Abstract
Grain boundary (GB) oxidation of proton-irradiated 304 nuclear grade stainless steel in primary water of pressurized water reactor was investigated. The investigation was conducted by studying microstructure of the oxide and oxide precursor formed at GB on an "atom-by-atom" basis by a combination of atom-probe tomography and transmission electron microscope. The results revealed that increasing irradiation dose promoted the GB oxidation, in correspondence with a different oxide and oxide precursor formed at the GB. Correlation of the oxide and oxide precursor with the GB oxidation behavior has been discussed in detail.
Similar content being viewed by others
Introduction
Irradiation-assisted stress corrosion cracking (IASCC) is a potential cause of material degradation that may lead to failure of austenitic stainless steel (SS) used in light water reactor core components. Up to date, numerous studies have been conducted to clarify the mechanism of IASCC1,2,3,4,5,6,7,8. It is widely accepted that localized deformation promoted by the irradiation in the alloy is a dominant mechanism for IASCC2,4,5,6,7,8. The irradiation produces high density of defect clusters such as dislocation loops and precipitates in the irradiated steels, which act as obstacles for dislocation motion and result in a heterogeneous localized deformation. The localized deformation is usually accompanied by significant changes in mechanical properties such as a large increase in yield strength and decrease in ductility8,9,10. Such changes in the irradiated steel promote localized strain accumulation at grain boundary (GB), which may result in nucleation sites of intergranular cracking5,11,12. The localized deformation, on the other hand, leads to formation of dislocation channels by annihilating the radiation-induced defects to GB2,5,10,13. As a result, the dislocation channeling could also be a potential contributor to IASCC by promoting dislocation pile-ups at the GB region and localized GB sliding. These investigations revealed that the changes in deformation modes by radiation induced microstructure and the interaction of localized dislocation channels with the GB promote the IASCC.
In the process of stress corrosion cracking, corrosion occurs simultaneously with localized deformation in the vicinity of the crack tip14,15,16, indicating that corrosion is one of the other potential contributors to IASCC. In fact, importance of the corrosion role in clarifying the mechanism of IASCC has been acknowledged. For instance, the irradiated stainless steels that are resistant to intergranular cracking at 288 °C in argon gas are susceptible to intergranular cracking in high temperature water at the same temperature2. This suggests that to fully clarify the IASCC mechanism, attentions should also be paid on the corrosion. In order to clarify the role of corrosion in IASCC, it at first needs to know how the irradiation affects the corrosion of the material, especially for the intergranular corrosion since the IASCC is usually in the intergranular mode and the initiation of intergranular SCC is directly related to the preferential intergranular corrosion7,17,18. For this reason, GB oxidation of the irradiated stainless steel will be investigated at nanoscale to attain a better understanding of the corrosion role in IASCC mechanisms.
The intergranular corrosion traditionally requires that a protective surface oxide film is not created18,19,20, which allows for the penetration of oxidation through the surface oxide film to the GB, while the subsurface GB oxidation is further dependent on protectability of intergranular oxide itself and the mass diffusion at the oxide front21,22. This suggests that to fully clarify the GB oxidation of the irradiated steel, attentions should be paid on how the irradiation affects the protectability of the surface and GB oxide, as well as the mass diffusion at the oxide front.
In recent years, the effect of irradiation on corrosion of austenitic SS has received increased attentions, while only a few studies have been reported. Our previous study as well as the study by Perrin et al. found an increase in the number and size of oxide particles formed on irradiated specimens, indicating a less protective surface oxide film by irradiation23,24. Promoted intergranular corrosion by irradiation was also confirmed in one study on irradiated 304 SS23. Discussion has mainly focused on the change in oxide composition by radiation-induce segregation (RIS). The possible change in oxide precursors and their effect on the GB corrosion, however, has not been studied. Since growth of the oxide is related to mass diffusion at the oxide/metal interface22, the oxide precursors and their interaction with microstructural defects at the oxide/matrix interface should play a role in the oxidation behavior.
The objective of this study was to present a more extensive understanding of the irradiation effects on GB oxidation in austenitic SS, using the atom probe tomography (APT) in conjunction with transmission electron microscope (TEM). Correlation of the oxide microstructure to oxidation along GB was discussed.
Experimental
Material and specimens
The material used for the experiment was solution annealed 304 nuclear grade SS (304NG SS), and alloying constituents was reported in a previous study23. Corrosion specimens with a dimension of 20 mm × 3 mm × 2 mm were cut from the steel, followed by wet grounding using SiC papers to a final grit of 3000# and diamond pastes polishing to achieve mirror-like surfaces. At last, the specimens were exposure to 40-nm colloidal silica slurry polishing for about 2 h to ensure the removal of surface residual strain before proton irradiation. The irradiation was conducted using 2 meV protons to a dose of 0.5 and 3 displacement per atom (dpa) at a dose rate of about 6 × 10–6 dpa per second (dpa/s) in a Tandetron accelerator at Michigan Ion Beam Laboratory. The irradiation temperature was controlled at 360 °C, monitored by a two-dimensional thermal imager, which could keep the target temperature variation within ± 10 °C during the irradiation. As presented in a previous work23, the irradiation created a nearly uniform damage profile within the ~ 1 to ~ 10 μm of the whole 20 µm-thick damaged layer, and showed an implantation peak at ~ 18 μm. Additional details of the irradiation setup and procedure have been available elsewhere25,26.
Analysis of RIS at grain boundary
Following the irradiation, characterization of RIS at GB on 0.5- and 3-dpa irradiated specimens was performed in an APT system (CAMECA LEAP 4000X HR). Samples for the APT examination were prepared by a FEI QUANTA 200 3D focus ion beam (FIB) system, which greatly increased the chance of hitting a selected GB in an APT tip. The random high-angle grain boundaries were of interest to select, while the small-angle and twin grain boundaries were avoided by using ion channeling contrast of the grains. The ion channel contrast corresponded to the secondary electron emission coefficient, which varied as a function of the crystallographic orientation. As a result, the grains showed different contrasts depending on their orientations. The grains sharing a small-angle boundary usually have similar ion channeling contrast due to their small orientation difference. The high-angle and twin grain boundaries, on the other hand, generally showed visible ion channeling contrast, which was used to reveal the location of the boundaries. In addition, the high-angle boundaries were usually curved, while twin boundaries were generally straight in appearance. This further aided in the boundary identification. Once a high-angle GB was selected, the APT tips were prepared using the traditional lift-out techniques, by which sample wedges were cut from the selected GB, welded on to Si micro-posts and then annular milled to diameters of ~ 100 nm. Details of the lift-out techniques were described elsewhere27. The milled tips were subsequently analyzed in the APT system at a base temperature of 50 K in laser pulsing mode with an optimized laser energy of 60 pJ and a pulse repetition frequency of 200 kHz, which allowed a quicker evaporation of the tip and minimized chances of fracture failing. Following the evaporation, the commercial CAMECA Imago Visualization and Analysis Software package (IVAS, Version 3.6.8) was used to reconstruct and analyze the data.
Corrosion test in simulated primary water
Prior to corrosion test, the irradiated specimens were once again polished by 40-nm colloidal silica slurry for about an hour, in order to achieve consistent surfaces of the 0.5- and 3-dpa irradiated specimens by removing the surfaces with a thickness of 1–2 μm. Then exposure of the specimens in simulated primary pressurized water reactor (PWR) water was conducted in a refreshed 316L autoclave at 320 °C for a fixed period of 500 h. The primary water in the autoclave contained 1200 mg/L of B as H3BO3 and 2.3 mg/L of Li as LiOH·H2O, and refreshed at a low flow rate of roughly 100 mL/min at 13 MPa pressure. Before ramping the autoclave to target temperature, the water was deoxygenated to ≤ 5 ppb dissolved oxygen by bubbling H2 gas into the water tank, followed by storing H2 in the tank with a hydrogen overpressure of 0.08 MPa, resulting in a dissolved hydrogen concentration of 2.6 mg/L. After the exposure, the specimens were removed from the autoclave for characterization of the oxide scale.
Analysis of oxide at grain boundary
Following the corrosion test, characterization of the oxide scale formed at grain boundaries in the 0.5- and 3-dpa irradiated specimens was performed to clarify the GB oxidation behavior, including the cross-section observation by a JEM-2100 TEM and the composition characterization by APT. The TEM was equipped with a Gatan 4k charge coupled device camera for capturing high-resolution TEM images. The high-resolution TEM images were involved for identifying the oxides at the GB as well as the metallic grain boundaries ahead of the oxidation front. The accurate composition profile of the oxide and oxide precursors, on the other hand, was analyzed by APT equipped with a reflection lens for high mass resolution. Additional descriptions of the APT procedure and parameters were previously presented in the section of RIS analysis.
Both the TEM and APT samples were prepared using the FEI QUANTA 200 3D FIB system, so that precise sampling of the cross-section of the oxide scale containing a portion of the same selected GB for the TEM observation and APT analysis can be attained. To be consistent with the RIS analysis, only the random high-angle GB was selected to analyze the intergranular corrosion behavior, and sampling intervals of the TEM and APT samples were controlled at 1–2 μm. One TEM sample was produced from the selected GB and a series of APT samples were extracted from the lifted-out wedge following the method described in “Analysis of RIS at grain boundary” section.
Results
RIS at grain boundary in 304NG SS
Color-coded APT atom maps of the specimens following the irradiation to a dose of 0.5 and 3 dpa at 360 °C are shown in Fig. 1a,b. As illustrated, an enrichment of Ni, Si and Fe, and a depletion of Cr at GB were evident from the individual atom density map on both specimens. While a similar nature of RIS was observed on the 0.5- and 3-dpa irradiated specimens, the magnitude of RIS showed difference, as displayed by the composition profiles across the grain boundaries shown in Fig. 1c The average RIS magnitude at the GB on 0.5-dpa irradiated specimen was measured to be 3.1 ± 0.3, 3.2 ± 0.2 and 1.8 ± 0.4 at% for Cr, Ni and Si, respectively, and increased to 7.8 ± 0.4, 5.2 ± 0.5 and 2.8 ± 0.3 at% by the 3-dpa irradiation, which suggested a higher magnitude of RIS at GB by increasing the irradiation dose. Figure 1e,f summarize the magnitude of RIS at the two grain boundaries.
Oxide at grain boundary observed by TEM
Figure 2 shows the TEM observation of the morphology of the oxide formed at the GB in 0.5- and 3-dpa irradiated specimens. It was found that a sharp oxide was formed at the grain boundary, suggesting a typical nature of intergranular corrosion. While the morphology of the oxide in 0.5- and 3-dpa irradiated specimens was similar, the depth of the penetration oxidation through the surface oxide film into the grain boundary differed with the irradiation dose. As shown in Fig. 2a,b, a penetration of oxidation with a depth of approximately 70 nm was observed on the 0.5-dpa specimen, and it increased to ~ 130 nm by increasing the irradiation dose to 3 dpa. This suggested a promoted intergranular corrosion by the irradiation.
Composition profiles of the oxide formed at the GB in 0.5- and 3-dpa irradiated specimens were performed by APT, as to be stated in the following section.
Oxide at grain boundary analyzed by APT
Figure 3a,b show two APT data sets containing part of the same grain boundaries in the 0.5- and 3-dpa irradiated specimens that were characterized in the TEM. Both data sets consist of two regions with different compositions, i.e. an oxidized GB going almost vertically down the matrix and the matrix at the bottom. The concentration profiles across the oxide/matrix interfaces shown in Fig. 3c,d revealed the composition of the oxide formed at the GB in the 0.5- and 3-dpa irradiated specimens. While the oxides were both depleted in Fe, Ni, Si and enriched in Cr, the Cr content varied with the irradiation dose. It was 32 at% in the oxide in the 0.5-dpa irradiated specimen, and decreased to 25 at% by increasing the irradiation to 3 dpa. Further, the profiles in Fig. 3c,d also displayed the composition changes across the oxide/matrix interface layer. A similar thin Ni- and Si-rich interface layer separating the matrix and oxide regions was observed in both the 0.5- and 3-dpa irradiated specimens. In the interface layers, the Ni and Si concentration in the interface layer in the 0.5-dpa irradiated specimen peaked at about 25 and 1 at%, respectively, and decreased to ~ 14 and 0.5 at% by increasing the irradiation to 3 dpa. This suggested a decreased enrichment of Ni and Si ahead of the interface between the oxide and the matrix by a higher irradiation dose.
More details of the elements distribution at the oxide/matrix interfaces was observed and analyzed by using the iso-concentration surface analysis technique (Fig. 4). The iso-concentration surface shows regions containing more/less than a given concentration of a particular element, which aids in elements distribution analysis at the interface. A concentration of 20 and 27% oxygen was employed for the 0.5- and 3-dpa irradiated specimens to reveal location of the oxide/matrix interfaces (Fig. 4a–d). At the interfaces, difference in the Ni-enrichment behavior adjacent to the oxide was observed. While both specimens showed a slight Ni enrichment ahead of the whole interface between the GB oxide and the base metal, a localized enrichment of Ni with a concentration of ~ 67 at% was also observed ahead the tip of the GB oxide in the 0.5-dpa specimen (Fig. 4c,d). This was further confirmed in Fig. 4e,f by employing iso-concentration surface of Ni with a concentration of 15 at%, which was much higher than that in the base metal (8.87 at%). The iso-concentration surface at 15 at% Ni in the 0.5-dpa specimen gave rise to a connected volume with an overall high Ni content, while the 3-dpa irradiated specimen showed a discrete concentration plot of Ni surrounding the oxide surface, suggesting a slight enrichment of Ni ahead of the interface. This was in agreement with the concentration profiles across the oxide/matrix interfaces shown in Fig. 3c,d.
Figure 5a,b show the separate maps of the evaporated species for the oxides formed at the grain boundaries in the 0.5- and 3-dpa specimens. It revealed a similar ion types prevalent in different parts of both oxides. A continuous oxygen signal was observed throughout the entire oxides, where there was a decrease in the alloying species such as Fe, Cr, Ni and Si. Further, while a slight density of Ni and Si was present in the GB oxide, NiOx and SiOx were completely undetected in all oxidized regions, suggesting the possible absence of Ni and Si oxidization. On the other hand, the presence of CrO3 suggested that all the Cr in oxides was likely oxidized since CrO3 was formed subsequently to CrO and CrO2 in case of additional oxygen. The plots of FeO, CrO and CrO2 corresponded well to the oxygen map, while the morphology of CrO3 varied with the irradiation dose. In the 3-dpa irradiated specimen, a widespread CrO3 was observed throughout the oxide. In contrast, the CrO3 in the 0.5-dpa irradiated specimen was not continuous but showed a type of filaments, suggesting a difference in concentration. Concentration profiles of evaporated species across the GB oxides in Fig. 5c,d revealed that concentration of CrO3 was increased by a higher irradiation dose (< 1% for 0.5-dpa and ~ 5% for 3-dpa).
Discussion
The previous TEM and APT analysis shown in Figs. 3, 4 and 5 revealed that the oxide formed at the GB in the 3-dpa irradiated specimen had a lower Cr content but a higher concentration of CrO3 than that in the 0.5-dpa irradiated specimen, indicating that increasing the irradiation dose led to a difference in the microstructure of the oxide formed at the GB in 304NG SS in primary PWR water. This is primarily attributed to the depletion of Cr at the primary GB by RIS, as has been discussed in a previous study23. In addition, the depletion of Cr by RIS also accounts for the formation of CrO3 by decreasing the content ratio of Cr/O in the oxide at the GB.
The APT analysis in Figs. 3 and 4 also revealed Ni enrichment ahead of the interface between the oxide and the matrix was decreased by a higher irradiation dose. Further, a localized enrichment of Ni was also observed ahead the tip of the GB oxide in the 0.5-dpa specimen. The enrichment of Ni adjacent to the oxide most likely resulted from the selective oxidation of Fe and Cr28,29,30. According to the Gibbs free energy-temperature (ΔG° − T) map of Cr-, Fe-, and Ni-oxides, the critical oxygen partial pressure required for formation of the oxides is Cr < Fe < Ni30, indicating that the Cr- and Fe-oxides were formed prior to the Ni-oxides. This was also supported by the absence of evaporated NiOx in the GB oxides (Fig. 5a,b). As the diffusion rate of Ni in Cr-enriched oxide is much lower than that of Fe21,31, the preferential oxidation of Cr along the GB could push Ni into the base metal by the growing Cr-oxide29,32,33,34,35. This led to the enrichment of Ni at the oxide/matrix interface. As such, the different Ni enrichment behavior adjacent to the oxide is again attributed to the difference in the composition of the primary GB in 0.5- and 3-dpa irradiated specimens. During the irradiation, RIS occurred as a result of the unequal participation of solutes in the vacancy and interstitial fluxes to sinks, while the depletion of Cr at GB was formed due to its faster diffusion rate than Fe and Ni3,36. According to the APT analysis of RIS shown in Fig. 1, increasing the irradiation dose led to a higher magnitude of Cr-depletion at GB. Consequently, the primary GB in 0.5-dpa irradiated specimen had a relative higher Cr content than that following 3-dpa irradiation. A higher content of Cr promoted more Cr-oxide formed at the GB, leading to a higher Ni enrichment adjacent to the oxide. Further, as GB is a more effective diffusion path than the grain33,37, localized Ni enrichment with a higher concentration ahead of the oxide tip can also be expected.
As has been acknowledged, Cr content in an oxide scale formed on austenitic alloys in high temperature water could affect the protectability of the oxide18,38,39. As such, the different oxidation behavior along the GB in 0.5- and 3-dpa irradiated specimens resulted from a combined effect of the change in Cr content of the intergranular oxide and Ni enrichment adjacent to the oxide. A higher Cr content in oxide indicated a higher protectability of the oxide, which could mitigate further oxidation by decreasing oxygen diffusion rate through the oxide itself18,23,38,39. As a result, a lower GB oxidation rate was observed in the 0.5-dpa irradiated specimen (Fig. 3) due to the lower Cr content in oxide by RIS23.
On the other hand, the depletion of Cr by RIS also affected the Ni enrichment behavior adjacent to the oxide. Difference in the Ni enrichment behavior led to difference in further oxidation along GB. The APT data in Fig. 4 shows enhanced oxidation just above the Ni-rich particle. From this it appears probable that Ni enrichment can stop or at least delay further oxygen diffusion along the GB. As a result, the lower GB oxidation rate on the 0.5-dpa specimen is a combined effect of a higher protectability of the oxide itself and a smaller diffusion rate of oxygen at the oxide/matrix interface.
The GB oxidation process for the 0.5- and 3-dpa irradiated specimens as discussed above are schematically shown in Fig. 6.
Conclusions
GB oxidation of proton-irradiated 304NG SS in primary PWR water was successfully investigated by a combination of APT and analytical TEM. The following conclusions can be drawn from the investigation:
-
1.
GB segregation of Fe, Cr, Ni and Si by RIS is measured by APT, while the RIS was increased by a higher irradiation dose.
-
2.
RIS decreases Cr content in the oxide formed at the GB in the steel in primary PWR water, in addition to the Ni enrichment adjacent to the oxide.
-
3.
Increasing the irradiation dose led to a higher GB oxidation rate in primary PWR water. This is attributed to a decreased Cr content in the oxide and Ni enrichment adjacent to the oxide by RIS.
Change history
22 April 2021
A Correction to this paper has been published: https://doi.org/10.1038/s41598-021-88868-3
References
Scott, P. A review of irradiation assisted stress corrosion cracking. J. Nucl. Mater. 211, 101–122 (1994).
Jiao, Z. & Was, G. S. The role of irradiated microstructure in the localized deformation of austenitic stainless steels. J. Nucl. Mater. 407, 34–43 (2010).
Was, G.S. Recent developments in understanding irradiation assisted stress corrosion cracking. In Proc. 11th International Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors 965–985 (Washington, 2003).
Jiao, Z., Was, G. S., Miura, T. & Fukuya, K. Aspects of ion irradiations to study localized deformation in austenitic stainless steels. J. Nucl. Mater. 452, 328–334 (2014).
Was, G. S., Farkas, D. & Robertson, I. M. Micromechanics of dislocation channeling in intergranular stress corrosion crack nucleation. Curr. Opin. Solid State Mater. Sci. 16, 134–142 (2012).
Jiao, Z. & Was, G. S. Impact of localized deformation on IASCC in austenitic stainless steels. J. Nucl. Mater. 408, 246–256 (2011).
Jiao, Z. & Was, G. S. Localized deformation and IASCC initiation in austenitic stainless steels. J. Nucl. Mater. 382, 203–209 (2008).
Fukuya, K., Fujii, K. & Kitsunai, Y. Deformation structure in 316 stainless steel irradiated in a PWR. In Proc. 12th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors 389–393 (Salt Lake City, 2005).
Bailat, C., Gröschel, F. & Victoria, M. Deformation modes of proton and neutron irradaiated strainless steels. J. Nucl. Mater. 276, 283–288 (2000).
Nishioka, H., Fukuya, K., Fujji, K. & Kitsunai, Y. Deformation structure in highly irradiated stainless steels. J. Nucl. Sci. Technol. 45, 274–287 (2008).
Fukuya, K., Nishioka, H., Fujii, K., Miura, T. & Kitsunai, T. Local strain distribution near grain boundaries under tensile stresses in highly irradiated SUS316 stainless steel. J. Nucl. Mater. 432, 67–71 (2013).
Chimi, Y. et al. Correlation between locally deformed structure and oxide film properties in austenitic stainless steel irradiated with neutrons. J. Nucl. Mater. 475, 71–80 (2016).
Karlsen, W., Dohi, K. & Onchi, T. Observations of channel deformation in mildly-deformed, low-dose 304L austenitic stainless steel. In Proc. 13th International Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (Whistler, British Columbia, 2007).
Bruemmer, S. M., Olszta, M. J., Toloczko, M. B. & Schreiber, D. K. Grain boundary selective oxidation and intergranular stress corrosion crack growth of high-purity nickel binary alloys in high-temperature hydrogenated water. Corros. Sci. 131, 310–323 (2018).
Shen, Z., Arioka, K. & Lozano-Perez, S. A mechanistic study of SCC in alloy 600 through high-resolution characterization. Corros. Sci. 132, 244–259 (2018).
Dong, L. J., Peng, Q. J., Han, E.-H., Ke, W. & Wang, L. Stress corrosion cracking in the heat affected zone of a stainless steel 308L–316L weld joint in primary water. Corros. Sci. 107, 172–181 (2016).
Nishioka, H., Fukuya, K., Fujii, K. & Torimaru, T. IASCC initiation in highly irradiated stainless steels under uniaxial constant load conditions. J. Nucl. Sci. Technol. 45, 1072–1077 (2008).
Han, Y. L., Han, E.-H., Peng, Q. J. & Ke, W. Effects of electropolishing on corrosion and stress corrosion cracking of alloy 182 in high temperature water. Corros. Sci. 121, 1–12 (2017).
Langelier, B., Persaud, S. Y., Newman, R. C. & Botton, G. A. An atom probe tomography study of internal oxidation processes in Alloy 600. Acta Mater. 109, 55–68 (2016).
Lozano-Perez, S. & Titchmarsh, J. M. TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions. Mater. High Temp. 20, 573–579 (2003).
Robertson, J. The mechanism of high temperature aqueous corrosion of stainless steels. Corros. Sci. 32, 443–465 (1991).
Macdonald, D. D. & Macdonald, M. U. Theory of steady-state passive films. J. Electrochem. Soc. 137, 2395–2402 (1990).
Deng, P. et al. Effect of irradiation on corrosion of 304 nuclear grade stainless steel in simulated PWR primary water. Corros. Sci. 127, 91–100 (2017).
Perrin, S., Marchetti, L., Duhamel, C., Sennour, M. & Jomard, F. Influence of irradiation on the oxide film formed on 316L stainless steel in PWR primary water. Oxid. Met. 80, 623–634 (2013).
Jiao, Z. & Was, G. S. Novel features of radiation-induced segregation and radiation-induced precipitation in austenitic stainless steels. Acta Mater. 59, 1220–1238 (2011).
Gupta, G., Jiao, Z., Ham, A. N., Busby, J. T. & Was, G. S. Microstructural evolution of proton irradiated T91. J. Nucl. Mater. 351, 162–173 (2006).
Miller, M. K. Atom Probe Tomography: Analusis at the Atomic Level (Springer, New York, 2012).
Terachi, T., Fujii, K. & Arioka, K. Microstructural characterization of SCC crack tip and oxide film for SUS 316 stainless steel in simulated PWR primary water at 320 °C. J. Nucl. Sci. Technol. 42, 225–232 (2005).
Deng, P., Peng, Q. J., Han, E.-H. & Ke, W. Effect of the amount of cold work on corrosion of 304 nuclear grade stainless steel in high temperature water. Corrosion 73, 1237–1249 (2017).
Lemire, R. J. & McRae, G. A. The corrosion of alloy 690 in high-temperature aqueous media-thermodynamic considerations. J. Nucl. Mater. 294, 141–147 (2001).
Dong, L. J. et al. Effect of dissolved hydrogen on corrosion of 316NG stainless steel in high temperature water. Nucl. Eng. Des. 295, 403–415 (2015).
Lozano-Perez, S., Saxey, D. W., Yamada, T. & Terachi, T. Atom-probe tomography characterization of the oxidation of stainless steel. Scr. Mater. 62, 855–858 (2010).
Kruska, K. et al. Nanoscale characterisation of grain boundary oxidation in cold-worked stainless steels. Corros. Sci. 63, 225–233 (2012).
Terachi, T., Yamada, T., Chiba, G. & Arioka, K. Influence of cold work on IGSCC of 316 stainless steel in hydrogenated high-temperature water. CORROSION 2007, paper no. 605 (Houston, TX: NACE, 2007).
Lozano-Perez, S. et al. Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content. Acta Mater. 57, 5361–5381 (2009).
Allen, T. R., Busby, J. T., Was, G. S. & Kenik, E. A. On the mechanism of radiation-induced segregation in austenitic Fe–Cr–Ni alloys. J. Nucl. Mater. 255, 44–58 (1998).
Lozano-Perez, S., Kruska, K., Iyengar, I., Terachi, T. & Yamadac, T. The role of cold work and applied stress on surface oxidation of 304 stainless steel. Corros. Sci. 56, 78–86 (2012).
Han, Y. L., Mei, J. N., Peng, Q. J., Han, E.-H. & Ke, W. Effect of electropolishing on corrosion of nuclear grade 316L stainless steel in deaerated high temperature water. Corros. Sci. 112, 625–634 (2016).
Han, Y. L., Mei, J. N., Peng, Q. J. & Han, E.-H. Ke, W, Effect of electropolishing on corrosion of alloy 600 in high temperature water. Corros. Sci. 98, 72–81 (2015).
Acknowledgements
This work is financially supported by International Science & Technology Cooperation Program of China (2014DFA50800). The authors gratefully acknowledge the Michigan Ion Beam Laboratory at the University of Michigan for performing proton implantation experiments, and Mrs. X. Liang for her support to prepare the TEM and APT samples.
Author information
Authors and Affiliations
Contributions
Q.P. conceived and designed the experiments, P.D. performed the data analyses and wrote the manuscript, E.-H.H. helped perform the analysis with constructive discussions. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
The original online version of this Article was revised: In the original version of this Article Qunjia Peng was incorrectly affiliated with ‘Nuclear Power Institute of China, Chengdu City, 610213, China’. The correct affiliations are listed here: Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, Shenyang City, 110016, China. Suzhou Nuclear Power Research Institute, Suzhou City, 215004, China.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Deng, P., Peng, Q. & Han, EH. Grain boundary oxidation of proton-irradiated nuclear grade stainless steel in simulated primary water of pressurized water reactor. Sci Rep 11, 1371 (2021). https://doi.org/10.1038/s41598-020-80600-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-80600-x
- Springer Nature Limited
We’re sorry, something doesn't seem to be working properly.
Please try refreshing the page. If that doesn't work, please contact support so we can address the problem.