Abstract
Al-alloy/carbon fibre reinforced polymer (CFRP) joint systems offer exceptionally lightweight, superior fatigue behaviour and impact resistance for aerospace applications. Nevertheless, the galvanic corrosion at the joint interfaces accelerates the adhesive failure and strength damage. In this work, oxidation of Al 7075 alloy was studied by employing plasma electrolytic oxidation (PEO) and thin film sulphuric acid anodizing (TFSAA) methods, addressing their galvanic corrosion (GC) protection performance in contact with CFRP. Structural and electrochemical characterisations were carried out in tandem with varied oxidation process parameters, revealing that high voltage PEO resulted in crystallized compact ceramic coating and thus improved GC protection. A decrease in the GC current by ~ 90% has been achieved by using the PEO coating at 700 V compared with the ~ 12% current reduction of commercial TFSAA coating. Further microstructure studies revealed that the improved GC protection of the crystallized PEO coating was realized by suppressing the initiation and propagation of localized pitting due to the improved electrical isolation between the Al-alloy/CFRP interfaces. A high voltage PEO process provides sufficient energy to produce uniform and crystalline ceramic coating consisting of Al2O3 and mullite, which give rise to improved corrosion protection.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Fibre-reinforced polymer (FRP) composites are widely used in various engineering areas due to their unique properties, typically the lightweight, high specific stiffness, improved tailorability, and high corrosion resistance. Their incorporation into structural materials, forming adhesion bonding and/or mechanical joining to the host structures, can significantly reduce the weight while improve the mechanical performance. Such reinforced structures widely broadened the fit for purpose structural designs, particularly in aerospace and marine applications1,2,3,4.
Aluminium (Al)-alloy/carbon fibre reinforced polymer (CFRP) joint systems have been widely applied in aerospace industry, e.g., to fabricate the inner/outer flaps and the outer wings of airplanes1,5,6. As a promising material candidate for structural applications, the Al-alloy/CFRP systems combine the high strength of metallic materials and the lightweight of CFRPs, offering enhanced fatigue life and increased impact resistance. However, the implementation of Al-alloy/CFRP system brings up new challenges: the galvanic corrosion (GC) of Al alloy in contact with CFRP. In recent years, the GC behaviours of Al alloys have been extensively studied in contact with various metals, such as Al/Fe, Al/stainless steel, Al/Cu, Al/Mg, etc.7,8,9,10. The GC of Al-alloy in contact with CFRP has also been studied2,4,11. For example, Zou et al. investigated the corrosion effect of Al alloy in contact with CFRP in a 3.5 wt% NaCl solution and observed a severe selective corrosion on the surface of Al alloy 2219 and ZL205A11. Such selective corrosion may cause the damage of the Al-alloy/CFRP joining structures and thus degrade the mechanical properties of the components. In this regard, it is necessary to improve the corrosion resistance by suitable surface treatment of Al alloy, to electrically separate the Al-CFRP contact.
Chemical conversion, anodization, electrochemical deposition, and sol–gel process are currently the most popular surface treatment methods that have been used for Al alloys to reduce their corrosion susceptibility12,13,14,15,16. Among them, anodization produces a thin oxide film on the surface of base material with excellent adhesion and high resistance to hydration. These characters of Al anodization make it extensively used in the aerospace industry in the past few decades17. Plasma electrolytic oxidation (PEO) is evolved from the traditional anodization process, but with a much higher working voltage18,19,20. PEO coatings are quite promising for light alloys (Al- and Mg- and Ti-based ones) treatments, not only to improve their corrosion protections but also to enhance their wear resistance21,22,23,24,25,26,27,28,29,30,31. Through PEO process, a ceramic coating can be intrinsically formed on the surface under the instantaneous high temperature and strong electric field generated by sparking discharge32,33. Although the effect of PEO coatings on the general corrosion and tribological behavior of light alloys is well documented in the literature, the GC protection effect of such coating on the couples of Al-alloy/CFRP is still lacking, neither has PEO coating properties been optimized for the Al-alloy/CFRP applications.
In this work, with the zero-resistance ammeter (ZRA) method, we studied the GC behaviour between CFRP and Al 7075, which is a widely used metal-fibre system in aerospace industry. Structural and electrochemical characterizations were carried out to compare the effects of PEO coating and traditional anodization coating on the GC behaviour of the Al 7075 alloy in contact with CFRP. The effect of the PEO process voltage on the structural and compositional properties and therefore the GC protection performance was further studied, providing an optimization for the protection of Al 7075 in the Al/CFRP coupling.
Results and discussion
Electrochemical and corrosion property of Al-alloy/CFRP coupling
Al 7075 alloy has been extensively used in aerospace industry due to its high strength provided by the added strengthening phases34. They form several intermetallic precipitates with the size ranging from 1.0 to 20.0 μm as shown in the insert of Fig. 1a, which play important roles in the mechanical properties of the alloy. EDX mapping of the Al 7075 alloy before the corrosion test indicates that most of the intermetallic precipitates consisted of Al, Cu, Fe and Mg with varied compositions (Fig. S1 of Supplementary Material). The coarse particles are most likely Al7Cu2Fe and (Al,Cu)6(Fe,Cu), which are commonly formed during the solidification of Al 7075 alloy, while Mg2Si and MgZn2 intermetallics are of much smaller quantities35,36,37,38.
Figure 1a and b shows the variations in the galvanic electrode potential and current density of Al-alloy/CFRP coupling as a function of time. CFRP has more positive standard electrode potential (0.52 V) when compared with most metals (negative standard electrode potential). When CFRP was coupled to Al 7075, it served as the cathode with oxygen reduction and/or hydrogen evolution through the cathodic reactions. Likewise, Al 7075 served as the anode, where accelerated dissolution takes place driven by galvanic reactions4. The Al-alloy/CFRP couplings started with a high current density (65.7 μA/cm2) as shown in Fig. 1b. The current density rapidly decreased to lower than 49.0 μA/cm2 within 10 min, which was followed by oscillations at about 53.5 μA/cm2 in 20–80 min and about 58.0 μA/cm2 in 90–120 min, respectively. The current oscillation was typically due to the initiation of the localized corrosions and their re-passivation on the surface of the Al alloy8. In the initial stage of the corrosion, the high-density corrosion products tended to improve the performance of the electronic shielding as compared with that of the bare Al alloy. As the corrosion proceeded, the galvanic potential of Al-alloy/CFRP approached a steady state (i.e., − 0.685 V) at around 100 min and the corresponding galvanic current was around 58.2 μA/cm2. The corrosion reactions stabilized gradually with reduced fluctuations in the instantaneous current density. This indicates that the corrosion products on the surface can serve as corrosion passivator for the underneath Al alloy and they increased with the corrosion time.
Microstructures and the elemental distributions of Al, O, Cu, Fe, and Mg in the Al alloy were measured using SEM and EDX mapping after the GC testing for two hours in the 3.5 wt% NaCl electrolyte, and they are presented in Fig. 2a–f, respectively. The results indicate that the intermetallics were the initiation sites of the localized corrosions. Figure 2g and h shows the top and cross sectional view of a typical localized corroded spot. The cross sectional EDX results (Fig. S2 of Supplementary Material) of the corroded area in Fig. 2h indicates the spot was a Cu-rich intermetallic area. Their combinations reveal that Al-oxide/hydroxide precipitated at the rim of the spot and covered the opening underneath, and there was a dissolution of the Al matrix and its resultant gap between the Al matrix and the Cu-rich intermetallics. Due to the standard electrode potential difference between the intermetallics and the Al alloy matrix, the localized corrosions occur with the dissolution of either the matrix or the intermetallics38,39. The localized corrosion reactions were illustrated in Fig. 2i. The intermetallics containing Cu and Fe are cathodic with respect to the matrix and hence promote the dissolution of the matrix. In comparison, the Mg-rich intermetallics are anodic with respect to the matrix and thus preferentially dissolve themselves40. In the current study, it is reasonable to conclude that the localized electron transfers from Al to Cu promote the dissolution of the Al matrix surrounding the Cu-rich spot.
Although the oxidation products may inhibit the exchange of ions and slow down the corrosion reactions, excessive trenching will cause mechanical detachment of the particles and their dissolution into the electrolyte. The trenching effect has been discussed extensively in the literature, however, the precise mechanism is far beyond a simple galvanic coupling that caused the anodic dissolution at the interface between cathodic intermetallics and the Al alloy matrix. The locally increased pH value as a result of oxygen reduction reactions could also attack the passive films formed on the Al alloy matrix41,42.
Microstructures and phase transformations upon varied PEO process voltages
To study the effect of the PEO voltage as well as the comparison between the PEO and the conventional thin film sulphuric acid anodizing (TFSAA) process, 20-min oxidation treatments were carried out for both the TFSAA and PEO processes. Different phases can be formed on Al through PEO process as the electrolyte compounds vary43. In this work, Na2SiO3 and KOH electrolyte were employed. Some studies have shown that the SiO32− can enter the discharge channels leading to the increase of coating thickness and hardness, while KOH leads to the reduction in breakdown voltage and offers improvement in coating properties44,45. Figure 3 presents the SEM images and the XRD curves of anodized Al by TFSAA and PEO at VPEO = 300–700 V, respectively. The SEM images recorded from the surface of the Al alloy processed by TFSAA and PEO at 300 V (Fig. 3a,b), show similar porous microstructures with the pore size of around 0.2 µm and 1.0 µm, respectively. The cracks in the TFSAA coating suggested tensile stresses build-up due to the different thermal expansions between Al substrate and Al2O346 coating. There was no plasma generated at VPEO = 300 V by visual observation. As the VPEO was increased to 500 V, although onset of plasma occurred and round bumps were observed at some areas of the sample surface, the coating surface was not uniform (Fig. 3c). When the VPEO was further increased, continuously plasma spreaded on the surface of the Al alloy throughout the entire process and the plasma intensity became more violent. As a result, more compact and uniform structures were formed when the VPEO was increased to 600 and 700 V as those shown in Fig. 3d and e, respectively.
The XRD data were presented in Fig. 3g. Besides the XRD peaks from the Al substrate, no XRD peaks can be observed from the TFSAA coating and coatings grown at 300 V, indicating the amorphous nature of the coatings. Although plasma can be observed during the PEO-500 coating growth, hardly no XRD peaks can be distinguished from the Al background for PEO-500 coating, suggesting the coating is also amorphous or/and non-stoichiometric. The coating was partially crystallized at VPEO = 600 V47. More crystallized structures formed at VPEO = 700 V. Mullite (3Al2O3·2SiO2 or 2Al2O3·SiO2, JCPDS 15-0776) and Al2O3 (JCPDS 10-0425 and JCPDS 71-1123) were the two main constituents in the crystallized PEO coating. The mullite phase has a more compact structure than the Al2O3 in the PEO-produced coating48. During the PEO process, the molten alumina can react with silicate ions present in the electrolyte bath to form a stable alumina-silicate phase, i.e., the mullite49,50. Or they may transform to a mixture of γ- Al2O3 and α- Al2O3 according to literature51. The absence of the XRD peaks related to mullite or Al2O3 in the coatings produced at VPEO < 500 V indicates that the magnitude of the applied voltages was not sufficient to support these phase transformations52,53,54. The structure difference of TFSAA and PEO coatings is illustrated in Fig. 3f. The TFSAA coating was amorphous and highly porous. While the ceramic PEO coatings (VPEO > 600 V) showed much more compact crystallized structure with few isolated micro-pores, thus improved corrosion protection effects were expected.
GC protections of Al alloy by the PEO coating
Figures 4a shows the time-dependent galvanic current densities of the Al alloys, which were coated by TFSAA and PEO with varied VPEO, coupled to CFRP in 3.5 wt% NaCl. The corresponding data derived from the GC testing were summarized in Table 1. For the TFSAA and PEO-300 samples, large oscillations occurred in the current density at the initial stage and the current oscillated all the way along the testing up to 120 min. Regarding sample PEO-300 showing a more notable fluctuation, this may be caused by the larger pore size of the PEO-300 coating compared to other coatings. Larger pore size leads to wider channels for electrolyte penetration and re-passivation, thus more significant change in the potential when such events occur. The current oscillations of the anodized alloys were much more serious than that of the bare Al alloy (Fig. 1b). The highly porous structure of the anodized surface may facilitate more complex initiation and re-passivation processes by trapping the oxidized products within the pores and channels, giving rise to the increased current oscillations.
The oscillation period of galvanic current decreased with the increase of VPEO. On the other hand, for PEO-500 and PEO-600 samples, the current oscillations significantly reduced after GC for 60 min, indicating the stabilization of the corrosion and re-passivation; the stabilized current densities were 9.7 and 6.1 μA/cm2 up to 120 min, respectively. In the case of PEO-700, the current density did not exhibit apparent oscillations except the electrical noise. In this case, the galvanic current represented the anodic current of Al alloy and the current density reached to a stabilized value of 6.2 μA/cm2. Up to GC for 120 min, the galvanic current density of PEO-600 and PEO-700 were similar, and they were ~ 90% decreased from that of the Al-alloy/CFRP coupling without employing any anodization process. When compared with the TFSAA coating, the PEO-600 and PEO-700 samples can averagely reduce the galvanic current density by ~ 88% over the 120 min testing. The absence of galvanic current oscillations in the GC testing of the PEO-700 sample indicates an effective suppression of the pitting corrosions, which provides a promising corrosion protection for practical applications.
As shown in Fig. 4b, with the increase in VPEO, the amplitudes of the potential oscillations decrease. The oscillations of potential exhibited the similar trends with the oscillations of the current, due to the initiation of localized corrosion and re-passivation. The more notable potential fluctuation for PEO-300 sample is mainly caused by the larger pore size of the PEO-300 coating compared to other coatings. Larger pore size leads to wider channels for electrolyte penetration and re-passivation, thus more significant change in the potential when such events occur. For the PEO-500 sample, even though the amplitude of the potential oscillations was smaller than that of the coated Al at lower voltages, the oscillations were still observed in the first 24 min. The initial corrosion potential was − 0.2 V, and decreased to approximately − 0.55 V afterwards (stabilized voltage data also shown in Table 1). When the coating voltage was increased to 600 V, the oscillation amplitude and time were largely reduced and shortened until the galvanic potential was stabilized to be about − 0.42 V. No oscillation can be observed in the case of PEO-700 (except the electrical noise) and the stabilized potential was − 0.36 V.
Figure 5a shows the surface of PEO-500 after the galvanic coupling for two hours. Corrosion pits were clearly seen on the coating surface, and typical examples were highlighted in Fig. 5a by the red circles. Figure 5b shows a cross sectional SEM image taken from the specimen prepared by focused ion beam (FIB) at a typical corroded pit. As we discussed in the microstructure part (Fig. 3), the PEO-500 coating showed amorphous structure with some pores and cracks, which may provide some tunnels for the electrolytes thus initiating the pitting corrosion (Fig. 5c). However, such localized pitting disappeared for the PEO-600 and PEO-700 samples (Fig. 5d,e). Besides the reason of much more compact crystalized coating structure, this could also be explained by the difference in galvanic potentials. The pitting potential of Al 7075 in 3.5 wt% NaCl solution is − 0.55 V38, which is more negative than the stabilized galvanic potentials (Table 1) of PEO-600 and PEO-700 samples, i.e., − 0.42 and − 0.36 V, respectively. However, the morphology of the oxidation products on the surface of PEO-600 (circle highlights in Fig. 5d) indicates that besides the pitting damage, GC damage may also occur during the galvanic coupling with CFRP. As illustrated in Fig. 5f, the electrolyte may flow through a few micro-pores and micro-cracks forming the galvanic connecting between Al alloy and CFRP. Such connection may cause the crevice corrosion without pitting since the galvanic potential was lower than the pitting potential of Al 7075. During this process, the Al3+ ions transported through the cracks and oxidized on the coating surface. Compared with the PEO-600 sample, the PEO-700 sample exhibited much less oxidation products around the cracks and pores (Fig. 5e). It may be due to the much more compact crystalized structures of the ceramic coating. The reduced galvanic potentials, together with the surface characterizations, show that the PEO-700 coatings effectively hindered the pitting formation on the Al alloy and provide excellent protection during the Al-alloy/CFRP coupling.
The protection effect of PEO coating against GC can be explained in two aspects, one is the high insulation performance and the other is the anti-permeability55. The higher VPEO contributes enhanced plasma and higher temperature during the PEO process that provides sufficient energy for phase transformations, resulting in more crystallized compact ceramic phase with improved insulation property (e.g., see the mullite in Fig. 3f). In addition, the super high temperature tends to accelerate the diffusions, speed up the reaction, and promote the melting of the surface oxides that, in turn, contributes to the uniformity of the element distributions and the formation of the compact structures. Figure 6 shows cross-sectional SEM images and EDX mappings taken from the PEO-600 and PEO-700 samples. The PEO-produced coating layer was about 10–11 μm thick for both samples. However, the Si distribution was much more uniform in PEO-700 than that in PEO-600. The uniform element distributions and the compact structures produced by the PEO process with increased VPEO are believed to inhibit the GC.
Conclusion
PEO process has been carried out on Al alloy at various voltages for its GC protections in contact with CFRP. Structural and electrochemical characterizations show that the PEO-600 and PEO-700 coatings are dominated by crystallized Al2O3 and mullite (i.e., 3Al2O3·2SiO2 and/or 2Al2O3·SiO2) phases. Due to the electrical insulation of these ceramic phases, the galvanic coupling between the CFRP and the PEO coated Al alloy base material tends to be isolated, which provides the corrosion protection. A comparison between the anodized coatings processed by the commercial TFSAA and the PEO methods reveals that the PEO process can significantly reduce the GC current density and the reductions can be up to ~ 90% by increasing the PEO voltage. However, microscale pores and cracks appeared in PEO-produced ceramic coatings with VPEO ≤ 600 V, and they could decrease the corrosion protection effect of the coating. A high PEO process voltage of 700 V provides sufficient energy to produce uniform and crystalline structures that give rise to improved corrosion protections.
Materials and methods
Materials
The Al 7075-T6 alloy coupons of 2 mm thick were used in this study. The chemical compositions of the alloy are summarized in Table 2. The CFRP composite sheets, consisted of unidirectional carbon fibres (55 vol%) and epoxy, are also 2 mm in thickness. The interlacing structure of CFRP is shown in Fig. S3 of Supplementary Material. The surface of the Al 7075 T6 coupons was polished using SiC papers in the sequence of 400-, 600-, 800-, 1200-, and 2000-grit. After grinding, they were cleaned by ethanol and deionised water in sequence, followed by flowing air drying.
Anodizing and PEO process
The Al anodization was carried out in a two-electrode cell system using a 15 vol% H2SO4 solution as the electrolyte and a Pt wire as counter electrode56,57. The anodizing voltage was set at 15 V for 20 min with the increment of 3 V/min. The PEO process was carried out using a specially designed AC (alternating current) high voltage power supply (manufactured by SOYIPOWER, China). The Al alloy coupon was used as the working electrode and a stainless steel 316 panel (40 mm × 20 mm × 3 mm) as the counter electrode. The distance between the two electrodes was fixed at 30 mm. The processing time was 20 min at an AC frequency of 50 Hz with the duty ratio of 30%. To study the effect of the applied voltage, PEO was processed at VPEO = 300, 500, 600, and 700 V for the individual Al alloy coupon, and the coated samples were labelled as PEO-300, PEO-500, PEO-600, PEO-700, respectively. The electrolyte of the PEO process contains a mixture of 2 g/L KOH and 10 g/L Na2SiO3, the total volume is 1L. The temperature of the electrolyte was maintained at 33–35 °C throughout the PEO process using a heat exchanger. After the PEO process, the Al alloy coupons were cleaned using deionized water followed by air-blow drying.
Electrochemical testing
The flow of the galvanic coupling current between the Al 7075 T6 and CFRP specimens was monitored using Metrohm Autolab (PGSTAT302N) with ZRA model. Ag/AgCl was used as the reference electrode. The current densities and relative potentials were collected at an interval of 0.5 s. The Al alloy coupon to be tested was sealed in a sample holder that has an exposed area of 1.0 cm2. The exposed area of the CFRP sheets in this test is 0.8 cm2. The distance between the Al alloy and the CFRP electrodes is 1.0 cm. All measurements were carried out in a 3.5 wt% sodium chloride solution (pH 6.5, 25 °C) that was kept in a container open to air and without stirring.
Physical and chemical characterization
X-ray diffraction (XRD) characterizations were performed on Bruker D8 Advance with Cu-Kα X-ray source. While a JEOL Nova Nanosem 230 microscope was used for the scanning-electron microscopy (SEM) analysis and the energy dispersive X-ray (EDX) spectral analysis. Cross-section analysis was performed using a Helios NanoLab 450S dual beam focused ion beam instrument.
References
Sinmazçelik, T., Avcu, E., Bora, M. Ö. & Çoban, O. A review: Fibre metal laminates, background, bonding types and applied test methods. Mater. Des. 32, 3671–3685. https://doi.org/10.1016/j.matdes.2011.03.011 (2011).
Ireland, R., Arronche, L. & La Saponara, V. Electrochemical investigation of galvanic corrosion between aluminum 7075 and glass fiber/epoxy composites modified with carbon nanotubes. Compos. B. Eng. 43, 183–194. https://doi.org/10.1016/j.compositesb.2011.08.001 (2012).
Botelho, E. C., Silva, R. A., Pardini, L. C. & Rezende, M. C. A review on the development and properties of continuous fiber/epoxy/aluminum hybrid composites for aircraft structures. Mater. Res. 9, 247–256 (2006).
Srinivasan, R., Nelson, J. A. & Hihara, L. H. Development of guidelines to attenuate galvanic corrosion between mechanically-coupled aluminum and carbon-fiber reinforced epoxy composites using insulation layers. J. Electrochem. Soc. 162, C545–C554. https://doi.org/10.1149/2.0611510jes (2015).
Zhang, X. et al. Effect of surface treatment on the corrosion properties of magnesium-based fibre metal laminate. Appl. Surf. Sci. 396, 1264–1272. https://doi.org/10.1016/j.apsusc.2016.11.131 (2017).
Pan, L. et al. Galvanic corrosion protection and durability of polyaniline-reinforced epoxy adhesive for bond-riveted joints in AA5083/Cf/Epoxy laminates. Mater. Des. 160, 1106–1116. https://doi.org/10.1016/j.matdes.2018.10.034 (2018).
Finšgar, M. Galvanic series of different stainless steels and copper- and aluminium-based materials in acid solutions. Corros. Sci. 68, 51–56. https://doi.org/10.1016/j.corsci.2012.10.032 (2013).
Kosaba, T., Muto, I. & Sugawara, Y. Effect of anodizing on galvanic corrosion resistance of Al coupled to Fe or type 430 stainless steel in diluted synthetic seawater. Corros. Sci. 179, 109145. https://doi.org/10.1016/j.corsci.2020.109145 (2021).
Mansfeld, F., Hengstenberg, D. H. & Kenkel, J. V. Galvanic corrosion of Al alloys I. Effect of dissimilar metal. Corrosion 30, 343–353. https://doi.org/10.5006/0010-9312-30.10.343 (2013).
Bai, L.-J., Kou, G., Zhao, K., Chen, G.-T. & Yan, F.-X. Effect of in-situ micro-arc oxidation coating on the galvanic corrosion of AZ31Mg coupled to aluminum alloys. J. Alloys Compd. 775, 1077–1085. https://doi.org/10.1016/j.jallcom.2018.10.154 (2019).
Zou, S. et al. Galvanic corrosion behavior of aluminum alloy (2219 and ZL205A) coupled to carbon fiber-reinforced epoxy composites. Int. J. Electrochem. Sci. 1, 9625–9633 (2016).
Huang, Y. et al. Evaluation of the corrosion resistance of anodized aluminum 6061 using electrochemical impedance spectroscopy (EIS). Corros. Sci. 50, 3569–3575. https://doi.org/10.1016/j.corsci.2008.09.008 (2008).
Twite, R. L. & Bierwagen, G. P. Review of alternatives to chromate for corrosion protection of aluminum aerospace alloys. Prog. Org. Coat. 33, 91–100. https://doi.org/10.1016/S0300-9440(98)00015-0 (1998).
Wang, D. & Bierwagen, G. P. Sol–gel coatings on metals for corrosion protection. Prog. Org. Coat. 64, 327–338. https://doi.org/10.1016/j.porgcoat.2008.08.010 (2009).
He, Q.-Q., Zhou, M.-J. & Hu, J.-M. Electrodeposited Zn-Al layered double hydroxide films for corrosion protection of aluminum alloys. Electrochim. Acta 355, 136796. https://doi.org/10.1016/j.electacta.2020.136796 (2020).
Sheffer, M., Groysman, A. & Mandler, D. Electrodeposition of sol–gel films on Al for corrosion protection. Corros. Sci. 45, 2893–2904. https://doi.org/10.1016/S0010-938X(03)00106-9 (2003).
Zhang, J.-S., Zhao, X.-H., Zuo, Y. & Xiong, J.-P. The bonding strength and corrosion resistance of aluminum alloy by anodizing treatment in a phosphoric acid modified boric acid/sulfuric acid bath. Surf. Coat. Technol. 202, 3149–3156. https://doi.org/10.1016/j.surfcoat.2007.10.041 (2008).
Ao, N., Liu, D., Zhang, X. & He, G. Microstructural characteristics of PEO coating: Effect of surface nanocrystallization. J. Alloys Compd. 823, 153823. https://doi.org/10.1016/j.jallcom.2020.153823 (2020).
Wang, D.-D. et al. Evolution process of the plasma electrolytic oxidation (PEO) coating formed on aluminum in an alkaline sodium hexametaphosphate ((NaPO3)6) electrolyte. J. Alloys Compd. 798, 129–143. https://doi.org/10.1016/j.jallcom.2019.05.253 (2019).
Sobolev, A., Peretz, T. & Borodianskiy, K. Synthesis and growth mechanism of ceramic coatings on an Al-Cu alloy using plasma electrolytic oxidation in molten salt. J. Alloys Compd. 869, 159309. https://doi.org/10.1016/j.jallcom.2021.159309 (2021).
Wierzbicka, E. et al. Flash-PEO as an alternative to chromate conversion coatings for corrosion protection of Mg alloy. Corros. Sci. 180, 109189. https://doi.org/10.1016/j.corsci.2020.109189 (2021).
Martin, J. et al. Formation of a metastable nanostructured mullite during plasma electrolytic oxidation of aluminium in “soft” regime condition. Mater. Des. 180, 107977. https://doi.org/10.1016/j.matdes.2019.107977 (2019).
Mohedano, M., Matykina, E., Arrabal, R., Mingo, B. & Pardo, A. PEO of pre-anodized Al–Si alloys: Corrosion properties and influence of sealings. Appl. Surf. Sci. 346, 57–67. https://doi.org/10.1016/j.apsusc.2015.03.206 (2015).
Liu, C. et al. Influence of post-treatment process on corrosion and wear properties of PEO coatings on AM50 Mg alloy. J. Alloys Compd. 870, 159462. https://doi.org/10.1016/j.jallcom.2021.159462 (2021).
Gawel, L., Nieuzyla, L., Nawrat, G., Darowicki, K. & Slepski, P. Impedance monitoring of corrosion degradation of plasma electrolytic oxidation coatings (PEO) on magnesium alloy. J. Alloys Compd. 722, 406–413. https://doi.org/10.1016/j.jallcom.2017.06.120 (2017).
Wei, F., Zhang, W., Zhang, T. & Wang, F. Effect of variations of Al content on microstructure and corrosion resistance of PEO coatings on MgAl alloys. J. Alloys Compd. 690, 195–205. https://doi.org/10.1016/j.jallcom.2016.08.111 (2017).
Ma, C. et al. Anticorrosive non-crystalline coating prepared by plasma electrolytic oxidation for ship low carbon steel pipes. Sci. Rep. 10, 15675. https://doi.org/10.1038/s41598-020-72787-w (2020).
Gabor, R. et al. Preparation of highly wettable coatings on Ti–6Al–4V ELI alloy for traumatological implants using micro-arc oxidation in an alkaline electrolyte. Sci. Rep. 10, 19780. https://doi.org/10.1038/s41598-020-76448-w (2020).
Kaseem, M., Yang, H. W. & Ko, Y. G. Toward a nearly defect-free coating via high-energy plasma sparks. Sci. Rep. 7, 2378. https://doi.org/10.1038/s41598-017-02702-3 (2017).
Chen, Y., Yang, Y., Zhang, W., Zhang, T. & Wang, F. Influence of second phase on corrosion performance and formation mechanism of PEO coating on AZ91 Mg alloy. J. Alloys Compd. 718, 92–103. https://doi.org/10.1016/j.jallcom.2017.05.010 (2017).
Polo, T. O. B. et al. Plasma electrolytic oxidation as a feasible surface treatment for biomedical applications: An in vivo study. Sci. Rep. 10, 10000. https://doi.org/10.1038/s41598-020-65289-2 (2020).
Jiang, D. et al. A novel coating system with self-reparable slippery surface and active corrosion inhibition for reliable protection of Mg alloy. Chem. Eng. Prog. 373, 285–297. https://doi.org/10.1016/j.cej.2019.05.046 (2019).
Zhang, X. et al. Microstructure, formation mechanism and antifouling property of multi-layered Cu-incorporated Al2O3 coating fabricated through plasma electrolytic oxidation. Ceram. Int. 46, 2901–2909. https://doi.org/10.1016/j.ceramint.2019.09.284 (2020).
Abreu, C. M., Cristóbal, M. J., Figueroa, R. & Pena, G. Wear and corrosion performance of two different tempers (T6 and T73) of AA7075 aluminium alloy after nitrogen implantation. Appl. Surf. Sci. 327, 51–61. https://doi.org/10.1016/j.apsusc.2014.11.111 (2015).
Andreatta, F., Terryn, H. & de Wit, J. H. W. Corrosion behaviour of different tempers of AA7075 aluminium alloy. Electrochim. Acta 49, 2851–2862. https://doi.org/10.1016/j.electacta.2004.01.046 (2004).
Gao, M., Feng, C. R. & Wei, R. P. An analytical electron microscopy study of constituent particles in commercial 7075–T6 and 2024–T3 alloys. Metall. Mater. Trans. A 29, 1145–1151. https://doi.org/10.1007/s11661-998-0240-9 (1998).
Andreatta, F., Terryn, H. & de Wit, J. H. W. Effect of solution heat treatment on galvanic coupling between intermetallics and matrix in AA7075-T6. Corros. Sci. 45, 1733–1746. https://doi.org/10.1016/S0010-938X(03)00004-0 (2003).
Birbilis, N., Cavanaugh, M. K. & Buchheit, R. G. Electrochemical behavior and localized corrosion associated with Al7Cu2Fe particles in aluminum alloy 7075–T651. Corros. Sci. 48, 4202–4215. https://doi.org/10.1016/j.corsci.2006.02.007 (2006).
Boag, A., Hughes, A. E., Glenn, A. M., Muster, T. H. & McCulloch, D. Corrosion of AA2024-T3 Part I: Localised corrosion of isolated IM particles. Corros. Sci. 53, 17–26. https://doi.org/10.1016/j.corsci.2010.09.009 (2011).
Chemin, A. et al. Influence of Al7Cu2Fe intermetallic particles on the localized corrosion of high strength aluminum alloys. Mater. Des. 53, 118–123. https://doi.org/10.1016/j.matdes.2013.07.003 (2014).
Pathak, S. S., Blanton, M. D., Mendon, S. K. & Rawlins, J. W. Investigation on dual corrosion performance of magnesium-rich primer for aluminum alloys under salt spray test (ASTM B117) and natural exposure. Corros. Sci. 52, 1453–1463. https://doi.org/10.1016/j.corsci.2009.11.032 (2010).
Song, G., Johannesson, B., Hapugoda, S. & StJohn, D. Galvanic corrosion of magnesium alloy AZ91D in contact with an aluminium alloy, steel and zinc. Corros. Sci. 46, 955–977. https://doi.org/10.1016/S0010-938X(03)00190-2 (2004).
Vakili-Azghandi, M., Fattah-alhosseini, A. & Keshavarz, M. K. Optimizing the electrolyte chemistry parameters of PEO coating on 6061 Al alloy by corrosion rate measurement: Response surface methodology. Measurement 124, 252–259. https://doi.org/10.1016/j.measurement.2018.04.038 (2018).
Dunleavy, C. S., Golosnoy, I. O., Curran, J. A. & Clyne, T. W. Characterisation of discharge events during plasma electrolytic oxidation. Surf. Coat. Technol. 203, 3410–3419. https://doi.org/10.1016/j.surfcoat.2009.05.004 (2009).
Gupta, P., Tenhundfeld, G., Daigle, E. O. & Ryabkov, D. Electrolytic plasma technology: Science and engineering: An overview. Surf. Coat. Technol. 201, 8746–8760. https://doi.org/10.1016/j.surfcoat.2006.11.023 (2007).
Abd-Elnaiem, A., Mebed, A., Gaber, A. & Abdel-Rahim, M. Effect of the anodization parameters on the volume expansion of anodized aluminum films. Int. J. Electrochem. Sci. 8, 10515–10525 (2013).
Hakimizad, A. et al. The effect of pulse waveforms on surface morphology, composition and corrosion behavior of Al2O3 and Al2O3/TiO2 nano-composite PEO coatings on 7075 aluminum alloy. Surf. Coat. Technol. 324, 208–221. https://doi.org/10.1016/j.surfcoat.2017.05.068 (2017).
Liu, C. et al. The correlation between the coating structure and the corrosion behavior of the plasma electrolytic oxidation coating on aluminum. Surf. Coat. Technol. 286, 223–230. https://doi.org/10.1016/j.surfcoat.2015.12.040 (2016).
Raj, V. & Mubarak Ali, M. Formation of ceramic alumina nanocomposite coatings on aluminium for enhanced corrosion resistance. J. Mater. Process. Technol. 209, 5341–5352. https://doi.org/10.1016/j.jmatprotec.2009.04.004 (2009).
Xin, S.-G., Song, L.-X., Zhao, R.-G. & Hu, X.-F. Composition and thermal properties of the coating containing mullite and alumina. Mater. Chem. Phys. 97, 132–136. https://doi.org/10.1016/j.matchemphys.2005.07.073 (2006).
Xiaohu Huang, L. F. Plasma electrolytic oxidation coatings on aluminum alloys: Microstructures, properties, and applications. Mod. Concept Mater. Sci. 2, 1–13 (2019).
Li, K. et al. Effects of Si phase refinement on the plasma electrolytic oxidation of eutectic Al-Si alloy. J. Alloys Compd. 790, 650–656. https://doi.org/10.1016/j.jallcom.2019.03.217 (2019).
Hussein, R. O., Nie, X., Northwood, D. O., Yerokhin, A. & Matthews, A. Spectroscopic study of electrolytic plasma and discharging behaviour during the plasma electrolytic oxidation (PEO) process. J. Phys. D: Appl. Phys. 43, 105203. https://doi.org/10.1088/0022-3727/43/10/105203 (2010).
Arrabal, R. et al. Characterization and wear behaviour of PEO coatings on 6082–T6 aluminium alloy with incorporated α-Al2O3 particles. Surf. Coat. Technol. 269, 64–73. https://doi.org/10.1016/j.surfcoat.2014.10.048 (2015).
Pan, Y. et al. Galvanic corrosion behaviour of carbon fibre reinforced polymer/magnesium alloys coupling. Corros. Sci. 98, 672–677. https://doi.org/10.1016/j.corsci.2015.06.024 (2015).
Liu, H. F., Lim, E. S., Tung, P. K. H. & Xiang, N. Fabrication and transfer of nanoporous alumina thin films for templating applications: Metal dots array deposition and porous ZnO film growth. Thin Solid Films 519, 3050–3054. https://doi.org/10.1016/j.tsf.2010.12.023 (2011).
Liu, H. F., Xiang, N. & Chua, S. J. Growth of InAs on micro- and nano-scale patterned GaAs(001) substrates by molecular beam epitaxy. Nanotechnology 17, 5278–5281. https://doi.org/10.1088/0957-4484/17/20/039 (2006).
Acknowledgements
This research is supported by the Agency for Science, Technology and Research (A*STAR) under its Singapore Aerospace Program (A17-8R1709).
Author information
Authors and Affiliations
Contributions
J.L.: Conceptualization, Methodology, Investigation, Validation, Formal analysis, Writing—original draft. X.H.: Conceptualization, Methodology, Investigation, Formal analysis, Project administration, Writing—review & editing. Y.R.: Investigation, Writing—review & editing. L.M.W.: Investigation, Writing—review & editing. H.L.: Investigation, Writing—review & editing. S.W.: Conceptualization, Supervision, Project administration, Funding acquisition, Writing—review & editing.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Liu, J., Huang, X., Ren, Y. et al. Galvanic corrosion protection of Al-alloy in contact with carbon fibre reinforced polymer through plasma electrolytic oxidation treatment. Sci Rep 12, 4532 (2022). https://doi.org/10.1038/s41598-022-08727-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-022-08727-7
- Springer Nature Limited
This article is cited by
-
Effect of Different Types of Glass Powders on the Corrosion and Wear Resistance of Peo Coatings Produced on 6061 Aluminum Alloy
Metals and Materials International (2024)
-
Forming challenges of small and complex fiber metal laminate parts in aerospace applications—a review
The International Journal of Advanced Manufacturing Technology (2023)