Abstract
Stimuli-responsive nanogels offer promising perspectives for the development of next generation formulations for biomedical applications. In this work, poly(N-vinylcaprolactam) nanogels were synthesized varying the concentration of monomer and crosslinking agent. Thus, the inhibitory effect of poly(N-vinylcaprolactam) nanogels against HIV-1 infection is presented for the first time. In particular, we have demonstrated that one of the synthesized poly(N-vinylcaprolactam) nanogels with initial concentration of 80 mg of vinylcaprolactam and 4% of crosslinking agent shows antiviral behavior against HIV-1 infection since this nanogel inhibits the viral replication in TZM.bl target cells.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
The Joint United Nations Program on HIV/AIDS (UNAIDS) estimates that approximately 37 million people were living with HIV-1 worldwide at the end of 20161,2. In addition, HIV-1 sexual transmission is held accountable for around 80% of all infections, with roughly half of the affected individuals being women3. In the last years, the use of long-lasting, female-controlled and efficacious topical microbicides to decrease and control HIV-1 epidemic among women has strongly emerged4,5,6,7.
Many compounds with anti-HIV-1 activity have been tested as topical microbicides, such as sulfated polysaccharides like carrageenan and dextran sulfated8,9, drugs like tenofovir10,11,12 or dapivirine13, and nanostructures like dendrimers14,15,16. However, most of them have failed in the clinical trials due to vaginal toxicity and irritation, increasing the susceptibility to sexually transmitted infections rather than providing protection17,18. Recently, a patent in which hypotonic formulations of synthetic hydrogel based on poloxamer were used as vaginal or colorectum mucosal barriers was published19. Its ability for trapping viruses including HIV was demonstrated. This work constitutes, to the best of our knowledge, the only report of the use of synthetic polymeric hydrogels as anti-HIV agents by themselves. However, the development of polymeric formulations with low polydispersity values and a well-defined molecular weight results challenging. In this sense, nanogels (NGs) have emerged as sized-controlled nanostructures with important biomedical applications. NGs are three-dimensional-crosslinked polymeric matrices that have nanometric sizes in their three dimensions20. NGs combine the solids and fluids properties, and some of their properties depend on the contributions of each portion21. The liquid presence prevents the network from collapsing into an insoluble compact mass and the solid part prevents the liquid from flowing freely.
NGs have unique properties, such as, high encapsulation efficiency and protection of active agents from degradation, which make them ideal candidates as drug delivery or theranostic systems. In addition, the hydrophilic nature of NGs gives high biocompatibility, which represents a clear advantage over other types of nanomaterials in this kind of applications22. In other words, unique multifunctionality and stability of NGs are difficult to find in other types of nanosystems23,24. For example, inorganic nanomaterials such as quantum dots and magnetic and gold nanoparticles, that have numerous applications, including against sexual infection diseases (SIDs), have low colloidal stability and are rapidly eliminated by the mononuclear phagocytic system22.
Moreover, stimuli-responsive NGs respond to external stimuli (pH, temperature, magnetic field, redox environments, among others)25. These smart materials offer new promising perspectives for the development of next generation therapeutic agents. Considering all the stimuli-responsive systems, poly(N-vinylcaprolactam) (PVCL) is one of the most studied thermo-responsive polymers26,27,28,29,30, after poly(N-isopropylacrylamide) (PNIPAm)26. Recent studies have reported that PVCL is biocompatible, and then it is very attractive for biomedical and environmental applications26. Also, the possible hydrolysis of amide group of VCL will produce a polymeric carboxylic acid, which is innocuous for biomedical applications. On the contrary, PNIPAm can yieldsmall toxic amide compound31. However, deeper studies on the synthesis, functionalization, characterization and applications of PVCL-based NGs are required.
PVCL displays a thermo-responsive behavior, with a characteristic lower critical solution temperature (LCST). Accordingly, below LCST the polymer swells in water and after heating, it shrinks rapidly to a collapsed state32. It has been found that for PVCL hydrogels the swelling-collapse behavior is completely reversible with the same LCST for both processes, between 30 and 32 °C26,33.
NGs have not been tested previously as antiviral agent for inhibition of HIV-1 infection. In this context, we present, for the first time, the effect of NGs against the HIV-1 infection. Particularly, we have demonstrated that a PVCL NG with initial concentration of 80 mg of VCL and 4% of crosslinking agent (PVCL804 NG) can be considered as new potential microbicide against the HIV-1 infection since the PVCL804 NG inhibits the viral replication in TZM.bl target cells.
Experimental Section
Reagents
N-Vinylcaprolactam (VCL) was obtained from Aldrich; N,N′-methylenebisacrylamide (BIS) (99%) from Sigma-Aldrich; N,N,N′,N′ tetramethylethylenediamine (TEMED) (98%) from Fluka; potassium persulfate (KPS) from Merck; sodium dodecyl sulfate (SDS) (96%) from BioPack; 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) from Sigma-Aldrich; dimethyl sulfoxide (DMSO) from Sigma-Aldrich; nuclease-free water from Promega, Madrid, Spain; phosphate-buffered saline (PBS) from Lonza, Walkersville, MD, USA; Dulbecco’s Modified Eagle’s Medium (DMEM) from Biochrom, AG, Germany; supplemented with 5% heat-inactivated-fetal bovine serum from Life Technologies, Madrid, Spain and a cocktail of antibiotics. Dialysis membranes of cellulose ester with a molecular weight cut-off of 50 kDa were purchased from SpectrumLabs. All chemicals were used as purchased. MilliQ grade water was employed as the polymerization medium.
Synthesis of nanogels
PVCL NGs were prepared by thermo-precipitation in aqueous phase via free radical polymerization as follows: appropriate amounts of VCL and crosslinker (BIS) and, 0.0013 g of SDS (between 0.8–1.0%), were added to 3 mL MilliQ grade water. The solution was purged with nitrogen for 15 min under continuous stirring to remove dissolved oxygen. The reaction was carried out at 70 °C for about 5 h after the addition of 1% mol of KPS and 1% mol TEMED to initiate the polymerization by thermal decomposition. After the reaction, the NGs were purified by dialysis with membranes of cellulose ester with a molecular weight cut-off of 50 kDa against distilled water (2 liters) for one week (1 change of water per day) to remove unreacted monomers and the surfactant. Subsequently, for biological assays the samples were freeze-dryed obtaining a white solid.
The following NGs were obtained: PVCL800, PVCL801, PVCL802, PVCL804, PVCL600, PVCL604 and PVCL6010. They were called according to their composition as PVCLxy, where x means mg of VCL and y mol percentage of BIS respect to mols of VCL.
Spectroscopic analysis
Fourier transform infrared spectra (FT-IR) bands of the lyophilized NGs were obtained on a Nicolet iN10 (Thermo Scientific, USA; ST 2425-CONICET) using a liquid nitrogen cooled detector of Mercury Cadmium Tellurium (MCT). Data were analyzed using the OMNIC 8.3 Picta software package.
Nuclear magnetic resonance spectra were recorded on a Bruker Ultra Shield 400 (1H-NMR: 400 MHz ST 1027-CONICET) in deuterated water. Data were analyzed using the Mestre Nova software package.
Average particle diameter and phase transition temperature
Average hydrodynamic particle diameter (Dh) at different temperatures and the phase transition temperatures (Tp), were determined by dynamic light scattering (DLS) in a Nano Zetasizer instrument with a He–Ne laser (λ = 633 nm) and scattering angle of 173°. Measurements were made in a temperature range from 15 °C to 50 °C with a temperature equilibrium time of 120 s. All samples were prepared with a dilution of 1 in 10.
Cloud point temperatures (Tcp) were measured on a Shimadzu 1800 UV-vis spectrophotometer. Suspensions of NGs were heated from 15 to 50 °C while monitoring every 2 °C both the transmittance at 600 nm (1 cm path length) and the solution temperature. The Tcp of each NG was determined using the inflection point of the curve of the absorbance vs. temperature.
Thermogravimetric Analysis (TGA)
Thermal degradation curves of NGs were performed on a Shimadzu DTG-60 (Japan) (ST 2901-CONICET), measurements were carried out from room temperature to 800 °C at a heating rate of 10 °C/min under a pure nitrogen atmosphere.
Size and morphology of nanogels
Transmission electron microscopy (TEM) observations were carried out on a JEOL JEM EXII 1200 of high contrast, operating with 80 kV (INTI-IPAVE-CONICET). Samples were prepared on carbon-coated copper grids of 200 mesh from TED PELLA. The solution of each NG was dripped on a grid and left to dry at room temperature. Then, they were covered with a 2% uranyl acetate solution and again allowed to dry at room temperature.
The size distribution determined from TEM images was performed by using Image J software. Average diameter values were obtained from populations of 200 particles.
Cell viability assays
PVCL NGs toxicity was determined on TZM.bl cell line by MTT assay according to the manufacturer’s instructions by using a Synergy 4 Plate Multileaver, Biotek Instrument (USA). A stock suspension of NGs (in order to give 100 µg/mL in the experiment) was prepared by weighing the white solid obtained after freeze-drying and mixing it with nuclease-free water. Then, this sample was sonicated by 15 min to obtain a stable suspension. Lower-concentration suspensions were prepared by dilution of this stock suspension using nuclease-free water. DMSO (10%) and culture medium were used as positive and negative controls of cellular death, respectively. Each experiment was performed in triplicate.
Inhibition of HIV-1 replication experiments
Cells were seeded in p96-well plates 24 h prior to experiments (15 × 103cells/well). TZM.bl cells were treated with non-toxic concentrations of PVCL NG for 1 h before infection with R5-HIV-1NLAD8 isolate (30 ng of p24/106cells) under culture conditions. After 3 h, cells were washed twice with sterile phosphate-buffered saline (PBS) and incubated for 48 h at 37 °C and 5% CO2. Cells were lysed and the percentage of HIV-1 infection was determined by quantification of luciferase activity (Luciferase Assay System, Promega). G2-S16 dendrimer (10 µM) was used as a positive control of HIV-1 inhibition34,35. Each experiment was performed in triplicate.
Results and Discussion
In this work, a series of NGs from VCL were prepared by thermo-precipitation in aqueous phase in the presence of a surfactant (SDS) to control the size and reduce the distribution of the particles (Fig. 1). The polymerization was carried out at 70 °C, a temperature above the LCST of PVCL, and the reaction begins with a thermal initiator (KPS). When the chain length of the oligomers grows, their solubility in water decreases and the previous homogeneous systems becomes heterogeneous with particles that form a dispersed phase. Within the dispersed phase, the particles grow as the polymerization continues until the so-called “critical length” in which the polymerization is stopped. The reaction was initiated via free radical polymerization by the thermo-initiator KPS/TEMED. The polymeric NGs were synthesized by varying monomer and crosslinker ratios. NGs were purified through dialysis against water and obtained as a white solid after freeze-drying.
Spectroscopic analysis
In order to confirm the polymerization of VCL and the crosslinking with BIS, FT-IR and 1H-NMR spectroscopy measurements were carried out. Figure 2 shows FT-IR spectra corresponding to VCL and NGs. The FT-IR spectrum of the PVCL (without crosslinker) exhibited the characteristics bands at 2900–3000, 1631, and 1479 cm−1 corresponding to the stretching vibration of the C-H, C=O, and C-N, respectively36.
On the other hand, the FT-IR spectrum of the crosslinked NGs with BIS also showed a signal at 1530 cm−1 corresponding to the deformation of the N-H (amide group) and it was clearly observed that the relative intensity of this signal increased with the amount of crosslinker. The 1H-NMR spectrum of the monomer VCL exhibited the peaks at 7.2, 4.8 and 4.6 ppm (1H each, =CH) corresponding to the vinyl protons, and the peaks at 3.7, 2.6 (2H each, –CH2) and 1.7 ppm (6H, −CH2) corresponding to the caprolactam ring37. Regarding at the 1H-NMR spectra of the PVCL NGs was possible to observe the typical widening of bands as well as the disappearance of the signals coming from the vinyl protons. These facts confirm the polymerization reaction and the absence of free monomer (Fig. 3).
Average particle diameter and phase transition temperature
A large number of variables influence the nanostructure of the NGs and their thermo-responsive behavior, such as type of solvent, concentration of polymer, degree of crosslinking and ionization, among others30. In order to evaluate structure and thermo-responsive behavior, a series of NGs were synthesized.
The swelling/thermal behaviors of the NGs obtained by DLS are shown in Fig. 4. All the NGs are sized within the nanometric scale when the temperature of the medium is below LCST with a polydispersity index (PDI) values between 0.2 and 0.4. In most of the systems, the response of the NGs to the temperature leads to an increase in average size indicating the aggregation of the particles. However, the PVCL804 NG is the only one which displays collapse without aggregation when increasing the temperature. When considering both set of experiments performed using different initial amount of VCL, a clear trend can be observed: as the BIS concentration increases, the degree of aggregation observed after the Tp decreases (Fig. 4). This behavior could be attributed to stronger intra-molecular interactions present in these experimental conditions.
The average hydrodynamic diameters were determined below Tcp (Table 1). For the same initial VCL concentration, a Dh value increase was observed as a consequence of the increment of the crosslinker amount (BIS). Forcada et al.38,39 have reported the temperature-sensitive behavior according the nanostructure of gel. Because the fact that the crosslinker BIS reacts faster than VCL, a BIS rich core and a shell of VCL can be formed. According to this, at higher BIS concentration the core size increases resulting in NGs with higher sizes. This behavior can be observed for the two sets of experiment with different initial VCL concentrations. Besides, to the same BIS percentage (see PVCL804 and PVCL604), lower Dh values were obtained for lower initial concentration of VCL. This result could corroborate the presence of a core-shell structure in which the length of the shell decreases with the initial concentration of VCL.
Table 1 also shows that Tp decreases with the increase of BIS percentage, in agreement with previous work30. As it was mentioned previously, as BIS percentage increases, stronger intra-molecular interactions can be formed, for example hydrogen bonds between the amide groups of the BIS molecules. Accordingly, these hydrogen bonds behave as hydrophobic arrangements in which polymer–polymer interactions prevails on the polymer–water ones40. Consequently, the Tp decreases because the polymeric matrix interacts poorly with water molecules.
The phase transition behavior was confirmed by UV-Vis-based turbidity experiments in which the cloud point temperature (Tcp), which represents the phase transition temperature (Tp), can be determined. Transmittance values were recorded at λ = 600 nm against temperature and resulted in a sharp transition between a narrow temperature range, which varied according amount of BIS in the NG, as shown in Table 1. As it can be seen, the values and trends of Tp and Tcp are similar.
Size and morphology of nanogels
To examine the size distribution and morphology of the NGs, TEM studies were performed. Figure 5 shows TEM images and size distribution corresponding to PVCL804 and PVCL600.
The TEM images reveal that the size was estimated up to about 40 and 50 nm, respectively, showing low polydispersity in both cases and spherical shape of the particles.
The size values determined by DLS and TEM result similar for the case of the PVCL without BIS (PVCL600). However, the Dh value determined by DLS is higher than the one obtained from TEM for the crosslinked NG PVCL804. This fact can be due to the swelling in solution of the crosslinked NGs networks, this situation did not take place in the case of PVCL600 NGs due to the absence of crossing points and the poor hydrophilic character of VCL.
Thermogravimetric analysis
Thermal behavior of the dried NGs was qualitatively investigated by thermogravimetric analysis (Fig. 6). In the case of non-crosslinked NG (PVCL800), a single weight loss is observed around 460 °C corresponding to the PVCL decomposition, in accordance with previous reports41. For crosslinked nanogels (PVCL802 and PVCL804), thermograms show the beginning of thermal degradation at lower temperatures (around 360 °C) and the major weight loss is similar to the observed for not-crosslinked NG.
Cytotoxic effect and antiviral properties of NGs
We tested PVCL804 NG as a potential candidate for its use in anti-HIV topical microbicide formulation because it has a collapsed ideal size at physiological temperature. Accordingly, we first evaluated the toxicity of this NG in a cervicovaginal epithelial cell line by using a well-established metabolic activity assay (MTT).
A concentration range of PVCL804 NG (0.01 to 100 µg/mL) was tested for 48 h of exposure. Concentrations were considered non-toxic if the cellular viability was above 80% compared with non-treated control. The results show that PVCL804NG was non-toxic up to 10 µg/mL (Fig. 7). Above 10 μg/mL, a strong increase in toxicity can be observed. This may occur as a result of the increase in the size of the nanogel in the biological environment in which the assay was performed. Probably, this difference in size might be triggering cell death.
HIV-1 inhibition assays were carried out to determine the anti-HIV-1 efficacy of the PVCL804 NG. We selected the R5-HIV-1NLAD8 isolate because it is a widely used laboratory virus predominantly in the first steps of HIV-1 infection42. PVCL804 NG showed an inhibitory effect against the R5-HIV-1 isolate in vitro since we obtained inhibition rates >70% at the maximum non-toxic concentration (10 µg/mL) (Fig. 8). The ability to inhibit HIV-1 infection decreases as we reduce the concentration of the PVCL NG, exerting a dose-dependent effect.
Synthesized PVCL NGs cannot form anionic moieties which have been demonstrated to be important for antiviral activity43, therefore, its inhibitory effect should be due to the functional groups of the polymer matrix. These results support for the first time that PVCL NGs could be considered as candidates for a new HIV-1 microbicide. Nevertheless, more studies are required to reveal the mechanisms involved in this inhibitory effect.
Conclusions
Thermo-responsive PVCL NGs were easily synthesized by thermo-precipitation in aqueous phase via free radical polymerization. Chemical structure of NGs was confirmed by FT-IR and 1H-NMR, the average sizes were determined by DLS and TEM, and thermo-responsive behavior was characterized by DLS and UV-Vis-based turbidity. Most of the NGs get agglomerated with the increase of temperature. However, the NG with initial concentration of 80 mg of VCL and 4% of BIS crosslinking agent (PVCL804 NG) collapses when it is heated. Therefore, this NG has a collapsed nanometric size at physiological temperature which is ideal for biomedical applications. Taking advantage of this thermal behavior, the cytotoxicity and antiviral effect of PVCL804 NG were tested. By using a well-established metabolic activity assay (MTT), it was determined that PVCL804 NG shows no cytotoxic effect at concentrations lower than 10 µg/mL in cervicovaginal epithelial cell line. Finally, we have demonstrated the antiviral effect of PVCL804 NG against the HIV-1 infection by quantification of luciferase activity. To the best of our knowledge, we report the first NG with in vitro inhibitory effect against the R5-HIV-1 by itself. Consequently, PVCL NGs could be considered as potential candidates for new HIV-1 microbicide formulations.
References
Joint United Nations Programme on HIV/AIDS. Global AIDS UP DATE 2016. UNAIDS, https://doi.org/10.1073/pnas.86.15.5781 (2016).
Demarino, C. et al. Antiretroviral Drugs Alter the Content of Extracellular Vesicles from HIV-1-Infected Cells. Sci. Rep. 8, 1–20 (2018).
De Cock, K. M., Jaffe, H. W. & Curran, J. W. The evolving epidemiology of HIV/AIDS. Aids 26, 1205–1213 (2012).
Baeten, J. M. et al. Use of a vaginal ring containing dapivirine for HIV-1 prevention in women. Obstet. Gynecol. Surv. 71, 466–468 (2016).
Nel, A. et al. Safety and Efficacy of a Dapivirine Vaginal Ring for HIV Prevention in Women. N Engl J Med 375, 2133–2143 (2016).
Farr Zuend, C., Nomellini, J. F., Smit, J. & Horwitz, M. S. Generation of a Dual-Target, Safe, Inexpensive Microbicide that Protects Against HIV-1 and HSV-2 Disease. Sci. Rep. 8, 1–15 (2018).
Lakshmi, Y. S., Kumar, P., Kishore, G., Bhaskar, C. & Kondapi, A. K. Triple combination MPT vaginal microbicide using curcumin and efavirenz loaded lactoferrin nanoparticles. Sci. Rep. 6, 1–13 (2016).
Marais, D. et al. The effectiveness of Carraguard, a vaginal microbicide, in protecting women against high-risk human papillomavirus infection. Antivir. Ther. 16, 1219–1226 (2011).
López-Aldeguer, J., Aguirrebengoa, K., Arribas, J. R., Esté, J. A. & Kindelán, J. M. New targets and new drugs in the treatment of HIV. Enferm Infecc Microbiol Clin 23(Suppl 2), 33–40 (2005).
Andrei, G. et al. Topical tenofovir, a microbicide effective against HIV, inhibits Herpes simplex virus-2 replication. Cell Host Microbe 10, 379–389 (2011).
Klatt, N. R. et al. Vaginal bacteria modify HIV tenofovir microbicide efficacy in African women. Science (80-.). 356, 938–945 (2017).
Jayant, R. D. et al. Multifunctional Nanotherapeutics for the Treatment of neuroAIDS in Drug Abusers. Sci. Rep. 8, 1–12 (2018).
Devlin, B., Nuttall, J., Wilder, S., Woodsong, C. & Rosenberg, Z. Development of dapivirine vaginal ring for HIV prevention. Antiviral Res. 100, S3–S8 (2013).
Price, C. F. et al. SPL7013 Gel (VivaGel®) Retains Potent HIV-1 and HSV-2 Inhibitory Activity following Vaginal Administration in Humans. PLoS One 6 (2011).
Sepúlveda-Crespo, D., Gómez, R., De La Mata, F. J., Jiménez, J. L. & Muñoz-Fernández, M. Á. Polyanionic carbosilane dendrimer-conjugated antiviral drugs as efficient microbicides: Recent trends and developments in HIV treatment/therapy. Nanomedicine Nanotechnology, Biol. Med. 11, 1481–98 (2015).
Sepúlveda-Crespo, D. et al. Prevention vaginally of HIV-1 transmission in humanized BLT mice and mode of antiviral action of polyanionic carbosilane dendrimer G2-S16. Nanomedicine Nanotechnology, Biol. Med. 11, 1299–1308 (2015).
Peterson, L. et al. SAVVY® (C31G) Gel for Prevention of HIV infection in Women: A Phase 3, Double-Blind, Randomized, Placebo-Controlled Trial in Ghana. PLoS One 2 (2007).
Moscicki, A.-B. et al. Measurement of mucosal biomarkers in a phase 1 trial of intravaginal 3% SPL 7013 gel (VivaGel®) to assess expanded safety. J Acquir Immune Defic Syndr. 59, 134–140 (2012).
Maisel, K., Ensign, L., Hanes, J. & Cones, R. Hypotonic hydrogel formulations for enhanced transport of active agents at mucosal surfaces (2018).
Macchione, M. A., Biglione, C. & Strumia, M. Design, Synthesis and Architectures of Hybrid Nanomaterials for Therapy and Diagnosis Applications. Polymers (Basel). 10, 527 (2018).
Rimondino, G., Biglione, C., Martinelli, M., Alvarez Igarzábal, C. & Strumia, M. Chapter 7: Design of Multifunctional Nanogels with Intelligent Behavior. In Polymer Gels: Science and Fundamentals (eds Thakur, V. K. & Thakur, M. K.) 279–307 (Springer Singapore), https://doi.org/10.1007/978-981-10-6086-1 (2018).
Soni, K. S., Desale, S. S. & Bronich, T. K. Nanogels: An overview of properties, biomedical applications and obstacles to clinical translation. J. Control. Release 240, 109–126 (2016).
Li, Y., Maciel, D., Rodrigues, J., Shi, X. & Tomás, H. Biodegradable polymer nanogels for drug/nucleic acid delivery. Chem. Rev. 115, 8564–8608 (2015).
Ekkelenkamp, A. E., Elzes, M. R., Engbersen, J. F. J. & Paulusse, J. M. J. Responsive crosslinked polymer nanogels for imaging and therapeutics delivery. J. Mater. Chem. B 6, 210–235 (2018).
Zhan, Y. et al. Thermo/redox/pH-triple sensitive poly(N-isopropylacrylamide-co-acrylic acid) nanogels for anticancer drug delivery. J. Mater. Chem. B 3, 4221–4230 (2015).
Cortez-Lemus, N. A. & Licea-Claverie, A. Poly(N-vinylcaprolactam), a comprehensive review on a thermoresponsive polymer becoming popular. Prog. Polym. Sci. 53, 1–51 (2016).
Vihola, H., Laukkanen, A., Valtola, L., Tenhu, H. & Hirvonen, J. Cytotoxicity of thermosensitive polymers poly(N-isopropylacrylamide), poly(N-vinylcaprolactam) and amphiphilically modified poly(N-vinylcaprolactam). Biomaterials 26, 3055–3064 (2005).
Madeiros, S., Barboza, J., Ré, M., Giudici, R. & Santos, A. Solution Polymerization of N-vinylcaprolactam in 1,4-dioxane. Kinetic Dependence on Temperature, Monomer, and Initiator Concentrations. J. Appl. Polym. Sci. 118, 229–240 (2010).
Shao, L., Hu, M., Chen, L., Xu, L. & Bi, Y. RAFT polymerization of N-vinylcaprolactam and effects of the end group on the thermal response of poly(N-vinylcaprolactam). React. Funct. Polym. 72, 407–413 (2012).
Imaz, A. & Forcada, J. Optimized buffered polymerizations to produce N-vinylcaprolactam-based microgels. Eur. Polym. J. 45, 3164–3175 (2009).
Ramos, J., Imaz, A. & Forcada, J. Temperature-sensitive nanogels: Poly(N-vinylcaprolactam) versus poly(N-isopropylacrylamide). Polym. Chem. 3, 852–856 (2012).
Boyko, V. et al. Thermo-sensitive poly(N-vinylcaprolactam-co-acetoacetoxyethyl methacrylate) microgels: 1 - Synthesis and characterization. Polymer (Guildf). 44, 7821–7827 (2003).
Sahle, F. F., Giulbudagian, M., Bergueiro, J., Lademann, J. & Calderón, M. Dendritic polyglycerol and N-isopropylacrylamide based thermoresponsive nanogels as smart carriers for controlled delivery of drugs through the hair follicle. Nanoscale 9, 172–182 (2017).
Ceña-Diez, R., García-Broncano, P., De La Mata, F., Gómez, R. & Muñoz-Fernández, M. Efficacy of HIV antiviral polyanionic carbosilane dendrimer G2-S16 in the presence of semen. Int J Nanomedicine 11, 2443–2450 (2016).
Chonco, L. et al. Carbosilane dendrimer nanotechnology outlines of the broad HIV blocker profile. J. Control. Release 161, 949–958 (2012).
Wang, Y., Zheng, J., Tian, Y. & Yang, W. Acid degradable poly(vinylcaprolactam)-based nanogels with ketal linkages for drug delivery. J. Mater. Chem. B 3, 5824–5832 (2015).
Prabaharan, M., Grailer, J. J., Steeber, D. A. & Gong, S. Stimuli-responsive chitosan-graft-Poly(N-vinylcaprolactam) as a promising material for controlled hydrophobic drug delivery. Macromol. Biosci. 8, 843–851 (2008).
Imaz, A. & Forcada, J. N-Vinylcaprolactam-Based Microgels: Effect of the Concentration and Type of Cross-linker. J Polym Sci Part A Polym Chem 46, 2766–2775 (2008).
Imaz, A. & Forcada, J. N-Vinylcaprolactam-Based Microgels: Synthesis and Characterization. J Polym Sci Part A Polym Chem 46, 2510–2524 (2008).
Rimondino, G. N. et al. Rational design of dendritic thermoresponsive nanogels that undergo phase transition under endolysosomal conditions. J. Mater. Chem. B 5, 866–874 (2017).
Phetrong, S., Sansuk, C., Tangboriboonrat, P. & Paoprasert, P. Temperature-responsive crosslinked materials prepared from natural rubber and poly(N-vinylcaprolactam). Macromol. Res. 25, 799–805 (2017).
Maeda, K., Das, D., Nakata, H. & Mitsuya, H. Success, and challenges. Expert Opin. Emerg. Drugs 17, 135–145 (2012).
Peña-González, C. E. et al. Dendronized Anionic Gold Nanoparticles: Synthesis, Characterization, and Antiviral Activity. Chemistry 22, 2987–2999 (2016).
Acknowledgements
We particularly acknowledge the Spanish HIV HGM BioBank integrated in the Spanish AIDS Research Network and the National Network BioBank. This work has been (partially) funded by the RD16/0025/0019, project as part of Acción Estratégica en Salud, Plan Nacional R&D&i (2013–2016), cofinanced by Instituto de Salud Carlos III (ISCIII) and Fondo Europeo de Desarrollo Regional (FEDER), PAIS-PT17/0015/0042, Fondo Investigacion Sanitaria (PI16/01863) and EPIICAL project. CIBER-BBN is an initiative funded by the VI National R&D&i (2008–2011), Iniciativa Ingenio 2010, Consolider Program, and CIBER Actions (financed by ISCIII with assistance from FEDER). This work has been supported by Faculty of Biology and Environmental Protection for interdisciplinary research and innovation of the University of Lodz: NAWA International Academic Partnership Programme. This article is based upon work from COST Action CA17140 “Cancer Nanomedicine from the Bench to the Bedside” (European Cooperation in Science and Technology). Also, this work has been funded by argentinian financial supports as FONCYT (PICT-2015-2477), CONICET (11220150100344CO) and SECYT-UNC (30720150100698CB, 30920150100233CB and 30720150100225CB). Micaela A. Macchione, Anabella P. Rosso and Esteban M. Euti thank CONICET for the fellowship awarded. The authors also acknowledge to CYTED project 214RT0482 and Dr. Gloria Bonetto (FCQ, UNC, Argentina) for NMR determinations.
Author information
Authors and Affiliations
Contributions
A.P.R. and E.M.E. worked on the nanogels synthesis and physicochemical characterization. M.A.M. and C.G.-B. performed the biological assays. M.A.M., M.M. and M.C.S. worked on the discussions and analysis of the physicochemical characterization of nanogels. M.A.M.-F. worked on the discussions and analysis of the biological assays. All authors have contributed to writing the manuscript and reviewing the manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Macchione, M.A., Guerrero-Beltrán, C., Rosso, A.P. et al. Poly(N-vinylcaprolactam) Nanogels with Antiviral Behavior against HIV-1 Infection. Sci Rep 9, 5732 (2019). https://doi.org/10.1038/s41598-019-42150-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-42150-9
- Springer Nature Limited
This article is cited by
-
A review on the nanotechnology-based approaches for managing sexually transmitted infections
Journal of Pharmaceutical Investigation (2024)
-
Biomedical polymers: synthesis, properties, and applications
Science China Chemistry (2022)
-
The Age of Multistimuli-responsive Nanogels: The Finest Evolved Nano Delivery System in Biomedical Sciences
Biotechnology and Bioprocess Engineering (2020)