Abstract
High bandwidth, low voltage electro-optic modulators with high optical power handling capability are important for improving the performance of analog optical communications and RF photonic links. Here we designed and fabricated a thin-film lithium niobate (LN) Mach-Zehnder modulator (MZM) which can handle high optical power of 110 mW, while having 3-dB bandwidth greater than 110 GHz at 1550 nm. The design does not require etching of thin-film LN, and uses hybrid optical modes formed by bonding LN to planarized silicon photonic waveguide circuits. A high optical power handling capability in the MZM was achieved by carefully tapering the underlying Si waveguide to reduce the impact of optically-generated carriers, while retaining a high modulation efficiency. The MZM has a \(V_\pi L\) product of 3.1 V.cm and an on-chip optical insertion loss of 1.8 dB.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
Electro-optic modulators (EOMs) are essential components for optical communications, radio frequency (RF)-photonic links, frequency combs, optical phased arrays and optical information processing. In recent years, thin-film lithium niobate (TFLN) EOMs with a high electro-optic 3-dB bandwidth of at least 100 GHz have been reported with a low voltage-times-length (\(V_\pi L\)) product and low optical insertion loss1,2,3,4. However, these demonstrations have been performed at relatively low optical power levels less than 10 mW. The ability to handle high optical powers without increasing \(V_\pi\) would be beneficial, by increasing the RF link gain and reducing the noise figure of an analog communications system5,6,7. For a given photodiode responsivity, reducing \(V_\pi\) and increasing the optical power are both important in the noise figure of an RF photonic link. Recently, a higher optical power level, around 25 mW, was shown using TFLN Mach-Zehnder modulator (MZM) with about 50 GHz bandwidth8. Here, we report the first TFLN MZM which achieves both above-100 GHz bandwidth and above-100 mW optical power handling capability, while also achieving a low \(V_\pi L\) product and low on-chip optical insertion loss, and integration with silicon photonics.
TFLN-based waveguides have been made using various methods such as etching, blade-dicing or polishing of ridge or rib waveguides, and rib-loading of a TFLN slab using other materials1,9,10,11,12,13,14,15,16,17,18,19. Our approach is based on hybrid optical modes, in which the waveguide core consists of a combination of silicon (Si) and LN, and the cladding consists of silicon dioxide (\(\mathrm {SiO}_2\)). This approach takes advantage of both the scalability of Si photonics, which is fabricated on large wafers using mature foundry processing, and the EO properties of crystalline LN without having to etch or pattern it. The Si waveguides are formed in the crystalline layer of a silicon-on-insulator (SOI) wafer, and are tapered in the hybrid region to implement inter-layer optical mode transitions; the TFLN layer is not etched or patterned. The Si waveguides can be continuously connected, without breaks, to other photonic components outside the bonded region, and thus present a simple and scalable way to include ultrahigh bandwidth EOMs with other photonic components19,20.
At higher optical powers, Si waveguides suffer from two-photon absorption (TPA) and free carrier absorption (FCA) and dispersion (FCD) effects21,22,23,24. The nonlinear optical absorption of amorphous Si is sensitive to processing25 and can even exceed that of crystalline Si by a factor of 30 or more26. Therefore, it is preferable in hybrid TFLN design to use a layer of crystalline Si waveguides rather than depositing Si on top of TFLN which has been a popular strategy27,28. Also, by carefully designing the Si layer dimensions and tapers, the amount of optical power in the Si region can be minimized while still remaining in the single-mode regime, which is necessary for a high-bandwidth MZM. While our strategy does not totally eliminate the nonlinear loss of Si, it can keep the impairments of the hybrid mode adequately low for practically-useful optical power levels over the device lengths needed for a high-bandwidth, low-voltage MZM.
(a) Top-view schematic (not to scale) of the Si/LN MZM. The transition region consists of the transition waveguide and adiabatic tapers (shown in green), and the phase shifter section consists of the hybrid waveguide (shown in red). Cross-sectional simulated Poynting vector of the (b) feeder Si waveguide (no LN film), (c) transition Si waveguide, and (d) hybrid Si/LN waveguide. (e) The simulated effective index of the first three Si/LN modes (top), and the confinement factor in the TFLN layer and Si waveguide (bottom) as a function of Si waveguide width at \(\lambda = 1550\) nm. The dashed lines indicate the modes shown in panels (c) and (d).
Results
Theory and design
The phase shifter sections of the MZM, shown by the regions that are colored red in Fig. 1a, consist of a long single-mode waveguide in which the transverse localization of the hybrid optical mode is controlled by narrowed Si features (275 nm wide and 150 nm tall). Adiabatically tapering down the Si waveguide reduces the effective index of the guided mode (\(n_\mathrm {eff}\)), and transitions the confinement from the high index Si to the LN layer, as shown in Fig. 1e. For this TE-polarized hybrid mode, light exists mainly in the LN section, and as shown in Fig. 1d, only 2% of the Poynting vector resides in Si, with 84% in TFLN, and the rest in the cladding. Therefore, the nonlinear impairments can be expected to be much lower than for a conventional Si carrier-depletion MZM where most of the light is in Si29. Because the amount of light in Si is so small, the hybrid TFLN phase shifter does not have a significant nonlinear optical penalty compared to a etched TFLN design.
The transition waveguide regions, shown by the regions that are colored green in Fig. 1a, consist of wider Si features (650 nm wide and 150 nm tall) which confines light mainly in Si (Fig. 1c: 52% of the Poynting vector magnitude of the fundamental waveguide mode resides in Si, only 20% in the thin film of LN, and the rest in the cladding). Figure 1b and c show the simulated mode profile of the Si waveguides without and with the LN film above, respectively. The effective index (\(n_\mathrm {eff}\)) difference between these modes is 0.08 which results in an estimated loss of only about 0.074 dB. Because the mode fractions in Si (\(\Gamma _\mathrm {Si}\)) are similar, we do not expect this loss to significantly change at higher powers when the refractive index of Si changes slightly. Overall, this loss should be negligible compared to other losses in the device that are described below in detail. This allows light to propagate with minimal loss (< 0.1 dB) across the bonded LN edge, where one side has LN as part of the multi-layer stack and the other side does not. We can thus mitigate sensitivity to micro-roughness in the diced edges of the LN chip, which simplifies the fabrication process. The length of the transition waveguide segment is short: a few tens of microns can be sufficient to traverse the edge of the LN film, and thus, the length-integrated effects of these nonlinear impairments are low as shown using numerical simulations which are discussed below.
Silicon waveguides in which the mode closely resembles the transition mode (but with no TFLN layer on top, as shown in Fig. 1b) were used to form bends and the 3-dB multi-mode interference (MMI) couplers. These segments can also be kept very short, and the length-integrated nonlinear impairments are small at the relevant optical power levels. Our test chip also include tapered-waveguide edge couplers for guiding light from optical fibers to the waveguides. In our experiments, it was these segments, rather than the waveguides and transitions that constituted the MZM, were damaged at the highest optical power levels (above 150 mW). A detailed study of high-power fiber-to-waveguide coupling is beyond the scope of this report.
Nonlinear impairments in a traveling-wave MZM device can, in principle, limit the intrinsic MZM EO bandwidth, insertion loss (IL), and half-wave voltage (\(V_\pi\)). For a given material dielectric stack, high speed EO modulation depends on three design rules: (1) matching the velocities of the RF and optical waves; (2) matching the transmission line, source, and load impedances (typically 50 \(\Omega\)); and (3) minimizing the RF propagation losses30,31,32,33. The density of photo-generated electronic carriers caused by TPA is
where \(\beta\) is the TPA coefficient of Si (assumed to be 1.0 cm/GW22), hf is the energy of the photon, P is the optical power, and \(A_\mathrm {eff}\) is the effective area of the optical mode. The electronic carrier lifetime \(\tau _e\) in crystalline Si waveguides is typically in the range of 1–100 ns, and depends on the waveguide geometry and the surface properties34. We estimate our 150 nm thick strip waveguide to have an upper limit lifetime of 15 ns35. These photogenerated carriers lead to additional optical losses and a shift in refractive index in the Si waveguide via the plasma dispersion effect36 given by,
If the change in the modal cross-sectional area \(A_\mathrm {eff}\) is negligible, the evolution of the guided optical power as a function of propagation distance (y) with linear and nonlinear losses is
where \(\alpha _l\) is the linear absorption loss of the waveguide and \(\Gamma _\mathrm {Si} = \displaystyle \left( \iint _\mathrm {Si}{|E_\mathrm {o}|^2\mathrm {dA}}\right) \cdot \left( \iint _{-\infty }^{+\infty }|E_\mathrm {o}|^2\mathrm {dA}\right) ^{-1}\) is the optical confinement factor in the Si waveguide in terms of the electric field distribution of the optical mode, \(E_\mathrm {o}(x,y)\).
Figure 2a shows the calculated change in IL due to nonlinear effects (TPA and FCA) by numerically solving Eq. (3) for different lengths of hybrid waveguide (solid lines) and transition waveguides (dashed lines). We assume that the electronic carriers generated by light are confined to the Si waveguide, via \(\Gamma _\mathrm {Si}\) in Eq. (3). The cross-sectional modal areas \(A_\mathrm {eff}\) of the transition and hybrid modes are calculated to be 0.24 \(\upmu \mathrm{m}^2\) and 1.48 \(\upmu \mathrm{m}^2\), respectively. For the maximum considered lengths of 2 cm and 0.15 cm for the hybrid and transition waveguides in Fig. 2a, the 1 dB IL penalty due to TPA occurs at an optical power ten times higher in the hybrid waveguide than in the transition waveguide. If the transition section is reduced to 100 \(\mathrm {\mu }\)m (which is approximately the minimum for an adiabatic taper between the modes shown in Fig. 1c,d37), then the total additional IL should be less than 1 dB for optical powers up to 0.6 W.
(a) The calculated insertion loss (IL) due to TPA as a function of peak optical power in the hybrid waveguide mode (solid) and the transition mode (dashed) assuming different lengths of the phase-shift segment. (b) The change in refractive index due to the additional free carriers generated via TPA as a function of peak optical power for the hybrid and transition modes. (c) The calculated IL due to TPA as a function of peak optical power in the hybrid (solid) and transition (dashed) mode assuming a length of 0.5 cm for different waveguide widths. (d) The calculated 3-dB bandwidth of a traveling-wave MZM as a function of \(L_\mathrm {ps}\) assuming impedance matching to a 50 \(\Omega\) load, and for different values of the index mismatch, \(\Delta n_\mathrm {mo}\). WG, waveguide; TFLN, thin-film lithium niobate.
The electro-optic response (EOR) as a function of RF frequency and optical power is30
where the input impedance of the coplanar traveling wave electrodes is defined as
and the complex RF propagation constant is
Here, \(R_\mathrm {L,G}\) are the load and generator resistances, \(Z_\mathrm {L,G,c}\) are the load, generator, and characteristic impedances, \(\alpha _\mathrm {m}\) is the RF propagation loss, \(n_\mathrm {m}\) is the RF effective index, and \(L_\mathrm {ps}\) is the phase-shifter interaction length. \(F\left[ u_{\pm }(P)\right]\) and \(u_{\pm }(P)\) are defined as
and
The optical power dependence in Eq. (4a) is included by the associated FCD term affecting the optical group index, \(n_g\), from photogenerated carriers in Eq. (4e). There will be a similar shift in \(V_\pi L\) due to FCD, where the effective modulator length, L, may be limited by the additional nonlinear losses (Eq. 3)]and, thus, impact \(V_\pi\). Since the hybrid MZM uses an x-cut TFLN film and a TE-polarized fundamental waveguide mode, the effects of FCD on \(V_\pi\) can be expressed as
where \(n_\mathrm {eff}\) is the hybrid mode effective index, \(\lambda _0\) is the free-space wavelength, G is the signal-to-ground electrode gap spacing, \(n_e\) is the extraordinary index of TFLN, \(r_{33}\) is the electro-optic coefficient of TFLN, and \(\Gamma _{mo}\) is the overlap integral between the RF and optical modes in the electro-optic region.
Figure 2b shows the change in refractive index. Changes in the refractive index will effect the index matching condition (\(\Delta n = (1-n_m/n_g)\times 100\%\)) between the traveling RF and optical waves. Since the hybrid mode is predominantly localized in the LN film, the effect is expected to be negligible for optical peak powers less than 10 W in theory. Although high intensity optical inputs can also result in an increase in local temperature (and an associated thermo-optic effect), the time scales of such thermal shifts is much longer compared to the modulation speeds38 and could be compensated by the bias controller. Furthermore, the photorefractive effect of TFLN at a wavelength of 1550 nm results in refractive index changes on the order of \(10^{-5}\)39, which would only change \(\Delta n\) by 0.005%.
Assuming the impedance matching condition is met, the 3-dB bandwidth of a traveling wave hybrid TFLN MZM is plotted as a function of the length of the phase shifter segment for different values of \(\Delta n\) in Fig. 2d using Eq. (4a). For \(L_\mathrm {ps} = 0.5\) cm, to reduce the bandwidth by a factor of two (i.e., 3 dB), the \(\Delta n\) caused by nonlinear high power effects would need to be about 10%, corresponding theoretically to a peak power greater than 100 W, which is much greater than we are able to test experimentally. A MZM device using a longer phase shifter of length 1 cm, would decrease the bandwidth by 3 dB for \(\Delta n = 5\%\).
In this work, the total length of the MZM is about 1.7 cm, which includes the edge couplers, MMIs, transition region (\(L_\mathrm {Tr} = 0.14\) cm), and the hybrid region (\(L_\mathrm {Hb} = 1.4\) cm). The 3-dB 2 \(\times\) 2 MMI couplers are 38 \(\upmu\)m long, 6 \(\upmu\)m wide, and are designed for the C-band. Bezier S-bends are implemented to separate the MZM arms to allow appropriate space for a standard 55 \(\upmu\)m wide electrode. In the hybrid bonded region, the transition waveguides are adiabatically tapered down from a width of 650 nm to a width of 275 nm over a length of 300 \(\upmu\)m which pushes the optical mode up into TFLN. These transition sections were intentionally made longer than necessary to simplify our bonding process. If the waveguide had 300 nm width (instead of 275 nm), then \(\Gamma _\mathrm {Si}\) increases slightly from 2 to \(3.3\%\), which will increase the number of photogenerated carriers in Si. Figure 2b and c show the additional index change and IL as the Si width changes for a hybrid waveguide length of 0.5 cm. For an optical input power of 110 mW, the additional IL due to TPA increases from 0.002 to 0.006 dB as the hybrid waveguide Si width increases from the target value of 275–300 nm.
Hybrid Si/LN chip fabrication
The hybrid Si/LN EOM was made by direct hydrophilic bonding without using an intermediate adhesive layer, such as benzocyclobutene (BCB)40, whose performance and stability at high optical powers is uncertain. The Si waveguides were built on a 200 mm diameter SOI wafer with 150 nm thick Si, 3 \(\upmu\)m thick silicon dioxide (\(\hbox {SiO}_2\)), and 725 μm thick high resistivity Si handle. The Si waveguide features were fabricated using deep-UV lithography followed by reactive-ion-etching. \(\hbox {SiO}_2\) was deposited on top of the Si waveguide features and then the surface was planarized using a CMP process to achieve a bondable surface, leaving a thin \(\hbox {SiO}_2\) layer (\(< 50\) nm). The LNOI wafers were procured commercially from NanoLN, Jinan Jingzheng Electronics Co., Ltd. The LNOI is an x-cut 600 nm thick LN film with 2 \(\upmu\)m thick buried \(\hbox {SiO}_2\) and 500 \(\upmu\)m thick Si handle. There is typically some variation of LN film thickness and thin \(\hbox {SiO}_2\) layer of the SOI across the wafers. Variations in the thickness of \(\hbox {SiO}_2\) layer between the bonded Si waveguide and LN film will change the mode fraction (\(\Gamma\)) contained in each region, and will also change the modulation efficiency17. However, based on the outcomes of the CMP process, this effect should be relatively small. For less than 20 nm change in the \(\hbox {SiO}_2\) thickness, the corresponding change in \(\Gamma _\mathrm {Si}\) or \(\Gamma _\mathrm {LN}\) remains within a few percent of the target values. For each reticle of the larger SOI wafer, the thickness of the layer stack was verified by ellipsometry before bonding. Based on the ellipsometric measurements of both the LN wafer and the processed silicon wafer after CMP, a die dicing plan is developed, and specific pairs of diced LN and Si chips are selected for bonding. In this way, the yield of devices from a wafer is increased, and the EO properties of each hybrid modulator will be closer to optimal.
(a) Fabrication process flow of the hybrid bonded Si/LN MZM. (b) Optical microscope image of hybrid bonded Si/LN chip with gold SWE. (b) The fabricated hybrid bonded Si/LN MZM chip. (c) A stitched optical microscope image of a 5 mm long SWE. (d) A scanning electron microscope image of the inductively loaded slot features.
Figure 3a illustrates the direct bonding hybrid Si/LN modulator fabrication process. Before bonding, the surfaces of the LNOI and SOI singulated-dies were cleaned using an RCA-1 process followed by plasma surface activation19. After plasma surface activation, the dies were soaked in deionized water. After drying the dies, the bonding was performed by contacting the two dies at room temperature. To improve the bond strength, the bonded sample was annealed using temperature cycles up to 300 \(^\circ\)C under an applied pressure of 9.8 N.\(\hbox {cm}^{-2}\). At this stage, as described in our earlier work19, the bonded samples can be stored for processing at a later stage, if required. A plasma-enhanced-chemical-vapor-deposition (PECVD) was used to deposit a few microns of thick \(\hbox {SiO}_2\) as the top cladding. Before the handle removal step, a polymer coating was applied to protect bonded chips except on top of the LNOI Si handle. Next, the oxide on top of the LNOI Si handle was etched using hydrofluoric (HF) acid. The LNOI Si handle was removed using a selective \(\hbox {XeF}_2\)-based etching process and then the oxide layer above LN was etched using HF. The polymer was cleaned using a solvent cleaning step, and a direct-laser writer was used to define the traveling wave electrode patterns using a negative photoresist. Finally, titanium and gold of thicknesses 20 nm and 750 nm, respectively, was deposited followed by a lift-off process to complete the fabrication of the electrodes. All steps from bonding of the TFLN chips to the final electrode fabrication were performed either at room temperature or at a modestly-elevated temperatures, not exceeding about 300 \(^\circ\)C.
For this device, an inductively loaded slow-wave electrode (SWE) structure (Fig. 3b–d) was designed to achieve velocity matching to the hybrid Si/LN optical mode. The gap between the signal and ground electrodes is 9 \(\upmu\)m, and the signal width is 55 \(\upmu\)m. The inductive loading feature is a periodic slot that is 5 \(\upmu\)m wide (w) and 4 \(\upmu\)m deep (h) with a period of 25 \(\upmu\)m, as shown in Fig. 3d. These periodic features increase the effective index of the microwave mode and slow the RF traveling wave to match the optical wave41,42,43,44,45. Capacitively-loaded (T-rail based) SWE structures have been demonstrated in other reports45,46 to achieve RF-optical velocity matching when using lower index substrates such as quartz or selectively-removed Si. In this case, the hybrid Si/LN group index is simulated to be 2.32 and the slow-wave RF index is 2.34 at 110 GHz, resulting in \(\Delta n < 1\%\) between the optical and RF waves before the nonlinear change of the index is taken into account. For the fabricated structures with about 40 nm of CMP \(\hbox {SiO}_2\) thickness, we estimate the peak electric field strength at 110 mW optical power in the oxide region of Fig. 1c,d to be about \(5.4\times 10^4\) V.\(\hbox {cm}^{-1}\) and \(1.3\times 10^4\) V cm−1, which is smaller than the estimated breakdown field strength of the \(\hbox {SiO}_2\), about \(5\times 10^6\) V cm−1.
High-speed, high-power measurements
(a) The measured optical transmission of the asymmetric hybrid-bonded Si/LN MZM with no modulation signal applied. The asymmetric path-length difference gives an FSR of 2.3 nm, and an average ER of 28 dB over 50 nm. (b) The measured \(V_\pi L\) of the hybrid MZM (\(L_\mathrm {ps} = 0.5\) cm) as a function of driving trapezoidal signal frequency. (c) A schematic block diagram of the quasi-CW high power electro-optic response measurement setup. Active RF multipliers were used for generating \(f>\) 50 GHz.
The asymmetric MZM under test was measured using a tunable CW C-band laser source which resulted in a free spectral range of 2.3 nm, a mean extinction ratio (ER) of 28 dB over 50 nm (maximum of 31 dB at \(\lambda = 1560\) nm), and a fiber-to-fiber IL of 12.2 dB as shown in Fig. 4a. The half-wave voltage of the Si/LN modulator with \(L_\mathrm {ps} =\) 0.5 cm was measured by overdriving it with a trapezoidal signal and projecting the overshoots of the modulated signal19, resulting in an average \(V_\pi L\) of 3.1 V.cm in the range of 0.1–10 MHz as shown in Fig. 4b. Figure 4c shows a block diagram of the quasi-CW high power modulation experiment. An external commercial LN modulator (labeled Pulse Carver in Fig. 4c) with 30 dB extinction ratio was used to carve the CW laser source into quasi-CW pulses. The pulse carver was driven by a pulse pattern generator, setting voltages with a pulse width of 1 \(\upmu\)s and a period of 100 \(\upmu\)s. This corresponds to a pulse length greater than 100 m, which is much greater than the length (1.7 cm) of the chip. A polarization maintaining erbium-doped fiber amplifier (PM-EDFA) was used to amplify the quasi-CW pulses to the Si/LN MZM. Quasi-CW pulses were used to extract maximum gain from the PM-EDFA by reducing the average power and gain saturation. Also, the lower average power reduces the likelihood of damage to the lensed fibers used in the experiments. The amplified pulses were characterized by monitoring the PM-EDFA output using a PM 90-10 splitter, where a sampling oscilloscope (DCA) verified the pulse shape and peak power, while an optical power monitor measured the average power of the pulses as a function of the PM-EDFA current. Optical attenuators were placed before the DCA and optical spectrum analyzer (OSA) to avoid damage. This device was measured to have an edge coupling loss of 5.2 dB when using lensed tapered fibers with a nominal 2.5 \(\upmu\)m mode field diameter; therefore, the on-chip IL of the MZM was 1.8 dB (see “Methods” for more detail). These losses, as well as the fiber, splitter, and connector losses were factored in to calculate the peak power out of the PM-EDFA. The power levels labeled in Fig. 5 and in this discussion refer to the on-chip optical power levels in the feeder waveguide before the start of the MZM section. A peak power level of 110 mW corresponds to an intensity of 460 kW/\(\hbox {mm}^2\) and 74 kW/\(\hbox {mm}^2\) in the transition and hybrid waveguides, respectively.
The OSA-measured (blue points) EOR of the hybrid bonded Si/LN MZM with \(L_\mathrm {ps} = 0.5\) cm using no RF multiplier (circles), a 4x multiplier (diamonds), and a 6x multiplier (squares) resulting in a measured 3-dB bandwidth of 110 GHz for both: (a) Low power, CW optical input with 4 mW of power; and (b) Quasi-CW optical input with peak power of 110 mW. The solid red line is the calculated linear model using Eq. (4a) with no nonlinearities. The cyan line in panel (a) is the EOR of an identically designed Si/LN MZM using a high speed LCA.
The high-power quasi-CW pulses were then coupled to the device and modulated with varying frequency sinusoidal waves using an RF signal generator. A high-resolution OSA was used to detect the generated sidebands and carrier signal as the frequency was swept47. This high-speed modulation measurement was performed in three frequency bands: 1–50 GHz, 47–78 GHz, and 72–110 GHz, where active RF multipliers were used to reach the latter two bands. A CS-5 calibration substrate (GGB Industries, Inc.) and a 110 GHz RF power sensor were used to de-embed the cables and probes used in the experiment and determine the RF power delivered. These calibration measurements were then used to extract the measured EORs of the modulator at relatively low power CW optical input (4 mW), and at input peak powers of 110 mW, as shown in Fig. 5a and b, respectively. In both cases, the measured EOR has a 3-dB bandwidth of 110 GHz. The overlapping measured data between the bands was averaged and shifted accordingly to stitch the frequency responses together. Furthermore, the EO \(S_{21}\) of an identically designed hybrid bonded MZM on a different chip was independently verified at low CW optical power using a lightwave component analyzer (LCA). The LCA consisted of a Keysight PNA-X network analyzer, frequency extenders, and a 110 GHz photodetector which allowed us to measure modulated signals ranging from 100 MHz to 110 GHz. As can be seen in Fig. 5a, the OSA-measured response (blue marks) and LCA-measured response (cyan line) agree in both slope and 3-dB bandwidth. The 3-dB bandwidth is limited from impedance matching. Due to the fixed separation between the Si waveguides of the fabricated SOI chip, the signal electrode to electrode gap spacing is also fixed. This specific MZM was fabricated with an electrode gap of 9 \(\upmu\)m, resulting in a transmission line impedance of 42 \(\Omega\). If the Si waveguide separation is changed to accommodate a more optimal signal electrode width, then the impedance will be better matched to a 50 \(\Omega\) load, and further increase the 3-dB bandwidth of the MZM.
Discussion
The red lines in Fig. 5a,b are the calculated EORs using a linear model of the response function of a traveling wave MZM with no intensity dependent nonlinear effects30. The theoretical EOR predicts a 3-dB bandwidth above 110 GHz (approximately 156 GHz) for this 0.5 cm long modulator, which is agreement with the measured frequency responses in both the low and high optical power regimes. A large concentration of free carriers overlapping with the optical mode would cause a free-carrier dispersion effect which would decrease the 3-dB bandwidth. However, since the hybrid mode has only 2% of light in the Si waveguide, there is an insignificant impairment in our device, and the response at 110 mW is effectively the same as that at low (4 mW) power levels. Table 1 lists performance metrics of recent TFLN-based MZM. The present device is the first (to our knowledge) TFLN MZM that demonstrates greater than 100 GHz modulation of high optical power inputs greater than 100 mW. \(\text {FOM}\) (units: dB) in Table 1 is defined as \(\text {FOM} = 20\ \log _{10}(V_\pi ) - 20\ \log _{10}(r_d \times P_\text {opt} \times 50\ \Omega )\), where \(r_d\) is the detector responsivity, assumed to be 1 A/W. FOM is that portion of the noise figure (NF) expression for an RF photonic link6 which represents the contribution to the NF from the modulator \(V_\pi\) and optical power level. In addition, the laser RIN plays an important role in the overall NF in a practical system, but is not considered here in the FOM for the modulator alone. Lower values of the modulator FOM are preferable because they reduce the minimum achievable NF of the link. This shows the benefits of increasing \(P_\mathrm {opt}\) while keeping \(V_\pi\) low. The on-chip IL of our hybrid Si/LN device is comparable to that of other TFLN devices. The \(V_\pi L\) can be slightly improved by introducing a buffer \(\hbox {SiO}_2\) layer between the electrodes and LN film, which will reduce the optical loss due to electrode interaction and allow for a narrower electrode spacing48. In comparison to these TFLN MZM devices, a traditional Si depletion-mode MZM made with 250 nm thick Si rib waveguide (90 nm slab height and 650 nm width) will have 75% of the Poynting energy confined in Si and an \(A_\mathrm {eff}\) on the order of 0.2 \(\upmu\)\(\hbox{m}^2\). Both the linear and nonlinear optical propagation loss coefficients are high, and will limit the high-power handling capabilities of a Si MZM. Furthermore, the modulation speed of carrier depletion MZMs is typically RC-limited, with reported 3-dB electro-optic bandwidths < 60 GHz49,50,51,52,53.
Our experimental observations are consistent with the theoretical predictions shown in Fig. 2b. Using Eq. (5), the effect of TPA induced carriers on the \(V_\pi L\) through FCD (Fig. 2b) is insignificant at 110 mW, and would contribute less than 1% change in modulation efficiency assuming thermo-optic and photorefractive effects in the TFLN layer are negligible. The change in IL due to carrier effects in the Si regions are predicted to be under 1 dB as shown by Fig. 2a. Practically, such small changes are indistinguishable from other losses in this study, such as repeatability of fiber coupling in these bare-die test chips. Fiber-pigtailing the device will allow for easier testing. Although these tests were performed using long quasi-CW pulses, we expect similar performance, when packaged, under CW optical excitation as well.
As we scale to longer phase shifters (\(L_\mathrm {ps} > 1\) cm) to reduce the voltage, the walk-off between the RF and optical phases can occur from smaller velocity differences. Therefore, the changes caused by higher optical power can have a larger effect on the 3-dB bandwidth. However, our calculations show that the majority of the impairments will occur in the mode transition region rather than the phase-shifter region. The theoretical minimum length for a low-loss adiabatic taper between the transition mode and hybrid mode in this design is about 100 \(\upmu\)m37. In this batch of test chips, the transition waveguides were intentionally made longer for fabrication ease, and therefore the nonlinear losses will inevitably be higher. The feeder waveguide and taper lengths could be reduced, which in turn will minimize the TPA-induced FCA of the transition section. If the combined input and output transition sections were only 100 \(\upmu\)m long instead of 1.4 mm long as in these chips, then the additional insertion loss due to TPA would incur a 1 dB penalty only for optical powers greater than 0.6 W. For higher power operation, other materials with lower multiphoton absorption effects can be used. As an example, silicon nitride is another CMOS-compatible material, does not experience TPA in the telecom wavelength regime, and has been shown to be suitable for hybrid bonding with unpatterned LNOI56.
In summary, we have demonstrated that hybrid TFLN MZMs, which use an unetched thin-film of LN bonded to planarized crystalline Si waveguides, can withstand high optical input powers of 110 mW while maintaining high speed modulation bandwidths of 110 GHz. A high EO bandwidth was achieved by using an inductively loaded SWE design to achieve velocity matching between the RF and optical waves. The hybrid Si/LN device design was optimized to achieve a high modulation efficiency (\(V_\pi L = 3.1\) V.cm) while minimizing the nonlinear intensity dependent effects of Si. The on-chip IL of the hybrid MZM structure including the MMI couplers, transitions into and out of the bonded region and electrode interaction loss was measured to be 1.8 dB. High optical power operation was tested by amplifying quasi-CW pulses with a pulse width of 1 \(\upmu\)s and at power levels of up to 110 mW, we did not observe degradation of the EO bandwidth compared to measurements made at a conventional power level (4 mW). Compared to measurements made at an input power of 6 dBm, the additional nonlinear insertion loss was less than 1 dB at 20.4 dBm optical power. Our work demonstrates the integration of Mach-Zehnder modulators with high bandwidth and power handling capabilities well beyond the capabilities of traditional Si photonics.
Methods
Insertion loss characterization
To determine the low power (1 mW) IL of the hybrid bonded Si/LN MZM, a CW tunable laser was coupled to the device using lensed tapered fibers (2.5 \(\upmu\)m nominal mode field diameter). As shown in Fig. 6, the hybrid bonded Si/LN MZM consists of edge couplers (ECs), MMIs, wide Si transition sections and a narrow Si hybrid section. The propagation loss of the transition waveguide section is 0.8 dB/cm, measured using the cutback method57; whereas the propagation loss of the hybrid section was reported in an earlier work as 0.6 dB/cm58. To determine the IL of the 3-dB 2 \(\times\) 2 MMI splitters, adjacent test MMIs of the same design was measured, resulting in a loss of 0.2 dB per splitter. The 1 dB bandwidth of the MMI is over 50 nm with an imbalance between the output ports less than 0.3 dB. The IL of the phase shifter section was measured by subtracting the transmission spectra of the test device and an identical reference device, but without electrodes. Therefore, the IL of the \(L_\mathrm {ps} = 5\) mm long phase shifter is 0.4 dB. From these measurements, the individual component losses of the MZM were subtracted from the total transmission, resulting in an edge coupling loss of 5.2 dB/facet and an on-chip loss of 1.8 dB (assuming 0.1 dB of loss per LN edge transition) as shown in Fig. 6.
Data availability
Data underlying the results presented in this paper are not publicly available at this time but may be obtained from the corresponding author upon reasonable request.
References
Wang, C. et al. Integrated lithium niobate electro-optic modulators operating at CMOS-compatible voltages. Nature 562, 101–104 (2018).
Wang, X., Weigel, P. O., Zhao, J., Ruesing, M. & Mookherjea, S. Achieving beyond-100-GHz large-signal modulation bandwidth in hybrid silicon photonics Mach Zehnder modulators using thin film lithium niobate. APL Photon. 4, 5 (2019).
Yang, F. et al. Monolithic thin film lithium niobate electro-optic modulator with over 110 GHz bandwidth. Chin. Opt. Lett. 20, 022502 (2022).
Xu, M. et al. Dual-polarization thin-film lithium niobate in-phase quadrature modulators for terabit-per-second transmission. Optica 9, 61–62 (2022).
Ackerman, E. et al. Low noise figure, wide bandwidth analog optical link. Int. Top. Meet. Microwave Photon. MWP 2005(2005), 325–328 (2005).
Cox, C. H., Ackerman, E. I., Betts, G. E. & Prince, J. L. Limits on the performance of RF-over-fiber links and their impact on device design. IEEE Trans. Microwave Theory Tech. 54, 906–920 (2006).
Williamson, R. C. & Esman, R. D. RF photonics. J. Lightwave Technol. 26, 1145–1153 (2008).
Shams-Ansari, A. et al. Electrically pumped laser transmitter integrated on thin-film lithium niobate. Optica 9, 408–411 (2022).
Rabiei, P. & Steier, W. H. Lithium niobate ridge waveguides and modulators fabricated using smart guide. Appl. Phys. Lett. 86, 161115 (2005).
Hu, H., Ricken, R., Sohler, W. & Wehrspohn, R. Lithium niobate ridge waveguides fabricated by wet etching. IEEE Photon. Technol. Lett. 19, 417–419 (2007).
Zhao, J. et al. Shallow-etched thin-film lithium niobate waveguides for highly-efficient second-harmonic generation. Opt. Express 28, 19669–19682 (2020).
Courjal, N. et al. High aspect ratio lithium niobate ridge waveguides fabricated by optical grade dicing. J. Phys. D Appl. Phys. 44, 305101 (2011).
Wu, R. et al. Long low-loss-litium niobate on insulator waveguides with sub-nanometer surface roughness. Nanomaterials 8, 910 (2018).
Liang, Y. et al. Monolithically integrated electro-optic modulator fabricated on lithium niobate on insulator by photolithography assisted chemo-mechanical etching. J. Phys. Photon. 3, 034019 (2021).
He, M. et al. High-performance hybrid silicon and lithium niobate Mach-Zehnder modulators for 100 Gbit \(\text{ s}^{-1}\) and beyond. Nat. Photon. 13, 359–364 (2019).
Rao, A. et al. Heterogeneous microring and mach-zehnder modulators based on lithium niobate and chalcogenide glasses on silicon. Opt. Express 23, 22746–22752 (2015).
Weigel, P. O. et al. Bonded thin film lithium niobate modulator on a silicon photonics platform exceeding 100 GHz 3-dB electrical modulation bandwidth. Opt. Express 26, 23728 (2018).
Ahmed, A. N. R. et al. Subvolt electro-optical modulator on thin-film lithium niobate and silicon nitride hybrid platform. Opt. Lett. 45, 1112 (2020).
Mere, V., Valdez, F., Wang, X. & Mookherjea, S. A modular fabrication process for thin-film lithium niobate modulators with silicon photonics. J. Phys. Photon. 4, 024001 (2022).
Weigel, P. O. et al. Lightwave circuits in lithium niobate through hybrid waveguides with silicon photonics. Sci. Rep. 6, 1–9 (2016).
Tsang, H. K. et al. Optical dispersion, two-photon absorption and self-phase modulation in silicon waveguides at 1.5 \(\mu\)m wavelength. Appl. Phys. Lett. 80, 416–418 (2002).
Bristow, A. D., Rotenberg, N. & Van Driel, H. M. Two-photon absorption and kerr coefficients of silicon for 850–2200 nm. Appl. Phys. Lett. 90, 191104 (2007).
Lin, Q., Painter, O. J. & Agrawal, G. P. Nonlinear optical phenomena in silicon waveguides: Modeling and applications. Opt. Express 15, 16604–16644 (2007).
Leuthold, J., Koos, C. & Freude, W. Nonlinear silicon photonics. Nat. Photon. 4, 535–544 (2010).
Wathen, J. J. et al. Non-instantaneous optical nonlinearity of an a-Si: H nanowire waveguide. Opt. Express 22, 22730–22742 (2014).
Ikeda, K., Shen, Y. & Fainman, Y. Enhanced optical nonlinearity in amorphous silicon and its application to waveguide devices. Opt. Express 15, 17761–17771 (2007).
Cao, L., Aboketaf, A., Wang, Z. & Preble, S. Hybrid amorphous silicon (a-Si:H)-LiNbO3 electro-optic modulator. Opt. Commun. 330, 40–44 (2014).
Wang, Y. et al. Amorphous silicon-lithium niobate thin film strip-loaded waveguides. Opt. Mater. Express 7, 4018–4028 (2017).
Witzens, J. High-speed silicon photonics modulators. Proc. IEEE 106, 2158–2182 (2018).
Ghione, G. Semiconductor Devices for High-Speed Optoelectronics Vol. 116 (Cambridge University Press Cambridge, Uk, 2009).
Noguchi, K., Mitomi, O., Miyazawa, H. & Seki, S. A broadband Ti:LiNbO3 optical modulator with a ridge structure. J. Lightwave Technol. 13, 1164–1168 (1995).
Cox, C. Techniques and performance of intensity-modulation direct-detection analog optical links. IEEE Trans. Microw. Theory Tech. 45, 1375–1383 (1997).
Honardoost, A., Safian, R., Rao, A. & Fathpour, S. High-speed modeling of ultracompact electrooptic modulators. J. Lightwave Technol. 36, 5893–5902 (2018).
Kuwayama, T., Ichimura, M. & Arai, E. Interface recombination velocity of silicon-on-insulator wafers measured by microwave reflectance photoconductivity decay method with electric field. Appl. Phys. Lett. 83, 928–930 (2003).
Claps, R., Raghunathan, V., Dimitropoulos, D. & Jalali, B. Influence of nonlinear absorption on Raman amplification in Silicon waveguides. Opt. Express 12, 2774–2780 (2004).
Soref, R. & Bennett, B. Electrooptical effects in silicon. IEEE J. Quant. Electron. 23, 123–129 (1987).
Fu, Y., Ye, T., Tang, W. & Chu, T. Efficient adiabatic silicon-on-insulator waveguide taper. Photon. Res. 2, A41–A44 (2014).
Ruske, J.-P., Zeitner, B., Tunnermann, A. & Rasch, A. Photorefractive effect and high power transmission in \(\text{ LiNbO}_3\)channel waveguides. Electron. Lett. 39, 1048–1050 (2003).
Jiang, H. et al. Fast response of photorefraction in lithium niobate microresonators. Opt. Lett. 42, 3267–3270 (2017).
Poberaj, G. et al. Ion-sliced lithium niobate thin films for active photonic devices. Opt. Mater. 31, 1054–1058 (2009).
Spickermann, R. & Dagli, N. Millimetre wave coplanar slow wave structure on GaAs suitable for use in electro-optic modulators. Electron. Lett. 29, 774–775 (1993).
Sakashita, Y. & Segawa, H. Preparation and characterization of LiNbO3 thin films produced by chemical-vapor deposition. J. Appl. Phys. 77, 5995–5999 (1995).
Shin, J., Sakamoto, S. R. & Dagli, N. Conductor loss of capacitively loaded slow wave electrodes for high-speed photonic devices. J. Lightwave Technol. 29, 48–52 (2010).
Rosa, Á., Verstuyft, S., Brimont, A., Thourhout, D. V. & Sanchis, P. Microwave index engineering for slow-wave coplanar waveguides. Sci. Rep. 8, 1–8 (2018).
Kharel, P., Reimer, C., Luke, K., He, L. & Zhang, M. Breaking voltage-bandwidth limits in integrated lithium niobate modulators using micro-structured electrodes. Optica 8, 357–363 (2021).
Wang, Z. et al. Silicon-lithium niobate hybrid intensity and coherent modulators using a periodic capacitively loaded traveling-wave electrode. ACS Photon. 9, 2668–2675 (2022).
Shi, Y., Yan, L., Willner, A. E. & Member, S. High-Speed Electrooptic Modulator Characterization. J. Lightwave Technol. 21, 2358–2367 (2003).
Liu, X. et al. Wideband thin-film lithium niobate modulator with low half-wave-voltage length product. Chin. Opt. Lett. 19, 060016 (2021).
Watts, M. R., Zortman, W. A., Trotter, D. C., Young, R. W. & Lentine, A. L. Low-voltage, compact, depletion-mode, silicon mach-zehnder modulator. IEEE J. Sel. Top. Quant. Electron. 16, 159–164 (2010).
Dong, P., Chen, L. & Chen, Y.-K. High-speed low-voltage single-drive push-pull silicon Mach-zehnder modulators. Opt. Express 20, 6163–6169 (2012).
DeRose, C. T., Trotter, D. C., Zortman, W. A. & Watts, M. R. High speed travelling wave carrier depletion silicon mach-zehnder modulator. In 2012 Optical Interconnects Conference 135–136 (IEEE, 2012).
Xiao, X. et al. High-speed, low-loss silicon Mach-Zehnder modulators with doping optimization. Opt. Express 21, 4116–4125 (2013).
Li, M., Wang, L., Li, X., Xiao, X. & Yu, S. Silicon intensity Mach-Zehnder modulator for single lane 100 gb/s applications. Photon. Res. 6, 109–116 (2018).
Chen, G. et al. High performance thin-film lithium niobate modulator on a silicon substrate using periodic capacitively loaded traveling-wave electrode. APL Photon. 7, 026103 (2022).
Wu, R. et al. High-production-rate fabrication of low-loss lithium niobate electro-optic modulators using photolithography assisted chemo-mechanical etching (place). Micromachines 13, 378 (2022).
Boynton, N. et al. A heterogeneously integrated silicon photonic/lithium niobate travelling wave electro-optic modulator. Opt. Express 28, 1868–1884 (2020).
Wang, X., Valdez, F., Mere, V. & Mookherjea, S. Integrated thin-silicon passive components for hybrid silicon-lithium niobate photonics. Opt. Continuum 1, 2233–2244 (2022).
Weigel, P. O. High-Speed Hybrid Silicon-Lithium Niobate Electro-Optic Modulators & Related Technologies (University of California, San Diego, 2018).
Acknowledgements
C. Coleman, R. Scott, G. Lee, B. Szafraniec, G. VanWiggeren, V. Moskalenko, and K. K. Abdelsalam (Keysight Technologies) for useful discussions and assistance with modeling. Part of this work was performed at the San Diego Nanotechnology Infrastructure (SDNI) of UCSD, a member of the National Nanotechnology Coordinated Infrastructure, which is supported by the National Science Foundation (Grant ECCS-2025752).
Disclosures
Sandia National Laboratories is a multi mission laboratory managed and operated by National Technology and Engineering Solutions of Sandia, LLC., a wholly owned subsidiary of Honeywell International, Inc., for the U.S. Department of Energy’s National Nuclear Security Administration under contract DE-NA0003525. This paper describes objective technical results and analysis. The views, opinions and/or findings expressed are those of the author and should not be interpreted as representing the official views or policies of the Department of Defense or the U.S. Government. Distribution Statement "A": Approved for Public Release, Distribution Unlimited.
Funding
This article was funded by DOD (HR001120S0008), NASA (80NSSC17K0166), ONR (N00014-21-1-2805), U.S. Government.
Author information
Authors and Affiliations
Contributions
F.V. and X.W. designed the SOI chip layout. F.V. designed the electrode layout. V.M. bonded the chips and fabricated the electrodes at UCSD. F.V., V.M., and X.W. conducted the experiments at UCSD. N.B., T.A.F., S.A., C.D., A.T.P., A.L.S., D.C.T. and A.L.L. performed the wafer-scale silicon photonics fabrication at Sandia. S.M. conceived the experiment(s) and helped analyze the results. F.V., V.M., X.W., and S.M. prepared the manuscript. A.L.L. leads the project which principally supported this work. All authors reviewed the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Valdez, F., Mere, V., Wang, X. et al. 110 GHz, 110 mW hybrid silicon-lithium niobate Mach-Zehnder modulator. Sci Rep 12, 18611 (2022). https://doi.org/10.1038/s41598-022-23403-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-022-23403-6
- Springer Nature Limited