Abstract
Photocatalysts produce free radicals upon receiving light energy; thus, they possess antibacterial properties. Silver (Ag) is an antibacterial material that disrupts bacterial physiology. Our previous study reported that the high antibacterial property of silver nanoparticles on the surfaces of visible light-responsive nitrogen-doped TiO2 photocatalysts [TiO2(N)] could be further enhanced by visible light illumination. However, the major limitation of this Ag-TiO2 composite material is its durability; the antibacterial property decreased markedly after repeated use. To overcome this limitation, we developed TiO2(N)/Ag/TiO2(N) sandwich films in which the silver is embedded between two TiO2(N) layers. Various characteristics, including silver and nitrogen amounts, were examined in the composite materials. Various analyses, including electron microscopy, energy dispersive spectroscopy, X-ray diffraction and ultraviolet–visible absorption spectrum and methylene blue degradation rate analyses, were performed. The antibacterial properties of the composite materials were investigated. Here we revealed that the antibacterial durability of these thin films is substantially improved in both the dark and visible light, by which bacteria, such as Escherichia coli, Streptococcus pyogenes, Staphylococcus aureus, and Acinetobacter baumannii, could be efficiently eliminated. This study demonstrated a feasible approach to improve the visible-light responsiveness and durability of antibacterial materials that contain silver nanoparticles impregnated in TiO2(N) films.
Similar content being viewed by others
Introduction
Disinfectants are crucial for reducing pathogenic microorganisms for personal hygiene and in water treatment, food production and health care facilities1. Titanium dioxide (TiO2) substrates are the most frequently used photocatalyst for antibacterial purposes2. After exposure to ultraviolet (UV) light, the photon energy excites electrons from the valence band to the conduction band, leaving positive holes in the valence band. The electrons and holes may recombine, releasing energy in the form of light or heat, causing inefficient photocatalysis. However, the excited electrons and holes may be trapped on or near the TiO2 surface and subsequently react with atmospheric water and oxygen, yielding reactive oxygen species (ROS) such as hydroxyl radicals (•OH) and superoxide anions (O2−)3. These ROS aid in eliminating pathogenic microorganisms; however, UV irradiation is hazardous to humans. Therefore, UV-responsive photocatalysts, such as TiO2, are unsuitable for use in living environments.
To avoid this problem, impurity may be doped in TiO2 films with carbon, sulfur, nitrogen (N), or silver (Ag) results in an excitation wavelength shift from UV to the visible light region4,5,6,7. In addition, impurity doping or metal-particle-impregnated TiO2 may reduce the recombination rates of pairs of electrons and holes. Furthermore, impregnated material such as silver possesses antibacterial properties. Therefore, visible-light-responsive antibacterial photocatalysts, which ensure a high quantum efficiency under sunlight and can be used safely in indoor settings to prevent users from being exposed to biohazardous UV light, have been developed2,5,6,8,9,10,11,12,13.
Our previous study indicated that nitrogen-doped TiO2 [TiO2(N)] thin film coated with silver nanoparticles exhibited higher antibacterial activity under the illumination of visible light6. However, the major limitation of this film is its durability. Because the silver nanoparticles are directly exposed to the environment and easily detached from the surfaces of the thin films, we observed that the antibacterial activity was substantially reduced after repeated usages. This demonstrates the need for a multilayer or sandwich thin film in which the silver is embedded between the two TiO2(N) layers of thin films.
The concept of multilayered TiO2/Ag films has been described in research for decades, with various purposes and rationales provided. For example, transparent heat‐mirror films of TiO2/Ag/TiO2 were proposed for solar energy collection and radiation insulation14 and transparent conductive coatings of TiO2/Ag/TiO215 were also reported. The multilayered TiO2/Ag films described in the literature enhance photocatalysis under UV irradiation16. However, visible-light-responsive Ag-TiO2 sandwich films with higher durability and effective antibacterial properties are yet to be developed. Previous studies have described the development of visible-light-responsive antibacterial photocatalysts, which ensure high quantum efficiency under sunlight and can be used safely in indoor settings, preventing users from UV exposure, as a major advancement in photocatalytic material research2,5,6,8,9,10,11,12,13. In addition, most antibacterial studies have employed normal bacterial flora, such as E. coli, which may not reflect the real targets of human pathogens. Notably, antibacterial materials may apply to particular type (e.g. Gram-negative bacteria17) but not the other types of bacteria. Therefore, in this study, we developed various novel Ag-TiO2 sandwich films with a high visible-light-responsiveness and then investigated their antibacterial properties. In addition to E. coli, pathogenic bacteria, such as S. aureus, S. pyogenes (Gram-positive) and A. baumannii (Gram-negative), were first used to analyze the bactericidal effects of these Ag-TiO2 sandwich films.
Results
Effects of silver level on photocatalytic and antibacterial properties of TiO2(N)/Ag/TiO2(N) sandwich films
To regulate the amount of Ag deposition in the middle layer of sandwich films, various sputtering periods, namely 0, 15, 30, 60 and 120 s, were examined. X-ray diffraction patterns of the sandwich films revealed that the anatase phase of titania was formed after annealing (Supplementary Fig. S1). Energy-dispersive X-ray spectroscopy analysis indicated that the amount of Ag deposition increased with time (Supplementary Fig. S2). Furthermore, a field-emission scanning electron microscopy analysis revealed that the thickness of the sandwiched thin films was nearly 700 ± 50 nm, in which the thickness for the silver layers are 1.9, 3.8, 7.5 and 15 nm for the specimens prepared under various sputtering time periods of 15, 30, 60, 120 s, respectively (Fig. 1A–J). In addition, various amounts of Ag nanoparticles were observed on the TiO2(N) surfaces of some films before and after annealing (Fig. 1K–T, white spots). An ultraviolet–visible (UV–Vis) absorption spectroscopy analysis revealed no significant difference after annealing; whereas the Ag-containing samples showed a redshift, indicating an increased visible light absorption (Fig. 2A,B). The visible-light-responsive photocatalytic property was determined using a methylene blue (MB) degradation analysis as described18. Data revealed that Ag doping did not markedly increase the visible-light-responsive photocatalysis (Fig. 2C). Despite this, the antibacterial property was determined. Because of the lack of the visible-light-induced photocatalytic activity, no significant difference was observed between the groups with or without visible light illumination (Fig. 2D). Because these thin films contained Ag, the antibacterial property was detectable even in the dark conditions. The NTA120s sample, which contained the highest Ag levels (Supplementary Fig. S1) exhibited the most antibacterial activity compared with the other tested samples (Fig. 2D).
Effect of nitrogen level on photocatalytic and antibacterial properties of TiO2(N)/Ag/TiO2(N) sandwich films
To increase the visible-light responsiveness, N doping is critical6. The nitrogen content in these films was minimal when oxygen flow was high [5 sccm (standard cubic centimeters per minute)] during film deposition. We hypothesized that this was caused by an excess supply of oxygen, rendering N unable to be efficiently integrated into the lattice structure of TiO2. Thus, various low-O2-supplying conditions, including the O2 flow rate of 2, 3, 4 and 5 sccm, were tested (Supplementary Table 1). Consistent with our hypothesis, an X-ray photoelectron spectroscopy analysis revealed that reduced O2 supply improved N levels in composite thin films (Fig. 3A). However, the Ti-to-O ratio was also changed, with the N(4)TA and N(5)TA samples exhibiting a relatively 1:2 ratio, whereas the N(2)TA and N(3)TA samples exhibited a ratio of approximately 1:1 (Fig. 3A; the amount of oxygen supplied was indicated in brackets, e.g., N(4)TA was prepared with 4 sccm O2). These results indicated that 2 and 3 sccm O2 supply were insufficient to oxidize Ti and produce TiO2; instead, TiN or TiON was formed. Consistently, X-ray photoelectron spectroscopy analysis for the 1 s atomic orbital of N indicated a significant increase in the formation of TiN (Fig. 3B). X-ray diffraction analysis further revealed the production of TiN in N(2)TA and N(3)TA samples before and after annealing (Fig. 3C,D). Because TiO2 was not efficiently produced in the N(2)TA and N(3)TA samples, the rutile and anatase TiO2 signals were observed only in the N(4)TA and N(5)TA thin films after annealing (Fig. 3D). The field-emission scanning electron microscopy analysis indicated that the N(2)TA and N(3)TA samples formed thicker films, with less surface-exposed Ag nanoparticles compared with the N(4)TA and N(5)TA samples (Fig. 4A–E). A UV–Vis absorption spectroscopy analysis indicated that reduced O2 supply caused remarkable redshifts in the samples (Fig. 5A,B). The band gaps were calculated using the UV–Vis spectroscopy and Tauc plots19. However, the band gaps for the N(2)TA and N(3)TA were not derived, because the two samples produced under 2 and 3 sccm O2 supply were insufficient to form TiO2; instead, TiN or TiON was formed with high amount of nitrogen of 18.8% and 13.5% and thus, with high absorbance (Fig. 3A,B). These results indicated that the increased N content reduced the band gap of the thin films (Fig. 5C, Supplementary Table S1). Analyses of MB and Hoechst dye degradation rates further revealed that the N(4)TA sample exhibited a superior visible-light-induced photocatalytic ability than did the other samples (Fig. 5D; Supplementary Fig. S3), suggesting that the balance of the N-doping amount and TiO2 production was critical. In accordance with the aforementioned analyses, antibacterial experiments demonstrated that the N(4)TA sample exhibited the highest antibacterial activity among the thin film samples under visible light illumination (Fig. 5E, N(4)TA-N500). In addition, visible light illuminating the N(4)TA sample exerted higher bactericidal activity than did the control groups with the N(4)TA sample in the dark (Fig. 5E, N(4)TA-N500; *P < 0.05).
Durability of visible-light-responsive antibacterial property
The visible-light-responsive antibacterial property of these novel sandwich films after repeated usages was compared with that of our previously developed single-layer thin films containing Ag nanoparticles6. Although the first use of the single-layer thin films could achieve an approximately 5-log reduction in bacteria6, the data indicated that these thin films could not efficiently eliminate the bacteria after frequently use (Fig. 6, second- and third-cycle use of single-layer groups). By contrast, favorable performance was observed after these multilayer films were repeated used, which eliminated E. coli efficiently after the second and third use (Fig. 6, second- and third-cycle use of multilayer groups). Scanning electron microscopy was employed to investigate the E. coli cell damage caused by the sandwich films. We observed that if the bacterial cells were not treated with Ag present in the N-doped TiO2 sandwich films with or without visible light illumination, they displayed relatively smooth surfaces (Fig. 7A,B). Because of the antibacterial property of Ag, bacterial cells displayed rough surfaces after being treated with a sandwich film in the dark (Fig. 7C). More vigorous changes, which were showed as unique cracks, such as structures on their surfaces, were observed after the bacterial cells were illuminated with visible light on a sandwich film (Fig. 7D, arrows).
Pathogen analyses
To investigate the performance of TiO2(N)/Ag/TiO2(N) sandwich films in eradicating pathogenic bacteria and human pathogens, including S. pyogenes, S. aureus and A. baumannii, the films were subjected to visible-light-induced catalysis. Among these, S. aureus and A. baumannii are pathogenic bacteria with a high antibiotic resistance rate, causing increased incidence of nosocomial infections20. We demonstrated that all the tested pathogens were efficiently eliminated after exposure to the sandwich films illuminated with visible light (Fig. 8, dark vs. light groups). The effectiveness showed a nearly 1-log reduction of the bacterial population. In addition, the TiO2(N)/Ag/TiO2(N) sandwich films appeared equally potent in eliminating the bacteria when applied to both the Gram-positive (S. aureus and S. pyogenes) and Gram-negative (E. coli and A. baumannii) bacteria (Fig. 8).
Discussion
Silver has been used to prevent infections for thousands of years21, with Hippocrates describing the antimicrobial properties of the metal in 400 BC. Antibacterial silver products have been widely used for the handling and cleaning of burn, trauma, catheter and dental amalgam22,23. Previous studies have demonstrated that both Ag+ ions and Ag nanoparticles possess antibacterial properties22,23,24. Silver disrupts various bacterial physiologies, including disulfide bond formation, metabolism and iron homeostasis; these changes increase production of ROS and membrane permeability and disrupt membrane respiratory electron transport chains and DNA replication components23,25. Thus, silver is widely used as tableware and a hygiene product. In these cases, the durability of the antibacterial property is not a problem because the entire metal product is able to release a sufficient amount of Ag ions and nanoparticles with time. However, this is not the case when only a nanoscaled layer of silver is used.
Previous studies have indicated that Ag particles or their coating on TiO2 surfaces can enhance the light-driven photoinactivation of bacteria2,6,26,27,28,29,30. However, the antibacterial activity of such thin films after repeated use has not been investigated thoroughly. In addition, the antibacterial property of Ag-TiO2 composite thin films remains to be elucidated. For example, our previous study reported that TiO2 containing nanoscale Ag wires exhibited strong visible-light enhanced antibacterial properties6. The durability of these thin films is always a problem; because their antibacterial properties rapidly decline after repeated use (Fig. 6, second- and third-cycle use of single-layer groups). Therefore, we described the influence of the various amounts of silver and nitrogen on the antibacterial property of the sandwich films. Analysis results indicated that silver depositions improved the antibacterial activity of the thin films (Fig. 2). In addition, the amount of nitrogen supplied is crucial for the formation of high-performance antibacterial thin films under visible light illumination (Fig. 5). Thus, we developed the TiO2(N)/Ag/TiO2(N) sandwich films, which exhibited sustainable antibacterial properties after repeated use.
Nanoscaled thin films have been used to achieve a controlled release of embedded materials31,32,33. In the original experimental design, the silver layer was embedded in the middle of TiO2(N)/Ag/TiO2(N) sandwich films. Notably, in addition to the embedded Ag layer, we observed certain scattered Ag nanoparticles on the surface of the as-deposited sandwich films and a higher density of Ag nanoparticles on annealed films. Ag nanoparticles appeared to emerge on the film surface by atomic diffusion through the grain boundaries of the upper TiO2(N) layer. In addition, this could happen when silver atoms gain sufficient energy from the bombardment of atoms and ions during sputtering growth or from thermal annealing. In either case, the Ag nanoparticles are impregnated in the TiO2(N) films and not merely placed or attached on the film surface, which could be the main reason for the high durability of the photocatalytic TiO2(N)/Ag/TiO2(N) sandwich films.
The silver-induced bactericidal effect is a complex response, involving the disruption of bacterial physiologies and abnormal elicitation of ROS in bacteria23,25,34. Combined treatment with exogenous ROS and silver revealed a synergistic antibacterial effect35. ROS production is the main antibacterial mechanism of photocatalysts2,36,37. Thus, it is reasonable that the silver synergizes with the photocatalytic components of the sandwich films to efficiently eradicate pathogenic bacteria under the visible light (Fig. 8). However, nanoscale Ag particles and TiO2 appear to exert a synergistic impact on the environment38,39. The increased production and use of silver nanoparticles in products leads to the inevitable increase in the release of these particles into the environment through the lives of these products, from the raw material stage to disposal40. Likewise, the increased disposal of TiO2 nanoparticles exerts a considerable impact on the ecosystem41. Although the mechanism remains to be further elucidated, the coexistence of Ag and TiO2 nanoparticles has been shown to exert increased environmental impact under sunlight38,39. Furthermore, exposure to Ag nanoparticles was shown to influence the immune system42. However, previously reported Ag–TiO2 thin films have typically had a surface-exposed Ag layer6,43,44,45,46. Thus, the increase reusability of the nanoscaled Ag-TiO2 composite material with a TiO2-covered layer will reduce the environmental impact of products and will benefit human health.
In conclusion, we successfully demonstrated the antibacterial properties of TiO2(N)/Ag/TiO2(N) sandwich films, which could be optimized through Ag and N depositions on titania substrates. The silver and TiO2(N) composite materials exhibited synergistic antibacterial activity under visible light illumination. These findings suggest that the concepts used in this study and multilayer TiO2(N)/Ag/TiO2(N) composite materials have potential applications in the developing alternative disinfectants.
Methods
Various thin films, including single layers of Ag, TiO2 and TiO2(N) and TiO2(N)/Ag/TiO2(N) sandwich layers were prepared in a reactive magnetron sputtering system
As Supplementary Fig. S4 illustrates, five sputtering targets exist in the deposition system, but only two titanium (Ti) targets and one silver (Ag) target were used and the base pressure was below 1.3 × 10−5 Pa. To prepare pure TiO2 or TiO2(N) and Ag, two Ti targets and one Ag target were used, respectively. Before sputtering, we used argon plasma to etch the surface of the substrate for 10 min to remove residual particles on the surface. The substrate holder was rotated at a speed of 5 rpm without applying substrate bias during deposition. Silicon wafer (100) and glass substrates were used. The substrate was nearly at room temperature without external heating. The target powers were set at 250 W each and 20 W in the DC mode for the two Ti targets and one Ag target, respectively. For pure TiO2 deposition, the gas contained argon and oxygen with the fixed flow rates of Ar at 20 sccm and O2 at 7 sccm and the total pressure was approximately 4.7 × 10−1 Pa (3.5 × 10−3 Torr). For the TiO2(N) films, the gas contained Ar, O2 and N2 at the flow rates of 20, 5–2 and 8 sccm, respectively, whereas for the Ag film, the gas used contained only Ar with a flow rate of 20 sccm without adding other gases.
In addition, for forming a monolithic layer of Ag, TiO2 and TiO2(N), two series of sandwiched TiO2(N)Ag/TiO2(N) films were prepared. Furthermore, one series was prepared with various amounts of Ag in the sandwiched films, whereas the other series was prepared with a fixed amount of Ag but with various nitrogen contents in the sandwiched films. In the first series, the amount of Ag was regulated by changing the deposition time from 30 s to 60, 90 and 120 s and the corresponding sample IDs were denoted as NTAxxxs, where xxx was the Ag deposition time. In the second series, the amount of Ag was fixed with the deposition time of 120 s and the nitrogen contents in the TiO2(N) films were regulated by reducing the oxygen flow rates from 5 sccm to 4, 3 and then 2 sccm and the corresponding sample IDs were denoted as N (x)TA, where x was the oxygen flow rate. The as-deposited films were further annealed at 500 °C for 1 h in the nitrogen atmosphere by using a conventional vacuum furnace.
The deposition rate of TiO2(N) films varied with the oxygen flow rate and was approximately 350 nm/h with the oxygen flow rate of 4 sccm. The deposition rate of silver was approximately 7.5 nm/min. The deposition times of the typical sandwich TiO2(N)/Ag/TiO2(N) film used in this study were 1 h and 2 min and 1 h. Thus, an average thickness of the Ag impregnated TiO2(N) films was 700 ± 50 nm. The thickness for the silver layer are 1.9, 3.8, 7.5 and 15 nm for the specimens prepared under various sputtering time periods of 15, 30, 60, 120 s, respectively.
Characterization analysis
The structure and crystallinity of films were analyzed using X-ray diffraction measurements recorded using the Rigaku X-ray diffractometer D/MAX-2500 V with a Cu Kα radiation (40 kV, 100 mA) source. The surface morphology and the cross-sectional view of the films were observed using the JEOL JEM-6500 F field-emission scanning electron microscopy. The UV–Vis absorption spectra of the films were recorded using a JASCO V-650 spectrophotometer ranging from 300 to 900 nm. The composition of samples was determined using an energy dispersive spectroscopy (Horiba, EMAX-ENERGY) and a K-Alpha™ X-ray photoelectron spectrometer using an AlK α X-ray radiation source to estimate elements semi-quantitatively.
Antibacterial experiment
Bacterial culturing and plating were performed following the previously described standard methods5,47,48,49. The bacterial concentration was determined using the standard plating method or from optical density readings at 595 nm (OD595). For example, the conversion factor for E. coli BL 21 was calculated to be 1 × 109 colony-forming unit (CFU)/mL at OD595 and the cultures were diluted with the culture medium to 1 × 107 CFU/mL. The 1 × 106 CFU culture was allowed to drip on the sample (approximately 6.25 cm2) and was then placed in a dark room or exposed under the visible light and at room temperature. The visible light source was an incandescent lamp (Classictone incandescent lamp, 60 W, Philips Taiwan; Taipei, Taiwan) and the illumination density was recorded using a light meter (model LX-102; Lutron Electronic Enterprises, Taipei, Taiwan). In the photocatalytic reaction, the illumination distance between the sample and lamp was approximately 10 cm, which was exposed for 30 min and the light intensity on the sample surface was nearly 1.2 × 103 lux (lumen/m2) (30 mW/cm2). After illumination, 100 μL of the bacterial solution was recovered from the sample. Finally, the bacterial concentration was determined using standard dilution and plating methods and the percentage of surviving bacteria was calculated18,19. S. pyogenes (strain M29588), pandrug-resistant A. baumannii (strain M36788) and S. aureus (strain SA02) were the clinical isolates provided by Buddhist Tzu-Chi General Hospital in Hualien, Taiwan5. E. coli and A. baumannii were grown and maintained in the lysogeny broth (LB) medium or LB agar (BD Diagnostics, Sparks, MD, USA) at 37 °C. By contrast, S. pyogenes and S. aureus were grown in the trypticase soy broth with yeast extract (TSBY) medium or TSBY agar (MDBio, Inc., Taipei, Taiwan) at 37 °C. When the visible light was used to elicit the photocatalysis reaction, a UV cut-off filter (400 nm; Edmund Optics, Barrington, NJ, USA) was used to prevent the illumination of small fractions with UV-range wavelength in the photocatalytic experiments.
Photocatalytic properties
Analysis methods were based on recently reported literatures4,50,51, which used the MB degradation rate to analyze the photocatalytic performance of impurity-doped TiO2, in accordance with the generally accepted method and reported format of MB photodecomposition. Photocatalytic efficiency was evaluated by examining the decomposition of 10 ppm MB (Sigma-Aldrich, St. Louis, MO, USA). The MB concentration was determined according to the intensity of the light-absorption peak at 664 nm wavelength, as measured using a UV–Vis spectrometer. A fixed size (1 cm × 1 cm) of the sample sank in 2 mL of the MB aqueous solution. The visible light illumination was conducted using a fluorescent lamp (Philips; P-LF27W/865) with a wavelength distribution of approximately 400–750 nm and a maximum intensity at the range of 543–611 nm, producing an average power density of 4.2 mW/cm2 at a distance of 8 cm between the visible light source and sample.
Statistical analysis
The means, standard deviations and statistics of the quantifiable data were calculated using Microsoft Office Excel 2003, SigmaPlot 10 and SPSS 19. The significance of data was determined using a one-way analysis of variance followed by a post hoc Bonferroni corrected test. The probability of type I error α = 0.05 was recognized as statistically significant.
Additional Information
How to cite this article: Wong, M.-S. et al. Antibacterial property of Ag nanoparticle-impregnated N-doped titania films under visible light. Sci. Rep. 5, 11978; doi: 10.1038/srep11978 (2015).
References
McDonnell, G. & Russell, A. D. Antiseptics and disinfectants: activity, action and resistance. Clinical microbiology reviews 12, 147–179 (1999).
Liou, J. W. & Chang, H. H. Bactericidal effects and mechanisms of visible light-responsive titanium dioxide photocatalysts on pathogenic bacteria. Archivum immunologiae et therapiae experimentalis 60, 267–275 (2012).
Linsebigler, A. L., Lu, G. & Yates, J. T. Photocatalysis on TiO2 surfaces: principles, mechanisms and selected results. Chemical Reviews 95, 735–758 (1995).
Asahi, R. et al. Visible-light photocatalysis in nitrogen-doped titanium oxides. Science 293, 269–271 (2001).
Wong, M. S. et al. Visible-light-induced bactericidal activity of a nitrogen-doped titanium photocatalyst against human pathogens. Applied and environmental microbiology 72, 6111–6116 (2006).
Wong, M. S., Sun, D. S. & Chang, H. H. Bactericidal performance of visible-light responsive titania photocatalyst with silver nanostructures. PLoS One 5, e10394 (2010).
Yu, J. C. et al. Efficient visible-light-induced photocatalytic disinfection on sulfur-doped nanocrystalline titania. Environmental science & technology 39, 1175–1179 (2005).
Cheng, C. L. et al. The effects of the bacterial interaction with visible-light responsive titania photocatalyst on the bactericidal performance. J Biomed Sci 16, 7 (2009).
Kau, J. H. et al. Role of visible light-activated photocatalyst on the reduction of anthrax spore-induced mortality in mice. PLoS One 4, e4167 (2009).
Chang, W. K. et al. Visible light responsive core-shell structured In2O3@CaIn2O4 photocatalyst with superior bactericidal property and biocompatibility. Nanomedicine : nanotechnology, biology and medicine 8, 609–617 (2012).
Chen, Y. L. et al. The use of nanoscale visible light-responsive photocatalyst TiO2-Pt for the elimination of soil-borne pathogens. PLoS One 7, e31212 (2012).
Liou, J. W. et al. Visible light responsive photocatalyst induces progressive and apical-terminus preferential damages on Escherichia coli surfaces. PLoS One 6, e19982 (2011).
Tseng, Y. H. et al. Antibacterial performance of nanoscaled visible-light responsive platinum-containing titania photocatalyst in vitro and in vivo. Biochimica et biophysica acta 1830, 3787–3795 (2013).
Fan, J. C. C., Bachner, F. J., Foley, G. H. & Zavracky, P. M. Transparent heat‐mirror films of TiO2/Ag/TiO2 for solar energy collection and radiation insulation Applied Physics Letters 25, 693–695 (1974).
Dhar, A. & Alford, T. L. High quality transparent TiO2/Ag/TiO2 composite electrode films deposited on flexible substrate at room temperature by sputtering. APL Materials 1, ID: 012102 (2013).
Goei, R. & Lim, T. T. Ag-decorated TiO2 photocatalytic membrane with hierarchical architecture: photocatalytic and anti-bacterial activities. Water research 59, 207–218 (2014).
Zaknoon, F. et al. Antibacterial properties of an oligo-acyl-lysyl hexamer targeting Gram-negative species. Antimicrobial agents and chemotherapy 56, 4827–4832 (2012).
Wu, M. S. et al. Nanodiamonds protect skin from ultraviolet B-induced damage in mice. Journal of nanobiotechnology 13, 35 (2015).
Tauc, J. Optical properties and electronic structure of amorphous Ge and Si. . Materials Research Bulletin 3, 37–46 (1968).
Chen, Y. Y. et al. Surveillance on secular trends of incidence and mortality for device-associated infection in the intensive care unit setting at a tertiary medical center in Taiwan, 2000-2008: a retrospective observational study. BMC infectious diseases 12, 209 (2012).
Silver, S., Phung le, T. & Silver, G. Silver as biocides in burn and wound dressings and bacterial resistance to silver compounds. J Ind Microbiol Biotechnol 33, 627–634 (2006).
Dunn, K. & Edwards-Jones, V. The role of Acticoat with nanocrystalline silver in the management of burns. Burns 30 Suppl 1, S1–9 (2004).
Silver, S. Bacterial silver resistance: molecular biology and uses and misuses of silver compounds. FEMS Microbiol Rev 27, 341–353 (2003).
Sondi, I. & Salopek-Sondi, B. Silver nanoparticles as antimicrobial agent: a case study on E. coli as a model for Gram-negative bacteria. Journal of colloid and interface science 275, 177–182 (2004).
Morones-Ramirez, J. R., Winkler, J. A., Spina, C. S. & Collins, J. J. Silver enhances antibiotic activity against gram-negative bacteria. Science translational medicine 5, 190ra181 (2013).
Choi, J. Y. et al. Photocatalytic antibacterial effect of TiO(2) film formed on Ti and TiAg exposed to Lactobacillus acidophilus. J Biomed Mater Res B Appl Biomater 80, 353–359 (2007).
Hu, C., Guo, J., Qu, J. & Hu, X. Photocatalytic degradation of pathogenic bacteria with AgI/TiO2 under visible light irradiation. Langmuir : the ACS journal of surfaces and colloids 23, 4982–4987 (2007).
Hu, C. et al. Ag/AgBr/TiO2 visible light photocatalyst for destruction of azodyes and bacteria. J Phys Chem B 110, 4066–4072 (2006).
Matsui, Y. et al. Effect of silver-carrying photocatalyst “Hikari-Gintech” on mycobacterial growth in vitro. Microbiol Immunol 48, 489–495 (2004).
Yao, Y. et al. Self-sterilization using silicone catheters coated with Ag and TiO2 nanocomposite thin film. J Biomed Mater Res B Appl Biomater 85, 453–460 (2008).
Caruso, F. & Ariga, K. Modern Techniques for Nano- and Microreactors/-reactions. Springer Science & Business Media (2010).
Mane, S. T. et al. A study of nano crystalline Cd1-XCoXS thin composite films deposited by a liquid phase chemical bath deposition Advances in Applied Science Research 2, 8–18 (2011).
Kurtulus, O., Daggumati, P. & Seker, E. Molecular release from patterned nanoporous gold thin films. Nanoscale 6, 7062–7071 (2014).
Marambio-Jones, C., Hoek EMV. A review of the antibacterial effects of silver nanomaterials and potential implications for human health and the environment. Journal of Nanoparticle Research 12, 1531–1551 (2010).
Batarseh, K. I. & Smith, M. A. Synergistic activities of a silver(I) glutamic acid complex and reactive oxygen species (ROS): a novel antimicrobial and chemotherapeutic agent. Current medicinal chemistry 19, 3635–3640 (2012).
Cai, Y., Stromme, M. & Welch, K. Photocatalytic antibacterial effects are maintained on resin-based TiO2 nanocomposites after cessation of UV irradiation. PLoS One 8, e75929 (2013).
Carre, G. et al. TiO2 photocatalysis damages lipids and proteins in Escherichia coli. Applied and environmental microbiology 80, 2573–2581 (2014).
George, S. et al. Differential effect of solar light in increasing the toxicity of silver and titanium dioxide nanoparticles to a fish cell line and zebrafish embryos. Environmental science & technology 48, 6374–6382 (2014).
Zou, X., Shi, J. & Zhang, H. Coexistence of silver and titanium dioxide nanoparticles: enhancing or reducing environmental risks? Aquatic toxicology 154, 168–175 (2014).
El-Badawy, A., Feldhake, D. & Venkatapathy, R. State of the Science Literature Review: Everything Nanosilver and More. US Environmental Protection Agency. EPA/600/R–610/084 (2010).
Minetto, D., Libralato, G. & Volpi Ghirardini, A. Ecotoxicity of engineered TiO2 nanoparticles to saltwater organisms: an overview. Environment international 66, 18–27 (2014).
Klippstein, R. et al. Silver nanoparticles interactions with the immune system: implications for health and disease. In: Nanotechnology and Nanomaterials (ed Perez D ). Intech (2010).
Juan, L. et al. Deposition of silver nanoparticles on titanium surface for antibacterial effect. International journal of nanomedicine 5, 261–267 (2010).
Peng, B. et al. Study on the Thermal Treatment of Nano-Ag/TiO2 Thin Film. ISRN Nanotechnology 2011, Article ID 614243 (2011).
Yu, B. et al. Synthesis of Ag-TiO2 composite nano thin film for antimicrobial application. Nanotechnology 22, 115603 (2011).
Prasada, R. G. S. V. et al. Nanostructured TiO2 and TiO2-Ag Antimicrobial Thin Films. In: Nanoscience, Technology and Societal Implications (NSTSI), 2011 International Conference. IEEE (2011).
Chang, H. H. & Lo, S. J. Modification with a phosphorylation tag of PKA in the TraT-based display vector of Escherichia coli. J Biotechnol 78, 115–122 (2000).
Chang, H. J., Sheu, S. Y. & Lo, S. J. Expression of foreign antigens on the surface of Escherichia coli by fusion to the outer membrane protein traT. J Biomed Sci 6, 64–70 (1999).
Chang, H. H., Shih, K. N. & Lo, S. J. Receptor-mediated endocytosis as a selection force to enrich bacteria expressing rhodostomin on their surface. J Biomed Sci 7, 42–50 (2000).
Lin, L. et al. Uniform carbon-covered titania and its photocatalytic property. Journal of Molecular Catalysis A: Chemical 236, 46–53 (2005).
Zhang, H., Zong, R., Zhao, J. & Zhu, Y. Dramatic visible photocatalytic degradation performances due to synergetic effect of TiO2 with PANI. Environmental science & technology 42, 3803–3807 (2008).
Acknowledgements
This work was supported by Ministry of Science and Technology of Taiwan R.O.C. under grant no. 95-2314-B-320-009-MY3 and 102-2221-E-259-005-MY3 and Ministry of Economic Affairs of Taiwan R.O.C. under grant no. 98-EC-17-A-19-S2-0111.
Author information
Authors and Affiliations
Contributions
M.S.W., D.S.S. and H.H.C. conceived and designed the experiments. M.S.W., C.W.C., C.C.H. and S.C.H. performed the experiments. M.S.W. and H.H.C. analyzed the data. M.S.W. and H.H.C. wrote the main manuscript text. All authors reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Wong, MS., Chen, CW., Hsieh, CC. et al. Antibacterial property of Ag nanoparticle-impregnated N-doped titania films under visible light. Sci Rep 5, 11978 (2015). https://doi.org/10.1038/srep11978
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep11978
- Springer Nature Limited
This article is cited by
-
Synthesis of nanosize zinc oxide through aqueous sol–gel route in polyol medium
BMC Chemistry (2022)
-
Exposure to low levels of photocatalytic TiO2 nanoparticles enhances seed germination and seedling growth of amaranth and cruciferous vegetables
Scientific Reports (2022)
-
Targeting the molecular chaperone SlyD to inhibit bacterial growth with a small molecule
Scientific Reports (2017)
-
Potential of biosynthesized silver nanoparticles using Stenotrophomonas sp. BHU-S7 (MTCC 5978) for management of soil-borne and foliar phytopathogens
Scientific Reports (2017)
-
Soluble P-selectin rescues viper venom–induced mortality through anti-inflammatory properties and PSGL-1 pathway-mediated correction of hemostasis
Scientific Reports (2016)