-biased Fe/MnPd. Phys. Rev. B 81, 134414 (2010).
Langridge, S., Schmalian, J., Marrows, C. H. Dekadjevi, D. T. & Hickey, B. Quantification of Magnetic Domain Disorder and Correlations in Antiferromagnetically Coupled Multilayers by Neutron Reflectometry. Phys. Rev. Lett. 85, 4964 (2000).
Singh, S. & Basu, S. Separation and correlation of structural and magnetic roughness in a Ni thin film by polarized off-specular neutron reflectometry. J. Phys.: Condens. Matter 21, 055010 (2009).
Springell, R. et al. Chemical and magnetic structure of uranium/gadolinium multilayers studied by transmission electron microscopy, neutron scattering, and x-ray reflectivity. Phys. Rev. B 81, 134434 (2010).
Bergmann, A., Grabis, J., Nefedov, A., Westerholt, K. & Zabel, H. X-ray resonant magnetic scattering study of [Co2MnGe/Au]n and [Co2MnGe/V]n multilayers. J. Phys. D: Appl. Phys. 39, 842 (2006).
Haskel, D. et al. Enhanced Interfacial Magnetic Coupling of Gd/Fe Multilayers. Phys. Rev. Lett. 87, 207201 (2001).
Nelson, C. S. et al. Charge-magnetic roughness correlations in an Fe/Gd multilayer. Phys. Rev. B 60, 12234 (1999).
Lee, D. R. et al. X-ray resonant magnetic scattering from structurally and magnetically rough interfaces in multilayered systems. II. Diffuse scattering. Phys. Rev. B 68, 224410 (2003).
Osgood, III, R. M., Sinha, S. K., Freeland, J. W. Idzerda, Y. U. & Bader, S. D. J. Magn. Magn. Mater. 198–199, 698 (1999).
Freeland, J. W., Bussmann, K., Idzerda, Y. U. & Kao, C.-C. Understanding correlations between chemical and magnetic interfacial roughness. Phys. Rev. B 60, R9923 (1999).
Acknowledgements
This work was supported by the Office of Basic Energy Science (BES), U.S. Department of Energy (DOE), BES-DMS funded by the DOE’s Office of BES, the National Science Foundation (DMR 1410237) (AB). Use of the Advanced Photon Source at Argonne National Laboratories was supported by the US DOE under contract DE-AC02-06CH11357. This research partially supported by the Laboratory Directed Research and Development Program of Oak Ridge National Laboratory, managed by UT-Battelle, LLC, for the U. S. Department of Energy.
Author information
Authors and Affiliations
Contributions
S.S. and M.R.F. designed the experiment. S.S. and J.W.F. carried out x-ray resonant experiments. S.S., M.R.F. and J.W.F. analyzed the data. H.J. and A.B. grew the samples by pulsed laser deposition. S.S. and M.R.F. wrote the manuscript with contributions from all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Singh, S., Freeland, J., Fitzsimmons, M. et al. Composition dependence of charge and magnetic length scales in mixed valence manganite thin films. Sci Rep 6, 29632 (2016). https://doi.org/10.1038/srep29632
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep29632
- Springer Nature Limited