Abstract
The aim of this study is to establish prediction models for the non-destructive evaluation of the carbonization characteristics of lignin-derived hydrochars as a carbon material in real time. Hydrochars are produced via the hydrothermal carbonization of kraft lignins for 1–5 h in the temperature range of 175–250 °C, and as the reaction severity of hydrothermal carbonization increases, the hydrochar is converted to a more carbon-intensive structure. Principal component analysis using near-infrared spectra suggests that the spectral regions at 2132 and 2267 nm assigned to lignins and 1449 nm assigned to phenolic groups of lignins are informative bands that indicate the carbonization degree. Partial least squares regression models trained with near-infrared spectra accurately predicts the carbon content, oxygen/carbon, and hydrogen/carbon ratios with high coefficients of determination and low root mean square errors. The established models demonstrate better prediction than ordinary least squares regression models.
Similar content being viewed by others
Introduction
Lignin is an abundant, naturally occurring organic material. Increasing environmental restrictions and fossil fuel prices have rendered lignocellulosic biomass an important source of renewable materials. Most of the currently commercialized carbon materials are coal based, and carbon dioxide and toxic gases generated during mining and refining can result in climate change, in addition to environmental pollution. By contrast, lignin is an eco-friendly and economical raw material that is mass produced as a byproduct of pulping in the paper industry. Lignins produced in industry are used primarily as a fuel for generating electricity and heat1. However, recent studies have been conducted to produce various high-value-added products from lignins, such as carbon fibers, activated carbon, vanillin, phenol derivatives, and phenolic resins2,3,4,5.
Hydrothermal carbonization (HTC), one of the major approaches to utilizing lignin, is a thermochemical conversion process from biomass for producing coal-like products6. Compared with pyrolysis, which is another important category of biomass conversion, HTC offers the advantage of relatively low processing requirements, stability, and nontoxicity owing to its low process temperature (180–250 °C). Hydrochars produced by the HTC of lignin can be used in various applications, including lightweight polymer composites, absorbents, electrochemical devices, energy devices, batteries, and automotive1,7,8,9, not for low-cost fuels.
Although the carbonization characteristics of lignin-derived hydrochars must be evaluated, real-time measurements are not possible through conventional elemental analysis based on high-temperature combustion and gas chromatography. Owing to its advantages of fast and non-destructive measurements, simple sample preparation, and low cost10,11, near-infrared spectroscopy (NIRS) may be a promising alternative for overcoming the limitations of conventional methods. In combination with multivariate analysis, NIRS is suitable for physical and chemical analyses of wood12,13,14,15, as well as for wood identification16,17.
The aim of this study is to establish accurate models for predicting the carbonization characteristics of kraft-lignin-derived hydrochars. The hydrochars were produced under various HTC conditions, and their elemental compositions were determined via elemental analysis. Principal component analysis (PCA) and partial least squares regression (PLSR) were employed to analyze the carbonization characteristics from near infrared (NIR) spectra obtained from the hydrochars and to establish prediction models, respectively.
Results and discussion
Elemental analysis
The elemental compositions of the hydrochars produced by HTC are listed in Table 1. The carbon content (C wt%) of the control (uncarbonized) sample was 62.83 wt%, and this value increased with the HTC temperature and residence time. The HTC process at 175 °C for 1 h increased the carbon content by approximately 2.5 wt% compared with the control, and the process at 250 °C for 5 h increased by approximately 6.5 wt%. As the HTC temperature and residence time increased, i.e., as the reaction severity increased, more carbon-intensive hydrochars were produced.
As shown in Fig. 1a, the carbon content increased logarithmically with the residence time at each temperature. This suggests that temperature imposes a more prominent effect on the carbon content than the residence time in the HTC of lignin. The van Krevelen diagram (Fig. 1b), which shows the changes in the oxygen/carbon (O/C) and hydrogen/carbon (H/C) ratios, shows the formation of a carbon-intensive structure via HTC. As the reaction severity increased, both O/C and H/C decreased. This is because HTC is an exothermic process that reduces both the oxygen and hydrogen contents of the feed via dehydration and oxidation6,18,19.
Spectral characteristics of HTC lignin
Figure 2 shows the original NIR spectra and the second-derivative spectra of hydrochars in the spectral region of 1250–2300 nm. In the original spectra (Fig. 2a), it was difficult to distinguish the difference among the spectra by the HTC temperature, except that some peaks disappeared at 250 °C. By contrast, in the second-derivative spectra (Fig. 2b), not only was the baseline of the spectrum adjusted, but the peaks were amplified, rendering the difference among the spectra with HTC temperatures more evident. Some differences were observed at wavelengths of 1449, 1685, 1927, and 2132 nm. These bands, except for those at 1927 nm assigned to water20, were associated with lignin. The bands at 1449, 1685, and 2132 nm were assigned to the phenolic group, aromatic ring associated, and lignin, respectively21,22,23,24.
PCA
Figure 3 shows a two-dimensional scatter plot of scores and loadings for the first two principal components (PCs) from the PCA of the second-derivative NIR spectra. The first two PCs constituted 96% of the total variance (Fig. 3a). In the plot, the scores for each HTC temperature were segmented into clusters. Because the scores for each HTC temperature were primarily aligned along the PC1 axis, it was discovered that this component contained information regarding the reaction severity, whereas PC2 and PC1 contained information that can determine whether HTC occurred in lignin.
In the PC loading plot (Fig. 3b), the two PCs indicated high loading values in the bands related to lignin, and among them, PC1 showed the highest values at 2132 and 2267 nm, both of which were assigned to lignin23,24. As shown from the second-derivative NIR spectra in Fig. 2b, the hydrochars and control indicated a clear spectral difference at 2132 and 2267 nm, where a higher HTC temperature resulted in a higher peak. PC2 indicated a relatively high loading at 1449 nm, which was assigned to the phenolic groups of lignin. It appeared that as the HTC temperature increased, the number of phenolic groups decreased, thereby increasing the carbon content. A decrease in the aromatic structure as the reaction severity increases has been reported in natural and HTC coals25.
Regression models
Regression models were established to predict the carbonization characteristics of kraft-lignin-derived hydrochars produced via HTC. Figure 4 shows the results of the PLSR models trained with the second-derivative NIR spectra for C (wt%), O/C, and H/C predictions. The models predicted C (wt%), O/C, and H/C with high coefficients of determination (R2) of 0.976, 0.964, and 0.984, respectively, demonstrating that PLSR with NIRS is promising for predicting the carbonization characteristics of hydrochars.
In this study, the spectral region of 1250–2300 nm was selected from the original range of 870–2500 nm and used to analyze the carbonization characteristics and establish prediction models. Although the unselected regions were noisy, some informative spectral bands related to lignin were present within these regions. Therefore, to determine whether the selection of the spectral region was appropriate, the prediction performance of the PLSR models in the second-derivative spectra with a full range of 870–2500 nm was investigated. As shown in Fig. 5, the selected spectral region (1250–2300 nm) yielded higher R2 values than those of the full spectral region (870–2500 nm) for all carbonization characteristics, thereby justifying the spectral selection.
Spectrum pretreatment contributed insignificantly to the improvement in the prediction performance of the PLSR models. Models trained with the second-derivative NIR spectra produced higher R2 values and lower root mean square errors (RMSEs) as well as reduced numbers of optimal partial least squares (PLS) factors than those trained with the original spectra (Table 2).
To evaluate the prediction performance of the PLSR models, ordinary least squares regression (OLSR) models trained with identical spectral data were developed, and their performance comparisons are listed in Table 2. The PLSR models outperformed the OLSR models in predicting all the carbonization characteristics tested. In contrast to OLSR, which used all of the selected NIR spectral regions as input variables (165-dimensional vector), PLSR yielded better performances, even from variables (PLS factors) scaled down to eight or fewer. We attribute this result to the presence of non-informative or non-contributing spectral bands for the prediction in the NIR spectra. In contrast to spectral bands assigned to the phenolic group (1449 nm), aromatic ring associated (1685 nm), and lignin (2132 and 2267 nm), bands assigned to water (1927 nm) and non-lignin-related components lack direct relevance to the HTC process. In other words, the new variables created via dimensional reduction by PLS sufficiently preserved the variance of the original data and simultaneously revealed the unique features of each observation. For data with a high correlation among input variables, i.e., high multicollinearity, it has been reported that PLSR provided more stable results than OLSR26.
The PLSR model combined with NIRS is a promising approach for predicting the carbonization characteristics of lignin-derived hydrochars produced via HTC, which allows for non-destructive analysis.
Conclusions
As the reaction severity in HTC increased, more carbon-intensive hydrochars were produced. NIRS is an effective tool for capturing information regarding the reaction severity, and PCA provided insights into some of the spectral regions that contained the information thereof. The PLSR models established with NIR data accurately predicted the carbonization characteristics of hydrochars, and the selection of the spectral region and spectral pretreatment by the second derivative improved the performance of the models. The results of this study demonstrated that the PLSR model combined with NIRS is a promising approach for the rapid and non-destructive prediction of the carbonization characteristics of kraft-lignin-derived hydrochars produced via HTC. The operational simplicity and speed of NIRS allow for real-time measurements; thus, this method can be applied to industry as an on-line measurement system in the HTC process or an at-line system if additional sample conditioning is required.
Materials and methods
Sample preparation
Hydrochars were produced by the HTC of kraft lignin, a byproduct of industrial-scale pulping for producing bleached hardwood pulp. In cooking and bleaching, a strong alkaline white liquor comprising sodium hydroxide, sodium sulfide, and chlorine dioxide is used. Suspensions of 5.6 g of lignin powder and distilled water (140 mL of distilled water, i.e., a solid-to-liquid ratio of 2/50), were hydrothermally carbonized.
Hydrothermal carbonization
To produce hydrochars from lignin and to investigate the effects of temperature and reaction time on the carbonization characteristics of lignin in HTC, the suspension was placed in a glass liner and heated for 1, 2, 3, and 5 h in a heating mantle set at temperatures of 175 °C, 200 °C, 225 °C, and 250 °C, respectively. The heating rate was 2.6 °C/min, and the reaction time refers to the period in which the temperature is maintained constant after reaching each set temperature. At the end of the target reaction time, heating was stopped, and the reaction vessel was stored at room temperature for natural cooling. Subsequently, hydrochars, i.e., solid residues formed via HTC, were vacuum filtered and dried in an oven at 60 °C for 48 h. The dried samples were pulverized and then humidified at 25 °C and 60% relative humidity for elemental analysis and NIRS measurements.
Elemental analysis
The carbonization characteristics of the hydrochars were investigated by quantifying C, H, N, and S using an elemental analyzer (Flash 2000, Thermo Fisher Scientific, Waltham, MA, USA). The C, H, N, and S in the sample reacted with pure oxygen at a high temperature of 850–950 °C and converted into CO2, H2O, N2, and SO2. These gases were purified, passed through a gas chromatography column, separated, and then quantified using a thermal conductivity detector.
NIRS
NIR spectra were obtained from the HTC lignin and control samples using an NIR spectrometer (NIR Quest, Ocean Insight, Orlando, FL, USA) equipped with a tungsten-halogen light source and a reflection probe (QR400-7-VIS-BX, Ocean Insight, Orlando, FL) with an outer diameter of 6.35 mm and a core diameter of 0.4 mm. The spectra were collected at a wavelength of 870–2500 nm and an optical resolution of 6.6 nm; subsequently, 16 scans were averaged per scan. Three spectra were obtained per sample; hence, 51 spectra were obtained from the prepared samples. Prior to performing the multivariate analysis, the original NIR spectrum was normalized and second derivatized via Savitzky–Golay filter smoothing27 to 11 points using the fifth-order function. As regions under 1250 nm and beyond 2300 nm were noisy, the spectral range of 1250–2300 nm was used for the multivariate analysis.
Multivariate analysis
PCA was performed to analyze the chemical changes in the lignin samples caused by HTC. PCA transformed the NIR data with a spectral range of 1250–2300 nm into a new orthogonal coordinate system comprising six components. The carbonization characteristics of the lignin and the spectral regions affecting it were investigated by analyzing the scores and loadings of the PCs.
PLSR was employed to establish models for predicting the carbonization characteristics of the lignin via HTC. Models that output the carbon content (C wt%), O/C ratio, and H/C ratio were designed using NIR spectral data as input variables. The optimal number of latent variables for the PLSR models was obtained using the leave-one-out cross-validation technique28. The performance of the PLSR models was evaluated using R2 and the RMSE for the calibration and prediction sets.
where \({y}_{i}\) and \({\widehat{y}}_{i}\) are the measured and predicted values of the i-th observation, respectively, μ is the overall mean, and n is the number of observations in the calibration and prediction sets. The PCA and PLSR models were implemented using Python 3.8, with programming libraries for multivariate analysis.
Data availability
The datasets generated and/or analyzed during the current study are available from the corresponding author upon reasonable request.
References
Luo, H. & Abu-Omar, M. M. Chemicals from lignin. In Encyclopedia of Sustainable Technologies (ed. Abraham, M.) 573–585 (Elsevier, 2017).
Agrawal, A., Kaushik, N. & Biswas, S. Derivatives and applications of lignin–an insight. Sci. Technol. J. 1, 30–36 (2014).
Mandlekar, N. et al. An overview on the use of lignin and its derivatives in fire retardant polymer systems. In Lignin: Trends and Applications (ed. Poletto, M.) 207–231 (InTech, 2018).
Kim, K. H., Kim, J. Y., Kim, C. S. & Choi, J. W. Pyrolysis of lignin obtained from cinnamyl alcohol dehydrogenase (CAD) downregulated Arabidopsis thaliana. J. Korean Wood Sci. Technol. 47, 442–450 (2019).
Kleinert, M. & Barth, T. Phenols from lignin. Chem. Eng. Technol. 31(5), 736–745 (2008).
Funke, A. & Ziegler, F. Hydrothermal carbonization of biomass: A summary and discussion of chemical mechanisms for process engineering. Biofuels Bioprod. Biorefin. 4(2), 160–177 (2010).
Feng, Q., Chen, F. & Wu, H. Preparation and characterization of a temperature-sensitive lignin-based hydrogel. BioResources 6, 4942–4952 (2011).
Puziy, A. M., Poddubnaya, O. I. & Sevastyanova, O. Carbon materials from technical lignins: Recent advances. Top. Curr. Chem. 376, 33. https://doi.org/10.1007/s41061-018-0210-7 (2018).
Aro, T. & Fatehi, P. Production and application of lignosulfonates and sulfonated lignin. Chemsuschem 10(9), 1861–1877 (2017).
Roggo, Y. et al. A review of near infrared spectroscopy and chemometrics in pharmaceutical technologies. J. Pharm. Biomed. Anal. 44(3), 683–700 (2007).
Tsuchikawa, S. A review of recent near infrared research for wood and paper. Appl. Spectrosc. Rev. 42(1), 43–71 (2007).
Zhou, C., Jiang, W., Via, B. K., Fasina, O. & Han, G. Prediction of mixed hardwood lignin and carbohydrate content using ATR-FTIR and FT-NIR. Carbohydr. Polym. 121, 336–341 (2015).
Raymond, C. A. & Schimleck, L. R. Development of near infrared reflectance analysis calibrations for estimating genetic parameters for cellulose content in Eucalyptus globulus. Can. J. For. Res. 32(1), 170–176 (2002).
Via, B. K., Shupe, T. F., Groom, L. H., Stine, M. & So, C. L. Multivariate modelling of density, strength and stiffness from near infrared spectra for mature, juvenile and pith wood of longleaf pine (Pinus palustris). J. Near Infrared Spectrosc. 11(5), 365–378 (2003).
Yang, S. Y. et al. Partial least squares analysis on near-infrared absorbance spectra by air-dried specific gravity of major domestic softwood species. J. Korean Wood Sci. Technol. 45, 399–408 (2017).
Horikawa, Y., Mizuno-Tazuru, S. & Sugiyama, J. Near-infrared spectroscopy as a potential method for identification of anatomically similar Japanese diploxylons. J. Wood Sci. 61(3), 251–261 (2015).
Hwang, S. W., Horikawa, Y., Lee, W. H. & Sugiyama, J. Identification of Pinus species related to historic architecture in Korea using NIR chemometric approaches. J. Wood Sci. 62(2), 156–167 (2016).
Ross, D. S., Loo, B. H., Tse, D. S. & Hirschon, A. S. Hydrothermal treatment and the oxygen functionalities in Wyodak coal. Fuel 70, 289–295 (1991).
Peterson, A. A. et al. Thermochemical biofuel production in hydrothermal media: A review of sub- and supercritical water technologies. Energy Environ. Sci. 1(1), 32–65 (2008).
Workman, J. Jr. & Weyer, L. Practical Guide and Spectral Atlas for Interpretive Near-Infrared Spectroscopy (CRC Press, 2007).
Fackler, K. & Schwanninger, M. Polysaccharide degradation and lignin modification during brown rot of spruce wood: A polarised Fourier transform near infrared study. J. Near Infrared Spectrosc. 18(6), 403–416 (2010).
Bailleres, H., Davrieux, F. & Ham-Pichavant, F. Near infrared analysis as a tool for rapid screening of some major wood characteristics in a eucalyptus breeding program. Ann. For. Sci. 59(5–6), 479–490 (2002).
Michell, A. J. & Schimleck, L. R. NIR spectroscopy of woods from Eucalyptus globulus. Appita J. 49, 23–26 (1996).
Schwanninger, M., Rodrigues, J. C. & Fackler, K. A review of band assignments in near infrared spectra of wood and wood components. J. Near Infrared Spectrosc. 19(5), 287–308 (2011).
Sugimoto, Y. & Miki, Y. Chemical structure of artificial coals obtained from cellulose, wood and peat. In Proceedings of the 9th International Conference on Coal Science 187–190, (1997).
Farahani, H. A., Rahiminezhad, A., Same, L. & Immannezhad, K. A comparison of partial least squares (PLS) and ordinary least squares (OLS) regressions in predicting of couples mental health based on their communicational patterns. Proced. Soc. Behav. Sci. 5, 1459–1463 (2010).
Savitzky, A. & Golay, M. J. E. Smoothing and differentiation of data by simplified least squares procedures. Anal. Chem. 36(8), 1627–1639 (1964).
Hastie, T., Tibshirani, R. & Friedman, J. The Elements of Statistical Learning: Data Mining, Inference, and Prediction (Springer, 2009).
Acknowledgements
This study was supported by the Korea Forestry Promotion Institute through the R&D Program for Forest Science Technology, funded by the Korea Forest Service (Project No. 2020215D10-2122-AC01). The authors thank MOORIM P&P Co., Ltd. for providing the kraft lignin. We would like to thank Editage (www.editage.co.kr) for English language editing.
Author information
Authors and Affiliations
Contributions
S.H. was the major contributor of this study and wrote the manuscript. U.H., K.J., T.L., J.P., and J.K. contributed to sample preparation and data analysis. H.K., I.C., and H.Y. conceived the original ideas. H.Y. edited the manuscript and supervised the study. All authors have read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hwang, SW., Hwang, U.T., Jo, K. et al. NIR-chemometric approaches for evaluating carbonization characteristics of hydrothermally carbonized lignin. Sci Rep 11, 16979 (2021). https://doi.org/10.1038/s41598-021-96461-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-021-96461-x
- Springer Nature Limited