Abstract
In this study, gold-reduced graphene oxide (Au@rGO) nanocomposite has been synthesized by repurposing electronic waste and dry batteries. This innovative approach involved utilizing the graphite rod from dry batteries to produce reduced graphene oxide (rGO), which was subsequently modified through the incorporation of gold nanoparticles obtained from recycled electronic waste. This methodology marks a significant breakthrough in electronic waste recycling, presenting a cost-effective and sustainable means of creating novel nanocomposites for applications in photocatalysis and adsorption, particularly in the removal of crystal violet (CV) from aqueous media. The synthesized Au@rGO nanocomposite was characterized using X-ray diffraction, scanning electron microscopy, energy dispersed X-ray, and N2 adsorption/desorption. Parameters that affect the adsorption and photocatalytic degradation of CV dye have been studied in detail. The optimal conditions for CV adsorption and photocatalytic degradation were pH of 10, equilibrium time of 30 min, CV concentration of 10 mg/L and adsorbent dosage of 40 mg. Furthermore, the isotherm and kinetics of CV removal were also studied. The removal of CV dye using adsorption and photocatalytic degradation techniques reached 95% and 99%, respectively. Consequently, the results showed that photocatalytic degradation of CV dye onto the mesoporous Au@rGO nanocomposite is more proper way than the adsorption technique for removing the CV dye from aqueous media. The designed photocatalyst has high efficiency and it can be reused and activated several times so it can be used in real water treatment applications.
Similar content being viewed by others
Introduction
Recently, carbon material has gained significant attention from scientists and researchers due to its unique composition and characteristics1,2,3. One of the carbon compounds that has garnered particular interest is graphene, which is a single-layer graphite consisting of one-atom-thick hexagonal rings of SP2 hybridized carbon atoms4. Graphene sheets exhibit exceptional properties such as high thermal conductivity, electrical conductivity (5000 W/m K), and other interesting transport phenomena like the quantum Hall effect for each layer5,6. The remarkable features of graphene have led to numerous applications in various fields7,8. Graphene-based technologies have been employed in sensors, field emission devices, batteries, supercapacitors, membrane design, water desalination, and catalysis9,10,11.
One of main challenges in advanced nanocomposites manufacturing is the high cost. Therefore, finding low-cost precursors for these materials’ preparation is quite a promising approach from economic and environmental aspects12,13. Graphene could be obtained from zero-cost precursors such as graphite rod of the spent dry batteries. Furthermore, electronic waste (EW) accumulation has reached alarming levels, with approximately 25–40 million tons generated annually14. Improper disposal methods, including crushing, burying, or burning EW, have led to environmental pollution due to the release of hazardous components15,16,17,18. Innovative approaches are being developed to recycle EW and recover valuable components to combat this issue. Consequently, the global initiative to recycle EW, particularly computer parts like random access memory (RAM), aims to extract precious metals such as gold, silver, gallium, copper, platinum, tantalum, palladium, tellurium, germanium, and selenium19,20,21.
Among the various types of EW, computers, including laptops and desktops, contain essential hardware components such as a motherboard, central processing unit, RAM, hard drive, power supply unit, and expansion cards22. Given the significant annual production of computers globally, EW is expected to increase significantly.
Water purification has emerged as a critical humanitarian objective and has gained substantial research attention23,24,25,26. Industrial wastewater, containing various toxic organic compounds, has become a major environmental concern27,28,29,30. Industries such as leather, paper, plastics, printing, electroplating, and cosmetics contribute to the contamination of water sources with organic pollutants. Dye manufacturing produces a large number of toxic dyes like hetero polyaromatic, anthraquinone, and xanthinic dyes, which are difficult to remove from polluted water due to their high molecular weight24,31,32,33. These pollutants pose potential dangers to human health, including the risk of severe diseases like cancer. Therefore, effective separation of toxic dyes from industrial influent water is crucial before disposal into the environment. One commonly encountered cationic dye is crystal violet (CV), which is extensively used in the textiles, cosmetics, paper, printing, and leather industries34. Efforts have been made to decontaminate water through various methods such as filtration, electrochemical processes, precipitation, coagulation, and adsorption. Photocatalysis, an advanced oxidation process, has gained popularity in recent years due to its high efficiency, low cost, and absence of secondary toxic contaminants35,36,37,38,39,40. This process utilizes suitable catalysts and UV or sunlight to generate electrons and holes, which initiate oxidation–reduction reactions that degrade organic compounds on the catalyst's surface41,42. Photocatalytic degradation has shown promise as an eco-friendly and cost-effective method for treating wastewater, including the removal of CV dye43,44,45,46.
In this study, the mesoporous Au@rGO nanocomposite is prepared from waste precursors (graphite rod of spent dry battery and EW). In addition, the Au@rGO nanocomposite is used for the adsorption and photocatalytic degradation of CV dye in aqueous solutions.
Experimental
Chemicals
The chemicals used in this study were of a high purity grade and were not further purified. Sulfuric acid, orthophosphoric acid, nitric acid, hydrogen peroxide, potassium permanganate, glycerol, polyvinyl pyrrolidone (PVP), and CV were purchased from Sigma Aldrich Ltd. USA. Ethanol and hydrochloric acid were purchased from Merck, Germany. EW, RAM, and dry cell battery waste were collected from local shops.
Characterization tools
The phase and structure of Au@rGO nanocomposite were verified using X-ray diffraction (XRD, Philips PW1700 diffractometer, Netherlands) with Cu-Kα radiation (λ = 1.541 Å). The scanning electron microscopy (SEM) analysis of the synthesized Au@rGO was conducted using a Carl Zeiss Sigma (500 VP and JSM5400 LV, Germany) to observe its surface morphology, equipped with energy dispersed X-ray (EDX). The surface area and porosity of Au@rGO were explored using N2 adsorption–desorption isotherms that was recorded using Quantachrom (Model Nova 3200, USA) at 77 K.
Preparation of reduced graphene oxide from dry cell battery by modified Hummer method
Graphene oxide (GO) and reduced graphene oxide (rGO) were synthesized from graphite powder obtained from waste dry cell batteries. The graphite powder was first washed with water to remove impurities. The powder was then ground and crushed to obtain fine graphite powder. However, some inorganic materials remained in the powder, so it was treated with a mixture of hydrochloric acid and nitric acid (3:1) for 4 h. The mixture was then centrifuged and washed with distilled water until the pH reached neutrality. The recovered graphite powder was then dried at 60 ºC for 24 h. In a beaker, 270 mL of sulfuric acid was mixed with 30 mL of phosphoric acid (9:1), followed by stirring with 2.25 g of graphite powder. Then, 13.2 g of potassium permanganate was slowly added while stirring for 10 h until the color turned dark green. After that, 6.7 mL of hydrogen peroxide was added drop by drop over 10 min under stirring. The mixture was cooled for 30 min and then treated with 100 mL of hydrochloric acid and 300 mL of deionized water. Centrifugation was performed, and subsequent washes with distilled water were carried out. Finally, the sample was dried at 80 ºC for 24 h. To convert it into rGO, the dried sample was subjected to hydrothermal treatment at 150 ºC for 18 h47,48,49,50.
Preparation of gold nanoparticles from electronic waste
The spent RAM was collected from EW collection stores, then pins were cut using scissors. Around 50 g of pins were added to a beaker containing 60 mL of nitric acid and 60 mL of deionized water (1:1) on a hot plate for 2 h at 150 ºC. This process facilitated the extraction of gold from the chips. Then, 0.18 g of Au chips was dissolved in 16 mL of aqua regia solution, which is a mixture of concentrated HNO3 and concentrated HCl in a ratio of 1:3. The gold solution was mixed with 0.115 g of PVP and 45 g of glycerol. The mixture was stirred for 1 h at 100 ºC, followed by centrifugation, washing, and then dispersed in 20 mL H2O to obtain gold nanoparticles suspension solution51 (Fig. 1).
Preparation of Au@rGO nanocomposite
A solution of 20 mL of gold nanoparticles (9.5 mg/mL) was mixed with 0.44 g of rGO and stirred for 45 min. The mixture was then subjected to hydrothermal treatment at 150 ºC for 18 h. Afterwards, it was washed with deionized water and dried at 80 ºC for 24 h.
Batch-adsorption and photocatalytic degradation of CV dye
Lab experiments were conducted to assess the adsorption capacity of materials for CV pollutants. Controlled conditions were maintained while conducting these experiments, where CV was adsorbed onto the materials. Furthermore, the efficiency of the Au@rGO for photocatalytic degradation of CV dye was observed using sunlight and examined extensively. A typical experiment was performed by adding 25 mg of Au@rGO photocatalyst to 25 mL with a concentration of 10 mg/L of CV dye. The mixture was then stirred magnetically at 70 rpm. Afterwards, the mixture of CV dye and the synthesized nanocomposite was rapidly centrifuged to eliminate the used Au@rGO. To ensure adsorption equilibrium between the CV molecules and Au@rGO, the mixture of CV Au@rGO was agitated in a dark room before exposure to sunlight for 30 min. A UV–Vis spectrophotometer was used to evaluate the supernatant resulting from centrifugation, which included the CV dye solution. The absorbance was measured using a quartz cuvette at a UV wavelength of 580 nm that was used as λmax. The removal efficiency (%) and the adsorption capacity (mg/g) of CV dye using the designed sorbent was calculated according to Eqs. 1 and 2, respectively52.
To assess the reduction of CV dye from an aqueous solution by adsorption and photocatalytic degradation, measurements were taken for the initial and final CV absorbance (Ai and Af). Additionally, the initial and final CV concentrations (Ci and Cf) were determined. The volume of the CV solution (V) and the mass of Au@rGO (m) were also recorded. The intensity of incident sunlight was monitored at 30-min intervals using a Lutron LX-101 digital meter. The measured sunlight intensity ranged from approximately 185 × 102 to 190 × 102 lx. The experimental setup involved magnetic stirring of the mixture under direct sunlight between 11:00 AM and 3:00 PM on sunny days when the temperature was around 25 ± 2 °C. Various factors, including the quantity of adsorbent, duration, pH level, etc., were investigated to evaluate the efficacy of CV removal from the aqueous solution under different conditions. Subsequently, the optimal conditions for CV removal were determined.
Results and discussion
Au@rGO nanocomposite characterizations
X-ray powder diffraction
Figure 2 reveals that the XRD patterns of the rGO and Au@rGO nanocomposite are well-matched with the carbon and gold structure. In fact, no change was noticed in the previously prepared rGO structure53. The broad peak that characterize rGO at 25.81° is attributed to (002) plane 10. Diffraction peaks at 2θ° of 38.55°, 44.58°, 65.29° and 77.86° are assigned to the (111), (200), (220) and (311) diffraction planes, respectively, of the pure face-centered cubic (fcc) Au nanostructure. The obtained XRD data refer to the Au@rGO is synthesized successfully and Au particles are embedded in the rGO surface54.
Scanning electron microscopy and energy dispersed X-ray analyses
Due to its higher magnification, greater depth of focus, and ease of observing samples, the SEM was considered one of the most utilized devices in scientific research scope. Figure 3a–d demonstrates the SEM images of the synthesized Au@rGO nanocomposite at different magnifications. The figures clearly show the rGO layers had been synthesized successfully. Moreover, they demonstrate the gold nanoparticles and homogeneously distributed on the rGO surface.
Figure 3e,f displays the EDX spectra of the rGO and Au@rGO nanocomposite, respectively prepared by the hydrothermal method. The strong peak in EDX analysis at about 0.3 keV and small peak at around 0.5 keV are characterized by the carbon and oxygen, respectively, of rGO (Fig. 3e). While three peaks appeared in Fig. 3f, at about 2.23, 9.75 and 11.7 keV are attributed to the Au nanoparticles with weight ratio of 7.9%55. These results confirmed the formation of Au@rGO nanocomposite and Au nanoparticles were distributed on the rGO surface.
N2 adsorption/desorption study
The N2 adsorption/desorption isotherms Au@rGO are shown in Fig. 4 and the pore size distributions are displayed in the inset of the synthesized materials. The isotherm type was found to be type IV curves with hysteresis loops, demonstrating the mesoporous structure of the designed Au@rGO nanocomposites56. The pore size distributions for rGO and Au@rGO nanocomposite exhibit pore sizes ranging from 2 to 3 nm for rGO and from 2 to 4 nm for Au@rGO nanocomposite. It also shows that Au@rGO nanocomposite has a larger pore size and volume, which may be due to the appearance of more pores on the surface of the rGO. Consequently, these mesopores serve a vital function in increasing the adsorption efficiency during CV dye adsorption on the surface of Au@rGO sorbent. The specific surface areas of rGO and Au@rGO are 29.34 and 69.8 m2/g, respectively (calculated according to the details reported elsewhere57), and these data agree with the previous data that have been reported10.
Optimization of adsorption and photocatalytic degradation processes
Effect of pH
The pH of the solution has a significant impact on the surface charge of Au@rGO nanocomposite, which in turn affects the efficiency of CV adsorption and photocatalytic degradation. To investigate this effect, experiments were conducted at an adsorbent dose of 40 mg, CV concentration of 10 mg/L, and a solution volume of 40 mL under sunlight and room temperature. The results, shown in Fig. 5a, indicate that the efficiency of CV adsorption and photocatalytic degradation is limited to low pH values. This is because the surface of the Au@rGO nanocomposite is positively charged at low pH values, which reveals the positively charged CV molecules. As the pH of the solution increases, the surface of Au@rGO nanocomposite becomes more negatively charged, which attracts the positively charged CV molecules. This leads to an increase in the adsorption of CV molecules onto the surface of Au@rGO nanocomposite, hence, increasing its efficiency in the removal of CV from aqueous solutions. At alkaline pH values, CV removal efficiency using Au@rGO nanocomposite improves significantly. This is because the Au@rGO nanocomposite attracts CV molecules, which then undergo photocatalytic degradation under sunlight. At a pH of 10, the adsorption process exhibited removal of the CV dye efficiency of 95% approximately, while the photocatalytic degradation displayed removal efficiencies of about 99% for the CV. The improved performance observed at higher pH levels can be attributed to the presence of negative charges on the external surface-active sites of the Au@rGO nanocomposite. As CV is a cationic dye, it acquires a positive charge when dissolved in distilled water. Consequently, the interaction between the function groups with a positive charge of CV ions and the sites that have a negative charge of the Au@rGO nanocomposite adsorption catalyst becomes more pronounced at higher pH values. This enhanced interaction leads to greater rates of both adsorption and photocatalytic degradation of CV, resulting in higher removal efficiencies58.
Effect of adsorbent dose
Moreover, the amount of adsorbent also plays an important role in the efficiency of adsorption and photocatalytic destruction of various organic toxins59,60,61,62. It has a direct impact on the accessibility of surface-active sites for the entrapment of pollutants, thereby influencing the extent of color removal. To investigate this phenomenon, the effect of varying adsorbent doses ranging from 10 to 150 mg was examined on the adsorption and photocatalytic degradation of CV. Other variables such as solution volume, CV dye initial concentration, pH value of the solution, temperature, and contact duration were kept constant. The results in Fig. 5b demonstrated that increasing the quantity of adsorbent from 10 to 150 mg led to the increasing decolourization of CV contaminants. This enhancement can be attributed to the larger surface area and a greater number of active sites provided by the higher dosage of the adsorbent, resulting in improved entrapment of CV molecules. Therefore, an optimal adsorbent dose of 40 mg was determined for the removal of CV, exhibiting approximately 95% efficiency through adsorption and 99% efficiency through photocatalytic degradation63.
Effect of contact irradiation time
The contact irradiation time has a significant impact on the efficiency of CV adsorption and photocatalytic degradation on Au@rGO nanocomposites. This is because the contact irradiation time between the designed photocatalyst and CV dye affects the saturation state of the surface of the synthesized Au@rGO. As the contact time increases, the surface of the Au@rGO nanocomposite becomes more saturated with CV adsorbate, which leads to increased adsorption and photocatalytic degradation rates. The results shown in Fig. 5c demonstrate the influence of contact irradiation time on CV removal efficiency. The experiments were conducted by mixing 40 mg of adsorbent with 40 mL of 10 mg/L of CV dye solution under sunlight irradiation, 25 °C and a pH of 10. As contact irradiation time increased, both the adsorption and photocatalytic degradation of CV showed enhanced efficiency. Within 30 min, 95% of CV was removed through adsorption, while 99% was removed through photocatalytic degradation. Based on these findings, a contact irradiation time of 30 min was determined as the optimum condition for both methods64.
Effect of initial concentration on the dye adsorption and photocatalytic degradation
The effect of the initial concentration of CV was examined by varying the concentration from 1 to 100 mg/L, while keeping other factors constant, such as pH 10, adsorbent dose of 40 mg, and room temperature. The influence of the initial concentration of CV dye on its adsorption and photocatalytic degradation using Au@rGO nanocomposite was investigated, as depicted in Fig. 6. The adsorption process involved adding 40 mg of Au@rGO nanocomposite to 25 mL of CV solution with various concentrations of CV dye (ranging from 1 to 10 mg/L). The experimental conditions remained constant, with a pH value of 10 and a stirring rate of 70 rpm. Figure 6a illustrates that increasing the initial CV concentration enhances the adsorption capacity of CV dye on the Au@rGO nanocomposite until it reaches equilibrium (maximum adsorption). Based on the data obtained from Fig. 6a, the actual quantity of CV absorbed utilizing the Au@rGO adsorbent was approximately 50 mg/g. This can be attributed to the fact that higher CV concentrations result in shorter photon path lengths through the solution and coverage of active surface sites on the Au@rGO nanocomposite.
On the other hand, the catalytic photocatalytic degradation of CV dye was achieved by introducing 25 mg of Au@rGO nanocomposite into 25 mL of CV solution and stirring it at 70 rpm for 30 min in a closed dark reactor. The concentration of CV dye was adjusted as shown in Fig. 6b. The results indicate that increasing the CV concentration from 1 to 5 mg/L leads to a significant decrease in the effectiveness of CV dye degradation. This phenomenon can be attributed to the increased number of CV molecules occupying the surface-active sites of the synthesized Au@rGO nanocomposite, thereby reducing the diffusion and penetration of radiation to these sites57,65. As a result, there is a decrease in light absorption by the Au@rGO, leading to a reduction in the generation of electron–hole pairs and ultimately lowering the percentage of CV photocatalytic degradation66. Therefore, an optimized concentration for CV dye solution using a mesoporous Au@rGO nanocomposite is 10 mg/L or less67.
Adsorption isotherms study
Investigation of the adsorption isotherm of CV dye on Au@rGO nanocomposite provides insights into the interactions between CV molecules and the adsorbent. To investigate the correlation between the equilibrium concentration (Ce) of CV and the adsorption capacity (qe) of Au@rGO nanocomposite, various concentrations of CV were employed under optimal adsorption conditions. Two commonly used adsorption isotherm models, Langmuir and Freundlich, were employed to understand the mechanism of CV adsorption. According to the Langmuir isotherm model, CV molecules adhere to the outer surface of Au@rGO nanocomposite, forming a monolayer through chemical interactions. This suggests that both the interior and active exterior sites of Au@rGO nanocomposite are involved in trapping CV molecules. The results suggest that CV molecules are adsorbed onto both the interior and active exterior sites of Au@rGO nanocomposite. The Freundlich adsorption isotherm model supports this, as it indicates that CV molecules form multiple layers on the surface of the nanocomposite through physical binding events. Overall, these findings provide valuable information about the type of interactions between CV dye and Au@rGO nanocomposite as an effective adsorbent. The research helps in understanding the mechanism of CV adsorption and can contribute to further advancements in designing efficient adsorbents for dye removal applications68. linear relations that describe Langmuir and Freundlich's isotherms were presented as follows:
The theoretical CV adsorption capacity of Au@rGO nanocomposite is represented by Qm (mg/g), while the constant of the CV adsorption equilibrium is denoted as KL. The proportional adsorption capacity of Au@rGO nanocomposite is indicated by KF, and the adsorption strength is represented by n. The value of n provides insight into the favorability of CV adsorption, where a higher value suggests stronger adsorption.
To estimate these constants, linear relations of Ce/qe versus Ce and lnqe versus lnCe plots were used, and the slope and intercept of these relationships were determined. The R2 values indicate that Freundlich isotherm is a better fit compared to the Langmuir. In this case, the R2 value is 0.991, as shown in Fig. 7a,b and Table 1.
Based on the data of the Langmuir isotherm model, the maximum CV adsorption capacity on the surface of Au@rGO nanocomposite was determined to be 55.9 mg/g. Furthermore, the reversibility factor (RL) for the adsorption of CV dye on the surface of Au@rGO nanocomposite was determined to be 0.642. This is less than 1, which indicates that the adsorption process is favorable and fully reversible. In other words, the Au@rGO nanocomposite adsorbent can effectively release the trapped CV molecules using a suitable eluent agent. Table 2 compares the main adsorption findings with some related materials with their main characteristics and experimental conditions.
The Freundlich isotherm was used to analyze the adsorption data. The value of n was measured to be 1.974, suggesting that the CV adsorption process is a reasonable or hard adsorption method. Additionally, the value of 1/n was found to be less than 1, implying that the adsorption of CV dye on Au@rGO is favorable and involves a chemisorption process. The presence of microporosity in the Au@rGO nanocomposite facilitates the diffusion of CV molecules within the adsorbent. This makes it a promising option for the removal of CV contaminants.
Photocatalytic degradation mechanism
To determine the main active species governing the degradation of CV dye using Au@rGO nanocomposites, a series of experiments were conducted employing various scavengers, including p-benzoquinone (p-BQ) to quench O2−· radicals, ammonium oxalate (AO) to scavenge holes, and tert-butyl alcohol (t-BuOH) to capture OH· radicals. These scavengers were introduced into the CV solution before UV irradiation under the optimized removal conditions. As illustrated in Fig. 8, adding AO and p-BQ exhibited negligible effects on the CV degradation performance, suggesting that holes (h+) and O2−· radicals have an inconsequential impact on the CV degradation. Conversely, the inclusion of t-BuOH distinctly diminished the CV degradation rate. Thus, the preeminent active species in the photocatalytic degradation of the CV pollutant are identified as OH· radicals.
This finding suggests that the mechanism of CV adsorption onto Au@rGO nanocomposite involves layer formation through chemical bonds, as shown in Fig. 9.
The experiment under solar irradiation was carried out using 25 mL of 10 mg/L CV solutions. The absorbance of CV dye before and after 24 h was recorded using UV–Vis spectrophotometer. Based on the results in Fig. 10a, more than 98% of CV remained after 24 h in the direct photolysis test.
The photocatalytic degradation of CV dye using Au@rGO nanocomposite under UV light excitation entails the generation of electron (e−) and positive electron–hole (h+) pairs, a consequence of the excitation of an electron (e−) from the valence band (VB) to the conduction band (CB). The determination of the bandgap, achieved through the Tauc method utilizing UV–vis spectra of Au@rGO nanocomposite, is encapsulated in the subsequent equation69:
where Eg represents the bandgap of Au@rGO nanocomposites, h denotes Planck's constant, υ signifies frequency, α corresponds to the absorption coefficient, and A is the proportionality constant. As illustrated in Fig. 10b, the bandgap computed for Au@rGO nanocomposite is approximately 3.2 eV. Under UV light, H2O molecules can engage with holes (h+VB), generating OH·, while e−CB can capture O2 molecules, producing anionic superoxide (O2−·) radicals at the Au@rGO surface. The ensuing reaction between O2−· and H+ ions yield hydroperoxy (HOO·) radicals. Subsequently, the HOO· radical undergoes further transformation into H2O2 and O2. The dissociation of H2O2 yields additional OH· radicals, which play a pivotal role in the degradation of CV dye, as exemplified in the subsequent equations70:
Adsorption kinetics study
To discover the CV dye removal process and gain insight into its mechanism under ideal adsorption conditions, two frequently utilized kinetic models, the pseudo-first-order (PFO) and pseudo-second-order (PSO) models, were utilized to analyze the experimental findings79. The adsorption kinetics were examined over 2.5 to 30 min. PFO and PSO models can be calculated according to the following equations80:
In these equations, k1 and k2 represent the adsorption rate constants for PFO and PSO, respectively. Qe indicates the amount of adsorbed CV dye in mg/g of Au@rGO nanocomposite adsorbent at equilibrium while qe indicates the amount of adsorbed CV dye by mg/g on the sorbent at time t. To determine the parameters and constants, linear plots of Log(qe-qt) and t/qt versus time were analyzed, as shown in Table 3 (Fig. 11a,b). The R2 values of the fitted lines indicated that the adsorption of CV dye adhered more closely to the PSO than to the PFO model. This suggests that the removal mechanism of CV involves chemical adsorption through the utilization of Au@rGO nanocomposite. During the adsorption process, the decolourization of CV was initially rapid but slowed down as it approached equilibrium. The PSO model provided an estimated qe value that was very close to the experimental qe value when the initial concentration of CV dye was 25 mg/L.
Photocatalytic degradation kinetic study
The PFO and PSO linear model equations were utilized to analyze the kinetic rate of CV-photocatalytic degradation with the Au@rGO. The equations for the PFO and PSO kinetics models of photocatalytic degradation are as follows79,81,82:
In these equations, Co represents the initial CV concentration, Ct represents the final CV concentration after a certain period, k1 is the rate constant for the pseudo-first-order model, and k2 is the rate constant for the PSO model. Figure 12 illustrates the kinetic study of CV photocatalytic degradation on the surface of the Au@rGO nanocomposite. The plot shows ln(Co/Ct) and 1/Ct on the Y-axis against irradiation time on the X-axis, representing the PFO and PSO kinetics of CV-photocatalytic degradation on the Au@rGO nanocomposite, respectively (Fig. 12a,b).
Additionally, Table 3 summarizes various kinetic parameters such as the rate constants k1 and k2 for the PFO and PSO models, respectively, the half-life period (t0.5), and the coefficient of determination (R2). The half-life time of the reaction, t0.5 (in minutes), can be calculated using the formulas (0.693/k1) for PFO and (1/k2Co) for PSO. The kinetic data presented in the table represent the CV photocatalytic degradation kinetics study of Au@rGO nanocomposites. The R2 values for PFO and PSO are 0.9968 and 0.9850, respectively, indicating that the data for PFO fits the model better than PSO. Therefore, to achieve complete CV removal through the photocatalytic degradation approach, CV molecules must be adsorbed on the surface of the Au@rGO nanocomposite.
The rate of CV degradation using Au@rGO nanocomposite can be evaluated through the application of Langmuir–Hinshelwood using the following equation83:
In Eq. (10) ko is the initial rate, Co is the initial concentration of CV, kr is the apparent kinetic constant and ks is the adsorption constant. The first-order rate constant values were further utilized to explore the Langmuir–Hinshelwood model for CV removal using Au@rGO nanocomposite at different initial CV concentrations, as depicted in a graph between 1/ko and 1/Co (Fig. 12c). Values of Kr and Ks were defined from the slope and intercept of the plot, resulting in Kr being 12.87 mg/L.min and Ks being 0.459 L/mg. These results illustrate that when Kr > Ks, CV trapping onto the surface of the Au@rGO nanocomposite was the controlling step of the photodegradation process.
Regeneration and reusing of Au@rGO
The reusability and repeated use cycles of Au@rGO sorbent/catalysts offer important prospects for laboratory and scale-up applications. Because of their simplicity, safety and the possibility of reuse, the adsorption and photolysis processes are the most cost-effective methods for removing CV dye from wastewater. By employing the elution process, it becomes feasible to reuse the discarded adsorbent/photocatalyst multiple times. This leads to a reduction in the overall expenditure associated with the removal of the adsorption of CV dye at the inner/outer active sites of the surface of the mesoporous Au@rGO adsorbent/catalyst, whether via adsorption or photocatalytic degradation, which can potentially decrease the availability of these active sites. Consequently, this is resulting in a reduction in the efficiency of Au@rGO for the adsorption and photocatalytic degradation of CV dye. Therefore, the goal of these experiments is to efficiently analyze how to utilize the synthesized materials used as adsorbents/catalysts for using them in the long term. Nitric acid had been used as an eluent solution and the influence of HNO3 concentration and elution time were performed through batch experiments to investigate the efficiency of CV-elution. The regenerated CV-free Au@rGO solid was filtered, dried, and reused as displayed in Fig. 13, the efficiency of the adsorption and photocatalytic degradation of CV dye using Au@rGO in the first cycle reached about 95% and 99%, respectively. Then its efficiency decreases at cycle number five from the repeated experiments 78% and 84%, respectively. Based on these findings, the reusability of Au@rGO nanocomposite numerous times enabled a low-cost technique for real-world large-scale applications. The SEM micrographs of the Au@rGO nanocomposite before and after five cycles confirmed the high stability of its morphology even after many reusing cycles, as shown in the inset of Fig. 13.
Conclusions
In this work, Au@rGO nanocomposite was synthesized using sustainable, simple, and cost-effective method via recycling the electronic waste. The nanocomposite showed high adsorption and photocatalytic degradation ability for CV removal from polluted water. At pH 10 and 30 min, the nanocomposite can remove more than 99% of CV content from wastewater under irradiation. The adsorption of CV dye on the Au@rGO nanocomposite follows the Langmuir model, which means that the CV molecules are adsorbed onto the surface of the nanocomposite to form a monolayer. The theoretical value of the CV-adsorbed amount was calculated based on the Langmuir isotherm and it was found to be 55 mg/g, which agrees with the actual value of the CV adsorbed amount. The kinetic data obtained for both adsorption and photocatalytic degradation of CV dye on the surface of the Au@rGO nanocomposite fit better into the PFO kinetic model than the PSO kinetic model. The Au@rGO nanocomposite can be readily regenerated and reused for several cycles with high efficiency of 99%. The recycled Au@rGO nanocomposite is a promising candidate for water purification technologies (CV removal).
Data availability
All data generated or analysed during this study are included in this published article.
References
Lee, S. P., Ali, G. A. M., Algarni, H. & Chong, K. F. Flake size-dependent adsorption of graphene oxide aerogel. J. Mol. Liq. 277, 175–180. https://doi.org/10.1016/j.molliq.2018.12.097 (2019).
Sadegh, H., Ali, G. A. M., Agarwal, S. & Gupta, V. K. Surface Modification of MWCNTs with carboxylic-to-amine and their superb adsorption performance. Int. J. Environ. Res. 13, 523–531. https://doi.org/10.1007/s41742-019-00193-w (2019).
Sharifi, A. et al. Investigation of photocatalytic behavior of modified ZnS:Mn/MWCNTs nanocomposite for organic pollutants effective photodegradation. J. Environ. Manag. 247, 624–632. https://doi.org/10.1016/j.jenvman.2019.06.096 (2019).
Stankovich, S. et al. Graphene-based composite materials. Nature 442, 282–286 (2006).
Park, S. & Ruoff, R. S. Chemical methods for the production of graphenes. Nat. Nanotechnol. 4, 217–224 (2009).
Choi, J. T. et al. Functionalized graphene sheet/polyurethane nanocomposites: effect of particle size on physical properties. Macromol. Res. 19, 809–814 (2011).
Vasseghian, Y. et al. Spotlighting graphene-based catalysts for the mitigation of environmentally hazardous pollutants to cleaner production: A review. J. Clean. Prod. 365, 132702 (2022).
Misra, U., Dixit, N. & Singh, S. P. Effect of laser parameters on laser-induced graphene filter fabrication and its performance for desalination and water purification. ACS Appl. Mater. Interfaces 15, 7899–7910 (2023).
Bahri, M. et al. Recent advances in chemical vapour deposition techniques for graphene-based nanoarchitectures: From synthesis to contemporary applications. Coord. Chem. Rev. 475, 214910 (2023).
Ali, G. A. M., Makhlouf, S. A., Yusoff, M. M. & Chong, K. F. Structural and electrochemical characteristics of graphene nanosheets as supercapacitor electrodes. Rev. Adv. Mater. Sci. 40, 35–43 (2015).
Gupta, V. K. et al. Facile route synthesis of novel graphene oxide-β-cyclodextrin nanocomposite and its application as adsorbent for removal of toxic bisphenol A from the aqueous phase. J. Mol. Liq. 237, 466–472. https://doi.org/10.1016/j.molliq.2017.04.113 (2017).
Gomaa, H. et al. A novel, spongy mesoporous hybrid bio-adsorbents derived from agricultural waste for highly selective thorium recovery. J. Clean. Prod. 402, 136819. https://doi.org/10.1016/j.jclepro.2023.136819 (2023).
Habeeb, O. A., Ramesh, K., Ali, G. A. M. & Yunus, R. M. Low-cost and eco-friendly activated carbon from modified palm kernel shell for hydrogen sulfide removal from wastewater: adsorption and kinetic studies. Desalin. Water Treat. 84, 205–214 (2017).
Robinson, B. H. E-waste: An assessment of global production and environmental impacts. Sci. Total Environ. 408, 183–191. https://doi.org/10.1016/j.scitotenv.2009.09.044 (2009).
Banerjee, P., Das, P., Zaman, A. & Das, P. Application of graphene oxide nanoplatelets for adsorption of ibuprofen from aqueous solutions: Evaluation of process kinetics and thermodynamics. Process Saf. Environ. Prot. 101, 45–53 (2016).
Ali, G. A. M. Recycled MnO2 nanoflowers and graphene nanosheets for low-cost and high performance asymmetric supercapacitor. J. Electron. Mater. 49, 5411–5421. https://doi.org/10.1007/s11664-020-08268-7 (2020).
Ali, G. A. M., Tan, L. L., Jose, R., Yusoff, M. M. & Chong, K. F. Electrochemical performance studies of MnO2 nanoflowers recovered from spent battery. Mater. Res. Bull. 60, 5–9. https://doi.org/10.1016/j.materresbull.2014.08.008 (2014).
Ali, G. A. M., Yusoff, M. M., Algarni, H. & Chong, K. F. One-step electrosynthesis of MnO2/rGO nanocomposite and its enhanced electrochemical performance. Ceram. Int. 44, 7799–7807. https://doi.org/10.1016/j.ceramint.2018.01.212 (2018).
Bajpai, A., Kumbhakar, P., Tiwary, C. S. & Biswas, K. Conducting graphene synthesis from electronic waste. ACS Sustain. Chem. Eng. 9, 14090–14100 (2021).
Gomaa, H. et al. Three-dimensional, vertical platelets of ZnO carriers for selective extraction of cobalt ions from waste printed circuit boards. ACS Sustain. Chem. Eng. 6, 13813–13825. https://doi.org/10.1021/acssuschemeng.8b01906 (2018).
Gomaa, H. et al. Inorganic-organic mesoporous hybrid segregators for selective and sensitive extraction of precious elements from urban mining. J. Colloid Interface Sci. 604, 61–79. https://doi.org/10.1016/j.jcis.2021.07.002 (2021).
Hossain, M. S., Al-Hamadani, S. M. & Rahman, M. T. E-waste: A challenge for sustainable development. J. Health Pollut. 5, 3–11 (2015).
Ishak, S. A. et al. The application of modified natural polymers in toxicant dye compounds wastewater: A review. Water 12, 2032 (2020).
Khan, A. et al. Removal of crystal violet from wastewater using synthesized graphene quantum dots as adsorbents: Kinetic approach. Int. J. Environ. Sci. Technol. https://doi.org/10.1007/s13762-023-04881-1 (2023).
Pourebrahim, F., Ghaedi, M., Dashtian, K., Kheirandish, S. & Goudarzi, A. Optimization of solid phase dispersive field-assisted ultrasonication for the extraction of auramine O and crystal violet dyes using central composite design. Appl. Organomet. Chem. 32, e4181. https://doi.org/10.1002/aoc.4181 (2018).
Pathan, A., Bhatt, S. H., Vajapara, S. & Bhasin, C. P. Solar light induced photo catalytic properties of α-Fe2O3 nanoparticles for degradation of methylene blue dye. Int. J. Thin Film Sci. Technol. 11, 213–224. https://doi.org/10.18576/ijtfst/110209 (2022).
Yan, Z. et al. Occurrence and ecological risk assessment of organic micropollutants in the lower reaches of the Yangtze River, China: A case study of water diversion. Environ. Pollut. 239, 223–232 (2018).
Ali, G. A. M. et al. High surface area mesoporous silica for hydrogen sulfide effective removal. Curr. Nanosci. 16, 226–234 (2020).
Essa, W. K. et al. Taguchi L25 (54) approach for methylene blue removal by polyethylene terephthalate nanofiber-multi-walled carbon nanotube composite. Water 14, 1242 (2022).
Vajapara, S., Pathan, A. & Bhasin, C. P. Adsorption and photocatalytic performance of activated carbon and activated carbon-La2O3 nanoparticles composites for malachite green. Int. J. Thin Film Sci. Technol. 12, 21–37. https://doi.org/10.18576/ijtfst/120104 (2023).
Karam, F. F., Saeed, N. H., Al Yasasri, A., Ahmed, L. & Saleh, H. Kinetic study for reduced the toxicity of textile dyes (reactive yellow 14 dye and reactive green dye) using UV-A Light/ZnO system. Egypt. J. Chem. 63, 2987–2998 (2020).
Isalou, A., Pourbasheer, E., Beheshti, A. & Ganjali, M. R. Magnetic solid-phase extraction based on chitosan coated with Fe3O4 nanoparticles for the removal of everzol black ED-2R Dye from wastewater. J. Anal. Chem. 78, 18–24. https://doi.org/10.1134/S1061934823010069 (2023).
Irshad, S. et al. Solubilization of direct dyes in single and mixed surfactant system: A comparative study. J. Mol. Liq. 321, 114201. https://doi.org/10.1016/j.molliq.2020.114201 (2021).
Azad, F. N., Ghaedi, M., Dashtian, K., Hajati, S. & Pezeshkpour, V. Ultrasonically assisted hydrothermal synthesis of activated carbon–HKUST-1-MOF hybrid for efficient simultaneous ultrasound-assisted removal of ternary organic dyes and antibacterial investigation: Taguchi optimization. Ultrason. Sonochem. 31, 383–393. https://doi.org/10.1016/j.ultsonch.2016.01.024 (2016).
Khan, I. et al. Enhanced visible-light photoactivities of porous LaFeO3 by synchronously doping Ni2+ and coupling TS-1 for CO2 reduction and 2,4,6-trinitrophenol degradation. Catal. Sci. Technol. 11, 6793–6803. https://doi.org/10.1039/D1CY01112J (2021).
Zeng, B. & Long, H. Graphene spheres-CuO nanoflowers composites for use as a high performance photocatalyst. Nanomater. Nanotechnol. 6, 21 (2016).
Sanei, A., Dashtian, K., Yousefi Seyf, J., Seidi, F. & Kolvari, E. Biomass derived reduced-graphene-oxide supported α-Fe2O3/ZnO S-scheme heterostructure: Robust photocatalytic wastewater remediation. J. Environ. Manag. 332, 117377. https://doi.org/10.1016/j.jenvman.2023.117377 (2023).
Siddique, M., Fayaz, N. & Saeed, M. Synthesis, characterization, photocatalytic activity and gas sensing properties of zinc doped manganese oxide nanoparticles. Phys. B: Condens. Matter 602, 412504. https://doi.org/10.1016/j.physb.2020.412504 (2021).
Khan, I. et al. Green synthesis of SrO bridged LaFeO3/g-C3N4 nanocomposites for CO2 conversion and bisphenol A degradation with new insights into mechanism. Environ. Res. 207, 112650. https://doi.org/10.1016/j.envres.2021.112650 (2022).
Abd Elkodous, M. et al. Nanocomposite matrix conjugated with carbon nanomaterials for photocatalytic wastewater treatment. J. Hazard. Mater. 410, 124657. https://doi.org/10.1016/j.jhazmat.2020.124657 (2021).
Abdel Maksoud, M. I. A. et al. Gamma irradiation-assisted synthesis of PANi/Ag/MoS2/LiCo0.5Fe2O4 nanocomposite: Efficiency evaluation of photocatalytic bisphenol A degradation and microbial decontamination from wastewater. Opt. Mater. 119, 111–396. https://doi.org/10.1016/j.optmat.2021.111396 (2021).
Abd Elkodous, M. et al. Enhanced photocatalytic and antimicrobial performance of a multifunctional Cu-loaded nanocomposite under UV light: Theoretical and experimental study. Nanoscale 14, 8306–8317. https://doi.org/10.1039/D2NR01710E (2022).
Ahmed, M. A. & Mohamed, A. A. Recent progress in semiconductor/graphene photocatalysts: Synthesis, photocatalytic applications, and challenges. RSC Adv. 13, 421–439 (2023).
Stepanova, I. A., Lebedeva, A. N., Shik, A. V., Skorobogatov, E. V. & Beklemishev, M. K. Recognition and determination of sulfonamides by Near-IR fluorimetry using their effect on the rate of the catalytic oxidation of a carbocyanine dye by hydrogen peroxide. J. Anal. Chem. 76, 1399–1407. https://doi.org/10.1134/S1061934821120121 (2021).
Faizan, S., Bakhtawara, A. & Ali Shah, L. Facile fabrication of hydrogels for removal of crystal violet from wastewater. Int. J. Environ. Sci. Technol. 19, 4815–4826. https://doi.org/10.1007/s13762-021-03454-4 (2022).
Naggar, A. H. et al. A hybrid mesoporous composite of SnO2 and MgO for adsorption and photocatalytic degradation of anionic dye from a real industrial effluent water. Environ. Sci. Pollut. Res. 30, 108247–108262. https://doi.org/10.1007/s11356-023-29649-5 (2023).
Alam, S. N., Sharma, N. & Kumar, L. Synthesis of graphene oxide (GO) by modified hummers method and its thermal reduction to obtain reduced graphene oxide (rGO). Graphene 6, 1–18 (2017).
Fan, X., Cai, C., Gao, J., Han, X. & Li, J. Hydrothermal reduced graphene oxide membranes for dyes removing. Sep. Purif. Technol. 241, 116730. https://doi.org/10.1016/j.seppur.2020.116730 (2020).
Huang, H.-H., De Silva, K. K. H., Kumara, G. R. A. & Yoshimura, M. Structural evolution of hydrothermally derived reduced graphene oxide. Sci. Rep. 8, 6849. https://doi.org/10.1038/s41598-018-25194-1 (2018).
Vermisoglou, E. C. et al. Effect of hydrothermal reaction time and alkaline conditions on the electrochemical properties of reduced graphene oxide. Appl. Surf. Sci. 358, 100–109. https://doi.org/10.1016/j.apsusc.2015.08.127 (2015).
do Nascimento, J. d. R. V., Wohnrath, K. & Garcia, J. R. Synthesis of gold nanoparticles using recovered gold from electronic waste. Orbital: Electron. J. Chem. 66, 153–159 (2021).
Kassem, K. O. et al. Design of mesoporous ZnO@ silica fume-derived SiO2 nanocomposite as photocatalyst for efficient crystal violet removal: Effective route to recycle industrial waste. J. Clean. Prod. 326, 129416 (2021).
Maryami, M., Nasrollahzadeh, M., Mehdipour, E. & Sajadi, S. M. Preparation of the Ag/RGO nanocomposite by use of Abutilon hirtum leaf extract: A recoverable catalyst for the reduction of organic dyes in aqueous medium at room temperature. Int. J. Hydrog. Energy 41, 21236–21245. https://doi.org/10.1016/j.ijhydene.2016.09.130 (2016).
Mondal, P. et al. A highly active recyclable gold–graphene nanocomposite material for oxidative esterification and Suzuki cross-coupling reactions in green pathway. J. Colloid Interface Sci. 459, 97–106 (2015).
Karapanagiotis, I. et al. Shellfish purple and gold threads from a Late Antique tomb excavated in Thessaloniki. I ARACHNI 5, 64–77 (2018).
Liu, C., Yu, Z., Neff, D., Zhamu, A. & Jang, B. Z. Graphene-based supercapacitor with an ultrahigh energy density. Nano Lett. 10, 4863–4868 (2010).
Yasin, M. et al. Development of Bi2O3–ZnO heterostructure for enhanced photodegradation of rhodamine B and reactive yellow dyes. Surf. Interfaces 30, 101846. https://doi.org/10.1016/j.surfin.2022.101846 (2022).
Minale, M. et al. Application of graphene-based materials for removal of tetracyclines using adsorption and photocatalytic-degradation: A review. J. Environ. Manag. 276, 111310 (2020).
Gholami, D. et al. In situ growth of CuFeS2/CuS bridged heterojunction catalyst with mixed redox-couple cations for excellent photocatalytic degradation of organophosphate insecticide: CFD and DFT modeling. Chem. Eng. J. 461, 141950. https://doi.org/10.1016/j.cej.2023.141950 (2023).
Dashtian, K., Shahbazi, S., Tayebi, M. & Masoumi, Z. A review on metal-organic frameworks photoelectrochemistry: A headlight for future applications. Coord. Chem. Rev. 445, 214097. https://doi.org/10.1016/j.ccr.2021.214097 (2021).
Rashid, M., Parsaei, S., Ghoorchian, A., Dashtian, K. & Mowla, D. A spiral shape microfluidic photoreactor with MOF(NiFe)-derived NiSe-Fe3O4/C heterostructure for photodegradation of tetracycline: Mechanism conception and DFT calculation. J. Ind. Eng. Chem. 121, 275–286. https://doi.org/10.1016/j.jiec.2023.01.031 (2023).
Mampilly, R. B., Bhatt, S. H., Modi, N. J. & Pathan, A. Adsorption of eriochrome Black-T dye by batch investigations using waste tea@Fe NPs as low-cost adsorbent. Int. J. Thin Film Sci. Technol. 13, 17–25. https://doi.org/10.18576/ijtfst/130103 (2024).
Caldas, M. P. K., Martins, T. A. G., de Moraes, V. T., Tenório, J. A. S. & Espinosa, D. C. R. Synthesis of Ag nanoparticles from waste printed circuit board. J. Environ. Chem. Eng. 9, 106845 (2021).
Kocijan, M. et al. Graphene-based TiO2 nanocomposite for photocatalytic degradation of dyes in aqueous solution under solar-like radiation. Appl. Sci. 11, 3966 (2021).
Sittipol, W., Sronsri, C. & Kongpop, U. Effect of magnetic fields on the efficiency of the photocatalytic degradation of methylene blue in a dynamic fluid system. J. Clean. Prod. 325, 129284 (2021).
Abdel-Khalek, A. A., Mahmoud, S. & Zaki, A. Visible light assisted photocatalytic degradation of crystal violet, bromophenol blue and eosin Y dyes using AgBr-ZnO nanocomposite. Environ. Nanotechnol. Monit. Manag. 9, 164–173 (2018).
Weng, C.-H., Lin, Y.-T. & Tzeng, T.-W. Removal of methylene blue from aqueous solution by adsorption onto pineapple leaf powder. J. Hazard. Mater. 170, 417–424 (2009).
Li, X. & Li, Y. Adsorptive removal of dyes from aqueous solution by KMnO4-modified rice husk and rice straw. J. Chem. 2019, 66 (2019).
Gomaa, H. et al. A hybrid mesoporous CuO@barley straw-derived SiO2 nanocomposite for adsorption and photocatalytic degradation of methylene blue from real wastewater. Colloids Surf. A Physicochem. Eng. Asp. 644, 128811. https://doi.org/10.1016/j.colsurfa.2022.128811 (2022).
Aboraia, A. M. et al. A heterostructural MoS2QDs@UiO-66 nanocomposite for the highly efficient photocatalytic degradation of methylene blue under visible light and simulated sunlight. RSC Adv. 13, 34598–34609. https://doi.org/10.1039/D3RA06299F (2023).
Khan, A. et al. Removal of crystal violet from wastewater using synthesized graphene quantum dots as adsorbents: Kinetic approach. Int. J. Environ. Sci. Technol. 66, 1–14 (2023).
Wang, R.-F. et al. Fabrication and characterization of sugarcane bagasse–calcium carbonate composite for the efficient removal of crystal violet dye from wastewater. Ceram. Int. 46, 27484–27492 (2020).
Mechnou, I., Meskini, S., Mourtah, I., Lebrun, L. & Hlaibi, M. Use of phosphorus-doped microporous carbon from olive mill wastewater for effective removal of crystal violet and methylene blue. J. Clean. Prod. 393, 136333 (2023).
Shayesteh, H., Rahbar-Kelishami, A. & Norouzbeigi, R. Adsorption of malachite green and crystal violet cationic dyes from aqueous solution using pumice stone as a low-cost adsorbent: Kinetic, equilibrium, and thermodynamic studies. Desalin. Water Treat. 57, 12822–12831 (2016).
Akin, K., Ugraskan, V., Isik, B. & Cakar, F. Adsorptive removal of crystal violet from wastewater using sodium alginate–gelatin–montmorillonite ternary composite microbeads. Int. J. Biol. Macromol. 223, 543–554 (2022).
Mirhosseini, H., Shamspur, T. & Mostafavi, A. Novel adsorbent g-C3N4/ZnV2O4 for efficient removal of crystal violet dye: Removal process optimization, adsorption isotherms, and kinetic modeling. Appl. Organomet. Chem. 36, e6867 (2022).
Homagai, P. L., Poudel, R., Poudel, S. & Bhattarai, A. Adsorption and removal of crystal violet dye from aqueous solution by modified rice husk. Heliyon 8, 66 (2022).
Liu, W., Jiang, X. & Chen, X. Synthesis and utilization of a novel carbon nanotubes supported nanocables for the adsorption of dyes from aqueous solutions. J. Solid State Chem. 229, 342–349 (2015).
Saeed, M. et al. Calotropis gigantea leaves assisted biosynthesis of ZnO and Ag@ZnO catalysts for degradation of rhodamine B dye in aqueous medium. Environ. Prog. Sustain. Energy 39, e13408. https://doi.org/10.1002/ep.13408 (2020).
Pang, J. et al. Adsorption behaviors of methylene blue from aqueous solution on mesoporous birnessite. J. Taiw. Inst. Chem. Eng. 77, 168–176. https://doi.org/10.1016/j.jtice.2017.04.041 (2017).
Rahman, K. H. & Kar, A. K. Effect of band gap variation and sensitization process of polyaniline (PANI)-TiO2 pn heterojunction photocatalysts on the enhancement of photocatalytic degradation of toxic methylene blue with UV irradiation. J. Environ. Chem. Eng. 8, 104181 (2020).
Matouq, M., Al-Anber, Z., Susumu, N., Tagawa, T. & Karapanagioti, H. The kinetic of dyes degradation resulted from food industry in wastewater using high frequency of ultrasound. Sep. Purif. Technol. 135, 42–47. https://doi.org/10.1016/j.seppur.2014.08.002 (2014).
Fatimah, I., Wang, S. & Wulandari, D. ZnO/montmorillonite for photocatalytic and photochemical degradation of methylene blue. Appl. Clay Sci. 53, 553–560. https://doi.org/10.1016/j.clay.2011.05.001 (2011).
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Author information
Authors and Affiliations
Contributions
S.H.A.: Methodology; Writing—original draft; H.G. and R.D.A.: Formal analysis; Investigation; Methodology; Writing—original draft; ِA.M.N.: Formal analysis; Investigation; Writing—review & editing; G.A.M.A.: Data curation; Resources; Software; Visualization; Writing—original draft; Writing—review & editing.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Al-Ansari, S.H., Gomaa, H., Abdel-Rahim, R.D. et al. Recycled gold-reduced graphene oxide nanocomposite for efficient adsorption and photocatalytic degradation of crystal violet. Sci Rep 14, 4379 (2024). https://doi.org/10.1038/s41598-024-54580-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-024-54580-1
- Springer Nature Limited
Keywords
This article is cited by
-
Optimization of methyl orange decolorization by bismuth(0)-doped hydroxyapatite/reduced graphene oxide composite using RSM-CCD
Environmental Science and Pollution Research (2024)