Abstract
Ordered Fe-doped In2O3 nanodot arrays with diameters between 35 nm and 80 nm are fabricated using pulsed laser deposition with the aid of ultrathin porous anodized aluminumoxide templates. The 5 at.% Fe doped In2O3 nanodot arrays are shown to consist of the cubic bixbyite structure of In2O3. The nanodot arrays are demonstrated to be doped by Fe ions with mixed valences of +2 and +3, ruling out the presence of cluster and secondary phase related to Fe. The nanodot arrays exhibit the ferromagnetism at room temperature, where the magnetic moment increases as the dot size is reduced, rising to a maximum of about 230 emu/cm3 (equivalent to an average moment on the Fe ions of 15.30 µB/Fe). This indicates an effect due to the surface of the nanodot arrays. The optical band width is also increased to 4.55 eV for the smallest dot array, thus indicating that the surface states are responsible for the magnetism and also enhance the band gap due to Burstein-Moss effect. Our results will be benefit for understanding the physical properties of oxide semiconductor nanostructures in the application of nano-spintronics devices.
Similar content being viewed by others
Introduction
Dilute magnetic semiconductors (DMSs), combining both semiconductor and ferromagnetic properties, have gained great attention due to their potential applications in spintronic devices1. Since Dietl et al. theoretically predicted the room temperature (RT) ferromagnetism in Mn doped ZnO and GaN semiconductors via Zener’s p-d exchange model2, many efforts have been carried out on a series of transition metal (TM) elements doped wide-band-gap oxide semiconductors, such as ZnO3,4,5, TiO26,7, In2O38,9,10,11,12,13 and SnO214,15. Among them, Fe-doped In2O3 magnetic semiconductor is very attractive mainly due to its excellent electrical conductivity, high optical transparency, and high solubility of Fe ions in In2O3 host lattice9,11. In the past decade, lots of studies have mainly focused on the thin film, bulk, and polycrystalline powders of Fe-doped In2O38,9,10. As advanced devices call for smaller nanostructured systems, the fabrication of lower-dimensional DMS structures is drawing increasing interest due to their advantages of small size, unique magnetic and optical properties16,17.
Actually, the fabrication and magnetic properties of Mn or Cr doped Ge, GaAs and InAs DMS nanostructured materials, such as quantum dots, have been reported18,19,20. In these studies, the self-assembly Stranski-Kranstanov (SK) growth method is adopted. However, this method results in randomly distribution, easily aggregate, and applies only to growing the material which has a large lattice mismatch with the substrate, such as MnGe and GaMnAs quantum dots on Si. Another method used to fabricate the well-patterned semiconductor nanostructures is the lithography technique or electron beam lithography, but they are impractical for large array sizes and cost relatively high21,22. Recently, ultrathin porous anodized aluminum (PAA) was used as contact templates to fabricate the large-areas, highly ordered nanostructures because of their low cost, more flexibility for pore size and separation control, easy fabrication, and so forth23,24,25,26. This bottom-up template can be used as the mask which excellently adheres to the substrate for direct deposition, and the highly ordered nanodot arrays can be obtained after removal the PAA templates.
In this paper, we presented the growth of DMS nanodot arrays by pulsed laser deposition (PLD) using the PAA templates, and provided the insights into the origin of the RT ferromagnetism in Fe-doped In2O3 nanodot arrays by a comprehensive analysis of structure and magnetic properties of the arrays. The band gap dependence on the size of Fe-doped In2O3 nanodot arrays was also investigated by the experiment.
Results and Discussion
Figure 1(a–c) show the morphology of (In0.95Fe0.05)2O3 nanodot arrays with average diameters of 80, 65 and 50 nm, respectively. The dot height and inter-dot distance of these arrays are 40 nm and 105 nm, respectively. The highly ordered nanodot arrays are the same hexagonally lattice pattern as the PAA templates. The diameter distribution of the (In0.95Fe0.05)2O3 arrays is homogenous, and the diameters of these dot arrays are approximately equal to those of the corresponding templates. Moreover, the smaller diameter of nanodot arrays than that of the PAA templates can also be obtained by reducing the height of nanodot arrays. Figure 1(d) shows the morphology of (In0.95Fe0.05)2O3 nanodot arrays with the height of 10 nm and diameter of 35 nm, where the PAA template with the pore diameter of 50 nm is left behind intentionally. The AFM profiles (Supplementary Figure S2) also clearly show that the diameter of nanodot array is reduced with the decrease of its height.
Figure 1(e–h) show the cross-sectional SEM images of nanodot arrays with different average diameters, which clearly presents the different shape and size of the nanodot arrays. From the images, we can find that the nanodot arrays with diameters of 80, 65, 50 and 35 nm are cylinder-like shape, Mongolia package-like shape, hemi-ellipsoid-like shape, and dome-like shape, respectively. The difference of the nanodot arrays in shape are thought to arise from the closure effect during the deposition process due to the different aspect ratio (pore diameter over height) of the templates27.
The diffraction patterns of the (In0.95Fe0.05)2O3 nanodot arrays with different diameters are shown in Fig. 2(a). All samples are indexed as cubic bixbyite structure of In2O3 and exhibit a preferred (222) orientation. No extra diffraction peaks of secondary phases, such as metallic Fe and Fe oxides, could be detected. A slight shift in the position of the (222) peaks to higher angles is observed, indicating a reduction in the lattice constant (see Fig. 2(b)), which might be due to the increased oxygen vacancies in the surface of the smaller nanodot arrays derived from their larger surface-to-volume28. It is also found that the (222) full width at half maximum (FWHM) peak of the nanodot arrays is large, and the FWHM becomes broader with the decrease of the diameter. This reveals the weak crystallinity and the small grain size of nanodot arrays. The grain size of (In0.95Fe0.05)2O3 nanodot arrays is also calculated by the Scherrer formula of d = 0.89λ/(β · cosθ) (λ is the wavelength of the x-ray, θ is the bragg angle, and β is the FWHM of 2θ in radians). As shown in Fig. 2(b), the grain size is decreased as the diameter reduces.
The XPS measurement was performed to investigate the valence state of Fe element in the (In0.95Fe0.05)2O3 nanodot arrays. As shown in Fig. 3(a), the binding energy of Fe 2p3/2 and Fe 2p1/2 are located at 710.3 and 723.9 eV, respectively, which excludes the formation of metallic Fe clusters, the binding energy of Fe 2p3/2 and Fe 2p1/2 in which are respectively 707.0 and 720.0 eV29. Furthermore, comparing with the binding energies of Fe2+ 2p3/2 (709.9 eV) and Fe3+ 2p3/2 (711.0 eV)29, we can conclude that the Fe element exists in the ion form with the mixed valence of +2 and +3 in the (In0.95Fe0.05)2O3 nanodot array, which is likely facilitated by the oxygen vacancies due to the very low deposition oxygen pressure (5 × 10−3 mTorr). To further study the local structure of Fe in the In2O3 lattice, we performed the XAS measurements at the Fe L-edge. Figure 3(b) presents the normalized Fe L2,3 XAS spectra of the samples. It can be found that the L 3 edge is composed of two peaks (707 eV and 709 eV) and 720 eV and 722 eV are related to the L2 edge. The split in the Fe L2,3 edges is usually attributed to the Fe ions with mixed valence of Fe2+ and Fe3+, further ruling out the appearance of metallic Fe30,31, which is consistent with the above XPS analysis. Moreover, as presented in the Fig. 3(b), there is a slight shift of Fe L 3 edge shoulder peaks to lower energies with the decreased diameter of nanodot arrays, indicating an increase of the Fe2+/Fe3+ ratio. This increase of the Fe2+ ions in smaller nanodot arrays may be ascribed to the more oxygen vacancies due to the increase in surface-to-volume ratio as the diameter decreases28.
All above structural and compositional results approve that the Fe element incorporates into the In2O3 host matrices by substituting the position of In atoms. In the following section, we will discuss the magnetic properties of our samples. Figure 4(a) shows the curves of magnetization versus magnetic field (M-H) when the external magnetic field is applied parallel to the sample surface (in-plane) after subtracting the diamagnetic background from the substrate (Supplementary Figure S3). The well-defined hysteresis loops can be clearly observed for all (In0.95Fe0.05)2O3 nanodot arrays, indicating a strong ferromagnetism above RT. As shown in Fig. 4(a), the saturation magnetic moment (Ms) of nanodot arrays sharply increases from 1.85 to 15.30 µB/Fe as the nanodot size decreases (Noted that the calculated dot volume is based on its surface and cross-section morphology in order to reduce calculate error, which is shown in Supplementary), which is much larger than that of the 5 at.% Fe doped In2O3 films8,11. Such huge Ms in zero dimensional nanodot arrays may be attributed to the abundant defects associated with the larger surfaces since the defects are reported to play an important role in the magnetic behavior of DMSs31. It is known that the vacancies and interstitials in oxide semiconductors can occur during the growth32. For zero-dimensional nanostructures, such defects are more prevalent as compared to films because of the increase in the surface area33. As the nanodot size decreases, the surface defects are increased due to the increase of the surface-to-volume ratio, and therefore, the enhanced magnetic moments is observed. Plot of Ms (µB/Fe) vs 1/D shown in the inset of Fig. 4(a) indicates the importance of surface states to the magnetism in the (In0.95Fe0.05)2O3 nanodot arrays.
The zero-field cooled (ZFC) and field-cooled (FC) curves for the 50 nm-diameter nanodot array is shown in Fig. 4(b). The obvious divergence of the ZFC and FC curves indicates that the samples are ferromagnetic in the whole temperature range. The blocking temperature do not appears in the ZFC curves, suggesting that the tiny ferromagnetic nano-clusters, such as metallic Fe and Fe oxides nanoparticle, can be ruled out34. This agrees with our results of XRD, XPS and XAS.
Figure 5(a) shows the absorption spectra of the (In0.95Fe0.05)2O3 nanodot arrays with different diameters. With the decrease of the nanodot arrays in diameter, the absorption edge of nanodot arrays shows an obvious blue-shift, indicating an increase of the band gap. Figure 5(b) shows the optical band gap determined by the Tauc model35:
where α is the absorption coefficient; hν is the photo energy; E g is the optical band gap; and A is a constant. The E g of the samples is obtained by extrapolating the linear region to zero absorption. It can be seen that the band gap increases from 3.54 to 4.55 eV as the diameter decreases from the 80 to 35 nm. The increased band gap in (In0.95Fe0.05)2O3 nanodot arrays can be possibly attributed to the Burstein-Moss effect (BM effect). The BM shift of the E g can be obtained by the following equation:36
where \({m}_{e}^{\ast }\), n e , and h are the effective electron mass in the conduction band, carrier concentration and Plank’s constant, respectively. As the diameter of nanodot arrays gets smaller, as mentioned above, there will be more oxygen vacancies which act as donors and contribute to carriers. Obviously, an increase in the carrier density will ultimately induce a blue-shift of the band gap. The decrease of the lattice constant and grain size shown Fig. 2(b) will also contribute a wider band gap37,38.
Conclusions
In summary, we have observed the RT ferromagnetism in the highly ordered Fe-doped In2O3 nanodot arrays with different sizes. The Fe-doped In2O3 nanodot arrays exhibit the obvious size-dependent magnetic and optic behaviors. Moreover, the surface defects play a crucial role in the unique huge magnetic moment of the Fe-doped In2O3 nanodot arrays. The increased band gap in (In0.95Fe0.05)2O3 nanodot arrays is possibly attributed to the Burstein-Moss effect. These results are very promising for future spintronic devices.
Experimental Details
In our experiment, the ultrathin PAA templates with various pore diameters were fabricated by a two-step anodization at a constant voltage of 40 V in 3.6 wt% H2C2O4 at 0 °C. After the two-step anodization, a thin polymethylmetacrylate (PMMA) layer was spin-coated onto the top surface of the PAA templates, and then the aluminum was etched away by immersing the template in a mixture of CuCl2 and HCl. The thin nonporous barrier layer was removed by floating the PAA templates in 5 wt% H3PO4 at 30 °C for 40 min. The template was transferred to the Al2O3 substrate, and the PMMA layer was dissolved by C3H6O at 60 °C. In this work, the average pore diameter of the PAA templates can be tuned from 50 to 80 nm by immersing the PAA templates in H3PO4 for different durations, and the thickness and inter-pore distance of the mask was about 200 and 105 nm, respectively. The Fe-doped In2O3 nanodot arrays was subsequently deposited on the PAA/Al2O3 (0001) substrate from the ceramic target of nominal composition (In0.95Fe0.05)2O3 by the PLD using a KrF excimer laser (λ = 248 nm) with a pulse repetition rate of 10 Hz and an energy density of 250 mJ/pulse. The target-to-substrate was 7 cm and the ceramic (In0.95Fe0.05)2O3 target was prepared from high-purity In2O3 (99.995%, Alfa Aesar) and α-Fe2O3 (99.995%, Alfa Aesar) powders by a conventional solid-state reaction technique. During deposition, the substrate temperature was maintained at 600 °C, the chamber oxygen pressure was 5 × 10−3 mTorr, and the height of nanodots were controlled by the deposition time. After deposition, the samples were cooled down to room temperature slowly at the same oxygen pressure. The PAA template was then dissolved using a 5 wt% NaOH solution at 35 °C and highly ordered (In0.95Fe0.05)2O3 nanodot arrays were obtained.
The morphology of the (In0.95Fe0.05)2O3 nanodot arrays and PAA templates were investigated by scanning electron microscope (SEM) and atomic force microscopy (AFM). The crystal structures of the nanodot arrays and the films were characterized by x-ray diffraction (XRD) using Cu Kα radiation (λ = 0.15406 nm). The composition of the samples was determined by x-ray photoelectron spectroscopy (XPS) and x-ray absorption spectra (XAS). Optical transmission spectra of the samples were measured by an UV-vis spectrophotometer. The magnetic properties measurements were performed by a superconducting quantum interference device (SQUID) magnetometer.
References
Wolf, S. A. et al. Spintronics: a spin-based electronics vision for the future. Science 294, 1488–1495 (2001).
Dietl, T., Ohno, H., Matsukura, F., Cibert, J. & Ferrand, D. Zener model description of ferromagnetism in zinc-blende magnetic semiconductors. Science 287, 1019–1022 (2000).
Behan, A. J. et al. Two magnetic regimes in doped ZnO corresponding to a dilute magnetic semiconductor and a dilute magnetic insulator. Phys. Rev. Lett. 100, 047206 (2008).
Xu, X. H. et al. Carrier-induced ferromagnetism in n-type ZnMnAlO and ZnCoAlO thin films at room temperature. New J. Phys. 8, 135 (2006).
Cong, C. et al. Giant magnetic moent in an anomalous ferromagnetic insulator: Co-doped ZnO. Phys. Rev. B 73, 024405 (2006).
Matsumoto, Y. et al. Room temperature ferromagnetism in transparent transition metal-doped titanium dioxide. Science 291, 854–856 (2001).
Sarkar, T. P. et al. Unexpected observation of spatially separated kondo scattering and ferromagnetism in Ta alloyed anatase TiO2 thin films. Sci. Rep. 5, 13011 (2015).
Xu, X. H. et al. Magnetic and transport properties of n-type Fe-doped In2O3 ferromagntic thin films. Appl. Phys. Lett. 94, 212510 (2009).
Yoo, Y. K. et al. Bulk synthesis and high-temperature ferromagnetism of (In1−xFe x )2O3−σ with Cu co-doping. Appl. Phys. Lett. 86, 042506 (2005).
Yan, S. M., Qiao, W., Zhong, W., Au, C. T. & Dou, Y. W. Effects of site occupancy and valence state of Fe ions on ferromagnetism in Fe-doped In2O3 diluted magnetic semiconductor. Appl. Phys. Lett. 104, 062404 (2014).
Jiang, F. X. et al. Room temperature ferromagnetism in metallic and insulating (In1−xFe x )2O3 thin films. J. Appl. Phys. 109, 053907 (2011).
Xing, P. F. et al. High temperature ferromagnetism and perpendicular magnetic anisotropy in Fe-doped In2O3. Appl. Phys. Lett. 92, 022513 (2008).
An, Y., Ren, Y., Yang, D., Wu, Z. & Liu, J. Oxygen vacancy-induced room temperature ferromagnetism and magnetoresistance in Fe-doped In2O3 films. J. Phys. Chem. C 119, 4414–4421 (2015).
Coey, J. M. D., Douvalis, A. P., Fitzgerald, C. B. & Venkatesan, M. Ferromagnetism in Fe-doped SnO2 thin films. Appl. Phys. Lett. 84, 1332 (2004).
Ogale, S. B. et al. High temperature ferromagnetism with a giant magnetic moment in transparent Co-doped SnO2−σ. Phys. Rev. Lett. 91, 077205 (2003).
Hanson, R., Kouwenhoven, L. P., Petta, J. R. & Vandersypen, L. M. K. Spin in few-electron quantum dots. Rev. Mod. Phys. 79, 1217 (2007).
Beaulac, R., Archer, P. I., Ochsenbein, S. T. & Gamelin, D. R. Mn2+-doped CdSe Quantum dots: new inorganic materials for spin-electronics and spin-photonics. Adv. Funct. Mater. 18, 3873–3891 (2008).
Xiu, F. X. et al. Electric-field-controlled ferromagnetism in high-curie-temperature Mn0.05Ge0.95 quantum dots. Nat. Mater. 9, 337334 (2010).
Wang, S. L. et al. Origin of ferromagnetism in self-assembled Ga1−xMnxAs quantum dots grown on Si. Appl. Phys. Lett. 97, 242505 (2010).
Meng, H. J., Lu, J., Yan, S., Tan, P. H. & Zhao, J. H. Systematic investigation on the influence of the As4 flux on the magnetic property of (In,Cr)As quantum dots. Eur. Phys. Lett. 84, 58007 (2008).
Kimura, H., Kobayashi, S., Yamaguchi, T. & Munekata, H. Magnetic anisotropy and magnetization reversal of (Ga, Mn) As dot-array. J. Appl. Phys. 109, 07C319 (2011).
Chen, L. et al. Enhancing the curie temperature of ferromagnetic semiconductor (Ga,Mn)As to 200 K via nanostructure engineering. Nano Lett. 11, 2584–2588 (2011).
Liang, J., Chik, H., Yin, A. & Xu, J. Two-dimensional lateral superlattices of nanostructures: nonlithographic formation by anodic membrane template. J. Appl. Phys. 91, 2544 (2002).
Bennett, S. P., Menon, L. & Heiman, D. Magnetic properties of GaMnAs nanodot arrays fabricated using porous alumina templates. J. Appl. Phys. 104, 024309 (2008).
Lei, Y. et al. Ordered arrays of highly oriented single-crystal semiconductor nanoparticles on silicon substrates. Nanotechnology 16, 1892–1898 (2005).
Mei, X. et al. Highly-ordered GaAs/AlGaAs quantum-dot arrays on GaAs (001) substrates grown by molecular-beam epitaxy using nanochannel alumina masks. Appl. Phys. Lett. 82, 967–969 (2003).
Lei, Y. & Chim, W. K. Shape and size control of regularly arrayed nanodots fabricated using ultrathin alumina masks. Chem. Mater. 17, 580–585 (2005).
Neeleshwar, S. et al. Size-dependent properties of CdSe quantum dots. Phys. Rev. B 71, 201307 (2005).
Descostes, M., Mercier, F., Thromat, N., Beaucaire, C. & Gautier-Soyer, M. Use of XPS in the determination of chemical environment and oxidation state of iron and sulfur samples: constitution of a data basis in binding energies for Fe and S reference compounds and applications to the evidence of surface species of an oxidized pyrite in a carbonate medium. Appl. Surf. Sci. 165, 288–302 (2000).
Sakai, E. et al. X-ray absorption and magnetic circular dichroism characterization of Fe-doped TiO2−δ thin films. J. Mang. Mang. Mater. 333, 130–133 (2013).
Green, R. J. et al. Adjacent Fe-Vacancy Interactions as the Origin of Room Temperature Ferromagnetism in (In1−xFe x )2O3. Phys. Rev. Lett. 115, 167401 (2015).
Shaldin, Y. V., Warchulska, I., Rabadanov, M. K. & Komar, V. K. Magnetic investigations of Cd1−xZnxTe (x = 0.12, 0.21) wide-gap semiconductors. Semiconductors 38, 288–292 (2004).
Murray, C. B., Kagan, C. R. & Bawendi, M. G. Synthesis and characterization of monodisperse nanocrystals and close-packed nanocrystal assemblies. Annu. Rev. Mater. Sci. 30, 545–610 (2000).
Fernandes, V. et al. Room temperature ferromagnetism in Co-doped CeO2 films on Si (001). Phys. Rev. B 75, 121304 (2007).
Chen, J. Z., Li, C. H. & Cheng, I. C. Phase transitions of room temperature RF-sputtered ZnO/Mg0.4Zn0.6O multilayer thin films after thermal annealing. Thin Solid Films 520, 1918–1923 (2012).
Ahn, C. H., Kim, J. H. & Cho, H. K. Tunable electrical and optical properties in composition controlled Hf:ZnO thin films grown by atomic layer deposition. J. Electrochem. Soc. 159, H384–H387 (2012).
Ghosh, R., Basak, D. & Fujihara, S. Effect of substrate-induced strain on the structural, electrical, and optical properties of polycrystalline ZnO thin films. J. Appl. Phys. 96, 2689 (2004).
Li, C.-H., Chen, J.-Z. & Cheng, I.-C. Transition of bandgap and built-in stress for sputtered HfZnO thin films after thermal treatments. J. Appl. Phys. 114, 084503 (2013).
Acknowledgements
This work is financially supported by National Key R&D Program of China (No. 2017YFB0405703), NSFC (No. 61434002), and the Special Funds of Shanxi Scholars Program. We thank Wensheng Yan for the XAS measurement at Beamline BL12-a in National Synchrotron Radiation Laboratory (NSRL).
Author information
Authors and Affiliations
Contributions
X.H. proposed and conducted the experiment. G.W. performed the XAS measurement. F.X. and D.C. wrote the manuscript. All authors contributed to the analysis and discussion for the results.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Jiang, FX., Chen, D., Zhou, GW. et al. The dramatic enhancement of ferromagnetism and band gap in Fe-doped In2O3 nanodot arrays. Sci Rep 8, 2417 (2018). https://doi.org/10.1038/s41598-018-20751-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-20751-0
- Springer Nature Limited
This article is cited by
-
Study of Variation in Optical Properties and Dispersion Parameters of Fe-Doped TiO2 Nanopowders
Transactions on Electrical and Electronic Materials (2024)
-
Magnetic and Optical Properties of Dilute Magnetic Semiconducting (In0.9Mn0.1)2O3 Nanoparticles
Journal of Electronic Materials (2023)