Abstract
We report a universal terahertz (THz) emission behavior from simple Ni, Fe, and Co metallic ferromagnetic films, triggered by the femtosecond laser pulse and subsequent photoinduced demagnetization on an ultrafast time scale. THz emission behavior in ferromagnetic films is found to be consistent with initial magnetization states controlled by external fields, where the hysteresis of the maximal THz emission signal is observed to be well-matched with the magnetic hysteresis curve. It is experimentally demonstrated that the ultrafast THz emission by the photoinduced demagnetization is controllable in a simple way by external fields as well as pump fluences.
Similar content being viewed by others
Introduction
Very recently, THz spintronics in ferromagnetic materials has attracted much attention due to possible future applications1,2. THz spintronics based on an interaction between THz wave and spins could be promising since it is involved with key aspects of spintronics such as spin transport3,4, spin wave excitation5, spin current control6, and spin-flop transition7.
On the other hand, THz emission from the ferromagnetic materials has been explored as well since the seminal work on a femtosecond laser-induced demagnetization dynamics in Ni film8, followed by numerous extensive studies on photoinduced ultrafast spin dynamics9,10,11,12,13,14,15. One of the important finding regarding the ultrafast photoinduced demagnetization is that THz light should be emitted from ferromagnetic thin films when the film is illuminated by femtosecond laser pulses so that the subsequent photoinduced demagnetization/remagnetization generates the THz emission15. However, relatively few studies have been reported for THz emission by ultrafast demagnetization. Moreover, there have been reports that there might be other THz emission mechanisms such as an inverse spin Hall effect in addition to the ultrafast demagnetization16,17. Recently, we have reported our direct observation of THz emission and photoinduced demagnetization/remagnetization signals in Co films with comparison to each other, demonstrating that the THz emission from the ultrafast demagnetization becomes dominant in relatively thick (> 30 nm) Co films, regardless of selection of capping layers18. For THz emission by inverse spin Hall effect, a strong spin–orbit coupling occurring in interface between ferromagnetic and heavy metal layers is required as in Fe/Pt19, Fe/Au, and Fe/Ru6 bilayers where the emission behavior sensitively depends on the film thickness and capping layer selection6,18,20. Thus, to realize a THz spintronics, THz emission behavior requires a further understanding. Unfortunately, little studies have been devoted to a field-dependent THz emission probably due to several emission mechanisms and sensitivity to the material selection, although systematic investigation on the field-dependent THz emission behavior could be the first step for applications. For Ta/CoFeB/MgO trilayer films, a field-dependent THz emission by the inverse spin Hall effect has been reported21. Recently, THz emission by the ultrafast demagnetization of 20-nm NdFeCo and GdFeCo films together with a 12-nm Co film with oppositely saturated magnetization22 has been reported, where the measured THz emissions from GdFeCo and NdFeCo alloy films are found to have a faster magnetization dynamics due to Nd element. Thus, a systematic study of THz emission from the ultrafast demagnetization dynamics with variation of element as well as external magnetic fields becomes necessary. Here, we report our experimental investigation on the field-dependent THz emission by ultrafast photoinduced demagnetization in 30-nm Fe, Ni, and Co films with variation of external fields, where a universal THz emission behavior is regardless of film elements is clearly observed with field-tunability.
Results
The electric field profile of emitted THz wave upon ultrafast demagnetization of Fe, Ni, and Co films is illustrated in Fig. 1a for several magnetic states including oppositely saturated states. It is clear that the THz emission profile of Co film (bottom) from oppositely saturated states are quite symmetric, as reported in22. As seen in the figure, it seems that the THz emission profile is not significantly different for each element. It is also observed that peak amplitudes of generated THz wave are gradually changing by external magnetic fields for all cases of Fe, Ni, and Co thin films, allowing a control of the THz emission strength easily by external fields. The overall profile and field-dependency does not seem to be depending on the element selection, implying that the THz emission could be simply originated from the ultrafast photoinduced demagnetization of Fe, Ni, and Co films. It should be mentioned that there have been reports on different timescales for Fe, Ni, and Co elements12,13,24,25,26,27,28,29. We consider that there have been substantial differences in timescale with respect to measurement technique and sample thickness. The capping layer role particularly for thinner samples should be also seriously taken into consideration. Moreover, there has been a report about the difference in ultrafast demagnetization for magnetic moment either from intrinsic one or induced one13, which could add complexity. In this regard, we believe that our measurement makes sense because we compared for single-elemental thick (30 nm) film of Co, Ni, and Fe with the same Pd capping layer, expecting the dominant THz emission mechanism to be involved with ultrafast demagnetization, thereby hoping to minimize the complex effect of ferromagnetic element with capping layer in observed THz signal.
In Fig. 1b, THz emission waves at non-saturated intermediate magnetic states are compared to the saturated one with proper normalization multipliers denoted in the figure, where a shape of all data matches with one another without a particular dependence on the external field strength. It should be also noted that Fourier transformed (FT) signals of the THz emissions from 3 different elements are almost the same as shown in Fig. 1c. For comparison, FT of THz emissions from negatively saturated states of 3 elements are plotted. The frequency range in Fig. 1c roughly matches but with substantial difference when compared to previous experimental reports for Co (0–3 THz)22, Fe (0–1.5 THz)23, and Ni (0.5–4 THz)29 films. It should be commented that the seemingly universal THz emission behavior observed in the present study regardless of element selection is observable after selecting thick enough (~ 30 nm) films based on our previous work18 to exactly distinguish the THz emission contribution by the ultrafast photoinduced demagnetization dynamics from other possible mechanisms originated from the interface.
We have also directly compared the THz emission signals from 30-nm Co with 1-nm Pt18 and with 1-nm Pd (present work), as in Fig. 2a, where we could see no significant difference in the emission profiles. The FFT spectra of the THz emission for two cases with Pt and Pd capping layers are plotted in Fig. 2b. The major peak regions in the spectra are roughly matching although there is a little deviation which could be originated from different capping layer role. It is interesting to note that the difference in THz emission spectra by selecting different element among Co, Fe, and Ni seems to be smaller than the difference by selecting different capping layer between Pt and Pd.
As a pump laser irradiate on the sample surface to induce the ultrafast demagnetization dynamics, THz wave emitted from a sample should pass through the sample to be detected in the end. If a current density J and the conductivity σ are approximated to follow the Ohm’s law in metallic films of Fe, Ni, and Co30: the electric field E is described as: \(E \approx \frac{J}{\sigma }\). In other word, the amplitude of THz wave is expected to be inversely proportional to the conductivity σ of metallic samples, which is demonstrated in Fig. 3a. σ value of each film is from the literature values31,32. It is clearly observed that the amplitude of electric field profile (Ey max) is inversely proportional to σ for Fe, Ni and Co. Electric field profiles of emitted THz wave at positively saturated magnetic state for Fe, Ni, and Co are plotted in Fig. 3b, where the lowest (highest) amplitude is observed for Co (Fe) with highest (lowest) conductivity.
Since THz emission is dominantly contributed from the ultrafast photoinduced demagnetization, it is expected to have stronger THz emission by the pump pulse with higher fluences due to larger demagnetization. THz emission profile with various fluences is plotted in Fig. 4 for the case of Fe film. It is observed that there is no significant change in terms of shape and phase of Ey after normalization by multiplying proper numbers, whereas amplitudes gradually increase with respect to the pump fluence. The same trend is also found for Ni and Co films as well. The amplitude of THz emission with variation of pump fluences are shown for Fe, Ni, and Co films in the inset figure, where it is clearly observed that the THz amplitude increases as the fluence increases. It should be also noted that the THz peak amplitude variation with respect to the pump fluences for different 3 elements again falls into the same overall tendency when the signal is normalized by the maximum peak intensity of each element. It is clearly observed that the THz amplitude increases as fluence increases.
We have further analyzed THz emission behavior with variation of external fields, as seen in Fig. 5. Hysteresis curves measured for Fe, Ni, and Co films are plotted in Fig. 5a, while THz peak amplitude measured with respect to the field strength is plotted in Fig. 5b. It is very interesting to note that there also exists a hysterectic behavior even in THz emission, which is a clear indication that the THz emission is basically from the magnetic state of ferromagnetic films. This is explainable since the stroboscopic observation of THz emission, originated from the ultrafast photoinduced demagnetization, should depend on the initial magnetization state along the magnetic hysteresis curve of Fe, Ni, and Co films. Correlated hysteresis curves of magnetization and THz emission peak amplitude under cycling external fields implies a direct proportional control of the THz emission behavior based on the magnetization state information on an ultrafast time scale. Since the polarity of emitted THz wave depends exactly on the initial magnetization direction (Fig. 1a), it is concluded that the emitted THz peak amplitude can be fully tunable within the range spanned by the magnetization state along the whole magnetic hysteresis curve.
Discussion
In conclusion, we have explored the field-dependent THz emission in 30 nm Fe, Ni, and Co films, where ultrafast demagnetization universally generates THz emission regardless of elements. It is observed that the THz emission behavior directly corresponds to the magnetization state of samples, where field-tunability as well as fluence-tunability of the ultrafast THz emission on a femtosecond time scale is experimentally demonstrated. Our finding is believed to be an important experimental evidence in designing future THz spintronic devices operating on an ultrafast time scale.
Methods
Fe, Ni, and Co films were prepared by sputtering on SiO2 substrate with thickness to be all fixed to be 30 nm. The 30-nm thickness was selected since it has been confirmed that dominant THz emission mechanism in 30-nm Co film is the photoinduced ultrafast demagnetization/remagnetization dynamics18 and that the effect of other mechanisms such as inverse spin Hall effect, arising from the interface, can be neglected. On top of Fe, Ni, and Co layer, 1-nm Pd was deposited as a capping layer. Stroboscopic optical pump and THz emission measurement was carried out at the fs-THz beamline of Pohang Accelerator Laboratory, as the overall optical layout is illustrated in Ref.33. Ti:Sapphire regenerative amplifier was used to produce a laser pulse of 800 nm wavelength with 1 kHz repetition rate, 3.2 W power, and 120 fs duration. THz radiation emitted from the sample is measured by electro-optic (EO) sampling method. THz radiation is collected and focused onto a 10 × 10 mm2 \(\left\langle {110} \right\rangle\) ZnTe nonlinear crystal (3-mm thickness) using parabolic mirrors, which can be measured by a combination of a quarter-wave plate, a Wollaston polarizer, and a pair of balanced photodiodes. The signal current was sent to a lock-in amplifier. THz low pass filter (Microtech, Inc.) was used to remove the residual pump beam. Spectral bandwidth of the detector is found to cover up to 2.5 THz. Arbitrary unit is used in the THz emission signal due to the low signal intensity for calibration using other detectors such as bolometer or pyroelectric detector. We estimate that THz field in the present study might be lower than 1 kV/cm. The fluence of pump pulse was varied from 0.03 to 1.27 mJ/cm2 (300 μJ, area: ~ 0.2 cm2) with keeping the pump beam size to be 5 mm. In-plane external magnetic field was applied to film samples to control the magnetic states along the full hysteresis curve with the maximum field of 250 Oe.
Data availability
The data that support the findings of this study are available from the corresponding authors upon reasonable request.
References
Walowski, J. & Münzenberg, M. Perspective: ultrafast magnetism and THz spintronics. J. Appl. Phys. 120, 140901 (2016).
Kirilyuk, A., Kimel, A. V. & Rasing, T. Ultrafast optical manipulation of magnetic order. Rev. Mod. Phys. 82, 2731 (2010).
Jin, Z. et al. Accessing the fundamentals of magnetotransport in metals with terahertz probes. Nat. Phys. 11, 761 (2015).
Bonetti, S. et al. THz-driven ultrafast spin-lattice scattering in amorphous metallic ferromagnets. Phys. Rev. Lett. 117, 087205 (2016).
Kampfrath, T. et al. Coherent terahertz control of antiferromagnetic spin waves. Nat. Photon. 5, 31 (2011).
Kampfrath, T. et al. Terahertz spin current pulses controlled by magnetic heterostructures. Nat. Nanotechnol. 8, 256 (2013).
Becker, J. et al. Ultrafast magnetism of a ferrimagnet across the spin-flop transition in high magnetic fields. Phys. Rev. Lett. 118, 117203 (2017).
Beaurepaire, E., Merle, J.-C., Daunois, A. & Bigot, J. Y. Ultrafast spin dynamics in ferromagnetic nickel. Phys. Rev. Lett. 76, 4250 (1996).
Schellekens, A. J., Verhoeven, W., Vader, T. N. & Koopmans, B. Investigating the contribution of superdiffusive transport to ultrafast demagnetization of ferromagnetic thin films. Appl. Phys. Lett. 102, 252408 (2013).
La-O-Vorakiat, C. et al. Ultrafast demagnetization measurements using extreme ultraviolet light: comparison of electronic and magnetic contributions. Phys. Rev. X 2, 011005 (2012).
Muller, B.-Y. et al. Feedback effect during ultrafast demagnetization dynamics in ferromagnets. Phys. Rev. Lett. 111, 167204 (2013).
Koopmans, B. et al. Explaining the paradoxical diversity of ultrafast laser-induced demagnetization. Nat. Mater. 9, 259 (2010).
Hofherr, M. et al. Induced versus intrinsic magnetic moments in ultrafast magnetization dynamics. Phys. Rev. B 98, 174419 (2018).
Shim, J.-H. et al. Ultrafast giant magnetic cooling effect in ferromagnetic Co/Pt multilayers. Nat. Commun. 8, 796 (2017).
Beaurepaire, E. et al. Coherent terahertz emission from ferromagnetic films excited by femtosecond laser pulses. Appl. Phys. Lett. 84, 3465 (2004).
Seifert, T. et al. Efficient metallic spintronic emitters of ultrabroadband terahertz radiation. Nat. Photon. 10, 483 (2016).
Huisman, T. J. et al. Femtosecond control of electric currents in metallic ferromagnetic heterostructures. Nat. Nanotechnol. 11, 455 (2016).
Huang, L. et al. Direct observation of terahertz emission from ultrafast spin dynamics in thick ferromagnetic films. Appl. Phys. Lett. 115, 142404 (2019).
Torosyan, G., Keller, S., Scheuer, L., Beigang, R. & Papaioannou, ETh. Optimized spintronic terahertz emitters based on epitaxial grown Fe/Pt layer structures. Sci. Rep. 8, 1311 (2018).
Wu, Y. et al. High-performance THz emitters based on ferromagnetic/nonmagnetic heterostructures. Adv. Mater. 29, 1603031 (2017).
Sasaki, Y., Suzuki, K. Z. & Mizukami, S. Annealing effect on laser pulse-induced THz wave emission in Ta/CoFeB/MgO films. Appl. Phys. Lett. 111, 102401 (2017).
Huisman, T. J., Mikhaylovskiy, R. V., Tsukamoto, A., Rasing, Th. & Kimel, A. V. Simultaneous measurements of terahertz emission and magneto-optical Kerr effect for resolving ultrafast laser-induced demagnetization dynamics. Phys. Rev. B 92, 104419 (2015).
Hilton, D. J. et al. Terahertz emission via ultrashort-pulse excitation of magnetic metal films. Opt. Lett. 29, 1805 (2004).
Radu, I. et al. Ultrafast and distinct spin dynamics in magnetic alloys. SPIN 5, 1550004 (2015).
La-O-Vorakiat, C. et al. Ultrafast demagnetization dynamics at the m edges of magnetic elements observed using a tabletop high-harmonic soft X-ray source. Phys. Rev. Lett. 103, 257402 (2009).
Shalaby, M. et al. Coherent and incoherent ultrafast magnetization dynamics in 3d ferromagnets driven by extreme terahertz fields. Phys. Rev. B 98, 014405 (2018).
Buhlmann, K. et al. Ultrafast demagnetization in iron: Separating effects by their nonlinearity. Struct. Dyn. 5, 044502 (2018).
Longa, F. D., Kohlhepp, J. T., de Jonge, W. J. M. & Koopmans, B. Influence of photon angular momentum on ultrafast demagnetization in nickel. Phys. Rev. B 75, 224431 (2007).
Shalaby, M., Vicario, C. & Hauri, C. P. Low frequency terahertz-induced demagnetization in ferromagnetic nickel. Appl. Phys. Lett. 108, 182903 (2016).
Huisman, T. J. & Rasing, T. J. THz emission spectroscopy for THz spintronics. Phys. Soc. Jpn. 86, 011009 (2017).
Raymond, A. S. Principles of Physics 2nd edn, 602 (Saunders College Pub, London, 1998).
Engineering Tool Box, Electrical Conductivity of common Materials. https://www.engineeringtoolbox.com/conductors-d_1381.html. (2008).
Park, J. et al. Generation, transport, and detection of linear accelerator based femtosecond-terahertz pulses. Rev. Sci. Instrum. 82, 013305 (2011).
Acknowledgements
This work has been supported by Korea Research Foundation (NRF) (Grant No. 2018R1A2B3009569) and by a KBSI Grant D010200. This work was also supported in part by Max Planck POSTECH/KOREA Research Initiative Program [Grant No 2016K1A4A4A01922028] through the National Research Foundation of Korea (NRF) funded by Ministry of Science, ICT and Future Planning.
Author information
Authors and Affiliations
Contributions
L.H., S.H.L. and S.D.K. collected data and performed all the analyses; J.H.S., H.J.S., S.K. and J.P. conducted the experiments; H.J.Kim and J.I.H. fabricated all the samples; S.Y.P., Y.S.C. and D.E.K. performed the analysis; D.H.K. is involved in study design. All authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Huang, L., Lee, SH., Kim, SD. et al. Universal field-tunable terahertz emission by ultrafast photoinduced demagnetization in Fe, Ni, and Co ferromagnetic films. Sci Rep 10, 15843 (2020). https://doi.org/10.1038/s41598-020-72855-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-72855-1
- Springer Nature Limited
This article is cited by
-
Three-stage ultrafast demagnetization dynamics in a monolayer ferromagnet
Nature Communications (2024)
-
Efficient ultrafast field-driven spin current generation for spintronic terahertz frequency conversion
Nature Communications (2023)