Abstract
CuI is a p-type transparent conductive semiconductor with unique optoelectronic properties, including wide band gap (3.1 eV), high hole mobility (>40 cm2 V−1 s−1 in bulk) and large room-temperature exciton binding energy (62 meV). The difficulty in epitaxy of CuI is the main obstacle for its application in advanced solid-state electronic devices. Herein, room-temperature heteroepitaxial growth of CuI on various substrates with well-defined in-plane epitaxial relations is realized by reactive sputtering technique. In such heteroepitaxial growth the formation of rotation domains is observed and hereby systematically investigated in accordance with existing theoretical study of domain-epitaxy. The controllable epitaxy of CuI thin films allows for the combination of p-type CuI with suitable n-type semiconductors with the purpose to fabricate epitaxial thin film heterojunctions. Such heterostructures have superior properties to structures without or with weakly ordered in-plane orientation. The obtained epitaxial thin film heterojunction of p-CuI(111)/n-ZnO(00.1) exhibits a high rectification up to 2 × 109 (±2 V), a 100-fold improvement compared to diodes with disordered interfaces. Also a low saturation current density down to 5 × 10−9 Acm−2 is formed. These results prove the great potential of epitaxial CuI as a promising p-type optoelectronic material.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Over the last decades transparent conducting materials (TCMs) had a dramatic increase in interest in the field of optoelectronics. Fully-transparent devices gave rise to a novel concept of transparent electronics1. To realize advanced active devices, it is necessary to have materials that can be electron- and hole-conducting. Except for the group-III nitrides2, however, most TCMs are unipolar n-type semiconductors such as ZnO3, GaInZnO4. Thus bipolar devices will largely depend on heterostructures from n-type and p-type materials. Therefore, it is of great importance to explore new p-type TCMs with superior optical and electrical characteristics which are compatible to the commonly used n-type TCMs.
Copper iodide in the zincblende ground-state phase (γ-CuI) has p-type conductivity with a high Hall mobility (>40 cm2 V−1 s−1 in bulk)5,6, a wide band gap (3.1 eV) with a direct band structure and a large exciton binding energy (62 meV)6. These advantageous properties make it one of the most promising p-type TCMs. Actually, it is historically the first TCM found by Bädeker as early as 19077,8. CuI has been successfully applied in scintillators9, organic electronics10,11 and bipolar diodes12,13,14. The development of high quality bipolar diodes opens up the application of CuI in transparent electronics.
Polycrystalline heterojunctions of p-type CuI are reported combining with various n-type semiconductors, such as n-Si, n-TiO2 and n-ZnO. So far, the highest rectification of diodes involving CuI as p-side is obtained for p-CuI/n-ZnO heterojunctions. In refs 14,15, CuI thin films were obtained from vapor iodization of copper films or from thermal evaporation of CuI powders, exhibiting an already fairly high rectification (current on/off-ratio) of about 4 × 107 (±2 V). However, the device performance was dominantly limited by the poor crystallinity of CuI.
In the fabrication of advanced solid-state electronic and photonic devices, epitaxial growth and the control, reduction and possibly avoidance of defects in thin film heterostructures are usually the key considerations. From this point of view, epitaxy of γ-CuI and combination with suitable n-type semiconductors is a critical issue.
Up to date, it is still a challenge to grow epitaxial thin films of γ-CuI due to the lack of lattice-matched substrates. Rather than for semiconductors, only for single-crystalline Cu(111) or NaCl(001) substrates heteroepitaxy of γ-CuI was reported16,17. A study in thermal evaporation of γ-CuI on ZnO epilayer revealed the possible existence of epitaxial crystallites within the polycrystalline CuI matrix15, indicating the opportunity of epitaxial growth of γ-CuI at appropriate growth conditions. However, thermal evaporation is not a very advantageous method for epitaxial growth due to the uncontrollable and high deposition rate which is commonly over 1 nm/s. Advanced thin film growth techniques, such as sputtering, molecular beam epitaxy (MBE), metal-organic vapor phase epitaxy (MOVPE) or pulsed laser deposition (PLD), seem more suitable for well-controlled epitaxy of CuI.
In the presence of lattice mismatch, domain epitaxy allows for a variety of advanced matching conditions18. The minimum energy lattice-matching condition involves rotation of the epilayer crystal lattices. In heteroepitaxy, rotation domains are a fundamental consequence of the mismatch of rotational symmetry across the heterointerface. The unified theory of formation of rotation domains was described elsewhere19,20. With the guidance of this theory, we systematically investigate the epitaxy of γ-CuI thin films fabricated by reactive sputtering at room temperature on various substrates with the purpose to achieve epitaxy with a well-defined in-plane epitaxial relation. We generally expect such heterostructures to have superior properties to structures without or with weakly ordered in-plane orientation2,7. Here we report such advanced epitaxial thin film heterojunctions of p-CuI(111)/n-ZnO(00.1) with a high rectification of 2 × 109 (±2 V) of the diodes.
Results and Discussion
Epitaxy
Figure 1 shows X-ray diffraction (XRD) 2θ-ω-scans of CuI thin films grown on NaCl and sapphire single-crystal substrates with different crystal orientations and glass. All XRD patterns exhibit peaks corresponding to the (111), (222), (333) and (444) planes of CuI in zincblende structure, suggesting the growth of γ-CuI along the [111]-direction on all substrates. This result agrees with the reported growth nature of γ-CuI21. The additional XRD peaks that are seen in the patterns can be assigned to the single-crystal substrates.
X-ray diffraction (XRD) 2θ-ω-scans of CuI thin films grown on the indicated NaCl and sapphire single-crystal substrates and glass.
Dashed lines are guide to the eyes corresponding to the partly weak diffraction peaks of the CuI thin films. The additional peaks in the patterns can be assigned to the corresponding substrate materials including Kβ and Lα spectral lines.
The structural properties of selected substrates and bulk γ-CuI are compiled in Table 1. It is obvious that large lattice mismatch (along a-axis) exists for most substrates, which tends to induce a significant density of dislocations in the γ-CuI epilayer and thereby hinder the conventional epitaxial growth. In this case, domain epitaxy is favored for unconventional in-plane lattice matching. Rotation domains occur, when the rotational symmetry of the substrate surface and epilayer are different. The substrate surface and epilayer rotational symmetries are denoted as Cn and Cm, respectively. The minimum number of rotation domains NRD is given by19
![](http://media.springernature.com/lw189/springer-static/image/art%3A10.1038%2Fsrep21937/MediaObjects/41598_2016_Article_BFsrep21937_Equ1_HTML.gif)
where lcm denotes the least common multiple. In this work, the as-deposited γ-CuI thin films exhibit (111)-orientation along the surface normal for all substrates, thus setting the 3-fold symmetry (m = 3) of the epilayer. Therefore, the predicted NRD depends fundamentally on the Cn symmetry of the substrate.
The rotational symmetries of the substrates used in this study are n = 2, 3, 4 and 6, namely for a-sapphire [Al2O3()], NaCl(111), NaCl(001), c-sapphire [Al2O3(0001)], respectively. The azimuthal (in-plane) orientation of the γ-CuI epilayers with respect to the substrate was characterized by XRD ϕ-scans around the surface normal. As shown in Fig. 2, well-defined CuI(022) peaks periodically appear for all these samples, demonstrating the successful heteroepitaxial growth of γ-CuI on selected single-crystals. For each single-crystal substrate, the number of diffraction peaks observed in ϕ-scan corresponds well to its symmetry. For example, the ϕ-scan of (222) plane of the NaCl(001) substrate (n = 4) shows four peaks with a separation of 90° due to the 4-fold rotational symmetry of rocksalt in (001) direction. Considering the 3-fold rotational symmetry of the (111)-oriented CuI epilayer, a single domain exhibits three peaks with ϕ-scan for the asymmetric (022) peak. However, there are twelve peaks observed by ϕ-scan of CuI(022), indicating four rotation domains (NRD = 4) rotated by 30° (or 90°) against each other. Differently, for other CuI films on substrates of Al2O3(
) (n = 2), NaCl(111) (n = 3) and Al2O3(0001) (n = 6), six CuI(022) peaks in ϕ-scans indicate the presence of two rotation domains (NRD = 2) with relative azimuthal orientation of 60°. This result agrees with the minimum number of rotation domains NRD deduced by Eq. 1. We note that on NaCl(111) (n = 3), the NRD has a theoretical minimum value of one but an experimental value of two. It is owing to the formation of mirror twinned CuI(111) domains. This phenomenon is similar to the growth of TiN(111) on Si(111), where fully twinned material was obtained22.
According to the angular peak positions in XRD ϕ-scans, as depicted schematically in Fig. 3(a), the heteroepitaxial relationships can be deduced as CuI[](111) || Al2O3[0001](
), CuI<
>(111) || NaCl[
](111), CuI<
>(111) || NaCl[110](001) and CuI<
>(111) || Al2O3[
](0001). The formation of these different rotation domains can be explained using atomic configurations as sketched in Fig. 3(b). The material combinations for γ-CuI epilayer on selected substrates in all conditions of rotational symmetry are summarized in Table 2.
These results show that our sputter deposition from metallic Cu target in ioidine/argon atmosphere is suitable for achieving epitaxial layers. Also we further corroborate previous theoretical studies on rotation domains19,20. It reveals the typical conditions in heteroepitaxy of CuI thin film on various substrates, paving the way to fabricate epitaxial multilayers for advanced heterojunctions. For a functional heterostructure we investigate in the following epitaxy on ZnO which serves as n-type contact in a bipolar diode.
Figure 4(a) shows the XRD 2θ-ω patterns of CuI/ZnO multilayers on a-sapphire and (amorphous) glass substrates, respectively. The PLD of such ZnO epilayer on sapphire has been described previously and exhibits c-plane orientation, i.e. the out-of-plane epitaxial relation ZnO[0001] || Al2O3[]23. On both ZnO(0001) and glass the CuI exhibits (111) orientation. As shown in Fig. 4(b), the full width at half maximum (FWHM) of CuI(111) rocking curve is significantly smaller on ZnO than on glass.
(a) XRD 2θ-ω-scans of CuI/ZnO/a-sapphire and CuI/glass, (b) XRD ω-scans of CuI(111) on ZnO/a-sapphire and glass, respectively and (c) lattice constant a of CuI grown on glass determined from a cos2θ-extrapolation of the peak positions in the 2θ-ω-scan to θ = 90°. In (c) the precise lattice constant is obtained from the interception of the linear fit of the data with y-axis at coss θ = 0.
From the peak positions in the 2θ-ω-scans, the out-of-plane lattice constant of CuI thin film can be calculated by applying the Bragg equation for cubic crystals. To minimize the height error of the goniometer, an extrapolation with the function a = f (cos2 θ) is performed. The linear fit provides the lattice constant at cos2 θ = 0, i.e. at θ = 90°. Figure 4(c) shows the extrapolation of the lattice constant of CuI/glass of a = (6.052 ± 0.001) Å, which is very close to the bulk value. The lattice constants of all the samples on different substrates are treated with the same fitting process, which can be found in Supplementary Table S1. There is no clear dependence of lattice constants on substrates, probably due to the low growth temperature (room temperature) under which the lattice strains release easily. However, comparing with the polycrystalline CuI grown on glass, the samples on single-crystalline substrates exhibited generally small FWHM values of CuI(111) peaks in rocking curves, indicating the reduced tilt mosaicity of CuI thin films by epitaxy.
While the different rocking curve widths of the CuI/ZnO and CuI/glass thin films suggest a quantitatively better crystallinity of the CuI/ZnO layer, a major qualitative difference between the two systems is revealed in the XRD ϕ-scans as depicted in Fig. 5(a). The X-ray scattering intensity in a ϕ-scan for CuI/glass is constant over the angle and thus, as expected for deposition on an amorphous substrate, no preferred azimuthal orientation of CuI grains is present. In contrary, clearly defined peaks are found for the CuI/ZnO system. The c-axis-oriented ZnO epilayer offers a 6-fold symmetry similar to c-sapphire (n = 6), resulting in six peaks of ZnO(10.1). Six CuI(022) peaks separated by 60° were observed, indicating the heteroepitaxy of CuI on ZnO. This corresponds to the number of minimum NRD = 2 determined from Eq. 1, which is similar to the case of epitaxy on c-sapphire. The epitaxial relationship of CuI<>(111) || ZnO[
](0001) can be deduced in Fig. 5(b) and the corresponding atomic configurations are shown in Fig. 5(c).
(a) XRD ϕ-scans of sample CuI/ZnO/a-sapphire and CuI/glass, (b) schematic alignment and (c) atomic configurations of CuI lattices on c-plane ZnO surface and (d) SEM images of CuI thin films on glass and ZnO/a-sapphire respectively. In (d), triangular grains have been marked according to their orientation. Only two different orientations of the triangles have been found for CuI on ZnO/a-sapphire. Examples for each group are marked by colored triangles in red and yellow.
The surface morphology of the CuI thin films is investigated with scanning electron microscopy (SEM). As shown in Fig. 5(d), the SEM image on the left clearly reveals triangularly shaped grains on glass substrate, which confirms the (111)-oriented γ-CuI according to XRD patterns. However, rather than a continuous thin film it was comprised of loosely compacted μm-sized crystallites. The random orientation of these grains indicates a thin film without in-plane epitaxial order and with poor quality (non-continuous substrate covering and arbitrary grain boundaries). On the other hand, the CuI epilayer grown on the ZnO surface (see SEM image on the right in Fig. 5(d)) exhibits a compact thin film with a larger grain size than that of the CuI/glass thin film. On closer inspection each grain of triangular shape can be assigned to one of the two groups marked by the different colors in Fig. 5(d) according to their orientation. On comparison of the triangles of two rotational domains, they are rotated with respect to each other with an angle of 180° (or 60°). This confirms the conclusion from the XRD ϕ-scan that the CuI thin film grows epitaxially on the c-plane ZnO surface. Compared to the polycrystalline sample, this epitaxial thin film of CuI has a significantly higher crystal quality which is favorable for device fabrication.
Diodes
Based on these results, bipolar heterodiodes were fabricated from epitaxial p-CuI/n-ZnO on a-sapphire heterostructures. The schematic of the fabricated heterodiodes is shown in Fig. 6(a). The sputtered gold contacts on CuI were checked to be Ohmic. In order to achieve a good Ohmic contact of the obtained n-ZnO layer, a ZnO:Al current spreading layer is introduced as a back Ohmic contact with gold to reduce the series resistance23,24,25. The diode characteristics of current density j vs. voltage V can be descripted by the equation
(a) Schematic of the CuI/ZnO diode structure, (b) photograph of CuI/ZnO bilayer on a-sapphire substrate and (c) Current density vs. voltage characteristic of CuI/ZnO diode. The inset depicts the characteristics of the fitted multiple barriers near the kink region. Black arrow: kink at ~0.6 V probably related to inhomogeneous diode properties. Grey arrow: voltage sweeping direction.
![](http://media.springernature.com/lw380/springer-static/image/art%3A10.1038%2Fsrep21937/MediaObjects/41598_2016_Article_BFsrep21937_Equ2_HTML.gif)
where Rs (Rp) denotes the series (parallel) resistance, η the ideality factor, T the absolute temperature, k Boltzmann’s constant, A the junction area, js the saturation current density and jc an offset current to take capacitive effects into account.
Figure 6(c) shows the j-V characteristic of one of the best specimen of such CuI/ZnO diodes (with contact area A = 2.25 × 10−4 cm2). However, in forward direction, two distinct regions can be detected where j depends exponentially on V. This behavior could be attributed to the lateral variation of the CuI layer within the contact area according to the multi-contact theory26. The inset of Fig. 6(c) depicts the characteristics of the two barriers which result in a kink of measured j–V curve at ~0.6 V. Hence the diode characteristics are numerically fitted with multi-contact model as the dashed red line in Fig. 6(c). Below 0.6 V the ideality factor η is ~1.7 and the saturation current density js is ~5 × 10−9 Acm−2. While above 0.6 V the lateral variation of the CuI layer within the contact area results in a larger η value of ~2.2. Further fit parameters can be found in Supplementary Table S2.
Our epitaxial CuI/ZnO diodes exhibit generally high rectifications in the range from 107 to 109 at ±2 V. The best rectification ratio (see Fig. 6(c)) reaches up to ~2 × 109 (±2 V), which is nearly two orders of magnitude higher than that of polycrystalline diodes15. As far as we know, no report in the literature on crystalline diodes involving ZnO or other n-type wide bandgap oxide semiconductors exceeds a rectification of 103 except a p-6H-SiC/n-ZnO diode reaches 1.3 × 104 at ±8 V27 and a p-NiOx/n-TiOx diode reaches 6.7 × 105 at ±2 V28. Hence our epitaxial p-CuI/n-ZnO diode compares favorably with other diode from n-type oxide semiconductors and amorphous p-type oxides (ZnCo2O4 and NiO)25,29,30 and is additionally fully transparent (see Fig. 6(b)). This result demonstrates the advantages and high potential of CuI in application of transparent electronics.
Conclusion
In summary, heteroepitaxial growth of CuI on various substrates at room temperature was realized. The formation of rotation domains was systematically investigated. The epitaxial relationships of CuI[](111) || Al2O3[0001](
), CuI<
>(111) || NaCl[
](111), CuI<
>(111) || NaCl[110](001), CuI<
>(111) || Al2O3[
](0001) and CuI<
>(111) || ZnO[
](0001) were established. These results enable the controllable domain epitaxy of CuI thin films on various substrates. Based on the epitaxial p-CuI/n-ZnO heterostructure, bipolar diodes were demonstrated with a rectification ratio of ~2 × 109 at ±2 V, which is nearly two orders of magnitude higher than that made of polycrystalline CuI. This value presents by far the highest rectification of crystalline diodes involving oxide semiconductors. The low growth temperature (room temperature) and the use of sputtering technique make it a facile way to produce large area CuI epilayers for applications in transparent electronics.
Methods
The CuI films were deposited by DC sputtering in a dynamically pumped chamber with a base pressure of ~1 × 10−5 millibar. A high purity (99.999%) copper disk was used as the sputtering target. For the deposition of CuI thin films, iodine vapor was introduced by a needle valve connected with a heated iodine source. This iodine source was a stainless steel tube filled with iodine particles, which was kept at ~180 °C to sustain a sufficient iodine vapor pressure. The bearing of the turbomolecular pump is protected by nitrogen gas. The throttle valve between the chamber and turbomolecular pump was partially closed for adjusting the iodine partial pressure to ~1 × 10−3 millibar. Argon was introduced to set the total pressure to 0.02 millibar.
Presputtering was conducted with power of 30 W for 20 min with the shutter closed. For investigating various epitaxial relationships, substrates with different rotational symmetry were selected including NaCl(001), NaCl(111), a-plane and c-plane sapphire single-crystals, as well as amorphous Corning 1737 glass for a comparison. The CuI samples were sputtered at 30 W at room temperature. The typical thickness of CuI thin film was estimated as ~100 nm with a Dektak profilometer. Heterojunction of CuI with ZnO was subsequently fabricated. The 40 nm thin ZnO:Al (1 wt% Al2O3) current spreading layer (electrical resistivity ρ = 1 × 10−3 Ωcm) and the 100 nm thin ZnO film were grown successively by PLD at 650 °C and 0.016 millibar oxygen partial pressure on an a-plane sapphire substrate23.
Investigations of the epitaxial relationship were performed with a Philips X’Pert x-ray diffractometer equipped with a Bragg-Brentano powder goniometer using divergent/focusing slit optics and Cu Kα radiation. SEM was done using a FEI NOVA Nanolab 200. The I-V measurement was performed with a Süss wafer prober and an Agilent 4155C Semiconductor Parameter Analyzer.
Additional Information
How to cite this article: Yang, C. et al. Room-temperature Domain-epitaxy of Copper Iodide Thin Films for Transparent CuI/ZnO Heterojunctions with High Rectification Ratios Larger than 109. Sci. Rep. 6, 21937; doi: 10.1038/srep21937 (2016).
References
Thomas G. Materials science: Invisible circuits. Nature 389, 907–908 (1997).
Akasaki I. & Amano H. Breakthroughs in improving crystal quality of GaN and invention of the p-n junction blue-light-emitting diode. Jpn. J. Appl. Phys. 45, 9001–9010 (2006).
Grundmann M. et al. Transparent semiconducting oxides: Materials and devices. Phys. Status Solidi A 207, 1437–1449 (2010).
Fortunato E., Barquinha P. & Martins R. Oxide semiconductor thin-film transistors: A review of recent advances. Adv. Mater. 24, 2945–2986 (2012).
Wang J., Li J. B. & Li S. S. Native p-type transparent conductive CuI via intrinsic defects. J. Appl. Phys. 110, 054907–5 (2011).
Chen D. et al. Growth strategy and physical properties of the high mobility p-type CuI cystal. Cryst. Growth Des. 10, 2057–2060 (2010).
Bädeker K. Über die elektrische Leitfähigkeit und die thermoelektrische Kraft einiger Schwermetallverbindungen. Ann. Physik 327, 749–766 (1907).
Grundmann M. Karl Bädeker (1877–1914) and the discovery of transparent conductive materials. Phys. Stat. Sol. A 212, 1409–1426 (2015).
Derenzo S. E., Weber M. J. & Klintenberg M. K. Temperature dependence of the fast, near-band-edge scintillation from CuI, HgI2, PbI2, ZnO:Ga and CdS:In. Nucl. Instrum. Methods Phys. Res. A 486, 214–219 (2002).
Zhou Y. et al. Glancing angle deposition of copper iodide nanocrystals for efficient organic photovoltaics. Nano Lett. 12, 4146–4152 (2012).
Rand B. P. et al. The impact of molecular orientation on the photovoltaic properties of a Phthalocyanine/Fullerene heterojunction. Adv. Funct. Mater. 22, 2987–2995 (2012).
Iimori H. et al. High photovoltage generation at minority-carrier controlled n-Si/p-CuI heterojunction with morphologically soft CuI. J. Phys. Chem. C 112, 11586–11590 (2008).
Li P. et al. CuI-Si heterojunction solar cells with carbon nanotube films as flexible top-contact electrodes. Nano Res. 4, 979–986 (2011).
Schein F. L., von Wenckstern H. & Grundmann M. Transparent p-CuI/n-ZnO heterojunction diodes. Appl. Phys. Lett. 102, 092109–4 (2013).
Grundmann M. et al. Cuprous Iodide - a p-type transparent semiconductor: History and novel applications. Phys. Status Solidi A 210, 1671–1703 (2013).
DiCenzo S. B., Wertheim G. K. & Buchanan D. N. E. Epitaxy of CuI on Cu(111). Appl. Phys. Lett. 40, 888–890 (1982).
Reichelt K. & Mair G. Preparation of CuI films on NaCl single crystals by reactive sputtering and characterization by electron microscopy and Rutherford backscattering. J. Vac. Sci. Technol. 16, 896–898 (1979).
Narayan J. & Larson B. C. Domain epitaxy: A unified paradigm for thin film growth. J. Appl. Phys. 93, 278–285 (2003).
Grundmann M., Böntgen T. & Lorenz M. The occurrence of rotation domains in heteroepitaxy. Phys. Rev. Lett. 105, 146102–4 (2010).
Grundmann M. Formation of epitaxial domains: Unified theory and survey of experimental results. Phys. Status Solidi B 248, 805–824 (2011).
Li W. J. & Shi E. W. Growth habit and habit variation of γ-CuI crystallites under hydrothermal conditions. Cryst. Res. Technol. 37, 1041–1048 (2002).
Rouleau C. M., Kang S. & Lowndes D. H. Pulsed KrF laser deposited GaN/TiN/Si(111) heterostructures by sequential TiN and liquid Ga laser ablation. Appl. Phys. A 69, S441–S445 (1999).
von Wenckstern H. et al. Donor levels in ZnO. Adv. Sol. St. Phys. 45, 263–274 (2005).
von Wenckstern H. et al. Mean barrier height of Pd Schottky contacts on ZnO thin films. Appl. Phys. Lett. 88, 092102–3 (2006).
Schein F. L., Winter M., Böntgen T., von Wenckstern H. & Grundmann M. Highly rectifying p-ZnCo2O4/n-ZnO heterojunction diodes. Appl. Phys. Lett. 104, 022104–4 (2014).
Johnson V. A., Smith R. N. & Yearian H. J. D. C. Characteristics of silicon and germanium point contact crystal rectifiers. Part II. The multicontact theory. J. Appl. Phys. 21, 283–289 (1950).
Alivov Y. I. et al. Photoresponse of n-ZnO/p-SiC heterojunction diodes grown by plasma-assisted molecular-beam epitaxy. Appl. Phys. Lett. 86, 241108–3 (2005).
M. J. Lee. et al. A low-temperature-grown oxide diode as a new switch element for high-density, nonvolatile memories. Adv. Mater. 19, 73–76 (2007).
Grundmann M., Karsthof R. & von Wenckstern H. Interface recombination current in type II heterostructure bipolar diodes. ACS Appl. Mat. Interfaces 6, 14785–14789 (2014).
Grundmann M., Schein F. L., Karsthof R., Schlupp P. & von Wenckstern H. Several Approaches to Bipolar Oxide Diodes With High Rectification. Adv. Sci. Technol. 93, 252–259 (2014).
Acknowledgements
This work was funded by Deutsche Forschungsgemeinschaft (DFG, GR 1011/28-1) and Universität Leipzig within the program of Open Access Publishing.
Author information
Authors and Affiliations
Contributions
C.Y. and M.G. conceived the experiments, M.L. and F.-L.S. gave experiment instructions, C.Y. and M.K. conducted the experiments, C.Y. analysed the results and wrote the manuscript. M.L. and M.G. revised the manuscript. All authors discussed the results and reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Yang, C., Kneiß, M., Schein, FL. et al. Room-temperature Domain-epitaxy of Copper Iodide Thin Films for Transparent CuI/ZnO Heterojunctions with High Rectification Ratios Larger than 109. Sci Rep 6, 21937 (2016). https://doi.org/10.1038/srep21937
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep21937
- Springer Nature Limited
This article is cited by
-
A new strategy for fabricating low haze p-type CuI film
Surface Science and Technology (2024)
-
Photoluminescence enhancement in cuprous iodide crystalline thin films achieved through repeated step-growth and rapid thermal annealing
Journal of the Korean Physical Society (2023)
-
Optoelectronic properties and ultrafast carrier dynamics of copper iodide thin films
Nature Communications (2022)
-
Temperature-dependent device properties of γ-CuI and β-Ga2O3 heterojunctions
SN Applied Sciences (2021)
-
Optimization of the nitrogen content for room temperature rapid synthesis of CuI thin films via liquid iodination method using Cu3N film as precursor
Journal of Materials Science: Materials in Electronics (2020)