Abstract
We demonstrate a 4-f terahertz time-domain spectroscopy (THz-TDS) system using an organic crystal DSTMS as the THz emitter and a low temperature grown (LTG) InGaAs/InAlAs photoconductive antenna as the receiver. The system covers a frequency range from 0.2 up to 8 THz. The influences of the pump laser power, the probe laser power and the azimuthal angle of the DSTMS crystal on the time-domain THz amplitude are experimentally analyzed. The frequency accuracy of the system is verified by measuring two metamaterial samples and a lactose film in this THz-TDS system. The proposed combination of DSTMS emission and PC antenna detection realizes a compact and low-cost THz-TDS scheme with an ultra-broad bandwidth, which may promote the development and the applications of THz-TDS techniques.
Similar content being viewed by others
Introduction
Terahertz (THz) radiation covers a frequency range from 0.1–10 THz, which has many unique features such as low photon energy, good penetrability and excellent capability for spectral analysis1,2. These make THz technology useful in different fields, including high-speed communication, non-destructive inspection, security check, biology research, gas sensing, cancer diagnosis and so on3,4,5. Among various THz techniques, THz time-domain spectroscopy (THz-TDS) is the most frequently used, in which material characteristics are recorded as time-domain THz electrical field pulses transmitted through or reflected from an object. Compared with other far-infrared spectroscopic techniques, THz-TDS with coherent detection has tremendous advantages in terms of high sensitivity, pure polarization and direct measurement of both real and imaginary parts of the dielectric function6. As a popular spectroscopy technique, bandwidth is one of the most important parameters for THz-TDS. A broader bandwidth enables a more accurate material identification ability. For example, particular sensitive chemicals such as TNT, RDX, HMX and 2, 4-DNT all have multi-signatures beyond 4 THz. However, the broadband THz-TDS schemes with over 6 THz bandwidth are usually very expensive and difficult to operate thus hindering their practical applications. One possible and easy solution here is to develop best matched THz sources and detectors thus bringing down the cost but remaining the broadband feature. Among different types of exist THz emitters and detectors, photoconductive (PC) switching and optical rectification (OR) have been widely used to emit picosecond THz pulses and PC sampling and electro-optical (EO) sampling have been the two main THz wave coherent detection methods7,8,9,10. Recently, thanks to the development of organic crystals such as HMQ-TMS11, DAST12, DSTMS13,14 and OH115, OR emission and EO detection can give a higher center frequency performance than PC antennas when the pump laser pulse width is longer than 50 fs. For example, the frequency range of most low temperature grown (LTG) GaAs PC antenna-based THz-TDS is limited by about 5 THz and the center frequency is less than 1 THz. Though ultra-broadband THz radiation up to 20 and 30 THz were obtained from semi-insulating and LTG GaAs PC antennas respectively16,17, the pump laser pulse width needed to be less than 15 fs. On the other hand, THz pulses with a center frequency higher than 1 THz can easily be obtained in nonlinear crystals such as ZnTe and GaP, even pumped by femtosecond lasers with a duration of tens of femtoseconds. By use of ultrashort laser pulses the generation of THz radiation by OR process has been reported to reach over 41 THz18.
Besides the consideration on the center frequency and the bandwidth, in recent years, more and more potential applications require optical-fiber-friendly THz-TDS systems pumped at 1550 nm, where LTG InGaAs/InAlAs based PC antennas and organic crystals such as DAST, DSTMS are used as promising THz sources19,20,21 and receivers22,23. The band coverage of LTG InGaAs/InAlAs based PC antennas can reach up to 5 THz but the center frequency is mainly less than 0.8 THz24,25,26. In contrast, the center frequency and the bandwidth of DSTMS emitters and detectors are much better. DSTMS has good velocity match at a wide range of wavelengths (from 720–1650 nm)19,27,28,29. When pumped with IR radiation between 1.3 and 1.5 μm, the radiated THz wave can fill the entire THz gap and the center frequency is up to 2 THz30. However, the PC antenna is much easier to integrate with the fiber technique, especially at the detection side, where as the optics of EO sampling is nearly impossible to be directly coupled with a fiber. Thus to realize an optical fiber coupled THz-TDS with a broad bandwidth and a high center frequency, a combination of DSTMS OR emission and LTG InGaAs/InAlAs PC sampling is strongly suggested. So far, this combination is still lack of experimental verification.
In this letter, we demonstrate a typical free-space 4 f THz-TDS system with a DSTMS crystal as the emitter and a LTG InGaAs/InAlAs PC antenna as the detector, which has a frequency coverage up to 8 THz with a center frequency at 1.44 THz. To verify the frequency accuracy of the proposed system, two different metamaterial samples: U-shape split-ring resonators (SRRs) and rectangle hole arrays, as well as a lactose film are tested in the system. The proposed DSTMS along with PC antenna scheme not only realizes a compact and low-cost ultra-broadband THz-TDS, but also inherits the fiber coupling capability of the PC antenna. The demonstrated system here may pave a new way for the development of ultra-broadband THz systems, thus promoting the applications of THz-TDS techniques in security check, drug prevention and medical research.
Experimental setup
Since the first discovery of DAST, it has been used as a broadband and high-energy THz source. The organic crystal DSTMS is derived from DAST but has a lower absorption around 1 THz and a faster crystal growth rate13,31,32. What’s more, DSTMS has the best performances when pumped in the IR regime. For example, DSTMS has a nonlinear coefficient as high as when pumped with IR radiation between 1.3 and 1.5 μm, as well as a good phase match. Therefore, DSTMS has become a favored potential emitter for assembling all fiber THz-TDS system and has been widely studied. In this work, a commercial DSTMS crystal from Rainbow Photonics is utilized as the THz emitter, which has a total area of 4 × 5 mm2 with a thickness of 0.3 mm. Although DSTMS has been utilized as detector in several previous works, its giant birefringence and EO sampling based detection optics hinder its utilization as a fiber-coupled THz receiver. Thus the detection of THz pulses in this work was accomplished by a commercial LTG InGaAs/InAlAs PC antenna (TERA15-DP25) from Menlo Systems GmbH. This is a typical H-type dipole antenna, which has a 4 × 4 mm2 total area and a 0.35 mm thickness with a 25 μm long dipole arm and a 10 μm wide PC gap. Compared with bare LTG InGaAs grown lattice-matched to InP substrate, beryllium-doped LTG InGaAs/InAlAs has a higher resistivity up to 106 Ω/sq, a suppressed dark conductivity and a reduced relaxation time33,34. A 4.5 THz response bandwidth and a 60 dB dynamic range are specified by the manufacturer.
The schematic of the DSTMS emission and LTG InGaAs/InAlAs PC antenna detection based THz-TDS system is shown in Fig. 1. The source is a 100 fs fiber amplifier (TOPTICA, FemtoFiber Pro NIR) operating at 1560 nm with an 80 MHz repetition rate. The output is split into two beams by using a beam splitter consisting of a λ/2 wave plate and a cubic polarizer and the powers in each beam can be tuned by rotating the wave plate. One beam is used to pump the DSTMS crystal and the other one with an average power of 25 mW is used as the probe beam of the PC antenna. In front of the emitter there is a lens with a 50 mm focal length to adjust the beam size. The pump power measured in front of the crystal is 172.9 mW, which is the net average power used to pump the DSTMS crystal. The THz wave emitted from the DSTMS crystal is collimated and re-focused by two parabolic mirrors with a 50.8 mm effective focal length. A high-resistivity silicon wafer with a thickness of 500 μm is placed in the middle of the parabolic mirrors to block part of the residual pump beam. For concentrating the THz wave and shrinking the light spot and at the same time, improving the signal to noise ratio (SNR), the crystal and the antenna are positioned at the respective foci of the parabolic mirrors. The probe beam with a power of 25 mW is focused onto the front side of the antenna by a lens with a focal length of 100 mm. Such an experimental scheme excludes the influences from the InP substrate and the silicon hyper-semispherical lens. The probe beam and THz spot overlap at the gap of the PC antenna and the THz signal is sampled by the photocurrent versus time delay. The amplitude and phase spectra are obtained by Fourier Transform of the temporal waveform of the detected THz pulses. The scanning time window of the waveform is set to 14 ps for cutting off the Fresnel reflection echo of the antenna substrate.
Results and Discussion
Figure 2(a) shows the THz signals in the time domain measured under conditions of different humidity. A humidity of 44% causes a decrease in the THz amplitude and strong oscillations after the main peak. As the humidity is reduced to 3.6%, this disorder decreases and the peak amplitude of the THz pulse increases by 42.6%. Figure 2(b) shows the frequency spectra and the power spectrum calculated by Fourier transform, which shows an unexpected frequency coverage up to 8 THz and 4.4 THz (full width at 1/10 of maximum) bandwidth with a center frequency at 1.44 THz. The dynamic range obtained from the power spectrum in Fig. 2(b) is larger than 50 dB. This ultra-broad bandwidth, as far as we know, is far beyond the usually reported frequency range of 5 THz observed in InGaAs/InAlAs PC antenna. In the spectra, there are obvious absorption peaks around 1.15, 1.31, 1.42, 1.69, 1.81 THz due to ambient water vapor, which agrees with the values reported in other references35,36. There are two spectral valleys centered at 0.61 and 0.98 THz even in a dry-air environment. This is mainly caused by the characteristic absorption in the DSTMS crystal13,37, which is responsible for the time-domain oscillations following the main peak of the signal. However, in the spectrum there is a relatively broad dip around 2.6 THz that needs subsequent investigation in the future work to clarify its origin.
Though usually water vapor absorption lines are used to test the spectral accuracy of a THz-TDS, water vapor absorption under large humidity can not be clearly recognized at high frequencies due to the too weak THz spectral amplitude. So to verify the high frequency accuracy of this system, two metamaterial samples with a few designed frequency resonances were fabricated. One is a U-shape SRR array with typical LC and high-order plasmonic resonances. The other is a rectangular hole array with surface plasmonic polarization (SPP) resonance. These two 10 × 10 cm2-sized aluminum patterns were thermally evaporated on a 500-μm-thick semi-insulating silicon substrate. The unit cells of the SRR and the hole array structures with their geometrical parameters are shown in Fig. 3(a). In the experiment, the samples are placed midway between the two parabolic mirrors to ensure a nearly plane wave incidence. A piece of the blank silicon wafer, which is the same as the sample substrate, is used as the reference. The THz pulses propagate through the metamaterial samples at normal incidence with the same polarization of the electric field as the one in Fig. 3(a). The amplitude transmission t(ω) is defined as , where and are the Fourier amplitudes of the transmitted THz fields through the sample and reference, respectively. In Fig. 4(a) the red line is the result measured with this system while the black line is obtained by a commercial FTIR system. The FTIR system, which has essentially different THz emission and detection mechanisms but covers nearly the whole THz band can objectively verify the spectral accuracy of our THz-TDS system. As shown in Fig. 4(a) there are three resonances at 0.74, 2.13 and 3.41 THz corresponding to three modes of the SRR sample: the LC, the second-order and the third-order SPP resonances38. These resonances coincide with the results from the FTIR measurement by employing a commercial THz polarizer, considering the 0.06 THz frequency accuracy of the FTIR apparatus. Figure 4(b) shows the measured frequency-dependent amplitude transmission of the hole array sample. The resonance at 5.53 THz is primarily attributed to the resonant excitation of the SPP mode at the metal–dielectric interface. The measured result is also verified by the FTIR measurement. Besides the artificial metamaterials, pure lactose film on the semi-insulating silicon wafer was also measured in our system. The well-known absorption peaks of lactose at 0.54, 1.36, 1.82, 2.56, 2.89, 3.24, 3.91 and 4.25 THz are clearly observed as shown in Fig. 4(c), which coincides with the reported results in Refs [39,40]. It demonstrates that the DSTMS emission plus PC antenna detection scheme proposed here has an accurate frequency response and the frequency coverage up to 8 THz is experimentally reliable.
As mentioned above, the pump laser in our THz-TDS is a fiber femtosecond amplifier with small volume, low cost and fiber-coupling capability. But for feasible devices in realistic applications, a small pump power and low nonlinear effects in the fiber are of the same importance as the fiber integration capability. To investigate the pump power dependence of this system, we changed the power of the pump beam by two neutral density filters and measured the amplitude of the THz time-domain pulses, while the power of the probe beam remained at 25 mW. As shown in Fig. 5(a) the amplitude linearly increases by 8 times as the pump power rises from 20–180 mW, which is verified by linear fitting. The results are entirely in accordance with the second-order nonlinear feature of the OR process. Besides the pump power on the crystal, the obtained amplitude of the THz signal also changes when the DSTMS crystal is rotated along its normal, which originates from the polarization dependence of OR emission and antenna detection. Based on these two factors, we fit the azimuthal angle dependence of our system, as shown in Fig. 5(b), where the azimuthal angle θ was defined as the angle between the b-axis of the crystal (The pump beam incidents along the c-axis of the crystal onto its ab surface) and the polarization of the pump beam (the same direction with the dipole of the antenna). As we can see in Fig. 5(b), the fit is in good accordance with the experimental result. Two maximum amplitudes were obtained when the a-axis of the crystal is parallel to the polarization of the pump beam. Besides the pump power and the azimuthal angle dependences, the power of the probe beam also strongly influences the whole response of the THz-TDS system by determining the detection efficiency, which is investigated by changing the power of the probe beam from 5 mW to 35 mW (the breakdown limitation power) while keeping the pump power at 177 mW. Figure 5(c) demonstrates that the amplitude increases linearly as the probe power is raised from 5 mW to 20 mW. But after that, the amplitude turns to saturation when the probe beam power continues to rise41,42,43.
Even though in this work the PC antenna was still sampled by free space optics, its fiber coupling capability has been demonstrated by previous works33,34. The DSTMS emission plus PC antenna detection scheme proposed here has a promising future in developing compact ultra-broadband THz-TDS systems, which is urgently needed in many important areas. Firstly, both DSTMS and LTG InGaAs/InAlAs PC antenna have very good performances around 1550 nm, where pumping lasers, propagation devices and modulation components are relatively compact, flexible, low-costly and fiber-technique integratable, making the scheme much easier to be accepted by the society33,34. Secondly, the frequency coverage up to 8 THz is broader than most THz-TDS systems commercially available today, which means our proposal has a higher spectral signature identification capability. However, before the realistic application of this scheme, the remaining issues such as the echo from the substrate, the absorption of the InP substrate, the SNR of the whole system and the reason of the fine structures in the spectrum need more through studies.
Conclusion
We presents a new scheme to generate and detect broadband THz wave. The proposed THz-TDS with a DSTMS crystal as the source and an LTG InGaAs/InAlAs PC antenna as the detector shows a frequency response up to 8 THz with a central frequency of 1.44 THz. The transmission of two metamaterial samples with different structures measured in this system coincides with the results measured by FTIR. And the absorption signatures of lactose tested in this system are in good accordance with the previously reported results. The performance dependence on the pump power, the azimuthal angle of the crystal and the probe excitation power is experimentally analyzed. This demonstration paves a way to realize a compact, low-cost and fiber technology friendly THz-TDS with a much broader frequency range in future.
Additional Information
How to cite this article: Zhang, Y. et al. A Broadband THz-TDS System Based on DSTMS Emitter and LTG InGaAs/InAlAs Photoconductive Antenna Detector. Sci. Rep. 6, 26949; doi: 10.1038/srep26949 (2016).
References
Federici, J. F. et al. THz imaging and sensing for security applications—explosives, weapons and drugs. Semicond. Sci. Technol. 20, S266 (2005).
Ferguson, B. & Zhang, X. C. Materials for terahertz science and technology. Nat.Mater. 1, 26–33 (2002).
Schmuttenmaer, C. A. Exploring dynamics in the far-infrared with terahertz spectroscopy. Chem.Rev. 104, 1759–1780 (2004).
Dragoman, D. & Dragoman, M. Terahertz fields and applications. Prog. Quantum Electron 28, 1–66 (2004).
Hangyo, M., Tani, M. & Nagashima, T. Terahertz time-domain Spectroscopy of solids: A review. Int. J. infrared and millimeter waves 26, 1661–1690 (2006).
Nuss, M. C. & Orenstein, J. Terahertz time-domain spectroscopy. Top. Curr. Chem. 74, 7–50 (1998).
Katzenellenbogen, N. & Grischkowsky, D. Efficient generation of 380 fs pulses of THz radiation by ultrafast laser pulse excitation of a biased metal‐semiconductor interface. Appl. Phys. Lett. 58, 222–224 (1991).
Zhao, G. et al. Design and performance of a THz emission and detection setup based on a semi-insulating GaAs emitter. Rev. Sci.Instrum. 73, 1715–1719 (2002).
Wu, Q. & Zhang, X. C. Free-space electro-optics sampling of mid-infrared pulses. Appl. Phys. Lett. 71, 1285–1286 (1997).
Jeong, J. H. et al. High-power broadband organic THz generator. Sci. Rep. 3, 1–8 (2013)
Tomasino, A. et al. Wideband THz time domain spectroscopy based on optical rectification and electro-optic sampling. Sci. Rep. 3, 1–8 (2013).
Schneider, A. et al. Generation of terahertz pulses through optical rectification in organic DAST crystals: theory and experiment. J. Opt. Soc. Am. B 23, 1822–1835 (2006).
Mutter, L. et al. Linear and nonlinear optical properties of the organic crystal DSTMS. J. Opt. Soc. Am. B 24, 2556–2561 (2007).
Somma, C. et al. Ultra-broadband terahertz pulses generated in the organic crystal DSTMS. Opt. Lett. 40, 3404–3407 (2015).
Brunner, F. D. et al. A hydrogen-bonded organic nonlinear optical crystal for high-efficiency terahertz generation and detection. Opt. Express 16, 16496–16508 (2008).
Shen, Y. C., Upadhya, P. C., Linfield, E. H. & Beere, H. E. Ultrabroadband terahertz radiation from low-temperature-grown GaAs photoconductive emitters. Appl. Phys. Lett. 83, 3117–3119 (2003).
Hale, P. J. et al. 20 THz broadband generation using semi-insulating GaAs interdigitated photoconductive antennas. Opt.Express 22, 26358–26364 (2014).
Huber, R., Brodschelm, A., Tauser, F. & Leitenstorfer, A. Generation and field-resolved detection of femtosecond electromagnetic pulses tunable up to 41 THz. Appl. Phys. Lett. 76, 3191–3193 (2000).
Schneider, A., Stillhart, M. & Günter, P. High efficiency generation and detection of terahertz pulses using laser pulses at telecommunication wavelengths. Opt. Express 14, 5376–5384 (2006).
Zhang, X. C. et al. Terahertz optical rectification from a nonlinear organic crystal. Appl. Phys. Lett. 61, 3080–3082 (1992)
Vicario, C. et al. Generation of 0.9-mJ THz pulses in DSTMS pumped by a Cr: Mg2SiO4 laser. Opt. Lett. 39, 6632–6635 (2014).
Martin, M., Mangeney, J., Crozat, P. & Mounaix, P. Optical phase detection in a 4-N,N-dimethylamino-4′-N′-methyl-stilbazolium tosylate crystal for terahertz time domain spectroscopy system at 1.55 μm wavelength. Appl. Phys. Lett. 97, 111112 (2010).
Han, P. Y., Tani, M., Pan, F. & Zhang, X. C. Use of the organic crystal DAST for terahertz beam applications. Opt. Lett. 25, 675–677 (2000).
Preu, S. et al. 1550 nm ErAs : In(Al)GaAs large area photoconductive emitters. Appl. Phys. Lett. 101, 101105 (2012).
Mittendorff, M. et al. Large area photoconductive terahertz emitter for 1.55 μm excitation based on an InGaAs heterostructure. Nanotechnology 24, 214007 (2013).
Kostakis, I., Saeedkia, D. & Missous, M. Terahertz generation and detection using low temperature grown InGaAs-InAlAs photoconductive antennas at 1.55 μm pulse excitation. IEEE Transactions on Terahertz Sci. Technol. 2, 617–622 (2012).
Monoszlai, B., Vicario, C., Jazbinsek, M. & Hauri, C. P. High-energy terahertz pulses from organic crystals: DAST and DSTMS pumped at Ti: sapphire wavelength. Opt. Lett. 38, 5106–5109 (2013).
Vicario, C., Monoszlai, B. & Hauri, C. P. GV/m single-cycle terahertz fields from a laser-driven large-size partitioned organic crystal. Phys. Rev. Lett. 112, 213901 (2014).
Liu, P. et al. Widely tunable and monochromatic terahertz difference frequency generation with organic crystal DSTMS. Europhys. Lett. 106, 60001 (2014).
Jazbinsek, M., Ruiz, B., Medrano, C. & Günter, P. Broadband THz-Wave Generation with Organic Crystals OH1 and DSTMS. Conference on Lasers and Electro-Optics Europe and International Quantum Electronics Conference: Lasers and Electro-Optics Europe (CLEO EUROPE/IQEC), Munich. Place of publication: IEEE. (doi: 10.1109/CLEOE-IQEC.2013.6800806) (2013, May 12–16) (2013).
Vicario, C. et al. High efficiency THz generation in DSTMS, DAST and OH1 pumped by Cr : forsterite laser. Opt. Express 23, 4573–4580 (2015).
Yang, Z. et al. Large-size bulk and thin-film stilbazolium-salt single crystals for nonlinear optics and THz generation. Adv. Funct. Mater. 17, 2018–2023 (2007).
Roehle, H. et al. Next generation 1.5 μm terahertz antennas: mesa-structuring of InGaAs/InAlAs photoconductive layers. Opt. Express 18, 2296–2301 (2010).
Sartorius, B. et al. All-fiber terahertz time-domain spectrometer operating at 1.5 μm telecom wavelengths. Opt. Express 16, 9565–9570 (2008).
Yang, Y., Shutler, A. & Grischkowsky, D. Measurement of the transmission of the atmosphere from 0.2 to 2 THz. Opt. Express 19, 8830–8838 (2011).
Exter, M. V., Fattinger, C. & Grischkowsky, D. Terahertz time-domain spectroscopy of water vapor. Opt. Lett. 14, 1128–1130 (1989).
Vicario, C., Ruchert, C. & Hauri, C. P. Intense THz radiation produced in organic salt crystals for high-field applications. SPIE LASE:Int. Soc. Opt. Phot. 8604, 86040C-1–86040C-11 (2013).
Rockstuhl, C. et al. On the reinterpretation of resonances in split- ring resonators at normal incidence. Opt. Express 14, 8827–8836 (2006).
McIntosh, A. I. et al. Crystallization of amorphous lactose at high humidity studied by terahertz time domain spectroscopy. Chem. Phys. Lett. 558, 104–108 (2013).
Hoshina, H., Sasaki, Y., Hayashi, A., Otani, C. & Kawase, K. Non-invasive mail inspection system with terahertz radiation. Appl. Spectrosc. 63, 81–86 (2009).
Yano, R. et al. Terahertz wave detection performance of photoconductive antennas: Role of antenna structure and gate pulse intensity. J. Appl. Phys. 97, 103103 (2005).
Estacio, E. S. et al. Saturation and Polarization Characteristics of 1.56 μm Optical Probe Pulses in a LTG-GaAs Photoconductive Antenna Terahertz Detector. J Infrared Milli. Terahz. Waves. 34, 423–430 (2013).
Suzuki, M. & Tonouchi, M. Fe-implanted InGaAs photoconductive terahertz detectors triggered by 1.56 μm femtosecond optical pulses. Appl. Phys. Lett. 86, 163504 (2005).
Acknowledgements
We acknowledge Professor Z.W. Zhang at Capital Normal University for his help in the FTIR measurements. This work was supported by the National Key Basic Research Special Foundation of China (2014CB339800), the Cooperative Innovation Center of Terahertz Science, the U.S. National Science foundation (ECCS-1232081), the Specialized Research Fund for the Doctoral Program of Higher Education, the National Science Foundation of China(61575141, 61138001, 61422509, 61427814 and 61420106006), the Program for Changjiang Scholars and Innovative Research Team in University, ‘PCSIRT’ (IRT13033) and the Major National Development Project of Scientific Instruments and Equipment of China (2011YQ150021).
Author information
Authors and Affiliations
Contributions
Y.Z. and X.Z. set up the experimental system, Y.Z. fabricated the metamaterial samples, S.L. fabricated the lactose film, Y.Z. and J.G. measured all the samples, Y.Z., J.G., Y.L., Z.T. and C.O. analyzed the data, M.H., J.H. and W.Z. supervised the theory and the measurements. All the authors contributed to the writing and revision of the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Zhang, Y., Zhang, X., Li, S. et al. A Broadband THz-TDS System Based on DSTMS Emitter and LTG InGaAs/InAlAs Photoconductive Antenna Detector. Sci Rep 6, 26949 (2016). https://doi.org/10.1038/srep26949
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep26949
- Springer Nature Limited
This article is cited by
-
Metacaspase MC1 enhances aluminum-induced programmed cell death of root tip cells in Peanut
Plant and Soil (2020)
-
Analytical framework of small-gap photoconductive dipole antenna using equivalent circuit model
Optical and Quantum Electronics (2017)