Abstract
We report the observation of exchange bias in a ferromagnetic Ga0.94Mn0.06As0.77P0.23/ Ga0.94Mn0.06As bilayer, in which the easy axis in one layer is oriented out-of-plane, and in the other in-plane. Magnetization reversal in this system is explored using planar Hall effect (PHE) measurements under various initial conditions and with various field-cooling orientations. Our results show that the two magnetic layers are ferromagnetically exchange-coupled, and that such coupling results in pronounced exchange-bias-like shifts of magnetic hysteresis loops during reversal of in-plane magnetization. The presence of exchange bias in this system can be understood on the basis of magnetic closure domains formed in the layer with the out-of-plane easy axis.
Similar content being viewed by others
Introduction
Ferromagnetic (FM) films with easy axes normal to the film plane have been extensively studied because of their promise for applications in perpendicular magnetic recording media1,2. It is well established that magnetic anisotropy in the FM semiconductor (Ga,Mn)As can be manipulated by alloying this material with phosphorus (P), which modifies strain conditions of the film in a way that results in an easy axis normal to the film when the concentration of P is sufficiently high3,4,5. By fabricating Ga0.94Mn0.06As0.77P0.23/Ga0.94Mn0.06As bilayers on GaAs (100) substrates, one can therefore, obtain monolithic FM structures consisting of two dissimilar magnetic layers, with a common in-plane lattice parameter, but with magnetizations at right angles to one another, thus providing a model system for investigating the behavior of orthogonal interfacial exchange coupling in FM semiconductor systems2,6.
One interesting phenomenon in such orthogonally-coupled FM bilayers is the occurrence of exchange bias effect in these geometries7,8,9,10,11,12. This effect is different from the more familiar exchange bias resulting from interfacial exchange interaction between a ferromagnetic and an antiferromagnetic material13, and can be explained as a consequence of the interplay between the out-of-plane and the in-plane anisotropies of the two adjacent FM films14. It is suggested that closure domains in the layer with the easy axis normal to the film are created in the region close to the interface between the two coupled FM layers, as shown schematically in Fig. 1(d–e). In micromagnetic simulations15, such closure domains with magnetizations oriented parallel and anti-parallel to an applied magnetic field change their respective volumes, and the resulting net in-plane magnetic moment of the closure domains then induces an exchange bias in the FM layer magnetized in-plane.
(a) Schematic diagram of the Ga0.94Mn0.06As0.77P0.23(21 nm)/Ga0.94Mn0.06As(12.5 nm) bilayer grown on GaAs (100) substrate. (b) Polar plot of in-plane magnetic free energy of the Ga0.94Mn0.06As layer, showing the four easy magnetization directions. (c) Optical image of Hall bar for planar Hall resistance measurement. (d) Closure domain at the Ga0.94Mn0.06As0.77P0.23/Ga0.94Mn0.06As interface, accommodating the closure of domains in GaMnAsP magnetized normal to the film plane in zero field. (e) Closure domains after field cooling, resulting in exchange bias, as discussed in the text.
Encouraged by these expectations, we grew a series of Ga0.94Mn0.06As0.77P0.23/Ga0.94Mn0.06As bilayers on GaAs (100) substrates by low-temperature molecular beam epitaxy16. The structure of the bilayer is shown schematically in Fig. 1(a). In order to further understand the interface exchange coupling mechanisms between the two FM layers, we carried out a comprehensive study of magnetization reversal in these Ga0.94Mn0.06As0.77P0.23/ Ga0.94Mn0.06As bilayers using planar Hall effect (PHE) measurements. Our results show that the Ga0.94Mn0.06As0.77P0.23 and Ga0.94Mn0.06As layers are indeed orthogonally exchange-coupled, as evidenced by the observation of pronounced shifts of the PHE loops of the Ga0.94Mn0.06As layer described in what follows.
Experiment
The growth of Ga0.94Mn0.06As0.77P0.23/Ga0.94Mn0.06As bilayers was carried out as follows. The Ga1-xMnxAs layer was grown first to a thickness of 12 nm with the phosphorus cracker cell closed. The phosphorus cell was then opened, and a ~21 nm Ga0.94Mn0.06As0.77P0.23 layer was deposited directly on Ga0.94Mn0.06As. The thicknesses of 12 nm and 21 nm for Ga0.94Mn0.06As and Ga0.94Mn0.06As0.77P0.23 layers, respectively, were selected in order to have well-defined in-plane easy axes in Ga1-xMnxAs and out-of-plane easy axes in Ga0.94Mn0.06As0.77P0.2317, so that we can investigate the interaction between orthogonal magnetic configuration in Ga0.94Mn0.06As0.77P0.23/Ga0.94Mn0.06As0.77 bilayers. During the growth the Mn content was kept constant in both layers at ~0.06. The P content in the Ga0.94Mn0.06As0.77P0.23 layer was selected in order to achieve a large tensile strain, to make certain that the easy axis in that layer was normal to the layer plane5,16. The growth was monitored by reflection high energy electron diffraction (RHEED), which showed a streaky (1 × 2) RHEED pattern throughout the growth of both layers, indicating high crystalline quality of the samples.
Temperature dependences of in-plane and out-of-plane magnetizations on the Ga0.94Mn0.06As0.77P0.23/Ga0.94Mn0.06As bilayer were carried out using a magnetometer; the Curie temperatures Tc of the Ga0.94Mn0.06As and the Ga0.94Mn0.06As0.77P0.23 were identified as 70 K and 45 K, respectively. Measurement of the planar Hall resistance (PHR) in magnetic fields whose direction can be applied along arbitrary in-plane direction provides a particularly convenient tool for investigating the details of magnetization reversal in the layer plane18,19, and we have adapted this approach for investigating the effects of exchange bias in the Ga0.94Mn0.06As layer20. For this purpose the sample was patterned by photolithography and by chemical wet etching into 100 μm × 1500 μm Hall bars with the long dimension lying along the [110] direction, as shown in Fig. 1(c). Measurements of the planar Hall resistance Rxy were performed by using a sample holder and experimental arrangement such that a magnetic field could be applied in the plane of the sample at an arbitrary angle. The experiments consisted of measuring the dependence of the planar Hall resistance (PHR) on the external field swept in several selected field directions, after cooling fields of various strengths and orientations were applied to the bilayer. The angles of magnetization ϕM, of the applied magnetic field ϕH, and of the cooling field ϕHFC are measured counterclockwise from the [110] crystallographic direction in the (001) plane.
Results
The in-plane anisotropy of the Ga0.94Mn0.06As layer were determined by measuring the angular dependence of PHR and by analyzing the results based on conditions that minimize magnetic free energy during the rotation of magnetization, as described by Son et al.21. This method is now well established as a tool for investigating magnetic anisotropy of ferromagnetic films. The obtained magnetic anisotropy energy density for the Ga0.94Mn0.06As layer is plotted in Fig. 1(b), showing the in-plane easy axes near the <100> directions.
Cooling field dependence of PHE
Figure 2(a) shows results of PHR measurements at 3 K during magnetization reversal scans for several field orientations. To discuss these results, it is important to describe the sequence of steps used in taking the data. The sample was cooled to 3 K in a field of 1 kOe applied in-plane either at ϕHFC = 45° or at 225° with respect to the [110] direction. After reducing the field to zero, the magnet was rotated to ϕH = 10°, as indicated in the figure, and the PHR was measured during a field scan between −1000 Oe and 1000 Oe. Qualitatively, the behavior of PHR scan shown in Fig. 2 is typical for Ga0.94Mn0.06As, showing abrupt changes of sign when magnetization experiences quasi-90° reorientations between the two in-plane easy axes in adjacent quadrants as the field is swept. This behavior can be described by the equation22
where t is sample thickness, k is a negative constant related to anisotropic magnetoresistance, and ϕM is the angle between the current (i.e., the [110] direction) and magnetization.
(a) Two hysteresis loops of PHR data obtained after the sample was cooled to 3 K in a field of 1 kOe applied either at 45° or 225° with respect to the [110] direction. (b) Two hysteresis loops of PHR data obtained after the sample was cooled to 3 K in a field of 1 kOe applied perpendicular, either up or down, with respect to the sample plane.
The most interesting feature of the hysteresis shown in Fig. 2(a) is the conspicuous asymmetry of the PHR data obtained after in-plane field cooling, indicating exchange-bias-like behavior. Marking the fields at which magnetization switches from one easy axis to the next during magnetization reversal as H1 … H4, as shown in Fig. 2, the PHR asymmetry is conveniently expressed by the differences of the switching fields |H1|-|H3| and |H2|-|H4|.
In Fig. 2(b), the sample was cooled to 3 K in a field of 1 kOe applied normal to the sample plane, either up or down. The field was then brought to zero, and PHR was measured during in-plane field scans between −1000 Oe and 1000 Oe at ϕH = 10°, as in Fig. 2(a). In this case the hysteresis loops of PHR are symmetric, but with a vertical shift. The data in Fig. 2 thus reveal that exchange-bias-like shifts are only observed after cooling in an in-plane field.
PHE and exchange bias
In Fig. 3(a,b) we plot the hysteresis loops of PHR for field sweeps along ϕH = 10° after applying the cooling field in several in-plane directions. From the data we conclude that the exchange bias of our bilayer film depends on the orientation of the cooling field. The observed behavior of PHR can be readily understood by considering the free energy of the (Ga,Mn)As layer that includes the additional bias field HEB oriented at some angle ϕEB in the layer plane. This can be written as19
where H is the external magnetic field; Hc and Hu are the cubic and uniaxial anisotropy fields; and HEB is the exchange bias field. The angles ϕM, ϕH, and ϕEB are the directions of magnetization M, the applied magnetic field H, and the exchange bias field HEB, respectively, measured counterclockwise from the [110] direction. In our experiment we assume that the cooling field imprints the field HEB along its direction, so that ϕEB = ϕHFC.
(Left column) Hysteresis loops of PHR data obtained after the sample was cooled to 3 K in an in-plane field of 1 kOe applied in various angles with respect to the [110] direction. (Right column) Results of simulation for the PHR during magnetization reversal obtained with HEB = 38 Oe. The asymmetric behavior of magnetization transitions shown in the left column is nicely reproduced in the simulation on the right.
The free energy, Eq. (2), determines the four easy magnetization directions of the Ga0.94Mn0.06As film in the layer plane with respect to the [110] crystal axis, shown at 45° + δ, 135°−δ, 225° + δ, and 315°−δ in Fig. 4(a). Here the δ is a deviation angle of magnetic easy axes from the <100> directions. We have plotted the energy profiles calculated at zero applied field H = 0, using the cubic and uniaxial anisotropy parameters in the absence of exchange bias. Since the energy profile at H = 0 is symmetric with respect to the <110> crystallographic directions, magnetization transitions between the easy axes are also symmetric with respect to the <110> directions. This is seen in Fig. 2(b), obtained when the sample was cooled in a field applied normal to the sample plane, i.e., when there is no exchange bias, as discussed later in the paper. It is readily seen from Eq. (2) that when the field is swept along some direction, the values of the free energy minima change relative to one another. In particular, when the magnetization lies initially along the energy minimum in quadrant, and the energy minimum in the adjacent quadrant is made deeper by the applied field, the magnetization will switch to the lower minimum when the difference between the initial and the final minimum exceeds a domain pinning energy23,24. By inserting the switching fields observed for this symmetric results shown in Fig. 2(b), we can then determine the difference between two energy minima required for the magnetization transition to occur in the absence of HEB.
Magnetic free-energy density of the film without (a) and with HEB = 38 Oe (b) The presence of an exchange bias field distorts the energy profile, making it asymmetric with respect to the crystallographic directions. (c–f) Magnetic free-energy density profile at the moment of rotation of magnetization corresponding to the switching fields H1, H2, H3 and H4. The relative change of the energy minima and maxima can be clearly seen at each switching field. The energy minima involving each transition are marked with shaded region. Open dots at the minima indicate the orientation of the initial state of magnetization, and solid dots indicate its final state after reorientation occurs.
The energy profile is no longer symmetric with respect to the < 110 > directions when HEB is present in the sample plane, as seen in Fig. 4(b) (HEB = 38 Oe and ϕEB = 45°). However, for magnetization transitions to occur between adjacent quadrants, the same conditions on the difference between adjacent energy minima are expected to apply as in the symmetric case. By varying the strength of HEB, we can then simulate the behavior of such asymmetric transitions obtained for different field cooling directions. The best results of simulation for several field cooling directions are obtained with HEB = 38 Oe, and are plotted in Fig. 3(c,d). The simulation nicely describes the asymmetric behavior of switching fields that is observed in the experiment (see the corresponding panels in the left column of Fig. 3).
Additionally, when a magnetic field is applied along 10°, that further distorts the free energy profile by making the energy of some minima deeper and maxima weaker, and others higher. This is illustrated in Fig. 4(c–f), where we show the energy profile at the four fields corresponding to transitions of magnetization calculated H1, H2, H3 and H4 as the applied field is swept along ϕH = 10°.
The specific case illustrated in Fig. 4(c–f) is as follows: the field is initially swept along ϕH = 10°, which has a component along the easy axis in the Quadrant 1, and orients the magnetization along that axis (near 45°). The field is then reversed. As the field increases in the reverse direction, its projection on the easy axis in Quadrant 2 first “flips” the magnetization to that easy axis as the minimum in Quadrant 2 is deep enough to overcome the intervening barrier, and finally flips it again to the easy axis in Quadrant 3. As the field is then swept in the positive direction, in a similar sequence the magnetization first “flips” to Quadrant 4, and finally back to Quadrant 1. Note, however, that the magnetization transition at H4 to the easy axis in Quadrant 1 occurs at a lower field than the transition at H2, in Quadrant 3 because the projection of the applied field causing the transitions is aided by the bias field in Quadrant 1, while it is opposed by the presence of the bias field in Quadrant 3. This is the cause of the observed asymmetry in PHR. The cases with HEB oriented in other directions, shown in Fig. 3(a,b) can be similarly analyzed.
Cooling field and temperature dependences of exchange bias
For completeness, we carried out PHR measurements at 3 K using cooling fields of different magnitude. Figure 5(a) shows representative PHR hysteresis loops obtained for four different cooling fields. The asymmetry of the PHR hysteresis curves systematically increases as the cooling field strength is increased. In order to quantify this asymmetry, the differences of transition fields |H1|-|H3|and|H2|-|H4|are plotted in Fig. 5(b). It is clear from the figure that as the cooling field increases, the exchange bias first increases rapidly, but eventually levels off at fields over ~100 Oe. These results indicate that a moderate cooling field of a few hundred Oe is sufficient to generate an exchange bias in our structure.
(a) The hysteresis loops of PHR data obtained under different magnitudes of cooling field. (b) The shifts observed in (a) plotted as function of the magnitude of cooling field. (c) Hysteresis loops of PHR data plotted for various temperatures. (d) The shifts shown in (c) plotted as function of the temperature.
Additionally, we have also studied the temperature dependence of exchange bias by using a cooling field of the same value (1.0 kOe), and cooling the system to a series of different temperatures. The data of this series of measurements are plotted in Fig. 5(c). Clearly, the asymmetry of PHR gradually decreases with increasing temperature, with the hysteresis becoming symmetric at temperatures over 20 K. In order to see the temperature dependence of the asymmetry, the differences of transition fields|H1|-|H3|and |H2|-|H4|obtained at several temperatures are plotted in Fig. 5(d). The asymmetries of the observed PHR scans decrease monotonically at similar rates for both |H1|-|H3| and |H2|-|H4|as the temperature increases, indicating that the exchange bias in the Ga0.94Mn0.06As0.77P0.23/Ga0.94Mn0.06As bilayer is strong function of temperature.
Discussion
The observed exchange bias can be explained in terms of closure domains created in the region at the top of the Ga0.94Mn0.06As0.77P0.23 layer, as suggested schematically in Fig. 1(d,e). Due to its out-of-plane anisotropy, under in-plane field-cooling conditions, the magnetic structure in Ga0.94Mn0.06As0.77P0.23 layer is expected to occur in multi-domain form comprised of out-of-plane and in-plane configurations that satisfy magnetic flux closure requirements indicated in the figure, similar to that observed in metallic systems involving out-of-plane films12. The presence of in-plane components of magnetization in the closure domains occurring at Ga0.94Mn0.06As0.77P0.23 interfaces then provides a mechanism for exchange coupling with the in-plane magnetization of the Ga0.94Mn0.06As layer14. Specifically, when the Ga0.94Mn0.06As0.77P0.23/Ga0.94Mn0.06As bilayer is cooled in an in-plane field, the closure domains at the interfaces of the Ga0.94Mn0.06As0.77P0.23 layer oriented parallel and anti-parallel to the cooling field change their respective sizes, as shown Fig. 1(e), so that the net in-plane magnetic moment of the closure domains induces an exchange bias effect on the hysteresis loop in in-plane phase.
Finally, we note that while the exchange bias effect occurs when the cooling field is applied in-plane, no exchange bias is observed when the cooling field is applied out-of-plane, as seen in Fig. 2(b). This can be understood as follows. When the structure is cooled in an out-of-plane field, the entire Ga0.94Mn0.06As0.77P0.23 layer will be magnetized normal to the film, either up or down, depending on the direction of the field. There is then no in-plane magnetic component in the Ga0.94Mn0.06As0.77P0.23 layer to couple to the in-plane magnetization of the Ga0.94Mn0.06As layer. In that situation the Ga0.94Mn0.06As0.77P0.23 layer will only contribute to the Hall resistance through the anomalous Hall effect, without coupling. This explains why PHR of Ga0.94Mn0.06As0.77P0.23/Ga0.94Mn0.06As bilayers after out-of-plane field cooling shows only up- and down-shifts of the PHR value, without any asymmetry of the PHR hystereses in the direction of the applied in-plane field, as is indeed seen in Fig. 2(b).
References
Richter, H. J. Journal of Physics D: Applied Physics 40(9), R149 (2007).
Dieny, B. & Chshiev, M. Reviews of Modern Physics 89(2), 025008 (2017).
Thevenard, L. et al. Physical Review B 82(10), 104422 (2010).
Cubukcu, M. et al. Physical Review B 81(4), 041202(R) (2010).
Xiang, L Ph. D dissertation, University of Notre Dame (2017).
Jiang, J. et al. Applied Physics Express 9(6), 063003 (2016).
Qin, Q. et al. Physical Review Materials 2, 104405 (2018).
Markou, A., Panagiotopoulos, I., Stoleriu, L., Stancu, A. & Ott, F. Journal of Magnetism and Magnetic Materials 485, 205–211 (2019).
Navas, D. et al. New Journal of Physics 14(11), 113001 (2012).
Manna, P. K. & Yusuf, S. M. Physics Reports 535(2), 61–99 (2014).
Sort, J., Popa, A., Rodmacq, B. & Dieny, B. Phys. Rev. B 70, 174431 (2004).
Bollero, A., Buda-Prejbeanu, L. D., Balt, V., Rodmacq, B. & Dieny, B. IEEE Trans. Magn. 42, 2990 (2006).
Nogues, J. & Schuller, I. K. J. Magn. Magn. Mater. 192, 203 (1999).
Bollero, A. et al. Phys. Rev. B 73, 144407 (2006).
Vukadinovic, N., Ben Youssef, J., Castel, V. & Labrune, M. Phys. Rev. B 79, 184405 (2009).
Li, X. et al. AIP Advances 8, 056401 (2018).
Chang, J. et al. J. Crystal Growth 512, 112 (2019).
Tang, H., Kawakami, R., Awschalom, D. & Roukes, M. Phys. Rev. Lett. 90, 107201 (2003).
Shin, D. Y., Chung, S. J., Lee, S., Liu, X. & Furdyna, J. K. Phys. Rev. Lett. 98, 047201 (2007).
Choi, S. et al. Appl. Phys. Lett. 101, 132403 (2012).
Son, H. et al. J. Appl. Phys. 103, 07F313 (2008).
Okamoto, K. J. Magn. Magn. Mater. 35, 353 (1983).
Cowburn, R. P., Gray, S. J., Ferre, J., Bland, J. A. C. & Miltat, J. J. Appl. Phys. 78, 7210 (1995).
Kim, J. et al. Phys. Rev. B 84, 184407 (2011).
Acknowledgements
This work is supported by the NSF Grant DMR14-00432; by Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education (2018R1D1A1A02042965); by Ministry of Science ICT (2018R1A4A1024157); and by a Korea University Future Research Grant.
Author information
Authors and Affiliations
Contributions
X.L. and S.L. conceived and designed the project. X.L. fabricated the bilayers. S.C. and S.K.B. carried out transport measurements. S.K.B. and S.D. conducted the structural and magnetic measurements. S.C., S.K.B. and S.L. conducted the simulations and calculations. X.L., S.L., M.D., and J.K.F. supervised the project and wrote the manuscript. All authors contributed to the scientific understanding and discussions.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Choi, S., Bac, SK., Liu, X. et al. Exchange bias in ferromagnetic bilayers with orthogonal anisotropies: the case of GaMnAsP/GaMnAs combination. Sci Rep 9, 13061 (2019). https://doi.org/10.1038/s41598-019-49492-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-49492-4
- Springer Nature Limited