Abstract
Integrating multiple properties in a single system is crucial for the continuous developments in electronic devices. However, some physical properties are mutually exclusive in nature. Here, we report the coexistence of two seemingly mutually exclusive properties-polarity and two-dimensional conductivity-in ferroelectric Ba0.2Sr0.8TiO3 thin films at the LaAlO3/Ba0.2Sr0.8TiO3 interface at room temperature. The polarity of a ∼3.2 nm Ba0.2Sr0.8TiO3 thin film is preserved with a two-dimensional mobile carrier density of ∼0.05 electron per unit cell. We show that the electronic reconstruction resulting from the competition between the built-in electric field of LaAlO3 and the polarization of Ba0.2Sr0.8TiO3 is responsible for this unusual two-dimensional conducting polar phase. The general concept of exploiting mutually exclusive properties at oxide interfaces via electronic reconstruction may be applicable to other strongly-correlated oxide interfaces, thus opening windows to new functional nanoscale materials for applications in novel nanoelectronics.
Similar content being viewed by others
Introduction
Oxide interfaces provide a fertile ground for multifunctional integration because the delicate balance between spin, orbit, charge, and lattice degrees of freedom in oxides can be easily destabilized with relatively small stimuli1,2,3,4. Ground-breaking examples are the coexistence of ferromagnetism and superconductivity at the LaAlO3/SrTiO3 (LAO/STO) interface although ferromagnetism is expected to destroy the pairing interaction responsible for superconductivity5,6, and the coexistence of ferromagnetism and ferroelectricity at Fe/BaTiO3 interface although ferroelectricity normally requires empty d orbitals while ferromagnetism is usually a result of partially filled d orbitals3,7. Recently, polar metals, which possess another pair of seemingly mutually exclusive properties, ferroelectric-like polarity and conductivity, has attracted a flurry of interest. Traditionally, it was considered that introducing itinerant electrons into a ferroelectric can eliminate ferroelectricity and associated polarity as the electrons screen the long-range Coulomb forces, which favor a polar structure8,9,10,11. However, recent first-principles calculations show that the charge rearrangements associated to electrostatic screening induces local lattice response, which favors polar distortions and that local off-centering can be sustained up to ~0.1 electron per unit cell (e/uc)11,12,13, suggesting that there is no fundamental incompatibility between metallicity and polar distortions.
In recent decades, the research on polar metals has been mainly on three routes: (i) searching for native polar metals, such as LiOsO314, Bi5Ti5O1715, Cd2Re2O716, and WTe217; (ii) doping charges into ferroelectric insulators, such as BaTiO3-δ10,11 and CaTiO3-δ12; and (iii) stabilizing a polar phase in an otherwise non-polar metal (NdNiO3) by deliberate geometric design18. However, most of the research was focused on bulk polar metals and the question of whether such coexistence can occur in a two-dimensional system remains largely unexplored. In this report, we directly show that polarity and two-dimensional electron gas (2DEG) can coexist in a single phase by charge transfer doping to a ferroelectric insulator.
A promising candidate to study this problem is the interface between a “polar” oxide (LAO) and a ferroelectric (Ba0.2Sr0.8TiO3). In essence, ferroelectricity arises from the charge separation between positive and negative ions, which create a spontaneous polarization and an internal electric field. Similar to the charge separation in ferroelectrics, in the “polar” oxide LAO, the physically separated alternating stacking of charge-positive (LaO)+ and charge-negative (AlO2)− layers also creates a built-in electric field. The possible charge transfer generated by the potential across LaAlO3/Ba0.2Sr0.8TiO3 (LAO/BST) interface created by the difference between the electric fields in LAO and BST can thus serve as a useful method to dope electrons into ferroelectric BST. This charge transfer is possible because the polar-discontinuity, which generates the 2DEG at the LAO/STO interface is also present at the LAO/BST interface as BST have a stacking of charge-neutral Ti4+O22− and Sr2+O2− (or Ba2+O2−) layers similar to that of STO19,20. We use ferroelectric BST thin films instead of the conventional BaTiO3 (BTO) used in previous studies10,11 as we found that the Coulomb forces in BTO strongly localize electrons (see Supplementary Note 1 for more details), while doping Sr in BTO is known to weaken the ferroelectricity and hence improving electron mobility.
Results
Ferroelectricity of BST thin films on conducting Nb-doped STO substrate
We first check the ferroelectricity of the BST thin films by performing hysteresis loops, domain writing and reading experiments on a 10 uc BST/Nb:STO (001) sample using piezoresponse force microscopy at room temperature (Fig. 1a). In its bulk form, the Curie temperature of BST is 105 K21. However, we find that the as-grown BST film is ferroelectric at room temperature in a single-domain state with a downward spontaneous polarization (pointing from BST to Nb:STO). This large Curie temperature enhancement is probably a result of strain22 and dimensional effects23. The 180° phase change between 4 and −7 V (Fig. 1b, c) and the good domain writing and reading with both positive and negative voltages (Fig. 1d, e) indicate robust ferroelectricity in the BST thin film.
Piezoresponse force microscopy characterization of a 10 unit cells of Ba0.2Sr0.8TiO3 thin film at room temperature. a Schematic diagram of the geometry for the piezoresponse force microscopy (PFM) setup, the red arrow indicates the as-grown polarization direction of Ba0.2Sr0.8TiO3 (BST). The Nb-doped SrTiO3 (Nb:STO, 0.1 wt% Nb doping) substrate is used as the bottom electrode. b Local PFM phase hysteresis loops and, c butterfly-like amplitude loops of the BST/Nb:STO sample, different colors stand for different voltage scans, the solid lines are guides for the eyes. d, e PFM amplitude (d) and phase (e) images (5 × 5 µm2) of the piezoelectric domains after application of −8 and 8 V tip bias to the 3 × 3 and 1 × 1 µm2 regions, respectively. Yellow region corresponds to as-grown downward polarization, purple region represents switched upward polarization. The same color between the as-grown 5 × 5 µm2 region and the central 1 × 1 µm2 region indicates that the as-grown BST has a downward polarization. The scale bars in d and e are 1 µm
The −1.5 V voltage shift in the phase and amplitude hysteresis loops is due to the well-known imprint effect as commonly observed in other ferroelectric thin films24,25,26. This could be collectively caused by the following mechanisms: (i) strain effect imposed on BST thin film by Nb:STO substrate24, (ii) asymmetric electrostatic boundary condition caused by the different work functions between the two electrodes25, (iii) defect dipole accumulation at the BST/Nb:STO interface due to interfacial diffusion of chemical species26. Note that in Fig. 1e, some partial relaxation is observed, which is attributed to polarization relaxation, as is commonly observed in other ferroelectric ultrathin films, such as BaTiO327.
Ferroelectricity modulated electronic transport properties of the 2DEG
Having observed room temperature ferroelectricity in BST thin film, we grew BST and LAO successively on atomically flat TiO2-terminated STO (001) substrates by pulsed laser deposition (PLD) to form a LAO/BST/STO heterostructure (see Supplementary Notes 2–4 for more details), where a 2DEG is observed at the LAO/BST interface. On one hand, the itinerant electrons introduced by the polar discontinuity at the LAO/BST interface tend to destroy the ferroelectricity and associated polarity of BST. On the other hand, the downward polarization of BST creates a downward electric field in LAO, which obstructs the polar-discontinuity-induced charge transfer from the LAO surface to the LAO/BST interface. The competition between the built-in electric field of LAO and the polarization of BST is exploited by varying the magnitude of the polarization of BST with different thicknesses. Figure 2 shows the electronic transport properties of a set of samples with fixed LAO thickness (15 uc) and different BST thicknesses. Figure 2a shows temperature-dependent sheet resistance (Rs–T) for these metallic samples. It should be noted that a single layer of BST with varying thicknesses deposited on STO substrate is insulating, indicating that a LAO layer is required to obtain conductivity in LAO/BST/STO heterostructure. Above 100 K, sheet resistance gradually increases with increasing BST thickness. However, a crossover in the Rs–T curves can be observed around 20–50 K and the sheet resistance dependence on BST thickness is reversed at low temperatures (2–20 K).
Electronic transport characterization of the two-dimensional electron gas in LaAlO3/Ba0.2Sr0.8TiO3/SrTiO3 heterostructure. a–c Temperature-dependent sheet resistance Rs (a), carrier density n (b), and mobility μ (c) for samples with fixed LaAlO3 thickness (15 unit cells) and different unit cells (uc) of Ba0.2Sr0.8TiO3 (BST) on SrTiO3 substrates. Different colors represent different BST thicknesses. The red arrows indicate increasing BST thickness. d A summary of the carrier density (at 300 and 2 K) and mobility (at 2 K) dependence on BST thickness from b and c
Carrier density gradually decreases with increasing BST thickness as the magnitude of the polarization increases (Fig. 2b)27. Another feature in Fig. 2b is that the temperature-dependent carrier density (n–T) curves become less temperature dependent with increasing BST thickness and finally turns into (nearly) temperature independent when BST exceeds 8 uc (see Supplementary Notes 5 and 6 for more details). The decreasing carrier density with decreasing temperature in STO is attributed to freeze-out of oxygen-vacancy-induced carriers20. The decreasing carrier density dependence on temperature indicates that the oxygen vacancies in our samples decrease with increasing BST thickness. This is confirmed by the decreasing photoluminescence (PL) intensity with increasing BST thickness in our PL measurements (see Supplementary Note 7 for more details), where the PL intensity is proportional to the oxygen vacancy concentration in STO. In addition, theoretical calculations show that under reducing conditions, the oxygen vacancy formation energy in ferroelectric BTO is higher than that in STO28. Hence, we conclude that the oxygen vacancy formation energy in ferroelectric BST is higher than that in paraelectric STO. When the BST thickness is below 8 uc, a 2DEG resides in both STO and BST, and a large number of oxygen-vacancy-induced carriers are present in STO. In this case, the decreasing carrier density with increasing BST thickness is a result of both the electric field effect and reduced oxygen vacancy concentration. When the BST thickness exceeds 8 uc, the 2DEG lies only in the BST and few oxygen-vacancy-induced carriers are present, leading to observation of temperature-independent carrier density. In this case, the transport properties are influenced only by the competition between the built-in electric field of LAO and the polarization of BST without the influence of oxygen vacancies, signifying the coexistence of polarity and the 2DEG above 8 uc of BST. The carrier density of the 8 uc sample is ~3 × 1013 cm−2, which corresponds to ~0.05 e/uc. Here, we estimate the thickness of the 2DEG to be 8 uc (~3.2 nm). This is in good agreement with previous observations, which showed that the thickness of the 2DEG at the LAO/STO interface is around 2–4 nm29,30. As discussed above, both carrier density and oxygen vacancies decrease with increasing BST thickness, leading to less electron–electron scattering and defect scattering, which consequently account for the mobility enhancement with increasing BST thickness (Fig. 2c, d).
We note the results in Fig. 2 are strikingly similar to the electric field gating experiments of LAO/STO interface31,32, suggesting that the 2DEG is modulated by the electric field provided by the ferroelectric BST. We also note that the upturn of the Rs–T curve and the corresponding decreasing carrier density with decreasing temperature of the 15 uc BST sample suggest carrier localization and is consistent with Mott variable-range hopping model (see Supplementary Note 8 for more details). This behavior could be due to the strong expulsion of electrons as the BST becomes thicker, as well as increasing interfacial disorder with increasing film thickness and strain effects introduced by substrate misfit as observed in epitaxial LAO/STO systems33.
Direct observation of the coexistence of polar displacements and 2DEG
We next turn to characterize the structural, elemental, and electronic features of a 15 uc LAO/10 uc BST/STO heterostructure with scanning transmission electron microscopy (STEM), coupled with electron energy loss spectroscopy (EELS). We detected the positions of A-site (A = La, Ba or Sr), B-site (B = Al or Ti), and oxygen atoms from the contrast-inverted annular-bright-field (ABF) STEM image (Fig. 3a, b and Supplementary Note 9). The BST layer shows a downward polarization, which is consistent with the as-grown BST thin film on Nb:STO (Fig. 1). The B-OII and A-OI displacements are largest at the LAO/BST interface with magnitudes as high as ~40 and 25 pm, respectively, which are comparable to the displacements of PbZr0.2Ti0.8O3 thin films on STO substrate34. The displacements gradually decrease into both LAO and STO and becomes negligibly small far away from the LAO/BST interface (Fig. 3c). The remnant displacement in LAO is probably due to BST diffusion into LAO (Fig. 4) and/or the buckling effect commonly observed in LAO/STO heterostructures35,36,37.
Structural, elemental, and electronic characterization of a LaAlO3/Ba0.2Sr0.8TiO3/SrTiO3heterostructure. a, b The heterostructure has 15 unit cells (uc) of LaAlO3 (LAO) and 10 unit cells of Ba0.2Sr0.8TiO3 (BST) on SrTiO3 (STO) substrate. Atomically resolved inverted annular-bright-field scanning transmission electron microscopy (ABF-STEM) images of the LAO/BST interface (a) and BST/STO interface (b), respectively. The orange dashed squares focus on regions which are representative unit cells of LAO, the LAO/BST interface, the BST/STO interface and STO, respectively, and are enlarged for clearer view. The brighter atomic columns in the corner are A-site (Sr, Ba, La) columns and the darker columns at/near the center are B-site (Ti, Al) columns. c Out-of-plane B-OII and A-OI displacements across the LAO/BST/STO heterostructure. d High-angle annular dark-field (HAADF) STEM image and electron energy loss spectroscopy (EELS) spectrum images of La M4,5 (yellow), Ba M4,5 (blue), Ti L2,3 (green), and O K (red) edges. BO2 layers are numbered from bottom to top. e Layer-resolved Ti L2,3 spectra. Reference spectra for Ti4+ (red) and Ti3+ (blue) are shown at the bottom, taken from SrTiO3 and Ti2O3/Al2O3, respectively. f Layer-resolved O K spectra, which are normalized by their respective main peaks near 535 eV. g Layer-resolved Ti3+ fraction (orange), which is defined as Ti3+/(Ti3+ + Ti4+), and ΔE from the O K edge (olive). The purple shaded area indicates the approximate location of the 2DEG. e–g are all aligned with the HAADF image and EELS spectra in d. The error bars show the standard deviations of the averaged measurements for each vertical atomic layer
First-principles calculations of the two-dimensional electron gas and polar displacements in LaAlO3/Ba0.5Sr0.5TiO3/SrTiO3 heterostructure. a Layer-resolved in-plane average charge density along the 〈001〉 direction. b Layer-resolved out-of-plane displacements of B-OII (red balls) and A-OI (green squares), respectively. c Structural guide of the supercell used in the calculations (only half of the structure used in the calculations is shown)
STEM-EELS spectrum imaging (Fig. 3d–g) was employed to reveal the layer-by-layer elemental distribution and electronic structure by tracing the Ti L2,3 (Fig. 3e) and O K (Fig. 3f) edges from the STO substrate to the top LAO layer. The BST/STO interface is atomically sharp, while some Ti diffusion (~1 uc) into the LAO layer at the LAO/BST interface is observed (Fig. 3d). The Ti valence evolution from STO and BST to the LAO/BST interface is clearly observed from the red-shift of the peak around 465 eV (Fig. 3e). In STO and BST regions far away from the LAO/BST interface, each Ti L2,3 curve is a typical Ti4+ spectrum, while around the LAO/BST interface, each Ti L2,3 curve is a mixture of Ti4+ and Ti3+ spectra. The layer-by-layer relative ratio Ti3+/(Ti3+ + Ti4+) grows gradually from BST to the LAO/BST interface and reaches ~0.2 at the interface (Fig. 3g), as evidenced via multiple linear least squares (MLLS) fitting of the experimental spectra (see Supplementary Note 10 for more details)38. Another way to trace the valence state of Ti is from the O K edge, which also shows significant changes when the Ti oxidation state changes across the interface (Fig. 3f)37. The energy difference between peak A and C (ΔE) has been recognized as an accurate indicator of valence change in perovskites37, the decrease of ΔE from BST to LAO/BST interface is evident in Fig. 3f–g and is related to a decrease in the Ti valence. These results unambiguously reflect a decrease of Ti valence from Ti4+ in BST to Ti3+ at the LAO/BST interface, indicating that the 2DEG lies at the LAO/BST interface and the carrier density of the 2DEG decreases away from the LAO/BST interface into the BST (Fig. 3g). The STEM and EELS results directly show that the polar displacements and Ti3+ (i.e. excess electrons) coexist at the LAO/BST interface in a single phase without any detectable phase separation.
First-principles calculations of the 2DEG and polar displacements in LaAlO3/Ba0.5Sr0.5TiO3/SrTiO3 heterostructure
In order to investigate the relation between the charge density and polarity in LAO/BST/STO heterostructure, we performed density-functional theory (DFT)-based calculations. The profile of the conducting electron density and the displacements between anions and cations for the whole LAO/BST/STO heterostructure are shown in Fig. 4. For simplicity, instead of using a LaAlO3/Ba0.2Sr0.8TiO3/SrTiO3 heterostructure as in the experiments, we used a LaAlO3/Ba0.5Sr0.5TiO3/SrTiO3 heterostructure.
Our first-principles calculations were performed using DFT-based Vienna ab initio Simulation Package (VASP)39,40 with the local density approximation (LDA) for the exchange-correlation functional41 and the frozen-core all-electron projector-augmented wave (PAW) method42,43. The cutoff energy for the plane wave expansion is set to 400 eV. Monkhorst-Pack k-point grids for Brillouin zone sampling are set to 6 × 6 × 6 for bulk SrTiO3, 6 × 6 × 6 for bulk LaAlO3, 5 × 5 × 6 for bulk Ba0.5Sr0.5TiO3, and 5 × 5 × 1 (10 × 10 × 1) for LaAlO3/Ba0.5Sr0.5TiO3/SrTiO3 superlattice structure relaxation (static calculations), respectively. The structures are fully relaxed until the forces are smaller than 0.01 eV Å−1 for the bulk LaAlO3, Ba0.5Sr0.5TiO3, SrTiO3, and 0.02 eV Å−1 for LaAlO3/Ba0.5Sr0.5TiO3/SrTiO3 superlattice structure. The equilibrium lattice constant for SrTiO3 is 3.865 Å. We fix the in-plane lattice constant of LaAlO3 and Ba0.5Sr0.5TiO3 to this number and optimize their c-axis into 3.66 and 3.96 Å, respectively. For Ba0.5Sr0.5TiO3, the ratio of Ba and Sr is set to 1:1. We use \(\sqrt 2 \times \sqrt 2 \times 1\) supercell for LaAlO3/Ba0.5Sr0.5TiO3/SrTiO3 superlattice, which is a symmetric structure with 4.5 uc SrTiO3 in the middle, 5 uc Ba0.5Sr0.5TiO3 on each of its two TiO2 terminals, and then 3.5 LaAlO3 on top of Ba0.5Sr0.5TiO3. The charge density is calculated by performing a partial charge calculation of the conduction bands below Fermi level.
The electrons mainly locate at Ti atoms in both Ba0.5Sr0.5TiO3 and SrTiO3 with the largest charge density at LaAlO3/Ba0.5Sr0.5TiO3 interface (0.21 e/uc), and decays gradually from this interface into SrTiO3 (Fig. 4a). This result agrees both qualitatively and quantitatively with the Ti3+ fraction analysis in Fig. 3f. The B-OII and A-OI displacements, which are in downward polarization (see Supplementary Note 11 for more details), are largest at the LaAlO3/Ba0.5Sr0.5TiO3 interface and gradually decreases into LaAlO3 and SrTiO3 (Fig. 4b). The trend of the calculated layer-dependent displacements well reproduces the STEM results in Fig. 3b. We note that the absolute values of the calculated displacements are around one half of those from experimental observations. This may be attributed to the underestimation of lattice constant and polarization by LDA functional, possible defects in the samples and/or measurement errors in STEM-extracted displacements. Figure 4c shows the structural guide of the supercell used in the calculations.
Discussion
Several mechanisms may contribute to the behavior of the layer-dependent displacements observed in Figs. 3 and 4: (a) A depolarizing buckling, which has been widely reported in LAO/STO heterostructure, could occur in BST to compensate the built-in electric field in LAO35,36,37. (b) Screening of the depolarization field of BST by the insulating SrTiO3 substrate. In an earlier report, Chisholm et al. reported that the depolarization field of PbZr0.2Ti0.8O3 in PbZr0.2Ti0.8O3/SrTiO3 heterostructure could be screened by oxygen vacancies in SrTiO334. This screening mechanism could also lead to diminishing displacement in the first few layers of BST away from BST/STO interface. (c) Screening of ferroelectricity by itinerant electrons. As proposed by Wang et al. the critical electron density for stable polar displacement in BaTiO3 is 0.11 e/uc11. Here, we observed large Ti–O displacement (0.17 Å) at the LaAlO3/Ba0.5Sr0.5TiO3 interface with an electron density ~0.21 e/uc in Fig. 4. The discrepancy between our results and those reported by Wang et al. may be attributed to the substrate-imposed compressive strain, which has been reported to be a useful way to increase the critical electron density in BTO44. We also note that the carrier density calculated from DFT and that extracted from EELS measurement are larger than the experimental observations (0.05 e/uc). This is probably because that some of the charges are localized in the first few layers of BST at LAO/BST interface as commonly observed at LAO/STO interface29,30. To disentangle these inter-correlated mechanisms, more detailed experimental and theoretical work needs to be done. Nevertheless, the overall effect in Figs. 3 and 4 clearly suggests the coexistence of 2DEG and polarity in a single phase.
Our discoveries demonstrate a route to create a two-dimensional polar metal at oxide interface through interfacial electronic reconstruction, which is achieved by deliberately engineering the competition of the electric fields between a ferroelectric and a “polar” oxide. As coexistence of ferromagnetism and superconductivity has already been demonstrated at the LAO/STO interface5,6, the integration of polarity further expands the functionality of this interface and offers new opportunities for future multifunctional devices. Moreover, the ferroelectric soft phonons could be utilized to stabilize the superconducting phase at elevated temperatures45. We notice that during the review process of our work, a similar work by Cao et al. reported the coexistence of polarity and 2DEG in a tri-color BaTiO3/SrTiO3/LaTiO3 heterostructure and we highly recommend this work to the readers of our work46. Finally, we note that a recent publication reported an electrically switchable ferroelectric topological semimetal WTe217. Nevertheless, the switchability remains elusive in doped complex-oxide-based ferroelectrics, despite a previous theoretical report proposed a promising candidate Bi5Ti5O1715.
Methods
Sample preparation
The samples were grown by PLD equipped with in situ reflection high-energy electron diffraction (RHEED). BST layer and LAO layer were successively deposited on atomically flat TiO2-terminated STO (001) substrates at 760 °C and an oxygen pressure of 10–4 Torr. During the deposition, a KrF laser with a wavelength of 248 nm was used. The laser repetition was 1 Hz and the laser energy density was 1.5 J/cm2. The 10 uc BST/Nb:STO (0.1 wt% Nb doped) sample was prepared under the same conditions except that no LAO was deposited. To obtain TiO2-terminated surface, STO and Nb:STO substrates were treated with buffered hydrofluoric acid for 30 s followed by annealing at 950 °C for 1.5 h in air47.
Piezoresponse force microscopy
Ferroelectric properties were measured using piezoresponse force microscope (PFM) and piezoresponse force spectroscopy (PFS) techniques. In this study, a commercial SPM system (MFP-3D, Asylum Research 13.03.70, USA) was used, which was controlled by a commercial software (IGOR PRO 6.34A). In the PFM measurements, amplitude (A) and phase (ϕ) images can be obtained simultaneously by applying an AC bias to the tip. The applied AC bias was 0.2 V. The amplitude image refers to piezoresponse of the material, whereas the phase image regards to the polarization direction of the material. Before the PFM measurements, DC writing processes were conducted. In these processes, dc biases of −8/8 V were sequentially applied to the conductive tip. The corresponding written areas were 3 × 3 and 1 × 1 µm2, respectively. In the PFS measurement, the PFM was operated in the spectroscopy mode, the tip with a triangle–square waveform was fixed at a certain location. The frequency of the used waveform was 200 mHz, i.e., the bias-on and bias-off time was 25 ms. To exclude the electrostatic effect, the used phase hysteresis loops, ϕ(E) and amplitude loops A(E) here were obtained at bias-off state. In all the measurements, the scan rate was 1 Hz and the bottom electrode of the sample was grounded (Fig. 1a). A commercial Pt-coated Si tip (AC240TM, Olympus, Japan) with a radius of 15 nm was used in these measurements. The average spring constant is about 2 N/m, and the average resonance frequency is about 65 kHz.
Electronic transport measurements
All the electronic transport measurements (sheet resistance, carrier density, and mobility) were performed in a Van der Pauw geometry with a quantum design physical property measurement system (PPMS). The contacts of the samples were made with an aluminum wire-bonder.
Scanning transmission electron microscopy
STEM and EELS studies were conducted using a JEOL ARM200F atomic resolution analytical electron microscope equipped with a cold field-emission gun and a new ASCOR fifth-order aberration corrector and Gatan quantum ER spectrometer.
Data availability
The data that support the findings of this study are available from the corresponding author on request.
References
Tsymbal, E. Y., Dagotto, E. R. A., Eom, C. B., & Ramesh, R. Multifunctional Oxide Heterostructures (Oxford University Press, 2012).
Zubko, P., Gariglio, S., Gabay, M., Ghosez, P. & Triscone, J.-M. Interface physics in complex oxide heterostructures. Annu. Rev. Condens. Matter Phys. 2, 141–165 (2011).
Ramesh, R. & Spaldin, N. A. Multiferroics: progress and prospects in thin films. Nat. Mater. 6, 21–29 (2007).
Salje, E. K. H. Multiferroic domain boundaries as active memory devices: trajectories towards domain boundary engineering. ChemPhysChem 11, 940–950 (2010).
Li, L., Richter, C., Mannhart, J. & Ashoori, R. C. Coexistence of magnetic order and two-dimensional superconductivity at LaAlO3/SrTiO3 interfaces. Nat. Phys. 7, 762–766 (2011).
Bert, J. A. et al. Direct imaging of the coexistence of ferromagnetism and superconductivity at the LaAlO3/SrTiO3 interface. Nat. Phys. 7, 767–771 (2011).
Valencia, S. et al. Interface-induced room-temperature multiferroicity in BaTiO3. Nat. Mater. 10, 753–758 (2011).
Dawber, M., Rabe, K. M. & Scott, J. F. Physics of thin-film ferroelectric oxides. Rev. Mod. Phys. 77, 1083–1130 (2005).
Cohen, R. E. Origin of ferroelectricity in perovskite oxides. Nature 358, 136–138 (1992).
Kolodiazhnyi, T., Tachibana, M., Kawaji, H., Hwang, J. & Takayama-Muromachi, E. Persistence of ferroelectricity in BaTiO3 through the insulator–metal transition. Phys. Rev. Lett. 104, 147602 (2010).
Wang, Y., Liu, X., Burton, J. D., Jaswal, S. S. & Tsymbal, E. Y. Ferroelectric instability under screened Coulomb interactions. Phys. Rev. Lett. 109, 247601 (2012).
Benedek, N. A. & Birol, T. Ferroelectric metals reexamined: fundamental mechanisms and design considerations for new materials. J. Mater. Chem. C 4, 4000–4015 (2016).
Zhao, H. J. et al. Meta-screening and permanence of polar distortion in metallized ferroelectrics. Phys. Rev. B 97, 054107 (2018).
Shi, Y. et al. A ferroelectric-like structural transition in a metal. Nat. Mater. 12, 1024–1027 (2013).
Filippetti, A., Fiorentini, V., Ricci, F., Delugas, P. & Íñiguez, J. Prediction of a native ferroelectric metal. Nat. Commun. 7, 11211 (2016).
Sergienko, I. A. et al. Metallic “Ferroelectricity” in the pyrochlore Cd2Re2O7. Phys. Rev. Lett. 92, 065501 (2004).
Fei, Z. et al. Ferroelectric switching of a two-dimensional metal. Nature 560, 336–339 (2018).
Kim, T. H. et al. Polar metals by geometric design. Nature 533, 68–72 (2016).
Ohtomo, A. & Hwang, H. Y. A high-mobility electron gas at the LaAlO3/SrTiO3 heterointerface. Nature 427, 423–426 (2004).
Liu, Z. Q. et al. Origin of the two-dimensional electron gas at LaAlO3/SrTiO3 interfaces: the role of oxygen vacancies and electronic reconstruction. Phys. Rev. X 3, 021010 (2013).
Kumar, A., Naithani, U. C. & Semwal, B. S. Specific heat of BaxSr1-xTiO3 ferroelectric perovskites. Br. Ceram. Trans. 103, 153–157 (2004).
Haeni, J. H. et al. Room-temperature ferroelectricity in strained SrTiO3. Nature 430, 758–761 (2004).
Lee, D. et al. Emergence of room-temperature ferroelectricity at reduced dimensions. Science 349, 1314–1317 (2015).
Zhou, Y., Chan, H. K., Lam, C. H. & Shin, F. G. Mechanisms of imprint effect on ferroelectric thin films. J. Appl. Phys. 98, 024111 (2005).
Liu, F., Fina, I., Bertacco, R. & Fontcuberta, J. Unravelling and controlling hidden imprint fields in ferroelectric capacitors. Sci. Rep. 6, 25028 (2016).
Barrionuevo, D. et al. Tunneling electroresistance in multiferroic heterostructures. Nanotechnology 25, 495203 (2014).
Kim, D. J. et al. Polarization relaxation induced by a depolarization field in ultrathin ferroelectric BaTiO3 capacitors. Phys. Rev. Lett. 95, 237602 (2005).
Lee, H. S., Mizoguchi, T., Yamamoto, T., Kang, S. J. L. & Ikuhara, Y. First-principles calculation of defect energetics in cubic-BaTiO3 and a comparison with SrTiO3. Acta Mater. 55, 6535–6540 (2007).
Delugas, P. et al. Spontaneous 2-dimensional carrier confinement at the n-type SrTiO3/LaAlO3 interface. Phys. Rev. Lett. 106, 166807 (2011).
Dubroka, A. et al. Dynamical response and confinement of the electrons at the LaAlO3/SrTiO3 interface. Phys. Rev. Lett. 104, 156807 (2010).
Bell, C. et al. Dominant mobility modulation by the electric field effect at the LaAlO3/SrTiO3 interface. Phys. Rev. Lett. 103, 226802 (2009).
Zeng, S. et al. Liquid-gated high mobility and quantum oscillation of the two-dimensional electron gas at an oxide interface. ACS Nano 10, 4532–4537 (2016).
Hernandez, T. et al. Localization of two-dimensional electron gas in LaAlO3/SrTiO3 heterostructures. Phys. Rev. B 85, 161407(R) (2012).
Chisholm, M. F., Luo, W., Oxley, M. P., Pantelides, S. T. & Lee, H. N. Atomic-scale compensation phenomena at polar interfaces. Phys. Rev. Lett. 105, 197602 (2010).
Pentcheva, R. & Pickett, W. E. Avoiding the polarization catastrophe in LaAlO3 overlayers on SrTiO3(001) through polar distortion. Phys. Rev. Lett. 102, 107602 (2009).
Pauli, S. A. et al. Evolution of the interfacial structure of LaAlO3 on SrTiO3. Phys. Rev. Lett. 106, 036101 (2011).
Cantoni, C. et al. Electron transfer and ionic displacements at the origin of the 2D electron gas at the LAO/STO interface: direct measurements with atomic-column spatial resolution. Adv. Mater. 24, 3952–3957 (2012).
Ohtomo, A., Muller, D. A., Grazul, J. L. & Hwang, H. Y. Artificial charge-modulationin atomic-scale perovskite titanate superlattices. Nature 419, 378–380 (2002).
Kresse, G. & Hafner, J. Ab initio molecular-dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Kresse, G. & Hafner, J. Ab initio molecular-dynamics simulation of the liquid-metal–amorphous-semiconductor transition in germanium. Phys. Rev. B 49, 14251–14269 (1994).
Perdew, J. P. & Zunger, A. Self-interaction correction to density-functional approximations for many-electron systems. Phys. Rev. B 23, 5048–5079 (1981).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Blochl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Ma, C., Jin, K., Ge, C. & Yang, G. Strain-engineering stabilization of BaTiO3-based polar metals. Phys. Rev. B 97, 115103 (2018).
Yildirim, T. Ferroelectric soft phonons, charge density wave instability, and strong electron–phonon coupling in BiS2 layered superconductors: a first-principles study. Phys. Rev. B 87, 020506 (2013).
Cao, Y. et al. Artificial two-dimensional polar metal at room temperature. Nat. Commun. 9, 1547 (2018).
Kawasaki, M. et al. Atomic control of the SrTiO3 crystal surface. Science 266, 1540–1542 (1994).
Acknowledgements
This work is supported by the National University of Singapore (NUS) Academic Research Fund (AcRF Tier 1 Grant Nos. R-144-000-403-114 and R-144-000-391-114) and the Singapore National Research Foundation (NRF) under the Competitive Research Programs (CRP Awards Nos. NRF-CRP15-2015-01 and NRF-CRP10-2012-02). A. A. would like to thank the Agency for Science, Technology and Research (A*STAR) under its Advanced Manufacturing and Engineering (AME) Individual Research Grant (IRG) (A1983c0034) for the financial support. C.J. Li acknowledges the financial support from Singapore Ministry of Education Academic Research Fund Tier 1 (R-284-000-158-114). S.J.P. thanks Singapore Ministry of Education under its Tier 2 Grant (MOE2017-T2-1-129).
Author information
Authors and Affiliations
Contributions
W.X.Z. and A.A. conceived and designed the project. W.X.Z. and S.W.Z. prepared the samples and performed the electronic transport measurements. H.J.W., Y.Z., C.J.L. and M.S.L. performed the scanning transmission electron microscopy measurements and analysis under the supervision of S.J.P. J.Z. performed the first-principles calculations under the supervision of Y.P.F. J.X.X., R.G. and H.W. performed the piezoresponse force microscopy measurements and analysis under the supervision of K.Y.Z. and J.S.C. C.G.L. performed the photoluminescence measurements and analysis under the supervision of S.J.C. P.Y. and W.X.Z. performed the X-ray diffraction measurements and analysis. C.J.L., S.W.Z., Z.H., W.M.L., K.H., Z.S.L. and T.V. discussed the results of the project. W.X.Z., C.J.L. and A.A. prepared the manuscript. All authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhou, W.X., Wu, H.J., Zhou, J. et al. Artificial two-dimensional polar metal by charge transfer to a ferroelectric insulator. Commun Phys 2, 125 (2019). https://doi.org/10.1038/s42005-019-0227-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s42005-019-0227-4
- Springer Nature Limited
This article is cited by
-
Quantum fluctuation of ferroelectric order in polar metals
npj Quantum Materials (2023)
-
Nonvolatile ferroelectric domain wall memory integrated on silicon
Nature Communications (2022)
-
Spectral weight reduction of two-dimensional electron gases at oxide surfaces across the ferroelectric transition
Scientific Reports (2020)