Abstract
Pterogyne nitens is commonly known in northeastern Brazil as a lesser-known fast-growing species in the Caatinga biome, which is a difficult place for tree development due to the low natural fertility soils and low availability of water. Due to the importance of expanding information about the anatomical wood properties of Caatinga native species, the aim of this work was to characterize the anatomical elements, to macroscopically describe the wood and make inferences about its possible end-uses. Maceration was performed which enabled measuring fiber dimensions, pore frequency and the following technological indexes: cell wall fraction, slenderness ratio, Runkel index and flexibility coefficient. Histological sections enabled describing the arrangements of the cellular elements in different observation sections and to determine the pore diameter. P. nitens wood has anatomical arrangements characterized by confluent axial parenchyma, being diffuse-porous with the presence of tylosis and heterogeneous/stratified rays (biseriate). The fibers were classified as very short (length 0.81 mm), not flexible and Runkel index 0.82. The pores were few in number with a frequency of 32.9 pores/mm2, distributed in a diffuse format and many were obstructed by tylosis. Based on the anatomical results and considering other technological studies, P. nitens wood is most suitable for charcoal production.
Similar content being viewed by others
Introduction
The Caatinga, the only exclusively Brazilian biome, is characterized as a developing region, as the population suffers from the social effects of having a low Human Development Index (HDI), and therefore the people are often searching the forests for means of subsistence. Wood appears as an attractive, cheap and available form of energy, but its irregular extraction leads to complex environmental problems such as deforestation1. The scarcity of knowledge and appreciation of this biome contributes to rapid environmental degradation which in turn enhances the desertification processes in the region2.
The Pterogyne nitens Tul. species is known in northeastern Brazil as amendoim-bravo or madeira nova, and is considered a fast-growing species in the Caatinga. The slower growth of forest species in this biome is justified by the presence of low natural fertility soils, usually shallow and stony, and low water availability due to the intermittent nature of most of the rivers in the biome2.
Caatinga species have also tortuous and twisted trunks, which makes their use for wood products very difficult. The arboreal size of the vegetation is relatively low; it reaches about 5 m in height, rarely has canopy continuity, and has low-diameter trunks and branches3. However, the P. nitens species has a straight trunk and elevated diameter breast height (DBH), even without any type of silvicultural development; however, it often has the presence of several trunks from the same root base. This species has moderate growth speed with an average annual increase of 7 m3/ha/year, and reaches about 9 m in height at 14 years old4.
Technological studies on wood are essential to subsidize future exploitation and to better use the raw material in order to develop energetic materials from forest biomass in socially and environmentally vulnerable areas. Another important consideration is to produce scientific knowledge in areas of low productive interest, where little research is carried out. On the other hand, they are places which have species with productive potential and adaptation to other regions and/or interesting technological characteristics to be better studied.
Among technological properties, wood anatomy with details on the fiber dimensions and the cellular arrangements in the wood of trees are important in order to be able to infer about the potential use of the material5. Complementary information on chemical, physical and mechanical properties is important for a more accurate indication regarding the end use of wood.
In this sense, the objective of this study was to characterize the anatomical elements in different positions of the trunk (base and top), and to macroscopically describe the wood from the Pterogyne nitens species and to make inferences about future uses.
Methods
Collection area
Pterogyne nitens Tul. wood samples came from an approximately 10-year-old experimental plantation located at the Southwestern Bahia State University (UESB), Vitória da Conquista campus, Bahia, Brazil. Plantation area has approximately 0.72 hectare and 3 m × 3 m initial spacing, situated in the Caatinga biome6. The region has a dry to subtropical highland (Cwb) characterized by average annual precipitation of 850 mm and temperature of 25 ºC7.
Seedlings were produced in a university greenhouse, using seeds collected in a forest fragment of Montana Semi-deciduous Seasonal Forest, called “cipó forest”, also located at UESB.
Plant material collection and authorization for publication is according to Public Notification no. 986/2005, with retroactive effect since August 16th, 2004, not specific for plant material, but for all researches in the UESB. It was based on Brazilian Register of Biological Collections (CCBIO)—Normative Instruction 160/2006, that follow the Resolution 11.15 of the Convention on International Trade in Endangered Species of Wild Fauna and Flora (CITES).
Wood sampling and microtomy
Five trees (11.3 m of commercial height and DBH of 16.4 cm) were randomly chosen and a 20 cm-high disk was removed from the base and top positions of the trunk, making a total of ten samples (Fig. 1). The minimum trunk diameter for commercial height considered in the sampling step was 7 cm.
The experimental procedures were performed at the Wood Properties Laboratory, Department of Forest Engineering, Federal University of Viçosa, in Minas Gerais, Brazil.
Rectangular specimens were cut with the following dimensions according to the main structural directions of the wood: 1.5 cm in the tangential longitudinal direction; 2.0 cm in the radial longitudinal direction; and 3.0 cm in the axial direction. After sampling, the material was softened by boiling in water with glycerin and cut in a Zeiss SM2000 R model slide microtome with a nominal thickness of 20 µm.
The cuts were cleared with sodium hypochlorite, colored with safranin and mounted on semi-permanent slides. A PixeLINK PL-A662 camera was used to remove photomicrographs from the transversal section of the samples to analyze porosity, and only two of them had the longitudinal sections (tangential and radial) photographed in order to describe the arrangement of the anatomical elements.
The anatomical elements studied were measured using a Zeiss optical microscope with a 10 × objective lens, with the pore diameter and frequency being determined with the aid of the AxionVision 4.8.2 software.
Maceration of wood samples
Wooden toothpicks were used by the method of Nicholls and Dadswell8 using aster blue as a dye. The same microscope and software previously mentioned were used, however an objective lens with 10 × magnification was used to determine the length of the fibers and a 20 × lens for the width, the flame diameter and the wall thickness of these anatomical elements, making a total of 120 whole fibers measured per sample.
Measuring the dimensions of anatomical elements and technological indexes
Once the dimensions of the anatomical elements were obtained, the following were measured: (c) fiber length, in mm; (e) fiber wall thickness, in µm; (D) fiber diameter, in µm; (d) fiber lumen diameter, in µm; pore frequency, pores/mm2; pore diameter, in µm; cell wall fraction (Eq. 1); slenderness ratio (Eq. 2); Runkel index (Eq. 3); and flexibility coefficient (Eq. 4).
In which: WF is the cell wall fraction; t is the fiber wall thickness (µm); D is the fiber diameter (µm), with the cell wall fraction expressing the fiber stiffness level9.
In which: II is the slenderness ratio; l is the fiber length (µm); D is the fiber diameter (µm), and the slenderness ratio infers about the fiber’s flexibility.
In which: RI is the Runkel index; t is the fiber wall thickness (µm) d is the fiber lumen diameter (µm), in order to assess the degree of fiber collapse during the papermaking process10.
In which: FC is the flexibility coefficient; d is the fiber lumen diameter (µm); D is the fiber diameter (µm), evaluating the flexibility level of the fibers and their ability to intertwine11.
Data processing and statistical analysis
The anatomical description was based on the frequent terminologies of the current scientific literature12,13.
The statistical analysis was performed using the Assistat 7.7 software program. A completely randomized design with two treatments (base and top positions) and five repetitions (5 trees) was considered.
The Lilliefors test was adopted to test the data normality and the Cochran test was applied to verify the homogeneity of variances. The t-test was subsequently performed to compare the mean of samples.
In addition, the means and coefficients of variation of the dimensions of the anatomical elements were presented.
Results
Anatomical description of the wood in the different observation sections
The wood has very thin bark macroscopically, with an easy distinction between external bark and internal bark, both at the base and at the top. It presents a low bark percentage in relation to the wood (Table 1).
P. nitens wood has medium macroscopic visualization and distinction of the cell layers, with both the marrow and the growth rings being noticeable to the naked eye. It also has a heartwood without a characteristic odor and a dark pink color. It is moderately hard when cut manually, and has medium texture with vessels also visible to the naked eye (Fig. 2).
The heartwood and sapwood layers do not have the same facility of distinguishing them from the other layers at the studied age, with the heartwood being characterized by a pink color which is slightly darker than the sapwood. The heartwood layer thickness was 13.9 cm at the base (7.6% of variation—low variation) and 7.7 cm at the top (5.5% of variation—low variation), while the sapwood layer thickness was 3.2 cm at the base (13.3% of variation—low variation) and 2.1 cm at the top (13.5% of variation—low variation), as shown in Table 1.
The bark percentage in relation to the tree diameter varied between 5.1 (base) and 3.0% (top), being considered a species with low bark content.
Considering the transverse section, P. nitens wood microscopically presents multiple diffuse (Fig. 3a,c) and solitary vessels (Fig. 3b,d), and many vessels obstructed by tylosis (Fig. 3b,d). The axial parenchyma is predominantly confluent vasicentric (Fig. 3a) and confluent aliform (Fig. 3b). There is the presence of apotracheal parenchyma forming lines at growth layer limits.
The fibers from the macerates were classified as libriform (Fig. 4a,a’) because they are elongated cells with tapered ends and few (Figs. 4a,a’), and the vessel elements presented a simple perforation plate with only one opening, the presence of intervascular points characterized by contact between two vessels (Fig. 4b) and an appendix (Fig. 4c).
In relation to the longitudinal observation sections, the P. nitens wood showed heterogeneous and bisected stratified rays (Fig. 5a,b), with procumbent and square cells (Fig. 5c,d).
Anatomical characterization based on the dimensions of the wood cellular elements
The analysis of variance indicated that the P. nitens wood fibers and vessels present some significant differences between the base and top positions analyzed, which confirms heterogeneity of the woody tissue of this species at 10 years of age.
The means found for the anatomical elements followed by the coefficient of variation and its classifications are presented in Table 2.
The fiber width, fiber lumen diameter and vessel diameter dimensions showed significant differences, demonstrating that their dimensions were influenced by the height growth of the wood at 10 years of age. In contrast, the same was not observed in fiber length, fiber wall thickness or pore frequency (Table 1).
The P. nitens wood pores were classified as medium with a larger diameter at the top of the tree (104 µm). The pore frequency was the same across the trunk (10.2 pores/mm2), classified as few.
Technological indexes
The technological indexes obtained for P. nitens wood accompanied by their respective classification are shown in the Table 3.
Discussion
Anatomical description of wood in different observation sections
The bark of the Pterogyne nitens species showed a very thin thickness at both the base and at the top, which gave it a low bark content in relation to the wood. The thinner bark uniformity along the tree is also an important feature for industrial use. It is common for Caatinga species to present large bark thickness (thick bark), mainly as one of the adaptations to the edaphoclimatic aspects (high local evapotranspiration, for example) which are characteristic of the biome14. On the other hand, fast-growing species generally have thinner bark, such as the Eucalyptus tereticornis species, belonging to the group of eucalyptus trees with thin bark15. The shells are usually undesirable in industrial use because they generally cause problems due to the greater presence of minerals, extractives and few fibers16,17.
Macroscopic observation of native woods focusing on cell layers enables greater agility in the identification (recognition and inspection) and observation of the management effects (silvicultural tracts and attack of pests/diseases), as well as better recommendation for industrial use (wood composition and layer thickness)13,18,19. The P. nitens wood presented a secondary xylem layer with a low distinction between heartwood and sapwood, wide and visible growth rings along with the presence of a lot of initial wood, thus constituting characteristics of more homogeneous woods. This is also a characteristic of young eucalyptus harvested up to 10 years old20, but it differs greatly from the pattern of other Caatinga species which have very distinct heartwood and sapwood21.
The cross-sectional observation section of P. nitens wood is microscopically characterized by the presence of solitary and multiple vessels (Fig. 3) with diffuse disposition, which is a common pattern in the wood of most species belonging to the Fabaceae family: Cedrelinga catenaeformis and Enterolobium shomburgkii22; Caesalpinia pyramidalis23, Acacia glomerosa, Mimosa acutistipula, and Geoffaeas pinosa24.
The axial parenchyma is defined as confluent aliform (Fig. 3b) and confluent vasicentric (Fig. 3a), also observed in Caesalpinia pyramidalis23 and Albizia inundata25 species, both from the Fabaceae family.
The tangential and radial observation sections are characterized by the marked presence of heterogeneous bisected and stratified rays with procumbent and square cells, also reported in Mimosa tenuiflora specie5, a native and commercial wood easily found at Caatinga biome, also from the Fabaceae family.
The secondary xylem is characterized as juvenile and very homogeneous according to the anatomical observations and because it is a native wood in the early stages of development (10 years). The axial variation appears along the trunk and can be explained by changes in the dimensions of the anatomical elements, and by the growth and hormonal production of the tree in the last case26. The change rate in most properties is very fast in the first growth rings, so that the later rings gradually assume the adult wood characteristics27.
Anatomical characterization (measurement) of wood components
The fiber length of Pterogyne nitens was 0.80 mm and did not show significant variation with the tree height. This value is considered lower than that obtained for fibers from other hardwoods, such as Eucalyptus urograndis (0.90 mm)28 and Eucalyptus grandis (1.02 mm)29 but more similar to other species of the Fabaceae family, such as Mimosa tenuiflora (0.75 mm)5 and Machaerium villosum (0.85 mm)30. Libriform fibers of P. nitens were reported in other researches, involving species from Fabaceae family31,32,33,34.
The fiber width showed a statistically significant difference between the base and top positions of the tree, with the largest width found in the top fibers with 17.6 µm. The mean value found for P. nitens was 17.1 µm, similar to the average value of E. urograndis at 8 years of age (16.9 µm)28 and E. grandis at 10 years (19.8 µm)29. Also, when comparing the fiber width of P. nitens with other native species of northeastern Brazil, it was greater than the value found for Mimosa tenuiflora (16.4 µm), a specimen from the Fabaceae family5 and lower than the width of the Cedrella fissilis fibers—24.1 µm, and Gallesia integrifolia—18.3 µm35.
The lumen diameter of the P. nitens fibers did not show significant variation between the base and top positions, with the largest diameter being found in the top fibers with 9.34 µm. The mean value for P. nitens was 9.40 μm, being very different from the values found for eucalyptus such as E. grandis (20.41 μm)29, and E. urograndis (16.91 μm)28, and to that of other native forest species of northeastern Brazil: M. tenuiflora—5.79 μm5, C. fissilis—15.13 μm, and G. integrifolia—10.05 µm35.
The fiber wall thickness did not show significant variation between the fibers in the base and top positions. The average value found was 3.86 μm, very similar to the value reported for the E. grandis species of 3.37 μm29 and lower than the values of E. urograndis—5.61 μm28, M. tenuiflora—5.32 μm5, C. fissilis—4.48 μm35 and M. ophthalmocentra species—4.00 μm21.
Hardwoods of the Fabaceae family corroborated with the average pore diameter of P. nitens (95.0 μm), such as Copaifera langsdorffii—102.4 μm30 and Mimosa ophthalmocentra—105 μm21. However, the species under study showed lower values in relation to fast growing commercial species: E. grandis—122.2 μm29 and E. saligna—100.61 μm36.
The frequency of pores presented by P. nitens wood was 10.2 pores/mm2, being higher than the value presented for the native species of M. tenuiflora—8.0 pores/mm25, C. fissilis—5.6 pores/mm2 and G. integrifolia—6.6 pores/mm2 35.
P. nitens wood was microscopically characterized by an increase in the dimensions and frequency of the cells, with the highest values found at the top of the wood. This variation in cell dimensions results in changes in shape, arrangement and disposition through the growth rings37, axial parenchyma and pores, and justify the noticeable variations in the wood formed at the base and top of the tree.
Technological indexes
The cell wall fraction is a technological index which indicates fiber stiffness9 and values below 40% characterize extremely rigid fibers. In this sense, Pterogyne nitens fibers presented a cell wall fraction of 45.0%, indicating high stiffness. The value found in this study was lower than the values found for the Eucalyptus saligna species of 58%38 and for native Mimosa tenuiflora species of 64.74%5.
The interlacing index also indicates fiber flexibility. According to this index, high values characterize more flexible fibers and indicate better properties for paper, in addition to being related to tear resistance when the fibers are subjected to physical–mechanical evaluation (the higher this value, the greater the tear resistance)39. The slenderness ratio calculated for the P. nitens species was 46.6, which indicates more rigid fibers. This value is very similar to that found for the M. tenuiflora species of 45.55 from the same family, and lower than the value found in E. saligna—48.0%38.
The Runkel index indicates the quality of the fiber for paper production. Values below 0.25 indicate excellent quality, while values above 1.0 indicate regular quality10. The P. nitens wood had a Runkel index of 0.82, which indicates the fibers as good for paper production. This value is lower than that found for the E. saligna species of 1.40%38 and M. teinuiflora of 1.865.
The flexibility coefficient of fibers is directly associated with the strength of the paper that will be formed40. P. nitens presented a coefficient of 0.55, higher than that obtained for the E. saligna species of 0.4238 and M. tenuiflora of 0.325. Thus, in following this parameter, the wood under study has low flexible fibers.
Technological implications of Pterogyne nitens wood considering wood properties
Greater rigidity and less flexibility of the Pterogyne nitens fibers was evidenced from the anatomical information, which makes its use in papermaking difficult. In addition to the anatomical properties, other studies related to wood technology should be considered in pointing out its best use.
Considering previously study, the basic density of P. nitens wood was high (641 kg/m3) and the chemical composition showed low cellulose content (41.9%), high extractives content (7.3%) and low S:G ratio of lignin (2.2), which are undesirable characteristics in the pulping and papermaking processes. In addition, kraft pulping simulations aiming at cellulosic pulp production resulted in low purified yield (46.0%) and very low final viscosity—1079 dm3/kg41.
Otherwise, these results are interesting and desirable in charcoal production to serve the commercial and residential energy sector. Also, considering a recent study42, P. nitens wood showed satisfactory results in terms of energy characterization after carbonization at 450 °C for 4 h: 30% charcoal yield containing 77.7% fixed carbon, a calorific value of 7967 kcal/kg and apparent density of 402 kg/m3. These results are better when compared to the results presented by other native Brazilian forest species43,44,45.
However, these results are inferior to those presented by commercial eucalyptus species used for this purpose46,47,48. Thus, the management of this species in sustainable production models with a focus on genetic and silvicultural improvement can be a way to make the species more attractive for small and medium producers and entrepreneurs who need energy sources (firewood) in Caatinga regions. This action is also important to stimulate planting native forest species and slow down deforestation in this Biome.
Conclusion
Pterogyne nitens presented a heterogeneous wood with statistical differences between its anatomical elements depending on the base-top position in the wood.
The anatomical elements, dimensions and arrangements were similar to those of other species of the Fabaceae family and occurring in the Caatinga, with a strong presence of vessels obstructed by tylosis.
References
Gioda, A. Características e procedência da lenha usada na cocção no Brasil. Estudos Av. 33. https://doi.org/10.1590/s0103-4014.2019.3395.0009 (2019).
Sena, L. M. M. Conheça e Conserve a Caatinga—O Bioma Caatinga. Vol. 1 (Associação Caatinga, 2011).
Queiroz, L. P., Rapini, A. & Giulietti, A. M. Towards Greater Knowledge of the Brazilian Semi-Arid Biodiversity. (Ministério da Ciência e Tecnologia, 2006).
Campos Filho, E. M. & Sartorelli, P. A. R. Guia de Árvores Com Valor Econômico. (Agroicone, 2015).
Oliveira, E. et al. Estrutura anatômica na madeira e qualidade do carvão de Mimosa tenuiflora (Willd.) Poir. Rev. Árvore 30, 311–318. https://doi.org/10.1590/S0100-67622006000200018 (2006).
Instituto Brasileiro de Geografia e Estatítica-IBGE. Cidades. http://cidades.ibge.gov.br/xtras/home.php (2014).
Barreto-Garcia, P. A. B, Matos, P. S., Sanquetta, C. R. & Monroe, P. H. M. Inventory of organic carbon in a Pterogyne nitens Tul. plantation in Southwest Bahia, Brazil. Floresta Ambient. 26 (4). https://doi.org/10.1590/2179-8087.042616 (2019).
Ramalho, R. S. O Uso de Macerado no Estudo Anatômico de Madeiras. (UFV, 1987).
Niskoski, S., Trianoski, R., Muniz, G. I. B., Matos, J. L. M. & Batista, F. R. R. Anatomia da madeira de Toona ciliata: características das fibras para produção de papel. Floresta. 41, 717–728. https://doi.org/10.5380/rf.v41i4.25337 (2011).
Paula, J. E. & Alves, J. L. H. Madeiras Nativas do Brasil: Anatomia, Dendrologia, Dendrometria, Produção e Uso (Cinco Continentes, 2010).
Castelo, P. A. R. Avaliação da Qualidade da Madeira de Pinus taeda em Diferentes Sítios e Espaçamentos Através do Método Não Destrutivo de Ondas de Tensão (Universidade Federal do Paraná, 2007).
International Association of Wood Anatomy-IAWA. Lent of microscopic features for hardwood identification. IAWA Bull. 10, 220–359 (1989).
Silva, J. C. Anatomia da Madeira e Suas Implicações Tecnológicas. (Universidade Federal de Viçosa, 2005).
Campanha, M. M. & Araújo, F. S. Árvores e Arbustos do Sistema Agrossilvipastoril Caprinos e Ovinos. (Embrapa Caprinos e Ovinos, 2010).
Gava, J. L., Ometto, M. L., Nibe, T. M. M. & Seixas. F. Influência da espessura da casca de Eucalyptus torelliana e Eucalyptus tereticornis sobre a variação da temperatura do câmbio durante a ocorrência de um incêndio florestal. IPEF. 126–132 (1995).
Lopes, Y. L. V. et al. Avaliação do potencial técnico da madeira e cascas de Eucalyptus grandis Hill ex Maiden na produção de painéis cimento-madeira. Sci. For. 67, 111–122 (2005).
Vital, B. R., Andrade, A. M. & Valente, O. F. Influência da casca no rendimento e na qualidade do carvão vegetal de Eucalyptus grandis. IPEF. 44–49 (1989).
Botosso, P. C. Identificação Macroscópica de Madeiras: Guia Prático e Noções Básicas Para o Seu Reconhecimento. (Embrapa Florestas, 2011).
Zenid, G. J. & Ceccanti, G. C. T. Identificação Macroscópica de Madeiras. (Instituto de Pesquisas tecnológicas do Estado de São Paulo, 2007).
Costa, A. S. et al. Propriedades da Madeira de cerne e alburno de Eucalyptus camaldulensis. Ciênc. Madeira (Braz. J. Wood Sci.) 8, 10–20. https://doi.org/10.15210/cmad.v8i1.8926 (2017).
Silva, L. B., Santos, F. A. R., Gasson, P. & Cutler, D. Estudo comparativo da madeira de Mimosa ophthalmocentra Mart. ex Benth e Mimosa tenuiflora (Willd.) Poir. (Fabaceae-Mimosoideae) na Caatinga nordestina. Acta Bot. Bras. 25, 301–314. https://doi.org/10.1590/S0102-33062011000200006 (2011).
Muniz, G. I. B., Nisgoski, S., França, R. F. & Schardosin, F. Z. Anatomia comparativa da madeira e carvão de Cedrelinga catenaeformis Ducke. e Enterolobium schomburgkii Benth. para fins de identificação. Sci. For. 40, 291–297 (2012).
Silva, L. B., Santos, F. A. R., Gasson, P. & Cutler, D. Anatomia e densidade básica da madeira de Caesalpinia pyramidalis Tul. (Fabaceae), espécie endêmica da Caatinga do Nordeste do Brasil. Acta Bot. Bras. 23, 436–445. https://doi.org/10.1590/S0102-33062009000200015 (2009).
Paula, J. E. Madeiras da Caatinga úteis para produção de energia. Pesq. Agrop. Bras. 28, 153–165 (1993).
Baldin, T. & Marchiori, J. N. C. Anatomia da madeira de Albizia inundata (Mart.) Barneby & J.W. Grimes (Fabaceae). Balduinia 46, 25–31. https://doi.org/10.5902/2358198014969 (2014).
Larson, P. R. The physiological basis for wood specific gravity in conifers. in Proceedings IUFRO Division 5 Meeting (Stellenbosch, 1973).
Bendtsen, B. Properties of wood from improved and intensively managed trees. For. Prod. J. 28, 61–72 (1978).
Gonçalez, J. C., Santos, G. L., Silva Junior, F. G. S., Martins, I. S. & Costa, J. A. Relações entre dimensões de fibras e de densidade da madeira ao longo do tronco de Eucalyptus urugrandis. Sci. For. 42, 81–89 (2014).
Silva, J. C., Tomazello Filho T., Oliveira, J. T. S. & Castro, V. R. Influência da idade e da posição radial nas dimensões das fibras e dos vasos da madeira de Eucalyptus grandis Hill ex. Maiden. Rev. Árvore 31, 1081–1090. https://doi.org/10.1590/S0100-67622007000600013 (2007).
Cury, G. Descrição da estrutura anatômica do lenho e sua aplicação na identificação de espécies arbóreas do Cerrado e da Mata Atlântica do estado de São Paulo. Dissertação, Escola Superior de Agricultura “Luiz de Queiroz” (2001).
Benicio, J. R. W. et al. A new fossil Fabaceae wood from the pleistocene touro passo formation of Rio Grande do Sul, Brazil. Fossil Imprint 72, 251–264. https://doi.org/10.14446/FI.2016.251 (2016).
Carlquist, S. Wood anatomy of Cercidium (Fabaceae), with emphasis on vessel wall sculpture. Aliso 12, 235–255. https://doi.org/10.5642/aliso.19891202.02 (1989).
Longui, E. L., Romeiro, D. & Alves, E. S. Differences in antomy and potential hydraulic conductivy between rood and stem of Caesalpinia echinata Lam. (Fabaceae). Hoehnea 39, 649–655. https://doi.org/10.1590/S2236-89062012000400010 (2012).
Oskolski, A. A., Stepanova, A. V., Boatwright, J. S., Tilney, P. M. &Van Wyk, B. E. A survey of wood anatomical characters in the tribe Crotalarieae (Fabaceae) South. Afr. J. Bot. 94, 155–165. https://doi.org/10.1016/j.sajb.2014.06.006 (2014).
Motta, J. P., Oliveira, J. T. S., Braz, R. L., Duarte, A. P. C. & Alves, R. C. Caracterização da madeira de quatro espécies florestais. Ciênc. Rural. 44, 2186–2192. https://doi.org/10.1590/0103-8478cr20130479 (2014).
Alzate, S. B. A. Caracterização da madeira de árvores de clones de Eucalyptus grandis, E. saligna e E. grandis × urophylla. Tese, Escola Superior de Agricultura Luiz de Queiroz (2004).
Ramsay, W. & Briggs, D. Juvenile wood: has it come of age? in Proceedings of the Technical Workshop: Juvenile Wood—What Does It Mean to Forest Management and Forest Products 5–11 (1986).
Foekel, C. E. B., Barrichelo, L. G. & Milanez, A. F. Estudo comparativo das madeiras de Eucalyptus saligna, E. paniculata, E citriodora, E. maculata e E. tereticornis para produção de celulose sulfato. IPEF 10, 17–37 (1975).
Rocha, C. B. R. & Potiguara, R. C. V. Morfometria das fibras de folhas de Astrocaryum murumuru var. murumuru Mart. (ARECACEAE). Acta Amazon. 37, 511–516. https://doi.org/10.1590/S0044-59672007000400005 (2007).
Barrichelo, L. E. G. & Foelkel, C. E. B. Utilização de madeiras de essências florestais nativas na obtenção de celulose: bracatinga (Mimosa bracatinga), embaúba (Cecropia sp.), caixeta (Tabebuia cassinoides) e boleira (Joannesia princeps). IPEF 10, 43–56 (1975).
Pereira, A. K. S., Longue Junior, D., Mafra Neto, C. S., Colodette, J. L. & Gomes, F. J. B. Determinação da composição química e potencial de polpação da madeira Pterogyne nitens Tul. Ciênc. Florestal 29, 1490–1500. https://doi.org/10.5902/1980509831021 (2019).
Figueiredo, M. E. O., Longue Junior, D., Pereira, A. K. S, Carneiro, A. C. O. & Silva, C. M. S. Potencial da madeira de Pterogyne nitens Tul. (madeira-nova) para produção de carvão vegetal. Ciênc. Florestal. 28, 420–431. https://doi.org/10.5902/1980509831620 (2018).
Brand, M. A., Cunha, A. B., Carvalho, A. F., Brehmer, D. R. & Kuster, L. C. Análise da qualidade da madeira e do carvão vegetal produzido a partir da espécie Miconia cinnamomifolia (De Candolle) Naudin (Jacatirão-açu) na agricultura familiar, em Biguaçu, Santa Catarina. Sci. Florestalis. 41, 401–410 (2013).
Medeiros Neto, P. N. et al. Características físico-químicas e energéticas de duas espécies de ocorrência no semiárido brasileiro. Ciênc. Florestal 22, 579–588. https://doi.org/10.5902/198050986624 (2012).
Vale, A. T., Dias, I. S. & Santana, M. A. E. Relação entre as propriedades químicas, físicas e energéticas da madeira de cinco espécies do cerrado. Ciênc. Flor. 20, 137–145. https://doi.org/10.5902/198050981767 (2010).
Carneiro, A. C. O., et al. Potencial energético da madeira de Eucalyptus sp. em função da idade e de diferentes materiais genéticos. Rev. Árvore 38, 375–381. https://doi.org/10.1590/S0100-67622014000200019 (2014).
Neves, T. A. et al. Avaliação de clones de Eucalyptus em diferentes locais visando à produção de carvão vegetal. Pesquisa Florestal Bras. 31, 319–330. https://doi.org/10.4336/2011.pfb.31.68.319 (2011).
Santos, R. C. et al. Influência das propriedades químicas e da relação siringil/guaiacil da madeira de eucalipto na produção de carvão vegetal. Ciênc. Florestal 26, 657–669. https://doi.org/10.5902/1980509822765 (2016).
Acknowledgements
The authors acknowledge the financial support from the Foundation of Support for Research of the State of Bahia (FAPESB), in association with the Southwestern Bahia State University (UESB), and to the Wood Properties Laboratory of the Federal University of Viçosa (UFV) for technical support.
Author information
Authors and Affiliations
Contributions
All co-authors contributed to the study conception and design. Material preparation, data collection and analysis were performed by A.K.S.P. and C.M.d.S.N. The first draft of the manuscript was written by D.L.J. and A.M.M.L.C. and all authors commented on previous versions of the manuscript. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Pereira, A.K.S., Longue Júnior, D., Carvalho, A.M.M.L. et al. Anatomical characterization and technological properties of Pterogyne nitens wood, a very interesting species of the Brazilian Caatinga biome. Sci Rep 11, 15344 (2021). https://doi.org/10.1038/s41598-021-94785-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-021-94785-2
- Springer Nature Limited