Abstract
Carvacrol and linalool are natural compounds extracted from plants and are known for their insecticidal and repellent activities, respectively. However, their low aqueous solubility, high photosensitivity, and high volatility restrict their application in the control of agricultural pests. The encapsulation of volatile compounds can be an effective way of overcoming such problems. Inclusion complexes between beta-cyclodextrin (β-CD) and carvacrol (CVC) or linalool (LNL) were investigated. Inclusion complexes were prepared by the kneading method. Both complexes presented 1:1 host:guest stoichiometry and the highest affinity constants were observed at 20 °C for both molecules. The nanoparticles containing carvacrol and linalool had mean diameters of 175.2 and 245.8 nm, respectively and high encapsulation efficiencies (<90%) were achieved for both compounds. Biological assays with mites (Tetranychus urticae) showed that the nanoparticles possessed repellency, acaricidal, and oviposition activities against this organism. Nanoencapsulated carvacrol and linalool were significantly more effective in terms of acaricidal and oviposition activities, while the unencapsulated compounds showed better repellency activity. The nanoformulations prepared in this study are good candidates for the sustainable and effective use of botanical compounds in agriculture, contributing to the reduction of environmental contamination, as well as promoting the effective control of pests in agriculture.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
Invertebrates, weeds, and pathogens, collectively termed pests, have always caused significant losses in agricultural production worldwide. On a global scale, weeds are the greatest cause of agricultural losses, while insects are also responsible for substantial decreases in production1,2,3,4. The advent of the green revolution led to the discovery and intensification of the use of chemical products for the control of pests and consequently increased agricultural production. However, the inappropriate use of pesticides has led to problems including residues in soil and food, contamination of hydric resources, rapid development of resistant pests, reemergence of pests, and toxicity towards nontarget organisms3,5,6,7. The increasing popularity of organic agriculture, together with the need to overcome problems associated with the emergence of resistant pests, has led to interest in natural pesticides, especially botanical insecticides and repellents, due to their easier degradation and lower toxicity in the environment. Most of these substances are site-specific and present low toxicity towards mammals and nontarget species6,7,8,9.
Carvacrol (2-methyl-5-[1-methyl-ethyl]phenol) (CVC) is a phenolic monoterpene found in the essential oils of aromatic plants of the genera Origanum, Thymus, and Thymbra, among others. This compound is generally considered safe and is approved by the Food and Drug Administration for use in foods10. Many studies have shown that CVC possesses antimicrobial, insecticidal, and antitumor activities, among other properties, as a result of which it finds uses in agriculture, medicine, and the cosmetics and food industries11.
Linalool (3,7-dimethyl-1,6-octadien-3-ol), an alcoholic monoterpene found in the essential oils of the genera Anibia, Ocimum, and Cinnamomum, is known to have antifungal12 and antimicrobial12,13 activities, and is also widely used as an insect repellent14,15.
However, important limitations on the use of these compounds in agriculture are: (i) their low aqueous solubility, resulting in reduced contact with pathogens16,17, and (ii) their susceptibility to degradation due to exposure to ultraviolet radiation, high temperatures, and oxidation by atmospheric oxygen18.
One way to overcome these limitations is by the formation of inclusion complexes with cyclodextrins19 and/or encapsulation in nanoparticles20,21, resulting in reduced losses by volatilization, photodegradation, and oxidation, as well as increased apparent solubility of the compounds.
Beta-cyclodextrin (β-CD) is a cyclic polysaccharide composed of seven units of glucose (α-D-glucopyranose) linked by α-(1,4) type bonds, which presents a hydrophilic external surface and a hydrophobic internal cavity. This structure enables cyclodextrins to form full inclusion complexes with small molecules or partial inclusion complexes with macromolecules, hence improving the physicochemical and biological properties of the complexed compound19,22,23.
Chitosan (CS) is a linear chain polyaminosaccharide obtained from the alkaline deacetylation of chitin. This cationic polymer is composed of D-glucosamine residues linked by β(1→4) glycosidic bonds. Chitosan possesses several valuable structural and functional properties, including biocompatibility, biodegradability, low toxicity, and good miscibility with other polymers, and also has a highly chemically reactive structure, due to the presence of primary amines24,25.
A factor that limits the use of chitosan in sustained release applications is its hydrophilicity, resulting in a poor capacity to carry hydrophobic molecules. Efforts have been made to improve the ability of chitosan to carry hydrophobic substances26,27, notably by means of functionalization of the chitosan structure with cyclodextrins28. In some studies, the advantages of both carriers have been combined in order to develop more efficient carrier systems, such as those providing improved mucoadhesive properties for effective release of drugs for biomedical purposes29,30, enhanced protein delivery23, sustained release of insecticides31, and removal of environmental contaminants28,32.
The aim of this work was to prepare and characterize inclusion complexes of carvacrol and linalool with β-CD. In addition, a hybrid polymer was prepared and characterized, and evaluation was made of its ability to form nanoparticles for the encapsulation of carvacrol and linalool. The physicochemical characteristics of the nanoparticles were evaluated in terms of mean diameter, polydispersity index, zeta potential, and encapsulation efficiency. In addition, their biological activities were investigated using a mite (Tetranychus urticae) as a model insect. There have been no previous studies concerning the development of chitosan nanoparticles functionalized with cyclodextrin for the encapsulation of carvacrol and linalool, with a view to their use as release systems for these active agents.
Materials and Methods
Materials
Carvacrol (98%), linalool (97%), β-cyclodextrin (MW: 1134.98 g/mol), chitosan glycol (≥60% titration), low molecular weight chitosan, N-(3-dimethylaminopropyl)-N′-ethylcarbodiimide (EDC), N-hydroxysuccinamide (NHS), and Tween 80 were purchased from Sigma. The solvent employed for the chromatographic analyses was HPLC grade acetonitrile (JT Baker, Phillipsburg, New Jersey).
Preparation of the inclusion complexes
The inclusion complexes of carvacrol and linalool with the β-CD were prepared at a 1:1 molar ratio (guest:host), using the kneading method described by Santos et al.33. A 1 g mass of β-CD was homogenized in a mortar together with 0.132 g of CVC or 0.135 g of LNL, followed by the addition of ethyl alcohol (700 μL) and manually mixing for 45 min. The resulting solid was dried in a desiccator and then stored in a hermetically sealed flask, protected from light. The encapsulation efficiencies (EEs) of the oils in the inclusion complex were determined by the method described by Marreto et al.34. The quantities of CVC and LNL present in the inclusion complexes were determined using spectrophotometric measurements at 275 and 210 nm for CVC and LNL, respectively. Firstly, the total concentrations of active agents associated with the complexes (present in the cavities and adsorbed on the surfaces) were determined by extraction with acetonitrile:water (95:5, v/v) for 48 h. This was followed by determination of the amount of active agent adsorbed on the surface. The EE was determined as the difference between the initial concentration added and the concentration adsorbed on the surface and entrapped within the cyclodextrin cavity. Quantification employed the following analytical curves: CVC = 0.0112 × + 0.0208 (r2 = 0.99386); LNL = 0.0137 × + 0.0496 (r2 = 0.99893).
Solubility isotherms
Phase solubility assays were performed according to the method described by Higuchi and Connors35. Excess CVC or LNL was added to a water:ethanol (95:5, v/v) mixture, followed by addition of increasing amounts of β-CD (0 to 10 mmol/L). The solutions were agitated for 48 h at 200 rpm, after which they were centrifuged and the supernatant was filtered through a 0.22 μm membrane. The concentrations of CVC and LNL were determined spectrophotometrically using wavelengths of 275 and 210 nm, respectively. The experiments were performed in triplicate at different temperatures (20, 25, 30, and 35 °C). The association constant was calculated using Equation 1:
where S0 is to the concentration of the bioactive substance in the absence of β-cyclodextrin.
Thermodynamic parameters
The solubility isotherm data were used to calculate the thermodynamic properties of the inclusion complexes. The parameters ΔH° and ΔS° are the standard enthalpy and entropy for transfer of carvacrol or linalool from the dispersing medium into the cyclodextrin cavity, respectively, and can be calculated using the van’t Hoff thermodynamic relation (Equation 2).
where T is the temperature (in Kelvin), R is the gas constant, and k is the affinity constant. For a linear van’t Hoff relation (ln k vs. 1/T), the slope and the intercept represent ΔH°/R and ΔS°/R, respectively36.
Preparation of the functionalized chitosan (CSgCD)
Functionalization of the chitosan glycol skeleton by the β-CD was performed according to the methodology described by Tan et al.37. Firstly, 70 mg of β-CD was dissolved in 70 mL of phosphate buffered saline (PBS) at pH 7, followed by the addition of 125 μL volumes of the EDC and NHS crosslinking agents at concentrations of 0.1 and 0.4 mol L−1, respectively. After 6 h of reaction between the β-CD and the crosslinking agents, at ambient temperature, 10.25 mg of chitosan glycol was added and the reaction was continued for a further 18 h. After 24 h of reaction, the final solution was dialyzed against PBS buffer (pH 7) for 24 h, followed by drying of the product in an oven at 35 °C for 3 days.
Characterization of the inclusion complex and the functionalized chitosan
Infrared spectroscopy (FTIR)
Infrared spectra were obtained for the β-CD, chitosan, carboxymethyl chitosan, chitosan glycol, and the functionalized polymer, using a Varian 660 spectrometer equipped with an attenuated total reflectance accessory (GladiATR, Pike Technologies) with a diamond crystal (2.2 × 3.0 mm). The instrument was operated in transmittance mode, in the frequency range from 4000 to 400 cm−1, using an incidence angle of 45°, 32 accumulations, and resolution of 8 cm−1.
X-ray diffraction (XRD)
XRD analyses were performed in transmission mode, using a PANalytical X’Pert3 diffractometer. X-ray diffraction patterns were recorded using CuKα radiation, 40 kV voltage, 20 mA current, 0.02° step resolution, and 5 s per step, in the 2θ ranges from 1° to 60° for the CD and the CSgCD38.
Thermal analyses
Thermal analyses were performed using a TA Instruments DSC Q20 calorimeter equipped with a cooling system. Calibration was achieved using the element indium. The sample (5 mg) was placed in an aluminum sample holder and the thermal profile was obtained between 5 and 300 °C, with heating at a rate of 10 °C/min under a flow of nitrogen (50 mL/min). An empty sample holder was used as a reference. Thermogravimetric analyses were performed using a Shimadzu DTG-60H instrument, with heating between 30 and 300 °C, at a rate of 10 °C/min, under a nitrogen atmosphere.
Characterization by nuclear magnetic resonance (NMR)
The 1H NMR technique was used to study the formation of the inclusion complexes between the cyclodextrin and the active agents (carvacrol and linalool), as well as the functionalization of the chitosan skeleton with cyclodextrin39. Spectra for the samples in water were collected at 25 °C, using a Varian Inova 500 MHz spectrometer equipped with a triple resonance probe. The solvent peak at 4.7 ppm was used as an internal reference. All the spectra were collected using 5 mm tubes, averaging 64 scans and with digital resolution of 0.30 Hz. The residual water signal was suppressed by pre-saturation at low irradiation power. For the inclusion complexes, ROESY spectra were collected using a mixing time of 500 ms, a window of 4000 × 4000 Hz, and acquisition of between 128 and 256 transients with 2 k data points along the ts axis18.
Preparation of functionalized chitosan nanoparticles (CSgCD)
Functionalized chitosan nanoparticles were produced using sodium tripolyphosphate (TPP) as the crosslinking agent, according to the procedure described by Keawchaoon and Yoksan40, with some modifications. Chitosan (1.5%, w/v) was dissolved overnight in an aqueous solution of acetic acid (0.5%, v/v). Tween 80 (1%, m/v) and CVC or LNL were added to the chitosan solution, followed by Turrax homogenization at 5000 rpm for 5 min. TPP solution (0.5%, w/v) was then added rapidly to the stirred emulsion, using a syringe, and moderate agitation was continued for 10 min.
Characterization of the chitosan nanoparticles
The hydrodynamic diameter and polydispersity index of the chitosan nanoparticles were determined by photon correlation spectroscopy. The zeta potential was measured by microelectrophoresis, using a ZetaSizer ZS90 analyzer (Malvern Instruments, UK). The measurements were performed in triplicate, at 25 °C. The nanoparticle tracking analysis (NTA) technique was used to measure the hydrodynamic diameter and concentration of the nanoparticles, using a laser with a wavelength of 532 nm and processing of the images with NanoSight v. 3.1 software. The analyses were performed in triplicate, with five measurements of 60 s. In order to ensure that different particles were analyzed in the replicates, the volume injected was greater than the capacity of the cell, hence displacing the content analyzed previously. For the DLS and zeta potential analyses, the nanoparticles were diluted 1:100 (v/v) in deionized water, while 1000-fold dilution was used for the NTA analyses.
Determination of encapsulation efficiency
The efficiency of encapsulation of the oils in the nanoparticles was evaluated by the ultrafiltration/centrifugation method, using Millipore ultrafiltration units with exclusion pore size of 10 kDa. The concentrations of unencapsulated CVC and LNL in the filtrate were determined by HPLC, and the encapsulation efficiency was calculated as the difference between the initial concentration added (100%) and the concentration in the ultrafiltrate. The analyses (in triplicate) were performed with an UltiMate 3000 RSLCnano HPLC system (Thermo Scientific). For CVC, a Phenomenex Gemini C18 reverse phase column (100 × 4.6 mm; 2.6 μm) was used, and the mobile phase consisted of acetonitrile:water (50:50, v/v), at a flow rate of 1 mL/min. For LNL, a Phenomenex Kinetex C18 column (250 × 4.6 mm; 3 μm) was employed, and the mobile phase consisted of acetonitrile:water (65:35, v/v), at a flow rate of 1.5 mL/min. The analytical curves used for quantification could be described by the following equations:
Transmission electron microscopy
The morphology of the nanoparticles was evaluated by transmission electron microscopy, The suspension of nanoparticles was dripped onto 200 mesh copper grids and allowed to dry for 25 min. Uranyl acetate (2%) was then dripped onto the grids containing the samples, as a contrast agent. After drying, the samples were analyzed using a Zeiss LEO 906 microscope operated at 80 kV41.
Biological assays using mites
The biological activity experiments were conducted in the Acarology Laboratory of UNESP/FCAV (Jaboticabal campus), using the mite species T. urticae, kept in greenhouse cultivations on bean plants (P. vulgaris). In order to avoid problems of mite resistance to pesticides, mite collection was made in areas without application of agricultural chemicals. The repellency, acaricidal, and oviposition activities of the formulations were analyzed. For evaluation of the biological activities, disks (diameter of 2.5 cm) were cut from the leaves of the host plant (P. vulgaris). The disks (arenas) were placed in 9 × 2 cm Petri dishes containing moistened foam (height of 1.0 cm) and a thin layer of hydrophilic cotton on the foam. In order to evaluate the repellency activity and avoid escape of the mites, the arenas were surrounded with entomological glue. The formulations were applied with a Potter spray tower calibrated at 4 lbf.in−2, using 2 mL of the formulation per arena, corresponding to 1.56 mg cm−2. Evaluation was made of the effects of the CVC and LNL formulations encapsulated in nanoparticles, as well as the unencapsulated active agents emulsified with Tween 80 (1%). After drying the products on the leaves for approximately 2 h, 10 adult female T. urticae mites were transferred to each arena. Each treatment was repeated 8 times and each repetition was composed of one arena, totaling 80 mites per treatment. The arenas were conditioned in a climate chamber at a temperature of 25 ± 1 °C, relative humidity of 60 ± 10%, and photoperiod of 12 h. Quantifications of dead and live mites, mites adhered to the glue barrier, and the numbers of eggs were performed 12, 24, 48, and 72 h after transfer of the mites. The mite repellency percentage (% repellency) was calculated considering the total number of mites and the number adhered to the entomological glue barrier. The acaricidal effect percentage was calculated considering the total number of mites and the number of dead mites. The effect on oviposition was calculated by dividing the total number of eggs by the number of live mites.
Results and Discussion
Characterization of the inclusion complexes
The kneading technique was used to obtain the inclusion complexes of β-CD with the oils, due to its effectiveness and simple implementation at the laboratory scale. Formation of the inclusion complex proceeds by removal of water molecules from the interior of the hydrophobic cavity of the cyclodextrin and their spontaneous substitution by more nonpolar molecules, which is thermodynamically favorable19,33,42. The complexation efficiencies for CVC and LNL were 86.2 ± 1.2% and 74.2 ± 3.5%, respectively. Both molecules were efficiently complexed by the cyclodextrin, with only small amounts of the molecules being adsorbed on the surfaces. In previous studies, higher complexation efficiencies of 91.3 and 91.7% were obtained for carvacrol and eugenol, using the freeze-drying method33,36. The lower efficiency achieved with the kneading method could have been due to possible volatilization losses during the maceration and drying steps33,34. However, the kneading method was easier and more convenient in the case of the chitosan functionalized with cyclodextrins.
Solubility isotherms
The formation of inclusion complexes using cyclodextrins can provide advantages to the guest molecule including increased solubility, stabilization of the molecule in solution, and reduced losses by volatilization or photodegradation19. However, these effects are dependent on the stability and solubility of the complex formed. The phase solubility curves obtained for CVC (Fig. 1A) and LNL (Fig. 1B) at different temperatures (20–25 °C) were linear, with slopes less than unity, for all the temperatures tested. Such linear relationships are considered type AL and here indicated that the solubilities of CVC and LNL were proportional to the increase of the cyclodextrin concentration and that the molar ratio for the formation of soluble complexes was 1:135. The affinity constant of the complex (Kc) decreased with increasing temperature, due to dissociation of the complex, since these are volatile compounds.
The values of K for carvacrol and linalool were calculated for the different temperatures, using the linear sections of the curves, with the values of the linear fits inserted in Equation 1. Table 1 shows the values of K obtained for the interactions of carvacrol or linalool with the β-CD at different temperatures.
The ΔH° and ΔS° values for the complexation of carvacrol and linalool were determined from the affinity constants for each temperature, using the van’t Hoff equation. The ΔH° and ΔS° values were −25.90 and −0.046 kJ/mol/K, respectively, for CVC, and −36.96 and −0.0806 kJ/mol/K, respectively, for LNL. The Gibbs free energies calculated from these thermodynamic parameters were −12.24 kJ/mol (carvacrol) and −12.94 kJ/mol (linalool), indicative of favorable complexation.
Similar results were reported by Santos33, who studied the thermodynamics of inclusion complexes of β-CD and carvacrol. It was observed that the stability constant decreased as the temperature increased, with a value of 197 M−1 obtained at 10 °C. The enthalpy and entropy values were both negative, indicating that the complexation of carvacrol was due to strong hydrophobic interactions and was mainly governed by enthalpic processes. Classically, the formation of inclusion complexes with cyclodextrins is associated with negative enthalpy (ΔH°) values, reflecting the existence of strong hydrophobic interactions, while entropy (ΔS°) values are negative or slightly positive, indicating that the inclusion of the guest molecule is not accompanied by strong desolvation and that formation of the complexes is governed primarily by enthalpic processes. Moraes et al.43 evaluated the influence of temperature on formation of the inclusion complex between bupivacaine and hydroxypropyl-β-cyclodextrin (HP-β-CD) and calculated the thermodynamic parameters. Different from the present findings, it was reported that the affinity constant increased as the temperature increased. The ΔH° and ΔS° values for the complexation were 4.75 and 53.48 J/mol K, respectively, and the Gibbs free energy calculated from these values was −11.19 kJ/mol. The positive values obtained for the enthalpy (ΔH°) could be explained by strong interaction between the guest molecule and the solvent, while the highly positive entropy (ΔS°) could be attributed to strong desolvation of both bupivacaine and the HP-β-CD in order to enable formation of the inclusion complex.
X-ray diffraction
The β-CD:CVC and β-CD:LNL inclusion complexes produced by the kneading method were investigated using XRD (Fig. 2A). The many narrow and intense lines present in the cyclodextrin diffractogram (Fig. 2A) were indicative of crystallinity. However, the diffractograms of the inclusion complexes (Fig. 2A) differed from the characteristic β-CD pattern. The formation of inclusion complexes can lead to changes in the diffraction patterns of the cyclodextrin and the guest molecule, such as amorphization (reduced crystallinity), disappearance of characteristic cyclodextrin peaks, and the appearance of new peaks. These features provide evidence for the formation of inclusion complexes19,42.
Abarca et al.44 prepared and characterized β-CD:2-NN (2-nonanone) inclusion complexes by the co-precipitation method. XRD analyses showed that the cyclodextrin peaks at 4.8° and 8° disappeared, while new peaks appeared at 12° and 18°, which could be attributed to the change in molecular organization of the cyclodextrin, with a shift from a cage-type to a channel-type structure, indicative of the formation of inclusion complexes.
Differential scanning calorimetry
The β-CD thermogram (Fig. 2B) showed a strong endothermic peak at 115 °C, associated with loss of water present in the hydrophobic cavity of the cyclodextrin. This peak was smaller in the thermograms of the inclusion complexes of carvacrol (Fig. 2B) and linalool (Fig. 2C), which could be explained by the displacement of water molecules by the molecules of carvacrol and linalool, indicating formation of the inclusion complex36,45. In addition, there were no endothermic peaks corresponding to the boiling points of carvacrol (238.7 °C) or linalool (198 °C) in the thermograms of the inclusion complexes.
Similar results were obtained by Aguiar et al.42 and Santos et al.33, who used the DSC technique to characterize inclusion complexes of β-CD with the essential oil of Croton zehntneri and carvacrol, respectively. In both cases, formation of the inclusion complex resulted in decreased intensity of the endothermic peak related to water loss, and no endothermic peaks corresponding to the essential oils were observed in the thermograms of the inclusion complexes.
Nuclear magnetic resonance analyses
Characterization of inclusion complexes should include determination of their stoichiometric formation affinity constants and their geometry. Use of nuclear magnetic resonance (NMR) enabled characterization of the inclusion complexes by means of the changes observed in the chemical shifts of the hydrogens of the cyclodextrin and guest molecules (CVC or LNL), following formation of the inclusion complexes. Table 2 presents the values of the chemical shifts obtained for carvacrol and linalool in the presence and absence of cyclodextrin, as well as the effects on the chemical shifts of the cyclodextrin hydrogens.
Assignment of the protons of the β-CD (Figs 3 and 4A) was in agreement with the literature [18]. Changes in the chemical shifts of the cyclodextrin hydrogens were observed in the presence of CVC or LNL (Fig. 3). For both inclusion complexes, the chemical shifts of the H3′ and H5′ protons of the β-CD were greater, compared to the shifts of the other protons. Hydrogens 3 and 5 are located within the cavity of the cyclodextrin molecule and were therefore most affected by the entry of the guest molecules, indicating that both molecules interacted with the cavity46,47,48. In the case of the inclusion complex containing carvacrol, the greatest effect occurred in the lower (narrower) side of the cavity of the cyclodextrin molecule, since a large change was observed in the shift of the H6′ hydrogen of the β-CD. Locci et al.18 and Kfoury et al.49 also observed changes in the shift of hydrogen 6 of the cyclodextrin molecule following the formation of inclusion complexes with carvacrol.
The results demonstrated that the chemical shifts of both guest molecules were modified by formation of the inclusion complexes (Fig. 3). Changes were observed in the chemical shifts of the hydrogens associated with the aromatic rings of the carvacrol molecules, which were probably inserted within the hydrophobic cavity of the cyclodextrin. This supported the changes observed for the hydrogens in the internal cavity of the cyclodextrin molecule, since it is known that the ring current effect can induce changes in the shifts of internal hydrogens of the cyclodextrin cavity.
Similar results were obtained by Kfoury et al.49, who studied the ability of β-CD to encapsulate and solubilize carvacrol and thymol. For both molecules, it was observed that the hydrophobic interactions occurred between the hydrogen atoms present in the aromatic rings of the molecules and the hydrogens of the internal cavity of the cyclodextrin. In addition, Locci et al.18 prepared inclusion complexes of β-CD with carvacrol, eugenol, and thymol, and found that the aromatic rings of the molecules were responsible for the interactions with the host molecules.
In the case of linalool (data not shown), the hydrogens that showed the greatest chemical shift changes were H1, H4, and H5, which are the hydrogens located in the main chain of the molecule, indicating that these groups were probably close to the H3 and H5 hydrogens of the cyclodextrin. Numanoğlu et al.50 prepared inclusion complexes of linalool and benzyl acetate with hydroxypropyl-beta-cyclodextrin. Inclusion complex formation was confirmed by 1H NMR, which showed that complexation of the molecules caused changes in the chemical shifts of hydrogens 3 and 5 present in the hydrophobic cavity of the host molecule, as also found in the present work.
In order to confirm these observations, ROESY spectra were obtained in order to elucidate the presence and geometry of intermolecular interactions between β-CD and CVC or LNL. The most significant interactions identified from these spectra (Fig. 4B) were between the signals at 6.878, 6.558, and 6.539 ppm, corresponding to hydrogens H3, H4, and H6 of CVC, respectively, and the β-CD H5 signal at 3.639 ppm. In addition, the signal at 3.772 ppm, corresponding to H3 of the β-CD, showed interactions with the CVC H6 and H9,10 signals at 6.543 and 1.123 ppm, respectively. These results suggested that the aromatic ring of CVC was fully inserted in the hydrophobic cavity of the host molecule (S1, Supplementary Material).
Similar results were found by Locci et al.18, who used ROESY analysis to show that the isopropyl group was located near the wider extremity of the cyclodextrin cavity, while the OH group was positioned at the narrower side of the cavity.
ROESY analyses of the LNL complex (data not shown) revealed that the signal for the H5 hydrogen of the cyclodextrin (at 3.674 ppm) mainly interacted with the LNL signals at 5.207 ppm (H6) and 5.048 ppm (H1), while the signal for the cyclodextrin H3 hydrogen (at 3.802 ppm) interacted with the signal for the H8 hydrogen of LNL (at 1.578 ppm). There was also interaction of the H6 hydrogen of the CD with the -OH group (1.658 ppm) of the LNL, indicating that this group was located in the narrower side of the cyclodextrin cavity51,52,53.
Functionalized chitosan (CSgCD)
Chitosan glycol is a commercially available chitosan derivative whose high aqueous solubility is due to the presence of the glycol group. It is widely used in biomedical applications for the sustained release of active agents and as a carrier for siRNA, among other applications. Chitosan glycol was selected for the development of the functionalized polymers because its solubility facilitated substitution of the amino group by the cyclodextrin. The polymers were functionalized according to the methodology described by Tan et al.37, and were characterized using FTIR, XRD, DSC, TG, and NMR analyses.
Characterization of the functionalization of chitosan glycol with cyclodextrin
Functionalization of the chitosan with cyclodextrin was characterized using nuclear magnetic resonance (NMR), X-ray diffractometry (XRD), differential scanning calorimetry (DSC), thermogravimetry (TG), and infrared spectroscopy (FTIR).
In the NMR analyses, signals for gCS between δ 4.223 and 3.450 ppm were attributed to hydrogens H3-H6 (S2A, Supplementary Material), while a singlet at δ 3.131 ppm was attributed to H2 and a singlet at δ 2.037 was assigned to the methyl group of gCS. These assignments were in agreement with previous results reported in the literature54,55. In the β-CD spectrum, the hydrogens were assigned as shown in Table 2. In the spectrum of the functionalized polymer (S2C, Supplementary Material), a doublet at δ 4.94 ppm corresponded to H1 of the β-CD, while a triplet at δ 3.80 ppm, a double doublet at δ 3.52 ppm, and a triplet at δ 3.47 ppm were attributed to the H3, H2, and H4 hydrogens of the β-CD, respectively. Peaks between δ 3.76 and 3.64 ppm were attributed to H6 and H5 of the β-CD and H3-H6 of the gCS. Additionally, a singlet at δ 2.761 ppm was attributed to hydrogens of the methyl group (CH3) of gCS56,57.
In addition to the 1H spectra, analyses were also made of diffusion coefficient measurements (DOSY). This technique enables evaluation of the Brownian motion of the molecules, which is essentially governed by the size of the molecule and the diffusion resistance of the medium58,59. Molecular diffusion coefficients have been widely used in studies of molecular interactions between macromolecules; when a molecule of lower molecular mass binds to a molecule with greater molecular mass, its translational movement decreases, resulting in a lower diffusion coefficient value59,60. The results showed that the diffusion rate of the β-CD molecule was 2.15 ± 0.12 × 10−10 m2/s, while association with the polymer reduced the diffusion rate to 1.80 ± 0.09 × 10−10 m2/s, indicating that the mobility of the cyclodextrin molecules decreased after functionalization with the chitosan glycol.
X-ray diffraction analysis of chitosan glycol (S3, Supplementary Material) revealed a broad peak at 20–25° associated with the semicrystalline structure of this polymer61,62. Analysis of the β-CD reflected the crystalline nature of this material (S3, Supplementary Material), as shown by narrow peaks at 9.14°, 10.8°, 12.6°, and 22.8°, in agreement with results reported previously63. In the case of functionalized chitosan (Fig. 5A), the diffractogram showed the disappearance of the β-CD lines at 9.14°, 10.8°, and 12.6°54,61,62, while the appearance of an intense line at 31.7° and low intensity lines at 45.5°, 56.5°, and 66.4° reflected new solid crystalline phases associated with the formation of a modified polymer of the same nature. Changes in the crystalline phase of chitosan after functionalization with cyclodextrins have also been observed elsewhere28,32,56.
Thermal analysis of the unmodified chitosan glycol (S4, Supplementary Material) revealed a broad endothermic peak at 92 °C, associated with the loss of hydration water of the solid state polymer, together with an exothermic peak at 265 °C, due to decomposition of the chitosan carbon chain. The cyclodextrin (S4, Supplementary Material) showed dehydration and decomposition peaks at 145 and 320 °C, respectively. The functionalized polymer (CSgCD) (Fig. 5B) showed an endothermic peak at 115 °C, associated with the evaporation of water. The shift of this peak was indicative of physical and molecular changes in the chitosan following functionalization with the cyclodextrin molecule. There was also a small increase in the thermal stability of the functionalized polymer, indicated by an increase of the temperature required for degradation of the carbon chain. Gonil et al.56 functionalized chitosan with cyclodextrin with different proportions of N-substitution (5, 11, and 23%), and DSC analyses showed that the degree of N-substitution affected the affinity of the polymer for water, as evidenced by a shift and change of area of the endothermic peak corresponding to water, compared to the unmodified chitosan.
The TG/DTA curves for chitosan glycol (S5, Supplementary Material) showed a 10% mass loss between 25 and 149 °C, corresponding to the loss of water associated with this hydrophilic polymer. The second stage of mass loss (34%), between 154 and 290 °C, corresponded to the decomposition of organic matter64. The β-CD (S5, Supplementary Material) showed a 15% mass loss between 27 and 95 °C, attributed to the elimination of water from the hydrophobic cavities of the cyclodextrin48. In the case of the functionalized polymer (Fig. 5C), the decomposition of organic matter started at a higher temperature (194 °C), compared to the non-functionalized chitosan, indicative of the effect of functionalization with the cyclodextrin. Similar results were obtained by Tan et al.37, who studied the functionalization of chitosan glycol with carboxymethyl-β-CD. Thermogravimetric data showed that the decomposition temperature of the functionalized polymer was higher than that for the chitosan but lower than for the carboxymethyl-β-CD, indicating that functionalization of the chitosan resulted in greater thermal stability.
Characterization using FTIR provided further confirmation of functionalization of the chitosan with the β-CD (S6, Supplementary Material). The β-CD spectrum presented characteristic bands including α-pyranyl vibration at 3405 cm−1, axial deformation of OH bonds, CH2 stretching at 2926 cm−1, stretching of C-C bonds at 1155 cm−1, and α-pyranyl vibration at 946.8 cm−1. The chitosan spectrum showed a band corresponding to β-pyranyl vibration at 888.5 cm−1. The spectrum of the functionalized polymer showed bands corresponding to β-CD at 945 cm−1 and chitosan glycol at 867.2 cm−1, while the band at 1744 cm−1 corresponding to stretching vibration of the carbonyl group almost disappeared after reaction with the amino group of the chitosan glycol. Similar results were obtained by Tan et al.37 for functionalization of chitosan glycol with carboxymethyl-β-CD.
Chitosan/TPP nanoparticles containing LNL and CVC
The NP nanoparticles were prepared by the ionic gelation technique, in which ionic interaction between the positively charged CS and the negative charges of TPP results in the formation of inter- and intramolecular bonds. Table 2 summarizes the physicochemical characteristics of the nanoparticles prepared with the functionalized chitosan in the absence of an active agent (NP), the nanoparticles containing carvacrol (NP/CVC), and those containing linalool (NP/LNL).
Due to the low aqueous solubilities of the two active agents used in this work, the functionalized chitosan nanoparticles (NP) were produced using Tween 80 to solubilize the compounds. The mean diameter of the control nanoparticles was 465 ± 45.4 nm, while addition of the active agents led to significant reductions of the mean diameters to 175.2 ± 2.97 and 245.8 ± 29.5 nm, respectively, for the NP_CVC and NP_LNL nanoparticles. The polydispersity index values of both nanoparticulate systems containing the active agents were lower than obtained for the control nanoparticles (NP), indicating that the former nanoformulations were more homogeneous in the presence of the oils. However, it is worth noting that these were not comparable systems, since the control nanoparticles did not include any type of oil in their composition; they were formed only by the mixture of functionalized chitosan and the Tween surfactant. The zeta potential and pH values showed no significant differences between the control nanoparticles and the nanoparticles containing the active compounds.
The encapsulation efficiencies obtained for CVC and LNL were 95.3 ± 0.8% and 93.1 ± 1.2%, respectively. The higher encapsulation efficiency for CVC could be explained by the lower aqueous solubility of this compound (0.11 g/L), compared to LNL (1.589 g/L), as well as the different values of the affinity constant (170.1 ± 0.57 for CVC and 228.2 ± 0.05 for LNL) and the free energy of formation of the complex (−12.24 and −12.94 for CVC and LNL, respectively).
Morphological characterization of the nanoparticles containing the active agents by transmission electron microscopy showed that the nanoparticles were spherical (Fig. 6), with sizes of 136.3 and 175.7 nm, respectively, for the particles containing carvacrol and linalool. The diameter values were smaller than those obtained by photon correlation spectroscopy, because the TEM technique measures the diameter of dry nanoparticles, while the DLS method measures the size of the nanoparticles in solution, including the hydration barriers surrounding the nanoparticles41.
Yuan et al.30 prepared β-cyclodextrin-grafted chitosan nanoparticles (CDgCS) as a novel carrier for drugs with low solubility in water, using ketoprofen as a model drug. The nanoparticles were prepared by the ionic gelation method, with TPP as a crosslinking agent. The spherical nanoparticles obtained were between 202 and 589 nm in size, with polydispersity index between 0.1 and 0.3, and zeta potential between +23 and +43 mV. The encapsulation efficiency and drug loading values were in the ranges 55.4–75.3% and 13.4–16.2%, respectively. Nanoparticles with higher substitution percentage provided lower release of ketoprofen, while higher release occurred when the release medium was more acidic (pH 4.0) than when it was more basic (pH 6.8).
Izawa et al.57 investigated the carboxymethylation of α, β, and γ cyclodextrins and subsequent functionalization of chitosan. Nanoparticles were prepared containing doxorubicin crosslinked with TPP, which showed sizes of around 100 nm and the presence of aggregates (~600 nm). The efficiencies of encapsulation of doxorubicin by the nanoparticles produced with CS and the α, β, and γ cyclodextrins were 17, 17.1, 20.2, and 28.6%, respectively. The nanoparticles produced with the γ-CD-functionalized polymer formed a moderate inclusion complex with doxorubicin, resulting in an encapsulation efficiency 1.7-fold higher than obtained with CS. The higher encapsulation efficiency was attributed to ligand:host interactions as well as electrostatic interactions.
Sajomsang et al.29 prepared and characterized a mucoadhesive carrier composed of an inclusion complex between eugenol and a soluble cyclodextrin derivative grafted onto chitosan (QCD-g-CS). Different concentrations of β-CD (5–23%) were studied in order to improve solubility and mucoadhesion. The results showed that the QCD-g-CS self-aggregated at the critical aggregation concentration (CAC). The CAC values for QCD5-g-CS, QCD11-g-CS, and QCD23-g-CS were 0.156, 0.156, and 0.312 mg/mL, respectively. These self-aggregates were able to capture eugenol in both the hydrophobic β-CD cavities and the hydrophobic cores of the aggregates. Encapsulation efficiencies of 63.8, 77.5, and 59.5% were obtained for QCD5-g-CS, QCD11-g-CS, and QCD23-g-CS, respectively.
The functionalization of chitosan with cyclodextrin performed in this study resulted in materials with colloidal characteristics analogous to those described in the literature for similar systems, with higher complexation efficiency values. These systems therefore have many potential applications, for example in the biotechnological and agricultural sectors.
Biological assays
The biological activity assays were conducted using the mite Tetranychus urticae Koch, which is an important agricultural pest that affects crops such as cotton, beans, and others, causing extensive damage.
The assays were performed as a function of time (0, 12, 24, 48, and 72 h), with evaluation of repellency, acaricidal activity, and effect on oviposition. Figure 6 shows the results of the assays for encapsulated CVC and LNL, as well as for CVC and LNL in emulsions with Tween 80. As discussed previously, the control nanoparticles (without the presence of oils), showed very different physico-chemical characteristics, while the presence of the oils improved the stability of the suspensions. Hence, the biological assays were not performed for these particles, in view of the differences in properties between them, which would lead to difficulties in comparing the results.
It can be seen from Fig. 7A that the compounds presented high repellency activities against the mites, which were killed in the times studied. The nanoencapsulated compounds initially presented significantly lower effects, compared to the unencapsulated compounds, with the activities increasing as a function of time. This could have been due to modification of the release profiles of the compounds after encapsulation, since the compounds were not immediately fully available to cause an effect, but were progressively released over time65. However, despite their lower initial effectiveness, at the end of the trial period the encapsulated compounds showed repellency activities greater than 80%. The high repellency activities of the compounds towards Tetranychus urticae were in agreement with previous studies66,67,68,69,70,71. Pavela et al.67 studied the fumigant effect of 18 different commercial essential oils on Tetranychus urticae. According to the authors, the composition of the essential oils played a crucial role in the fumigant effect for all stages of development of T. urticae. The most effective essential oils were those of Mentha spicata and Ocimum basilicum, mainly composed of linalool and carvone (a precursor of carcavrol in the process of acid-catalyzed isomerization).
Biological effects of the botanical compounds (encapsulated or not) against the two-spotted spider mite (Tetranychus urticae), as a function of time. (A) Repellency effect, (B) acaricidal effect, and (C) effect on oviposition. A significance level of p < 0.05 was considered for the differences obtained for the same time; ξ* and ϕ* indicate significant differences relative to unencapsulated carvacrol and linalool, respectively.
It is noteworthy that even with high repellency activity, the compounds also presented acaricidal activity and hindered oviposition (Fig. 7B,C). It should also be emphasized that when the active substances were encapsulated in the nanoparticles, there were significant increases in acaricidal activity, in addition to significant decreases in oviposition. At the final time studied (72 h), CVC and LNL presented acaricidal activities of 3.75 ± 0.51 and 2.5 ± 0.47%, respectively, whereas the encapsulated compounds presented values of 15.35 ± 1.87 and 16.25 ± 2.02%, respectively. In the case of oviposition, at 72 h the encapsulated CVC and LNL decreased the amounts of eggs per female by 1.3 ± 0.2 and 1.8 ± 0.1 times, compared to the unencapsulated CVC and LNL, respectively. The greater effectiveness of the nanoparticle formulations could have been due to improved stability of the compounds after encapsulation, in addition to the modified release, allowing the compounds to remain at concentrations causing effective toxicity towards the mites. These results were similar to those found by Ebadollahi et al.65, who evaluated the acaricidal activity (against Tetranychus urticae) of the essential oils of Thymus eriocalyx and Thymus kotschyanus nanoencapsulated in mesoporous material (MCM-41). According to the authors, the nanoencapsulation of the essential oils increased their effectiveness about 4-fold, compared to the unencapsulated compounds. It was also suggested that the observed effects were due to decreased degradation of the compounds and the slow release of the active substances in the essential oils.
Ziaee et al.72 encapsulated the essential oil of Carum copticum in nanogels of chitosan/myristic acid and evaluated its effects on two agricultural pests, Sitophilus granarius and Tribolium confusum. According to the findings, the oil-loaded nanogels were 8.9 and 3.7 times more toxic than the unencapsulated oil against S. granarius and T. confusum, respectively. The nanoencapsulation also increased the effectiveness of the oil as a function of time. These results were ascribed to increased oil stability (decreased degradation), as well as sustained release of the compound as a function of time.
In summary, both CVC and LNL, whether nanoencapsulated or not, showed high repellency against Tetranychus urticae. However, use of the encapsulated compounds resulted in significant increases in acaricidal activity, as well as decreases in oviposition. It should be noted that all the formulations presented significant differences, relative to the control (Table S1, Supplementary Information). Hence, the prepared nanoparticles containing these essential oils were shown to be promising for the control of the mite, since the formulations simultaneously presented repellency and acaricidal effects. Tak et al.66 studied the acaricidal and repellency activities of active compounds derived from plant essential oils towards Tetranychus urticae Koch, and also observed simultaneous acaricidal and repellency effects of carvacrol and linalool. However, it was suggested that a number of factors could greatly affect the toxicity or repellency of the active compounds. These included the effects of vapor pressure, interaction with treated surfaces (speed/degree of metabolism and penetration into leaf structures), test methods (direct contact, residual contact, or spraying), and the interaction between the compounds and the target species (including the effects of body size, degree of penetration, and delivery).
Conclusions
Beta-cyclodextrin inclusion complexes were produced with carvacrol (a botanical insecticide) and linalool (a botanical repellent) as guest molecules. Characterization of the materials by different methods confirmed formation of the inclusion complexes. The β-CD complexation efficiency obtained for carvacrol was higher than for linalool, although high efficiencies were observed in both cases. Nanoparticulate systems based on natural polysaccharides (chitosan and cyclodextrin) were prepared using the ionic gelation method and were used as carriers for carvacrol and linalool. This is the first report concerning the use of nanoparticulate systems of chitosan functionalized with cyclodextrins to carry these low aqueous solubility compounds. The nanoformulations presented good colloidal characteristics (size, polydispersity, and zeta potential) and high encapsulation efficiencies for both active agents. The findings suggest that these nanocarrier systems may be good candidates for improving the lifetimes of carvacrol and linalool when exposed to the environment. Nanoencapsulated carvacrol and linalool showed repellency, acaricidal, and oviposition activities against Tetranychus urticae. The results open perspectives for the encapsulation of other active agents, since hydrophilic substances can be transported in the polymeric chitosan matrix, while hydrophobic substances can be carried in the cavities of the cyclodextrins present on functionalized chitosan, offering the potential for applications in different areas, including agriculture.
Change history
16 May 2018
A correction to this article has been published and is linked from the HTML and PDF versions of this paper. The error has not been fixed in the paper.
References
Oerke, E.-C. Crop losses to pests. J. Agric. Sci. 144, 31 (2006).
Oliveira, C. M., Auad, A. M., Mendes, S. M. & Frizzas, M. R. Crop losses and the economic impact of insect pests on Brazilian agriculture. Crop Prot. 56, 50–54 (2014).
Pretty, J. & Pervez Bharucha, Z. Integrated Pest Management for Sustainable Intensification of Agriculture in Asia andAfrica. Insects 6, 152–182 (2015).
Savary, S., Ficke, A., Aubertot, J.-N. & Hollier, C. Crop losses due to diseases and their implications for global food production losses and food security. Food Secur. 4, 519–537 (2012).
Copping, L. G. & Duke, S. O. Natural products that have been used commercially as crop protection agents. Pest Manag. Sci. 63, 524–554 (2007).
Dayan, F. E., Cantrell, C. L. & Duke, S. O. Natural products in crop protection. Bioorg. Med. Chem. 17, 4022–4034 (2009).
Xu, P., Choo, Y.-M., Rosa, A. D. L. & Leal, W. S. Mosquito odorant receptor for DEET and methyl jasmonate. Proc. Natl. Acad. Sci. 111, 16592–16597 (2014).
Ponsankar, A. et al. Target and non-target toxicity of botanical insecticide derived from Couroupita guianensis L. flower against generalist herbivore, Spodoptera litura Fab. and an earthworm, Eisenia foetida Savigny. Ecotoxicol. Environ. Saf. 133, 260–270 (2016).
Xiong, X., Yao, M., Fu, L., Ma, Z. & Zhang, X. The botanical pesticide derived from Sophora flavescens for controlling insect pests can also improve growth and development of tomato plants. Ind. Crops Prod. 92, 13–18 (2016).
Llana-Ruiz-Cabello, M. et al. In vitro toxicological evaluation of essential oils and their main compounds used in active food packaging: A review. Food Chem. Toxicol. 81, 9–27 (2015).
Can Baser, K. Biological and Pharmacological Activities of Carvacrol and Carvacrol Bearing Essential Oils. Curr. Pharm. Des. 14, 3106–3119 (2008).
Duman, A. D. et al. Evaluation of bioactivity of linalool-rich essential oils from Ocimum basilucum and Coriandrum sativum varieties. Nat. Prod. Commun. 5, 969–974 (2010).
Park, S.-N. et al. Antimicrobial effect of linalool and α-terpineol against periodontopathic and cariogenic bacteria. Anaerobe 18, 369–372 (2012).
Beier, R. C. et al. Evaluation of linalool, a natural antimicrobial and insecticidal essential oil from basil: Effects on poultry. Poult. Sci. 93, 267–272 (2014).
Ryan, M. F. & Byrne, O. Plant-insect coevolution and inhibition of acetylcholinesterase. J. Chem. Ecol. 14, 1965–1975 (1988).
Kalemba, D. & Kunicka, A. Antibacterial and antifungal properties of essential oils. Curr. Med. Chem. 10, 813–829 (2003).
Mastelić, J. et al. Comparative study on the antioxidant and biological activities of carvacrol, thymol, and eugenol derivatives. J. Agric. Food Chem. 56, 3989–3996 (2008).
Locci, E., Lai, S., Piras, A., Marongiu, B. & Lai, A. 13C-CPMAS and 1H-NMR study of the inclusion complexes of beta-cyclodextrin with carvacrol, thymol, and eugenol prepared in supercritical carbon dioxide. Chem. Biodivers. 1, 1354–1366 (2004).
Marques, H. M. C. A review on cyclodextrin encapsulation of essential oils and volatiles. Flavour Fragr. J. 25, 313–326 (2010).
Hosseini, S. F., Zandi, M., Rezaei, M. & Farahmandghavi, F. Two-step method for encapsulation of oregano essential oil in chitosan nanoparticles: Preparation, characterization and in vitro release study. Carbohydr. Polym. 95, 50–56 (2013).
Joye, I. J. & McClements, D. J. Biopolymer-based nanoparticles and microparticles: Fabrication, characterization, and application. Curr. Opin. Colloid Interface Sci. 19, 417–427 (2014).
Davis, M. E. & Brewster, M. E. Cyclodextrin-based pharmaceutics: past, present and future. Nat. Rev. Drug Discov. 3, 1023–1035 (2004).
Zhang, X. et al. Chitosan bearing pendant cyclodextrin as a carrier for controlled protein release. Carbohydr. Polym. 77, 394–401 (2009).
Kumirska, J., Weinhold, M. X., Thöming, J. & Stepnowski, P. Biomedical Activity of Chitin/Chitosan Based Materials—Influence of Physicochemical Properties Apart from Molecular Weight and Degree of N-Acetylation. Polymers 3, 1875–1901 (2011).
Zargar, V., Asghari, M. & Dashti, A. A Review on Chitin and Chitosan Polymers: Structure, Chemistry, Solubility, Derivatives, and Applications. ChemBioEng Rev. 2, 204–226 (2015).
Hua, D. et al. Smart Chitosan-Based Stimuli-Responsive Nanocarriers for the Controlled Delivery of Hydrophobic Pharmaceuticals. Macromolecules 44, 1298–1302 (2011).
Ding, Y. et al. Design and construction of polymerized-chitosan coated Fe3O4 magnetic nanoparticles and its application for hydrophobic drug delivery. Mater. Sci. Eng. C 48, 487–498 (2015).
Fan, L. et al. Fabrication of magnetic chitosan nanoparticles grafted with β-cyclodextrin as effective adsorbents toward hydroquinol. Colloids Surf. B Biointerfaces 95, 42–49 (2012).
Sajomsang, W. et al. A comparison of spacer on water-soluble cyclodextrin grafted chitosan inclusion complex as carrier of eugenol to mucosae. Carbohydr. Polym. 92, 321–327 (2013).
Yuan, Z. et al. Chitosan-graft-β-cyclodextrin nanoparticles as a carrier for controlled drug release. Int. J. Pharm. 446, 191–198 (2013).
Lopez, M. D., Maudhuit, A., Pascual-Villalobos, M. J. & Poncelet, D. Development of Formulations to Improve the Controlled-Release of Linalool to Be Applied As an Insecticide. J. Agric. Food Chem. 60, 1187–1192 (2012).
Chai, K. & Ji, H. Dual functional adsorption of benzoic acid from wastewater by biological-based chitosan grafted β-cyclodextrin. Chem. Eng. J. 203, 309–318 (2012).
Santos, E. H., Kamimura, J. A., Hill, L. E. & Gomes, C. L. Characterization of carvacrol beta-cyclodextrin inclusion complexes as delivery systems for antibacterial and antioxidant applications. LWT - Food Sci. Technol. 60, 583–592 (2015).
Marreto, R. N. et al. Thermal analysis and gas chromatography coupled mass spectrometry analyses of hydroxypropyl-β-cyclodextrin inclusion complex containing Lippia gracilis essential oil. Thermochim. Acta 475, 53–58 (2008).
Higuchi, T. & Connors, K. Phase solubility studies. Adv Anal Chem Instrum 4, 117–212 (1965).
Hill, L. E., Gomes, C. & Taylor, T. M. Characterization of beta-cyclodextrin inclusion complexes containing essential oils (trans-cinnamaldehyde, eugenol, cinnamon bark, and clove bud extracts) for antimicrobial delivery applications. LWT - Food Sci. Technol. 51, 86–93 (2013).
Tan, H., Xue, Y., Luan, Q. & Yao, X. Evaluation of glycol chitosan-graft-carboxymethyl β-cyclodextrin as potential pH-sensitive anticancer drug carrier by surface plasmon resonance. Anal. Methods 4, 2784 (2012).
García, A., Leonardi, D., Salazar, M. O. & Lamas, M. C. Modified β-Cyclodextrin Inclusion Complex to Improve the Physicochemical Properties of Albendazole. Complete In Vitro Evaluation and Characterization. PLoS ONE 9, e88234 (2014).
Schönhoff, M. NMR studies of sorption and adsorption phenomena in colloidal systems. Curr. Opin. Colloid Interface Sci. 18, 201–213 (2013).
Keawchaoon, L. & Yoksan, R. Preparation, characterization and in vitro release study of carvacrol-loaded chitosan nanoparticles. Colloids Surf. B Biointerfaces 84, 163–171 (2011).
Lacava, B. M. et al. Particle sizing of magnetite-based magnetic fluid using atomic force microscopy: A comparative study with electron microscopy and birefringence. Appl. Phys. Lett. 77, 1876 (2000).
Aguiar, U. N. et al. Preparação e caracterização do complexo de inclusão do óleo essencial de Croton zehntneri com β-Ciclodextrina. (2014).
Moraes, C. M., Abrami, P., de Paula, E., Braga, A. F. A. & Fraceto, L. F. Study of the interaction between S(−) bupivacaine and 2-hydroxypropyl-β-cyclodextrin. Int. J. Pharm. 331, 99–106 (2007).
Abarca, R. L., Rodríguez, F. J., Guarda, A., Galotto, M. J. & Bruna, J. E. Characterization of beta-cyclodextrin inclusion complexes containing an essential oil component. Food Chem. 196, 968–975 (2016).
Hedges, A. R., Shieh, W. J. & Sikorski, C. T. Use of Cyclodextrins for Encapsulation in the Use and Treatment of Food Products. in Encapsulation and Controlled Release of Food Ingredients 590, 60–71 (American Chemical Society, 1995).
Bekiroglu, S., Kenne, L. & Sandström, C. 1H NMR studies of maltose, maltoheptaose, alpha-, beta-, and gamma-cyclodextrins, and complexes in aqueous solutions with hydroxy protons as structural probes. J. Org. Chem. 68, 1671–1678 (2003).
Jiang, H., Zhang, S., Shi, Q. & Jia, Y. 1H NMR investigation of supramolecular complex between β-cyclodextrin and cholesterol. Wuhan Univ. J. Nat. Sci. 16, 79–82 (2011).
Raoov, M., Mohamad, S. & Abas, M. R. Synthesis and characterization of β-cyclodextrin functionalized ionic liquid polymer as a macroporous material for the removal of phenols and As(V). Int. J. Mol. Sci. 15, 100–119 (2013).
Kfoury, M. et al. Determination of formation constants and structural characterization of cyclodextrin inclusion complexes with two phenolic isomers: carvacrol and thymol. Beilstein J. Org. Chem. 12, 29–42 (2016).
Numanoğlu, U. et al. Use of cyclodextrins as a cosmetic delivery system for fragrance materials: linalool and benzyl acetate. AAPS PharmSciTech 8, E85 (2007).
Donze, C. & Coleman, A. W. β-CDinclusion complexes: Relative selectivity of terpene and aromatic guest molecules studied by competitive inclusion experiments. J. Incl. Phenom. Mol. Recognit. Chem. 16, 1–15 (1993).
Menezes, P. P. et al. Inclusion complex of (−)-linalool and β-cyclodextrin. J. Therm. Anal. Calorim. 115, 2429–2437 (2014).
Quintans-Júnior, L. J. et al. β-Cyclodextrin-complexed (−)-linalool produces antinociceptive effect superior to that of (−)-linalool in experimental pain protocols. Basic Clin. Pharmacol. Toxicol. 113, 167–172 (2013).
Knight, D. K., Shapka, S. N. & Amsden, B. G. Characterization of Glycol Chitosan: A Potential Material for Use in Biomedical and Pharmaceutical Applications: A Comparison of Fractionation Techniques. in Polysaccharides for Drug Delivery and Pharmaceutical Applications (eds Marchessault, R. H., Ravenelle, F. & Zhu, X. X.) 934, 227–242 (American Chemical Society, 2006).
Yu, J. et al. Folic acid conjugated glycol chitosan micelles for targeted delivery of doxorubicin: preparation and preliminary evaluation in vitro. J. Biomater. Sci. Polym. Ed. 24, 606–620 (2013).
Gonil, P. et al. Novel quaternized chitosan containing β-cyclodextrin moiety: Synthesis, characterization and antimicrobial activity. Carbohydr. Polym. 83, 905–913 (2011).
Izawa, H. et al. Facile preparation of cyclodextrin-grafted chitosans and their conversion into nanoparticles for an anticancer drug delivery system. Polym. J. 48, 203–207 (2016).
Ovenden, S. P. & Bourne, D. J. The Diffusion Ordered SpectroscopY (DOSY) pulse sequence and defence applications. (2008).
Xu, C. et al. 19F DOSY diffusion-NMR spectroscopy of fluoropolymers: 19F DOSY diffusion-NMR spectroscopy of fluoropolymers. Magn. Reson. Chem. 55, 472–484 (2017).
Li, W., Chung, H., Daeffler, C., Johnson, J. A. & Grubbs, R. H. Application of 1H DOSY for Facile Measurement of Polymer Molecular Weights. Macromolecules 45, 9595–9603 (2012).
Dumont, V. C. et al. Glycol chitosan/nanohydroxyapatite biocomposites for potential bone tissue engineering and regenerative medicine. Int. J. Biol. Macromol. 93, 1465–1478 (2016).
Mansur, A. A. & Mansur, H. S. Quantum dot/glycol chitosan fluorescent nanoconjugates. Nanoscale Res. Lett. 10 (2015).
Mangolim, C. S. et al. Curcumin–β-cyclodextrin inclusion complex: Stability, solubility, characterisation by FT-IR, FT-Raman, X-ray diffraction and photoacoustic spectroscopy, and food application. Food Chem. 153, 361–370 (2014).
Alamdarnejad, G. et al. Synthesis and characterization of thiolated carboxymethyl chitosan-graft-cyclodextrin nanoparticles as a drug delivery vehicle for albendazole. J. Mater. Sci. Mater. Med. 24, 1939–1949 (2013).
Ebadollahi, A., Sendi, J. J. & Aliakbar, A. Efficacy of Nanoencapsulated Thymus eriocalyx and Thymus kotschyanus Essential Oils by a Mesoporous Material MCM-41 Against Tetranychus urticae (Acari: Tetranychidae). J. Econ. Entomol. https://doi.org/10.1093/jee/tox234 (2017).
Tak, J.-H. & Isman, M. B. Acaricidal and repellent activity of plant essential oil-derived terpenes and the effect of binary mixtures against Tetranychus urticae Koch (Acari: Tetranychidae). Ind. Crops Prod. 108, 786–792 (2017).
Pavela, R., Stepanycheva, E., Shchenikova, A., Chermenskaya, T. & Petrova, M. Essential oils as prospective fumigants against Tetranychus urticae Koch. Ind. Crops Prod. 94, 755–761 (2016).
Çalmaşur, Ö., Aslan, İ. & Şahin, F. Insecticidal and acaricidal effect of three Lamiaceae plant essential oils against Tetranychus urticae Koch and Bemisia tabaci Genn. Ind. Crops Prod. 23, 140–146 (2006).
Tabari, M. A., Youssefi, M. R., Maggi, F. & Benelli, G. Toxic and repellent activity of selected monoterpenoids (thymol, carvacrol and linalool) against the castor bean tick, Ixodes ricinus (Acari: Ixodidae). Vet. Parasitol. 245, 86–91 (2017).
Aslan, İ., Özbek, H., Çalmaşur, Ö. & Şahin, F. Toxicity of essential oil vapours to two greenhouse pests, Tetranychus urticae Koch and Bemisia tabaci Genn. Ind. Crops Prod. 19, 167–173 (2004).
Momen, F. M., Amer, S. A. A. & Refaat, A. M. Repellent and Oviposition-Deterring Activity of Rosemary and Sweet Marjoram on the Spider Mites Tetranychus urticae and Eutetranychus orientalis (Acari: Tetranychidae). Acta Phytopathol. Entomol. Hung. 36, 155–164 (2001).
Ziaee, M., Moharramipour, S. & Mohsenifar, A. Toxicity of Carum copticum essential oil-loaded nanogel against Sitophilus granarius and Tribolium confusum. J. Appl. Entomol. 138, 763–771 (2014).
Acknowledgements
This work was supported by the São Paulo Science Foundation (grant #2014/20273-4). The authors are grateful to the Plasma Technology Laboratory (LaPTec) of the Institute of Science and Technology of Sorocaba (UNESP) for the XRD analyses, to the National Biosciences Laboratory (LNBio) for the NMR analyses, and to Profa. Dra. Luciana de Matos Alves Pinto, of the Federal University of Lavras, for assistance in the TGA analyses.
Author information
Authors and Affiliations
Contributions
E.V.R.C. and L.F.F. proposed and designed the experiments; E.V.R.C., P.L.F.P and J.L.O. carried out nanoparticles synthesis and all characterization experiments. C.C.M., J.F.D. and D.J.A. performed biological activity experiments. E.V.R.C. wrote the manuscript. All the authors participated in discussion of the research.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Campos, E.V.R., Proença, P.L.F., Oliveira, J.L. et al. Chitosan nanoparticles functionalized with β-cyclodextrin: a promising carrier for botanical pesticides. Sci Rep 8, 2067 (2018). https://doi.org/10.1038/s41598-018-20602-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-20602-y
- Springer Nature Limited
This article is cited by
-
Crosslinked Cyclodextrin as Potent Composite For Removal of Wastewater Pollutants
Current Pollution Reports (2023)
-
Eco-friendly and safe alternatives for the valorization of shrimp farming waste
Environmental Science and Pollution Research (2023)
-
Mosquito‐repellent controlled‐release formulations for fighting infectious diseases
Malaria Journal (2021)
-
Cyclodextrin-based nanoparticles for pharmaceutical applications: a review
Environmental Chemistry Letters (2021)
-
Utilization of biodegradable chitosan-derived sponges as oil retainers
Environmental Science and Pollution Research (2020)