Abstract
The most studied perovskite-based solar cells reported up to date contain the toxic lead in its composition. Photovoltaic research and development towards non-toxic, lead-free perovskite solar cells are critical to finding alternatives to reduce human health concerns associated with them. Bismuth-based perovskite variants, especially in the form of methylammonium bismuth iodide (MBI), is a good candidate for the non-toxic light absorber. However, the reported perovskite variant MBI thin films prepared by the solution process so far suffers from poor morphology and surface coverage. In this work, we investigate for the first time the optoelectronic, crystallographic and morphological properties of MBI thin films prepared via thermal co-evaporation of MAI and BiI3. We find by modifying the precursor ratio that the layer with pure MBI composition lead to uniform, compact and homogeneous layers, broadening the options of deposition techniques for lead-free based perovskite solar cells.
Similar content being viewed by others
Introduction
Organic–inorganic metal halide perovskites have emerged as promising candidates for the next generation of photovoltaics (PV) given their unprecedented rise in power conversion efficiency (PCE) achieving 25.2%1 Beyond their superior optoelectronic properties, low cost and high versatility2,3,4,5, their instability and lead toxicity are at present major concerns, which greatly limit their incorporation into marketable products. Significant efforts are therefore oriented into the search of stable and non-toxic perovskite materials, yet real alternatives based on lead-free components are still missing.
Among the various lead-free perovskites variants proposed in the literature, Sn-based materials have demonstrated promising efficiencies leading to a PCE value of 9.6%6. However, Sn-based perovskites suffer from inevitable oxidation of Sn2+ to Sn4+, providing a source of inhomogeneity and pinholes that are further enhanced by their fast crystallization7. As a result, the most straightforward candidates possessing similar electronic properties to Pb2+, which are suitable for light-harvesting, are Ge2+, Sb3+ or Bi3+ cations. While Ge-based perovskites suffer from material instability due to hydrolytic decomposition in humid environment8,9,10, Sb-based perovskites show limited photovoltaic performances in spite of their good chemical stability8. Bismuth is a heavy metal with a stable oxidation state, little toxicity, and a similar polarizable electron density than Pb11. Thanks to the formation of BiX63− octahedron, it can also form perovskites with diverse dimensionalities and phases, from which methylammonium bismuth iodide ((CH3NH3)3Bi2I9, MBI) is at the forefront9. MBI is a wide-bandgap semiconductor with a zero-dimensional structure having reduced toxicity, high stability and promising photovoltaic efficiency12. Despite such remarkable potential, its use is limited by the low quality of the films resulted from conventional spin-coating deposition, which produces non-compact MBI layers with poor coverage and crystallinity8. Indeed, in the last few years, several reports have demonstrated the strong effect of solvents, precursor's concentration and processing conditions in achieving enhanced thin film coverage13,14,15,16,17.
Alternative strategies to enhance film morphology combined the use of two-step processes as well as additive inclusion such as Br− or N-methyl-2-pyrrolidone (NMP)18,19. However, such procedures rely on harmful polar solvents such as DMF or DMSO, which are not feasible for mass production. In an attempt to reduce the solvent toxicity while improving film coverage, ethanol has been proposed as a plausible solvent for BiI3, affording PCE of 0.053%20. Nevertheless, the toxicity is only partially reduced with this method as toxic methylamine gas is used as the organic precursor. Interestingly, additional deposition techniques like electric-field assisted spray coating21,22, vapour-assisted solution process (VASP)23, or chemical vapour deposition (CVD)24,25 among others, have been also investigated, providing a record in device efficiency exceeding 3%23. However, having homogeneous and conformal coating are still challenging, making it difficult to employ MBI as the real alternative.
Among the different options existing in literature, thermal co-evaporation of thin film deposition is well known to produce smooth, compact and pin-hole free lead-based perovskites26,27. This technique offers improved process control and high reproducibility, allowing as well the processing of large area substrates. In spite of its versatility, to date, there is no report on thermal co-evaporation of MBI films. Only co-evaporated fully inorganic bismuth-based perovskites can be found in the literature, such as A3Bi2I9 (A = Cs, Rb), or AgBi2I728,29.
In this work, we investigate for the first time the crystallization process of MBI thin films prepared via thermal co-evaporation of MAI and BiI3. Different perovskite layers (1–5) with various MAI:BiI3 ratios (conditions 1–5) have been analyzed and its optoelectronic and crystallographic properties were evaluated. In order to vary MAI:BiI3 ratio, the deposition rate of BiI3 was kept at 0.4 (Å s–1) while that of MAI varied from 0.4, 0.55, 0.7, 1 to 1.4 Å s–1, obtaining the films 1–5 respectively. Our results confirm that by using the optimal conditions, applied to layer 4 in this manuscript, a pure phase of hexagonal MBI crystal structure with the long-term structural stability of several months is achieved. In addition, we observed the deposition of conformal MBI films with remarkable homogeneity and surface coverage, contrary to those previously reported from solution-based methodologies, paving the way towards a successful implementation into lead-free based solar cells.
Results and discussion
MBI layers (1–5) were fabricated by thermal co-evaporation of the precursors, BiI3 and methylammonium iodide (MAI), in vacuum using varying precursor ratio (conditions 1–5, Table S1). For clarity, the deposited films obtained in condition 1–5 will be named as thin film 1–5, respectively. During the co-evaporation process the deposition rate of each material was controlled by independent quartz microbalance crystals, and the materials were simultaneously heated until their sublimation temperature. We varied the film composition by fixing the rate of BiI3 at 0.4 Å s–1 while that of MAI varied from 0.4, 0.55, 0.7, 1 to 1.4 Å s–1 (conditions 1–5, respectively), and analyzed its impact on the optical properties, layer morphology and crystal structure. For comparison, thin films of pure BiI3 were also fabricated and characterized.
Figure 1a shows the optical properties of the as-deposited films investigated by UV–Vis absorption spectroscopy. Whereas the BiI3 film presents a characteristic sharp absorption onset at 690 nm, the gradual insertion of MAI (1) reduces the onset sharpness as well as the intensity in the 450–630 nm range. As observed for the layers (2–5), the absorbance spectra show an onset (~ 600 nm) and an excitonic peak (~ 500 nm) typical of MBI. Such an excitonic peak is attributed to the electron ground-excitation transition of 1S0 to 3P1 from the Bi3+ to the face-shared bi-octahedrons [Bi2I9]3−30, thus confirming that MBI material is already formed at condition 2. This is also validated by the absence of absorption in the 600 to 690 nm region associated to BiI3, denoting a complete conversion of the precursor.
The optical bandgap of the BiI3 and thin-films 1–5 were derived from the corresponding indirect bandgap Tauc plots (Fig. 1b) respectively, and the calculated values are presented in Table 1. An indirect bandgap of 1.80 eV (BiI3), 1.81 (1), 2.11 (2 and 5), 2.12 (3 and 4) was obtained for the films, matching well with the reported values in literature24,31.
To further analyze the in situ synthetized new materials, X-Ray Diffraction (XRD) measurements were employed in Bragg–Brentano geometry. Figure 1c summarizes the diffraction patterns of FTO, BiI3 and the different MBI thin films (1–5). The film containing pure BiI3 presents two main diffraction peaks at 12.8° and 41.6°, corresponding to the (003) and (300) lattices planes of the hexagonal crystal structure respectively (JCPDS card no. 7-269)32. Despite the peak at 12.8° remains in layer 1, the incorporation of MAI gradually increases the diffraction signal at 29.2°, 31.7° and 45.5°, corresponding to (204), (205) and (4 − 2 6) lattice planes in MBI perovskite, suggesting its incipient formation. On increasing MAI content (films 2–3), intense diffraction peaks centered at 14.5°, 17.1°, 29.1°, 31.7° and 32.2° are clearly visible, related to (102) (103) (204) (205) and (2 − 1 6) MBI lattice planes, thus confirming its crystallization as hexagonal phase with the P63/mmc space group proposed by Jakubas et al.33. The further increase in MAI ratio (film 5) shows a decrease in the peak intensity which is concomitant to a lower absorption in the visible range (see Fig. 1a), indicative of either reduced MBI formation or lower quality. The additional peaks observed at low angle in films 4 and 5 are attributed to the MAI-excess in the film. Overall these results demonstrate promising optical and crystallographic properties for films 3 and 4, which invites deeper characterization.
The effect of thermal co-evaporation on film morphology was evaluated by scanning electron microscopy (SEM). MBI films were deposited on top of FTO substrates under different experimental conditions. The results, illustrated in Fig. 2, demonstrate homogeneous, compact pinhole-free perovskites (Fig. 2a,c) with conformal coating along the FTO substrate (see cross-section images in Fig. 2b,d). The presence of a non-uniform, inhomogeneous surface coverage would lead to the presence of pinholes, which are the cause of short-circuits and defect sites limiting the photovoltaic performance34. Therefore, the presence of a complete coverage would reduce the probability of shunting by an improved separation between the electron and the hole transport layer35. Interestingly, in our study both conditions lead to a compact multicrystalline film, but the grain size is highly dependent on the MAI:BiI3 ratios, changing from crystallites of around 50 nm for film 3, to a crystallite size over 300 nm for film 4. This dependence is also observed in MBI layers deposited by CVD, which grain crystal size increases twofold by increasing the MAI content in the film36.
The long-term stability of these materials was also tested after 4 months stored under dry air at room temperature (RH ~ 10%). Figure 3 shows the evolution of the XRD patterns corresponding to the best co-evaporated films, prepared at conditions 3 and 4, which did not present any significant change in the peak position and intensity over time. This excellent stability, observed in the co-evaporated film, is in good agreement with stoichiometric MBI films processed from the liquid phase, further demonstrating that the co-evaporation is a valid method for fabrication of pure hybrid bismuth halide perovskites. Previous studies on solution-processed MBI layers demonstrate that no or very small change is observed around the 29° diffraction peak after the first month of continuous air exposure24,35. Such small changes were attributed to a small amount of Bi2O3 or BiOI, formed at the MBI surface24. Interestingly, the peak attributed to the MAI-excess observed in film 4 disappears after aging, potentially due to its slow decomposition under 10% moisture.
The stability evolution observed for films 1, 2 and 5 is shown in the Supporting Information. The lack of crystallographic peaks in the XRD of the as-deposited film 1 (Figure S1) denotes a high degree of an amorphous phase. However, during ageing the precursors react and the peaks attributed to MBI appears together with a peak at low angle attributed to unreacted MAI excess. Note that the film 2 (Figure S2) demonstrate the same superior stability than films 3 and 4. However, the film with the highest MAI amount, presents the typical MBI peaks with low intensity and a peak attributed to MAI excess that disappears after ageing may be due to its slow decomposition (Figure S3).
After the analysis of the co-evaporated films, we can conclude that the optimum thin film MBI composition is between conditions 3 and 4. We selected film 4 for further analysis because of its film stability and adequate morphology. We further characterized the electronic properties of the MBI thin film by ultraviolet photoelectron spectroscopy (UPS), see UPS spectra in Figure S4. From the UPS measurement, the work function (WF) is calculated as the difference between the photon energy of the source, 21.22 eV, and the intercept of the secondary electron cutoff (SECO) and the zero intensity axis (Fig. 4b), and yields the value of 4.92 eV. The valence band maximum (VBM) was estimated by the intercept between the linear fitting of the valence band onset and the zero intensity axis (Fig. 4a) and is located 1.16 eV below the Fermi level, hence 6.08 eV below the vacuum level. As the calculated optical bandgap is 2.11 eV (see details below), the conduction band minimum (CBM) is therefore located at − 3.96 eV with respect to the vacuum level37. Finally, the Fermi energy (EF) being 1.16 eV above the valence band maximum reveals the n-type character of thin film 4. The energy level diagram is depicted in Figure S4b. These values are in the range of the values reported for solution-processed MBI films12,38,39.
For further characterization, we verified the time-resolved photoluminescence decay with MBI film (Figure S5). The sample was deposited on the glass for this measurement. The time constant was τ1 = 2.6 ns and τ2 = 13.5 ns, which is almost corresponding to the solution-processed reports39,40, as well as closed to bulk properties of this material24. From these results, we expect that the defect in the crystal could be similar to the solution-processed MBI. In addition, the PL spectra was recorded in the same sample at an excitation wavelength of 450 nm. The PL spectra (Figure S6) presents a maximum at 581.9 nm (2.13 eV), in good agreement with the calculated band gap of the layer (2.12 eV, see Table 1). To finalize the analysis, the photovoltaic behavior of the co-evaporated MBI layer 4 was evaluated. The layer was integrated in devices with standard planar n-i-p architecture, sandwiched between compact TiO2 acting as an electron transport layer, and doped spiro-MeOTAD as hole transport material. The energy diagram of the device layout is shown in Fig. 5a. Two different thicknesses of 250 nm and 500 nm thick MBI layers were studied and their respective J–V curves are shown in Fig. 5b. The photovoltaic parameters extracted from the curves are presented in Table 2. The device containing 250 nm thick film presented the best solar cell performance with PCE of 0.04% (VOC of 668 mV, JSC of 129 μA cm−2 and FF of 0.43). In contrast, the device containing 500 nm MBI layer presented lower photovoltaic parameters, which we attribute to increased charge recombination due to the large distance carriers need to travel through the material. Note that such low performances cannot be attributed to a bad homogeneity of the film, neither to a bad materials quality. On the contrary, we believe that these values are deeply related to the high exciton binding energy of the material and the non-optimized device layout used for Bi-perovskite devices (see Fig. 5a). The external quantum efficiency (EQE) of the device containing 250 nm MBI film is depicted in Figure S7. The low EQE values at higher-energies have attributed the loss in photogenerated carrier extraction efficiency near the MBI/spiro-MeOTAD interface, reflected also in the low JSC values obtained in the devices.
In summary, we report for the first time the synthesis of hybrid bismuth-based MBI semiconductor by thermal co-evaporation. After optimization of the precursor ratio (MAI and BiI3), pure MBI layers can be fabricated without the need of thermal annealing. The optimized layers present the typical optical properties of MBI but with improved morphology thanks to a compact, dense and conformal coating with long-term stability. The successful deposition of MBI via co-evaporation is a revolutionary precedent for fabricating organic–inorganic bismuth-based perovskites, which may lead future investigations for optoelectronic applications. The photovoltaic performance is expected to be enhanced with the use of charge transporting layer with better energy band alignment with the MBI perovskite.
Methods
Materials
Methylammonium iodide and bismuth (III) iodide anhydrous were purchased from Lumtec and TCI, respectively. FTO substrates (TEC-15) were purchased from Nippon Sheet Glass (NSG) group. Spiro-MeOTAD was provided by ChemBorum, titanium diisopropoxide bis(acetylacetonate), Li-bis(trifluoromethanesulphonyl) imide (LiTFSI) and 4-tert-butylpyridine (TBP) were purchased from Sigma Aldrich and FK209 Co(III) TFSI from GreatCellSolar. All of the chemicals were used as received without further purification.
Thin-film fabrication
FTO-coated glass substrates were cleaned by sonication in a 2% Hellmanex III solution, deionized water and ethanol for 10 min each, followed by a 15 min UV–O3 treatment. After the surface treatment, the substrates were introduced into the vacuum chamber for perovskite deposition. The perovskite layer was deposited at the studied precursor evaporation rates 1–5 (Table S1). The deposition was made in the PRO Line PVD 75 vacuum chamber from Kurt J. Lesker Company equipped with thermal evaporator sources. The thin films were fabricated by thermal co-evaporation of the precursors bismuth iodide (BiI3) and methylammonium iodide (MAI) in vacuum. During co-evaporation, the deposition rate of each material was controlled by independent quartz microbalance crystal sensors (QCM). MAI and BiI3 were simultaneously heated under high vacuum until its sublimation temperature. To achieve a high degree of uniformity, the substrates were kept at room temperature and were continuously rotating during the deposition. To vary the film composition, the deposition rate of BiI3 was kept at 0.4 (Å s−1) while that of MAI varied from 0.4, 0.55, 0.7, 1 to 1.4 Å s−1, obtaining the films 1–5 respectively (Table S1). The final thickness of MBI layer was around 250 nm.
Thin-film characterization
UV–Vis spectra were measured by using Lambda 950S spectrometer (PerkinElmer, Inc.). X-ray diffractograms were recorded in Bragg–Brentano geometry on a Bruker D8 Advance equipped with a ceramic tube (Cu anode, λ = 1.54060 Å). Scanning electron microscopy (SEM) images were recorded by in-lens detector of FEI Teneo Schottky Field Emission SEM at tension of 5 kV. The UPS measurements were carried out on an Axis Supra (Kratos Analytical) using UV from an He(I) source. The pass energy of the analyser was set to 10 eV. The samples were electrically grounded, and the photoelectron intensity is presented as a function of the binding energy referenced at the Fermi level of the analyser. Time-resolved photoluminescence decay was measured in a sample of MBI deposited on glass with Flurolog TCSPC (FL-1000, HORIBA) proved at 575 nm upon excitation at 455 nm. The photoluminescence emission was measured in a sample of MBI deposited on glass with a fluorescence spectrometer PerkinElmer LS 55 upon excitation at 450 nm. The thin-film stability test was performed by keeping the layers without encapsulation in dark at dry air (10% humidity) at 25 °C.
Device fabrication
FTO glass were chemically etched with Zn powder and an HCl solution. The chemically etched substrate was cleaned by sonication in a 2% Hellmanex solution, deionized water and ethanol for 10 min each, followed by a 15 min UV–O3 treatment. Titanium diisopropoxide bis(acetylacetonate) (TAA) in ethanol solution (1:15 v/v) was sprayed at 450 °C and kept annealing during 30 min. Once the substrates were cooled down, they were introduced into the vacuum chamber for perovskite deposition. The perovskite layers were deposited until the desired thickness of 250 or 500 nm, respectively. After that, the spiro-MeOTAD solution (60 mM) was spin-coated at 4,000 rpm for 30 s. The molar ratio of additives for spiro-MeOTAD solution was 0.5, 3.3 and 0.05 for Li-TFSI, TBP and FK209, respectively. Finally, a 80 nm thick Au was thermally evaporated in vacuum (10−6 mbar).
Device characterization
J–V curves were measured by using a 2,400 Keithley system in a scan rate of 50 mV s−1 and 10 mV voltage step in combination with a Xe-lamp Oriel sol3A sun simulator (Newport Corporation), which was calibrated to AM1.5G standard conditions by using an Oriel 91,150 V reference cell. The solar cells were measured without light soaking and with an illumination area through a shadow mask of 16 mm2. EQE was measured with IQE200B Quantum Efficiency Measurement System (Oriel, Newport).
References
Park, N.-G. High efficiency perovskite solar cells: materials and devices engineering. Trans. Electr. Electron. Mater. 21, 1–15 (2020).
Torabi, N. et al. Progress and challenges in perovskite photovoltaics from single- to multi-junction cells. Mater. Today Energy 12, 70–94 (2019).
Jung, M., Ji, S. G., Kim, G. & Seok, S. I. Perovskite precursor solution chemistry: from fundamentals to photovoltaic applications. Chem. Soc. Rev. 48, 2011–2038 (2019).
Zhang, H., Nazeeruddin, M. K. & Choy, W. C. H. Perovskite photovoltaics: the significant role of ligands in film formation, passivation, and stability. Adv. Mater. 31, 1–29 (2019).
Jokar, E., Chien, C. H., Tsai, C. M., Fathi, A. & Diau, E. W. G. Robust tin-based perovskite solar cells with hybrid organic cations to attain efficiency approaching 10%. Adv. Mater. 31, 1–7 (2019).
Hao, F. et al. Solvent-mediated crystallization of CH3NH3SnI3 films for heterojunction depleted perovskite solar cells. J. Am. Chem. Soc. 137, 11445–11452 (2015).
Fu, H. Review of lead-free halide perovskites as light-absorbers for photovoltaic applications: from materials to solar cells. Sol. Energy Mater. Sol. Cells. 193, 107–132 (2019).
Ganose, A. M., Savory, C. N. & Scanlon, D. O. Beyond methylammonium lead iodide: prospects for the emergent field of ns2 containing solar absorbers. Chem. Commun. 53, 20–44 (2017).
Kopacic, I. et al. Enhanced performance of germanium halide perovskite solar cells through compositional engineering. ACS Appl. Energy Mater. 1, 343–347 (2018).
Benabdallah, I. et al. Lead-free perovskite based bismuth for solar cells absorbers. J. Alloys Compd. 773, 796–801 (2019).
Lyu, M. et al. Organic–inorganic bismuth (III)-based material: a lead-free, air-stable and solution-processable light-absorber beyond organolead perovskites. Nano Res. 9, 692–702 (2016).
Wenderott, J. K., Raghav, A., Shtein, M., Green, P. F. & Satapathi, S. Local optoelectronic characterization of solvent-annealed, lead-free, bismuth-based perovskite films. Langmuir 34, 7647–7654 (2018).
Shin, S. S. et al. Solvent-engineering method to deposit compact bismuth-based thin films: mechanism and application to photovoltaics. Chem. Mater. 30, 336–343 (2018).
Sanders, S. et al. Morphology control of organic–inorganic bismuth-based perovskites for solar cell application. Phy. Status Solidi A. 215, 1800409 (2018).
Lan, C. et al. Effect of lead-free (CH3NH3)3Bi2I9 perovskite addition on spectrum absorption and enhanced photovoltaic performance of bismuth triiodide solar cells. J. Alloys Compd. 701, 834–840 (2017).
Mali, S. S., Kim, H., Kim, D.-H. & Hong, C. K. Anti-solvent assisted crystallization processed methylammonium bismuth iodide cuboids towards highly stable lead-free perovskite solar cells. ChemistrySelect. 2, 1578–1585 (2017).
Shrivastava, P., Balasubramaniam, K. R. & Bhargava, P. Effect of Br-doping and choice of precursor solvent on morphology of lead free (CH3NH3)3Bi2I9 perovskites. J. Renew. Sustain. Energy. 10, 043506 (2018).
Kulkarni, A., Singh, T., Ikegami, M. & Miyasaka, T. Photovoltaic enhancement of bismuth halide hybrid perovskite by N-methylpyrrolidone-assisted morphology conversion. RSC Adv. 7, 9456–9460 (2017).
Li, H. et al. Fabrication of lead-free (CH3NH3)3Bi2I9 perovskite photovoltaics in ethanol solvent. Chemsuschem 10, 3994–3998 (2017).
Mohammad, T., Kumar, V. & Dutta, V. Electric field assisted spray coated lead free bismuth iodide perovskite thin film for solar cell application. Sol. Energy 182, 72–79 (2019).
Wang, Y. et al. (CH3NH3)3Bi2I9 perovskite films fabricated via a two-stage electric-field-assisted reactive deposition method for solar cells application. Electrochim. Acta 329, 135173 (2020).
Jain, S. M. et al. An effective approach of vapour assisted morphological tailoring for reducing metal defect sites in lead-free, (CH3NH3)3Bi2I9 bismuth-based perovskite solar cells for improved performance and long-term stability. Nano Energy. 49, 614–624 (2018).
Hoye, R. L. Z. et al. Methylammonium bismuth iodide as a lead-free, stable hybrid organic-inorganic solar absorber. Chem. A Eur. J. 22, 2605–2610 (2016).
Stümmler, D. et al. Fabrication of methylammonium bismuth iodide layers employing methylamine vapor exposure. Phys. Status Solidi. 216, 1900169 (2019).
Malinkiewicz, O. et al. Perovskite solar cells employing organic charge-transport layers. Nat. Photon. 8, 128–132 (2014).
Ávila, J., Momblona, C., Boix, P. P., Sessolo, M. & Bolink, H. J. Vapor-deposited perovskites: the route to high-performance solar cell production?. Joule 1, 431–442 (2017).
Khazaee, M. et al. Dual-source evaporation of silver bismuth iodide films for planar junction solar cells. J. Mater. Chem. A. 7, 2095–2105 (2019).
Khazaee, M. et al. A versatile thin-film deposition method for multidimensional semiconducting bismuth halides. Chem. Mater. 30, 3538–3544 (2018).
Kawai, T. et al. Optical absorption in band-edge region of (CH3NH3)3Bi2I9 single crystals. J. Phys. Soc. Jpn. 65, 1464–1468 (1996).
Jain, S. M., Edvinsson, T. & Durrant, J. R. Green fabrication of stable lead-free bismuth based perovskite solar cells using a non-toxic solvent. Commun. Chem. 2, 1–7 (2019).
Zhang, X. et al. Active-layer evolution and efficiency improvement of (CH3NH3)3Bi2I9-based solar cell on TiO2-deposited ITO substrate. Nano Res. 9, 2921–2930 (2016).
Jakubas, R., Zaleski, J. & Sobczyk, L. Phase transitions in (CH3NH3)3Bi2I9 (MAIB). Ferroelectrics 108, 109–114 (1990).
Hoefler, S. F. et al. A zero-dimensional mixed-anion hybrid halogenobismuthate(III) semiconductor: structural, optical, and photovoltaic properties. Inorg. Chem. 57, 10576–10586 (2018).
Ahmad, K., Ansari, S. N., Natarajan, K. & Mobin, S. M. A (CH3NH3)3Bi2I9 perovskite based on a two-step deposition method: lead-free, highly stable, and with enhanced photovoltaic performance. ChemElectronChem. 6, 1192–1198 (2019).
Sanders, S. et al. Chemical vapor deposition of organic-inorganic bismuth-based perovskite films for solar cell application. Sci. Rep. 9, 1–8 (2019).
Shin, J. et al. Enhanced efficiency in lead-free bismuth iodide with post treatment based on a hole-conductor-free perovskite solar cell. Nano Res. 11, 6283–6293 (2018).
Öz, S. et al. Zero-dimensional (CH3NH3)3Bi2I9 perovskite for optoelectronic applications. Sol. Energy Mater. Sol. Cells. 158, 195–201 (2016).
Zhang, Z. et al. High-quality (CH3NH3)3Bi2I9 film-based solar cells: pushing efficiency up to 1.64%. J. Phys. Chem. Lett. 8, 4300–4307 (2017).
Wang, M. et al. High-quality sequential-vapor-deposited Cs2AgBiBr6 thin films for lead-free perovskite solar cells. Solar RRL. 2, 1800217 (2018).
Acknowledgements
This Project has received funding from the European Union’s Horizon 2020 research and innovaton programme under the Marie Skłodowska–Curie Grant Agreement No. 754462. The authors thank to the project German Research Foundation (DFG) (Projekt number 424101351)-Swiss National Foundation (SNF) (200021E_186390). C. M. thanks to the co-funded fellowship Horizon 2020-Marie Skłodowska–Curie (Agreement No. 754462).
Author information
Authors and Affiliations
Contributions
C.M. conceived the ideas, deposited and characterized films and devices and wrote the manuscript. A.A.S. and H.K. measured steady-state and time-resolved photoluminescence. M.M. measured ultraviolet photoelectron spectroscopy. M.K.N. and C.R.-C. supervised the project.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Momblona, C., Kanda, H., Sutanto, A.A. et al. Co-evaporation as an optimal technique towards compact methylammonium bismuth iodide layers. Sci Rep 10, 10640 (2020). https://doi.org/10.1038/s41598-020-67606-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-67606-1
- Springer Nature Limited