Abstract
Spin-states and charge-trappings in blue organic light-emitting diodes (OLEDs) are important issues for developing high-device-performance application such as full-color displays and white illumination. However, they have not yet been completely clarified because of the lack of a study from a microscopic viewpoint. Here, we report operando electron spin resonance (ESR) spectroscopy to investigate the spin-states and charge-trappings in organic semiconductor materials used for blue OLEDs such as a blue light-emitting material 1-bis(2-naphthyl)anthracene (ADN) using metal–insulator–semiconductor (MIS) diodes, hole or electron only devices, and blue OLEDs from the microscopic viewpoint. We have clarified spin-states of electrically accumulated holes and electrons and their charge-trappings in the MIS diodes at the molecular level by directly observing their electrically-induced ESR signals; the spin-states are well reproduced by density functional theory. In contrast to a green light-emitting material, the ADN radical anions largely accumulate in the film, which will cause the large degradation of the molecule and devices. The result will give deeper understanding of blue OLEDs and be useful for developing high-performance and durable devices.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Organic light-emitting diodes (OLEDs) have features such as highly efficient spontaneous-light-emission and flexibility and have attracted much attention as higher-generation displays and lighting1,2,3,4. A practical fluorescent OLED has been reported in 19875, then phosphorescent OLEDs have been developed6. More recently, efficient OLEDs utilizing thermally activated delayed fluorescence (TADF) have been reported, and they have been extensively studied from a fundamental viewpoint7,8. However, fluorescent materials have been still used mainly as luminescent materials for practical OLEDs from viewpoints of material cost, lifetime, and stability. Many studies have been performed on fluorescent OLEDs with a typical green light-emitting material tris(8-hydroxyquinoline) aluminum (Alq3)5,9,10,11,12,13. However, studies on blue light-emitting materials have not yet been fully performed with respect to high efficiency and long lifetime, compared to those on red or green light-emitting materials, because of the wide bandgap and the problem of complicated multilayered structures of blue OLEDs14,15,16,17,18,19,20,21,22,23,24,25. Such study on blue OLED materials in addition to red and green OLED materials is important to further develop products such as high-performance full-color display.
Blue OLED materials need the wide bandgap between energy levels of highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO). Owing to this reason, there have been problems for the device-performance improvement of blue OLEDs because of the difficulties such as stable molecular design, the increase in nonradiative deactivation rate by trapping sites, the increase in the difficulty in manufacturing high-efficiency devices by multilayered structures, etc14,15,16,17,18,19,20,21,22,23,24,25. It is not easy to measure what kind of changes occurring during device operation in multilayered thin-films. The internal states inside the devices cannot be directly obtained with macroscopic measurements such as current–voltage characteristics, and the information inside the devices cannot be also measured from the surface observation of devices. Thus, it is very important to clarify the internal states of devices during device operation from a microscopic viewpoint because these states are essential to determine the device performance and durability.
Electron spin resonance (ESR) spectroscopy is one of the useful measurement methods to study the microscopic states of devices. The ESR method can evaluate materials at the molecular level using unpaired electrons as a probe and can directly observe films and devices nondestructively. In particular, the ESR method has a feature of operando evaluation for the inside of devices. With this ESR method, studies have been performed from a microscopic viewpoint such as the spin-states of charges in organic devices, the charge-trappings in thin-films and at interfaces, and the orientation of molecules26,27,28,29,30,31,32,33,34. For OLED research, the correlation between the formation of radical species and the luminance degradation during device operation has been discussed using an electron transport material 4,7-diphenyl-1,10-phenanthroline (BPhen)21 and the green fluorescent material Alq332. However, no ESR research has been performed on the spin-states of blue OLED materials in addition to their devices during device operation.
Here, we report operando spin analysis of organic devices to directly elucidate the microscopic properties of blue OLED materials such as 1-bis(2-naphthyl)anthracene (ADN) in their devices. The reason for the use of ADN is to firstly study the blue OLED with a simple spin-state. That is, the fluorescent ADN is expected to show no complicated ESR signal due to triplet states that are expected for phosphorescent or TADF OLED materials. Metal–insulator–semiconductor (MIS) diode structures were fabricated, and the spin-states of the blue OLED materials and the charge dynamics in the devices have been clarified at the molecular level using operando ESR method, for the first time to the best of our knowledge. Clear ESR signals from the blue OLED materials were observed and their g-factors have been well reproduced by density functional theory (DFT). The existence of charge-trappings in the organic layers has been identified from the microscopic viewpoint. Moreover, the long-lived electron accumulation in ADN and Alq3 has been directly demonstrated at the molecular level. Electron or hole only devices and blue OLEDs have been studied with the ESR method for a comparison with the results of the MIS diodes. Our results will indicate that long-lived electron accumulation exists in blue OLEDs during device operation, and that such anion radicals react with oxygen and/or moisture in blue OLEDs during device operation, which will be one of the device-degradation causes, as discussed for Alq3-based OLEDs9.
Materials and methods
To attain a high signal-to-noise ratio of the ESR signal by increasing the device’s active area, we utilized a rectangular device structure (3 mm × 30 mm) in an ESR sample tube with an inner diameter of 3.5 mm33,34. The schematic of an organic MIS diode structure and the cross section are shown in Fig. 1a,b, respectively. The chemical structures of employed organic semiconductor materials are shown in Fig. 2. Figure 1c shows the energy diagram of the organic materials and electrodes of the blue OLED targeted in this study. A blue light-emitting material ADN, a hole transport material N,N,N',N'-tetrakis(4-biphenylyl)benzidine (TBD), and an electron transport material Alq3 were used as semiconductor layers in the MIS diodes. An ion-gel was used as the insulator. High charge density in semiconductors and low-voltage device operation have been achieved with the high-capacitance ion-gel insulator forming electric double layers (EDLs) at the semiconductor/insulator interfaces31,35,36,37. The ion-gel is composed of ionic liquid 1-ethyl-3-methylimidazolium (EMIM) and bis(trifluoromethylsulfonyl)imide (TFSI), and a gelator ABA-type triblock copolymer poly(styrene-b-methylmethacylate-b-styrene) (PS-PMMA-PS) (Fig. 2). Ni/Au or Al/LiF contact electrode was used for hole or electron injection, respectively, which was fabricated on a quartz substrate with a vacuum-deposition method (Fig. 1b). Ni/Au gate electrode was deposited on a polyethylene terephthalate (PET) substrate with the vacuum-deposition method. Here, Ni was used as an adhesion layer between Au and quartz or PET substrate. The layers of ADN, TBD, and Alq3 were formed on the contact electrode with the vacuum-evaporation method. An ion-gel was deposited on the gate electrode with a drop-casting method. Then the ion-gel was placed on the semiconductor layer, completing the MIS diode. The fabricated device was sealed in the ESR sample tube together with a desiccant in a nitrogen-filled glove box to suppress the influence by oxygen and moisture10. For a companion with the studies of the MIS diodes, we have fabricated hole or electron only devices and the above-mentioned blue OLEDs (Fig. 1c) with a method similar to that mentioned above.
The fabricated MIS diodes, hole or electron only devices, and blue OLEDs were measured with an ESR spectrometer and a source meter. A standard Mn2+ marker sample was used to calibrate the g-factor, the ESR linewidth, and the number of spins. The g-factor was evaluated from the resonance magnetic field where the ESR spectrum with a first derivative form has a value of zero. The peak-to-peak ESR linewidth (ΔHpp) was evaluated as the difference between the two magnetic fields at a peak and valley in the ESR spectrum. The gate-voltage VG was applied to the MIS diodes, and the ESR measurements were performed at room temperature. The direction of the external magnetic field H was parallel to the substrate plane unless otherwise stated. Further details of experimental methods are described in the “Methods” section.
The reasons why we use the MIS diodes are as follows. First, the use of the MIS diodes clearly selects the electric charge polarity such as cations and anions in the organic layer in the devices. This selection is important to identify the nature of charge species in the organic layer. In the case of OLEDs, it is usually hard to select the charge polarity in the organic layer. Second, we utilize a continuous-wave ESR method with a modulation frequency of 100 kHz for the H, that is, lock-in detection, in our ESR experiments30,31,32,33,34. Thus, the charge carriers with a lifetime of < 10 μs in OLEDs, which contribute to the standard OLED operation, cannot be observed using the present ESR method30,31,32,33,34. Here we mean the term of “lifetime” for the duration of the existence of charge carriers in devices. Thus, the observed ESR signals are due to charge carriers with a lifetime of > 10 μs in devices, namely, accumulated (or deeply trapped) carriers30,31,32,33,34. The lifetime of charges in the MIS diodes are enough longer than 10 μs because the charges in the semiconductor are accumulated in the MIS diodes. The 10-μs lifetime is calculated from one cycle of the H modulation frequency of 100 kHz, that is, 1/(100 × 103) (1/s−1). In the case of OLEDs, a typical lifetime of charge carriers in devices is estimated to be < 10 μs when we use the following parameters according to the literatures1,2,3: a mobility of > 2 × 10−6 cm2 V−1 s−1, an electric field in a device of 5 × 105 V cm−1, and a film thickness of 100 nm. This estimated lifetime is much shorter than that in the MIS diodes.
Results and discussion
Operando ESR spectra of organic devices
First, we present the spin-states of the blue light-emitting material ADN, the hole-transport material TBD, and the electron-transport material Alq3 in the MIS diodes using the operando ESR spectroscopy. Figure 3a,b outline the charge-accumulation mechanisms. When the ion-gel is polarized by a negative (or positive) VG, holes (or electrons) are electrically accumulated in the semiconductor at the semiconductor/ion-gel interface (Fig. 3a,b). In this case, an EDL is formed at the interface, which increases the electric capacity and decreases the charge-injection threshold voltage; the capacitance increase is one order of magnitude higher than that of MIS diodes with conventional solid insulators31,35,36,37.
The operando ESR spectra with the MIS diodes are shown in Fig. 4. In each figure, each data has the same scale in the axis of ordinate to compare the magnitude variation by VG, that is, the y-axes in Fig. 4 are adjusted for the different curves to have the same scale. The lower and upper data in each figure show the ESR spectrum of each MIS diode before and after VG application, respectively. The middle data shows the ESR spectrum of each MIS diode under VG application. When VG = 0 V before VG application, as shown by the lower data in each figure, no ESR signal was observed except for Fig. 4d, which means no doping of molecules due to extrinsic effects such as oxygen etc. before VG application. In contrast, a clear signal was observed with VG; an example of the signal is shown by the middle data in each figure. The ESR parameters, g-factor and peak-to-peak ESR linewidth ΔHpp, of each observed ESR spectrum have been measured and are summarized in Table 1. All spectra in Fig. 4 show an almost single resonance line. The observed signal in each figure has the same g-factor and ΔHpp, and only the intensity depends on VG. Here, we discuss the features of each spectrum using g-factor and ΔHpp, and do not discuss the dependence of the intensity or number of spins in the devices on VG because the information of the g-factor and ΔHpp is enough to identify the charge species. Figure 4a,b show the hole accumulation in ADN and TBD, respectively, and Fig. 4c,d show the electron accumulation in ADN and Alq3, respectively. These charges are electrically accumulated at a few voltages, which confirms the high-charge-accumulation capability by the ion-gel31. It should be noted that the ESR signals due to the electrically accumulated holes and electrons in ADN and holes in TBD have been clearly observed for the first time by using the high-capacitance ion-gel gated devices. The ESR studies with MIS diodes with conventional solid insulators could not show such clearly electrically-induced ESR signals because of low-capacitance solid insulators compared to the high-capacitance ion-gel insulator.
For the case in Fig. 4d, one can notice a weak signal with g = 2.0028 ± 0.0002 at VG = 0 V before VG application. The origin of the signal has been ascribed to Alq3 radical anions formed by electron doping due to the reaction at the interfaces of Alq3/LiF/Al layer: 3LiF + Al + 3Alq3 → AlF3 + 3Li+Alq3−32. In this case, Li atom is a light element with small spin-orbital interaction and has no large contribution to the g-factor shift, which results in a good agreement with the theoretical calculation for Alq3 radical anions shown in Table 2.
We here present the VG response of the ESR signal. As shown by the upper data in Fig. 4a,b, when the VG was returned to 0 V, the ESR signals due to electrically accumulated holes in ADN and TBD disappeared completely. These data confirm that the hole accumulation shows complete reversibility upon the VG application. In contrast, for the electron accumulation in ADN and Alq3, a considerably large or small ESR signal remained after turning off the VG, as shown by the upper data in Fig. 4c,d, respectively. The residual ESR signals will be discussed later in detail.
To examine the molecular orientation for the charge-accumulation sites in the organic materials, we measured the anisotropy of the ESR signals of all MIS diodes with respect to the direction of the external magnetic field H to the substrate plane. Although the H direction was varied from parallel to perpendicular to the substrate plane at the 15° intervals, we observed no ESR anisotropy within the error bars of the g-factor (0.0001–0.0002) and ΔHpp (0.01 mT) (see Table 1). Therefore, this anisotropy demonstrates that the molecules where charges electrically accumulate are amorphous, not oriented, in the thin-films. Such amorphous nature has been often observed for OLED materials32.
DFT analysis of spin-states of electrically accumulated charges
To analyze the g-factors obtained from the ESR spectra, DFT calculation was performed. We used the B3LYP functional and the 6-31G+(d,p) basis set for the DFT calculation with Gaussian 0938. For the DFT calculation, the cation state of the TBD monomer, the cation and anion states of the ADN monomer, and the anion state of the Alq3 monomer were calculated under structural optimization conditions. The obtained principle values (g1, g2, g3) of the g-tensors are summarized in Table 2, and the spin-density distributions of these states are shown in Fig. 5. As shown in Fig. 5, the spin-density spatially spreads over the molecules, except for the Alq3 anion. For the Alq3 anion, the present results of the principle values and spin-density distribution that are obtained with the B3LYP/6-31G+(d,p) level are almost consistent with those obtained by the previous work with the B3LYP/6-31G(d) level39.
The organic molecules with charge accumulation have amorphous nature for molecular orientation, as mentioned above. Thus, to compare the calculated g-factors (Table 2) with the experimental values (Table 1), the average value of the principle values, gave, was calculated. For the ADN and TBD radical cations, the calculated values of gave = 2.00265 and gave = 2.00284 are well consistent with the experimental value of g = 2.0026 ± 0.0001 and g = 2.0028 ± 0.0001 within the error bars, respectively. For the ADN radical anion, the calculated value (gave = 2.0024) is almost consistent with the experimental value (g = 2.0026 ± 0.0002) within the error bars. Since the ADN molecules have no heteroatoms such as N and O, charge-conjugation symmetry (CCS) for electrons and holes is maintained40,41. This CCS is reflected in the spin-density distribution of the ADN radical cation and anion which is similar with each other as shown in Fig. 5a,c. For Alq3, the calculated value (gave = 2.00285) is considerably smaller than the experimental value (g = 2.0036 ± 0.0001). The reason for the larger experimental value may be due to an effect of spin–orbital interaction in a positive EMIM ion in the ion-gel and the Alq3 anion42. That is, an electron on Alq3 spreads over the positively charged EMIM, which may increase the g-factor by the enhanced spin–orbital interaction. This effect has been supported by the DFT calculation for Alq3 coordinated with EMIM (Table 2; Figure S1 in Supplementary Information). In this case, the gave is calculated to be 2.00321 (Table 2), which is larger than that of Alq3 anion (gave = 2.00285) and is closer to that of experimental value (g = 2.0036). Figure S1 in Supplementary Information shows the calculated spin-density distribution, which shows a different distribution compared to the case without EMIM coordination (Fig. 5d).
The coordination effect with EMIM seems to strongly occur for the case of Alq3 anions, as mentioned above. However, such effect seems not to strongly occur for the case of ADN anions because the calculated value (gave = 2.0024) by DFT is almost consistent with the experimental value (g = 2.0026), as mentioned above. The reason for the different coordination effect may be due to the different molecular structures between Alq3 and ADN. That is, the Alq3 molecule has oxygen atoms with negative electrostatic property, which may tend to strongly coordinate with EMIM cations. In contrast, the ADN molecule has no oxygen atoms with negative electrostatic property, which may result in no strong coordination with EMIM cations. Thus, the results for ADN anions obtained with the MIS diodes will be applicable to the electronic states in the blue OLEDs because of no strong coordination effect between ADN anions and EMIM cations in the MIS diodes.
Charge-trappings in organic layers
Next, we discuss the charge-trappings in organic layers. We have studied the charge injection from the contact electrode to the organic layer by measuring the time evolution of the ESR signal from the beginning of the VG application to the device. It has been known that the ESR lineshape varies depending on whether the charge with a spin is static or mobile28. This is because hyperfine interactions occur between charges’ spins and nuclear spins in organic molecules, which determines the linewidth of the ESR signals39. When the charge with a spin is in motion, the hyperfine interactions are averaged, and the motional narrowing of the ESR linewidth has been reported43.
Figure 6 shows an example of the time evolution of the ESR spectrum of the ADN MIS diode, showing the charge-accumulation process. When the |VG| was increased from 0 V at an interval of 0.1 V, the charge injection occurred at a threshold voltage of − 1.7 V, where holes were injected from the contact Au electrode, and corresponding ESR signals were observed. Just after applying VG = − 1.7 V, the signal component with a broad linewidth was immediately observed in addition to the signal component with a narrow linewidth; the signal with the broad linewidth is indicated by black arrows for the lower data (0 min) in Fig. 6. After that, when the VG was fixed at − 1.7 V, the signal component with the narrow linewidth became larger, as shown by the middle data (10 min). This narrow component was clearly enhanced as indicated by red arrows for the upper data (30 min) in Fig. 6. This charge-accumulation process can be explained as follows. At the threshold voltage, holes are firstly injected and trapped at the trapping levels in the ADN layer. In this case, the charge motion is hindered, so that the motional narrowing does not occur and the linewidth remains broad. That is, the trapped and static charges with spins directly feel hyperfine interactions from nuclear spins in the ADN layer, which makes the linewidth surprisingly broader. After that, some charges are de-trapped from the trapping levels at a certain rate and move in the organic layer, which narrows the linewidth due to the average of the hyperfine interactions by the motion of charges with spins, as mentioned above. The time constant of the complete de-trapping seems to be longer than several minutes, as shown in Fig. 6. This result demonstrates that the charges are trapped in the ADN layer just after the charge injection and that the subsequent charge motion is directly observed from a microscopic viewpoint. The long time constant of the complete de-trapping may be due to the charge-trapping sites with deep trapping levels at the interface between the metal electrode and organic molecules. That is, the charges are firstly injected by the electrostatic attraction from ions in the ion-gel and are trapped in the deep trapping levels at the metal/organic interface. However, the electrostatic potential for the trapped charges from ions in the ion-gel may be minimum at another interface between organic molecules and the ion-gel. Thus, the trapped charges are de-trapped from the deep trapping levels beyond the high potential barrier due to the deep trapping levels, which may take a long time, and then move in the organic layer, as mentioned above. Similar result has been obtained for the MIS diode for TBD cations. Other MIS diodes for ADN or Alq3 anions have not shown such a clear change of the ESR spectrum shown in Fig. 6 because these ESR spectra have much broader linewidth, which causes lower peak-to-peak ESR intensity, compared to those of the MIS diodes for ADN or TBD cations (Fig. 4), as explained later.
For the charge-trapping sites, one can consider several possibilities, such as in bulk organic molecules, at the interface between metal electrode and organic molecules, and at the interface between organic molecules and ion-gel. To further study the charge-trapping sites, we have performed the ESR studies of a hole only device (HOD) of ITO (150 nm)/TBD (100 nm)/ADN (60 nm)/Au (50 nm), and an electron only device (EOD) of ITO (150 nm)/ADN (60 nm)/Alq3 (4 nm)/LiF (0.5 nm)/Al (100 nm). However, we could not observe a very clear change of ESR signals for the HOD and EOD after 1 h device operation compared to the cases with the MIS diodes. This result can be attributed to the smaller number of long-lived accumulated charges in the HOD and EOD than that in the MIS diodes with high-capacitance ion-gel; the flow of electric current shortens the lifetime of charges in the HOD and EOD than < 10 μs. Thus, we have not definitely identified further detailed charge-trapping sites such as in the bulk material and/or at the interface. However, the above discussion for Fig. 6 may indicate the charge-trapping sites at the metal/organic interface.
The previous study has reported the carrier drift mobilities in ADN films with 5–7 μm thickness by using optical time-of-flight (TOF) technique, where both electron and hole mobilities of ADN are the same in the range of 1–4 × 10−7 cm2 V−1 s−1 (electric field 0.5–0.8 MV/cm)44. In the case with the TOF method, the drift mobility is derived from the averaged running velocity over whole film with a rather thick film of 5–7 μm thickness. The ADN films have been reported to be amorphous44. Thus, the photogenerated charges encounter many grain boundaries when they move in the film, and the evaluated mobility may be affected by such grain boundaries, which may give the similar mobility between electrons and holes. In contrast, the above-mentioned motional narrowing of the ESR linewidth reflects the local motion of charges in organic molecules, without being affected by such grain boundaries. Thus, the narrower the ESR linewidth, the higher the local mobility in organic molecules. Figure 4a,c show that the ESR linewidth of ADN cations (ΔHpp = 0.12 mT) is narrower than that of ADN cations (ΔHpp = 0.69 mT). This result indicates that the local mobility of ADN cations is higher than that of ADN anions from a microscopic viewpoint.
Charge-trappings in organic multilayers
Finally, we discuss the charge-trappings in an organic multilayer MIS diode (Al/LiF/Alq3/ADN/ion-gel/Au, Fig. 3d). This organic multilayer is the same as that in the blue OLED of ITO/TBD/ADN/Alq3/LiF/Al (Fig. 1c). Thus, clarifying the charge states in the organic multilayer will be useful for understanding the behavior of the OLED further. Figure 7 shows the VG dependence of the ESR spectrum of the organic multilayer MIS diode, which shows the electron accumulation and discharge. When VG = 0, no ESR signal was observed (the lower data), except for the signal due to Li+Alq3− as discussed for the lower data in Fig. 4d. As the VG increased, the charge injection occurred at the threshold voltage of VG = 3.0 V and an ESR signal with g = 2.0035 ± 0.0001 was clearly observed (the second lower data). This threshold voltage is almost the same as that of the Alq3 MIS diode (Fig. 4d). If looking carefully at the data of VG = 3.0 V, one can notices a weak structure in the spectrum. This result indicates the overlapping of two ESR signals of Alq3 anions and ADN anions because the observed g-factor (g = 2.0035) is slightly smaller than that of Alq3 anions (g = 2.0036, Fig. 4d) but is larger than that of ADN anions (g = 2.0026, Fig. 4c). As the VG further increased to 4.0 V, the signal intensity increased and the g-factor slightly decreased to g = 2.0031 ± 0.0001 (the second upper data in Fig. 7). This g-factor decrease demonstrates that the ESR intensity of ADN anions becomes larger compared to that at VG = 3.0 V because the g-factor of ADN anions (g = 2.0026) is smaller than that of Alq3 anions (g = 2.0036), which indicates that ADN anions are largely formed at high VG of 4.0 V. After that, when we stopped applying the VG, the signal intensity decreased and an ESR signal with g = 2.0033 ± 0.0001 was still observed (the upper data in Fig. 7). This result indicates that ADN anions in addition to Alq3 anions remain in the organic layers even after turning off the VG because the observed g-factor is smaller than that of Alq3 anions (g = 2.0036, Fig. 4d).
For Alq3-based OLEDs, it has been reported that the formation of Alq3 anions in the device does not contribute to the luminance degradation while Alq3 cations degrade the device performance9,45. If the formation of Alq3 anions in the blue OLED does not contribute to the luminance degradation in the same way, ADN anions in the device will cause the luminance degradation. The ESR studies of the ADN MIS diodes have shown that the accumulated electrons remained (Fig. 4c) while no holes remained in ADN after turning off the VG (Fig. 4a). Therefore, for the ADN OLED, the formation of radical anions will be an important degradation factor compared to the case with radical cations because of the reasons such as the molecular degradation and carrier-balance loss in the device, resulting in the degradation of the devices characteristics. Obtaining the proof of the molecular degradation of ADN such as the change of the molecular structure in the device is an interesting issue, which may be performed by the detailed analysis of the ESR spectrum because the values of the ESR linewidth of the ADN anion signal are different as shown in Fig. 4c. That is, the ΔHpp is 0.69 mT at VG = 4.2 V (the middle data in Fig. 4c) while it is 1.20 mT at 0 V (the upper data in Fig. 4c after VG application), which may indicate a change of the molecular structure of ADN. This difference may be explained by performing the detailed DFT analysis with assumed degraded molecular structures, which is in progress and will be reported in a separate paper.
We comment on an ESR study of hole injection and discharge in another organic multilayer MIS diode (Ni/Au/TBD/ADN/ion-gel/Au, Fig. 3c). In this case, we have mainly observed the ESR signal of TBD cations; almost no clear change of the g-factor was observed when the |VG| increased. This result may be explained by the larger peak-to-peak ESR intensity Ipp of the ESR spectrum of TBD cations compared to that of ADN cations considering the noise levels as shown in Fig. 4a,b, which can be ascribed to the narrower ΔHpp of TBD cations (0.06 mT) compared to that of ADN cations (0.12 mT). A number of spins evaluated from an ESR spectrum is proportional to Ipp × (ΔHpp)2, and thus the narrower the ΔHpp, the larger the Ipp. After turning off the VG, no ESR signal was observed, which is consistent with those for the ADN or TBD MIS diodes (the upper data in Fig. 4a,b).
To study the charge-trappings in blue OLEDs, we have performed an ESR study of the blue OLEDs of ITO (150 nm)/TBD (100 nm)/ADN (60 nm)/ Alq3 (4 nm)/LiF (0.5 nm)/Al (100 nm) (Fig. 1c). However, we could not observe a very clear change in the ESR signal of the blue OLED after 1 h device operation compared to the cases with the MIS diodes. As mentioned in the studies of the HODs and EOD, this result can be attributed to the smaller number of long-lived accumulated charges in the blue OLEDs than that in the MIS diodes with the high-capacitance ion-gel; the flow of electric current shortens the lifetime of charges in the OLEDs.
Conclusion
We have performed the operando ESR study of the organic single- or multi-layer MIS diodes, HOD, EOD, and blue OLEDs to elucidate the spin-states in the organic semiconductor materials used for the blue OLEDs. For the organic single-layer MIS diodes, no ESR signal was observed at VG = 0 V before VG application except for the Alq3 MIS diode, while clear ESR signal was obtained in each device by applying the VG. The observed g-factors are well reproduced by the DFT calculation. We demonstrate the charge-trappings in the organic layers from a microscopic viewpoint. The trapping levels of electrons has been found to be deeper than those of holes; the electron accumulation in ADN is confirmed for the organic multilayer MIS diodes. In contrast to the case of the green light-emitting material Alq3, long-lived radical anions in the blue light-emitting material ADN will contribute the degradation of the molecules and devices, and thus blue ADN OLEDs with higher efficiency and longer lifetime will be developed by decreasing or eliminating the ADN electron accumulation. Decreasing or eliminating the ADN electron accumulation is an interesting topic, which is currently studied by optimizing of molecules and device structures and will be reported in a separate paper.
Methods
Fabrication of organic devices
The MIS devices were fabricated using two types of nonmagnetic substrates; one was a polyethylene terephthalate (PET) film with dimensions of 30 mm × 3 mm × 100 μm (Mitsubishi Polyester Film, Inc.), and the other was a quartz substrate with dimensions of 30 mm × 3 mm × 1 mm (IIYAMA PRECISION GLASS Co, Ltd.). Gate electrodes of Ni/Au (3/47 nm) were vapor-deposited on the PET substrate using an ULVAC VPC-260F vacuum evaporation system. Ion-gel solutions consisted of an ionic liquid, 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide ([EMIM][TFSI]) (52.2 wt%) (Ionic Liquids Technologies, Inc.), a gelator ABA-type triblock copolymer poly(styrene-b-methylmethacylate-b-styrene) (PS-PMMA-PS) (4.3 wt%) (Polymer Source, Inc.), and a solvent ethyl acetate (43.5 wt%) (Wako Pure Chemical Industries, Ltd.); the mixture was stirred for over one and half day, drop-casted on the gate electrode and then thermally annealed at 70 °C under vacuum for over one and half day. The contact electrodes of Ni/Au (3 nm/47 nm) or Al/LiF (100 nm/0.5 nm) for the hole or electron accumulation were fabricated with the vapor-deposition system on the quartz substrate, respectively. The TBD, ADN, and Alq3 organic layers with a film thickness of 100 nm, 60 nm, and 60 nm were vapor-deposited on the contact electrodes with the vacuum evaporation system under 5 × 10−4 Pa, respectively. Finally, the PET substrate was placed on the quartz substrate, completing the device fabrication. The fabricated device was sealed into an ESR sample tube after wiring with Ag paste in a nitrogen-filled glove box (O2 ≤ 0.5 ppm, H2O ≤ 0.5 ppm). The parts of the above-mentioned fabrication method have been described in the previous works31,35,46,47,48,49.
Device characterization
The ESR measurements were performed with a JEOL RESONANCE JES-FA200 ESR spectrometer (X-band 9.5 GHz) and a Keithley 2612A source meter. The ESR signals were measured as a function of VG by averaging the ESR spectrum over typically 10–15 min. The g-factor and linewidth of the ESR signals were calibrated using a standard Mn2+ marker sample. The calibration of the g-factor was performed with a software program of the JEOL RESONANCE ESR system, considering high second-order correction to the effective resonance field. Its correctness was also confirmed with 2,2-diphenyl-1-picrylhydrazyl (DPPH) as another standard sample. The parts of the above-mentioned characterization method have been described in the previous works30,31,32,33,34,35,46,47,48,49.
Data availability
The authors declare that the data supporting the findings of this study are available within the paper and its supplementary information file.
References
Forrest, S. R. The path to ubiquitous and low-cost organic electronic appliances on plastic. Nature 428, 911–918 (2004).
Farinola, G. M. & Ragni, R. Electroluminescent materials for white organic light emitting diodes. Chem. Soc. Rev. 40, 3467–3482 (2011).
Sasabe, H. & Kido, J. Recent progress in phosphorescent organic light-emitting devices. Eur. J. Org. Chem. 34, 7653–7663 (2013).
Sekine, C., Tsubata, Y., Yamada, T., Kitano, M. & Doi, S. Recent progress of high performance polymer OLED and OPV materials for organic printed electronics. Sci. Technol. Adv. Mater. 15, 034203 (2014).
Tang, C. W. & VanSlyke, S. A. Organic electroluminescent diodes. Appl. Phys. Lett. 51, 913–915 (1987).
Adachi, C., Baldo, M. A., Thompson, M. E. & Forrest, S. R. Nearly 100% internal phosphorescence efficiency in an organic light-emitting device. J. Appl. Phys. 90, 5048–5051 (2001).
Uoyama, H., Goushi, K., Shizu, K., Nomura, H. & Adachi, C. Highly efficient organic light-emitting diodes from delayed fluorescence. Nature 492, 234–238 (2012).
Zhang, Q. et al. Efficient blue organic light-emitting diodes employing thermally activated delayed fluorescence. Nat. Photon. 8, 326–332 (2014).
Aziz, H., Popovic, Z. D., Hu, N.-X., Hor, A.-M. & Xu, G. Degradation mechanism of small molecule-based organic light-emitting devices. Science 283, 1900–1902 (1990).
Ikeda, T. et al. Enhanced stability of organic light-emitting devices fabricated under ultra-high vacuum condition. Chem. Phys. Lett. 426, 111–114 (2006).
Thangaraju, K., Kumar, J., Amaladass, P., Mohanakrishnan, A. K. & Narayanan, V. Study on photoluminescence from tris-(8-hydroxyquinoline) aluminum thin films and influence of light. Appl. Phys. Lett. 89, 082106 (2006).
Rosselli, F. P. et al. Experimental and theoretical investigation of tris-(8-hydroxy-quinolinate) aluminum (Alq3) photo degradation. Org. Electron. 10, 1417–1423 (2009).
Thangaraju, K. et al. Studied on influence of light on fluorescence of tris-(8-hydroxyquinoline) aluminum thin film. Appl. Surf. Sci. 255, 5760–5763 (2009).
Raghunath, P., Reddy, M. A., Gouri, C., Bhanuprakash, K. & Rao, V. J. Electronic properties of anthracene derivatives for blue light emitting electroluminescent layers in organic light emitting diodes: a density functional theory study. J. Phys. Chem. A 110, 1152–1162 (2006).
Yu, J. et al. Enhancement of efficiency and lifetime of blue organic light-emitting diodes using two dopants in single emitting layer. Adv. Mater. Sci. Eng. 2012, 247976 (2012).
Li, H. et al. Study of the hole and electron transport in amorphous 9,10-Di-(2′-naphthyl)anthracene: the first-principles approach. J. Phys. Chem. C 117, 16336–16342 (2013).
Li, C., Tsuboi, T. & Huang, W. Characteristics of blue organic light emitting diodes with different thick emitting layers. Opt. Mater. 36, 1720–1723 (2014).
Yoon, J.-A. et al. Highly efficient blue organic light-emitting diodes using quantum well-like multiple emissive layer structure. Nano Res. Lett. 9, 191 (2014).
Seo, J.-A. et al. Long lifetime blue phosphorescent organic light-emitting diodes with an exciton blocking layer. J. Mater. Chem. C 3, 4640–4645 (2015).
Kajjam, A. B., Giri, S. & Vaidyanathan, S. Triphenylamine-based donor–π–acceptor organic phosphors: synthesis, characterization and theoretical study. Mater. Chem. Front. 1, 512–520 (2017).
Kajjam, A. B., Kumar, P. S. V., Subramanian, V. & Vaidyanathan, S. Triphenylamine based yellowish-orange light emitting organic dyes (donor–π–acceptor) for hybrid WLEDs and OLEDs: synthesis, characterization and theoretical study. Phys. Chem. Chem. Phys. 20, 4490–4501 (2018).
Tagare, J. et al. Highly twisted tetra-N-phenylbenzidine-phenanthroimidazole based derivatives for blue organic light emitting diodes: experimental and theoretical investigation. Org. Electron. 62, 419–428 (2018).
Tagare, J. & Vaidyanathan, S. Recent development of phenanthroimidazole-based fluorophores for blue organic light-emitting diodes (OLEDs): an overview. J. Mater. Chem. C 6, 10138–10173 (2018).
Tagare, J., Dubey, D. K., Jou, J.-H. & Vaidyanathan, S. Synthesis, photophysical, theoretical and electroluminescence study of triphenylamine-imidazole based blue fluorophores for solution-processed organic light emitting diodes. Dyes Pigm. 160, 944–956 (2019).
Tagare, J., Dubey, D. K., Yadav, R. A. K., Jou, J.-H. & Vaidyanathan, S. Triphenylamine-imidazole-based luminophores for deep-blue organic light-emitting diodes: experimental and theoretical investigations. Mater. Adv. 1, 666–679 (2020).
Marumoto, K., Kuroda, S., Takenobu, T. & Iwasa, Y. Spatial extent of wave functions of gate-induced hole carriers in pentacene field-effect devices as investigated by electron spin resonance. Phys. Rev. Lett. 97, 256603 (2006).
Pawlik, T. D., Kondakov, D. Y., Begley, W. J. & Young, R. H. Charge carriers and charge-transfer reactions in OLED devices studied by electron paramagnetic resonance. J. SID 18, 277–284 (2010).
Marumoto, K. et al. Microscopic mechanisms behind the high mobility in rubrene signal-crystal transistors as revealed by field-induced electron spin resonance. Phys. Rev. B 83, 075302 (2011).
Tanaka, H. et al. Electron spin resonance observation of charge carrier concentration in organic field-effect transistors during device operation. Phys. Rev. B. 87, 045309 (2013).
Nagamori, T. & Marumoto, K. Direct observation of hole accumulation in polymer solar cells during device operation using light-induced electron spin resonance. Adv. Mater. 25, 2362–2366 (2013).
Tsuji, M. et al. Two-dimensional magnetic interactions and magnetism of high-density charges in a polymer transistor. Appl. Phys. Lett. 102, 133301 (2013).
Sato, G. et al. Direct observation of the radical states and the correlation with the performance degradation in organic light-emitting diodes during device operation. Phys. Stat. Sol. A 215, 1700731 (2018).
Marumoto, K., Fujimori, T., Ito, M. & Mori, T. Charge formation in pentacene layers during solar-cell fabrication: direct observation by electron spin resonance. Adv. Energy Mater. 2, 591–597 (2012).
Son, D., Kuwabara, T., Takahashi, K. & Marumoto, K. Direct observation of UV-induced charge accumulation in inverted-type polymer solar cells with a TiOx layer: microscopic elucidation of the light-soaking phenomenon. Appl. Phys. Lett. 109, 133301 (2016).
Takahashi, Y. et al. Electron spin resonance study of organic interfaces in ion gel-gated rubrene single-crystal transistor. Appl. Phys. Express 6, 041603 (2013).
Kim, S. H. et al. Electrolyte-gated transistors for organic and printed electronics. Adv. Mater. 25, 1822–1846 (2013).
Nagasaki, Y., Lee, J.-H., Kubozono, Y. & Kambe, T. Dynamics of carrier injection in picene thin-film field-effect transistors with an ionic liquid sheet and ionic liquid gel. Org. Electron. 15, 3070–3075 (2014).
Frisch, M. J. et al., Gaussian 09, Revision A.02, Gaussian, Inc., Wallingford CT (2016).
Son, D., Marumoto, K., Kizuka, T. & Shimoi, Y. Electron spin resonance of thin films of organic light-emitting material tris(8-hydroxyquinoline) aluminum doped by magnesium. Synth. Met. 162, 2451–2454 (2012).
Swanson, L. S., Shinar, J., Lane, P. A., Hess, B. C. & Wudl, F. Optically detected magnetic resonance (ODMR) of polarons and charge-conjugation symmetry in conducting polymers. Synth. Met. 49–50, 481–489 (1992).
Shinar, J. & Swanson, L. S. Optically detected magnetic resonance (ODMR) studies of conducting polymers: an overview. Synth. Met. 49–50, 621–630 (1992).
Son, D., Shimoi, Y. & Marumoto, K. Study on n-type doped electron-transporting layers in OLEDs by electron spin resonance. Mol. Cryst. Liq. Cryst. 599, 153–156 (2014).
Matsuo, Y., Son, D., Shimoi, Y. & Marumoto, K. Direct observation of spins at bathocuproine (BCP) interfaces: an electron spin resonance study on BCP/metal (Al or Au) thin films. Chem. Phys. Lett. 607, 29–33 (2014).
Tse, S. C. et al. The role of charge-transfer integral in determining and engineering the carrier mobilities of 9,10-di(2-naphthyl)anthracene compounds. Chem. Phys. Lett. 422, 354–357 (2006).
Murata, H. & Sandanayaka, A. S. D. Degradation analysis of light emitting diodes by time resolved photoluminescence measurements. SID Symp. Dig. Tech. Pap. 45, 32–35 (2014).
Matsumoto, D., Yanagi, K., Takenobu, T., Okada, S. & Marumoto, K. Electrically induced ambipolar spin vanishments in carbon nanotubes. Sci. Rep. 5, 11859 (2015).
Fujita, N. et al. Direct observation of electrically induced Pauli paramagnetism in single-layer graphene using ESR spectroscopy. Sci. Rep. 6, 34966 (2016).
Sakurai, Y., Matsumoto, D. & Marumoto, K. Electrically controlled dimensionality of magnetic systems in organic materials. Appl. Magn. Reson. 49, 767–782 (2018).
Iguchi, S., Sakurai, Y., Fujita, N., Osawa, F. & Marumoto, K. Electrically controllable spin states of holes and electrons in organic semiconductor materials. ACS Appl. Electron. Mater. 1, 2522–2530 (2019).
Acknowledgements
This work was partially supported by JSPS KAKENHI Grant Number JP19K21955, by JST PRESTO, by The Hitachi Global Foundation, by The MIKIYA Science and Technology Foundation, by The Futaba Foundation, and by JST ALCA Grant Number JPMJAL1603, Japan.
Author information
Authors and Affiliations
Contributions
K.M. and F.O. conceived the research. F.O. and K.M. developed the fabrication method of the devices, fabricated the devices, carried out the measurements and analyzed the data. F.O. performed the DFT calculations. F.O. and K.M. wrote the manuscript. All authors discussed the results and reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Osawa, F., Marumoto, K. Operando direct observation of spin-states and charge-trappings of blue light-emitting-diode materials in thin-film devices. Sci Rep 10, 18800 (2020). https://doi.org/10.1038/s41598-020-75668-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-75668-4
- Springer Nature Limited
This article is cited by
-
Operando ESR observation in thermally activated delayed fluorescent organic light-emitting diodes
Scientific Reports (2023)